CN1009642B - 早凝早强钢渣矿渣水泥 - Google Patents
早凝早强钢渣矿渣水泥Info
- Publication number
- CN1009642B CN1009642B CN87104463A CN87104463A CN1009642B CN 1009642 B CN1009642 B CN 1009642B CN 87104463 A CN87104463 A CN 87104463A CN 87104463 A CN87104463 A CN 87104463A CN 1009642 B CN1009642 B CN 1009642B
- Authority
- CN
- China
- Prior art keywords
- slag
- cement
- early strength
- present
- blast
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Abstract
一种早凝早强钢渣矿渣水泥,其组分中除具有钢渣、矿渣、熟料外。还有3-7%的烧石膏,可使钢渣矿渣水泥终凝时间从17水时缩短至9小时以内,7天抗压强度提高5MPa,组分中具有含钠离子或钾离子的活性激发剂,可成为R型小泥,本发明解决了已有钢渣,矿渣水泥凝结时间缓慢、早期强度低、不能成为R型的技术难题、可广泛应用于工业民用建筑。水利、道路、机场、军事等工程,尤其适用于抢修工程及对早期强度有较高要求的工程。
Description
本发明涉及钢渣矿渣水泥,特别是一种早凝早强钢渣矿渣水泥,尤其适用于抢修工程及对早期强度有较高要求的工程。
钢渣矿渣水泥是我国研制成功的一个新的水泥品种,未见国外有此种水泥的技术指导。在本发明作出之前,以往的钢渣矿渣水泥以80%以上的钢渣矿渣(规定其中钢渣含量不小于35%)为主要原材料,掺入少量硅酸盐水泥熟料和生石膏,磨细而成为有一定细度的一种混合物或水硬性胶凝材料,它与普通硅酸盐水泥和矿渣硅酸盐水泥相比,具有后期强度高、抗折强度高、耐磨、水化热低、抗渗性好等特点,同时生产工艺简单、投资少、成本低、可变废为宝,节省大量耕地,改善环境污染,经济效益显著,可用于道路工程、水利工程、军事工程段等,因而为许多水泥厂家生产推广。然而该品种水泥还存在着凝结时间缓慢、早期强度偏低的弱点,以《CBn164-82》中325最高标号钢渣矿渣水泥为例,终凝时间24小时内,7天抗压强度为13MPa,比同标号矿渣硅酸盐水泥低2MPa,也达不到R型标准。于是在施工过程中,延长了混凝土拆模时间,延长了施工周期,更不能用于抢修工程及对早期强度有较高要求的工程,使其应用受到了极大限制。
本发明的目的在于克服上述钢渣矿渣水泥之弱点,发明出一种早凝早强钢渣矿渣水泥,以满足工程抢修和快速施工的需要。
本发明的技术要点是:该早凝早强水泥为一种具有3-7%(重量比)在烧石膏、钢渣、矿渣和熟料组分的有一定细度的混合物,它为一种新型的胶凝材料,这里说的熟料,指硅酸盐水泥熟料,这里说的烧石膏,可由生石膏(二水石膏或硬石膏)在200℃-900℃最好在700-800℃温度范围内煅烧而成的,这里说的钢渣,指平炉或转炉水淬或非水淬钢渣等,矿渣为粒化高炉矿渣或粒化冲天炉铁渣等。
为了进一步提高上述早凝早强水泥的标号(28天抗压强度),可限定熟粒的重量占总重量的5-20%,钢渣的重量占总重量的35-60%,铁渣的重量占总重量的35-50%;最好是熟料的重量占总重量的15-20%,钢渣的重量占总重量的35-45%,矿渣的重量占总重量的35-45%,烧石膏的重量占总重量的5-7%。
为了使早凝早强达到更好的效果,制成3天强度达到28天强度的45%的R型水泥,可在上述三种水泥的基础上加入一种活性激发剂,该活性激发剂能够激发钢渣和高炉渣的活性成分,使之具有活性,该活性激发剂,可以是具有钠离子或钾离子的碱和/或具有钢离子或钾离子的盐,可以是水玻璃,氢氧化钠、氢氧化钾,碳酸钠或碳酸钾等,或者它们之间不同的组合,如既加氢氧化钠,又加氢氧化钾等等。氢氧化钠和/或氢氧化钾的外掺重量最好为总重的1-4%。
