CN101082133A - 一种镀锌金属清洗剂 - Google Patents

一种镀锌金属清洗剂 Download PDF

Info

Publication number
CN101082133A
CN101082133A CN 200710025061 CN200710025061A CN101082133A CN 101082133 A CN101082133 A CN 101082133A CN 200710025061 CN200710025061 CN 200710025061 CN 200710025061 A CN200710025061 A CN 200710025061A CN 101082133 A CN101082133 A CN 101082133A
Authority
CN
China
Prior art keywords
water
weight ratio
clean
metal detergent
out system
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 200710025061
Other languages
English (en)
Other versions
CN100532650C (zh
Inventor
赵小宝
杨志慧
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wuhu Anhui Water Treatment Science & Technology Co Ltd
Original Assignee
Wuhu Anhui Water Treatment Science & Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuhu Anhui Water Treatment Science & Technology Co Ltd filed Critical Wuhu Anhui Water Treatment Science & Technology Co Ltd
Priority to CNB2007100250613A priority Critical patent/CN100532650C/zh
Publication of CN101082133A publication Critical patent/CN101082133A/zh
Application granted granted Critical
Publication of CN100532650C publication Critical patent/CN100532650C/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种镀锌金属清洗剂，包括有机络合剂、邻菲罗啉、水，有机络合剂、邻菲罗啉、水的重量比为3－10∶0.005－0.04∶100；本发明与现有技术相比，具有对金属镀锌层的腐蚀率小，除垢时间适中、主清洗剂可以回收利用的特点。

Description

一种镀锌金属清洗剂
技术领域：
本发明属于清洗剂这一技术领域，特别属于用于镀锌金属的清洗剂这一技术领域。
背景技术：
随着镀锌、镀锌铝合金金属使用范围扩大，以镀锌钢材为材料的设备也越来越普遍，所述的镀锌镀锌铝合金金属包括钢、铁，在上述设备的运行过程中，在金属镀层上容易产生硬垢和腐蚀性产物，影响设备的正常运行，使设备的能耗提高。常用的清洗剂为酸溶液如盐酸或者硫酸溶液，或者加了缓蚀剂的酸溶液，酸溶液在清洗过程中，对金属镀层的腐蚀率高，不能用于镀锌层较薄的电镀金属。
发明内容：
本发明所要解决的技术问题是提供一种对金属镀锌层腐蚀率小的清洗剂。
本发明解决技术问题的技术方案为：一种镀锌金属清洗剂，包括有机络合剂、邻菲罗啉、水，有机络合剂、邻菲罗啉、水的重量比为3-10∶0.005-0.04∶100；
优选的有机络合剂、邻菲罗啉、水的重量比为4-7∶0.01-0.03∶100；
所述的有机络合剂为EDTA-2Na，EDTA-2K；
为了增加清洗剂的缓蚀效果，还可在清洗剂中增加缓蚀剂，所述的缓蚀剂为：硫脲、乌洛托品、苯胺、邻二甲苯硫脲，其与水的重量比为0.2-2；
为了增加清洗的效果，还可在清洗剂中加入黄莲素，黄莲素与水的重量比为0.03-0.1∶100。
为了增加清洗的效果，还可在清洗剂中增加表面活性剂，所述的表面活性剂为十二烷基苯磺酸钠，平平加、吐温-80，表面活性剂与水的重量比为1∶0.005-0.05。
本发明中，有机络合剂为主清洗剂，起着溶垢的作用，邻菲罗啉作为锌的专属缓蚀剂，并能消除铁离子与金属锌的置换反应。
清洗后的清洗液，还可以通过PH值的调节，对有机络合剂进行回收利用。
本发明与现有技术相比，具有对金属镀锌层的腐蚀率小，除垢时间适中、主清洗剂可以回收利用的特点。
具体实施方式：
下面结合实施例对本发明做详细的说明。
实施例1：
将EDTA-2Na、邻菲罗啉加入水中，搅拌至完全溶解即可，EDTA-2Na、邻菲罗啉、水的重量比为3∶0.005∶100；
实施例2：
将EDTA-2K、邻菲罗啉加入水中，搅拌至完全溶解即可，EDTA-2Na、邻菲罗啉、水的重量比为4∶0.01∶100；
实施例3：
将EDTA-2Na、邻菲罗啉加入水中，搅拌至完全溶解即可，EDTA-2Na、水的重量比为7∶0.03∶100；
实施例4：
将EDTA-2K、邻菲罗啉加入水中，搅拌至完全溶解即可，EDTA-2Na、邻菲罗啉、水的重量比为10∶0.04∶100；
实施例5：
除在清洗剂中增加硫脲，硫脲与水的重量比为0.8∶100外，其余与实施例2相同。
实施例6：
除在清洗剂中增加苯胺，苯胺与水的重量比为0.2∶100外，其余与实施例3相同。
实施例7：
除在清洗剂中增加乌洛托品，乌洛托品与水的重量比为1.2∶100外，其余与实施例2相同。
实施例8：
除在清洗剂中增加邻二甲苯硫脲，邻二甲苯硫脲与水的重量比为2∶100外，其余与实施例3相同。
实施例9：除在清洗剂中增加黄莲素，黄莲素与水的重量比为0.03∶100外，其余与实施例5相同。
实施例10：除在清洗剂中增加黄莲素，黄莲素与水的重量比为0.05∶100外，其余与实施例6相同。
实施例11：除在清洗剂中增加黄莲素，黄莲素与水的重量比为0.1∶100外，其余与实施例7相同。
实施例12：
除在清洗剂中加入十二烷基苯磺酸钠，其与水的重量比为1∶0.005外，其余与实施例9相同。
实施例13：
除在清洗剂中加入平平加，其与水的重量比为1∶0.025外，其余与实施例10相同。
实施例14：
除在清洗剂中加入吐温-80外，其与水的重量比为1∶0.05外，其余与实施例11相同。
目前市场上清洗剂的主要含有重量浓度为盐酸3％，硫脲1％：黄连素0.05％，以此做为本发明的对照例。
本发明的腐蚀率按照《金属材料实验室均匀腐蚀全浸试验方法》GB10124-88的标准进行挂片失重试验，所用的试片金属材料为镀锌铁片，浸泡时间为3小时。
    镀锌层是否被破坏     腐蚀率(g/m2*h)
  实施例1     无     2.13
  实施例2     无     1.82
  实施例3     无     1.81
  实施例4     无     1.84
  实施例5     无     0.63
  实施例6     无     1.46
  实施例7     无     1.54
  实施例8     无     0.54
  实施例9     无     0.37
  实施例10     无     0.33
  实施例11     无     0.32
  实施例12     无     0.31
  实施例13     无     0.31
  实施例14     无     0.31
  对照例     镀锌层完全腐蚀     --

