BE485212A - - Google Patents

Info

Publication number
BE485212A
BE485212A BE485212DA BE485212A BE 485212 A BE485212 A BE 485212A BE 485212D A BE485212D A BE 485212DA BE 485212 A BE485212 A BE 485212A
Authority
BE
Belgium
Prior art keywords
loss
low
electrodes
loss material
high frequency
Prior art date
Application number
Other languages
English (en)
Publication date
Publication of BE485212A publication Critical patent/BE485212A/fr

Description


   <Desc/Clms Page number 1> 
 



   PROCEDE DE SOUDURE A HAUTE   FREQUENCE   DES MATIERES A FAIBLES PERTES   DIELECTRIQUES.   



   La présente invention se rapporte à aes méthodes et appa- reils pour le chauffage à haute fréquence, et plus particulière- ment pour le   ohaufiage   et la soudure de matières thermoplastiques ayant des pertes diélectriques relativement faibles. 



   Plusieurs matériaux ont été traités et préparés   pour   être utilisés dans les installations électroniques, ces matériaux oonservant de bonnes propriétés diélectriques aux fréquences ultra-élevées. Certains de ces matériaux offrent des propriétés de grande utilité du fait qu'ils peuvent présenter une bonne transparence, une bonne résistance et une granae durabilité, mais le travail de ces matières pour un emploi journalier ordinaire présente cependant quelques difficultés. 



   A titre d'exemple on peut citer le polyéthylène qui s'a- dapte bien à un emploi sous forme de feuilles pour la   fabrioa-   tion de sacs ou autres récipients servant à contenir des aliments. 

 <Desc/Clms Page number 2> 

 cependant la souaure de cette matière pour la formation de ces récipients présente certaines difficultés.   'application   d'un   ohaufiage   ordinaire n'est pas satisfaisante tandis que les pro- priétes diélectriques de cette matière n'ont pas jusqu'à présent permis l'emploi d'appareils commerciaux ordinaires à haute fré- quence.   j'emploi   d'éléments intermédiaires de soucure ou plas- tifiants a été trouvé préjudiciable, car ils peuvent contaniner la matière contenue par le rédpient. 



   Un des buts ae la présente invention est de prévoir une   méthoce   et des appareils par lesquels des matières de raible perte   diélectrique   peuvent être soudées ou autrement réunies par l'emploi d'appareils de chauffage à haute fréquence fonc- tionnant à des fréquences qui jusqu'à présent n'étaient pas suffisamment élevées pour obtenir ladite soudure. 



   Un autre but de l'invention est d'effectuer cette soudure sans l'emploi de substances intermédiaires ou plastifiants. 



   D'une manière générale, les buts envisagés sont réalisés dans la présente   invention   en plaçant une matière à perte rela- tivement élevée en contact aveo une matière de faible perte devant être Soudée, cette matière à perte élevée devant être chauffée au moyen d'électrodes convenables à haute fréquence, tandis qu'une pression simultanée est appliquée à la partie de la matière à faible perte qui doit être soudée.

   Ces divers points   caractéris-   tiques et d'autres points non spécialement mentionnés ioi, ainsi que la manière pour atteindre ces buts apparaîtront mieux de la description détaillée suivante d'une forme de réalisation de l'invention prise en connexion aveo le dessin ci-joint sur lequel la figure montre différents détails d'un appareil de chauffage à haute fréquence oonforme à l'invention. 



   Suivant la figure, une source d'énergie à haute fréquence est indiquée en 1, cette source étant montrée sohématiquement oomme connectée à une paire d'électrodes à haute fréquence 2 et 3. A l'exception des détails mentionnés par la suite, ces électrodes, 

 <Desc/Clms Page number 3> 

 ainsi que l'appareil à haute fréquence dans son ensemble, peu- vent être de forme et de dimensions ordinaires, les dimensions des électrodes, comme par exemple leur longueur, variant en conoordance avec les dimensions des pièces pour lesquelles elles doivent être utilisées. Cependant, suivant la présente invention, au moins une des électrodes, par exemple l'électrode 2, peut être formée d'une section élargie 4 recouverte tout d'abord d'une couohe de matière isolante à chaud 5 qui présente des caractéristiques de perte relativement faibles aux fréquences employées.

   Sur cette section est placée une autre cache de matière ayant des   oaracté-   ristiques de pertes élevées. Dans l'exemple montré, ces deux cou- ches sont attachées à l'électrodes 2 au moyen de vis de fixation 7 placées sur le côté de l'électrode qui est éloigné de l'électrode opposée 3. L'électrode 3 peut être constituée au moyen de cou- ches semblables et dans ce cas la matière devant être sondée,, oonsistant par exemple en des bords de recouvrement 8 et 9 d'une matière quelconque à faible perte, sera placée entre les reoou- vrements à perte élevée des deux électrodes opposées et en con- tact avec eux. 



   On doit comprendre que l'appareil de chauffage de la pré- sente invention est adapté pour fonctionner à de hautes fréquen- ces commerciales telles que celles utilisées actuellement et qui peuvent être produites économiquement par des appareils relati- vement simples. Par exemple, une bande de fréquences aux envi- rons de 20 mégacycles peut Être utilisée. Cependant, à ces fré- quenoes la matières à faible perte, telles que le polyéthylène, ne sont pas chauffées quand elles sont placées entre les éleotro- des.

