CH718459A2 - Watch or jewelery casing part comprising an interference color coating and method of manufacturing said part. - Google Patents

Abstract

The invention relates to a trim part (10) and its method of manufacture, the trim part comprising a substrate (11) comprising a coating (12) composed of the following successively superposed layers: a reflective layer (121) opaque or semi-opaque, configured to have a reflectance of at least 90% for wavelengths between 600 nm and 780 nm, a transparent (122) or semi-transparent layer, having a refractive index between 1.45 and 2.8 for a wavelength of 630 nm, an absorber layer (123), said layers providing the coating (12) with a predetermined interference color.

Description

Technical field of the invention

[0001] The invention relates to the field of watchmaking or jewelry, and relates more particularly to a watchmaking or jewelry casing part comprising a coating giving an interference color, and a process for manufacturing said part.

[0002] In the present text, the term "covering parts" designates any decorative article in the fields of watchmaking or jewelry, for example consisting of a case, a dial, a dial applique, a bracelet, etc intended to be visible to a user.

[0003]Preferably, the present invention relates to a watch or jewelery casing part comprising a coating whose interference color is a shade of red.

Technology background

[0004] In the field of watchmaking or jewelry, and more generally in that of decorative articles, the processes of deposition by painting, varnishing or enameling are not always suitable.

[0005] Indeed, on the one hand, the layer of material applied to the surface of an article to be decorated is too thick to reveal any surface structuring, for example a brushed, sunray, sandblasted, laser structured surface. , etc., and on the other hand, the lifetime of this layer and consequently of its color is not always satisfactory.

Thus, vacuum thin layer deposition techniques, such as physical vapor deposition processes (known by the acronym in English "PVD" for "Physical Vapor Deposition"), chemical deposition processes vapor phase (known by the acronym in English language "CVD" for "Chemical Vapor Deposition"), atomic layer deposition processes (known by the acronym in English language "ALD" for Atomic Layer Deposition), are preferred .

[0007] However, despite the fact that these deposition techniques make it possible to obtain coatings of a multitude of colors, the implementation of these processes does not make it possible to obtain certain specific colors industrially, such as the shades of red.

Summary of the invention

The invention solves the aforementioned drawbacks by proposing a solution making it possible to produce a trim part having a predetermined interference color resulting from an addition of destructive interference and constructive interference. In the present text, the term “interferential color” is used for a color generated by an optical phenomenon of interference.

To this end, the present invention relates to a trim part comprising a substrate comprising a coating composed of the following successively superimposed layers: an opaque or semi-opaque reflective layer, configured to have a reflectance of at least 90% for wavelengths between 600 nm and 780 nm, a transparent or semi-transparent layer, having a refractive index between 1.45 and 2.8 for a wavelength of 630 nm, an absorbent layer.

Said layers give the coating a predetermined interference color.

[0011] Advantageously, the predetermined color is a shade of red with a metallic sheen. More specifically, the predetermined color is a shade of burgundy red or purple red. This predetermined color is obtained thanks to the particular arrangement of the optical stack defined by the layers of the coating.

[0012] In addition, the coating has a very small thickness, typically less than 3 μm, which makes it possible to be suitable for covering any decorative article comprising a surface structuring or comprising a complex geometric shape.

Another advantage of the present invention lies in the fact that it makes it possible to obtain a very wide variety of shades of red without substantially modifying the thickness of the coating. By way of example, the thickness of the coating varies at most by a value of less than 3 nm between all the shades of red that said coating may exhibit.

[0014] In particular embodiments, the invention may also comprise one or more of the following characteristics, taken in isolation or in all technically possible combinations.

[0015] In particular embodiments, the reflective layer is made of a metallic material chosen from copper (Cu), gold (Au), rhodium (Rh), platinum (Pt).

[0016] In particular embodiments, the reflective layer is made of Cu.

In particular embodiments, the reflective layer has a thickness of at least 40 nm.

