CN105152573A - Clean odorless liquid accelerator and preparation method thereof - Google Patents
Clean odorless liquid accelerator and preparation method thereof Download PDFInfo
- Publication number
- CN105152573A CN105152573A CN201510534483.8A CN201510534483A CN105152573A CN 105152573 A CN105152573 A CN 105152573A CN 201510534483 A CN201510534483 A CN 201510534483A CN 105152573 A CN105152573 A CN 105152573A
- Authority
- CN
- China
- Prior art keywords
- parts
- raw material
- water
- select
- add
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the technical field of production of building materials, in particular to a clean odorless liquid accelerator, comprising 30-40 parts of sodium hydroxide, 30-40 parts of aluminum hydroxide, 20-30 parts of sodium carbonate, 20-30 parts of potassium carbonate, 25-35 parts of sodium silicate, 15-25 parts of limestone, 25-35 parts of hydrofluoric acid, 15-25 parts of glycerin, 15-25 parts of methyl cellulose, 80-100 parts of water, and 50-60 parts of accelerating powder. The clean odorless liquid accelerator and the preparation method thereof have the advantages that the technical process is simple, the ratio of materials is reasonable, the materials for use are all chemical materials nontoxic and harmless and free of any irritating odor, the prepared clean odorless liquid accelerator is widely applicable to the preparation of concrete with no influence upon work environment, the use of the accelerator in the preparation of the concrete ensures high processing efficiency of the concrete and rarity of cracking, the application effect is significant, and the accelerator has high market value and is convenient to popularize and use.
Description
Technical field
The present invention relates to material of construction preparing technical field, be specifically related to a kind of clean liquid with no taste accelerating chemicals and preparation method thereof.
Background technology
In material of construction, concrete is the general designation being cemented to overall engineered composite material by gathering materials.Usually concrete one word said refers to makes gelling material with cement, and sand, masonry gather materials, coordinate by a certain percentage with water, the cement concrete obtained through stirring, also normal concrete is claimed, it is widely used in civil engineering work, concrete is when normally preparing, can at inner adding portion additive, thus ensure concrete high rate of utilization, hardening accelerator uses more additive at present, it mainly can improve early age strength of concrete, and to the admixture that later strength does not make significant difference, the Main Function of accelerating chemicals is: mix the admixture that can make the rapid setting and harden of concrete in concrete, ensure that concrete adds the speed in man-hour, but because some chemical materialss containing a large amount of pungent odour that are adopted on the market are at present prepared, therefore, many times, can affect to Working environment, and most material is fixing existence, therefore, not easily preserve, and easily lost efficacy.
Summary of the invention:
Technical problem to be solved by this invention is to provide a kind of formula rationally, and production technique is simple, obvious clean liquid with no taste accelerating chemicals of result of use and preparation method thereof.
Technical problem to be solved by this invention realizes by the following technical solutions:
A kind of clean liquid with no taste accelerating chemicals, is characterized in that: be made up of the raw material of following component:
Sodium hydroxide 30-40 part, aluminium hydroxide 30-40 part, sodium carbonate 20-30 part, salt of wormwood 20-30 part, water glass 25-35 part, Wingdale 15-25 part, hydrofluoric acid 25-35 part, glycerine 15-25 part, methylcellulose gum 15-25 part, water 80-100 part, rapid hardening powder 50-60 part.
The preferred ingredient of each raw material is: 35 parts, sodium hydroxide, 35 parts, aluminium hydroxide, 25 parts, sodium carbonate, 25 parts, salt of wormwood, water glass 30 parts, 20 parts, Wingdale, 30 parts, hydrofluoric acid, glycerine 20 parts, methylcellulose gum 20 parts, 90 parts, water, 55 parts, rapid hardening powder.
Described rapid hardening powder by the Tai-Ace S 150 of employing 70%, the flyash of 20% and 10% silicon powder carry out mixed grinding and form.
Another object of the present invention is to provide a kind of method preparing the clean liquid with no taste accelerating chemicals of the present invention, it is characterized in that comprising the following steps:
1., select a heating kettle, the sodium carbonate in raw material, salt of wormwood and water glass are added wherein, then add 1/3 of the total component of water in raw material, open and be heated to 80-90 DEG C, Keep agitation 10-15min; Obtain clear solution, for subsequent use;
2., again select a heating kettle, the sodium hydroxide in raw material is added wherein, again add 1/3 of water in raw material, be heated to 100-120 DEG C, until after sodium hydroxide is all dissolved in water, add wherein by the aluminium hydroxide in raw material, stirring reaction 2-4h, discharging is for subsequent use;
3., select a ball mill, the remaining water in raw material is added wherein, then add the Wingdale in raw material, hydrofluoric acid, glycerine, methylcellulose gum and rapid hardening powder, carry out ball milling, until particle fineness is after 300-400 order;
4., select a stirred pot, by step 1., the material 2. 3. processed with step of step all puts into wherein, then after mixing and stirring, discharging, can obtain, packaging warehouse-in.
The invention has the beneficial effects as follows: present invention process flow process is succinct, reasonable raw material proportioning, and that selects is nontoxic industrial chemicals, simultaneously without any irritating smell, the clean liquid with no taste accelerating chemicals of preparation, can concrete preparation widely, and ensure that Working environment is not affected, prepare for mixed earth, ensure that concrete working (machining) efficiency is high, not easy to crack, result of use is obvious, marketable value is high, is convenient to promote and use.
Embodiment
The technique means realized to make the present invention, creation characteristic, reaching object and effect is easy to understand, below in conjunction with specific embodiment, setting forth the present invention further.
