CN101164769B - 储罐外覆用机制玻璃纤维增强聚酯板及其制备工艺 - Google Patents
储罐外覆用机制玻璃纤维增强聚酯板及其制备工艺 Download PDFInfo
- Publication number
- CN101164769B CN101164769B CN2007101314951A CN200710131495A CN101164769B CN 101164769 B CN101164769 B CN 101164769B CN 2007101314951 A CN2007101314951 A CN 2007101314951A CN 200710131495 A CN200710131495 A CN 200710131495A CN 101164769 B CN101164769 B CN 101164769B
- Authority
- CN
- China
- Prior art keywords
- film
- polyester
- glass fiber
- fiber felt
- storage tank
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明的目的是提供玻璃纤维增强聚酯板,其是一种玻璃钢板材新品种,表面均匀、平整,具有耐水、耐温、耐候、防霉、隔热、高强度的性能,可以作为储罐外覆专用板材。其包括MELINEX301或389聚酯薄膜和粘接在其表面的经不饱和聚酯树脂浸渍后的短切玻璃纤维毡。
Description
技术领域
本发明涉及机制玻璃纤维增强聚酯板,具体地说,是一种储罐外覆用机制玻璃纤维增强聚酯板及其制备工艺。
背景技术
随着我国经济建设的迅速发展,尤其是石化产业的大幅提升,对各类特殊用途的柱状罐式集装箱(储罐)的需求十分巨大,常用材料很难满足储罐对外覆层的耐水、耐温、耐候、防霉、隔热、高强度等特殊要求。
发明内容
本发明的目的是提供机制玻璃纤维增强聚酯板,其是一种玻璃钢板材新品种,表面均匀、平整,具有耐水、耐温、耐候、防霉、隔热、高强度的性能。
该机制玻璃纤维增强聚酯板,包括MELINEX301或389聚酯薄膜和粘接在其表面的经不饱和聚酯树脂浸渍后的短切玻璃纤维毡。
MELINEX301或389聚酯薄膜是现有的产品,系美国杜邦(DuPont)公司生产的聚单氟乙烯抗老化膜,在市场上可以购买到。MELINEX301或389聚酯薄膜有一面涂有能与不饱和聚酯相互亲和的粘接剂。所以,需要以不饱和聚酯树脂浸渍短切玻璃纤维毡,不饱和聚酯树脂对玻璃纤维具有良好的混溶性,也对MELINEX301或389聚酯薄膜有良好的粘接性。
本发明同时提出了制备上述玻璃纤维增强聚酯板的工艺,包括以下步骤:先将胶衣不饱和聚酯树脂涂覆在作为下膜的MELINEX301或389聚酯薄膜上;再对其进行加热,使得MELINEX301或389聚酯薄膜表面的粘接剂融化;将短切玻璃纤维毡平铺在下膜上,树脂对短切玻璃纤维毡进行浸渍;在短切玻璃纤维毡上覆盖作为上膜的普通聚酯膜得复合胚体;将复合胚体送入凝胶炉定型、固化炉固化后剥离上膜即得。
机制玻璃纤维增强聚酯储罐外覆用板材是以不饱和聚酯树脂为基体,短切玻璃纤维为增强材料,在玻璃钢板材连续生产线上粘覆MELINEX301或389聚酯薄膜而制成。生产出的板材的具体性能指标与储罐外覆用板材要求的性能指标见表1。可见本板材完全可以用作储罐外覆用板材。
表1
项目 | 储罐外覆用板材技术要求 | 本发明板材实测结果 |
外观 | 色泽均匀,板边齐直,不得有直径大于4mm气泡,不得有针孔,露丝、分层 | 符合要求 |
树脂含量 | ≥60% | 67% |
固化度 | ≥82 | 87 |
冲击强度 | 1kg重钢球冲击后,不应产生断裂或孔穴 | 符合要求 |
巴氏硬度 | ≥40 | 51 |
抗拉强度 | ≥100MPa | 179MPa |
抗弯强度 | ≥160MPa | 251MPa |
附图说明
图1为本发明的生产工艺图
具体实施方式
以下结合附图,对本发明的实施例作详细说明。
制毡机1把无捻无碱玻璃纤维粗纱经短切后,在气流分散负压沉降作用下均匀分散,制成短切玻璃纤维毡2。
将上表面涂覆有粘接剂的抗老化MELINEX301聚酯薄膜(下膜)3经过胶衣树脂辊5,将胶衣不饱和聚酯树脂均匀的涂覆在下膜的上表面。再经过加热区4,加热到160℃,使粘接剂融化,
将制毡机1制得的短切玻璃纤维毡2平铺在下膜上表面,再让不饱和聚酯树脂对短切玻璃纤维毡进行充分浸润(浸渍),然后经过精密挤压台6进行挤压,控制厚度。
然后再在短切玻璃纤维毡上覆盖普通的聚酯膜(上膜)7后进入凝胶炉13,凝胶定型后,进入固化炉14高温固化得复合胚体,固化完全后的短切玻璃纤维毡与MELINEX301聚酯薄膜牢固的粘接成一体。固化完全后复合胚体剥离上膜7,再进入切割工序,按设定的尺寸进行横向和纵向切割,切割成所需要的成品板材,最后进入清洗干燥系统,经清洗,强风干燥后的成品板材,由检验人员检验,包装。
参见图1,图中下膜3卷绕在轴9上,其抽出端设置在主动辊10之间,在主动辊10的带动下,下膜3不断向右移动。上膜7绕在轴11上,其抽出端与轴12连接。主动辊10、轴12、制毡机1等同时工作,固化完全后的复合胚体中的上膜7缠绕在轴12上,实现与复合胚体的分离。
制毡机1制取短切玻璃纤维毡2、对下膜进行加热、以及挤压、凝胶、固化、剥离上膜、切割、清洗干燥等均属于现有技术,不再描述。
本实施例的工艺可生产厚度0.6—2.5mm,宽度500—1400mm,任意长度的玻璃纤维增强聚酯板材。其覆盖在储罐外表面的工艺属于现有技术,不再描述。
Claims (7)
1. 玻璃纤维增强聚酯板,其特征是:其包括MELINEX301或389聚酯薄膜和粘接在其表面的经不饱和聚酯树脂浸渍后的短切玻璃纤维毡。
2. 制备权利要求1所述玻璃纤维增强聚酯板的工艺,其特征在于其包括以下步骤:将不饱和聚酯树脂涂覆在作为下膜的MELINEX301或389聚酯薄膜上;对下膜进行加热,使得MELINEX301或389聚酯薄膜表面的粘接剂融化;将短切玻璃纤维毡平铺在下膜上,树脂对短切玻璃纤维毡进行浸渍;在短切玻璃纤维毡上覆盖作为上膜的普通聚酯膜得复合胚体;将复合胚体送入凝胶炉定型、固化炉固化后剥离上膜即得。
3. 根据权利要求2所述工艺,其特征在于:对下膜进行加热时,温度为130—170℃。
4. 根据权利要求2或3所述工艺,其特征在于:在覆盖上膜前,对浸渍后短切玻璃纤维毡和下膜进行挤压至需要的厚度。
5. 根据权利要求2或3所述工艺,其特征在于:对剥离上膜后的复合胚体进行清洗、干燥。
6. 根据权利要求2或3所述工艺,其特征在于:对剥离上膜后的复合胚体进行切割。
7. 权利要求1所述玻璃纤维增强聚酯板在柱状罐式集装箱上的应用。