In particular embodiments, the reflective layer has a thickness of 100 nm.

In particular embodiments, the transparent layer is made of a material chosen from silicon dioxide (SiO2), titanium dioxide (TiO2), alumina (Al2O3), hafnium dioxide (HfO2 ), zirconium dioxide (ZrO2), tantalum oxide (Ta2O5), tin dioxide (SnO2), indium tin oxide (ITO), zinc oxide (ZnO), l magnesium oxide (MgO), silicon nitride (Si3N4) and aluminum nitride (AlN).

[0020] In particular embodiments, the transparent layer is made of SiO2.

In particular embodiments, the transparent layer has a thickness of between 10 nm and 50 nm.

In particular embodiments, the transparent layer has a thickness of 30 nm.

In particular embodiments, the absorbent layer is made of a material chosen from: titanium (Ti), nickel (Ni) or chromium (Cr).

In particular embodiments, the absorbent layer is made of Cr.

[0025] In particular embodiments, the absorbent layer comprises a thickness of between 5 nm and 8 nm.

In particular embodiments, the coating has a reflection rate of less than 10% for wavelengths between 350 nm and 600 nm, and greater than or equal to 10% for wavelengths between 620nm and 780nm.

In particular embodiments, the coating has a red color characterized in the CIELAB chromatic space, illuminating D65, by an L* parameter comprised between 25 and 35, an a* parameter comprised between 8 and 15, and a b* parameter between 0 and 7.

In particular embodiments, the coating comprises an acrylic and/or nitrocellulose protective layer superimposed on the absorbent layer and having a refractive index between 1.48 and 1.51 for a wavelength of 630 nm.

[0029] According to another object, the present invention relates to a method for manufacturing a watch or jewelery casing part, characterized in that it comprises the following successive steps of generating a coating on a surface of a substrate: depositing an opaque reflective layer on a substrate, said layer being configured to have a reflectance of at least 90% for wavelengths between 600 nm and 780 nm, deposition of a transparent layer having a refractive index between 1.45 and 2.8 at 630 nm, deposition of an absorbent layer.

[0030] In particular embodiments, the deposition of the reflective, transparent and absorbent layers is carried out by a process of physical vapor deposition by evaporation by electron gun.

In particular embodiments, the step of depositing the transparent layer is carried out with a deposition rate of between 0.01 nm/s and 0.1 nm/s.

In particular embodiments, the step of depositing the absorbent layer is carried out with a deposition rate of between 0.01 nm/s and 0.05 nm/s.

In particular embodiments, the method comprises a final step of depositing a protective layer configured to advantageously include a refractive index of between 1.48 and 1.51 for a wavelength of 630 nm.

Brief description of figures

Other characteristics and advantages of the invention will appear on reading the following detailed description given by way of non-limiting example, with reference to the appended drawings in which: FIG. 1 schematically represents a sectional view of a trim piece according to a preferred embodiment of the invention; FIG. 2 represents a spectral reflectance curve measured with a spectrocolorimeter on a coating according to the invention; FIG. 3 represents a curve of spectral reflectance measured with a spectrocolorimeter on a coating according to the invention further comprising a protective layer; FIG. 4 represents a flowchart of a method of manufacturing a trim part according to another aspect of the invention.

Detailed description of the invention

The present invention relates to a covering part 10 comprising a substrate 11 comprising a coating 12 composed of several successively superimposed layers making it possible to confer on the covering part, on a surface intended to be visible to a user, an interference color predetermined.

[0036] Preferably, the predetermined interference color is a shade of red.

The substrate 11 can be made of a metallic, ceramic or polymer material. Furthermore, it can be coated with a galvanic underlayer.

On the substrate 11 is deposited a reflective layer 121, opaque or semi-opaque, configured to reflect wavelengths between 600 nm and 780 nm.

