CN101191304A - 军用器材外罩织物阻燃防水透气吸波涂层胶的制备方法 - Google Patents
军用器材外罩织物阻燃防水透气吸波涂层胶的制备方法 Download PDFInfo
- Publication number
- CN101191304A CN101191304A CNA2007101354200A CN200710135420A CN101191304A CN 101191304 A CN101191304 A CN 101191304A CN A2007101354200 A CNA2007101354200 A CN A2007101354200A CN 200710135420 A CN200710135420 A CN 200710135420A CN 101191304 A CN101191304 A CN 101191304A
- Authority
- CN
- China
- Prior art keywords
- wave
- water
- coating adhesive
- ventilate
- proof
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种军用器材外罩织物阻燃防水透气吸波涂层胶的制备方法，其特征在于：所述方法是：用二异氰酸酯、羟甲基硅油和聚酯多元醇生成端基为－NCO的预聚体，然后用二羟甲基丙酸和一缩二乙二醇扩链反应，最后用成盐剂调节pH值至中性后，加入硅烷偶联剂封端，再加入纳米吸波剂的水性浆料、阻燃剂、防水剂和去离子水搅拌，即得到阻燃防水透气吸波涂层胶。本发明吸波涂层胶是一种加入吸波材料的单组分的水性聚氨酯为主体的乳液。使用该涂层胶的织物手感柔软，防水透气、对特定波长有吸收，且有防电磁辐射、抗静电和吸收电磁波的作用，同时有极高的阻燃性能，是极好的军用吸波材料。
Description
技术领域
本发明涉及一种军用器材外罩织物阻燃防水透气吸波涂层胶的制备方法，可用于军用织物的防辐射、电磁波干扰等领域。属纺织助剂技术领域。
背景技术
在本发明作出以前，以往的器材外罩织物仅具有普通的吸波功能，不同时具有阻燃防水透气等多功能。
发明内容
本发明的目的在于克服上述不足，提供一种具有明显阻燃效果、防水透气作用的军用器材外罩织物阻燃防水透气吸波涂层胶的制备方法。
本发明的目的是这样实现的：一种军用器材外罩织物阻燃防水透气吸波涂层胶的制备方法，其特征在于：所述方法是：用二异氰酸酯、羟甲基硅油和聚酯多元醇生成端基为-NCO的预聚体，然后用二羟甲基丙酸和一缩二乙二醇扩链反应，最后用成盐剂调节pH值至中性后，加入硅烷偶联剂封端，再加入纳米吸波剂的水性浆料、阻燃剂、防水剂和去离子水搅拌，即得到阻燃防水透气吸波涂层胶，所述方法的具体工艺为：在带搅拌器的反应容器中加入聚酯多元醇、二异氰酸酯和羟甲基硅油，在80-85℃反应1.5-2小时，降温至70-75℃，加入二羟甲基丙酸(DMPA)和一缩二乙二醇扩链反应，保温搅拌30-40min，滴加占二异氰酸酯重量0.08-0.12％的二丁基二月桂酸锡，加入占总体系重量8-12％重量百分比的丙酮降低体系粘度，在60-65℃保温4.5-5小时，降至室温，加入三乙胺中和后，加入硅烷偶联剂及纳米吸波剂的水性浆料、阻燃剂、防水剂和去离子水，搅拌，脱去丙酮，即得到阻燃防水透气吸波涂层胶。
所述各原料是按照以下配比进行反应的：
-NCO∶-OH＝3-4∶1(摩尔比)，其中-NCO表示异氰酸酯基，-OH表示聚酯多元醇的羟基。
二羟甲基丙酸与聚酯多元醇的摩尔比为0.5-1∶1。
一缩二乙二醇与聚酯多元醇的摩尔比为1-1.8∶1。
纳米吸波剂在涂层胶中的含量为5-30％。
阻燃剂在涂层胶中的含量为5-10％。
防水剂在涂层胶中的含量为5-8％。
硅烷偶联剂在涂层胶中的含量为≤10％。
所述羟甲基硅油在涂层胶中的含量为2％-10％。
所述的纳米吸波剂的水性浆料为纳米吸波剂粉体湿法球磨制得的水性浆料，所述纳米吸波剂粉体可以为纳米级的镍锌铁氧体、锰锌铁氧体、钛酸钡、导电炭黑、银包铁粉，水性浆料中纳米吸波剂粉体的含量为5-30％，优选的含量为10-20％。
所述的二异氰酸酯可以为IPDI，HDI，TDI，MDI，优选TDI，IPDI。
所述的聚酯多元醇可以为聚己二酸丁二醇酯或聚己内酯。
所述的硅烷偶联剂可以为KH550或KH560。
所述的防水剂可以为有机硅类防水剂或有机氟类防水剂。
所述的阻燃剂可以为有机磷或有机卤素类阻燃剂。
本发明吸波涂层胶是一种加入吸波材料的环保型单组分的水性聚氨酯为主体的乳液。使用该涂层胶的织物强度高，手感柔软，防水透气、对特定波长有吸收，且有防电磁辐射、抗静电和吸收电磁波的作用，同时有极高的阻燃性能，是极好的军用吸波材料。
