CN101200000A - 一种调节氢气露点还原氧化钼的方法 - Google Patents

一种调节氢气露点还原氧化钼的方法 Download PDF

Info

Publication number
CN101200000A
CN101200000A CNA200710179662XA CN200710179662A CN101200000A CN 101200000 A CN101200000 A CN 101200000A CN A200710179662X A CNA200710179662X A CN A200710179662XA CN 200710179662 A CN200710179662 A CN 200710179662A CN 101200000 A CN101200000 A CN 101200000A
Authority
CN
China
Prior art keywords
hydrogen
dew point
molybdenum
reduction
regulating
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CNA200710179662XA
Other languages
English (en)
Other versions
CN101200000B (zh
Inventor
刘俊怀
王仙琴
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jinduicheng Molybdenum Co Ltd
Original Assignee
Jinduicheng Molybdenum Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jinduicheng Molybdenum Co Ltd filed Critical Jinduicheng Molybdenum Co Ltd
Priority to CN200710179662XA priority Critical patent/CN101200000B/zh
Publication of CN101200000A publication Critical patent/CN101200000A/zh
Application granted granted Critical
Publication of CN101200000B publication Critical patent/CN101200000B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种调节氢气露点还原氧化钼的方法，涉及一种利用氢气还原氧化钼的生产钼粉方法。其特征在于在氧化钼－钼粉的还原工艺过程中，第一段还原的氢气露点为0～+20℃的湿氢；第二段还原的氢气的露点为－30～－60℃的干氢。本发明的一种调节氢气露点还原氧化钼的方法，第一段还原要求露点为0～+20℃的湿氢，使反应速率及放热过程可控，形成产物形貌对最终产品起重要作用；第二段还原则为了使反应加快及还原完全，则需要露点为－30～－60℃的干氢。通过提供不同露点的氢气用于氧化钼还原，得到的钼粉粒度均匀、形貌规则质量高。