More specifically, the reflective layer 121 preferably has a reflection coefficient greater than 0.9 for wavelengths between 600 nm and 780 nm.

[0040] The reflective layer 121 can be semi-opaque in the sense that it can have a non-zero transmittance, however, the transmittance must remain less than or equal to 15% over the range of wavelengths of the visible spectrum.

This reflective layer 121 is preferably made of metallic material and has a thickness of at least 40 nm.

Preferably, the reflective layer 121 is made of a material which is chosen from: Cu, Au, Rh or Pt. The material of the reflective layer 121 is chosen for its optical capacity to reflect wavelengths between 600 nm and 780 nm, this interval being representative of shades of red in the light spectrum. In addition, this material is chosen for its low absorption of wavelengths in the red.

More preferably still, the reflective layer 121 is made of Cu, in particular for economic reasons and ease of implementation.

The reflective layer 121 can be produced by a PVD process, by galvanizing or by any other suitable process for depositing a thin layer.

A transparent layer 122 is superimposed on the reflective layer 121.

The transparent layer 122 can also be semi-transparent in the sense that it can absorb light over a certain range of wavelengths, for example wavelengths below 500 nm in the case where said transparent layer 122 is made of TiO2, and be transparent to light over another range of wavelengths.

The material of this transparent layer 122 is chosen for its optical properties of transparency. By way of example, the transparent layer 122 is made of a material chosen from: SiO2, TiO2, Al2O3, HfO2, ZrO2, Ta2O5, SnO2, ITO, ZnO, MgO, Si3N4, AlN. Preferably, the transparent layer 122 is made of SiO2, in particular for economic reasons, ease of implementation and repeatability.

For example, the transparent layer 122 advantageously has a refractive index of between 1.45 and 2.8 for a wavelength of 630 nm and has a thickness of between 10 nm and 50 nm, depending on the refractive index of this last.

The transparent layer 122 can be deposited on the reflective layer 121 by PVD, CVD, ALD process, or by any other suitable thin layer deposition process.

Finally, as shown in Figure 1, an absorbent layer is superimposed on the transparent layer 122.

This absorbent layer 123 is made of a metallic material, chosen for its optical absorption properties. By way of example, the absorbent layer 123 is made of Ti, Ni or Cr. Preferably, the absorbent layer 123 is made of chromium.

The absorbent layer 123 has a thickness comprised between 4 nm and 10 nm, preferentially between 5 nm and 8 nm, and even more preferentially between 7.2 nm and 7.8 nm.

It is understood here that the present invention makes it possible, thanks to the coating 12, to advantageously obtain an interference color in a shade of red, said coating 12 having a very small thickness, of the order of a few thousandths of a millimeter, more precisely less than 3 µm.

The coating 12 is advantageously configured, thanks to the aforementioned characteristics, so as to have a reflection rate of less than 10%, varying from 8% to 3%, for wavelengths between 350 nm and 580 nm, and evolving from 3% to 24% for wavelengths between 580 nm and 750 nm. These values are represented graphically by the spectral reflectance curve in FIG. 2, resulting from measurements carried out with a spectrocolorimeter on coating 12.

These reflection rates can advantageously define a reflection spectrum representative of a user's visual perception of a color included in a shade of red.

In a preferred embodiment of the invention, the coating 12 can also advantageously comprise a protective layer 124, acrylic and / or nitrocellulose, superimposed on the absorbent layer 123, in order to protect the other layers from possible chemical and/or mechanical attacks.

The addition of such a protective layer 124, for example with a thickness of 3 μm with a refractive index close to 1.5, for example between 1.48 and 1.51 for wavelengths of 630 nm, also makes it possible to generate destructive interference which advantageously decreases the reflection rate between 350 nm and 550 nm leaving the wavelengths between 580 nm and 780 nm define the color of the coating 12.

In other words, in the preferred embodiment of the invention, the protective layer 124 advantageously participates in obtaining the final red color of the coating 12.

