CA2989710A1 - Bande d'acier galvanise a chaud a haute resistance - Google Patents

Bande d'acier galvanise a chaud a haute resistance Download PDF

Info

Publication number
CA2989710A1
CA2989710A1 CA2989710A CA2989710A CA2989710A1 CA 2989710 A1 CA2989710 A1 CA 2989710A1 CA 2989710 A CA2989710 A CA 2989710A CA 2989710 A CA2989710 A CA 2989710A CA 2989710 A1 CA2989710 A1 CA 2989710A1
Authority
CA
Canada
Prior art keywords
temperature
strip
steel strip
hot dip
steel
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
CA2989710A
Other languages
English (en)
Inventor
Joost Willem Hendrik Van Krevel
Cornelia IONESCU
Bernard Leo Ennis
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Tata Steel Ijmuiden BV
Original Assignee
Tata Steel Ijmuiden BV
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Tata Steel Ijmuiden BV filed Critical Tata Steel Ijmuiden BV
Publication of CA2989710A1 publication Critical patent/CA2989710A1/fr
Abandoned legal-status Critical Current

Abstract

L'invention concerne une bande d'acier galvanisé à chaud à haute résistance comprenant, en pourcentage, les éléments suivants : de 0,10 à 0,21 % de C, de 1,75 à 2,50 % de Mn, de 0,04 à 0,60 % de Si, de 0,20 à 1,40 % d'Al, de 0,001 à 0,025 % de P, de 0,0005 à 0,0050 % de B, 0,50 % de Cr maximum, 0,20 % de Ti maximum, 0,004 % de Ca maximum, 0,015 % de N maximum, le reste étant constitué de Fe et d'impuretés inévitables.
CA2989710A 2015-07-01 2016-06-24 Bande d'acier galvanise a chaud a haute resistance Abandoned CA2989710A1 (fr)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
EPEP15020109.3 2015-07-01
EP15020109 2015-07-01
PCT/EP2016/064704 WO2017001303A1 (fr) 2015-07-01 2016-06-24 Bande d'acier galvanisé à chaud à haute résistance

Publications (1)

Publication Number Publication Date
CA2989710A1 true CA2989710A1 (fr) 2017-01-05

Family

ID=53783025

Family Applications (1)

Application Number Title Priority Date Filing Date
CA2989710A Abandoned CA2989710A1 (fr) 2015-07-01 2016-06-24 Bande d'acier galvanise a chaud a haute resistance

Country Status (9)

Country Link
US (1) US20180230570A1 (fr)
JP (1) JP2018524471A (fr)
KR (1) KR20180025852A (fr)
CN (1) CN107787375A (fr)
BR (1) BR112017023814A2 (fr)
CA (1) CA2989710A1 (fr)
MX (1) MX2017016843A (fr)
WO (1) WO2017001303A1 (fr)
ZA (1) ZA201707294B (fr)

Families Citing this family (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
BR112018011831B1 (pt) 2015-12-15 2022-11-29 Tata Steel Ijmuiden Bv Tira de aço galvanizada por imersão a quente de alta resistência e método de produção
WO2020058330A1 (fr) * 2018-09-19 2020-03-26 Sms Group Gmbh Acier avancé à haute limite d'élasticité, bande en acier composée de cet acier ainsi que procédé pour la fabrication d'une bande en acier
WO2020221628A1 (fr) * 2019-04-30 2020-11-05 Tata Steel Ijmuiden B.V. Procédé de production d'une bande laminée sur mesure à recuit discontinu
WO2020245627A1 (fr) * 2019-06-03 2020-12-10 Arcelormittal Tôle d'acier laminée à froid et revêtue et son procédé de fabrication
WO2020245626A1 (fr) * 2019-06-03 2020-12-10 Arcelormittal Tôle d'acier laminée à froid et revêtue et son procédé de fabrication
DE102020110319A1 (de) 2020-04-15 2021-10-21 Salzgitter Flachstahl Gmbh Verfahren zur Herstellung eines Stahlbandes mit einem Mehrphasengefüge und Stahlband hinzu
CN113355604B (zh) * 2021-06-25 2022-05-24 攀钢集团攀枝花钢铁研究院有限公司 低成本700MPa级热镀锌复相钢板及其制备方法
CN117802400A (zh) * 2022-09-23 2024-04-02 宝山钢铁股份有限公司 一种低点焊裂纹敏感性的带镀层超高强钢及其制造方法

