CN101191267A - 纳米耐久抗静电纺织品 - Google Patents
纳米耐久抗静电纺织品 Download PDFInfo
- Publication number
- CN101191267A CN101191267A CNA2006100977074A CN200610097707A CN101191267A CN 101191267 A CN101191267 A CN 101191267A CN A2006100977074 A CNA2006100977074 A CN A2006100977074A CN 200610097707 A CN200610097707 A CN 200610097707A CN 101191267 A CN101191267 A CN 101191267A
- Authority
- CN
- China
- Prior art keywords
- nano
- antistatic
- fiber
- particle
- resin bed
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种纳米耐久抗静电纺织品,组成纺织品的纤维中85%以上的纤维为皮膜纤维;所述皮膜纤维的单纤维表面复合有纳米皮膜树脂层,在纳米皮膜树脂层中有纳米级抗静电粒子。本发明产品具有高耐久性、高安全性、高耐热性、高耐气候性与高耐洗涤性及卓越的抗静电性能。
Description
技术领域:
本发明所涉及一种抗静电性能纺织品。
背景技术:
众所周知,涤纶是疏水性的有机高分子化合物,它既不能电离,又没有自由电子,所以,十分容易积聚电子,造成种种不良的后果,给服装生产、人类的生活带来了很大的不便,严重影响了其使用价值。要解决静电造成的诸多问题,可采用以下两种方法:一是防止静电的产生(起电)、二是减少或导去积累的静电。关于第一种方法,因静电生成的机理在目前还不了解,要制成在摩擦和运动接触过程中不会生成静电的合成纤维,似乎还不能实现;因此目前的防静电措施都是以减少静电量和导去静电的方法为主。常用的方法一是对织物进行抗静电后整理,二是将导电性纤维用混纺、交织或其它方法混合织进织物,以导去静电。对织物进行抗静电后整理是使抗静电剂吸附在织物的表面,其抗静电机理是由于抗静电剂导电、吸湿而使静电泄漏。通常抗静电剂是表面活性剂或其它亲水性化合物或具有导电性的粒子,由于与织物的结合力偏小,其耐久性较差,一般经过几次水洗或干洗就失去抗静电作用。本产品所述的纳米耐久抗静电性能纺织品,是通过在纤维表面形成连续的皮膜,通过该皮膜将抗静电剂牢固地与纤维结合,从而提高抗静电的耐久性能。
发明内容:
本发明的目的在于提供一种具有高耐久性和高抗静电性能的纳米抗静电纺织品。
本发明的技术解决方案是:
一种纳米耐久抗静电纺织品,其特征是:组成纺织品的纤维中85%以上的纤维为皮膜纤维;所述皮膜纤维的单纤维表面复合有纳米皮膜树脂层,纳米皮膜树脂层中含有纳米级的抗静电粒子。
纳米皮膜树脂层的厚度为10~1000nm。纳米皮膜树脂层的成膜树脂为聚氨酯类、氮丙啶、丙烯酸酯类、碳化二亚胺类、三聚氰胺类中的一种或几种。纳米皮膜树脂层中含有纳米级的抗静电粒子,粒子直径为200nm以下。纳米级抗静电粒子是无机抗静电粒子。无机纳米抗静电粒子是钛、硅及它们的化合物中的一种或几种。
纳米皮膜树脂层中所含有的无机纳米抗静电粒子的重量/纤维重量比值为0.01~40/100。
本发明产品的制作过程依次包括下列步骤:
a、加工纺织品的准备;
b、工作液调制:将成膜剂(聚氨酯类、氮丙啶、丙烯酸酯类、碳化二亚胺类、三聚氰胺类中的一种或几种)、渗透剂(渗透剂JFC或烷基磺酸盐等)、分散剂(聚丙烯酸盐、氨基硅油、分散剂PAS或六偏磷酸盐等)、氧化剂(过氧化物或过硫酸盐等)、粘合剂(碳化二亚胺或氮丙啶等)、纳米无机抗静电粒子(钛、硅及它们的化合物中的一种或几种)以及水按照下列比例混合、充分搅拌调制成纳米抗静电整理工作液;
纳米抗静电整理工作液(1L):
成膜剂 10-50g
粘合剂 0-50g
渗透剂 0-20g
氧化剂 1-20g
分散剂 0~20g
纳米无机抗静电粒子 10~100g
其余都为软水;将步骤①中的织物浸渍在所制成的纳米抗静电整理工作液中(每升工作液中浸渍1.5公斤的织物),通过物理作用将成膜加工液附着在纤维表面。