Description

一种调节氢气露点还原氧化钼的方法
技术领域
一种调节氢气露点还原氧化钼的方法，涉及一种利用氢气还原氧化钼的生产钼粉方法。
背景技术
在氢气还原氧化钼生产钼粉的过程中，通常是使用纯氢进行还原。氢气生产厂家也大多致力于高纯气体的生产。氢气露点是反映气体中微量水蒸汽的含量。通常情况下，要求氢气纯度高，露点为-30～-60℃。但在有氢气参加的化学反应中，并不是露点越低越好，有时候气体中水蒸汽分压直接影响反应的产物，这就需要一种露点可调的装置技术来使反应可控，得到理想的目标产品。
氢气露点对反应过程的放热控制、最终产品形貌等起关键的作用，而且不同反应阶段需要的氢气露点不同。在国外生产企业中，通常采用氢气回收系统来调节：将工艺过程产生的含水气体通过干燥器，不同程度地吸附水分而提供干氢，再给设备通入湿氢，在设备内部得到不同露点需求的工艺段。
发明内容
本发明的目的在于提供一种能使氧化钼还原的反应过程可控，得到质量优良的调节氢气露点还原氧化钼的方法。
本发明的目的是通过以下技术方案实现的。
一种调节氢气露点还原氧化钼的方法，其特征在于在氧化钼-钼粉的还原工艺过程中，第一段还原的氢气露点为0～+20℃的湿氢；第二段还原的氢气的露点为-30～-60℃的干氢。
本发明的一种调节氢气露点还原氧化钼的方法，其特征在于其还原过程采用的氢气是以露点约-60℃的干氢作为氢气源，通过加湿的方法调节露点的。
本发明的一种调节氢气露点还原氧化钼的方法，其特征在于所述的氧化钼-钼粉的还原工艺过程中第一段还原为三氧化钼还原为二氧化钼；其工艺条件为首先给还原炉通氢升温，加热到工艺要求温度，既五温区温度为I区380℃II区420℃III区480℃IV区550℃V区500℃；调节氢气露点为+5℃，氢气流量0.2m3/h，给料舟加三氧化钼700克/舟，以每30分钟推2舟的速度进行推出料，来完成二氧化钼的加工；第二段还原为二氧化钼还原为钼粉；其工艺条件：同样是先给还原炉通氢升温，加热到工艺要求温度，既五温区温度为I区890℃II区950℃III区1000℃IV区1050℃V区980℃；调节氢气露点为-40℃，氢气流量为0.3Nm3/h，给料舟加二氧化钼800克/舟，以每40分钟推2舟的速度进行推出料，来完成钼粉的加工。
本发明的一种调节氢气露点还原氧化钼的方法，其特征在于其调节氢气露点的过程通过三个回路分别提供干氢、湿氢及不同露点的氮-氢混合气体；氢气露点常温加湿及加热加湿方法。
本发明的一种调节氢气露点还原氧化钼的方法，其特征在于其调节氢气露点的过程为将干氢直接与露点仪连接，测出干氢露点；干氢经过加湿器形成湿氢，与露点仪连接测出加湿后氢气的露点供还原使用。
本发明的一种调节氢气露点还原氧化钼的方法，其特征在于其调节氢气露点的过程为是将干湿氢的混合，将氮-氢混合后与露点仪连接，测出混合气体的露点供还原过程使用。
本发明的一种调节氢气露点还原氧化钼的方法，第一段还原要求露点为0～+20℃的湿氢，使反应速率及放热过程可控，形成产物形貌对最终产品起重要作用；第二段还原则为了使反应加快及还原完全，则需要露点为-30～-60℃的干氢。
本发明的方法，通过提供不同露点的氢气用于氧化钼还原，得到的钼粉粒度均匀、形貌规则质量高。
附图说明
图1为实施例1的产品形貌图。
具体实施方式
一种调节氢气露点还原氧化钼的方法，在氧化钼-钼粉的还原工艺过程中，第一段还原的氢气露点为0～+20℃的湿氢；第二段还原的氢气的露点为-30～-60℃的干氢；其调节氢气露点的过程通过三个回路分别提供干氢、湿氢及不同露点的氮-氢混合气体；氢气露点常温加湿及加热加湿方法。
本发明在氧化钼-钼粉的还原工艺过程中起到至关重要的作用。第一段还原要求露点为0～+20℃的湿氢，使反应速率及放热过程可控，形成产物形貌对最终产品起重要作用；第二段还原则为了使反应加快及还原完全，则需要露点为-30～-60℃的干氢。而且随原料及设备的不同，工艺气体露点也有不同的需求，因此露点调节装置是还原工艺的重要组成部分。
实施例1
在三氧化钼第一还原段，工艺需要露点为+5℃，氢气流量0.2Nm3/h，打开氢气露点调节器加湿器，打开加热开关，加热温度设为30℃；按工艺需求调节湿氢流量，则可以稳定输出+5℃的氢气。
在三氧化钼第二还原段，工艺需要露点为-40℃，氢气流量0.3Nm3/h打开加湿器但不加热，打开干、湿氢流量计，调节干-湿氢流量比例，达到工艺需求。产品钼粉粒度均匀，形貌规则，产品形貌图1。
实施例2
在三氧化钼第一还原段，工艺露点为0℃，氢气流量0.2Nm3/h，在三氧化钼第二还原段，工艺露点为-30℃，氢气流量0.3Nm3/h；产品钼粉粒度均匀，形貌规则，产品形貌好。
实施例3
在三氧化钼第一还原段，工艺露点为+20℃，氢气流量0.2Nm3/h，在三氧化钼第二还原段，工艺露点为-60℃，氢气流量0.3Nm3/h，产品钼粉粒度均匀，形貌规则，产品形貌好。

Claims (6)

1.一种调节氢气露点还原氧化钼的方法，其特征在于在氧化钼-钼粉的还原工艺过程中，第一段还原的氢气露点为0～+20℃的湿氢；第二段还原的氢气的露点为-30～-60℃的干氢。
2.根据权利要求1所述的一种调节氢气露点还原氧化钼的方法，其特征在于其还原过程采用的氢气是以露点约-60℃的干氢作为氢气源，通过加湿的方法调节露点的。
3.根据权利要求1所述的一种调节氢气露点还原氧化钼的方法，其特征在于所述的氧化钼-钼粉的还原工艺过程中第一段还原为三氧化钼还原为二氧化钼；第二段还原为二氧化钼还原为钼粉。
4.根据权利要求1所述的一种调节氢气露点还原氧化钼的方法，其特征在于其调节氢气露点的过程通过三个回路分别提供干氢、湿氢及不同露点的氮-氢混合气体；氢气露点常温加湿及加热加湿方法。
5.根据权利要求1所述的一种调节氢气露点还原氧化钼的方法，其特征在于其调节氢气露点的过程为将干氢直接与露点仪连接，测出干氢露点；干氢经过加湿器形成湿氢，与露点仪连接测出加湿后氢气的露点供还原使用。
6.根据权利要求1所述的一种调节氢气露点还原氧化钼的方法，其特征在于其调节氢气露点的过程为是将干湿氢的混合，将氮-氢混合后与露点仪连接，测出混合气体的露点供还原过程使用。
CN200710179662XA 2007-12-17 2007-12-17 一种调节氢气露点还原氧化钼的方法 Active CN101200000B (zh)