WO2025239368A1 - 高屈折率硬化性組成物、及び高屈折率硬化物 - Google Patents

高屈折率硬化性組成物、及び高屈折率硬化物

Info

Publication number
WO2025239368A1
WO2025239368A1 PCT/JP2025/017442 JP2025017442W WO2025239368A1 WO 2025239368 A1 WO2025239368 A1 WO 2025239368A1 JP 2025017442 W JP2025017442 W JP 2025017442W WO 2025239368 A1 WO2025239368 A1 WO 2025239368A1
Authority
WO
WIPO (PCT)
Prior art keywords
refractive index
high refractive
mass
curable composition
meth
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
PCT/JP2025/017442
Other languages
English (en)
French (fr)
Inventor
沙梨 山口
健 野口
隼輔 津田
秀次 波木
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dexerials Corp
Original Assignee
Dexerials Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dexerials Corp filed Critical Dexerials Corp
Publication of WO2025239368A1 publication Critical patent/WO2025239368A1/ja
Pending legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

下記一般式（１）で表される多官能（メタ）アクリレート化合物（Ａ）と、ナフタレン骨格を有する単官能（メタ）アクリレート化合物（Ｂ）と、無機ナノ粒子と、重合開始剤と、を含有する高屈折率硬化性組成物である。

Description

高屈折率硬化性組成物、及び高屈折率硬化物
　本発明は、高屈折率硬化性組成物、及び高屈折率硬化物に関する。
　太陽電池、レンズ等の光学素子、コーティング膜等の光学部品において、高い屈折率を有する材料を用いたコーティング、及び高屈折率層用の樹脂組成物が知られている。
　これまでに、複合体コーティングにおいて、アクリルまたはメタクリルモノマーまたはオリゴマー由来の繰り返し単位を有する高分子を含む高分子網目構造を有する樹脂、および前記樹脂内に配置された無機ナノ粒子、を含み、１．７超の屈折率および６０℃超のガラス転移温度を有する複合体コーティングが報告されている（例えば、特許文献１参照）。
特表２０１９－５３３０４０号公報
　しかしながら、更なる高屈折率化が実現でき、高ガラス転移温度、及び優れた透明性を兼ね備える高屈折率硬化物を製造可能な高屈折率硬化性組成物が要望されている。
　本発明は、従来における前記諸問題を解決し、以下の目的を達成することを課題とする。即ち、本発明は、高屈折率、高ガラス転移温度、及び優れた透明性を兼ね備える高屈折率硬化物を製造可能な高屈折率硬化性組成物を提供することを目的とする。
　前記課題を解決するための手段としては、以下の通りである。即ち、
　＜１＞　下記一般式（１）で表される多官能（メタ）アクリレート化合物（Ａ）と、
　ナフタレン骨格を有する単官能（メタ）アクリレート化合物（Ｂ）と、
　無機ナノ粒子と、
　重合開始剤と、を含有することを特徴とする高屈折率硬化性組成物である。
　前記一般式（１）中、Ｒ１は各々独立に水素又はメチル基を表し、ｌ、ｍ、ｎ、ｏ、ｐ、ｑ、ｒ、ｓ、ｔ、ｕ、ｖ及びｗは各々独立に０～１０までの整数であり、ａ及びｃは１であり、ｂ及びｄは各々独立に０又は１であり、ａ＋ｂ＋ｃ＋ｄが２、３又は４である。
　＜２＞　その他の（メタ）アクリレート化合物（Ｃ）を更に含有する前記＜１＞に記載の高屈折率硬化性組成物である。
