CN101099963A - 一种玻璃植绒方法 - Google Patents

一种玻璃植绒方法 Download PDF

Info

Publication number
CN101099963A
CN101099963A CNA2007100252549A CN200710025254A CN101099963A CN 101099963 A CN101099963 A CN 101099963A CN A2007100252549 A CNA2007100252549 A CN A2007100252549A CN 200710025254 A CN200710025254 A CN 200710025254A CN 101099963 A CN101099963 A CN 101099963A
Authority
CN
China
Prior art keywords
glass
glue
flocking
printing ink
low
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CNA2007100252549A
Other languages
English (en)
Inventor
王兆进
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CNA2007100252549A priority Critical patent/CN101099963A/zh
Publication of CN101099963A publication Critical patent/CN101099963A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种玻璃植绒方法,它包括如下步骤:第一步:将玻璃清洗干净,在需植绒部位的玻璃表面涂覆或印刷低温烘烤型玻璃胶水或油墨;第二步:将涂有玻璃胶水或油墨的玻璃进行低温烘烤;第三步:玻璃胶水或油墨经烘烤固化后,在其表面涂覆与第一层玻璃胶水或油墨相亲和的低温烘烤植绒胶水,采用静电植绒法在玻璃表面植绒,经低温固化成型。它能大大缩短玻璃植绒的生产周期,植绒牢度能达到目前布类或皮革植绒的牢度,实现了玻璃植绒的批量生产,使植绒玻璃能在工业及室内外装饰领域得到广泛应用。

