CN100577909C - Camouflage printing method for aramid fiber 1313 color silk and anti-flaming viscose blend fabric - Google Patents
Camouflage printing method for aramid fiber 1313 color silk and anti-flaming viscose blend fabric Download PDFInfo
- Publication number
- CN100577909C CN100577909C CN200810059896A CN200810059896A CN100577909C CN 100577909 C CN100577909 C CN 100577909C CN 200810059896 A CN200810059896 A CN 200810059896A CN 200810059896 A CN200810059896 A CN 200810059896A CN 100577909 C CN100577909 C CN 100577909C
- Authority
- CN
- China
- Prior art keywords
- aramid fiber
- fiber
- flaming viscose
- color silk
- fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention relates to a method for pattern-painting aramid fiber 1313 color filament and flame-retardant viscose blended fabrics. The method comprises: boiling the aramid fiber 1313 color filament and the and flame-retardant viscose blended fabrics before dying, then, putting into H2O2 8-15KgL-1, adjusting the pH value to 9-11, heating to 70-90DEG C, processing for 30-60min, steaming for 60-90min under steam with the temperature of 100-105DEG C, taking out and using hot water, warm water and cold water to wash, lastly, mercerizing, shaping, then, pattern-painting, then, steaming with the temperature of 100-105DEG C for 5-10min, and then soaping and water washing under the temperature of 98-100DEG C. The method of the invention mainly adds flame-retardant viscose fiber and conductive fiber when the aramid fiber is blended and can realize that dye is used to print the flame-retardant viscose only, which not only realize pattern-painting camouflage effect, but also solves the problems of the strong strength of the flame-retardant fiber, handing feeling, textile printing, color fastness and the like.
Description
Technical field
The present invention relates to the camouflage printing method of fabric, particularly relate to the camouflage printing method of a kind of aramid fiber 1313 color silk and anti-flaming viscose blend fabric.
Background technology
The aramid fiber chemical name is a Fanglun 1313, belongs to aromatic polyamide, is at first succeeded in developing in the sixties in 20th century by du pont company.Because the special structure of aramid fiber, aramid fiber has good heat-resisting quantity and anti-flammability, therefore as a kind of exotic material, can be used for the liner of filtering material (high temperature filtration bag and filter felt), fire proofing material and the industrial high temperature resistant equipment of use under aerospace field, High temperature textiles (heatproof protective clothing, fire-entry suit, military uniform and space suit etc.), the high temperature etc.But the vitrification point of aramid fiber is very high, and up to 270 ℃, dyeing is difficult, light fastness is poor, and many purposes all require fiber that high-quality color and luster is arranged,
Camouflage printing cloth is used for the camouflage clothes of army and tent etc. mostly.For the ease of camouflage and hidden, camouflage color should Sihe be close mutually with surrounding environment, such as sandy beach camouflage color, forest camouflage, greenery patches camouflage color etc.And that the aramid fiber camouflage printing is studied report relatively is less, and therefore, research aramid fiber camouflage printing tool has very important significance.
Summary of the invention
The object of the present invention is to provide the camouflage printing method of a kind of aramid fiber 1313 color silk and anti-flaming viscose blend fabric.
The technical solution adopted for the present invention to solve the technical problems is to comprise the steps:
1) boiling-off before the dyeing of aramid fiber 1313 color silk and anti-flaming viscose blend fabric, the prescription of boiling-off is: NaOH 30～50gL
-1, degreaser DO 8～10gL
-1, be heated to 90～100 ℃, boil 30～60min, under 100～105 ℃ of steam, steam 60～90min then, take out with 80～90 ℃ of hot water wash, 60～70 ℃ of Warm Wash, running water is cleaned then;
2) BLENDED FABRIC that will go up after the boiling-off is put into 8～15gL
-1H
2O
2In, regulate pH value 9～11, be heated to 70～90 ℃, handle 30～60min, under 100～105 ℃ of steam, steam 60～90min then, take out with 80～90 ℃ of hot water wash, 60～70 ℃ of Warm Wash, running water is cleaned then, and last mercerising formalizes on boarding machine;
3) the fabric stamp on printing machine after will formalizing, the camouflage printing prescription is DISPERSE DYES 80gL
-1, 5% sodium alginate, 450～500gL
-1, urea 3～12gL
-1, reservehao S 0.5～1gL
-1, sodium bicarbonate 1～2.5gL
-1
4) behind the camouflage printing again by evaporating, evaporating temperature is 100～105 ℃, time 5～10min, the 20～40min that soaps under 98～100 ℃ then 80～90 ℃ of washings, cleans at last.