　＜３＞　前記多官能（メタ）アクリレート化合物（Ａ）と前記単官能（メタ）アクリレート化合物（Ｂ）との質量比（Ａ／Ｂ）が、１／９９～７０／３０である前記＜１＞又は＜２＞に記載の高屈折率硬化性組成物である。
　＜４＞　前記多官能（メタ）アクリレート化合物（Ａ）及び前記単官能（メタ）アクリレート化合物（Ｂ）の合計含有量が、１５質量％以上４５質量％以下である前記＜１＞から＜３＞のいずれかに記載の高屈折率硬化性組成物である。
　＜５＞　前記無機ナノ粒子の含有量が、５５質量％以上８５質量％以下である前記＜１＞から＜４＞のいずれかに記載の高屈折率硬化性組成物である。
　＜６＞　前記無機ナノ粒子が、酸化チタンである前記＜１＞から＜５＞のいずれかに記載の高屈折率硬化性組成物である。
　＜７＞　前記無機ナノ粒子の粒子径が、１ｎｍ以上１００ｎｍ以下である前記＜１＞から＜６＞のいずれかに記載の高屈折率硬化性組成物である。
　＜８＞　前記＜１＞から＜７＞のいずれかに記載の高屈折率硬化性組成物を光硬化してなることを特徴とする高屈折率硬化物である。
　＜９＞　波長６３６ｎｍにおける屈折率ｎが、１．８０以上である前記＜８＞に記載の高屈折率硬化物である。
　＜１０＞　示差走査熱量測定により測定したガラス転移温度が、６０℃以上である前記＜８＞又は＜９＞に記載の高屈折率硬化物である。
　＜１１＞　ヘーズが、１．０以下である前記＜８＞から＜１０＞のいずれかに記載の高屈折率硬化物である。
　本発明によれば、従来における前記諸問題を解決し、前記目的を達成することができ、高屈折率、高ガラス転移温度、及び優れた透明性を兼ね備える高屈折率硬化物を製造可能な高屈折率硬化性組成物を提供することができる。
（高屈折率硬化性組成物）
　本実施形態の高屈折率硬化性組成物は、下記一般式（１）で表される多官能（メタ）アクリレート化合物（Ａ）と、ナフタレン骨格を有する単官能（メタ）アクリレート化合物（Ｂ）と、無機ナノ粒子と、重合開始剤と、を含み、更に必要に応じて、他の（メタ）アクリレート化合物（Ｃ）、溶媒などのその他の成分を含む。
　光学製品では光の反射、屈折を利用した技術が多く存在しており、屈折の作用には屈折率が大きく特性に影響する。
　非常に高い光学特性が要求される光トランシーバー等に用いられるコリメートレンズについては、ガラスのモールド成形による非球面レンズが主流となっている。屈折率が１．８以上の高屈折率であり、収差が小さい高品質なレンズを生産できることが特徴であるが、ガラスを用いることによる成形プロセスにおける高温及び冷却処理による金型の劣化などの生産コストや光トランシーバー小型化トレンドに伴う小型レンズ設計が困難であることが課題となっている。代替の手法として、樹脂組成物を用いたナノインプリントによる製造プロセスが検討されている。
　このような用途に用いる樹脂を高屈折率化するための手法としては、屈折率の高い化学構造を導入する方法がある。化学構造の具体例としては、フェニル基、硫黄などが挙げられる（例えば、特許文献１参照）。しかしながら、屈折率が高く、剛直な化学構造を多く導入した樹脂単独からなる高屈折率材料では、熱可塑性がなく成型加工が困難となる問題がある（例えば、文献：東工大院理工　東原ら　高分子学会　予稿　２０１１）。そのため、単独の樹脂で、屈折率１．８以上かつ易成形性を達成することが困難であり、利用可能な樹脂が存在しないのが実情である。
　高屈折率化の他の手法としては、樹脂に屈折率の高い金属酸化物ナノ粒子を添加する複合材料とする方法がある。しかしながら、易成形性を有する樹脂は屈折率が比較的低いことから、更なる高屈折率化には金属酸化物ナノ粒子を多量に添加する必要があり、複合材料の高ガラス転移温度や透明性を両立することが困難であるという問題がある。
　そのため、依然として、高屈折率、高ガラス転移温度、及び優れた透明性を兼ね備える高屈折率硬化物を製造可能な高屈折率硬化性組成物の開発が求められている。
　本発明者らは、前記従来における諸問題を解決し、前記目的を解決すべく、鋭意検討した結果、前記高屈折率硬化性組成物が、高屈折率、高ガラス転移温度、及び優れた透明性を兼ね備える高屈折率硬化物を製造可能であることを見出し、本発明の完成に至った。
