CN100423955C - Manufacturing method of decorative artistic pottery ware - Google Patents
Manufacturing method of decorative artistic pottery ware Download PDFInfo
- Publication number
- CN100423955C CN100423955C CNB2004100776841A CN200410077684A CN100423955C CN 100423955 C CN100423955 C CN 100423955C CN B2004100776841 A CNB2004100776841 A CN B2004100776841A CN 200410077684 A CN200410077684 A CN 200410077684A CN 100423955 C CN100423955 C CN 100423955C
- Authority
- CN
- China
- Prior art keywords
- pottery
- manufacture method
- paint
- nature
- mud
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention provides a manufacturing method of a decorative artistic pottery ware. The decorative artistic pottery ware is manufactured from pottery mud which has the components of 70 to 80% of ordinary clay, 15 to 25% of river sand and 3 to 7% of water through the steps of mud material processing, forming by using a mold, firing, coloring biscuits, coating water-proof adhesive, etc. The present invention has natural, native, coarse and primitive effects, fits for the moderns' aesthetic mentality of returning to nature, has the advantages of energy saving, easy obtainment of raw materials, low cost and is favorable to protect environments.
Description
Technical field
The present invention relates to a kind of manufacture method of ceramic, relate in particular to a kind of manufacture method of furnishing art pottery.
Background technology
At present, the furnishing art pottery on the market is various in style.But the incrustation of traditional furnishing art pottery mainly is to adopt artificial colored drawing pattern or decal paper.Artificial colored drawing pattern is made coating with ceramic paint or paint usually, though can play decorative effect preferably, ceramic paint is generally plumbous, cadmium content is higher, and paint solvent is toxic, and all difficulty reaches safety, health, environmental protection requirement; Adopting decal paper to decorate then need increase the decoration firing operation one, increase energy resource consumption, and the pattern of product is natural inadequately, true to nature.In addition, the firing temperature height of traditional furnishing art pottery (more than 1050 ℃), energy consumption is big, and the cost of raw material is also higher.
Summary of the invention
The objective of the invention is to overcome deficiency of the prior art; a kind of manufacture method of furnishing art pottery is provided, and it can make product have nature, simple and unsophisticated, rough bold and unrestrained effect, caters to the modern and returns Piao and return genuine aesthetic psychology; energy savings again simultaneously, cost is lower and be beneficial to environmental protection.
The present invention is achieved in that
A kind of manufacture method of ceramic, this method comprises the step of following order:
1, processing of pottery mud and Mold Making.The prescription of pug is: unselected clay 70-80%, river sand 15-25%, water 3-7%, each component all by weight percentage, through the batching, stirring obtains compliant pottery mud, the diameter of the described river sand grains of sand is not more than 0.2mm.Mould is material with the gypsum, makes by PRODUCT FORM DESIGN.
2, moulding moulage.Pottery mud is put in the gypsum mold,, allowed in the process of greenwave moulding, form the superficial makings of nature by manual pressed compact.
3, in ceramic kiln, greenwave is carried out sintering.Sintering temperature is controlled between 880-920 ℃, time 7.5-8.5 hour.
4, biscuit is carried out incrustation (colouring).Select for use water paint directly to spread upon billet surface, adopt again various decoration techniques as wipe, smear, bat etc., cooperate the superficial makings of biscuit, form and have nature, simple and unsophisticated, rough bold and unrestrained artistic effect.
5, evenly coat marine glue on the pottery surface.
Described water paint is ceramic special-purpose cement paint or emulsion paint for building.Described marine glue is the styrene synthetics.
Pottery of the present invention is adapted at public place and private indoor or gardens decoration use, is particularly suitable for developed country and areas such as America and Europe.
The invention has the beneficial effects as follows:
1, energy savings and resource: product only burns till through 880-920 ℃ of low-temperature primary, and without the secondary calcination, energy consumption is low behind the decoration, and uses unselected clay and river sand not to strive resource with other ceramic products.
