CH682551A5 - Verbundelement. - Google Patents
Verbundelement. Download PDFInfo
- Publication number
- CH682551A5 CH682551A5 CH3944/90A CH394490A CH682551A5 CH 682551 A5 CH682551 A5 CH 682551A5 CH 3944/90 A CH3944/90 A CH 3944/90A CH 394490 A CH394490 A CH 394490A CH 682551 A5 CH682551 A5 CH 682551A5
- Authority
- CH
- Switzerland
- Prior art keywords
- composite element
- fiber
- covered
- core material
- metal cladding
- Prior art date
Description
1
CH 682 551 A5
2
Beschreibung
Die Erfindung betrifft ein Verbundeiement nach dem Oberbegriff des Patentanspruchs 1. Dieses Verbundelement soll lärm- und wärmedämmend sein und als Boden- oder Wandelement eingesetzt werden können.
Aus der FR-A 2 195 744 ist ein derartiges Verbundelement bekannt, bei dem ein Kernmaterial ober- und unterseitig mit einer Platte abgedeckt ist, wobei auf die obere Platte ein Bodenbelag aufgeklebt ist.
Das separate Aufkleben eines Belages, einer Schutz- oder Dekorbeschichtung ist ein zusätzlicher Arbeitsschritt bei der Herstellung derartiger Verbundelemente, der abgesehen von der zusätzlichen Kleberschicht in der Platte unwirtschaftlich ist.
Es wird die Schaffung eines Verbundelementes bezweckt, bei dem der vorerwähnte Nachteil vermieden werden kann.
Die erfindungsgemässe Ausbildung des Verbundelementes ergibt sich aus dem kennzeichnenden Teil des Patentanspruchs 1.
Im folgenden wird die Erfindung anhand der Abbildung eines Ausführungsbeispiels dargelegt.
Ein Verbundelement besteht aus einem Kernmaterial, das ober- und unterseitig mit einer faserverstärkten Platte 2 und 3 aus einem thermoplastischen Material abgedeckt ist, wobei die obere faserverstärkte Platte 3 aus einem thermoplastischen Material mit einer BeSchichtung 4 versehen ist und die Beschichtung 4 ohne Kleber mit der faserverstärkten Platte 3 verbunden ist. Die nicht mit einer Platte abgedeckten Seiten des Kernmaterials sind mit einer Metallverkleidung 5 abgedeckt. Die Metallverkleidung bildet gewissermassen einen Rahmen, der mit den faserverstärkten Platten 2 und 3 innig verankert ist. Dies wird dadurch erreicht, dass die Metallverkleidung 5 breiter ist als die Dicke des Kernmaterials 1 und in Höhe der faserverstärkten Platten 2 und 3 rechtwinklig abgewinkelt ist, wobei die abgewinkelten Metallflächen auf den ober- und unterseitigen Randzonen des Kernmaterials 1 liegen und von den faserverstärkten Platten 2 und 3 überdeckt und mit diesen verbunden sind. Dieser Verbund wird dadurch verbessert, dass die Metallverkleidung 5 gelocht ist. Eine weitere Verbesserung des Verbundes ist dadurch gegeben, dass die Löcher in der Metallverkleidung 5 Durchreisslöcher sind.
Eine andere Möglichkeit, des innigen Verbundes zwischen den faserverstärkten Platten 2, 3 und der Metallverkleidung 5 besteht darin, dass Platten eingesetzt werden, die grösser sind als die ober- und unterseitige Fläche des Verbundelementes und wenn die überstehenden Flächen der faserverstärkten Platten aus einem thermoplastischen Material während des Herstellungsprozesses in plastischem Zustand in Richtung der Metallverkleidung 5 abgewinkelt und an diese angepresst werden.
In beiden Fällen ist die Metallverkleidung 5 ohne zusätzlichen Kleber mit dem übrigen Verbundelement verbunden.
