CN101244901B - 一种防水找平联结层 - Google Patents

一种防水找平联结层 Download PDF

Info

Publication number
CN101244901B
CN101244901B CN200810015416A CN200810015416A CN101244901B CN 101244901 B CN101244901 B CN 101244901B CN 200810015416 A CN200810015416 A CN 200810015416A CN 200810015416 A CN200810015416 A CN 200810015416A CN 101244901 B CN101244901 B CN 101244901B
Authority
CN
China
Prior art keywords
water
rubble
sands
proof leveling
binder course
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN200810015416A
Other languages
English (en)
Other versions
CN101244901A (zh
Inventor
陈江
王林
申全军
付建村
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shandong Transportation Institute
Original Assignee
Shandong Transportation Institute
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shandong Transportation Institute filed Critical Shandong Transportation Institute
Priority to CN200810015416A priority Critical patent/CN101244901B/zh
Publication of CN101244901A publication Critical patent/CN101244901A/zh
Application granted granted Critical
Publication of CN101244901B publication Critical patent/CN101244901B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明属于水泥混凝土桥面铺装领域。公开了一种沥青砂及含有该沥青砂的防水找平联结层结构。其特点是提供了沥青砂的混合料设计方法、沥青砂与热高粘沥青封层的合理组合及相应的施工工艺,得到一种防水效果好、平整度高、层间联结力强的防水找平联结层结构。可广泛地应用于各种路面、桥面的铺筑领域。

Description

一种防水找平联结层
技术领域
本发明涉及水泥混凝土桥面铺装领域,也可应用于水泥混凝土路面及隧道路面加铺领域等。具体地说是一种防水找平联结层。
背景技术
在路桥铺装过程中,铺装层的防水性、平整性控制质量关系着铺装层的使用寿命。在防水性方面,尤其是对于水泥混凝土桥面而言,如果未充分考虑铺装结构体系的防水效果,水份通过铺装层表面渗入铺装层与桥面之间,将加速铺装层与桥面的剥离;另一方面,渗入铺装层与桥面之间的水份,将进一步渗入桥面及梁体结构内,致使结构的钢筋锈蚀,在高寒地区还会产生冻融破坏,导致桥梁结构的性能下降,影响到桥梁的耐久性。而在平整性方面,由于传统方法施工的路桥铺装结构中缺乏必要的找平结构层,易造成路面、桥面铺装平整度下降,影响行车的舒适性;而车辆颠簸行驶的过程中,对路面、桥面的动荷载冲击增大,也加速了铺装结构的破坏。
发明内容
本发明的技术任务是针对上述现有技术的不足,提供一种防水找平联结层。
本发明的技术任务是按以下方式实现的:通过对沥青砂原料进行严格级配设计,得到防水找平效果显著的沥青砂,通过与与热高粘沥青封层的合理组合及相应的施工工艺,得到一种防水效果好、平整度高、层间联结力强的防水找平联结层结构。该结构不但有显著的防水找平效果,而且有利于加强与水泥混凝土桥面与沥青混合料铺装层的联结。
防水找平联结层的铺筑工艺为:
a、对待处理层面进行凿毛、清洗处理;
b、待处理层面干燥后,在其上表面进行热高粘沥青封层处理,具体为:
b-1、用沥青撒布机将170℃~180℃的高粘沥青撒布在待处理层面上,撒布层厚度为0.8~1.2mm;
b-2、在上述高粘沥青撒布层上撒布一层粒径为5~10mm的碎石,所述碎石以3~5%的沥青预拌;
b-3、用胶轮压路机将碎石碾压稳定;或者,用喷灯将碎石烘烤稳定;
c、完成上述热高粘沥青封层处理后,立即铺筑沥青砂层,沥青砂采用重型胶轮压路机压实3-4遍,然后用双钢轮压路机压实、压平,沥青砂层的铺筑厚度为2cm,空隙率为4-8%,
所述沥青砂的级配范围为:
9.5mm 100%~100%    4.75mm 95%~100%
2.36mm 60%~70%     1.18mm 40%~50%
0.6mm 21%~39%      0.3mm 11%~29%
0.15mm 8%~16%      0.075mm 6%~9%。
步骤c中,压实后沥青砂层的空隙率优选为4-6%。
本发明与现有技术相比具有以下突出的有益效果:
(1)采用的沥青砂结构具有良好的防水、找平的作用,减少了路面、桥面铺装层的厚度偏差,提高了铺装层的平整度,不但加强了沥青铺装层与水泥混凝土桥面的联结,同时,沥青砂上层的承重层施工后,混合料可以嵌入沥青砂结构层内,能够增强层间联结能力;
(2)热高粘沥青封层,不但起到防水层作用,还能增强待处理面与防水找平联结层之间的层间联结;
(3)沥青砂层与热高粘沥青结合使用,最大限度地增加了承重层与待处理面之间的联结强度,保证了良好地防水性能,避免水份的渗入,改善路面桥面铺装质量,可以提高沥青混合料铺装的使用性能,减少病害发生,延长路面桥面铺装层及桥梁的使用寿命。
附图说明
附图1是实施例中水泥混凝土桥桥面防水找平铺装结构的结构示意图
具体实施方式
参照说明书附图以具体实施例对本发明作以下详细地说明,但不以任何形式限制本发明。
实施例:(水泥混凝土桥桥面防水找平铺装结构)
如附图1所示:水泥混凝土桥桥面防水找平铺装结构由防水找平联结层1及承重层2构成。防水找平联结层1铺筑在桥面3与承重层2之间。防水找平联结层1包括SBS改性沥青封层1-1及沥青砂层1-2,承重层2为4cmSMA-13面层。
所述沥青砂依照下述级配范围备料(级配范围以各粒径矿料的通过百分率计):
9.5mm  100%    4.75mm  98%
2.36mm  65%    1.18mm 45%
0.6mm  30%     0.3mm  20%
0.15mm  12%    0.075mm  8%。
铺筑工艺为:
a、对水泥混凝土桥桥面3进行凿毛、清洗处理;
b、改性沥青封层1-1:桥面干燥后,用沥青撒布机将170℃~180℃的SBS改性沥青撒布在桥面上,撒布层厚度为0.8~1.2mm;随后,撒布一层粒径为5~10mm的碎石,所述碎石以3~5%的沥青预拌;最后,用胶轮压路机将碎石碾压稳定即可;
c、铺筑沥青砂层1-2:其厚度为2cm,用重型胶轮压路机压实3-4遍,然后用双钢轮压路机压实、压平即可,压实后沥青砂层的空隙率为4-6%;
d、采用现有技术铺筑承重层2。
要求在完成步骤b所述的热改性沥青封层处理后,立即进行步骤c所述的沥青砂层铺筑。

