CN100515621C - 比例电磁铁磁轭粉末冶金制作工艺 - Google Patents

比例电磁铁磁轭粉末冶金制作工艺 Download PDF

Info

Publication number
CN100515621C
CN100515621C CNB2007100545520A CN200710054552A CN100515621C CN 100515621 C CN100515621 C CN 100515621C CN B2007100545520 A CNB2007100545520 A CN B2007100545520A CN 200710054552 A CN200710054552 A CN 200710054552A CN 100515621 C CN100515621 C CN 100515621C
Authority
CN
China
Prior art keywords
powder metallurgy
magnetic yoke
magnet magnetic
proportion electro
powder
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CNB2007100545520A
Other languages
English (en)
Other versions
CN101108420A (zh
Inventor
靳长城
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANYANG JIAOLICHANG BASIC PARTS FACTORY
Original Assignee
ANYANG JIAOLICHANG BASIC PARTS FACTORY
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANYANG JIAOLICHANG BASIC PARTS FACTORY filed Critical ANYANG JIAOLICHANG BASIC PARTS FACTORY
Priority to CNB2007100545520A priority Critical patent/CN100515621C/zh
Publication of CN101108420A publication Critical patent/CN101108420A/zh
Application granted granted Critical
Publication of CN100515621C publication Critical patent/CN100515621C/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种比例电磁铁磁轭粉末冶金制作工艺涉及一种用粉末冶金工艺制作比例电磁铁外壳的方法。它主要用纯铁粉作原材料,将纯铁粉装入在振动粉台上的压模中用高压制成坯状制品,再放入烧结炉高温一定时间后,再复压提高密度和压出定位凹坑,之后再经过高温复烧,最后经精密加工即可。本发明制作电磁换磁轭(外壳)采用新的粉末冶金工艺,不仅满足了国家标准对密度和抗拉强度的要求,而且化合碳的含量极低;保证了产品对软磁性和机械性能的要求,达到了高成品率和节约了能源和材料。

Description

比例电磁铁磁轭粉末冶金制作工艺
一、技术领域:
本发明涉及一种用粉末冶金工艺制作比例电磁铁外壳的方法。
二、背景技术:
电磁铁是机电产品上的重要部件,比例电磁铁是电磁铁的一种,而磁轭又是制作比例电磁的关键零件。长期以来,比例电磁铁的磁轭(外壳)一直沿用纯铁棒料锻造,靠机械切削加工来保证最终几何形状和尺寸的要求。因在加工过程中产品异形度常使加工材料利用率低于30%,大量不合格成品造成了人力和能源的浪费。
三、发明内容:
本发明的目的是在采用粉末冶金工艺制作比例电磁铁磁轭,达到高成品率和节约能源材料。
制作比例电磁铁磁轭采用的主要原材料是纯铁粉;制作工艺为;(1)制作坯状制品:将纯铁粉装入压模然后以7-9T/cm2压力下成型、脱模;(2)制作烧结制品:将坯状制品放入烧结炉在温度1050℃-1250℃纯氢作保护气份下,时间1小时净化烧结;(3)复压:将烧结制品装入复压模具复压,使密度提高至≥7.0g/cm3,同时在需打孔位置上压出定位凹坑。(4)复烧:将复压制作再放入烧结炉在1050℃-1250℃纯氢作保护气份下,时间1小时,取出后续加工即可。所用原材料纯铁粉在装入压模前,掺入纯铁粉重量0.8-1.2%的润滑剂搅拌均匀。
制作电磁换磁轭(外壳)采用新的粉末冶金工艺,不仅满足了国家标准对密度和抗拉强度的要求,而且化合碳的含量极低;保证了产品对软磁性和机械性能的要求,达到了高成品率和节约了能源和材料,材料利用率达90%以上。
四、具体实施方式:
首先取一定重量的纯铁粉加入纯铁粉重量1%的润滑剂粉沫混合搅拌均匀,所用润滑剂可用如硬脂酸锌或硬脂酸锂等。将混合料加入振动装粉台上的压模中,然后以8T/cm2压力下成型、脱模,制作成设计形状的坯状制品。再经烧结炉在温度1100℃纯氢作保护气份下时间1小时净化烧结,同时也达到脱除润滑剂的目的。将烧结制品再装入复压模具复压,使密度提高至不小于7.0g/cm3,在复压时,在需要打孔的位置上压出约120°的定位凹坑。将复压制品再放入烧结炉在1000℃纯氢作保护气份下时间1小时,取出后在数控机床上精加工所有的孔即成为产品。用该工艺加工的比例电磁铁磁轭与原来的形状尺寸不作任何改动和变化。

Claims (2)

1、一种比例电磁铁磁轭粉末冶金制作工艺,其特征在于:
(1)制作比例电磁铁磁轭采用的主要原材料是纯铁粉;
(2)制作工艺为:
a、制作坯状制品:将纯铁粉装入压模然后以7-9T/cm2压力下成型、脱模;
b、制作烧结制品:将坯状制品放入烧结炉在温度1050℃-1250℃纯氢作保护气氛下,时间1小时净化烧结;
c、复压:将烧结制品装入复压模具复压,使密度提高至≥7.0g/cm3,同时在需打孔位置上压出定位凹坑;
d、复烧:将复压制品再放入烧结炉在1050℃-1250℃纯氢作保护气氛下,时间1小时,取出后续加工即可。
2、根据权利要求1所述的一种比例电磁铁磁轭粉末冶金制作工艺,其特征在于:所用原材料纯铁粉在装入压模前,掺入纯铁粉重量0.8-1.2%的滑润剂搅拌均匀。
CNB2007100545520A 2007-06-01 2007-06-01 比例电磁铁磁轭粉末冶金制作工艺 Expired - Fee Related CN100515621C (zh)