CN101028725A - Ceramic tile and its machining method - Google Patents
Ceramic tile and its machining method Download PDFInfo
- Publication number
- CN101028725A CN101028725A CN 200710073420 CN200710073420A CN101028725A CN 101028725 A CN101028725 A CN 101028725A CN 200710073420 CN200710073420 CN 200710073420 CN 200710073420 A CN200710073420 A CN 200710073420A CN 101028725 A CN101028725 A CN 101028725A
- Authority
- CN
- China
- Prior art keywords
- ceramic tile
- green compact
- base
- tool marks
- carved
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A ceramic tile with multiple color layers and layered pattern is prepared through preparing raw tile from at least two clay layers with different colors, drying, carving on its surface to form a pre-designed pattern, surface treatment and sintering.
Description
Technical field
The present invention relates to ceramic tile, and the processing method of ceramic tile, relate in particular to and adopt method and the product of etching technics at ceramic tile surface processing art pattern.
Background technology
In the prior art, have three-dimensional pattern effect, can produce epirelief or recessed pattern, but the expense of a secondary mould is very high, if the large-scale picture that is spliced just needs many moulds with the method for mold pressing in order to make ceramic tile surface.And mould pattern if make several different works, then needs the polylith mould in case formation just can not be changed.The long-term storage mould not only takes up room, and also can cause waste.The main method that is to use mold pressing is difficult to produce the indentation of manual graduating with cutter effect, can't solve the problem of ceramic tile artistic effect difference.
Summary of the invention
The objective of the invention is in order to solve the problem of existing ceramic tile artistic effect difference, and propose good ceramic tile and the processing method of the strong and whole decorative artistic effect of a kind of third dimension.Even if ceramic tile of the present invention not glaze, the green compact of ceramic tile of multilayered color-forming sintering after etching presents the clearly demarcated pattern of each layer light and shade, and specific artistic expression is arranged, if glaze, then more can highlight the artistic effect of ceramic tile.
The present invention realizes by adopting following technical scheme:
Implement a kind of first kind of processing method of ceramic tile, comprise the steps:
1. at first layering is made of the base soil of two kinds of different colours be combined into the green compact of ceramic tile of monoblock at least, and makes described green compact of ceramic tile that smooth green compact upper surface be arranged.
2. make the green compact of ceramic tile drying then; And green compact of ceramic tile is placed the processing stations of ceramic tile engraving.
3. then with the green compact upper surface processing recessed tool marks of lithography tool, make more than one tool marks form predetermined pattern at green compact of ceramic tile.
4. again the base that is carved into after the etching is carried out surface treatment, the formation surface has been handled and has been carved into base.
5. then the surface has been handled and be carved into base and go into the stove sintering.
In the said method: one of tool marks mode that the 3. described processing of step is recessed comprises:
A. sketch the contours of the etching profile of tool marks at the green compact upper surface.
B. carry out etching with hand-held lithography tool along the etching profile.
In the said method: two of the tool marks mode that the 3. described processing of step is recessed comprises:
Carry out etching at random with hand-held lithography tool at the green compact upper surface.
In the said method: three of the tool marks mode that the 3. described processing of step is recessed comprises:
A. the intelligent control center of ceramic tile intelligent carving machine has read the pattern data of wanting etching from storage medium at this moment, this pattern data is driven module and progressively calls and form and drive instruction, and will drive to instruct by output interface and be transferred to Vidacare corp successively.
B. next Vidacare corp drives the green compact upper surface processing recessed tool marks of lithography tool at green compact of ceramic tile, makes more than one tool marks form predetermined pattern.
In the said method: described surface treatment comprise to be carved into base cleaning, surface at least a in the layer operation; It is to adhere to glaze or base earth material at the green compact upper surface that described surface layer; Technology comprises brush, at least a in being coated with, printing, gluing, drenching, soaking, pressing, rubbing.
By a kind of ceramic tile of said method manufacturing, described ceramic tile comprises:
The brick body, described brick body is by the base soil material layering be combined into of at least two kinds of different colours.
Surface element, the recessed tool marks that the useful lithography tool of described surface element carves.
Further, on described surface element, the tool marks of carving are arranged after and the surface adhered to layer.
