CN102304336A - 新型sbs万能胶 - Google Patents
新型sbs万能胶 Download PDFInfo
- Publication number
- CN102304336A CN102304336A CN201110257298A CN201110257298A CN102304336A CN 102304336 A CN102304336 A CN 102304336A CN 201110257298 A CN201110257298 A CN 201110257298A CN 201110257298 A CN201110257298 A CN 201110257298A CN 102304336 A CN102304336 A CN 102304336A
- Authority
- CN
- China
- Prior art keywords
- styrene
- sbs
- essence
- ethyl acetate
- thermoplastic elastomer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种新型SBS万能胶，它由热塑性橡胶SBS、达玛树脂、石油油脂C5/C9、松香脂、乙酸乙酯EAC、6#溶剂油、碳酸二甲酯、香精组成，各组分的配比为（按重量百分比）：热塑性橡胶SBS 10-18%、达玛树脂 5-12%、石油油脂C5/C9 4-10%、松香脂 7-15%、乙酸乙酯EAC 9-11%、6#溶剂油 40-54.5%、碳酸二甲酯 10-15%、香精 0.5-1%；本发明的SBS万能胶既环保又降低成本，并且各项综合性能均达到标准要求。
Description
技术领域
本发明涉及一种粘胶剂，尤其是一种新型SBS万能胶。
背景技术
万能胶是一种常用的粘胶剂，被广泛应用家居装饰、家私制造、轿车制造、皮革制品的生产等诸多领域，主要用做不同材料之间的粘接。
传统装修用的氯丁型特效万能胶，因含有甲苯等有毒溶剂，既污染环境，又危害人体健康，因而随着人们对环保要求的日趋严格，其市场将逐步萎缩。另外，随着近年来国际原油价格的不断攀升，氯丁型特效万能胶的成本也越来越高，一些生产企业为了控制成本，采用降低胶水的固含量、减少装量（有的甚至只装半罐）等不良手段，造成很多不必要的资源浪费，也引发了氯丁胶市场上的恶性价格竞争。
与氯丁胶相比，SBS弹性体兼具塑料和橡胶的双重特性，具有高温时呈塑性、室温时呈弹性、不需要硫化和塑炼、高温能熔融、与很多聚合物相容性好和容易改性等诸多特点，非常适合制备胶粘剂和密封剂。另外，SBS弹性体还可以被多种弱极性溶剂所溶解，具有制备工艺简单、高固含量和低粘度等特点，容易制得环保型胶粘剂，目前已受到人们的普遍关注。
发明内容
本发明的目的是提供一种既环保又降低成本，并各项综合性能均达到标准要求的新型SBS万能胶。
为实现上述目的，本发明所采用的技术方案是：一种新型SBS万能胶，由热塑性橡胶SBS、达玛树脂、石油油脂C5/C9、松香脂、乙酸乙酯EAC、6#溶剂油、碳酸二甲酯、香精组成，各组分的配比为（按重量百分比）：
热塑性橡胶SBS 10-18%
达玛树脂 5-12%
石油油脂C5/C9 4-10%
松香脂 7-15%
乙酸乙酯EAC 9-11%
6#溶剂油 40-54.5%
碳酸二甲酯 10-15%
香精 0.5-1%。
所述热塑性橡胶SBS选用YH-792和AD-1101两种，它们的配比为6：7。
本发明的SBS万能胶，以天然的达玛树脂替代萜烯树脂，既环保又降低成本，并各项综合性能均达到标准要求。具有适用范围广，可以粘接多种材料的特点。
具体实施方式
下面结合具体实施例对本发明的SBS万能胶作具体说明，以助于理解本发明的内容。
实施例1
所用原料配方为：
热塑性橡胶SBS 13g、达玛树脂 10g、石油油脂C5/C9 6g、松香脂 7.4g、乙酸乙酯EAC 9.6g、6#溶剂油 40g、碳酸二甲酯 13g、香精 1g。
实施例2
所用原料配方为：
SBS YH-792 6g、SBS AD- 1101 7g、达玛树脂 10g、石油油脂C5/C9 6g、松香脂 7.4g、乙酸乙酯EAC 9.6g、6#溶剂油 40g、碳酸二甲酯 13g、香精 1g。
实施例3
所用原料配方为：
热塑性橡胶SBS 10g、达玛树脂 5g、石油油脂C5/C9 4g、松香脂 7 g、乙酸乙酯EAC 9g、6#溶剂油 54.5g、碳酸二甲酯 10g、香精 0.5g。
实施例4
所用原料配方为：
热塑性橡胶SBS 10g、达玛树脂 8g、石油油脂C5/C9 10g、松香脂 10g、乙酸乙酯EAC 11g、6#溶剂油 40g、碳酸二甲酯 10g、香精 1g。
实施例5
所用原料配方为：
热塑性橡胶SBS 18g、达玛树脂 5g、石油油脂C5/C9 4g、松香脂 8g、乙酸乙酯EAC 9.5g、6#溶剂油 40g、碳酸二甲酯 15g、香精 0.5g。
实施例6
所用原料配方为：
热塑性橡胶SBS 10g、达玛树脂 12g、石油油脂C5/C9 4g、松香脂 9g、乙酸乙酯EAC 9g、6#溶剂油 45.5g、碳酸二甲酯 10g、香精 0.5g。
实施例7
所用原料配方为：
热塑性橡胶SBS 12g、达玛树脂 5g、石油油脂C5/C9 5g、松香脂 15g、乙酸乙酯EAC 10g、6#溶剂油 40g、碳酸二甲酯 12g、香精 1g。
以上所述是本发明的优选实施方式而已，当然不能以此来限定本发明之权利范围，应当指出，对于本技术领域的普通技术人员来说，对本发明的技术方案进行修改或者等同替换，都不脱离本发明技术方案的保护范围。
Claims (2)
1.一种新型SBS万能胶，其特征是由热塑性橡胶SBS、达玛树脂、石油油脂C5/C9、松香脂、乙酸乙酯EAC、6#溶剂油、碳酸二甲酯、香精组成，各组分的配比为（按重量百分比）：
热塑性橡胶SBS 10-18%
达玛树脂 5-12%
石油油脂C5/C9 4-10%
松香脂 7-15%
乙酸乙酯EAC 9-11%
6#溶剂油 40-54.5%
碳酸二甲酯 10-15%
香精 0.5-1%。
2. 根据权利要求1所述的新型SBS万能胶，其特征是：所述热塑性橡胶SBS选用YH-792和AD-1101两种，它们的配比为6：7。