CN101003425A - Synthesized stone-plastic plate - Google Patents

Synthesized stone-plastic plate Download PDF

Info

Publication number
CN101003425A
CN101003425A CNA2007100716577A CN200710071657A CN101003425A CN 101003425 A CN101003425 A CN 101003425A CN A2007100716577 A CNA2007100716577 A CN A2007100716577A CN 200710071657 A CN200710071657 A CN 200710071657A CN 101003425 A CN101003425 A CN 101003425A
Authority
CN
China
Prior art keywords
parts
stone
plastic plate
board
good
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CNA2007100716577A
Other languages
Chinese (zh)
Other versions
CN100441535C (en
Inventor
赵颖义
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CNB2007100716577A priority Critical patent/CN100441535C/en
Publication of CN101003425A publication Critical patent/CN101003425A/en
Application granted granted Critical
Publication of CN100441535C publication Critical patent/CN100441535C/en
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

This invention discloses a synthetic stone-plastic board, which is produced by: (1) mixing volcanic ashes 76-80 parts and bleaching powder 3-6 parts, and stirring for 5-30 min until the color turns lighter; (2) adding phenol formaldehyde resin 9-13 parts, resin binder 3-7 parts, and resin curing agent 1-2 parts, mixing uniformly, and curing in a board mold at 200-300 deg.C and 200-600 kg/cm2 for 12-60 h. The stone-plastic board has such advantages as good corrosion resistance, good heat preservation, low cost, good fireproof and waterproof performance, good wear resistance, and no rupture. The stone-plastic board can be used as wallboard, wall brick, ceiling material and separating board for indoor decoration, especially the base material for floors, cabinets and tablets.

Description

Synthesized stone-plastic plate
Technical field
The present invention relates to sheet material.
Background technology
Existing sheet material can be divided into sheet metal, plastic plate, wooden boards and slabstone, the shortcoming that sheet metal exists is perishable, heat retaining property is poor, cost is high, there is easily aging, inflammable, not attrition resistant shortcoming in plastic plate, that wooden boards exists is inflammable, the shortcoming of moisture-sensitive distortion, and there is easily cracked shortcoming in slabstone.
Summary of the invention
The purpose of this invention is to provide a kind of above-mentioned various sheet material shortcoming that overcomes, integrate the synthesized stone-plastic plate of advantages such as corrosion-resistant, good heat preservation performance, cost be low, fire-resistant, water-fast, wear-resisting, not cracked
Technical solution of the present invention is: it is by weight ratio with 76～80 parts of volcanic ash, with 3～6 parts in chlorinated lime, after mixing is stirred and was dulled the color in 5～30 minutes, add after 1～2 part of 9～13 parts in resol, 3～7 parts of resinoid bonds and resin curing agent mixes, put into board mould at 200～600kg/cm 2Pressure and 200～300 ℃ of temperature compacted unders solidified 12～60 hours.
Technique effect of the present invention is: it integrates advantages such as corrosion-resistant, good heat preservation performance, cost be low, fire-resistant, water-fast, wear-resisting, not cracked.Surface treatment in addition, it can make indoor and outdoor Decorative wall plate, wall tile, ceiling material, partition panel etc.Be specially adapted to the floor, kitchen cabinet, the table top base material of plate.It has a wide range of applications field and deep development value.
Embodiment
It is by weight ratio with 78 parts of volcanic ash, with 4.5 parts in chlorinated lime, mix stir dulled the color in 10 minutes after, add after 1.5 parts of 11 parts in resol, 5 parts of resinoid bonds and resin curing agents mix, put into board mould at 200～600kg/cm 2Pressure and 200～300 ℃ of temperature compacted unders solidified 12～60 hours.The volcanic ash particle diameter is 0.2～1mm.

Claims (3)

1, synthesized stone-plastic plate, it includes volcanic ash, chlorinated lime, resol, resinoid bond and resin curing agent, it is characterized in that, it is by weight ratio with 76～80 parts of volcanic ash, with 3～6 parts in chlorinated lime, mix to stir dulled the color in 5～30 minutes after, add after 1～2 part of 9～13 parts in resol, 3～7 parts of resinoid bonds and resin curing agent mixes, put into board mould at 200～600kg/cm 2Pressure and 200～300 ℃ of temperature compacted unders solidified 12～60 hours.
2, synthesized stone-plastic plate as claimed in claim 1, it is characterized in that it is by weight ratio with 78 parts of volcanic ash, with 4.5 parts in chlorinated lime, after mixing is stirred and was dulled the color in 10 minutes, add after 1.5 parts of 11 parts in resol, 5 parts of resinoid bonds and resin curing agents mix, put into board mould at 200～600kg/cm 2Pressure and 200～300 ℃ of temperature compacted unders solidified 12～60 hours.
3, synthesized stone-plastic plate as claimed in claim 1 is characterized in that described volcanic ash particle diameter is 0.2～1mm.
CNB2007100716577A 2007-01-15 2007-01-15 Synthesized stone-plastic plate Expired - Fee Related CN100441535C (en)