　本実施形態の高屈折率硬化性組成物によれば、より剛直なナフタレン構造を主骨格とした多官能（メタ）アクリレート化合物（Ａ）を含有することで、高屈折率モノマーと配合及び硬化した際に屈折率の低下を抑制しながら樹脂の架橋密度を向上させることができる。また、有機材料よりも高屈折率を示す金属ナノ粒子を含有することで、更なる高屈折率化を達成できる。また、易成形性を有し、比較的高屈折率の単官能（メタ）アクリレート化合物（Ｂ）と配合することで、高屈折率、及び透明性を両立した高屈折率硬化物を製造できる高屈折率硬化性組成物を得ることができる。
＜多官能（メタ）アクリレート化合物（Ａ）＞
　前記多官能（メタ）アクリレート化合物（Ａ）は、下記一般式（１）で表され、ナフタレン骨格と、２官能～４官能の（メタ）アクリレート基と、を有する多官能（メタ）アクリレート化合物である。
　前記一般式（１）中、Ｒ１は各々独立に水素又はメチル基を表し、ｌ、ｍ、ｎ、ｏ、ｐ、ｑ、ｒ、ｓ、ｔ、ｕ、ｖ及びｗは各々独立に０～１０までの整数であり、ａ及びｃは１であり、ｂ及びｄは各々独立に０又は１であり、ａ＋ｂ＋ｃ＋ｄが２、３又は４である。
　置換基ａ及び置換基ｃは、それぞれ添え字ａ及びｃが１であり、置換基ａ及び置換基ｃが存在すると定義される。
　置換基ｂ及び置換基ｄは、それぞれ添え字ｂ及びｄが１であるときに存在すると定義され、０（ゼロ）であるときに存在しないと定義される。
　ａ＋ｂ＋ｃ＋ｄが２、３又は４である。言い換えると、前記多官能（メタ）アクリレート化合物（Ａ）は、２官能～４官能の（メタ）アクリレート化合物である。
　ａ＋ｂ＋ｃ＋ｄとしては、２又は３が好ましく、２がより好ましい。
　前記一般式（１）における置換基ａ及び置換基ｃは、互いに同一であってもよく、互いに異なっていてもよいが、前記多官能（メタ）アクリレート化合物（Ａ）の分子非対称性を有し、前記高屈折率硬化性組成物における前記多官能（メタ）アクリレート化合物（Ａ）の含有量を増加でき、より高屈折率及び高Ｔｇ化できる点で、互いに異なることが好ましい。
　置換基ｂ及び／又は置換基ｄが存在する場合、置換基ｂ及び／又は置換基ｄは、置換基ａ及び／又は置換基ｃと互いに同一であってもよく、互いに異なっていてもよい。
　各置換基ａ、ｂ、ｃ、及びｄにおいて、前記ｌ、ｍ、ｎ、ｏ、ｐ、ｑ、ｒ、ｓ、ｔ、ｕ、ｖ及びｗは各々独立に０～１０の整数である。
　前記ｌ、ｍ、ｎ、ｏ、ｐ、ｑ、ｒ、ｓ、ｔ、ｕ、ｖ及びｗとしては、各々独立に、０～５が好ましく、０～３がより好ましく、０～２が更に好ましい。
　前記多官能（メタ）アクリレート化合物（Ａ）としては、特に制限はなく、目的に応じて適宜選択することができ、例えば、以下の構造式で表される、２，７－ナフタレンジアクリレート（前記一般式（１）において、（ａ，ｂ，ｃ，ｄ）＝（１，０，１，０）、置換基ａ及びｃにおいてｌ＝ｍ＝ｎ＝ｒ＝ｓ＝ｔ＝０、Ｒ１＝Ｈ）；２（２－アクリロイル（７－（アクリロイルオキシ）エトキシ）ナフタレン（前記一般式（１）において、（ａ，ｂ，ｃ，ｄ）＝（１，０，１，０）、置換基ａにおいてｌ＝ｍ＝ｎ＝０、Ｒ１＝Ｈ、置換基ｃにおいてｒ＝０、ｔ＝１、ｓ＝２、Ｒ１＝Ｈ）などが挙げられる。
　前記多官能（メタ）アクリレート化合物（Ａ）の合成方法としては、特に制限はなく、目的に応じて適宜選択することができ、例えば、２官能～４官能のヒドロキシナフタレンを、必要に応じて、置換基ａ、ｂ、ｃ及びｄの部分構造を有し、Ｘ－｛（ＣＨ２）ｌ－｛Ｏ－（ＣＨ２）ｎ｝ｍ｝－ＯＨ等で表されるハロゲン化アルコールと反応させ、次いで、Ｘ－ＣＯ－ＣＲ１＝ＣＨ２で表されるハロゲン化（メタ）アクリル酸（例えば、アクリル酸クロリド）と反応させて合成する方法などが挙げられる。
　なお、Ｘは、Ｃｌ、Ｂｒ、Ｉ等のハロゲンを示す。
　前記多官能（メタ）アクリレート化合物（Ａ）の含有量としては、特に制限はなく、目的に応じて適宜選択することができるが、前記高屈折率硬化性組成物における重合性化合物の総量に対し、１質量％以上７０質量％以下が好ましく、１質量％以上５０質量％以下、１質量％以上４０質量％以下、及び５質量％以上４０質量％以下のいずれかがより好ましく、１０質量％以上３５質量％以下が更に好ましい。
　前記重合性化合物は、前記多官能（メタ）アクリレート化合物（Ａ）、及び前記単官能（メタ）アクリレート化合物（Ｂ）を含み、更に必要に応じて他の（メタ）アクリレート化合物（Ｃ）、その他の重合性化合物を含む成分である。
＜単官能（メタ）アクリレート化合物（Ｂ）＞
　前記単官能（メタ）アクリレート化合物（Ｂ）は、ナフタレン骨格と、１官能の（メタ）アクリレート基と、を有する単官能（メタ）アクリレート化合物である。