With the protective layer 124, the coating 12 has a reflection rate less than or equal to 5% in the range of wavelengths between 350 nm and 550 nm, changing from 5 to 21% for lengths d waves between 550 nm and 750 nm. These values are represented graphically by the spectral reflectance curve in FIG. 3, resulting from measurements carried out with a spectrocolorimeter on coating 12.

Thus, in the preferred embodiment of the invention, the coating 12 has a red color characterized in the CIELAB chromatic space, illuminating D65, by a parameter L* between 25 and 35, a parameter a* between 8 and 15, and a parameter b* between 0 and 7.

It should be noted that the protective layer 124 is not essential, and that in other embodiments of the invention, the coating 12 may have a red color characterized in the CIELAB chromatic space by example by the aforementioned parameters, without said protective layer 124.

[0062] The present invention also relates to a method of manufacturing a trim part 10 for timepieces or jewelry, for example as described above. The successive steps of this method are represented by the flowchart of FIG. 4 and consist of the generation of a coating 12 on a surface of a substrate 11 in order to generate a predetermined interference color.

More specifically, the method comprises the following successive steps: deposition 101 of an opaque reflective layer 121 on a substrate 11, said layer being adapted to reflect wavelengths between 600 nm and 780 nm, deposition 102 of a transparent layer 122 having a refractive index between 1.45 and 2.8 for a wavelength of 630 nm, deposit 103 of an absorbent layer 123.

An example of a manufacturing process described in detail below uses a vacuum deposition technique to deposit the reflective 121, transparent 122 and absorbent 123 layers.

More particularly, in a preferred embodiment, an electron gun evaporation physical vapor deposition process is used.

However, it should be noted that the deposition of the layers can be carried out by other PVD methods, such as magnetron sputtering in reactive media, or by CVD process, such as the ALD process and chemical vapor deposition. plasma assisted (known by the English language acronym PECVD for „Plasma Enhanced Chemical Vapor Deposition“).

The deposition 101 of the reflective layer 121 is carried out, for example so that said reflective layer 121 has a thickness of 100 nm. Preferably, among the following materials that can be envisaged to constitute the reflective layer 121: Cu, Au, Rh or Pt, Cu is preferred.

The transparent layer 122 is then deposited on the reflective layer 121, preferably so as to have a thickness of 30 nm. Preferably, among the following materials that can be envisaged to constitute the transparent layer 122: SiO2, TiO2, Al2O3, HfO2, ZrO2, Ta2O5, SnO2, ITO, ZnO, MgO, Si3N4, or AlN, SiO2 is preferred.

By way of example, in order to obtain good repeatability for the deposition of the transparent layer 122, the deposition rate is chosen between 0.01 nm/s and 0.1 nm/s, preferably 0.1 nm/s, and the flux of oxygen (02) is 5 sccm. These parameters also make it possible to obtain very precise control of the density of material and of the thickness of the transparent layer 122.

The absorbent layer 123 is then deposited on the transparent layer 122, preferentially so as to have a thickness comprised for example between 5 nm and 8 nm, preferentially between 7.2 nm and 7.8 nm. Preferably, the absorbent layer 123 is made of chromium.

By way of example, in order to obtain good repeatability for the deposition of the absorbent layer 123, the deposition rate is chosen between 0.01 nm/s and 0.05 nm/s, preferably 0.02 nm/s, and the flow of argon (Ar) is 2 sccm so as to minimize the influence of the fouling of the walls of the enclosure on the repeatability of the deposition of the absorbent layer 123.

In a preferred example of implementation of the invention, the manufacturing method also includes a final step 104 of depositing a protective layer 124. This protective layer 124 is configured to advantageously include a refractive index approximately between 1.48 and 1.51 for a wavelength of 630 nm.