The present invention also has the processing method of second kind of ceramic tile, and one of embodiment of described second method comprises the steps:
1. at first make the monoblock green compact of ceramic tile, and make described green compact of ceramic tile that smooth green compact upper surface be arranged with base soil.
2. make the green compact of ceramic tile drying then; And green compact of ceramic tile is placed the processing stations of ceramic tile engraving.
3. this moment the ceramic tile intelligent carving machine intelligent control center from storage medium, read the pattern data of wanting etching, this pattern data is driven module and progressively calls, and will drive to instruct by output interface and be transferred to Vidacare corp successively.
4. next Vidacare corp drives the green compact upper surface processing recessed tool marks of lithography tool head at green compact of ceramic tile, makes more than one tool marks form predetermined pattern.
5. the base that is carved into after the etching is carried out surface treatment, the formation surface has been handled and has been carved into base.
6. then the surface has been handled and be carved into base and go into the stove sintering.
Two of the embodiment of described second method comprises the steps:
1. at first make the monoblock green compact of ceramic tile, and make described green compact of ceramic tile that smooth green compact upper surface be arranged with base soil.
2. make the green compact of ceramic tile drying then; And green compact of ceramic tile is placed the processing stations of ceramic tile engraving.
3. next with the green compact upper surface processing recessed tool marks of hand-held lithography tool, make more than one tool marks form predetermined pattern at green compact of ceramic tile.
4. the base that is carved into after the etching is carried out surface treatment, the formation surface has been handled and has been carved into base.
5. then the surface has been handled and be carved into base and go into the stove sintering.
In one of embodiment of above-mentioned second method or two: described surface treatment comprise to be carved into base cleaning, surface at least a in the layer operation; It is to adhere to glaze or base earth material at the green compact upper surface that described surface layer; Technology comprises brush, at least a in being coated with, printing, gluing, drenching, soaking, pressing, rubbing.
Make a kind of ceramic tile by above-mentioned second method, described ceramic tile comprises:
The brick body, described brick body is made of the base soil material.
Surface element, the recessed tool marks that the useful lithography tool of described surface element carves.
Further, on described surface element, the tool marks of carving are arranged after and the surface adhered to layer.
The invention has the advantages that, the brick body that the useful base earth material of described ceramic tile material constitutes, described brick body layering is made of the base soil material of two kinds of different colours be combined into monoblock at least, green compact upper surface from the brick body carves predetermined pattern downwards with lithography tool then, described predetermined pattern can manifest each layer blank, is presented the artistic effect of predetermined pattern by the different colours of blank.Further, after predetermined pattern is carved into, can be on the top layer blank again glaze, again glaze the time, can grasp and appear what of top layer blank, after the green sintering, to embody different artistic effects.
Description of drawings
Fig. 1 is the schematic diagram that the base soil of at least two kinds of different colours in a kind of ceramic tile of the present invention and the processing method is made the green compact of ceramic tile that is combined into monoblock;
Fig. 2 A is in a kind of ceramic tile of the present invention and the processing method, and the base of two kinds of different colours soil is made and is combined into before the monoblock, and each layer blank prepared the schematic diagram of a kind of embodiment of combination;
Fig. 2 B is in a kind of ceramic tile of the present invention and the processing method, and the base of three kinds of different colours soil is made and is combined into before the monoblock, and each layer blank prepared the schematic diagram of a kind of embodiment of combination;
Fig. 3 is an etching profile of sketching the contours of tool marks in a kind of ceramic tile of the present invention and the processing method at the green compact upper surface, prepares with the schematic diagram of hand-held lithography tool in the green compact upper surface processing of green compact of ceramic tile;
Fig. 4 is a brick body of only making monoblock in a kind of ceramic tile of the present invention and the processing method of a kind of base soil material of color, and the surface carves the schematic diagram of predetermined pattern downwards with lithography tool thereon;
Fig. 5 is that the base soil of at least two kinds of different colours in a kind of ceramic tile of the present invention and the processing method is made the green compact of ceramic tile that is combined into monoblock, and the predetermined pattern that is carved can manifest each layer blank, presented the schematic diagram of the artistic effect of predetermined pattern by the different colours of blank;
Fig. 6 is a brick body of only making monoblock in a kind of ceramic tile of the present invention and the processing method of a kind of base soil material of color, after the surface carves predetermined pattern downwards with lithography tool thereon, again thereon on the surface again the schematic diagram of glaze;
Fig. 7 is that the base soil of at least two kinds of different colours in a kind of ceramic tile of the present invention and the processing method is made the green compact of ceramic tile that is combined into monoblock, and the predetermined pattern that is carved can manifest each layer blank, then on the top layer blank again the schematic diagram of glaze;
Fig. 8 is the schematic diagram that the lithography tool of use hand electric in a kind of ceramic tile of the present invention and the processing method is processed;
Fig. 9 is the schematic diagram that uses hand-held common lithography tool to process in a kind of ceramic tile of the present invention and the processing method;
Figure 10 is the schematic diagram that the lithography tool of intelligent carving machine system control processes that uses a computer in a kind of ceramic tile of the present invention and the processing method;
Figure 11 is the principle schematic when lithography tool is controlled by computer intelligence engraving machine system in a kind of ceramic tile of the present invention and the processing method.