　前記単官能（メタ）アクリレート化合物（Ｂ）は、下記一般式（２）で表される化合物であることが好ましい。
　前記一般式（２）中、Ｒ１は各々独立に水素又はメチル基を表し、ｌ、ｍ、及びｎは各々独立に０～１０までの整数である。
　前記ｌ、ｍ、及びｎは各々独立に０～１０の整数である。
　前記ｌは、０～５が好ましく、０～３がより好ましく、０～２が更に好ましい。
　前記ｍは、０～５が好ましく、０～３がより好ましく、０～２が更に好ましい。
　前記ｎは、０～５が好ましく、０～３がより好ましく、０～２が更に好ましい。
　前記単官能（メタ）アクリレート化合物（Ｂ）としては、特に制限はなく、目的に応じて適宜選択することができ、例えば、１－ナフタレンメチルアクリレート（ＮＭＴ－Ａ；前記一般式（２）において、ｌ＝１、ｎ＝ｍ＝０、Ｒ１＝Ｈ）などが挙げられる。
　前記単官能（メタ）アクリレート化合物（Ｂ）の含有量としては、特に制限はなく、目的に応じて適宜選択することができるが、前記高屈折率硬化性組成物における重合性化合物の総量に対し、３０質量％以上９９質量％以下が好ましく、４０質量％以上９９質量％以下がより好ましく、５０質量％以上９９質量％以下が更に好ましく、６０質量％以上９９質量％以下が特に好ましい。
　前記多官能（メタ）アクリレート化合物（Ａ）と前記単官能（メタ）アクリレート化合物（Ｂ）との質量比（Ａ／Ｂ）としては、特に制限はなく、目的に応じて適宜選択することができるが、１／９９～７０／３０が好ましく、１／９９～５０／５０、１／９９～４０／６０、及び５／９５～４０／６０のいずれかがより好ましく、１０／９０～３５／６５が更に好ましい。
　前記多官能（メタ）アクリレート化合物（Ａ）及び前記単官能（メタ）アクリレート化合物（Ｂ）の合計含有量としては、特に制限はなく、目的に応じて適宜選択することができるが、１５質量％以上４５質量％以下が好ましく、１５質量％以上４０質量％以下がより好ましく、２０質量％以上３０質量％以下が更に好ましい。
＜他の（メタ）アクリレート化合物（Ｃ）＞
　前記高屈折率硬化性組成物は、必要に応じて、他の（メタ）アクリレート化合物（Ｃ）を含有してもよい。
　前記他の（メタ）アクリレート化合物（Ｃ）としては、前記多官能（メタ）アクリレート化合物（Ａ）及び前記単官能（メタ）アクリレート化合物（Ｂ）以外の、（メタ）アクリレート基を有する（メタ）アクリレート化合物であれば、特に制限はなく、目的に応じて適宜選択することができ、例えば、アルキル（メタ）アクリレート、シクロアルキル（メタ）アクリレート、ビシクロアルキル（メタ）アクリレート、トリシクロアルキル（メタ）アクリレート、ヘテロシクロアルキル（メタ）アクリレート、ヘテロビシクロアルキル（メタ）アクリレート、フルオレン含有（メタ）アクリレート、ヒドロキシル基含有（メタ）アクリレート、トリメチロールプロパントリ（メタ）アクリレートなどが挙げられる。
　これらの中でも、高屈折率化の観点から、フルオレン構造等の環式構造を有する（メタ）アクリレートが好ましく、硬化物の熱安定性の観点から、多官能の（メタ）アクリレートが好ましい。
＜無機ナノ粒子＞
　前記無機ナノ粒子としては、高屈折率のナノ粒子であれば、特に制限はなく、目的に応じて適宜選択することができ、例えば、金属酸化物ナノ粒子、金属ナノ粒子、合金ナノ粒子などが挙げられる。
　前記金属酸化物ナノ粒子の材料としては、例えば、酸化チタン、酸化ニオブ、酸化ジルコニウム、酸化タンタル、酸化亜鉛、酸化インジウム、チタン酸バリウム（ＢａＴｉＯ３）、酸化インジウムスズ（ＩＴＯ）、アンチモンドープ酸化スズ（ＡＴＯ）などが挙げられる。
　前記金属ナノ粒子の金属としては、例えば、鉄、亜鉛、タングステン、プラチナなどが挙げられる。前記合金ナノ粒子の合金としては、前記金属を含む合金などが挙げられる。
　これらは１種単独で使用してもよく、２種以上を併用してもよい。
　これらの中でも、金属酸化物ナノ粒子が好ましく、酸化チタンがより好ましい。
　前記無機ナノ粒子の粒子径としては、特に制限はなく、目的に応じて適宜選択することができるが、１ｎｍ以上１００ｎｍ以下が好ましく、５ｎｍ以上５０ｎｍ以下がより好ましい。