Claims (3)

1.防水找平联结层,其特征在于,通过以下铺筑工艺得到:
a、对待处理层面进行凿毛、清洗处理;
b、待处理层面干燥后,在其上表面进行热高粘沥青封层处理,具体为:
b-1、用沥青撒布机将170℃~180℃的高粘沥青撒布在待处理层面上,撒布层厚度为0.8~1.2mm;
b-2、在上述高粘沥青撒布层上撒布一层粒径为5~10mm的碎石,所述碎石以3~5%的沥青预拌;
b-3、用胶轮压路机将碎石碾压稳定;
c、完成上述热高粘沥青封层处理后,立即铺筑沥青砂层,沥青砂采用重型胶轮压路机压实3-4遍,然后用双钢轮压路机压实、压平,沥青砂层的铺筑厚度为2cm,空隙率为4-8%,
所述沥青砂的级配范围为:
9.5mm  100%~100%        4.75mm  95%~100%
2.36mm 60%~70%          1.18mm  40%~50%
0.6mm  21%~39%          0.3mm   11%~29%
0.15mm 8%~16%           0.075mm  6%~9%。
2.根据权利要求1所述的防水找平联结层,其特征在于,所述步骤b-3为:用喷灯将碎石烘烤稳定。
3.根据权利要求1所述的防水找平联结层,其特征在于,步骤c中,压实后沥青砂层的空隙率为4-6%。 
CN200810015416A 2008-03-21 2008-03-21 一种防水找平联结层 Expired - Fee Related CN101244901B (zh)