c、热处理:在温度80~120℃的条件下热处理2~20分钟,使纳米皮膜包裹于单纤维的表面;
d、皂洗:热处理后,在温度为50~80℃水浴中洗涤5~20分钟,去除吸附在纤维表面的药剂;
e、烘干、定型:水洗后进行充分烘干,烘干处理后在温度为160~190℃的条件下定型30~120秒。
本发明产品具有高耐久性、高安全性、高耐热性、高耐气候性与高耐洗涤性及卓越的抗静电性能。
附图说明:
下面结合附图和实施例对本发明作进一步说明。
图1是本发明一个实施例皮膜纤维的结构示图。
图2图3是本发明一个实施例产品TEM(透射电镜)观察结果照片。
图4是本发明一个实施例产品SEM(扫描电镜)断面观察结果照片。
具体实施方式:
实施例1:
一种纳米耐久抗静电纺织品制造方法包括以下步骤:
①加工织物的准备:T/C织物;
②工作液调制:
纳米无机抗静电粒子 20g/L
丙烯酸酯类成膜剂 30g/L
过硫酸铵氧化剂 2g/L
其余为软水。其中纳米无机抗静电粒子为氧化硅粒子(或钛粒子或硅粒子或它们的化合物中的一种或几种),直径为200nm以下。将上述成分混合、充分搅拌调制成纳米抗静电整理工作液。将步骤①中的织物浸渍在所制成的纳米抗静电整理工作液中(每升工作液中浸渍1.5公斤的织物),通过物理作用将纳米抗静电整理工作液附着在纤维表面。
③热处理:在温度80~120℃(例80℃、90℃、100℃、110℃、120℃)的条件下处理2~20分钟(例4分钟、8分钟、12分钟、16分钟、20分钟)。
④皂洗:在温度为50~80℃(例50℃、70℃、80℃)水浴中洗涤5~20分钟(例5分钟、10分钟、20分钟)。
⑤烘干、定型:皂洗后在100~150℃(例100℃、130℃、150℃)的温度下烘干处理3~15分钟(例3分钟、5分钟、10分钟)。然后在温度为160~190℃(例160℃、170℃、180℃、190℃)的条件下定型30~120s(例30秒、90秒、120秒),得本产品。
得到的产品组成纺织品的纤维中85%以上(例85%、95%、100%)的纤维为单纤维1的表面复合有纳米皮膜树脂层2的皮膜纤维,在纳米皮膜树脂层2中有纳米级抗静电粒子3,纳米级抗静电粒子3被纳米皮膜成膜树脂固定在单纤维上。且纳米皮膜树脂层的厚度为10~1000nm(例10nm、500nm、1000nm)。纳米皮膜树脂层的成膜树脂为丙烯酸酯类。本发明产品具有高耐久性、高安全性、高耐热性、高耐气候性与高耐洗涤性及卓越的抗静电性能。
抗静电测试:
测试方法:JIS L1094
测试结果如下:
HL:家庭洗涤
实施例2:
①加工织物的准备:涤纶100%右斜织物
②工作液调制:
成膜剂(聚氨酯类、氮丙啶、碳化二亚胺类、三聚氰胺类中的一种或几种)10-50g(例10克、30克、50克)
氧化剂(过氧化物或过硫酸盐)1-20g(例1克、10克、20克)
纳米无机抗静电粒子10~100g(例10克、30克、50克、80克、100克),纳米无机抗静电粒子直径为200nm以下
其余都为软水。其余同实施例1。
得到的产品组成纺织品的纤维中85%以上的纤维为单纤维的表面复合有纳米皮膜树脂层的皮膜纤维,在纳米皮膜树脂层中有纳米级抗静电粒子,纳米级抗静电粒子被纳米皮膜成膜树脂固定在单纤维上。且纳米皮膜树脂层的厚度为10~1000nm(例10nm、500nm、1000nm)。纳米皮膜树脂层的成膜树脂为聚氨酯类、氮丙啶或三聚氰胺类等。本发明产品具有高耐久性、高安全性、高耐热性、高耐气候性与高耐洗涤性及卓越的抗静电性能。
Claims (6)
1.一种纳米耐久抗静电纺织品,其特征是:组成纺织品的纤维中85%以上的纤维为皮膜纤维;所述皮膜纤维的单纤维表面复合有纳米皮膜树脂层,纳米皮膜树脂层中含有纳米级的抗静电粒子。
2.根据权利要求1所述的纳米耐久抗静电纺织品,其特征是:纳米皮膜树脂层的厚度为10~1000nm。
3.根据权利要求1或2所述的纳米耐久抗静电纺织品,其特征是:纳米皮膜树脂层的成膜树脂为聚氨酯类、氮丙啶、丙烯酸酯类、碳化二亚胺类、三聚氰胺类中的一种或几种。
4.根据权利要求1或2所述的纳米耐久抗静电纺织品,其特征是:纳米皮膜树脂层中含有纳米级的抗静电粒子,粒子直径为200nm以下。
5.根据权利要求4所述的纳米耐久抗静电纺织品,其特征是:纳米级抗静电粒子是无机抗静电粒子。
6.根据权利要求5所述的纳米耐久抗静电纺织品,其特征是:无机纳米抗静电粒子是钛、硅及它们的化合物中的一种或几种。