为了满足抢修工程和快速施工的需要,也可以用另一种早凝早强水泥。该水泥是具有熟料、生石膏、钢渣、矿渣和活性激发剂组分的有一定细度的混合物,也可以在已有的钢渣水泥的基础上加入活性激发剂组成。该活性激发剂和上面所说的活性激发剂相同,氢氧化钠和/或氢氧化钾外掺重量为总重量的1-4%。该种水泥有的可达到R型标准。
附图是本发明的生产工艺流程图。
本发明称的早凝早强钢渣矿渣水泥,可以认为是对现有钢渣矿渣水泥(该水泥规定其中钢渣含量不少于35%)的改进,也可以认为是对钢渣矿渣
硅酸盐水泥的改进,也可以认为是对钢渣含量小于35%,熟料含量小于20%的钢渣矿渣胶凝材料性能的改进,等等。
本发明与已有钢渣矿渣水泥相比,具有早凝早强的特点,还可以具有R型水泥的特点,同时也可提高水泥标号,能生产出早凝早强R型425标号钢渣矿渣水泥。可广泛应用于工业民用建筑。水利工程,军事工程,道路,机场等工程,尤其适用于抢修工程及对早斯强度有较高要求的工程。
以下是本发明的实施例。
实施例(一):
1.原材料:
2.生产工艺(见附图)。
3.本发明组分及性能:
按照本发明不但可以提高钢渣矿渣水泥的7天强度,缩短凝结时间,而且标号可以达到425号钢渣矿渣水泥。
实施例(二):
1.原材料:
2.本发明组分及性能:
本发明在生产具有早凝早强特点和R型的同时,标号也可突破钢渣矿渣水泥最高标号(325号),达到425号。
实施例(三):
也可制得早凝早强水泥。
实施例(四):
1.原材料:
种类 来源 化学成分(%)
Cao Sio2 Ae2O3 Fe2O3 FeO MgO MnO P2O5 SO3
钢渣 邯郸钢铁厂 50.65 17.95 3.73 6.39 7.99 4.70 1.89 1.36
矿渣 邯郸钢铁厂 41.3 34.11 11.05 1.20 - 7.94 0.22 -
熟料 邯郸水泥厂 64.34 19.61 5.63 4.48 - 3.96 - -
750℃ 邯郸钢渣 37.97 49.7
烧石膏 水泥厂
2.生产工艺(见附图)。
3.本发明组分及性能:
1.原材料:
来源 化学成分(%)
CaO Sio2 Ae2O3 Fe2O3 FeO MgO M2O P2O5 SO3
邯郸钢渣 50.65 17.95 3.73 6.39 7.99 4.70 1.89 1.36 -
总厂钢渣
邯钢矿渣 41.30 34.11 11.05 1.20 - 7.94 0.22 - -
邯郸水泥 64.34 19.61 5.63 4.48 - 3.96 - - -
厂熟料
750℃烧石 37.97 - - - - - - - 49.70
膏
2.本发明组分及性能:
本发明在生产具有早凝早强特点和R型的同时,标号也可突破钢渣矿渣水泥最高标号(325号),达到425号。
实施例(三):
类别 熟料 钢渣 矿渣 烧石膏
组分C 21% 35% 39% 5%
组分D 25% 335% 35% 55%
也可制得早凝早强水泥。
实施例(四):
Claims (5)
1、一种早凝早强钢渣矿渣水泥,其特征是组分中具有钢渣35-45%,矿渣35-45%,熟料15-20%,烧石膏5-7%。
2、一种早凝早强钢渣矿渣水泥,其特征是组分中具有钢渣35-45%,矿渣35-45%,熟料15-20%,烧石膏5-7%,外加1-4%的含Na+或K+的活性激发剂。
3、根据权利要求2所述的水泥,其特征是所说的活性激发剂为水玻璃,氢氧化钠,氢氧化钾,碳酸钠或碳酸钾,或它们之间不同的组合。
4、一种早凝早强钢渣矿渣水泥,其特征是组分中具有钢渣35-45%,矿渣35-45%,熟料15-20%,生石膏5-7%,外加1-4%的含Na+或K+的活性激发剂。
5、根据权利要求4所述的水泥,其特征是所说的活性激发剂为水玻璃,氢氧化钠,氢氧化钾,碳酸钠或碳酸钾,或它们之间不同的组合。