The specific embodiment
Below in conjunction with accompanying drawing the present invention is done further detailed description:
Implement a kind of processing method of ceramic tile, comprise the steps:
1. at first shown in Fig. 1, Fig. 2 A, layering is made of the base soil of two kinds of different colours be combined into the green compact of ceramic tile 10 of monoblock at least, and makes described green compact of ceramic tile 10 that smooth green compact upper surface 13 be arranged.
2. make green compact of ceramic tile 10 dryings then; And green compact of ceramic tile 10 is placed the processing stations of ceramic tile engraving.
3. then as Fig. 8～shown in Figure 10,, make more than one tool marks 40 form predetermined pattern with the recessed tool marks 40 of green compact upper surface 13 processing of lithography tool 130 at green compact of ceramic tile 10.
4. Fig. 6, shown in Figure 7 for another example carries out surface treatment to the base 20 that is carved into after the etching, forms the surface and has handled and be carved into base 30.
5. then the surface has been handled and be carved into base 30 and go into the stove sintering.
In the said method: one of tool marks 40 modes that the 3. described processing of step is recessed as shown in Figure 3, comprising:
A. sketch the contours of the etching profile 19 of tool marks at green compact upper surface 13.
B. with hand-held lithography tool such as Fig. 8, shown in Figure 9, carry out etching along etching profile 19.
In the said method: two of the tool marks mode that the 3. described processing of step is recessed as Fig. 8, shown in Figure 9, comprising:
Carry out etching at random with hand-held lithography tool 130 at green compact upper surface 13.
In the said method: three of the tool marks mode that the 3. described processing of step is recessed as Figure 10, shown in Figure 11, comprising:
A. the intelligent control center 100 of ceramic tile intelligent carving machine has read the pattern data of wanting etching from storage medium 109 at this moment, this pattern data is driven module and progressively calls and form and drive instruction, and will drive to instruct by output interface 105 and be transferred to Vidacare corp 108 successively.
B. next Vidacare corp 108 drives the green compact upper surface 13 processing recessed tool marks 40 of lithography tool at green compact of ceramic tile 10, makes more than one tool marks 40 form predetermined pattern.
Among Figure 11, intelligent control center 100 connects with peripheral hardware 123 by communication interface 106.The storage medium 109 of pattern data comprises laser disc, hard disk, USB flash disk, storage card, internal memory, FLARSH dish or network data base.Vidacare corp 108 can drive directions X driver element 201, Y direction driver element 202, Z direction driver element 203, rotation driver element 204 and cutter head driver element 205.
Monitor the sensor groups 150 of ceramic tile intelligent carving machine work, be connected with intelligent control center 100 by input interface 107.
Green compact of ceramic tile 10 shown in Figure 10 only is the base earth material of single color individual layer, can also be that layering is made the green compact of ceramic tile 10 that is combined into monoblock with the base earth material of at least two kinds of different colours certainly.For ceramic tile intelligent carving machine or hand engraving, green compact of ceramic tile 10 process that individual layer, multilayer base earth material are constituted are the same substantially, consider just which layer the pattern that finally reveals arrives and get final product.
Shown in Fig. 2 A only is the combination of two-layer base earth material, and certain method of the present invention and product are not limit dried two-layer.In Fig. 2 A, a kind of implementation method of two-layer base earth material combination is: bottom base 12 has bottom base faying face 121, top layer base 11 has top layer base faying face 111, then by humidification or impose adhesive, the viscosity of two junction is strengthened, again with two-layer base earth material in conjunction with and exert pressure, the action that rubs is perhaps arranged when exerting pressure, make both in conjunction with closely.