　前記粒子径は、測定試料が無機ナノ粒子を含有する高屈折率硬化性組成物又は分散液である場合には、動的光散乱法により測定することができ、測定試料が高屈折率硬化物である場合には、透過型電子顕微鏡（ＴＥＭ）を用いた断片の観察により、観察視野内の円相当径を算出することにより測定することができる。
　前記無機ナノ粒子の含有量としては、特に制限はなく、目的に応じて適宜選択することができるが、前記高屈折率硬化性組成物の総量に対し、５５質量％以上８５質量％以下が好ましく、６０質量％以上８０質量％以下がより好ましく、７０質量％以上８０質量％以下が更に好ましい。
＜重合開始剤＞
　前記重合開始剤としては、波長４５０ｎｍよりも短波長の可視光又は紫外線の照射によりラジカルを生成する光重合開始剤が好ましく、例えば、２，４，６－トリメチルベンゾイル－ジフェニルフォスフィンオキシド（ＴＰＯ）、ジフェニル（２，４，６－トリメチルベンゾイル）ホスフィンオキシド、フェニルビス（２，４，６－トリメチルベンゾイル)ホスフィンオキシド等のアシルホスフィンオキシド系重合開始剤；１－ヒドロキシシクロへキシルフェニルケトン、２－ヒドロキシ－２－メチル－１－フェニルプロパン－１－オン等のアセトフェノン系重合開始剤；ベンゾイン、２，２－ジメトキシ－１，２－ジフェニルエタン－１－オン等のベンゾイン系重合開始剤；ベンゾフェノン、［４－（メチルフェニルチオ）フェニル］フェニルメタノン、４－ヒドロキシベンゾフェノン、４－フェニルベンゾフェノン、３，３´，４，４´－テトラ（ｔ－ブチルパーオキシカルボニル）ベンゾフェノン等のベンゾフェノン系重合開始剤；２－クロロチオキサントン、２，４－ジエチルチオキサントン等のチオキサントン系重合開始剤；などが挙げられる。
　これらは、１種単独で使用してもよく、２種以上を併用してもよい。
　前記重合開始剤の含有量としては、特に制限はなく、目的に応じて適宜選択することができるが、前記重合性化合物１００質量部に対して、０．１質量部以上１０質量部以下が好ましく、１質量部以上１０質量部以下がより好ましい。
＜その他の成分＞
　前記その他の成分としては、特に制限はなく、目的に応じて適宜選択することができ、例えば、溶媒などが挙げられる。
　前記溶媒としては、特に制限はなく、目的に応じて適宜選択することができ、例えば、メタノール、エタノール、イソプロピルアルコール等のアルコール類；テトラヒドロフラン、エチルメチルエーテル等のエーテル類；エチレングリコールモノメチルエーテル、エチレングリコールモノエチルエーテル、エチレングリコールモノブチルエーテル、エチレングリコールジメチルエーテル、ジエチレングリコールモノメチルエーテル、ジエチレングリコールモノエチルエーテル、ジエチレングリコールジメチルエーテル、ジエチレングリコールジエチルエーテル、ジエチレングリコールモノブチルエーテル、１－メトキシ－２－プロパノール（プロピレングリコールモノメチルエーテル、ＰＧＭＥ）、プロピレングリコールモノブチルエーテル（ＰＧＢ）等のグリコールエーテル類；メチルセロソルブアセテート、エチルセロソルブアセテート、ブチルセロソルブアセテート、プロピレングリコールメチルエーテルアセテート（ＰＧＭＥＡ）、３－メトキシブチル－１－アセテート等のアルキレングリコールモノアルキルエーテルアセテート類；トルエン、キシレン等の芳香族炭化水素類；メチルエチルケトン（ＭＥＫ）、メチルイソブチルケトン（ＭＩＢＫ）、メチルアミルケトン、シクロヘキサノン、４－ヒドロキシ－４－メチル－２－ペンタノン等のケトン類；２－ヒドロキシプロピオン酸エチル、２－ヒドロキシ－２－メチルプロピオン酸メチル、２－ヒドロキシ－２－メチルプロピオン酸エチル、エトキシ酢酸エチル、ヒドロキシ酢酸エチル、２－ヒドロキシ－２－メチルブタン酸メチル、３－メトキシプロピオン酸メチル、３－メトキシプロピオン酸エチル、３－エトキシプロピオン酸メチル、３－エトキシプロピオン酸エチル、酢酸エチル、酢酸ブチル、乳酸メチル、乳酸エチル等のエステル類などが挙げられる。
　これらは、１種単独で使用してもよく、２種以上を併用してもよい。
［粘度］
　前記高屈折率硬化性組成物の２５℃における粘度としては、１０００ｍＰａ以下が好ましく、５００ｍＰａ以下がより好ましく、３００ｍＰａ以下が更に好ましい。
　前記高屈折率硬化性組成物の２５℃における粘度が、１０００ｍＰａ以下であると、低粘度で成形性に優れ、スピンコーターなど低粘度が必要とされる塗工プロセスを利用して高屈折率硬化物を製造できる点で有利である。
