CN101186736A - Soft ceramic mud and preparation method thereof - Google Patents
Soft ceramic mud and preparation method thereof Download PDFInfo
- Publication number
- CN101186736A CN101186736A CNA2007101984987A CN200710198498A CN101186736A CN 101186736 A CN101186736 A CN 101186736A CN A2007101984987 A CNA2007101984987 A CN A2007101984987A CN 200710198498 A CN200710198498 A CN 200710198498A CN 101186736 A CN101186736 A CN 101186736A
- Authority
- CN
- China
- Prior art keywords
- ceramic mud
- soft ceramic
- weight
- parts
- pvc
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a soft ceramic mud and a preparation method, which is prepared by polyvinylchloride pasty resin 15-40 parts by weight, dioctyl phthalate 20-55 parts by weight, calcium carbonate 15-35 parts by weight, plasticizer 0.1-0.4 parts by weight, toner 0.5-0.15 parts by weight, and trace moisture and impurity. The invention further discloses a preparation method, which comprises weighting and arranging each component proportionally into a mixer to be mixed until all components have no nodular powder exist and are uniformly mixed with uniform color, arranging the uniformly mixedmud in a forming machine, to squeeze and mould. The invention provides the soft ceramic mud which is hard and fine in texture under normal temperature, low in softening temperature to soften by hand temperature, low in toasting temperature and short in time, while the toasted material is as hard as ceramic, without any odor, but with environment protection.
Description
Technical field:
The present invention relates to the handicraft material, be specifically related to a kind of soft ceramic mud and preparation method.
Background technology:
Soft ceramic mud is bread soil again, is a kind of polymerizability potter's clay, and this material color is abundant, and snappiness is good, is that a kind of characteristics such as potter's clay, paper clay, sculpture greasy filth, plasticine that collect are created material for handicraft all over the body.The audient is wide for this material, after manually person's sculpture, intention are made moulding, with the baking of family expenses common electrical baking box, may be molded to promptly that color is beautiful, pattern is ever-changing, hard as the exquisite ornaments and the artwork of making pottery.Soft ceramic mud is to make pottery in household person and all kinds of entertainment place, and the good material of self-recreation also is that school, kindergarten carry out aesthetic education to youngsters and children, the teaching aid of manual teaching.Present soft ceramic mud product quality is not meticulous, and plasticity-is not good, and has some chemical material tastes.
Summary of the invention:
For overcoming the technological deficiency that the quality particle is not meticulous, plasticity-is not good that existing soft ceramic mud exists, the objective of the invention is to, provide a kind of normal temperature quality hard careful, plasticity-good, the soft ceramic mud of environmental protection; The present invention also aims to, its preparation method is provided.
The technical scheme that the present invention is taked for achieving the above object is:
A kind of soft ceramic mud, comprise the component of following weight part ratio: polyvinyl chloride (PVC) RESINS 15～40, bizinc resin 20～55, lime carbonate 15～35, softening agent 0.1～0.4, toner 0.5～0.15, all the other are micro-moisture and impurity.
Described soft ceramic mud, comprise the component of following weight part ratio: polyvinyl chloride (PVC) RESINS 20～35, bizinc resin 25～40, lime carbonate 20～30, softening agent 0.1～0.3, toner 0.5～0.12, all the other are micro-moisture and impurity.
Described soft ceramic mud, comprise the component of following weight part ratio: polyvinyl chloride (PVC) RESINS 28, bizinc resin 36, lime carbonate 25, softening agent 0.25, toner 0.1, all the other are micro-moisture and impurity.
Described softening agent is a glycol ether dibenzoic acid fat.
Described polyvinyl chloride (PVC) RESINS is a polyvinyl chloride (PVC) paste resin.
The preparation method of soft ceramic mud as described above may further comprise the steps: take by weighing each component in proportion, the component that takes by weighing is put into stirrer stir, till all components evenly are blended together.
Described softening agent is a glycol ether dibenzoic acid fat.
Described polyvinyl chloride (PVC) RESINS is a polyvinyl chloride (PVC) paste resin.
The invention has the beneficial effects as follows:
1, quality is hard careful at normal temperatures for soft ceramic mud provided by the invention, can work with great care, and plasticity-is good stable molding;
2, it can soften moulding or repairing in tepor, and available hand temperature is softening, moulding easy, suitable teaching in classroom;
3, this soft ceramic mud is not touched with one's hand, is not shunk;
4, this soft ceramic mud storing temperature is low, and storing time is short, and baking back material is the same with pottery hard;
5, its nontoxic, tasteless, environmental protection, security is good concerning children.