Another method is that bottom base 12 is placed a container, and the paste top layer blank with dilution is put on the bottom base 12 then, and scrapes a smooth green compact upper surface 13 with scraper, treats just to form top layer base 11 after the paste top layer blank drying.
Another method is or executes water on the bottom base faying face 121 of bottom base 12, makes its surface be cream mud shape, or bottom base 12 is also when cream mud shape; Scrape a smooth upper surface with scraper, evenly execute thereon with the top layer blank of powdery again, lean on the moisture of bottom base 12 to make top layer blank formation cream mud shape, move, flatten, just form the green compact of ceramic tile 10 that top layer base 11 and bottom base 12 synthesize after the drying through gentle.
The method that can form the top layer base 11 of different colours and the green compact of ceramic tile 10 that bottom base 12 synthesizes is a lot, does not exemplify one by one at this.
The base 20 that is carved into shown in Figure 5 is two-layer embodiment, and its tool marks 40 comprise top layer tool marks 41 and bottom tool marks 42 that top layer base 11 and bottom base 12 manifest respectively.
When making multilayer, as Fig. 2 B, shown in Figure 3, top layer base 11, intermediate layer base 14 and bottom base 12 have synthesized ceramic tile brick body 10, and in like manner, intermediate layer base 14 can be a multilayer, and preparation method is identical when two-layer with making.Thickness to each layer is unqualified.
When making multilayer, technical process can be complicated.
When making multilayer, described tool marks 40 are divided into top layer tool marks, bottom tool marks and intermediate layer tool marks, and described tool marks comprise a kind of in top layer tool marks, bottom tool marks and the intermediate layer tool marks at least, or nested.
Described top layer tool marks are meant the tool marks that are engraved on the top layer, and described bottom tool marks are meant and are engraved in tool marks on the bottom that described intermediate layer tool marks are meant the tool marks that are engraved on the intermediate layer.
Each layer that the bottom tool marks must be carved on the layer of revealing the exact details could arrive this layer.
Each layer that the intermediate layer tool marks must be carved on this layer could arrive this layer.
In the said method: described surface treatment comprise to be carved into base 20 cleaning, surface at least a in the layer operation.
Described is the base bits that comprise after the clean-up etch to being carved into base 20 cleaning, and this moment as do not need further operation, the base 20 that is carved into after the cleaning just becomes the surface and handled and be carved into base 30, can carry out sintering.
If after the base after the clean-up etch bits, also need further the surface layer, as Fig. 6, shown in Figure 7, it is to adhere to glaze or base earth material at green compact upper surface 13 that described surface layer 15; Technology comprises brush, at least a in being coated with, printing, gluing, drenching, soaking, pressing, spraying, rubbing, forms the surface and handled and be carved into base 30, after the drying, can go into the klining knot.
Described brush comprises that the base earth material that dips in glaze or dilution with brush brushes skim on green compact upper surface 13.
Described seal comprises that the base earth material that dips in glaze or dilution with the seal roller stamps skim on green compact upper surface 13.
The described sticking base earth material for preparing skim glaze or dilution on the plane that is included in, green compact upper surface 13 dips in to going down then.
Described being coated with comprises with the base earth material of pressure with glaze or dilution and being sprayed on the green compact upper surface 13, forms skim.
By a kind of ceramic tile of said method manufacturing, as Fig. 1, Fig. 2 A, Fig. 5, Fig. 6, shown in Figure 8, described ceramic tile comprises:
The brick body, described brick body is by the base soil material layering be combined into of at least two kinds of different colours.
Surface element, the recessed tool marks 40 that the useful lithography tool 130 of described surface element carves.
Further, on described surface element, there is the surface of adhering to after tool marks of carving 40 layer 15.
Shown in Fig. 2 A only is the brick body of top layer base 11 and bottom base 12 two-layer base soil material be combined intos, is not limited only to two-layer in actual certainly the manufacturing.
The present invention also has the processing method of second kind of ceramic tile, and as shown in figure 10, one of embodiment of described second method comprises the steps:
1. at first make monoblock green compact of ceramic tile 10 with base soil, the green compact of ceramic tile 10 of this moment is only made with a kind of base soil material of color, and makes described green compact of ceramic tile 10 that smooth green compact upper surface 13 be arranged.