Description

一种玻璃植绒方法
技术领域
本发明涉及一种玻璃植绒方法。
背景技术
目前玻璃植绒一般采用单组份或双组份低温自黏合植绒胶水涂覆在玻璃表面,用静电植绒法进行植绒,它需要较长时间固化,长达十几小时甚至更长。在固化过程中,植绒后的表面不能有任何碰撞,如有灰尘或其它颜色的毛绒落入也无法避免,因固化时间长,也导致此工艺难以批量生产。另外低温自黏合植绒胶水对绒毛的粘接质量稍差,导致植绒绒毛竖感不强,牢度不够,针对此缺陷的改进方法是在植绒玻璃上先涂一层低温自黏合胶水,然后再进行植绒,这样确实会增加植绒胶水的对玻璃的附着度,但却更加延长了植绒的工作周期,增加了玻璃批量植绒难度。
市场上还有一些用烘烤型的胶水在玻璃表面植绒,但因其烘烤时间太长或烘烤温度过高,导致最后植绒的失败,即使植绒的外形很美观,但实际上颈毛的附着牢度及胶水对玻璃的附着牢度达不到要求,无法应用于装饰性领域。到目前为止,在装饰领域玻璃批量植绒法尚没有开发出来。
发明内容
本发明提供一种玻璃植绒方法,它能大大缩短玻璃植绒的生产周期,植绒牢度能达到目前布类或皮革植绒的牢度,实现了玻璃植绒的批量生产,使植绒玻璃能在工业及室内外装饰领域得到广泛应用。
本发明采用了如下技术方案:一种玻璃植绒方法,它包括如下步骤:
第一步:将玻璃清洗干净,在需植绒部位的玻璃表面涂覆或印刷低温烘烤型玻璃胶水或油墨;
第二步:将涂有玻璃胶水或油墨的玻璃进行低温烘烤;
第三步:玻璃胶水或油墨经烘烤固化后,在其表面涂覆与第一层玻璃胶水或油墨相亲和的低温烘烤植绒胶水,采用静电植绒法在玻璃表面植绒,经低温固化成型。
所述低温烘烤型玻璃胶水或油墨的固化温度在150℃-200℃之间,所述的低温烘烤植绒胶水的固化温度在80℃-130℃之间;所述低温烘烤是采用中波或短波红外线进行烘烤;所述低温烘烤型玻璃胶水或油墨为单组份或双组份胶水或油墨。
所述单组份低温烘烤型玻璃油墨的主要成份及配比如下:
水性丙烯酸树脂80份;偶联剂2份;消泡剂1份;
流平剂1份;颜料6份;填充料10份。
本发明的关键在于使用了低温烘烤型的玻璃胶水或油墨(150℃-200℃),能在短时间内烘干,并用更低温度的植绒胶水(80℃-130℃),也在短时间内烘烤固化,为玻璃植绒的批量生产及连续性生产提供了可行的方法。低温烘烤型玻璃胶水或油墨对玻璃的粘结牢度优良,而植绒胶水对低温烘烤型玻璃胶水或油墨的粘结牢度优良,使植绒胶水对玻璃的粘结牢度也达到优良,甚至比皮革植绒牢度更强,能耐酸碱及耐水(耐蒸煮)。
具体实施方式
将玻璃清洗干净,用单组份或双组份的低温烘烤型玻璃胶水或油墨涂覆在玻璃需要植绒的部位,所用玻璃胶水或油墨的固化温度在150℃-200℃之间。可选用江苏泰州新永泰印花科技有限公司的单组份8000W系列中的透明油墨涂覆,也可以用8000W的其它色墨进行印刷,增加基装饰性;也可以用法国杜比公司的双组份低温烘烤油墨,此两种油墨一种是单组份,一种是双组份,都可以应用,重要的是它们的烘烤温度均在150℃-200℃。烘烤时间,单组份油墨优于双组份,其烘烤时间更短。对涂有胶水或油墨的玻璃进行加热烘烤固化,用一般的加热方法要用20分钟左右,但为了在印刷或表面涂覆后马上进入植绒的生产线,采用中波或短波红外线的烘干方式,可以将烘干的时间大大缩短,单组份油墨只用100秒到130秒就可以固化,双组份油墨也只用170秒到210秒就可以完全固化,这样涂覆或印刷好的玻璃可以马上进入植绒的状态。
关于单组份低温烘烤型玻璃油墨的主要成份及配比如下:
水性丙烯酸树脂80份;偶联剂2份;消泡剂1份;
流平剂1份;颜料6份;填充料10份。
在玻璃胶水或油墨经烘烤固化后,在其表面涂覆与第一层玻璃胶水或油墨相亲和的低温烘烤植绒胶水,采用静电植绒法在玻璃表面植绒,经低温固化成型。植绒胶水的成份与玻璃胶水或油墨相似,只需要加强其固化剂的量,使其固化温度降至80℃-130℃。植绒胶水粘合在玻璃胶水或油墨,完全可在130℃内短时间固化,130℃可以适应植绒中的粘胶纤维、尼龙、晴纶、涤纶、棉等几乎所有成份的绒毛,使绒毛不受烘烤的影响而变形。
本发明适用于玻璃满幅植绒、玻璃印花图案植绒、玻璃套色植绒、纯白涤纶植绒再进行升华转印的玻璃植绒,玻璃印刷后植绒,采用阻燃绒毛的玻璃植绒等,可广泛应用于家电装饰面板、室内外装饰、家具行业的面板、工业品的外装饰、工艺品等。

Claims (5)

1、一种玻璃植绒方法,它包括如下步骤:
第一步:将玻璃清洗干净,在需植绒部位的玻璃表面涂覆或印刷低温烘烤型玻璃胶水或油墨;
第二步:将涂有玻璃胶水或油墨的玻璃进行低温烘烤;
第三步:玻璃胶水或油墨经烘烤固化后,在其表面涂覆与第一层玻璃胶水或油墨相亲和的低温烘烤植绒胶水,采用静电植绒法在玻璃表面植绒,经低温固化成型。
2、根据权利要求1所述的玻璃植绒方法,其特征在于所述低温烘烤型玻璃胶水或油墨的固化温度在150℃-200℃之间,所述的低温烘烤植绒胶水的固化温度在80℃-130℃之间。
3、根据权利要求1所述的玻璃植绒方法,其特征在于所述低温烘烤是采用中波或短波红外线进行烘烤。
4、根据权利要求1至3中任一项所述的玻璃植绒方法,其特征在于所述低温烘烤型玻璃胶水或油墨为单组份或双组份胶水或油墨。
5、根据权利要求4所述的玻璃植绒方法,其特征在于所述单组份低温烘烤型玻璃油墨的主要成份及配比如下:
水性丙烯酸树脂80份;偶联剂2份;消泡剂1份;
流平剂1份;颜料6份;填充料10份。
CNA2007100252549A 2007-07-19 2007-07-19 一种玻璃植绒方法 Pending CN101099963A (zh)