CN100337288C - 无氧铜母线的制备方法 - Google Patents

无氧铜母线的制备方法 Download PDF

Info

Publication number
CN100337288C
CN100337288C CNB2005100408100A CN200510040810A CN100337288C CN 100337288 C CN100337288 C CN 100337288C CN B2005100408100 A CNB2005100408100 A CN B2005100408100A CN 200510040810 A CN200510040810 A CN 200510040810A CN 100337288 C CN100337288 C CN 100337288C
Authority
CN
China
Prior art keywords
copper
oxygen
busbar
cold
free
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CNB2005100408100A
Other languages
English (en)
Other versions
CN1731534A (zh
Inventor
陈希康
冯岳军
刘轶伦
张忠良
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangyin Electrical Alloy Co Ltd
Original Assignee
Jiangyin Electrical Alloy Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangyin Electrical Alloy Co Ltd filed Critical Jiangyin Electrical Alloy Co Ltd
Priority to CNB2005100408100A priority Critical patent/CN100337288C/zh
Publication of CN1731534A publication Critical patent/CN1731534A/zh
Application granted granted Critical
Publication of CN100337288C publication Critical patent/CN100337288C/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种无氧铜母线的制备方法，材料中铜+银含量≥99.96%，氧含量≤0.001%。其制备工艺步骤：一、熔炼：将1#电解铜或阴极铜置于熔烧炉内，并升炉温保持铜液温度1150℃±20℃，铜液表面覆木炭层；二、上引连铸：将中空结晶器直接伸入铜液内，中空结晶器采用水隔套冷却，铜液在中空结晶器内凝结成固体，固体上端用牵伸机构牵伸制作成铜杆；三、连续挤压：将步骤二所得铜杆置于挤压机内连续挤压成坯料；四、冷拔成型：将步骤三所得坯料置于拉拔机上冷拔成型，制成无氧铜母线。本发明氧含量低。

Description

无氧铜母线的制备方法
技术领域：
本发明涉及一种电工用铜母线，具体涉及一种电工用无氧铜母线的制备方法。属电工合金材料技术领域。
背景技术：
铜母线是制作电机电器绕组线圈、高低压电器开关触头及供配电设备安装用导体材料。铜母线按其用途可分软铜母线和硬铜母线。传统的铜母线熔炼工艺采用“下引浇铸”的方法，在浇注时铜液有与氧接触的机会，故对氧含量不能得到控制。因此其含氧量较高，电阻较大，延展性较差，90°弯曲易裂口。对产品的质量带来影响。
发明内容：
本发明的目的在于克服上述不足，提供一种氧含量低的无氧铜母线的制备方法。
本发明的目的是这样实现的：一种无氧铜母线的制备方法，材料中铜+银含量≥99.96％，氧含量≤0.001％，
其制备方法包括以下工艺步骤：
步骤一、熔炼  将1#电解铜或阴极铜置于熔烧炉内，并升炉温保持铜液温度1150℃±20℃，铜液表面覆木炭层，使铜液始终与氧隔离；
步骤二、上引连铸  将中空结晶器直接伸入铜液内，中空结晶器采用水隔套冷却，铜液在中空结晶器内凝结成固体，固体上端用牵伸机构牵伸制作成铜杆；
步骤三、连续挤压  将步骤二所得铜杆置于挤压机内连续挤压成坯料；
步骤四、冷拔成型  将步骤三所得坯料置于拉拔机上冷拔成型，制成无氧铜母线。
由于本发明采用“上引连铸、水隔冷却”的方法，在连铸时铜液没有与氧接触的机会，故对氧含量能得到控制。本发明无氧铜母线是电机和变压器的绕组、高低压电器的较佳材料。其主要技术指标是：
一、材质：铜+银含量≥99.96％，氧含量≤0.001％；
二、机械性能
(1)伸长率≥40％(软无氧铜母线)
(2)抗拉强度≥206N/mm2，表面弯曲不出现裂口或三角口(硬无氧铜母线)
三、电阻
(1)软无氧铜母线电阻率≤0.01710Ω.mm/m2；
(2)硬无氧铜母线电阻率≤0.01760Ω.mm/m2；
四、无氧铜母线产品规格为：
宽度≤120mm，截面(宽×厚)≤1440mm2的各种规格，最大规格12mm×120mm。
与传统的铜母线制备方法相比，本发明具有如下优点：
1、含铜量纯，比普通铜母线纯0.06％；
2、氧含量低，氧含量≤0.001％；
3、电阻较小，导电性能好，比普通铜母线高1％；
4、延伸性大，伸长率比普通铜母线高5％；
具体实施方式：
实施例1：制备软无氧铜母线
步骤一、熔炼  将1#电解铜置于熔烧炉内，并升炉温保持铜液温度1150℃，铜液表面覆木炭层，使铜液始终与氧隔离；
步骤二、上引连铸  将中空结晶器直接伸入铜液内，中空结晶器采用水隔套冷却，铜液在中空结晶器内凝结成固体，固体上端用牵伸机构牵伸制作成铜杆；
步骤三、连续挤压  将步骤二所得铜杆置于挤压机上连续挤压成坯料；
步骤四、冷拔成型  将步骤三所得坯料置于拉拔机上冷拔成型，制成无氧铜母线。
步骤五、真空退火  将步骤四所得无氧铜母线置于真空退火炉内真空退火，退火温度560℃，即得软无氧铜母线。
主要技术指标：
1、材质：铜+银含量＝99.97％，氧含量＝0.00099％；
2、伸长率：42
3、电阻：0.01708Ω.mm/m2；
实施例2：制备硬无氧铜母线
步骤一、熔炼  将阴极铜置于熔烧炉内，并升炉温保持铜液温度1170℃，铜液表面覆木炭层，使铜液始终与氧隔离；
其余步骤同例1。
主要技术指标：
1、材质：铜+银含量＝99.96％，氧含量＝0.001％；
2、抗拉强度：206N/mm2，表面弯曲不出现裂口或三角；
3、电阻：0.01760Ω.mm/m2。

Claims (1)

1、一种无氧铜母线的制备方法，材料中铜+银含量≥99.96％，氧含量≤0.001％，其特征在于它包括以下工艺步骤：
步骤一、熔炼  将1#电解铜或阴极铜置于熔烧炉内，并升炉温保持铜液温度1150℃±20℃，铜液表面覆木炭层；
步骤二、上引连铸  将中空结晶器直接伸入铜液内，中空结晶器采用水隔套冷却，铜液在中空结晶器内凝结成固体，固体上端用牵伸机构牵伸制作成铜杆；
步骤三、连续挤压  将步骤二所得铜杆置于挤压机内连续挤压成坯料；
步骤四、冷拔成型  将步骤三所得坯料置于拉拔机上冷拔成型，制成无氧铜母线。
CNB2005100408100A 2005-06-27 2005-06-27 无氧铜母线的制备方法 Active CN100337288C (zh)