Family Cites Families (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20080175743A1 (en) * 2005-03-31 2008-07-24 Jfr Steel Corporation, A Corporation Of Japan Alloyed Hot-Dip Galvanized Steel Sheet and Method of Producing the Same
CN101151392A (zh) * 2005-03-31 2008-03-26 杰富意钢铁株式会社 合金化热镀锌钢板及其制造方法
JP5250939B2 (ja) * 2005-03-31 2013-07-31 Ｊｆｅスチール株式会社 合金化溶融亜鉛めっき鋼板の製造方法
EP2009128A1 (fr) * 2007-06-29 2008-12-31 ArcelorMittal France Acier au silicium galvanisé ou recuit après galvanisation
US8882938B2 (en) * 2009-12-21 2014-11-11 Tata Steel Ijmuiden B.V. High strength hot dip galvanised steel strip
US9228244B2 (en) * 2010-03-31 2016-01-05 Nippon Steel & Sumitomo Metal Corporation High strength, hot dipped galvanized steel sheet excellent in shapeability and method of production of same
JP2014531511A (ja) * 2011-09-13 2014-11-27 タタ、スティール、アイモイデン、ベスローテン、フェンノートシャップＴａｔａ Ｓｔｅｅｌ Ｉｊｍｕｉｄｅｎ Ｂｖ 高強度溶融亜鉛メッキ鋼帯
KR20150132208A (ko) * 2013-03-11 2015-11-25 타타 스틸 이즈무이덴 베.뷔. 고강도 용융 침지 아연도금 복합상 강 스트립
BR112018011831B1 (pt) * 2015-12-15 2022-11-29 Tata Steel Ijmuiden Bv Tira de aço galvanizada por imersão a quente de alta resistência e método de produção

Also Published As

Publication number Publication date
CN107787375A (zh) 2018-03-09
US20180230570A1 (en) 2018-08-16
MX2017016843A (es) 2018-04-24
ZA201707294B (en) 2019-02-27
BR112017023814A2 (pt) 2018-07-31
JP2018524471A (ja) 2018-08-30
WO2017001303A1 (fr) 2017-01-05
KR20180025852A (ko) 2018-03-09

Similar Documents

Publication Publication Date Title
CA2989710A1 (fr) Bande d'acier galvanise a chaud a haute resistance
CA3047690C (fr) Tole d'acier trempee et revetue et son procede de fabrication
CN108367539B (zh) 高强度热浸镀锌钢带材
US20120018058A1 (en) Process for manufacturing a cold rolled trip steel product
RU2686729C2 (ru) Способ производства высокопрочного стального листа с покрытием, обладающего высокой прочностью, пластичностью и формуемостью
EP2768989B1 (fr) Acier en bandes galvanisé à chaud à haute résistance
CA3047945A1 (fr) Tole d'acier trempe revetue douee d'une excellente aptitude au formage et son procede de fabrication
CA2903916A1 (fr) Bande d'acier haute resistance, a phase complexe et galvanisee a chaud
CA3110822C (fr) Tole d'acier laminee a chaud et son procede de fabrication
KR20130099138A (ko) 복합조직강, 복합조직강으로 제조된 냉연 평판 제품 및 제조 방법
CA2825240A1 (fr) Produit plat en acier lamine a chaud fabrique a partir d'un acier a phase complexe et procede de fabrication correspondant
ES2929345T3 (es) Acero de alta resistencia con propiedades mecánicas mejoradas
KR20170086062A (ko) 우수한 가공 특성을 갖는 고강도의 공기 경화 다상 강 및 상기 강으로부터 강 스트립을 제조하기 위한 방법
KR20170084210A (ko) 탁월한 가공 특성을 갖는 초고강도의 공기 경화 다상 강 및 상기 강의 스트립을 제조하기 위한 방법
JP6830468B2 (ja) 熱間形成性空気焼き入れ性溶接性鋼板
CA3081941C (fr) Tole d'acier laminee a froid et revetue et son procede de fabrication
JP2022501503A (ja) 穴広げ率の高い熱間圧延鋼板及びその製造方法
CA3157208C (fr) Feuille d'acier laminee a chaud et traitee thermiquement et procede de fabrication de cette derniere
JP2007063604A (ja) 伸びと穴拡げ性に優れた溶融亜鉛めっき高強度鋼板およびその製造方法
EP3390040B2 (fr) Bande d'acier galvanisé à chaud haute résistance
JP4788291B2 (ja) 伸びフランジ成形性に優れた高強度溶融亜鉛めっき鋼板の製造方法
EP3317431B1 (fr) Bande d'acier galvanisé à chaud haute résistance
CA3138625A1 (fr) Tole d'acier laminee a froid et revetue et son procede de fabrication
KR100978734B1 (ko) 복합조직강판 및 이를 제조하는 방법
US20230026116A1 (en) Steel sheet for a structure with excellent seawater corrosion resistance and method of manufacturing same

Legal Events

Date Code Title Description
EEER Examination request

Effective date: 20171215

FZDE Discontinued

Effective date: 20210831

FZDE Discontinued

Effective date: 20210831