CN101086031A - 一种单环热处理的加工工艺 - Google Patents
一种单环热处理的加工工艺 Download PDFInfo
- Publication number
- CN101086031A CN101086031A CN 200610085960 CN200610085960A CN101086031A CN 101086031 A CN101086031 A CN 101086031A CN 200610085960 CN200610085960 CN 200610085960 CN 200610085960 A CN200610085960 A CN 200610085960A CN 101086031 A CN101086031 A CN 101086031A
- Authority
- CN
- China
- Prior art keywords
- minutes
- heat treatment
- controlled
- treatment process
- monocycle
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种单环的热处理加工工艺，是将单环设置在热处理加工炉中；先淬火，温度控制在890℃－900℃，升温时间小于110分钟，保温时间控制在100－140分钟；然后回火，温度控制在640℃－670℃，保温时间控制在150－180分钟；再炉冷，在炉内冷却3－5分钟，取出投入冷水中。本发明热处理工艺比较简单，可以保证其单环钢材组织结构完全相同，从而避免了整条锚链由于某个单环出现组织结构缺陷，而造成整条锚链报废的问题。
Description
技术领域：本发明涉及到一种船舶锚链的制造领域，特别是涉及到船舶锚链的一种单环热处理的加工工艺。
技术背景：在我国每年要生产大量的船用锚链，由于制造基础比较薄弱，在生产过程中，不可避免地会产生某个单环存在缺陷。在实际使用过程中，由于这些缺陷的单环存在，往往会造成整条锚链的报废。如果将整条锚链中有缺陷的单环换掉，可以有效地解决整条锚链报废的问题。但换掉的单环如何进行热处理，以达到与整条锚链的同样性能，一直是船舶制造行业中存在的问题。
发明内容：本发明的目的就是要提供一种单环热处理的加工工艺，它可以使单环钢材的组织结构和整条锚链钢材结构完全相同。本发明的目的是这样实现的。一种单环的热处理加工工艺，是将单环设置在热处理加工炉中；先淬火，温度控制在890℃-900℃，升温时间小于110分钟，保温时间控制在100-140分钟；然后回火，温度控制在640℃-670℃，保温时间控制在150-180分钟；再炉冷，在炉内冷却3-5分钟，取出投入冷水中。本发明热处理工艺比较简单，可以保证其单环钢材组织结构完全相同，从而避免了整条锚链由于某个单环出现组织结构缺陷，而造成整条锚链报废。
具体实施方式：本发明一种单环的热处理加工工艺，是将单环设置在热处理加工炉中；先淬火，温度控制在890℃-900℃，升温时间小于110分钟，保温时间控制在100-140分钟；然后回火，温度控制在640℃-670℃，保温时间控制在150-180分钟；再炉冷，在炉内冷却3-5分钟，取出投入冷水中。具体实施时，是将单环相邻的邻环做好隔热处理，一般邻环可采用铜管通入冷却水的方法进行強制性的冷却，然后在邻环铜管的外层采用耐火泥，以及硅酸纤维带包裹起来，以防止单环热处理时对邻环的影响。打开热处理的炉盖，将需热处理的单环放入炉中，由于加热炉的两侧为通孔结构，可以使相邻的邻环由通孔伸出炉处，避免热处理时对其影响。加热时，采用加热管进行加热。首先对单环进行淬火，温度可控制在895℃，升温时间控制在100分钟，保温时间为120分钟；然后回火，回火温度控制在655℃，保温时间为165分钟；停炉，使单环在炉内冷却4分钟后，取出投入到冷水槽中冷却。本发明采用的热处理工艺简单，比较容易控制，且对相邻的邻环组织结构不会造成任何影响，从根本上解决了由于单环出现的缺陷而造成整条锚链报废的问题，从而大大节约了原材料，降低了生产成本，提高了工效。
Claims (1)
1.一种单环的热处理加工工艺，是将单环设置在热处理加工炉中；先淬火，温度控制在890℃-900℃，升温时间小于110分钟，保温时间控制在100-140分钟；然后回火，温度控制在640℃-670℃，保温时间控制在150-180分钟；再炉冷，在炉内冷却3-5分钟，取出投入冷水中。