　前記粘度は、レオメーター（例えば、装置名：レオメーター　ＡＲ－Ｇ２、ＴＡインスツルメント株式会社製）を用いて測定することができる。
［高屈折率硬化性組成物の調製方法］
　前記高屈折率硬化性組成物の調製方法としては、特に制限はなく目的に応じて適宜選択することができ、例えば、前記多官能（メタ）アクリレート化合物（Ａ）、前記単官能（メタ）アクリレート化合物（Ｂ）、前記無機ナノ粒子、前記重合開始剤、及び必要に応じてその他の成分を混合する方法などが挙げられる。
（高屈折率硬化物）
　前記高屈折率硬化物は、上述した本実施形態の高屈折率硬化性組成物を光硬化してなる硬化物である。
　前記高屈折率硬化性組成物を光硬化する方法としては、特に制限はなく、目的に応じて適宜選択することができ、例えば、基材上に前記高屈折率硬化性組成物を付与して、光照射を行い、前記高屈折率硬化性組成物を光硬化させる方法；成形用型の内部に前記高屈折率硬化性組成物を充填して、光照射を行い、前記高屈折率硬化性組成物を光硬化させる方法；などが挙げられる。
　これにより、前記高屈折率硬化物を製造することができる。
　前記基材上に前記高屈折率硬化性組成物を付与する方法としては、特に制限はなく、目的に応じて適宜選択することができ、例えば、バーコーターやスピンコーターなどにより基材上に均一な厚みで一面に前記高屈折率硬化性組成物を付与する方法；スクリーン印刷などにより基材上に所望のパターン形状に前記高屈折率硬化性組成物を付与する方法；などが挙げられる。
　前記高屈折率硬化性組成物は、比較的低粘度である単官能（メタ）アクリレート化合物（Ｂ）と、必要に応じて溶媒などの配合により粘度を調整することができ、成形性に優れ、低粘度が必要とされる塗工プロセスを利用して高屈折率硬化物を製造できる点で有利である。
　前記光照射としては、例えば、高圧水銀ランプ、メタルハライドランプ、ＵＶ－ＬＥＤ照射器による光照射が挙げられる。
　前記高屈折率硬化性組成物が溶媒を含む場合には、光硬化を行う前に、必要に応じて、加温、減圧などにより溶媒を除去する処理を実施してもよい。
［屈折率］
　本実施形態の高屈折率硬化物によれば、高屈折率とすることができ、具体的には、前記高屈折率硬化物の波長６３６ｎｍにおける屈折率ｎで、１．８０以上とすることができる。
　前記高屈折率硬化物の波長６３６ｎｍにおける屈折率ｎとしては、１．８０以上が好ましく、１．８２以上がより好ましい。
　前記高屈折率硬化物の波長６３６ｎｍにおける屈折率は、屈折率計（例えば、装置名：プリズムカプラー　２０１０／Ｍ、メトリコンジャパン株式会社製）を用いて測定することができる。
［ガラス転移温度（Ｔｇ）］
　本実施形態の高屈折率硬化物によれば、ガラス転移温度が高く、耐熱性に優れ、具体的には、Ｔｇ６０℃以上とすることができる。
　前記高屈折率硬化物のガラス転移温度（Ｔｇ）としては、６０℃以上が好ましく、７０℃以上がより好ましく、７５℃以上が更に好ましい。
　前記ガラス転移温度（Ｔｇ）は、示差走査熱量測定装置（例えば、装置名：ＤＳＣ　７０００Ｘ、日立ハイテク株式会社製）を用いて測定することができる。
　本実施形態の高屈折率硬化物によれば、透明であり、具体的には、全光透過率で８５％以上、ヘーズ１．０以下とすることができる。
　前記全光透過率としては、８５％以上が好ましく、８８％以上がより好ましい。
　前記ヘーズとしては、１．０以下が好ましく、０．８以下がより好ましく、０．５以下が更に好ましい。
　前記全光透過率は、平均厚み５μｍの高屈折率硬化物を測定試料として用い、ヘーズメーター（例えば、ＮＤＨ　７０００ＳＰ、日本電色工業株式会社製）により測定することができる。
　前記ヘーズは、平均厚み５μｍの高屈折率硬化物を測定試料として用い、ヘーズメーター（例えば、ＮＤＨ　７０００ＳＰ、日本電色工業株式会社製）を用いてＪＩＳ　Ｋ　７１３６に従って測定することができる。
　前記高屈折率硬化物の平均厚みとしては、特に制限はなく、目的に応じて適宜選択することができるが、０．１μｍ以上４０μｍ以下が好ましく、１μｍ以上１０μｍ以下がより好ましい。
　ここで、前記平均厚みとは、任意の箇所を１０箇所測定した際の算術平均値である。
［用途］
