CN101186776A - 一种地坪水基涂料 - Google Patents
一种地坪水基涂料 Download PDFInfo
- Publication number
- CN101186776A CN101186776A CNA2006101183876A CN200610118387A CN101186776A CN 101186776 A CN101186776 A CN 101186776A CN A2006101183876 A CNA2006101183876 A CN A2006101183876A CN 200610118387 A CN200610118387 A CN 200610118387A CN 101186776 A CN101186776 A CN 101186776A
- Authority
- CN
- China
- Prior art keywords
- water
- based paint
- terrace
- weight percent
- paint according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种地坪水基涂料,该涂料的原料配方的组分和重量百分比如下:有机硅-丙烯酸核壳聚合物乳液34~46%,分散剂1.0~2.5%,钛白粉3~8%,填料36~ 48%,颜料或色浆2~5%,成膜助剂2~5%,消泡剂重0.3~0.6%,pH调节剂0.2~1%,余量为水。与现有技术产品相比,本发明涂料具有环保、节能、安全可靠、快干保养时间短、易于重涂施工等优点。
Description
技术领域
本发明涉及一种水性的适合于地坪涂布的液膜型涂料,尤其涉及一种以有机硅改性丙烯酸核壳结构的乳液聚合物以及硅石灰为主要成膜物质,更配合其他助剂而制备的水性涂料。
背景技术
随着当今社会经济的飞速发展,建筑项目层出不穷。楼群、商场、工业园区、车库以及各类场所比比皆是,地坪养护已成为一种必不可少的建设措施,作为地坪涂料的使用,文明整洁、安全环保、可靠持久已成为其性能质量的主流要求。
我国目前所使用的地坪涂料,大多仍沿用传统型溶剂漆,少量也有见诸水性环氧涂料的报道使用,但前者含有大量有害物质伤害施工人员及影响环境,上海和其他地区每年都有施工人员中毒受伤害的事故发生。至于后者水性环氧虽然毒害性有所改善(水性,但未见VOC值公布),但由于涂布道数多,配方复杂、工序繁杂且涂布后保养时间长(需要一周以上时间),故亦在使用上受到很大限制。显然,研究开发制备高性能、安全环保且易于施工和重涂以及养护时间短的地坪涂料,已是刻不容缓的社会共同要求。
发明内容
本发明的目的就是为了克服上述现有技术存在的缺陷提供一种环保、节能、安全可靠、易于重涂施工的地坪水基涂料。
本发明的目的可以通过以下技术方案来实现:
一种地坪水基涂料,其特征在于,该涂料的原料配方如下:
组分 重量百分比
有机硅一丙烯酸核壳乳液 34~46%,
分散剂 1.0~2.5%,
钛白粉 3~8%,
填料 36~48%,
颜料或色浆 2~5%,
成膜助剂 2~5%,
消泡剂 0.2~0.6%,
PH调节剂 0.2~1%,
余量的水。
所述的有机硅一丙烯酸核壳乳液重量百分比为37~42%,分散剂重量百分比为1.4~2..1%,钛白粉重量百分比为5.0~8.0%,填料重量百分比为43~48%,颜料或色浆重量百分比为3~4%,成膜助剂重量百分比为3~4%,消泡剂重量百分比为0.3~0.6%,PH调节剂重量百分比为0.4~0.7%,余量为水。
所述有机硅一丙烯酸核壳乳液为硅氧烷接技反应的改性丙烯酸自交联型聚合物乳液。
所述的有机硅一丙烯酸聚合物乳液的单体组成重量比为硅氧烷∶丙烯酸丁酯∶甲基丙烯酸甲酯∶丙烯酸∶羟甲基丙烯酰胺=5-7∶38-42∶40-50∶2-4∶1-4。
所述的分散剂包括烷基酚聚氧乙烯醚、阴离子脂肪酸盐或其混合物。
所述的钛白粉为进口和国产的混合物,藉以奠定白色基色。
所述的填料包括硅灰石、石英粉,优选硅灰石。它可以起到成膜骨架作用。
所述的成膜助剂包括十二酯醇、苯甲醇或其混合物,优选十二酯醇。它可以起到降低最低成膜温度,提高成膜性能。
所述的消泡剂包括非硅类消泡剂。它起到消除体系孔泡作用,使成膜连续美观,无缺陷。
所述的PH调节剂包括三乙胺或醇胺类有机物。它有利于提高体系稳定作用。
本发明为一种水性的聚合物型的地坪涂料。施工涂布于地坪,具有渗透润湿性佳、封用性附着力强、耐水耐磨、持久防滑、施工方便成本低、养护时间极短、当天即可使用跑车走人、易于一次多次重涂等综合优点,尤其是其低VOC值(≤40g/L),主体是水基,不燃不爆、无毒无害,故给予施工现场安全可靠性、施工人员的健康保障、施工后的环境保护,带来了肯定的结果,这些都是传统型溶剂漆或水性环氧漆所无法比拟的。