Its preparation method provided by the invention, step is simple, and is easy and simple to handle, constant product quality.
The invention will be further described below in conjunction with embodiment.
Embodiment:
Embodiment 1: a kind of soft ceramic mud provided by the invention, it mainly is prepared from (unit: kilogram) by following parts by weight of component: polyvinyl chloride (PVC) RESINS 15～40, bizinc resin 20～55, lime carbonate 15～35, softening agent 0.1～0.4, toner 0.5～0.15, and all the other are micro-moisture and impurity; Wherein softening agent is glycol ether dibenzoic acid fat or DEDB or dibutylester, and polyvinyl chloride (PVC) RESINS is a polyvinyl chloride (PVC) paste resin.
Concrete, its parts by weight of component is: polyvinyl chloride (PVC) resin 15, bizinc resin 20, lime carbonate 15, softening agent 0.1, toner 0.5.
The preparation method of aforementioned soft ceramic mud may further comprise the steps:
Take by weighing each component in proportion, the component that takes by weighing is put into stirrer stir, in mixture till no thin bulk powder, the color even.The pug that obtains after stirring is put into shaper, and extrusion molding can make block finished product.
Embodiment 2: a kind of soft ceramic mud provided by the invention and preparation method thereof, it is basic identical in embodiment 1, its difference is that described soft ceramic mud is prepared from (unit: kilogram): polyvinyl chloride (PVC) RESINS 40, bizinc resin 55, lime carbonate 35, softening agent 0.4, toner 0.15 by following parts by weight of component; All the other are micro-moisture and impurity.
Embodiment 3: a kind of soft ceramic mud provided by the invention and preparation method thereof, it is basic identical in embodiment 1, its difference is, described soft ceramic mud is prepared from (unit: kilogram) by following parts by weight of component: polyvinyl chloride (PVC) RESINS 28, bizinc resin 36, lime carbonate 25, softening agent 0.25, toner 0.1, all the other are micro-moisture and impurity.
The soft ceramic mud product fineness that the above embodiment of the present invention provided all reaches more than 1000 orders, and just can toast with the family expenses electric oven, and storing temperature is 100～130 degree, is can make required pottery in 10～15 minutes according to the wall thickness situation of base substrate; Product provided by the invention can be by the test (ROHS) of Europe at electronic product, and the detection of the project of lead, mercury, cadmium, chromium, Polybrominated biphenyl, Poly Brominated Diphenyl Ethers is qualified, and technical superiority is obvious.
Adopt and described same or analogous component of the above embodiment of the present invention or method, resulting other soft ceramic mud is all within protection domain of the present invention.
Claims (6)
1. soft ceramic mud, it is characterized in that: it comprises the component of following weight part ratio: polyvinyl chloride (PVC) RESINS 15～40, bizinc resin 20～55, lime carbonate 15～35, softening agent 0.1～0.4, toner 0.5～0.15, all the other are micro-moisture and impurity.
2. soft ceramic mud according to claim 1, it is characterized in that: it comprises the component of following weight part ratio: polyvinyl chloride (PVC) RESINS 20～35, bizinc resin 25～40, lime carbonate 20～30, softening agent 0.1～0.3, toner 0.5～0.12, all the other are micro-moisture and impurity.
3. soft ceramic mud according to claim 1 is characterized in that: it comprises the component of following weight part ratio: polyvinyl chloride (PVC) RESINS 28, bizinc resin 36, lime carbonate 25, softening agent 0.25, toner 0.1, all the other are micro-moisture and impurity.
4. according to the described a kind of soft ceramic mud of one of claim 1～3, it is characterized in that: described softening agent is a glycol ether dibenzoic acid fat.
5. according to the described a kind of soft ceramic mud of one of claim 1～3, it is characterized in that: described polyvinyl chloride (PVC) RESINS is a polyvinyl chloride (PVC) paste resin.
6. preparation method as the described soft ceramic mud of one of claim 1 to 3 is characterized in that it may further comprise the steps:
(1) takes by weighing each component in proportion;
(2) component that takes by weighing is put into stirrer successively and stir, evenly be blended together until all components.