CN100366531C - 用煤矸石或电石渣或石灰石利用转炉直接炼电石的方法 - Google Patents

用煤矸石或电石渣或石灰石利用转炉直接炼电石的方法 Download PDF

Info

Publication number
CN100366531C
CN100366531C CNB2006100882642A CN200610088264A CN100366531C CN 100366531 C CN100366531 C CN 100366531C CN B2006100882642 A CNB2006100882642 A CN B2006100882642A CN 200610088264 A CN200610088264 A CN 200610088264A CN 100366531 C CN100366531 C CN 100366531C
Authority
CN
China
Prior art keywords
converter
carbide
coal
iron
parts
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CNB2006100882642A
Other languages
English (en)
Other versions
CN1884066A (zh
Inventor
徐建明
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CNB2006100882642A priority Critical patent/CN100366531C/zh
Publication of CN1884066A publication Critical patent/CN1884066A/zh
Application granted granted Critical
Publication of CN100366531C publication Critical patent/CN100366531C/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种用煤矸石或电石渣或石灰石利用转炉直接炼电石的方法，它是以煤矸石或电石渣或石灰石为主料，配以锰矿石或铁矿石或废钢铁作碳稳定剂，采用转炉顶吹蒸汽或氧气，炉底吹蒸汽或空气或煤气或乙炔气和煤粉的气、粉混合物，制成电石液，该方法的工艺步骤如下：在转炉中，先加入锰矿石或铁矿石或废钢铁，再加入煤矸石或电石渣或石灰石，炉顶吹蒸汽或氧气化渣，炉底吹蒸汽或空气或煤气或乙炔气和煤粉的气、粉混合物，吹炼20～25分钟，温度升高至1600℃以上还原制成电石液。本发明不用电炉，而是采用煤矸石或电石渣或石灰石利用转炉直接炼电石，与传统电炉炼电石方法相比，本发明投资小，能耗低。经测试，本发明可以比传统电炉炼电石方法节能100%～120%。