Claims (7)

1、一种镀锌金属清洗剂，其特征在于：包括有机络合剂、邻菲罗啉、水，有机络合剂、邻菲罗啉、水的重量比为3-10∶0.005-0.04∶100。
2、根据权利要求1所述的一种镀锌金属清洗剂，其特征在于：有机络合剂、邻菲罗啉、水的重量比为4-7∶0.01-0.03∶100。
3、根据权利要求1所述的一种镀锌金属清洗剂，其特征在于：所述的有机络合剂为EDTA-2Na，EDTA-2K。
4、根据权利要求1所述的一种镀锌金属清洗剂，其特征在于：在清洗剂中增加缓蚀剂，所述的缓蚀剂为：硫脲、乌洛托品、苯胺、邻二甲苯硫脲，其与水的重量比为0.2-2。
5、根据权利要求4所述的一种镀锌金属清洗剂，其特征在于：在清洗剂中加入黄莲素，黄莲素与水的重量比为0.03-0.1∶100。
6、根据权利要求5所述的一种镀锌金属清洗剂，其特征在于：在清洗剂中添加表面活性剂，所述的表面活性剂为十二烷基苯磺酸钠，平平加、吐温-80，表面活性剂与水的重量比为1∶0.005-0.05。
7、根据权利要求1所述的一种镀锌金属清洗剂，其特征在于：清洗后的清洗液，还可以通过PH值的调节，对有机络合剂进行回收利用。
CNB2007100250613A 2007-06-30 2007-06-30 一种镀锌金属清洗剂 Expired - Fee Related CN100532650C (zh)