AT307369B - Verfahren zur Herstellung von Whiskers aus Siliciumcarbid - Google Patents
Verfahren zur Herstellung von Whiskers aus SiliciumcarbidInfo
- Publication number
- AT307369B AT307369B AT68671A AT68671A AT307369B AT 307369 B AT307369 B AT 307369B AT 68671 A AT68671 A AT 68671A AT 68671 A AT68671 A AT 68671A AT 307369 B AT307369 B AT 307369B
- Authority
- AT
- Austria
- Prior art keywords
- whiskers
- production
- silicon carbide
- carbide
- silicon
- Prior art date
Links
Classifications
-
- C—CHEMISTRY; METALLURGY
- C30—CRYSTAL GROWTH
- C30B—SINGLE-CRYSTAL GROWTH; UNIDIRECTIONAL SOLIDIFICATION OF EUTECTIC MATERIAL OR UNIDIRECTIONAL DEMIXING OF EUTECTOID MATERIAL; REFINING BY ZONE-MELTING OF MATERIAL; PRODUCTION OF A HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; SINGLE CRYSTALS OR HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; AFTER-TREATMENT OF SINGLE CRYSTALS OR A HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; APPARATUS THEREFOR
- C30B25/00—Single-crystal growth by chemical reaction of reactive gases, e.g. chemical vapour-deposition growth
- C30B25/005—Growth of whiskers or needles
-
- C—CHEMISTRY; METALLURGY
- C30—CRYSTAL GROWTH
- C30B—SINGLE-CRYSTAL GROWTH; UNIDIRECTIONAL SOLIDIFICATION OF EUTECTIC MATERIAL OR UNIDIRECTIONAL DEMIXING OF EUTECTOID MATERIAL; REFINING BY ZONE-MELTING OF MATERIAL; PRODUCTION OF A HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; SINGLE CRYSTALS OR HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; AFTER-TREATMENT OF SINGLE CRYSTALS OR A HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; APPARATUS THEREFOR
- C30B25/00—Single-crystal growth by chemical reaction of reactive gases, e.g. chemical vapour-deposition growth
- C30B25/02—Epitaxial-layer growth
- C30B25/12—Substrate holders or susceptors
Landscapes
- Chemical & Material Sciences (AREA)
- Chemical Kinetics & Catalysis (AREA)
- General Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Crystallography & Structural Chemistry (AREA)
- Materials Engineering (AREA)
- Metallurgy (AREA)
- Organic Chemistry (AREA)
- Crystals, And After-Treatments Of Crystals (AREA)
- Paints Or Removers (AREA)
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
CH719170A CH525711A (de) | 1970-05-14 | 1970-05-14 | Verfahren zur Herstellung von Whiskers |
Publications (1)
Publication Number | Publication Date |
---|---|
AT307369B true AT307369B (de) | 1973-05-25 |
Family
ID=4321309
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
AT68671A AT307369B (de) | 1970-05-14 | 1971-01-28 | Verfahren zur Herstellung von Whiskers aus Siliciumcarbid |
Country Status (12)
Country | Link |
---|---|
US (1) | US3778296A (de) |
AT (1) | AT307369B (de) |
BE (1) | BE767030A (de) |
CH (1) | CH525711A (de) |
DE (1) | DE2122386A1 (de) |
ES (1) | ES388121A1 (de) |
FR (1) | FR2091412A5 (de) |
GB (1) | GB1292422A (de) |
NL (1) | NL7106611A (de) |
NO (1) | NO128900B (de) |
SE (1) | SE368556B (de) |
SU (1) | SU396862A3 (de) |
Families Citing this family (11)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4054635A (en) * | 1974-09-26 | 1977-10-18 | American Can Company | Copolymer of glycidyl methacrylate and allyl glycidyl ether |
USRE32843E (en) * | 1984-02-09 | 1989-01-24 | Martin Marietta Energy Systems, Inc. | Silicon carbide whisker reinforced ceramic composites and method for making same |
USRE34446E (en) * | 1984-02-09 | 1993-11-16 | Martin Marietta Energy Systems, Inc. | Silicon carbide whisker reinforced ceramic composites and method for making same |
US4543345A (en) * | 1984-02-09 | 1985-09-24 | The United States Of America As Represented By The Department Of Energy | Silicon carbide whisker reinforced ceramic composites and method for making same |
US4961757A (en) * | 1985-03-14 | 1990-10-09 | Advanced Composite Materials Corporation | Reinforced ceramic cutting tools |
US4789277A (en) * | 1986-02-18 | 1988-12-06 | Advanced Composite Materials Corporation | Method of cutting using silicon carbide whisker reinforced ceramic cutting tools |