Description

用煤矸石或电石渣或石灰石利用转炉直接炼电石的方法
技术领域：
本发明涉及一种炼电石的方法。具体涉及一种用煤矸石或电石渣或石灰石利用转炉直接炼电石的方法。属冶金技术领域。
背景技术：
在本发明作出以前，传统炼电石采用的是电炉法：即将石灰块和焦炭块加入电炉内，熔炼成1600℃以上的电石液。该法建电炉的厂房占地面积大，基础工程大，投资量大、用电量大，能耗高。
发明内容：
本发明的目的在于克服上述不足，提供一种投资小、能耗低的用煤矸石或电石渣或石灰石利用转炉直接炼电石的方法。
本发明的目的是这样实现的：一种用煤矸石或电石渣或石灰石利用转炉直接炼电石的方法，其特征在于：它是以煤矸石或电石渣或石灰石为主料，配以锰矿石或铁矿石或废钢铁作碳稳定剂，采用转炉顶吹蒸汽或氧气，炉底吹蒸汽或空气或煤气或乙炔气和煤粉的气、粉混合物，制成电石液，该方法的工艺步骤如下：在转炉中，先加入锰矿石或铁矿石或废钢铁，再加入煤矸石或电石渣或石灰石，炉顶吹蒸汽或氧气化渣，炉底吹蒸汽或煤气或空气或乙炔气和煤粉的气、粉混合物，吹炼20～25分钟，温度升高至1600℃以上还原制成电石液，转炉中各组份的投料重量份为：
煤矸石或电石渣或石灰石100份
锰矿石或铁矿石或废钢铁5～8份
煤粉5～20份。
本发明用煤矸石或电石渣或石灰石利用转炉直接炼电石的方法，所述的转炉中各组份的投料重量份为：
煤矸石100份
锰矿石或铁矿石或废钢铁5～8份
煤粉5～10份。
本发明用煤矸石或电石渣或石灰石利用转炉直接炼电石的方法，所述的转炉中各组份的投料重量份为：
电石渣100份
锰矿石或铁矿石或废钢铁5～8份
煤粉15～20份。
本发明用煤矸石或电石渣或石灰石利用转炉直接炼电石的方法，所述的转炉中各组份的投料重量份为：
石灰石100份
锰矿石或铁矿石或废钢铁5～8份
煤粉15～20份。
本发明不用电炉，而是采用煤矸石或电石渣或石灰石利用转炉直接炼电石，与传统电炉炼电石方法相比，本发明投资小，能耗低。经测试，本发明可以比传统电炉炼电石方法节能100％～120％。
具体实施方式：
实施例1：在转炉中，先加入锰矿石或铁矿石或废钢铁，再加入煤矸石，炉顶吹蒸汽或氧气化渣，炉底吹蒸汽或煤气或空气或乙炔气和煤粉的气、粉混合物，吹炼20～25分钟，温度升高至1600℃以上还原制成电石液，转炉中各组份的投料重量份为：煤矸石100份，锰矿石或铁矿石或废钢铁5～8份，煤粉5～10份。
实施例2：在转炉中，先加入锰矿石或铁矿石或废钢铁，再加入电石渣，炉顶吹蒸汽或氧气化渣，炉底吹蒸汽或煤气或空气或乙炔气和煤粉的气、粉混合物，吹炼20～25分钟，温度升高至1600℃以上还原制成电石液，转炉中各组份的投料重量份为：电石渣100份，锰矿石或铁矿石或废钢铁5～8份，煤粉15～20份。
实施例3：在转炉中，先加入锰矿石或铁矿石或废钢铁，再加入石灰石，炉顶吹蒸汽或氧气化渣，炉底吹蒸汽或煤气或空气或乙炔气和煤粉的气、粉混合物，吹炼20～25分钟，温度升高至1600℃以上还原制成电石液，转炉中各组份的投料重量份为：电石渣100份，锰矿石或铁矿石或废钢铁5～8份，煤粉15～20份。

Claims (4)

1.一种用煤矸石或电石渣或石灰石利用转炉直接炼电石的方法，其特征在于：它是以煤矸石或电石渣或石灰石为主料，配以锰矿石或铁矿石或废钢铁作碳稳定剂，采用转炉顶吹蒸汽或氧气，炉底吹蒸汽或空气或煤气或乙炔气和煤粉的气、粉混合物，制成电石液，该方法的工艺步骤如下：在转炉中，先加入锰矿石或铁矿石或废钢铁，再加入煤矸石或电石渣或石灰石，炉顶吹蒸汽或氧气化渣，炉底吹蒸汽或空气或煤气或乙炔气和煤粉的气、粉混合物，吹炼20～25分钟，温度升高至1600℃以上还原制成电石液，转炉中各组份的投料重量份为：
煤矸石或电石渣或石灰石100份
锰矿石或铁矿石或废钢铁5～8份
煤粉5～20份。
2.根据权利要求1所述的一种用煤矸石或电石渣或石灰石利用转炉直接炼电石的方法，其特征在于：所述的转炉中各组份的投料重量份为：
煤矸石100份
锰矿石或铁矿石或废钢铁5～8
煤粉5～10份。
3.根据权利要求1所述的一种用煤矸石或电石渣或石灰石利用转炉直接炼电石的方法，其特征在于：所述的转炉中各组份的投料重量份为：
电石渣100份
锰矿石或铁矿石或废钢铁5～8份
煤粉15～20份。
4.根据权利要求1所述的一种用煤矸石或电石渣或石灰石利用转炉直接炼电石的方法，其特征在于：所述的转炉中各组份的投料重量份为：
石灰石100份
锰矿石或铁矿石或废钢铁5～8份
煤粉15～20份。
CNB2006100882642A 2006-07-05 2006-07-05 用煤矸石或电石渣或石灰石利用转炉直接炼电石的方法 Expired - Fee Related CN100366531C (zh)