Claims (20)

1. Trim part (10) characterized in that it comprises a substrate (11) comprising a coating (12) composed of the following successively superimposed layers: – an opaque or semi-opaque reflective layer (121), configured to have a reflectance of at least 90% for wavelengths between 600 nm and 780 nm, – a transparent layer (122) or semi-transparent, having a refractive index between 1.45 and 2.8 for a wavelength of 630 nm, – an absorbent layer (123), said layers imparting to the coating (12) a predetermined interference color. 2. Trim part (10) according to claim 1, in which the reflective layer (121) is made of a metallic material chosen from: Cu, Au, Rh, Pt. 3. trim piece (10) according to claim 1 or 2, wherein the reflective layer (121) is made of Cu. 4. Trim part (10) according to one of claims 1 to 3, wherein the reflective layer (121) has a thickness of at least 40 nm. 5. trim piece (10) according to claim 4, wherein the reflective layer (121) has a thickness of 100 nm. 6. Trim part (10) according to one of claims 1 to 5, wherein the transparent layer (122) is made of a material chosen from: SiO2, TiO2, Al2O3, Hf02, ZrO2, Ta2O5, SnO2, ITO , ZnO, MgO, Si3N4, AlN. 7. trim piece (10) according to claim 6, wherein the transparent layer (122) is made of Si02. 8. Trim part (10) according to one of claims 1 to 7, wherein the transparent layer (122) has a thickness of between 10 nm and 50 nm. 9. Trim part (10) according to claim 8, wherein the transparent layer (122) has a thickness of 30 nm. 10. Trim part (10) according to one of claims 1 to 9, wherein the absorbent layer (123) is made of a material chosen from: Ti, Ni or Cr. 11. Trim piece (10) according to claim 10, wherein the absorbent layer (123) is made of Cr. 12. Trim part (10) according to one of claims 1 to 11, wherein the absorbent layer (123) has a thickness of between 5 nm and 8 nm. 13. Trim part (10) according to one of claims 1 to 12, in which the coating (12) has a reflection rate of less than 10% for wavelengths between 350 nm and 600 nm, and greater than or equal to 10% for wavelengths between 620 nm and 780 nm. 14. Trim part (10) according to one of claims 1 to 13, in which the coating (12) has a red color characterized in the CIELAB chromatic space, illuminating D65, by a parameter L* of between 25 and 35, an a* parameter between 8 and 15, and a b* parameter between 0 and 7. 15. Trim part (10) according to one of claims 1 to 14, wherein the coating (12) comprises an acrylic and/or nitrocellulose protective layer (124) superimposed on the absorbent layer (123) and having a refractive index between 1.48 and 1.51 for a wavelength of 630 nm. 16. Method for manufacturing a watch or jewelery covering part (10), characterized in that it comprises the following successive steps of generating a coating (12) on a surface of a substrate (11 ): – deposition 101 of an opaque reflective layer (121) on a substrate (11), said layer being configured to have a reflectance greater than 90% for wavelengths between 600 nm and 780 nm, – deposition 102 of a transparent layer (122) having a refractive index between 1.45 and 2.8 for a wavelength of 630 nm, – deposit 103 of an absorbent layer (123). 17. Manufacturing process according to claim 16, in which the deposition 101, 102 and 103 respectively of the reflective (121), transparent (122) and absorbent (123) layers is carried out by a physical vapor deposition process by evaporation by electron gun. 18. Manufacturing method according to one of claims 16 or 17 wherein the step 102 of depositing the transparent layer (122) is carried out with a deposition rate of between 0.01 nm/s and 0.1 nm/s. 19. Manufacturing method according to one of claims 16 to 18 wherein the step 103 of depositing the absorbent layer (123) is carried out with a deposition rate of between 0.01 nm/s and 0.05 nm/s. 20. Manufacturing process according to one of claims 16 to 19, comprising a final step 104 of depositing a protective layer (124) configured to advantageously comprise a refractive index of between 1.48 and 1.51 for a wavelength equal to 630 nm.