US4789536A (en) * | 1987-01-20 | 1988-12-06 | J. M. Huber Corporation | Process for producing silicon carbide whiskers |
US4911781A (en) * | 1987-05-05 | 1990-03-27 | The Standard Oil Company | VLS Fiber growth process |
US5037626A (en) * | 1988-11-22 | 1991-08-06 | Union Oil Company Of California | Process for producing silicon carbide whiskers using seeding agent |
US5221526A (en) * | 1991-05-24 | 1993-06-22 | Advanced Industrial Materials | Production of silicon carbide whiskers using a seeding component to determine shape and size of whiskers |
SE507706C2 (sv) * | 1994-01-21 | 1998-07-06 | Sandvik Ab | Kiselkarbidwhiskerförstärkt oxidbaserat keramiskt skär |
-
1970
- 1970-05-14 CH CH719170A patent/CH525711A/de not_active IP Right Cessation
-
1971
- 1971-01-11 GB GB0239/71A patent/GB1292422A/en not_active Expired
- 1971-01-28 AT AT68671A patent/AT307369B/de not_active IP Right Cessation
- 1971-02-10 ES ES388121A patent/ES388121A1/es not_active Expired
- 1971-02-26 NO NO00725/71A patent/NO128900B/no unknown
- 1971-05-04 SE SE05781/71A patent/SE368556B/xx unknown
- 1971-05-04 US US00140270A patent/US3778296A/en not_active Expired - Lifetime
- 1971-05-06 DE DE19712122386 patent/DE2122386A1/de active Pending
- 1971-05-10 FR FR7116849A patent/FR2091412A5/fr not_active Expired
- 1971-05-11 BE BE767030A patent/BE767030A/xx unknown
- 1971-05-12 SU SU1658471A patent/SU396862A3/ru active
- 1971-05-13 NL NL7106611A patent/NL7106611A/xx unknown
Also Published As
Publication number | Publication date |
---|---|
GB1292422A (en) | 1972-10-11 |
ES388121A1 (es) | 1974-02-16 |
US3778296A (en) | 1973-12-11 |
FR2091412A5 (de) | 1972-01-14 |
BE767030A (fr) | 1971-11-12 |
NL7106611A (de) | 1971-11-16 |
SE368556B (de) | 1974-07-08 |
SU396862A3 (de) | 1973-08-29 |
DE2122386A1 (de) | 1971-11-25 |
CH525711A (de) | 1972-07-31 |
NO128900B (de) | 1974-01-28 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
AT299124B (de) | Verfahren zur Herstellung von drahtförmigen Körpern, sogenannten Haarkristallen, kreisförmigen Querschnittes, die aus Siliziumkarbid-Einkristallen bestehen | |
AT297659B (de) | Verfahren zur Herstellung von Siliziumkarbidkristallen | |
AT317820B (de) | Verfahren zur Herstellung von hochbelastbarem Feindraht | |
AT320409B (de) | Verfahren zur Herstellung von Würzmitteln | |
AT277161B (de) | Verfahren zur Herstellung von Siliziumkarbidkristallen | |
AT307369B (de) | Verfahren zur Herstellung von Whiskers aus Siliciumcarbid | |
CH535329A (de) | Verfahren zur Herstellung von Strassendeckenmaterialien | |
AT315722B (de) | Verfahren zur Herstellung von keramischen Erzeugnissen | |
AT317169B (de) | Verfahren zur Herstellung von Sobrerol | |
CH494198A (de) | Verfahren zur Herstellung von Siliciumcarbidkörpern | |
AT302247B (de) | Verfahren zur Herstellung von Siliciumcarbidwhiskers | |
AT308075B (de) | Verfahren zur Herstellung von Monochlorbenzaldehyden | |
AT313878B (de) | Verfahren zur Herstellung von Alkylophenolen | |
AT313250B (de) | Verfahren zur Herstellung von Acrylnitril | |
AT300818B (de) | Verfahren zur Herstellung von reinem Hexetidin | |
AT313862B (de) | Verfahren zur Herstellung von Isopentanhydroperoxyd aus Isopentan | |
AT310769B (de) | Verfahren zur Herstellung von ɛ-Caprolacton | |
CH544575A (de) | Verfahren zur Herstellung von faserförmigem Siliciumcarbid | |
AT324546B (de) | Verfahren zur herstellung von aminopenicillinen | |
AT307418B (de) | Verfahren zur Herstellung von neuem 8-Cyano-5-octanolid | |
CH553236A (de) | Verfahren zur herstellung von formteilen aus polyamiden | |
AT291194B (de) | Verfahren zur Herstellung von Siliziumcarbidkristallen | |
AT305131B (de) | Verfahren zur Herstellung von gesinterten Formkörpern aus Bornitrid | |
AT306105B (de) | Verfahren zur Herstellung von Hohlkörpern aus Halbleitermaterial | |
CH510328A (de) | Verfahren zur Herstellung hochohmiger Siliziumkarbid-Dioden |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
ELJ | Ceased due to non-payment of the annual fee |