CN101029215A - 储能聚氨酯微胶囊的制备方法 - Google Patents

储能聚氨酯微胶囊的制备方法 Download PDF

Info

Publication number
CN101029215A
CN101029215A CN 200710020102 CN200710020102A CN101029215A CN 101029215 A CN101029215 A CN 101029215A CN 200710020102 CN200710020102 CN 200710020102 CN 200710020102 A CN200710020102 A CN 200710020102A CN 101029215 A CN101029215 A CN 101029215A
Authority
CN
China
Prior art keywords
weight part
proportion
energy
deionized water
preparation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 200710020102
Other languages
English (en)
Other versions
CN101029215B (zh
Inventor
华明扬
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangyin city's biological new Mstar Technology Ltd
Original Assignee
华明扬
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 华明扬 filed Critical 华明扬
Priority to CN200710020102XA priority Critical patent/CN101029215B/zh
Publication of CN101029215A publication Critical patent/CN101029215A/zh
Application granted granted Critical
Publication of CN101029215B publication Critical patent/CN101029215B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种储能聚氨酯微胶囊的制备方法，其特征在于它是由碳原子数14至22的正构烷烃和包裹在外的聚氨酯构成，粒径在10－20μm，所述聚氨酯微胶囊的制备材料的油相是由多异氰酸酯5－6重量份、碳原子数14至22的正构烷烃20－25重量份和环己烷20－30重量份组成；水相是由氢氧化钠0.3－0.5重量份、海藻酸钠0.3－0.5重量份和去离子水200重量份组成；制备工艺为在上述油相中加入乙二醇3－5重量份和去离子水适量，混合后滴加入水相中，1.5－2小时滴完，搅拌速度在400－600转/分，温度保持在40－60℃，滴完后，升温至50－70℃，反应1－1.5小时，将得到的产品抽滤，洗涤，80℃以下烘干，得微米级粉末。该法制备的微胶囊粒径在10－20μm，储能足、包覆规则，是一类很好的相变微胶囊。

Description

储能聚氨酯微胶囊的制备方法
技术领域：
本发明涉及一种储能材料的制备方法，尤其是涉及一种储能聚氨酯微胶囊的制备方法。属有机化学技术领域。
背景技术
储能材料是一类新型能源环保材料，它能把能量暂时储存起来，在适当的温度下又释放出来。在本发明作出以前，以往的储能材料大多采用以石蜡为核等的材料。它们都存在着一些不足，如：储能力不足、包覆不规则、石蜡容易泄漏等。
发明内容
本发明的目的在于克服上述不足，提供一种储能足、包覆规则的储能聚氨酯微胶囊的制备方法。
本发明的目的是这样实现的：一种储能聚氨酯微胶囊的制备方法，它是由碳原子数14至22的正构烷烃和包裹在外的聚氨酯构成，粒径在10-20um，所述聚氨酯微胶囊的制备材料的油相是由多异氰酸酯5-6重量份、碳原子数14至22的正构烷烃20-25重量份和环己烷20-30重量份组成；水相是由氢氧化钠0.3-0.5重量份、海藻酸钠0.3-0.5重量份和去离子水200重量份组成；制备工艺为在上述油相中加入乙二醇3-5重量份和去离子水适量，混合后滴加入水相中，1.5-2小时滴完，搅拌速度在400-600转/分，温度保持在40-60℃，滴完后，升温至50-70℃，反应1-1.5小时，将得到的产品抽滤，洗涤，80℃以下烘干，得微米级粉末。
上述多异氰酸酯可以为异氟尔酮二异氰酸酯、甲苯二异氰酸酯或二苯甲烷二异氰酸酯。
本发明采用一种新型的囊材对正构烷烃(碳原子数14至22)进行包覆，得到一种微胶囊材料，利用正构烷烃(碳原子数14至22)的相变热性能，将能量储存并释放出。它具有储能力强、包覆层规则、体系稳定等特点。
具体实施方式
实施例1：
一、微胶囊制备材料
油相：异氟尔酮二异氰酸酯(IPDI)5.55g，正构16烷烃24g，环己烷30g；
水相：15％NaOH 2g，海藻酸钠0.3g，去粒子水200g；
乙二醇：3.0g。
二、制备工艺
1、按上述配比，用200g去离子水在高速搅拌下，溶解海藻酸钠。
2、将油相、乙二醇与40g去离子水混合，在40℃，搅拌速度500转/分条件下，滴加到水相中，2小时滴完。
3、升温至50℃，继续反应1.5小时。
4、对粗产物进行抽滤，洗涤。
5、80℃以下烘干，产物为微米级粉末，其粒径在10-20um。
实施例2：
一、微胶囊制备材料
油相：二苯甲烷二异氰酸酯(HDI)6.0g，正构16烷烃24g，环己烷30g：水相：15％NaOH 2g，海藻酸钠0.3g，去粒子水200g；
乙二醇：3.0g。
二、制备工艺
1、按上述配比，用200g去离子水在高速搅拌下，溶解海藻酸钠。
2、将油相，乙二醇与40g去离子水混合，在50℃，搅拌速度500转/分条件下，滴加到水相中，2小时滴完。
3、升温至60℃，继续反应1小时。
4、对粗产物进行抽滤，洗涤。
5、80℃以下烘干，产物为微米级粉末，其粒径在10-20um。
实施例3：
一、微胶囊制备材料
油相：甲苯二异氰酸酯(TDI)5.50g，正构15烷烃25g，环己烷：30g；
水相：15％NaOH 2g，海藻酸钠0.3g，去粒子水200g；
乙二醇：3.0g。
二、制备工艺
1、按上述配比，用200g去离子水在高速搅拌下，溶解海藻酸钠。
2、将油相，乙二醇与40g去离子水混合，在40℃，搅拌速度500转/分条件下，滴加到水相中，2小时滴完。
3、升温至50℃，继续反应1.2小时。
4、对粗产物进行抽滤，洗涤。
5、80℃以下烘干，产物为微米级粉末，其粒径在10-20um。

Claims (2)

1、一种储能聚氨酯微胶囊的制备方法，其特征在于它是由碳原子数14至22的正构烷烃和包裹在外的聚氨酯构成，粒径在10-20um，所述聚氨酯微胶囊的制备材料的油相是由多异氰酸酯5-6重量份、碳原子数14至22的正构烷烃20-25重量份和环己烷20-30重量份组成；水相是由氢氧化钠0.3-0.5重量份、海藻酸钠0.3-0.5重量份和去离子水200重量份组成；制备工艺为在上述油相中加入乙二醇3-5重量份和去离子水适量，混合后滴加入水相中，1.5-2小时滴完，搅拌速度在400-600转/分，温度保持在40-60℃，滴完后，升温至50-70℃，反应1-1.5小时，将得到的产品抽滤，洗涤，80℃以下烘干，得微米级粉末。
2、根据权利要求1所述的一种储能聚氨酯微胶囊的制备方法，其特征在于所述多异氰酸酯为异氟尔酮二异氰酸酯、甲苯二异氰酸酯或二苯甲烷二异氰酸酯。
CN200710020102XA 2007-02-07 2007-02-07 储能聚氨酯微胶囊的制备方法 Expired - Fee Related CN101029215B (zh)