Das verwendete Kernmaterial 1 ist ein hohlraumreiches Material, bevorzugt ein Schaum oder ein Wabenelement mit beliebiger Wabengeometrie aus
üblichen Werkstoffen vorzugsweise aus Papier, Pappe oder Holz, wobei diese Werkstoffe gegebenenfalls mit Harzen oder sonstigen die Festigkeit und/oder Beständigkeit erhöhenden Mitteln ausgerüstet sein können; es ist aber auch eine Kombination eines Wabenelementes mit Schaum oder einer hohlraumreichen Schüttung möglich. Um die Feuerwiderstandsfähigkeit des erläuterten Verbundelementes zu verbessern ist das Kernmaterial 1 flammwidrig ausgerüstet, entweder dadurch, dass Schaum oder Wabenmaterial aus einem flammfesten Material bestehen, oder dass das Wabenmaterial mit flammwidrigen Substanzen, etwa üblichen Feuerschutzsalzen oder -harzen imprägniert oder beschichtet ist, oder dadurch, dass in den Wabenkammern flammwidriges Material eingeschlossen ist. Die Dicke des Kernmaterials 1 liegt im Bereich von 40 bis 100 mm, bevorzugt im Bereich von 45 bis 55 mm.
Als faserverstärkte Platte 2, 3 aus thermoplastischem Material sind alle Platten einsetzbar, die aus einem thermoplastischen Kunststoff bestehen der mit Fasergewebe, Faservlies oder mit statistisch in der Kunststoffmatrix verteilte Fasern verstärkt ist.
Derartige Platten 2, 3 haben eine Dicke von 2 bis 5 mm, bevorzugt von 2, 3 bis 4 mm. Beispiele für thermoplastische Kunststoffe sind Polyolefine wie z.B. Polyethylen, Polypropylen und deren Gemische, ferner Polyvinylverbindungen sowie Copoly-merisate wie ABS oder SAN, Polyamide, Polyaceta-le, Polycarbonate oder Polyester. Beispiele für Fasermaterial sind Cellulose, Kohlenstoff-, Kunststoff-, Glas-, Mineral- oder Keramikfasern.
Bevorzugt verwendet werden glasfaserverstärkte Platten 2, 3 aus Polyolefinen, insbesondere aus Polypropylen. Derartige Platten sind als sogenannte GMT-Platten im Handel.
Die Beschichtung 4 ist ohne Kleber mit der faserverstärkten Platte 3 verbunden, d.h. sie ist direkt mit der Matrix des Thermoplasten verankert. Daher sind als Beschichtung 4 alle Materialien geeignet, deren dem Kunststoff zugeneigte Seite nicht glatt ist, die somit eine mechanische Verankerung in der thermoplastischen Kunststoffmatrix ermöglichen. Beispiele hierfür sind Gewebe, Holz, Kork, Filz oder mineralische Materialien, insbesondere Fliesen oder Mineralgranulat. Als Beschichtung 4 einsetzbar sind aber auch Verbundwerkstoffe, die eine poröse oder rauhe Fläche besitzen wie z.B. Linoleum oder Kunststeinplatten mit einer Unterseite aus Mineralgranulat oder Blähton.
Die erläuterten Verbundelemente können beliebige äussere Abmessungen haben. Bevorzugte Abmessungen sind 60 x 60 cm bzw. 60 x 120 cm.
Claims (7)
1. Verbundelement, bestehend aus einem Kernmaterial (1), das ober- und unterseitig mit einer faserverstärkten Platte (2, 3) aus einem thermoplastischen Material abgedeckt ist, wobei die obere faserverstärkte Platte (3) mit einer Beschichtung (4) versehen ist, dadurch gekennzeichnet, dass die Beschichtung (4) ohne Kleber mit der oberen faserverstärkten Platte (3) verbunden ist.
5
10
15
20
25
30
35
40
45
50
55
60
65
2
3
CH 682 551 A5
2. Verbundelement nach Anspruch 1, dadurch gekennzeichnet, dass die nicht mit einer faserverstärkten Platte aus einem thermoplastischen Material abgedeckten Seiten des Kernmaterials (1) mit einer Metallverkleidung (5) abgedeckt sind.
3. Verbundelement nach Anspruch 2, dadurch gekennzeichnet, dass die Metallverkleidung (5) ohne zusätzlichen Kleber mit dem übrigen Verbundelement verbunden ist.
4. Verbundelement nach Anspruch 2 oder 3, dadurch gekennzeichnet, dass die Metallverkleidung (5) gelocht ist.
5. Verbundelement nach Anspruch 4, dadurch gekennzeichnet, dass die Löcher in der Metallverkleidung (5) Durchreisslöcher sind.
6. Verbundelement nach einem der Ansprüche 1 bis 5, dadurch gekennzeichnet, dass das Kemmate-rial (1) ein Wabenelement ist.
7. Verbundelement nach einem der Ansprüche 1 bis 6, dadurch gekennzeichnet, dass das Kernmaterial (1) flammwidrig ausgerüstet ist.
5
10
15
20
25
30
35
40
45
50
55
60
65
3