CN100404635C - Dry powder color ceramic tile adhesive - Google Patents
Dry powder color ceramic tile adhesive Download PDFInfo
- Publication number
- CN100404635C CN100404635C CNB2005100474367A CN200510047436A CN100404635C CN 100404635 C CN100404635 C CN 100404635C CN B2005100474367 A CNB2005100474367 A CN B2005100474367A CN 200510047436 A CN200510047436 A CN 200510047436A CN 100404635 C CN100404635 C CN 100404635C
- Authority
- CN
- China
- Prior art keywords
- dry powder
- ceramic tile
- water
- tile adhesive
- powder color
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention is a chemical building materials and technology, involving a dry powder color tile adhesive, involving a calcium sulfate whisker modified tile adhesive, include the following components (weight percentage) : white cement 35%~65%; quartz sand 20%-30%, filling materials 10%~35%; latex powder 2.0%~3.0%; aquasorb 0.1%~0.4%; lignocellulose 0.5%~1.0%; high alumina cement 0.5%-0.8%,crystal whiskers 0.3%~0.5%,water reducer 0.2%~1.0%, coloring agent fraction 0-0.6%. The invention of the low prices, high safety, can be directly moist surface-operation.
Description
Technical field
The invention belongs to the chemical building material technical field, relate to a kind of dry powder color ceramic tile adhesive, more specifically, relating to a kind of is the ceramic tile adhesive specially of main raw material with the white cement.
Background technology
Along with greatly developing of building decorating industry, ceramic tile use and to decorate consumption increasing, original adhesive technology and tackiness agent have many weak points.For example use cement and modified cement tackiness agent, the construction period is long, and Joint strength is low, and not attractive in appearance; With thermally melting acrylate glue or polystyrene glue, the low molecular solvent more than 40% is wherein arranged, the volatilization deal is big, polluted air, unfavorable decoration construction personnel's is healthy; Be mixed with glue with the Resins, epoxy scene, construction is inconvenient; Epoxy preparation two component adhesive mainly is applicable to be used for the hanging anchoring of ceramic tile parquets and to lay finishing, solidifying agent can occur and ooze out and pollute light ceramic tile surface phenomenon; Also have some ceramic tile tackiness agents such as JSF adds cement, macromolecule emulsion is filled, water glass is filled and the modified powdery product of macromolecular material and cement based etc.; its raw materials cost costs an arm and a leg; should not be extensive use of, and also unfavorable to environment protection.
Summary of the invention
The objective of the invention is to overcome the deficiency of above-mentioned tackiness agent, provide odorlessness under a kind of normal temperature, pollution-free, be convenient to operate, solidification intensity height, long service life be the dry powder color ceramic tile adhesive of main raw material with the white cement.
Technology solution case of the present invention can realize according to following mode:
A kind of dry powder color ceramic tile adhesive, it comprises following component (weight percentage):
White cement 35%～65%
Quartz sand 20%～30%
Filler 10%～35%
Latex powder 2.0%～3.0%
Water-holding agent 0.1%～0.4%
Lignocellulose 0.5%～1.0%
High-alumina cement 0.5%～0.8%
Plaster stone 0.3%～0.5%
Water reducer 0.2%～1.0%
Tinting material 0～0.6%.
As a kind of preferred version, described white cement label is 52.5, whiteness 〉=80 °; Filler is a water-ground limestone, quartz sand and filler fineness all 〉=200 orders; Water-holding agent: methylhydroxypropylcellulose; The high-alumina cement label is 42.5; Water reducer is Melment F10; Tinting material can select for use pigment dyestuff and mineral dye collocation to use.
Preparation method of the present invention is: the weight ratio according to afore mentioned rules takes by weighing white cement, quartz sand, filler, latex powder, water-holding agent, lignocellulose, high-alumina cement, plaster stone, water reducer, tinting material respectively, and put into stirring tank, mix through certain hour, get final product Dry Powder Shaped Tile Adhesive.The white cement of utilization of the present invention self is exactly a kind of gelling material, is used with latex powder to have cohesive strength preferably.When water exists, can generate compound with the filler reaction at normal temperatures with gelling.Add a spot of high-alumina cement and plaster stone, can increase early strength, can compensate the contraction that causes after the white cement drying again.The present invention is exactly a feature of utilizing these materials, and it as active filler, is produced a kind of Dry Powder Shaped Tile Adhesive of high-quality low-cost.In use, add a certain proportion of water, can use after stirring according to construction requirement.
Dry powder color ceramic tile adhesive of the present invention has following remarkable advantage:
1. when the bonding ceramic tile, not only can do operation, basic unit needn't sprinkle water and soak, and face brick needn't soak and dry in the shade, and has good water-retentivity.Furring brick does not play drum, does not come off, and saving of labor's grand occasion is than conventional cement mortar degree of safety height.