　本実施形態の高屈折率硬化物は、高屈折率、高ガラス転移温度、及び優れた透明性を兼ね備える高屈折率硬化物を製造可能な高屈折率硬化性組成物として用いることができる。具体的には、レンズ、フィルター、光ファイバー、ミラー、屈折光学素子、回折光学素子等の光学部品；発光デバイス部品、吸光デバイス部品、表示デバイス部品などの用途に用いることができる。
　本実施形態の高屈折率硬化物、及び高屈折率硬化物によれば、マイクロレンズアレイなどの光学レンズの薄型化の用途（例えば、特開２００８－０６０１２１号公報参照）や、光トランシーバーなどの集光率向上の用途（例えば、特開２００４－０９６０９１号公報参照）に用いることができる。また、空気と基材との屈折率差を徐々になくす積層構造とすることにより、太陽電池、ディスプレイのような表示装置の反射防止コーティングの用途（例えば、特開２０２２－１０６００２号公報参照）に好適に使用することができ、光学製品の高性能化に寄与することができる。
　以下、本発明の実施例を説明するが、本発明は、これらの実施例に何ら限定されるものではない。
＜合成例１：２，７－ナフタレンジアクリレートの合成＞
　不活性雰囲気下の２００ｍＬ三口フラスコに２，７－ジヒドロキシナフタレン（東京化成工業株式会社製）６．４０ｇ（４０ｍｍｏｌ）とトリエチルアミン（東京化成工業株式会社製）８．９０ｇ（８８ｍｍｏｌ）と超脱水アセトン（富士フィルム和光純薬株式会社製）７０ｇ加え溶液を５℃に冷却後、アクリル酸クロリド（東京化成工業株式会社製）７．９７ｇ（８８ｍｍｏｌ）を溶液温度が１０℃を超えないように撹拌しながらゆっくり滴下した。滴下終了後、室温で２４時間撹拌した。その後、反応溶液に水を添加し、析出した固体をろ過し、ジクロロメタン及び蒸留水で分液処理を行った。有機層を硫酸マグネシウムにて乾燥、ろ過後、ロータリーエバポレーターにて有機溶媒を留去し、４０℃終夜減圧乾燥して薄黄色固体の合成物１を８．４６ｇ（収率７８．８％）得た。得られた合成物１について、核磁気共鳴装置（ＮＭＲ装置、装置名：ＪＮＭ－ＥＸＺ４００Ｒ／Ｓ３、日本電子株式会社製）を用いてＮＭＲを測定した。
　得られた合成物１について、１Ｈ　ＮＭＲ測定結果、及び構造式を以下に示す。
　１Ｈ　ＮＭＲ（ＤＭＳＯ－ｄ６，４００ＭＨｚ）：８．０５－８．０２（ｄ，２Ｈ），７．７５－７．７４（ｄ，２Ｈ），７．３９－７．３６（ｄ，２Ｈ），６．６１－６．５６（ｄｄ，２Ｈ），６．５０－６．４３（ｄｄ，２Ｈ），６．２１－６．１７（ｄｄ，２Ｈ）．
＜合成例２：２－アクリロイル（７－（アクリロイルオキシ）エトキシ）ナフタレンの合成＞
　２００ｍＬ三口フラスコに蒸留水１２０ｇと水酸化ナトリウム（富士フィルム和光純薬株式会社製）４．８５ｇ（１２１ｍｍｏｌ）を加えて撹拌し、水酸化ナトリウムの溶解を確認後、２，７－ジヒドロキシナフタレン（東京化成工業株式会社製）９．６１ｇ（６０ｍｍｏｌ）加えて室温で２時間撹拌した。その後、２－ブロモエタノール（東京化成工業株式会社製）１５．２ｇ（１２１ｍｍｏｌ）を滴下し、８５℃、６時間の加熱撹拌を行い、放冷後室温で終夜撹拌を行った。翌日ろ過洗浄を行い、４０℃終夜減圧乾燥を行うことで黒色固体を９．４４ｇ得た。得られた固体を不活性雰囲気下の２００ｍＬ三口フラスコに２，７－ジヒドロキシナフタレン（東京化成工業株式会社製）６．８８ｇ（７６ｍｍｏｌ）とトリエチルアミン（東京化成工業株式会社製）７．６９ｇ（７６ｍｍｏｌ）と超脱水アセトン（富士フィルム和光純薬株式会社製）７０ｇ加え溶液を５℃に冷却後、アクリル酸クロリド（東京化成工業株式会社製）６．８８ｇ（７６ｍｍｏｌ）を溶液温度が１０℃を超えないように撹拌しながらゆっくり滴下した。滴下終了後、室温で２４時間撹拌した。その後反応溶液に水を添加し析出した固体をろ過し、ジクロロメタン及び蒸留水で分液処理を行った。有機層を硫酸マグネシウムにて乾燥、ろ過後、ロータリーエバポレーターにて有機溶媒を留去し、４０℃終夜減圧乾燥して得られた薄赤色固体の合成物２をシリカゲルクロマトグラフィー（溶媒　クロロホルム：ヘキサン：酢酸エチル＝５：４：１、体積比）にて処理することで白色固体を４．６２ｇ（収率２４．７％）得た。
　得られた合成物２について、１Ｈ　ＮＭＲ測定結果、及び構造式を以下に示す。
　１Ｈ　ＮＭＲ（ＤＭＳＯ－ｄ６，４００ＭＨｚ）：７．９０－７．８６（ｄ，２Ｈ），７．５９－７．５８（ｄ，１Ｈ），７．３７－７．３６（ｄ，１Ｈ），７，１９－７．１６（ｍ，２Ｈ），６．５９－５．９４（ｍ，６Ｈ），４．５２－４．５１（ｄ，２Ｈ），４．３６－４．３３（ｄ，２Ｈ）．