Described aramid fiber 1313 color silk/anti-flaming viscose blend fabric, aramid fiber percentage by weight in blending is 35%～45%, and the conductive fiber percentage by weight of interpolation is 1～2%, and all the other are anti-flaming viscose.
Described conductive fiber is that carbon black is conductive fiber or metallic compound type conductive fiber.
The present invention compares with background technology, and the beneficial effect that has is:
The present invention adds Fire resistant viscose fiber and conductive fiber when the aramid fiber blending, can realize only printing Fire resistant viscose fiber with dyestuff, can realize reaching the camouflage painting effect, has solved problems such as fire resistance fibre brute force, feel, stamp, fastness, cost again.
The specific embodiment
Embodiment 1:
(1) get 10m aramid fiber 1313 color silk/anti-flaming viscose blend fabric, wherein the percentage by weight of aramid fiber is 35%, and the percentage by weight of the composite conducting fiber Antron III of Du Pont company carbon black conductive core is 1～2%, and all the other are anti-flaming viscose.At NaOH 50gL
-1, degreaser DO 10gL
-1, be heated to 100 ℃, boil 30min, then at 100～105 ℃ of decatize 90min, take out with 80～90 ℃ of hot water wash, 60～70 ℃ of Warm Wash, running water is cleaned then;
(2) BLENDED FABRIC that will go up after the kiering is put into 15gL
-1H
2O
2In, regulate pH value 11, be heated to 90 ℃, handle 30min, then at 100～105 ℃ of decatize 60min, take out with 80～90 ℃ of hot water wash, 60～70 ℃ of Warm Wash, running water is cleaned then, and last mercerising formalizes on boarding machine;
(3) the fabric stamp on printing machine after will formalizing, the camouflage printing prescription is for disperseing the dark blue 20gL of HGL
-1, disperse H
2The yellow 40gL of RL
-1, disperse the red 8gL of H2GFL
-1, carbon black 12gL
-1, 5% sodium alginate 500gL
-1, urea 3gL
-1, reservehao S 0.5gL
-1, sodium bicarbonate 1gL
-1, print off brown camouflage color.
(4) behind the camouflage printing again by evaporating fast, evaporating temperature is 100～105 ℃, time 10min exists then, the 40min that soaps under 98～100 ℃ of the temperature 80～90 ℃ of washings, cleans at last.
Embodiment 2:
(1) get 10m aramid fiber 1313 color silk/anti-flaming viscose blend fabric, wherein the percentage by weight of aramid fiber is 45%, and the percentage by weight of the composite conducting fiber Antron III of Du Pont company carbon black conductive core is 1～2%, and all the other are anti-flaming viscose.At NaOH 30gL
-1, degreaser DO 8gL
-1, be heated to 90 ℃, boil 60min, then at 100～105 ℃ of decatize 60min, take out with 80～90 ℃ of hot water wash, 60～70 ℃ of Warm Wash, running water is cleaned then;
(2) BLENDED FABRIC that will go up after the kiering is put into 8gL
-1H
2O
2In, regulate pH value 9, be heated to 70 ℃, handle 60min, then at 100～105 ℃ of decatize 90min, take out with 80～90 ℃ of hot water wash, 60～70 ℃ of Warm Wash, running water is cleaned then, and last mercerising formalizes on boarding machine;
(3) the fabric stamp on printing machine after will formalizing, the camouflage printing prescription is for disperseing the dark blue 50gL of HGL
-1, disperse H
2The yellow 20gL of RL
-1, disperse the red 5gL of H2GFL
-1, carbon black 25gL
-1, 5% sodium alginate 450gL
-1, urea 12gL
-1, reservehao S 1gL
-1, sodium bicarbonate 2.5gL
-1, print off the navy blue camouflage color.