Embodiment 1
Weighing sodium hydroxide 30kg, aluminium hydroxide 30kg, sodium carbonate 20kg, salt of wormwood 20kg, water glass 25kg, Wingdale 15kg, hydrofluoric acid 25kg, glycerine 15kg, methylcellulose gum 15kg, water 80kg, rapid hardening powder 50kg;
In raw material rapid hardening powder by the Tai-Ace S 150 of employing 70%, the flyash of 20% and 10% silicon powder carry out mixed grinding and form.
Preparation method is as follows:
1., select a heating kettle, the sodium carbonate in raw material, salt of wormwood and water glass are added wherein, then add 1/3 of the total component of water in raw material, open and be heated to 80-90 DEG C, Keep agitation 10-15min; Obtain clear solution, for subsequent use;
2., again select a heating kettle, the sodium hydroxide in raw material is added wherein, again add 1/3 of water in raw material, be heated to 100-120 DEG C, until after sodium hydroxide is all dissolved in water, add wherein by the aluminium hydroxide in raw material, stirring reaction 2-4h, discharging is for subsequent use;
3., select a ball mill, the remaining water in raw material is added wherein, then add the Wingdale in raw material, hydrofluoric acid, glycerine, methylcellulose gum and rapid hardening powder, carry out ball milling, until particle fineness is after 300-400 order;
4., select a stirred pot, by step 1., the material 2. 3. processed with step of step all puts into wherein, then after mixing and stirring, discharging, can obtain, packaging warehouse-in.
Embodiment 2
Weighing sodium hydroxide 35kg, aluminium hydroxide 35kg, sodium carbonate 25kg, salt of wormwood 25kg, water glass 30kg, Wingdale 20kg, hydrofluoric acid 30kg, glycerine 20kg, methylcellulose gum 20kg, water 90kg, rapid hardening powder 55kg.
In raw material rapid hardening powder by the Tai-Ace S 150 of employing 70%, the flyash of 20% and 10% silicon powder carry out mixed grinding and form.
Preparation method is as follows:
1., select a heating kettle, the sodium carbonate in raw material, salt of wormwood and water glass are added wherein, then add 1/3 of the total component of water in raw material, open and be heated to 80-90 DEG C, Keep agitation 10-15min; Obtain clear solution, for subsequent use;
2., again select a heating kettle, the sodium hydroxide in raw material is added wherein, again add 1/3 of water in raw material, be heated to 100-120 DEG C, until after sodium hydroxide is all dissolved in water, add wherein by the aluminium hydroxide in raw material, stirring reaction 2-4h, discharging is for subsequent use;
3., select a ball mill, the remaining water in raw material is added wherein, then add the Wingdale in raw material, hydrofluoric acid, glycerine, methylcellulose gum and rapid hardening powder, carry out ball milling, until particle fineness is after 300-400 order;
4., select a stirred pot, by step 1., the material 2. 3. processed with step of step all puts into wherein, then after mixing and stirring, discharging, can obtain, packaging warehouse-in.
More than show and describe ultimate principle of the present invention and principal character and advantage of the present invention.The technician of the industry should understand; the present invention is not restricted to the described embodiments; what describe in above-described embodiment and specification sheets just illustrates principle of the present invention; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements all fall in the claimed scope of the invention.Application claims protection domain is defined by appending claims and equivalent thereof.
Claims (4)
1. a clean liquid with no taste accelerating chemicals, is characterized in that: be made up of the raw material of following component:
Sodium hydroxide 30-40 part, aluminium hydroxide 30-40 part, sodium carbonate 20-30 part, salt of wormwood 20-30 part, water glass 25-35 part, Wingdale 15-25 part, hydrofluoric acid 25-35 part, glycerine 15-25 part, methylcellulose gum 15-25 part, water 80-100 part, rapid hardening powder 50-60 part.
2. the clean liquid with no taste accelerating chemicals of one according to claim 1, it is characterized in that the preferred ingredient of each raw material is: 35 parts, sodium hydroxide, 35 parts, aluminium hydroxide, 25 parts, sodium carbonate, 25 parts, salt of wormwood, water glass 30 parts, 20 parts, Wingdale, 30 parts, hydrofluoric acid, glycerine 20 parts, methylcellulose gum 20 parts, 90 parts, water, 55 parts, rapid hardening powder.
3. the clean liquid with no taste accelerating chemicals of one according to claim 1, is characterized in that: described rapid hardening powder by the Tai-Ace S 150 of employing 70%, the flyash of 20% and 10% silicon powder carry out mixed grinding and form.
4. prepare the method for a kind of clean liquid with no taste accelerating chemicals in claim 1 or 2, it is characterized in that, comprise the following steps:
1., select a heating kettle, the sodium carbonate in raw material, salt of wormwood and water glass are added wherein, then add 1/3 of the total component of water in raw material, open and be heated to 80-90 DEG C, Keep agitation 10-15min; Obtain clear solution, for subsequent use;
2., again select a heating kettle, the sodium hydroxide in raw material is added wherein, again add 1/3 of water in raw material, be heated to 100-120 DEG C, until after sodium hydroxide is all dissolved in water, add wherein by the aluminium hydroxide in raw material, stirring reaction 2-4h, discharging is for subsequent use;
3., select a ball mill, the remaining water in raw material is added wherein, then add the Wingdale in raw material, hydrofluoric acid, glycerine, methylcellulose gum and rapid hardening powder, carry out ball milling, until particle fineness is after 300-400 order;
4., select a stirred pot, by step 1., the material 2. 3. processed with step of step all puts into wherein, then after mixing and stirring, discharging, can obtain, packaging warehouse-in.