2, the cost of material is low: prices such as used raw material such as clay, river sand, ceramic special-purpose cement paint and styrene synthetics are all cheaper, be easy to get.
3, the decoration process of product surface is harmless, can not pollute environment, is more suitable in batch process.
4, product has nature, honest, rough bold and unrestrained artistic effect.
The specific embodiment
Below by example, can do further understanding to the present invention.
The manufacture method of example 1 hand crude pottery flowerpot
(1) processing of pottery mud and Mold Making.In the ratio (percentage by weight) of unselected clay 75%, river sand 20%, water 5% through batching, stirring obtains compliant pottery mud, the diameter of the described river sand grains of sand is not more than 0.2mm.With the gypsum is that raw material is made the mould that can print flowerpot, and described mould can make goods have honest, natural, rough classic moulding, adds smooth graceful clue and pattern and moulds beautiful effect.
(2) moulding moulage.Pottery mud is put in the gypsum mold,, allowed in the process of greenwave moulding, form the superficial makings of nature by manual pressed compact.In the pressed compact process, suitably increase the base wall thickness to strengthen greenwave intensity.After finishing, pressed compact carries out repaired biscuit.
(3) in ceramic kiln, greenwave is carried out sintering.900 ℃ of sintering temperatures, sintering time 8 hours.
(4) biscuit is carried out incrustation (colouring).The ceramic special-purpose cement paint of choosing required color (as yellow, green, pink etc.) directly spreads upon billet surface, adopt again various decoration techniques as wipe, smear, bat etc., the superficial makings that cooperates biscuit, formation has nature, simple and unsophisticated, rough bold and unrestrained artistic style.After decorating (colouring) drying, color deep breath is attached to the surface of base substrate.
(5) evenly be coated with last layer styrene synthetics on the pottery surface in case make moist and the water pouring, promptly make hand crude pottery flowerpot.
The manufacture method of example 2 hand glazed colored pottery flowerpots
Step (1) is with example 1.
Step (2) moulding moulage behind the moulding moulage, is executed enamel on the part surface of greenwave by the requirement of product design pattern with example 1.
Step (3) is with example 1.
When step (4) was carried out incrustation (colouring) to biscuit, no longer colouring of glazing part was only coated ceramic special-purpose cement paint in unglazed part.
Step (5) promptly makes hand glazed colored pottery flowerpot with example 1.
Example 3 hand crude pottery sculptures of animals
Except the made gypsum mold of step (1) is shaped to the animal, other steps so just make hand crude pottery sculpture of animals with example 1.
Claims (3)
1. the manufacture method of a furnishing art pottery is characterized in that, it comprises the following steps:
(1) processing of pottery mud and Mold Making, the prescription of pug is: unselected clay 70-80%, river sand 15-25%, water 3-7%, each component all by weight percentage, the diameter of the river sand grains of sand can not be greater than 0.2mm, through the batching, stirring obtains compliant pottery mud, mould is material with the gypsum, makes by PRODUCT FORM DESIGN;
(2) moulding moulage is put into pottery mud in the gypsum mold, by manual pressed compact, allows in the process of greenwave moulding, forms the superficial makings of nature;
(3) in ceramic kiln greenwave is carried out sintering, sintering temperature is controlled between 880-920 ℃, time 7.5-8.5 hour;
(4) biscuit is carried out the incrustation colouring, select for use water paint directly to spread upon billet surface, cooperate the superficial makings of biscuit, formation has nature, simple and unsophisticated, rough bold and unrestrained artistic effect;
(5) evenly coat marine glue on the pottery surface.
2. the manufacture method of furnishing art pottery according to claim 1 is characterized in that, described water paint is ceramic special-purpose cement paint or emulsion paint for building.
3. the manufacture method of furnishing art pottery according to claim 1 is characterized in that, described marine glue is the styrene synthetics.