CN101054450A - 利用对苯二甲酸残渣生产塑料热稳定剂的方法 - Google Patents
利用对苯二甲酸残渣生产塑料热稳定剂的方法 Download PDFInfo
- Publication number
- CN101054450A CN101054450A CNA2006100854322A CN200610085432A CN101054450A CN 101054450 A CN101054450 A CN 101054450A CN A2006100854322 A CNA2006100854322 A CN A2006100854322A CN 200610085432 A CN200610085432 A CN 200610085432A CN 101054450 A CN101054450 A CN 101054450A
- Authority
- CN
- China
- Prior art keywords
- heat stabilizer
- plastic heat
- terephthalic acid
- rare earth
- reactor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种利用对苯二甲酸粗制品残渣生产塑料热稳定剂的方法,该方法是:在第一反应釜中加入液碱,加热升温至45-70℃,搅拌加入对苯二甲酸粗制品残渣至溶解;调节反应釜中的pH值为5.5~8.3;将上述反应生成液从第一反应釜经过滤过入第二反应釜中加热至45-70℃;将稀土溶入溶解稀土的溶剂中,搅拌加入第二反应釜中,保温0.1-5小时;将第二反应釜中的反应生成液过滤,过滤后溶剂返回第一反应釜,将生产物干燥、粉碎,即制成塑料热稳定剂成品。该方法采用稀土代替铅、钡、镉、锌等重金属盐,将对苯二甲酸残渣废料作为原料生产出的塑料热稳定剂,有效解决石化厂废渣出路,实现循环经济,变废为宝,无害无污染,降低生产成本10%以上。
Description
所属技术领域
本发明涉及的是一种利用对苯二甲酸粗制品残渣生产塑料热稳定剂的方法。
背景技术
目前,由于对苯二甲酸具有优异的特性,被大量地使用在纤维、薄膜、树脂等领域,其废品随着其产量和用量的增加而增加,石化厂所产生的对苯二甲酸残渣也在增加,通常该残渣作为废品处理,它不能被微生物降解和自然分解,只能将其作为工业废渣进行焚烧、填埋,不仅处理费用高,而且会造成对空气、水源和土壤的污染,严重影响环境。
发明内容
本发明的目的,在于解决现有技术存在的上述问题,提供一种利用对苯二甲酸残渣生产塑料热稳定剂的方法,使废弃物得到充分利用,又不污染环境。
为了实现上述目的,本发明采用了以下技术方案,一种利用对苯二甲酸残渣生产塑料热稳定剂的方法,该方法按下列步骤进行:
(A)在一反应釜中加入液碱,加热升温至45°-70℃;在搅拌下连续加入对苯二甲酸残渣至溶解;
(B)连续多次小批量加入对苯二甲酸残渣,调节反应釜中的PH值至5.5-8.3;
(C)将上述反应生成液从第一反应釜经过过滤抽入第二反应釜中加热至45°-70℃;
(D)将稀土或稀土化合物溶入溶解稀土的溶剂中,加入上述的第二反应釜中剧烈搅拌,保温0.1-5小时;
(E)将第二反应釜中的反应生成液过滤,过滤后溶剂泵回反应釜,将生产物干燥、粉碎即成塑料热稳定剂成品。
上述所述的溶解稀土的溶剂为甲醇、乙醇或者水。
本发明与现有技术相比具有如下优点:上述利用对苯二甲酸残渣生产塑料热稳定剂的方法采用稀土代替铅、钡、镉、锌等重金属盐,利用对苯二甲酸残渣作为原料生产出的塑料热稳定剂,有效解决石化厂废渣出路,实现循环经济,变废为宝,无害无污染,降低生产成本10%以上,效果显著。
具体实体方式
下面以实施例对本发明作进一步描述。
实施例1、上述利用对苯二甲酸残渣生产塑料热稳定剂的方法,按下列步骤进行:
(A)在一反应釜中加入200-800公斤液碱加热升温至45-50℃;)在搅拌下连续加入对苯二甲酸残渣150-700公斤,至溶解;
(B)小批量多次加入对苯二甲酸残渣,调节反应釜中PH值至5.7;
(C)将反应生成液过滤入第二反应釜中加热至65-70℃;
(D)将稀土150-700公斤溶入溶解稀土的溶剂,溶剂为300-700公斤,搅拌加入到上述的第二反应釜中,保温0.1-5小时;
(E)将第二反应釜中的反应生成液过滤,过滤后溶剂泵回反应釜,将生成物干燥、粉碎即成良好的塑料热稳定剂成品。
实施例2、该实施例的步骤与实施例1相同,只是步骤A-D中,原料液碱为700公斤,对苯二甲酸残渣450公斤、稀土250公斤,产出的塑料热稳定剂效果良好。
实施例3、该实施例的步骤与实施例1相同,只是步骤A-D中,原料液碱750公斤,对苯二甲酸残渣600公斤、稀土为420公斤,产出的塑料热稳定剂效果更好。
Claims (5)
1、一种利用对苯二甲酸残渣生产塑料热稳定剂的方法,其特征在于上述方法包括以下步骤:
A、在一反应釜中,加入液碱,加热升温至45-70℃,搅拌加入对苯二甲酸粗制品残渣至溶解;
B、连续多次小批量加入对苯二甲酸残渣,调节反应釜中的PH值为5.5~8.3;
C、将上述反应生成液从第一反应釜经过滤泵入第二反应釜中加热至45-70℃;
D、将稀土或稀土化合物溶入溶解稀土的溶剂中,搅拌加入上述的第二反应釜中,保温0.1-5小时;
E、将第二反应釜中的反应生成液过滤,过滤后溶剂泵回第一反应釜,将生产物干燥、粉碎,即制成塑料热稳定剂成品。
2、根据权利要求1所述的利用对苯二甲酸粗制品残渣生成塑料热稳定剂的方法,其特征在于:上述的溶解稀土的溶剂为甲醇、或乙醇,或者水。
3、根据权利要求1或2所述的利用对苯二甲酸粗制品残渣生产塑料热稳定剂的方法,其特征在于:上述液碱为200-800公斤,对苯二甲酸残渣为150-750公斤,稀土为200-500公斤。
4、根据权利要求1或2所述的利用对苯二甲酸粗制品残渣生成塑料热稳定剂的方法,其特征在于:上述液碱为700公斤,对苯二甲酸残渣为450公斤,稀土为250公斤。
5、根据权利要求1或2所述的利用对苯二甲酸粗制品残渣生成塑料热稳定剂的方法,其特征在于:上述液碱为750公斤,对苯二甲酸残渣为600公斤,稀土为420公斤。