2. make green compact of ceramic tile 10 dryings then; And green compact of ceramic tile 10 is placed the processing stations of ceramic tile engraving.
3. as shown in figure 11, this moment, the intelligent control center 100 of ceramic tile intelligent carving machine 109 read the pattern data of wanting etching from storage medium, this pattern data is driven module and progressively calls, and will drive instruction by output interface 105 and be transferred to Vidacare corp 108 successively.
4. next Vidacare corp 108 drives the green compact upper surface 13 processing recessed tool marks 40 of etching cutter head at green compact of ceramic tile 10, makes more than one tool marks 40 form predetermined pattern.
5. the base 20 that is carved into after the etching is carried out surface treatment, the formation surface has been handled and has been carved into base 30.
6. then the surface has been handled and be carved into base 30 and go into the stove sintering.
Two of the embodiment of described second method as Fig. 8, shown in Figure 9, comprises the steps:
1. at first make monoblock green compact of ceramic tile 10 with base soil, the green compact of ceramic tile 10 of this moment is only made with a kind of base soil material of color, and makes described green compact of ceramic tile 10 that smooth green compact upper surface 13 be arranged.
2. make green compact of ceramic tile 10 dryings then; And green compact of ceramic tile 10 is placed the processing stations of ceramic tile engraving.
3. next with the green compact upper surface 13 processing recessed tool marks 40 of hand-held lithography tool 130, make more than one tool marks 40 form predetermined pattern at green compact of ceramic tile 10.
4. the base 20 that is carved into after the etching is carried out surface treatment, the formation surface has been handled and has been carved into base 30.
5. then the surface has been handled and be carved into base 30 and go into the stove sintering.
In one of embodiment of above-mentioned second method or two: described surface treatment is the same with first method, comprise to be carved into base cleaning, surface at least a in the layer operation; As Fig. 6, shown in Figure 7, it is to adhere to glaze or base earth material at the green compact upper surface that described surface layer 15; Technology comprises brush, at least a in being coated with, printing, gluing, drenching, soaking, pressing, rubbing.
Make a kind of ceramic tile by above-mentioned second method, described ceramic tile comprises:
The brick body, described brick body is made of the base soil material.
Surface element, the recessed tool marks 40 that the useful lithography tool 130 of described surface element carves.
If needed, further, on described surface element, the tool marks of carving are arranged after and the surface adhered to layers 15.
Ceramic tile of the present invention, the area of monolithic ceramic tile size is not concrete to be limited, and when being spliced into significantly picture, each size of forming ceramic tile should be identical, certainly when special circumstances are arranged, exception can be arranged.
Ceramic tile processing method of the present invention, illustrated embodiments are to adopt the ceramic tile intelligent carving machine to process.Like this, monolithic ceramic tile artistic work no matter, the still large-scale pattern that is combined into by the polylith ceramic tile, the data of the ceramic tile of each position all are stored in the storage medium, can call at any time.A storehouse needn't be set specially stack mould.Every block of ceramic tile can be subjected to computer program control to carry out the identical etching of process, and therefore the product of a batch is when the industrialization volume production, and pattern, quality all are identical.
Even if a certain damage in the works of user's large-scale splicing as long as know the ceramic tile label, just can carve the identical ceramic tile of pattern and fill.
Certainly, instrumentation also can process the satisfied ceramic tile of effect by hand, but production efficiency can be hanged down.The simultaneously manual ceramic tile that carves more difficultly carves an identical ceramic tile when damaging, the works of especially large-scale splicing are all the more so.
Facts have proved, ceramic tile by method processing of the present invention, the base soil of at least two kinds of different colours is made and is combined into after the green compact of ceramic tile of monoblock, processes recessed tool marks with lithography tool on the green compact of ceramic tile upper surface then, makes more than one tool marks form predetermined pattern.The ceramic tile that for example adopts red, black, yellow three layers of base soil to make by manifesting different colors, just can carve " sunrise impression ".
The surface handled being carved into base and going into the stove sintering, just obtained final product.
Even if ceramic tile of the present invention not glaze, the green compact of ceramic tile of multilayered color-forming presents well-bedded pattern after etching, third dimension and artistic expression are strong.If glaze, then more can highlight the artistic effect of ceramic tile.