2. new design finalization, single component is pressed manufacturing technique requirent by factory, the proportioning of strict control effective constituent.Do not need field mix during construction, only need add tap water on request and stir and can use, bond quality is firm, stable.
3. can not tell white by the accumulation of salt in the surface soil.This tackiness agent has the excellent waterproof ability, can effectively stop moisture to enter basic unit, prevents that the accumulation of salt in the surface soil that hydrated cementitious causes from telling white phenomenon.
4. 4～5 hours initial condensation time, at this moment operator have ample time and carry out large-area levelling adjustment.About 6 hours of final setting time is compared with other rigid materials and have been accelerated speed of application, has shortened the whole duration.
5. the process of bonding applique surface brick is exactly the operation process of waterproof layer because this invention anti-permeability performance is good, at the position that needs are done facing tile, go to toilet bathe between, wall face etc., can not do waterproof layer in addition, promptly finished the operation of waterproof layer with this tackiness agent taping process.
6. directly operation on the basal plane of humidity.
7. add different tinting materials and can make the powder of different colours, and be applicable to do colored rigid roofing and colour ground concrete, ornamentally whitewash, navigation mark, the building in the seawater and other colored, water-repellent decorative engineerings in Haihe River.
8. be main raw material with cement, with low cost, production technique and equipment are simple, help suitability for industrialized production and apply, thereby have favorable economic benefit, social benefit and environmental benefit.
Embodiment
Processing step of the present invention is described by the following examples, but not limited by embodiment.
Embodiment 1: present embodiment is an example to prepare 1000 kilograms of Dry Powder Shaped Tile Adhesives:
(label is 52.5 to get 350 kilograms of white cements, whiteness 〉=80 °), add in the specific stirring tank, add 255 kilograms of quartz sands (〉=200 order), 340 kilograms of fillers (〉=200 order), 30 kilograms of latex powder, 2 kilograms of water-holding agents, 5 kilograms of lignocelluloses, 6 kilograms of high-alumina cements (label is 42.5), 4 kilogram of raw gypsum, 4 kilograms of water reducers, 4 kilograms of tinting materials again, in stirring tank, stir half an hour, after making uniform mixing, can obtain Dry Powder Shaped Tile Adhesive.
Detected result is as follows through Liaoning Province material of construction supervision and inspection institute:
Embodiment 2: chemical ingredients such as the white cement that present embodiment utilizes and index are same as the previously described embodiments, to produce 1000 kilograms of Dry Powder Shaped Tile Adhesives is example: (the type label is 52.5 to get 590 kilograms of white cements, whiteness 〉=80 °), add in the specific stirring tank, add 180 kilograms of quartz sands (〉=200 order) again, 180 kilograms of fillers (〉=200 order), 30 kilograms of latex powder, 1 kilogram of water-holding agent, 5 kilograms of lignocelluloses, 6 kilograms of high-alumina cements (label is 42.5), 4 kilogram of raw gypsum, 2 kilograms of water reducers, 2 kilograms of tinting materials, in stirring tank, stir half an hour, after making uniform mixing, promptly obtain in powdery ceramic tile tackiness agent.
Detected result is as follows through Liaoning Province material of construction supervision and inspection institute:
By above two examples as can be seen, according to different construction requirements at white cement 35%～60%, quartz sand 18%～30%, filler 18%～35%, water-holding agent 0.1%～0.4%, water reducer 0.2%～1.0%, the addition of tinting material 0～0.6% (more than be mass percent) is mediated, and can obtain the colored Dry Powder Shaped Tile Adhesive of different mechanical properties.
During use, according to construction requirement, can add a certain proportion of water, promptly Dry Powder Shaped Tile Adhesive and water mix in 0.25 ratio, after stirring, place and can use in 10 minutes.
Claims (3)
1. dry powder color ceramic tile adhesive is characterized in that, comprises following component (weight percentage):
White cement 35%～65%
Quartz sand 20%～30%
Filler 10%～35%
Latex powder 2.0%～3.0%
Water-holding agent 0.1%～0.4%
Lignocellulose 0.5%～1.0%
High-alumina cement 0.5%～0.8%
Plaster stone 0.3%～0.5%
Water reducer 0.2%～1.0%
Tinting material 0～0.6%.
2. according to the described dry powder color ceramic tile adhesive of claim 1, it is characterized in that: described white cement label is 52.5, whiteness 〉=80 °; Described filler is a water-ground limestone, the fineness of quartz sand and filler all 〉=200 orders;
3. according to claim 1 or 2 described dry powder color ceramic tile adhesives, it is characterized in that: described water-holding agent is a methylhydroxypropylcellulose; Described water reducer is Melment F10; Described high-alumina cement label is 42.5; Tinting material can select for use pigment dyestuff and mineral dye collocation to use.