   Par suite de la position intermédiaire des couches de ma- tières à perte élevée 6 qui sont chauffées pour les bandes de haute fréquence commercialement utilisées, une ohaleur suffisante est produite dans les matières à perte élevée à leur surface de contact aveo la matière à faible perte pour faire fondre cette dernière et produire une bonne soudure et de bon joint entre les deux bords de ladite matière. On a constaté que le chauffage 

 <Desc/Clms Page number 4> 

 direct de la matière à faible perte par la matière à perte éle- vée produit une soudure convenable entre les ceux couches de ma- tières à faible perte, mais on a aussi constaté que le chauffage de la matière à faible perte affecte d'une manière préjudiciable ses propriétés diélectriques.

   De cette manière il est très pos- sible que réchauffement de la matière à faible perte par la ma- tière à perte élevée peut aussi diminuer les propriétés diéleo- triques de la première de telle sorte que cette matière à faible perte peut être directement chauffée par le courant à haute fré- quence passant entre les deux éleotrodes. On ne sait pas si cette dernière aotion a lieu dans tous les cas, mais l'excellente qua- lité du joint obtenu suivant la présente méthode tend à confirmer cette possibilité dans certaines circonstances. 



   Le but de la couche isolante à faible perte entre les éleo- trodes et son recouvrement à perte élevée est de concentrer la chaleur sur la matière devant être isolée. Suivant l'énergie et les fréquences utilisées, ainsi que suivant la constante diélec- trique relative entre la matière à faible perte travaillée et le recouvrement à perte élevée, cette couohe isolante peut être omise d'une ou des deux électrodes. 



   En pratique, la présente invention avec les appareils oi-dessus décrits suppose qu'une ou les deux électrodes sont déplacées afin de comprimer la pièce travaillée entre-elles, et la pression ainsi appliquée est de préférence maintenue   perdent   un court espace de temps après que l'application des oourants à haute fréquence a cesse. Ceoi permet la soudure à froid sous pression et ainsi permet de réaliser un joint plus effectif. 



   Cependant la durée totale nécessaire, comprenant le main- tien de la pression après que le oourant à haute fréquence a été coupé, est jugée extrêmement courte et peut ne pas dépasser plus de 2 secondes pour une soudure complète. 



   L'interposition de la couohe isolante 5 aide au refroidis- sement rapide du reoouvrement à perte élevée 6, qui est ramené à la température normale, presque immédiatement après l'interruption 

 <Desc/Clms Page number 5> 

 du courant haute fréquence. 



   Bien qu'une forme préférée de réalisation de l'électrode à haute fréquence avec des recouvrements isolants et à perte élevée a été montrée à titre d'exemple, l'invention n'est nulle- ment limitée à cette forme particulière d'électrode, car il est clair que cette électrode avec ses oouohes additionnelles peut avoir, tout en restant conforme à l'invention, une forme conve- nable quelconque. 



   A titre d'exemple spécifique de l'invention, on peut no- ter que la couche isolante 5 peut consister en une mince feuille de papier huilé tandis que le reoouvrement à perte élevée qui fait contact aveo les   minc-es   couches de polyéthylène peut tire formé de fibrophénol. En plus du polyéthylène, la matière tra- vaillée peut comprendre d'autres matières à faible perte, telles que par exemple des polystyrènes, tandis que des expériences ont indiqué que le recouvrement a perte élevée peut être fait de chlorure de polyvynil.

   Sous son aspeot général, l'invention est applicable ?our la soudure ou la réunion de plusieurs matériaux dont les constantes diélectriques sont telles,qu' ils ne réa- gissent pas aux   finances   appliquées, tandis que d'autre part une ou plusieurs des électrodes sont   reoouvertes   d'une matière ayant une perte plus élevée que la matière devant être Boudée, les propriétés diélectriques de cette matière à perte élevée réa- gissant aux fréquences appliquées.

   Il est aussi nécessaire qu'il n'y ait auoune compatibilité entre le reoouvrement à perte élevée et la pièce travaillée à faible perte de manière que les deux matières ne collent pas ensemble quand la seconde est chauffée par la première. bien qu'on ait déorit ci-dessus les principes de l'inven- tion en connexion avec des appareils bien spécifies et conformé- ment à certaines mpthodes, il est évident que cette description est simplement donnée à titre d'exemple et ne limite en aucune façon la portée de l'invention.

Claims (1)

  1. RESUME L'invention se rapporte à des méthodes et appareils pour le chauffage à haute rréquence et la soudure de matières thermo- plastiques ayant des pertes diélectriques relativement faibles.
    L'invention est caractérisée par les faits suivants pris ensem- ble ou séparément : 1) Appareillage à haute fréquence pour la soudure de ma- tières thermoplastiques ayant une perte diélectrique relativement faible, comprenant une paire d'électrodes entre lesquelles ladite matière est placée, et une matière ayant une perte diélectrique relativement élevée en contact avec ladite matière à faible perte et placée entre les électrodes, de telle sorte que le chauffage de la matière à perte élevée par les électrodes produit le chauf- fage et la s oudure de la matière à faibleperte.
    2) Appareillage dans lequel la matière à perte élevée est attachée à et soutenue par une on deux des électrodes et est en contact avec une ou deux des surfaces opposées de la matière à faiblee perte.
    3) Appareillage dans lequel on a prévu une couche de ma- tière isolante pour la ohaleur et à faible perte, placée entre une on les deux couches de matière à perte élevée d'une part et l'électrode correspondante d'autre part.
    4) Appareillage dans lequel une on deux des électrodes peuvent 8tre déplacées dans la direction de la matière à faible perte destinée à être soudée, afin de comprimer la matière à faible perte.
    5) Méthode pour souder une matière à perte relativement faible, comprenant un chauffage à haute fréquence d'une matière à perte relativement élevée en contact avec la matière à faible perte.
BE485212D BE485212A (fr)