Claims (10)
1. the processing method of a ceramic tile is characterized in that, described method comprises the steps:
1. at first layering is made the green compact of ceramic tile (10) that is combined into monoblock with the base soil of at least two kinds of different colours, and described green compact of ceramic tile (10) has green compact upper surface (13);
2. make green compact of ceramic tile (10) drying then; And green compact of ceramic tile (10) is placed the processing stations of ceramic tile engraving;
3. use lithography tool (130) to go up the recessed tool marks (40) of processing then, make more than one tool marks (40) form predetermined pattern at the green compact upper surface (13) of green compact of ceramic tile (10);
4. again the base (20) that is carved into after the etching is carried out surface treatment, the formation surface has been handled and has been carved into base (30);
5. then the surface has been handled and be carved into base (30) and go into the stove sintering.
2. the processing method of ceramic tile according to claim 1 is characterized in that, the recessed tool marks (40) of the 3. described processing of step comprising:
A. sketch the contours of the etching profile (19) of tool marks (40) at green compact upper surface (13);
B. carry out etching with hand-held lithography tool (130) along etching profile (19).
3. the processing method of ceramic tile according to claim 1 is characterized in that, the recessed tool marks (40) of the 3. described processing of step comprising:
A. the intelligent control center (100) of ceramic tile intelligent carving machine has read the pattern data of wanting etching from storage medium at this moment, this pattern data is driven module and progressively calls and form to drive instruction, and will drive to instruct by output interface (105) and be transferred to Vidacare corp (108) successively;
B. next Vidacare corp (108) drives green compact upper surface (13) the processing recessed tool marks (40) of lithography tool (130) at green compact of ceramic tile (10), makes more than one tool marks (40) form predetermined pattern.
4. the processing method of ceramic tile according to claim 1 is characterized in that: described surface treatment comprise to be carved into base (20) cleaning, surface at least a in the layer operation; It is to adhere to glaze or base earth material at green compact upper surface (13) that described surface layer; Technology comprises brush, at least a in being coated with, printing, gluing, drenching, soaking, pressing, spraying, rubbing.
5. a ceramic tile is characterized in that, described ceramic tile comprises:
The brick body, described brick body is by the base soil material layering be combined into of at least two kinds of different colours;
Surface element, the recessed tool marks (40) that the useful lithography tool of described surface element (130) carves.
6. a kind of ceramic tile according to claim 5 is characterized in that: the surface that has tool marks of carving (40) to adhere to afterwards on described surface element layer.
7. the processing method of a ceramic tile is characterized in that, described method comprises the steps:
1. at first make monoblock green compact of ceramic tile (10), and make described green compact of ceramic tile (10) that green compact upper surface (13) be arranged with base soil;
2. make green compact of ceramic tile (10) drying then; And green compact of ceramic tile (10) is placed the processing stations of ceramic tile engraving;
3. the intelligent control center (100) of ceramic tile intelligent carving machine has read the pattern data of wanting etching from storage medium at this moment, this pattern data is driven module and progressively calls and form and drive instruction, and will drive to instruct by output interface (105) and be transferred to Vidacare corp (108) successively;
4. next Vidacare corp (108) drives green compact upper surface (13) the processing recessed tool marks (40) of lithography tool (130) at green compact of ceramic tile (10), makes more than one tool marks (40) form predetermined pattern;
5. the base (20) that is carved into after the etching is carried out surface treatment, the formation surface has been handled and has been carved into base (30);
6. then the surface has been handled and be carved into base (30) and go into the stove sintering.
8. the processing method of ceramic tile according to claim 7 is characterized in that: described surface treatment comprise to be carved into base (20) cleaning, surface at least a in the layer operation; It is to adhere to glaze or base earth material at green compact upper surface (13) that described surface layer; Technology comprises brush, at least a in being coated with, printing, gluing, drenching, soaking, pressing, rubbing.
9. a ceramic tile is characterized in that, described ceramic tile comprises:
The brick body, described brick body is made of the base soil material;
Surface element, the recessed tool marks (40) that the useful lithography tool of described surface element (130) carves.
10. a kind of ceramic tile according to claim 9 is characterized in that: the surface that has tool marks of carving (40) to adhere to afterwards on described surface element layer.