(4) behind the camouflage printing again by evaporating fast, evaporating temperature is 100～105 ℃, time 5min exists then, the 20min that soaps under 98～100 ℃ of the temperature 80～90 ℃ of washings, cleans at last.
Embodiment 3:
(1) get 10m aramid fiber 1313 color silk/anti-flaming viscose blend fabric, wherein the percentage by weight of aramid fiber is 45%, and the Belltron 632 conductive fiber percentage by weights that clock spins company are 1～2%, and all the other are anti-flaming viscose.At NaOH 40gL
-1, degreaser DO 9gL
-1, be heated to 95 ℃, boil 40min, then at 100～105 ℃ of decatize 80min, take out with 80～90 ℃ of hot water wash, 60～70 ℃ of Warm Wash, running water is cleaned then;
(2) BLENDED FABRIC that will go up after the kiering is put into 12gL
-1H
2O
2In, regulate pH value 10, be heated to 80 ℃, handle 40min, then at 100～105 ℃ of decatize 80min, take out with 80～90 ℃ of hot water wash, 60～70 ℃ of Warm Wash, running water is cleaned then, and last mercerising formalizes on boarding machine;
(3) the fabric stamp on printing machine after will formalizing, the camouflage printing prescription is for disperseing the dark blue 30gL of HGL
-1, disperse H
2The yellow 20gL of RL
-1, disperse the red 10gL of H2GFL
-1, disperse the peacock blue 20gL of SGL
-1, 5% sodium alginate 480gL
-1, urea 6gL
-1, reservehao S 0.8gL
-1, sodium bicarbonate 2gL
-1, print off blue camouflage color.
(4) behind the camouflage printing again by evaporating fast, evaporating temperature is 100～105 ℃, time 8min exists then, the 30min that soaps under 98～100 ℃ of the temperature 80～90 ℃ of washings, cleans at last.
Claims (3)
1, the camouflage printing method of a kind of aramid fiber 1313 color silk and anti-flaming viscose blend fabric comprises the steps:
1) boiling-off before the dyeing of aramid fiber 1313 color silk and anti-flaming viscose blend fabric;
2) BLENDED FABRIC after the boiling-off is bleached, formalized;
3) the fabric stamp on printing machine after will formalizing, the camouflage printing prescription is DISPERSE DYES 80gL
-1, 5% sodium alginate, 450～500gL
-1, urea 3～12gL
-1, reservehao S 0.5～1gL
-1, sodium bicarbonate 1～2.5gL
-1
4) behind the camouflage printing again by evaporating, evaporating temperature is 100～105 ℃, time 5～10min, the 20～40min that soaps under 98～100 ℃ then 80～90 ℃ of washings, cleans at last;
It is characterized in that:
In step 1): the prescription of boiling-off is: NaOH 30～50gL
-1, degreaser DO 8～10gL
-1, be heated to 90～100 ℃, boil 30～60min, under 100～105 ℃ of steam, steam 60～90min then, take out with 80～90 ℃ of hot water wash, 60～70 ℃ of Warm Wash, running water is cleaned then;
In step 2) in: the BLENDED FABRIC after the boiling-off is put into 8～15gL
-1H
2O
2In, regulate pH value 9～11, be heated to 70～90 ℃, handle 30～60min, under 100～105 ℃ of steam, steam 60～90min then, take out with 80～90 ℃ of hot water wash, 60～70 ℃ of Warm Wash, running water is cleaned then, and last mercerising formalizes on boarding machine.
2, the camouflage printing method of a kind of aramid fiber 1313 color silk according to claim 1 and anti-flaming viscose blend fabric, it is characterized in that: described aramid fiber 1313 color silk and anti-flaming viscose blend fabric, aramid fiber 1313 color silk percentage by weight in blending is 35%～45%, the conductive fiber percentage by weight that adds is 1～2%, and all the other are anti-flaming viscose.
3, the camouflage printing method of a kind of aramid fiber 1313 color silk according to claim 2 and anti-flaming viscose blend fabric is characterized in that: described conductive fiber is that carbon black is conductive fiber or metallic compound type conductive fiber.