CN100424931C - 铜板与铝板连接减小接触电阻的方法 - Google Patents

铜板与铝板连接减小接触电阻的方法 Download PDF

Info

Publication number
CN100424931C
CN100424931C CNB2006100960656A CN200610096065A CN100424931C CN 100424931 C CN100424931 C CN 100424931C CN B2006100960656 A CNB2006100960656 A CN B2006100960656A CN 200610096065 A CN200610096065 A CN 200610096065A CN 100424931 C CN100424931 C CN 100424931C
Authority
CN
China
Prior art keywords
aluminum plate
stainless steel
aluminium sheet
copper
contact resistance
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CNB2006100960656A
Other languages
English (en)
Other versions
CN1929205A (zh
Inventor
汤伦军
李定
付鹏
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Institute of Plasma Physics of CAS
Original Assignee
Institute of Plasma Physics of CAS
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Institute of Plasma Physics of CAS filed Critical Institute of Plasma Physics of CAS
Priority to CNB2006100960656A priority Critical patent/CN100424931C/zh
Publication of CN1929205A publication Critical patent/CN1929205A/zh
Application granted granted Critical
Publication of CN100424931C publication Critical patent/CN100424931C/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明提供一种铜板与铝板连接减小接触电阻方法，对铜板与铝板的接头处进行处理，将铜板进行烫锡处理，铝板抛光除去氧化层后，喷涂一层超薄不锈钢，使得铜板与铝板的接头处电阻大大降低，减少接头发热，延长使用年限。

Description

铜板与铝板连接减小接触电阻的方法
技术领域
本发明涉及一种铜铝板连接时，减小其接触电阻新方法。
技术背景
目前，电力线路的功能是传输和分配电能，常用的母导线主要是铜母线和铝母线。当铜、铝导体直接连接时，这两种金属的接触面在空气中水分、二氧化碳和其他杂质的作用下极易形成电解液，从而形成的以铝为负极、铜为正极的原电池，使铝产生电化腐蚀，造成铜、铝连接处的接触电阻增大。另外，由于铜、铝的弹性模量和热膨胀系数相差很大，在运行中经多次冷热循环(通电与断电)后，会使接触点处产生较大的间隙而影响接触，也增大了接触电阻。接触电阻的增大，运行中就会引起温度升高。高温下腐蚀氧化就会加剧，产生恶性循环，使连接质量进一步恶化，最后导致接触点温度过高甚至会发生冒烟、烧毁等事故。现今采用减小铜铝连接接触电阻的方法是在接触面上涂一层0.2mm厚的导电膏(电力复合脂)或采用铜铝过渡板，以降低连接处的接触电阻，减小接头发热。但其工作温度低，使用年限短，造价昂贵。
发明内容
本发明提供一种铜板与铝板连接减小接触电阻的方法，对铜板与铝板的接头处进行处理，使得铜板与铝板的接头处电阻大大降低，减小接头发热，延长使用年限。
本发明的技术方案如下：
铜板与铝板连接减小接触电阻的方法，其特征在于对铜板与铝板的接头处分别进行以下处理：
(1)、铜板的表面进行烫锡处理；
(2)、铝板的表面处理：
第一步：采用机械抛光方法除去铝板表面的氧化层；
第二步：采用除油方法对其铝板表面进行二次处理；
第三步：喷涂不锈钢喷剂；
第四步：表面干燥。
铝板上喷涂不锈钢喷剂得到的不锈钢层厚度为2-5微米，表面干燥时间为5-10分钟。(处理后的表面应该光亮，涂层均匀，颜色成灰白色)
所述的烫锡是指将铜板放入熔融的锡液中再拿出。
所述的除油方法是指用酒精或丙酮擦拭铝板表面。
本发明通过多次试验与测量，发现处理后的接触电阻阻值比处理前的接触电阻阻值小4-6倍。
本发明处理过的铝板表面耐热性能好，适用温度范围：-30℃-+320℃。
本发明处理过的铝板表面与处理后的铜板连接，不受年限影响。
本发明处理过的铝板表面具有强抗酸抗碱特性；
本发明适合铝板与铝板的连接；
工作原理说明：
1、利用不锈钢的耐高温与导热系数大特性，使得处理后的铝板表面工作温度升高；
2、利用不锈钢的强抗酸抗碱特性，使得处理后的铝板表面不产生电化腐蚀；
3、利用不锈钢的抗氧化特性，使得处理后的铝板表面不氧化；
4、虽然不锈钢的电阻率较大，但是其电阻值与长度成正比，与面积成反比，而表面不锈钢厚度为微米级单位，因此其表层不锈钢的自身电阻值很小，可忽略不计；
5、利用喷剂的强粘附性和不锈钢膨胀系数小特性，使得铝板处理表面长时间不变形、不断裂、不起层。
本发明利用不锈钢喷剂，此不锈钢喷剂是一种耐摩和防腐涂层，干膜不锈钢含量达75％的不锈钢喷剂，其中还含有金属与塑料成分，表面完全防腐和抗氧化，同时具有强抗酸碱性及粘附性特性，杜绝铜铝连接处金属的电化腐蚀，降低接头处的接触电阻，确保接头接触良好，减小接头发热。
本发明若与导电脂配合使用，其效果更佳。
本发明还有其他一些优点：
1、操作简单，加工方便；
2、加工后的铝板表面不怕划、耐撞击；
3、加工后的铝板表面具有很强的防锈耐腐蚀性；
4、无氟利昂，安全无副作用。
5、性价比高；
具体实施方式
铜板与铝板连接减小接触电阻的方法，其特征在于对铜板与铝板的接头处分别进行以下处理：
(1)、铜板的表面进行烫锡处理；指将铜板放入300-400℃熔融的锡液中再拿出。
(2)、铝板的表面处理：
1、用机械抛光方法除去铝板表面的氧化层；
2、用丙酮或酒精擦拭铝板表面进行二次处理；
3、喷涂不锈钢喷剂，喷涂采用雾状喷涂，不锈钢层厚度为2-5微米；
4、表面干燥处理：干燥时间为5-10分钟即可。(处理后的表面应该光亮，涂层均匀，颜色成灰白色)

Claims (4)

1. 铜板与铝板连接减小接触电阻的方法，其特征在于对铜板的接头处的表面进行烫锡处理，对铝板的接头处的表面进行如下处理：第一步，采用机械抛光方法除去铝板表面的氧化层；第二步，采用除油方法对其铝板表面进行二次处理；第三步，喷涂不锈钢喷剂；第四步，表面干燥。
2. 根据权利要求1所述的方法，其特征在于铝板上喷涂不锈钢喷剂得到的不锈钢层厚度为2-5微米，表面干燥时间为5-10分钟。
3. 根据权利要求1所述的方法，其特征在于所述的烫锡是指将铜板放入熔融的锡液中再拿出。
4. 根据权利要求1所述的方法，其特征在于所述的除油方法是指用酒精或丙酮擦拭铝板表面。
CNB2006100960656A 2006-09-14 2006-09-14 铜板与铝板连接减小接触电阻的方法 Expired - Fee Related CN100424931C (zh)