CN101157787A - Environment-friendly type macromolecule interfacial agent - Google Patents

Abstract

The invention relates to chemical technical field, in particular to an environment-friendly polymer interface agent. The ingredients of the agent comprise deionized water, acrylamide, isobutene, methacrylicacid-2-hydroxyethyl, sodium sulphite, endrate disodium, and ammonium persulfate and styrene-acrylic emulsion. The invention overcomes the serious defects like environment pollution of traditional adesive products that contains harmful material formaldehyde, which has serious toxicity, and the product is an environment-friendly product which has the advantages of simple production technique, low cost, innocuity, insipidity, no environment pollution, resources saving, high bonding strength and permeability, good waterproof performance and being convenient for construction. In addition, the invention can be a substitution for putty powder, ceramic tile adhesive, wallpaper adhesive, and 107 adhesive, etc.

Description

Environment-friendly type macromolecule interfacial agent

Technical field:

The present invention relates to chemical technology field, specifically is a kind of environment-friendly type macromolecule interfacial agent.

Background technology:

Adhesive products such as traditional putty powder, glue for tile, wallpaper glue, the 107 glue formaldehyde that contains hazardous substance, toxicity are more greatly, not environmental protection, waste resource, viscosity be strong inadequately, and durability deficiency, water tolerance are bad.

Summary of the invention:

The objective of the invention is to overcome the deficiency of adhesive products such as existing putty powder, glue for tile, wallpaper glue, 107 glue, provide a kind of and do not conform to free formaldehyde and environment-friendly type macromolecule interfacial agent excellent performance, be used for substituting adhesive products such as putty powder, glue for tile, wallpaper glue, 107 glue.

The present invention, its ingredients by weight part is: deionized water 80-85; Acrylamide 10-12; Iso-butylene 1.0-2.0; 2-hydroxyethyl methacrylate 0.5-1.0; S-WAT 0.01-0.02; Disodium ethylene diamine tetraacetate 0.005-0.01; Ammonium persulphate 0.01-0.02; Benzene emulsion 1.0-1.5, its synthesis technique comprises:

A, acrylamide, deionized water are dropped in the reactor, stir 30 ± 5min at a slow speed, be warming up to 40 ℃;

B, open stirrer continuously, add iso-butylene and 2-hydroxyethyl methacrylate, be warming up to 60-65 ℃ then;

C, adding S-WAT stir at a slow speed, and reaction 30 ± 5min heats up 80-85 ℃ then;

D, adding disodium ethylene diamine tetraacetate stir at a slow speed, reaction 60 ± 5min;

84-85 ℃ of E, control constant temperature add ammonium persulphate, stir reaction 30 ± 5min at a slow speed;

F, be cooled to 70 ℃, add benzene emulsion, stir 15 ± 5min at a slow speed;

G, be cooled to below 45 ℃, after the assay was approved packaging final prod.

The present invention, it is simple to have production technique, characteristics such as cost is low, nontoxic, tasteless, non-environmental-pollution, saving resource, it is a kind of environmental type interfacial agents, be widely used aspect many in tackiness agent, coating, building decoration, fabric processing, sheet processing etc., have the bonding strength height, very strong perviousness is arranged, water-tolerant, advantages such as easy construction.Uses such as alternative putty powder, glue for tile, wallpaper glue, 107 glue.

Embodiment:

The preparation environment-friendly type macromolecule interfacial agent, its synthesis technique comprises:

A, with acrylamide 11.5kg, deionized water 84.0kg, drop in the reactor, stir 30min at a slow speed, be warming up to 40 ℃ simultaneously;

B, open stirrer continuously, add iso-butylene 1.5kg, 2-hydroxyethyl methacrylate 0.8kg, be warming up to 65 ℃ then;

C, adding S-WAT 0.015kg stir at a slow speed, and reaction times 30min is warming up to 85 ℃ then;

D, adding disodium ethylene diamine tetraacetate 0.01kg stir reaction times 60min at a slow speed;

84-85 ℃ of E, control add ammonium persulphate 0.02kg, stir reaction times 30min at a slow speed;

F, be cooled to 70 ℃, add benzene emulsion 1.2kg, stir 15min at a slow speed;

G, be cooled to below 45 ℃, after the assay was approved packaging final prod.

This product can in use add each color filler according to user's needs, is deployed into various colors and selects for the user, can satisfy the various demands of decoration industry.Every index meets the regulation of the environment protection industry standard HJ/T220-2005 of the People's Republic of China (PRC), is real environmental protection healthy products.

Claims (1)

1. environment-friendly type macromolecule interfacial agent, its ingredients by weight part is: deionized water 80-85; Acrylamide 10-12; Iso-butylene 1.0-2.0; 2-hydroxyethyl methacrylate 0.5-1.0; S-WAT 0.01-0.02; Disodium ethylene diamine tetraacetate 0.005-0.01; Ammonium persulphate 0.01-0.02; Benzene emulsion 1.0-1.5, its synthesis technique is:

A, acrylamide, deionized water are dropped in the reactor, stir 30 ± 5min at a slow speed, be warming up to 40 ℃;

B, open stirrer continuously, add iso-butylene and 2-hydroxyethyl methacrylate, be warming up to 60-65 ℃ then;

C, adding S-WAT stir at a slow speed, and reaction 30 ± 5min heats up 80-85 ℃ then;

D, adding disodium ethylene diamine tetraacetate stir at a slow speed, reaction 60 ± 5min;

84-85 ℃ of E, control constant temperature add ammonium persulphate, stir reaction 30 ± 5min at a slow speed;

F, be cooled to 70 ℃, add benzene emulsion, stir 15 ± 5min at a slow speed;

G, be cooled to below 45 ℃, after the assay was approved packaging final prod.