具体实施方式
下面结合具体实施例,对本发明作进一步说明。
实施例1
一种地坪水基涂料,该涂料的配方为(重量百分比):
硅丙乳液(40%重量) 37.0
烷基酚聚氧乙烯醚(30%重量) 1.5
钛白粉 7.0
硅灰石 43.0
色浆 4.0
十二醇酯 2.0
苯甲醇 1.0
PD-550消泡剂 0.4
三乙胺 0.5
水 3.6
实施例2
一种地坪水基涂料,该涂料的配方为(重量百分比):
硅丙乳液(40%重量) 39
阴离子脂肪酸盐(30%重量) 1.5
钛白粉 8.0
硅灰石 35.0
石英粉 10.0
十二醇酯 3.0
苯甲醇 1.0
KLD-980(聚硅酮高效消泡剂) 0.5
三乙醇胺 0.4
水 1.6
实施例3
一种地坪水基涂料,该涂料的配方为(重量百分比):
硅丙乳液(40%重量) 40.0
烷基酚聚氧乙烯醚(30%重量) 1.5
钛白粉 5.0
颜料 2.5
硅灰石 45.0
十二醇酯 3.2
PD-550消泡剂 0.6
三乙胺 0.5
水 1.7
本发明的地坪水基涂料施工时地面宜干燥干净、无积水、无沙尘、无脂物,温度≥15℃,相对湿度≤70%,避免雨雾天气或潮湿冰冻状态作业,以利均匀连续成膜和快干。本发明一次配方,无需分底中面,可以一次或多次复涂,如遇原有漆面亦无须铲除,可以直接重涂。可视情况采用滚涂、刮涂、喷涂等方式作业;采用滚、刮涂可以直接以涂料涂布,采用喷涂可用适量水稀释操作。建议漆膜厚度:干膜30~50μm,湿膜60~80μm,一般30分钟即可通车或人行,24小时后即可达最高强度。
因为我国现行未有地坪水基涂料的国家标准或行业标准,故只能参照某些相关标准,如外墙涂料标准GB/T 9755-2001及交通行业标准JT/T 280-2004等标准进行对比测试,将上述配方涂布测试,均能达到如下性能:
表干时间(20℃,60%湿度)min | ≤30 |
实干时间(20℃,60%湿度)min | ≤60 |
硬度(GB/T 6739-1996)H | ≥2 |
附着力(GB/T 1720-1989) | ≤2 |
耐磨性(200转1000g,磨耗量)mg | ≤40 |
耐水性 | 96小时不起泡,不脱落 |
耐碱性[饱和Ca(OH)2溶液浸泡] | 96小时无异常 |
附:涂料VOC值
VOC(g/L)GB 18582-2001 | <40.0 |
上述结果以及有关实地试用表明,本发明之地坪水基涂料完全适合车库、楼层、商场、园区等场合地坪涂布施工,具有快干养护时间短暂、综合性能好、绿色环保、易于重涂、持久稳定、施工方便和综合成本低等优点。
Claims (9)
1.一种地坪水基涂料,其特征在于,该涂料的原料配方如下:
组分 重量百分比
有机硅一丙烯酸核壳乳液 34~46%,
分散剂 1.0~2.5%,
钛白粉 3~8%,
填料 36~48%,
颜料或色浆 2~5%,
成膜助剂 2~5%,
消泡剂 0.2~0.6%,
PH调节剂 0.2~1%,
余量的水。
2.根据权利要求1所述的地坪水基涂料,其特征在于,所述的有机硅一丙烯酸核壳乳液重量百分比为37~42%,分散剂重量百分比为1.4~2..1%,钛白粉重量百分比为5.0~8.0%,填料重量百分比为43~48%,颜料或色浆重量百分比为3~4%,成膜助剂重量百分比为3~4%,消泡剂重量百分比为0.3~0.6%,PH调节剂重量百分比为0.4~0.7%,余量为水。
3.根据权利要求1或2所述的地坪水基涂料,其特征在于,所述有机硅一丙烯酸核壳乳液为硅氧烷接技反应的改性丙烯酸自交联型聚合物乳液。
4.根据权利要求3所述的地坪水基涂料,其特征在于,所述的有机硅一丙烯酸聚合物乳液的单体组成重量比为硅氧烷∶丙烯酸丁酯∶甲基丙烯酸甲酯∶丙烯酸∶羟甲基丙烯酰胺=5-7∶38-42∶40-50∶2-4∶1-4。
5.根据权利要求1或2所述的地坪水基涂料,其特征在于,所述的分散剂包括烷基酚聚氧乙烯醚、阴离子脂肪酸盐或其混合物。
6.根据权利要求1或2所述的地坪水基涂料,其特征在于,所述的填料包括硅灰石、石英粉,优选硅灰石。
7.根据权利要求1或2所述的地坪水基涂料,其特征在于,所述的成膜助剂包括十二酯醇、苯甲醇或其混合物,优选十二酯醇。
8.根据权利要求1或2所述的地坪水基涂料,其特征在于,所述的消泡剂包括非硅类消泡剂。
9.根据权利要求1或2所述的地坪水基涂料,其特征在于,所述的PH调节剂包括三乙胺或醇胺类有机物。