本发明吸波涂层胶是以水为溶剂，在喷涂和刮涂固化过程无有害溶剂挥发。可以根本上消除物料中的有害物质。符合化工行业的环保需求。
具体实施方式
实施例1：
在烧瓶内加入70克聚己二酸丁二醇酯(PBA2000)、20克TDI、5克硅油7162(上海和盈化工有限公司)，在85℃下反应1.5小时，降温至70℃，加入2.7克二羟甲基丙酸(DMPA)，6克一缩二乙二醇，保温搅拌30min，加入50克丙酮，滴加5滴二丁基二月桂酸锡，在60℃保温4.5小时，降至室温，搅拌，加入2克三乙胺中和，再加入2克KH550，最后加入100g含量为10％的纳米镍锌铁氧体水性浆料、有机磷阻燃剂甲基磷酸二甲酯2克、有机硅类防水剂MH-11092.5克与700克离子水，搅拌，脱去丙酮，即得到阻燃防水透气吸波涂层胶。
实施例2：
在烧瓶内加入60克聚己内酯(PCL1000)、22克IPDI、5克硅油7162(上海和盈化工有限公司)，在85℃下反应1.5小时，降温至75℃，加入2.7克二羟甲基丙酸(DMPA)，6克一缩二乙二醇，保温搅拌30min，加入55克丙酮，滴加5滴二丁基二月桂酸锡，在60℃保温4.5小时，降至室温，加入2克三乙胺中和，再加入1.5克KH560，最后加入80克8％的纳米钛酸钡水性浆料、有机卤素类阻燃剂1，2-双(2，4，6-三溴苯氧基)乙烷2克、2.5克有机氟类防水剂WP-7与800克离子水，搅拌，脱去丙酮，即得到阻燃防水透气吸波涂层胶。
本发明制得的涂层胶的光泽度为90-95，拉伸强度达35-45Mpa。
Claims (10)
1.一种军用器材外罩织物阻燃防水透气吸波涂层胶的制备方法，其特征在于：所述方法是：用二异氰酸酯、羟甲基硅油和聚酯多元醇生成端基为-NCO的预聚体，然后用二羟甲基丙酸和一缩二乙二醇扩链反应，最后用成盐剂调节pH值至中性后，加入硅烷偶联剂封端，再加入纳米吸波剂的水性浆料、阻燃剂、防水剂和去离子水搅拌，即得到阻燃防水透气吸波涂层胶，所述方法的具体工艺步骤为：在带搅拌器的反应容器中加入聚酯多元醇、二异氰酸酯和羟甲基硅油，在80-85℃反应1.5-2小时，降温至70-75℃，加入二羟甲基丙酸和一缩二乙二醇扩链反应，保温搅拌30-40min，滴加占二异氰酸酯重量0.08-0.12％的二丁基二月桂酸锡，加入占总体系重量8-12％重量百分比的丙酮降低体系粘度，在60-65℃保温4.5-5小时，降至室温，加入三乙胺中和后，再加入硅烷偶联剂及纳米吸波剂的水性浆料、阻燃剂、防水剂和去离子水，搅拌，脱去丙酮，即得到军用器材外罩织物阻燃防水透气吸波涂层胶，
所述各原料是按照以下配比进行反应的：
-NCO∶-OH＝3-4∶1摩尔比，其中-NCO表示异氰酸酯基，-OH表示聚酯多元醇的羟基，
二羟甲基丙酸与聚酯多元醇的摩尔比为0.3-1∶1，
一缩二乙二醇与聚酯多元醇的摩尔比为1-1.8∶1，
纳米吸波剂在涂层胶中的含量为5-30％，
阻燃剂在涂层胶中的含量为5-10％，
防水剂在涂层胶中的含量为5-8％，
硅烷偶联剂在涂层胶中的含量为≤10％，
羟甲基硅油在涂层胶中的含量为2％-10％，
所述的纳米吸波剂的水性浆料为纳米吸波剂粉体湿法球磨制得的水性浆料，所述纳米吸波剂粉体为纳米级的镍锌铁氧体、锰锌铁氧体、钛酸钡、导电炭黑、银包铁粉，水性浆料中纳米吸波剂粉体的含量为5-30％。
2.根据权利要求1所述的一种军用器材外罩织物阻燃防水透气吸波涂层胶的制备方法，其特征在于：所述水性浆料中纳米吸波剂粉体的含量为10-20％。
3.根据权利要求1所述的一种军用器材外罩织物阻燃防水透气吸波涂层胶的制备方法，其特征在于：所述的二异氰酸酯为IPDI，HDI，TDI，MDI。
4.根据权利要求1所述的一种军用器材外罩织物阻燃防水透气吸波涂层胶的制备方法，其特征在于：所述的聚酯多元醇为聚己二酸丁二醇酯或聚己内酯。
5.根据权利要求1所述的一种军用器材外罩织物阻燃防水透气吸波涂层胶的制备方法，其特征在于：所述的硅烷偶联剂为H550或KH560。
6.根据权利要求1所述的一种军用器材外罩织物阻燃防水透气吸波涂层胶的制备方法，其特征在于：所述防水剂为有机硅类防水剂或有机氟类防水剂。
7.根据权利要求1所述的一种军用器材外罩织物阻燃防水透气吸波涂层胶的制备方法，其特征在于：阻燃剂为有机磷或有机卤素类阻燃剂。
8.根据权利要求6所述的一种军用器材外罩织物阻燃防水透气吸波涂层胶的制备方法，其特征在于：所述有机硅类防水剂为MH-1109。
9.根据权利要求6所述的一种军用器材外罩织物阻燃防水透气吸波涂层胶的制备方法，其特征在于：所述有机氟类防水剂为WP-7。
10.根据权利要求7所述的一种军用器材外罩织物阻燃防水透气吸波涂层胶的制备方法，其特征在于：所述有机磷阻燃剂为甲基磷酸二甲酯；或所述有机卤素类阻燃剂为1，2-双(2，4，6-三溴苯氧基)乙烷。