CN101117499A - 建筑涂层材料制备方法 - Google Patents
建筑涂层材料制备方法 Download PDFInfo
- Publication number
- CN101117499A CN101117499A CNA2006100150644A CN200610015064A CN101117499A CN 101117499 A CN101117499 A CN 101117499A CN A2006100150644 A CNA2006100150644 A CN A2006100150644A CN 200610015064 A CN200610015064 A CN 200610015064A CN 101117499 A CN101117499 A CN 101117499A
- Authority
- CN
- China
- Prior art keywords
- dispersed
- rotational speed
- rotating speed
- stirring mill
- minutes
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
一种建筑涂层材料制备方法，先将分散剂聚丙烯酸铵盐、润湿剂、羟乙基纤维素、消泡剂加入于水中，用搅拌机以500rpm转速进行搅拌分散10分钟；将纳米光催化剂Tio2－xNx粉末慢慢加入，用搅拌机在1000rpm转速下分散15分钟；加入颜料钛白粉，重质碳酸钙120g，高岭土、滑石粉，用高速搅拌机在2000rpm转速下搅拌1小时；在装有研磨分散头和研磨介质钢化玻璃球的搅拌器中以2000rpm转速将上述预混合分散的浆料进行充分粉碎和充分混合分散，直至浆料颗粒U时，即得。本发明的优点：有效降解周围空气中的污染物质，对室内的甲醛苯酚等有机有害小分子进行降解。
Description
技术领域
本发明涉及一种建筑涂层材料制备方法。
背景技术
目前，在涂料领域纳米技术往往出现纳米粉体不能很好分散，不能提高涂料的综合性能。
发明内容
本发明的目的在于克服上述的缺陷，提供一种建筑涂层材料制备方法。
本发明的技术方案是：一种建筑涂层材料，其特征在于：各种物质及其重量百分比含量如下：光催化剂TiO2-xNx 1-3％，成膜物质聚丙烯酸脂乳液15～25％，聚丙烯酸铵盐0.8-2.0％，润湿剂0.2-0.5％，羟乙基纤维素0.1-0.2％，消泡剂0.6-0.8％，钛白粉7-9％，重质碳酸钙25-30％，高岭土8-10％，滑石粉4-5％，成膜助剂0.8-1.0％，丙二醇1.8-2.0％，增稠剂0.5-1.0％，溶剂水20-30％。
本发明具有以下优点：有效降解周围空气中的污染物质，对室内的甲醛苯酚等有机有害小分子进行降解。
具体实施方式
实施例：一种建筑涂层材料制备方法，先将分散剂聚丙烯酸铵盐10g、润湿剂2.5g、羟乙基纤维素1.5g、消泡剂4g加入于150ml的水中，用搅拌机以500rpm转速进行搅拌分散10分钟；将纳米光催化剂Tio2-xNx粉末10g慢慢加入，用搅拌机在1000rpm转速下分散15分钟；加入颜料钛白粉40g，重质碳酸钙120g，高岭土50g、滑石粉25g，用高速搅拌机在2000rpm转速下搅拌1小时；在装有研磨分散头和研磨介质钢化玻璃球的搅拌器中以2000rpm转速将上述预混合分散的浆料进行充分粉碎和充分混合分散，直至浆料颗粒U时，即可制得。
Claims (1)
1.一种建筑涂层材料制备方法，其特征在于：先将分散剂聚丙烯酸铵盐10g、润湿剂2.5g、羟乙基纤维素1.5g、消泡剂4g加入于150ml的水中，用搅拌机以500rpm转速进行搅拌分散10分钟；将纳米光催化剂Tio2-xNx粉末10g慢慢加入，用搅拌机在1000rpm转速下分散15分钟；加入颜料钛白粉40g，重质碳酸钙120g，高岭土50g、滑石粉25g，用高速搅拌机在2000rpm转速下搅拌1小时；在装有研磨分散头和研磨介质钢化玻璃球的搅拌器中以2000rpm转速将上述预混合分散的浆料进行充分粉碎和充分混合分散，直至浆料颗粒U时，即可制得。