（実施例１）
　合成物１を５質量部と、１－ナフタレンメチルアクリレート（商品名：ライトアクリレートＮＭＴ－Ａ、共栄社化学株式会社製）２５質量部と、酸化チタン分散液（商品名：ＮＳ４０８、テイカ株式会社製、溶媒：ＭＥＫ、固形分：３５質量％、動的光散乱法による粒子径：１０ｎｍ～３０ｎｍ）２００質量部（酸化チタン７０質量部、及び溶媒１３０質量部）と、重合開始剤としての２－ヒドロキシ－２－メチルプロピオフェノン（商品名：Ｏｍｎｉｒａｄ１１７３、ＩＧＭ　Ｒｅｓｉｎｓ　Ｂ．Ｖ．株式会社製））１．４質量部、及び２，４，６－トリメチルベンゾイル－ジフェニルフォスフィンオキシド（商品名：Ｏｍｎｉｒａｄ　ＴＰＯ　Ｈ、ＩＧＭ　Ｒｅｓｉｎｓ　Ｂ．Ｖ．株式会社製）０．７質量部と、を配合して実施例１の高屈折率硬化性組成物を作製した。
　また、ワイヤレスバーコーター（装置名：ＯＳＰ－０８、オーエスジーシステムプロダクツ株式会社製）を用いて、スライドガラス（商品名：Ｓ９１１１、松浪硝子工業株式会社製）上に、作製した高屈折率硬化性組成物の塗布膜の平均厚みが８μｍとなるように塗布した。次に、酸化チタン分散液に含まれている溶媒（ＭＥＫ）を留去するため、パーフェクトオーブン（装置名：ＰＨＨ－１０２、エスペック株式会社製）を用いて６０℃、３０分間の乾燥処理を実施した。溶媒留去後、１分間の窒素パージを行い、窒素雰囲気下で高圧水銀ランプ（装置名：Ｈ０４－Ｌ４１、アイグラフィックス株式会社製）を設置したＵＶ照射装置（装置名：アイグランデージＥＣＳ－４０１ＧＸ、アイグラフィックス株式会社製）を用いて照度２Ｊ／ｃｍ２を照射して平均厚み５μｍの実施例１の高屈折率硬化物を作製した。
＜評価＞
　以下の手順により、作製した高屈折率硬化物について、ガラス転移温度（Ｔｇ）、屈折率、全光透過率、及びヘーズを測定し、評価を行った。結果を表１に示す。
＜＜高屈折率硬化物の屈折率＞＞
　高屈折率硬化物の屈折率は、屈折率計（装置名：プリズムカプラー　２０１０／Ｍ、メトリコンジャパン株式会社製）を用いて波長６３６ｎｍにおける屈折率を測定し、下記評価基準に基づき評価した。
－評価基準－
　◎：波長６３６ｎｍにおける屈折率が、１．８２以上である。
　○：波長６３６ｎｍにおける屈折率が、１．８０以上１．８２未満である。
　×：波長６３６ｎｍにおける屈折率が、１．８０未満である。
＜＜高屈折率硬化物のガラス転移温度（Ｔｇ）＞＞
　高屈折率硬化物のＴｇは、スライドガラスから高屈折率硬化物をはがし、示差走査熱量測定装置（装置名：ＤＳＣ　７０００Ｘ、株式会社日立ハイテク製）を用いて測定し、下記評価基準に基づき評価した。
－評価基準－
　◎：Ｔｇが、７５℃以上である。
　○：Ｔｇが、６０℃以上７５℃未満である。
　×：Ｔｇが、６０℃未満である。
＜＜高屈折率硬化物の全光透過率＞＞
　高屈折率硬化物の全光透過率は、ヘーズメーター（装置名：ＮＤＨ　７０００ＳＰ、日本電色工業株式会社製）を用いてＪＩＳ　Ｋ　７１３６－１にて測定し、下記評価基準に基づき評価した。
－評価基準－
　◎：全光透過率が、８８％以上である。
　○：全光透過率が、８５％以上８８％未満である。
　×：全光透過率が、８５％未満である。
＜＜高屈折率硬化物のヘーズ＞＞
　高屈折率硬化物のヘーズは、ヘーズメーター（装置名：ＮＤＨ　７０００ＳＰ、日本電色工業株式会社製）を用いてＪＩＳ　Ｋ　７１３６に従って測定し、下記評価基準に基づき評価した。
－評価基準－
　◎：ヘーズが、０．５以下である。
　○：ヘーズが、０．５超、１．０以下である。
　×：ヘーズが、１．０超である。
（実施例２）
　合成物２を５質量部と、１－ナフタレンメチルアクリレート（商品名：ライトアクリレートＮＭＴ－Ａ、共栄社化学株式会社製）２５質量部と、酸化チタン分散液（商品名：ＮＳ４０８、テイカ株式会社製、溶媒：ＭＥＫ、固形分：３５質量％、動的光散乱法による粒子径：１０ｎｍ～３０ｎｍ）２００質量部（酸化チタン７０質量部、及び溶媒１３０質量部）と、重合開始剤としての２－ヒドロキシ－２－メチルプロピオフェノン（商品名：Ｏｍｎｉｒａｄ１１７３、ＩＧＭ　Ｒｅｓｉｎｓ　Ｂ．Ｖ．株式会社製））１．４質量部、及び２，４，６－トリメチルベンゾイル－ジフェニルフォスフィンオキシド（商品名：Ｏｍｎｉｒａｄ　ＴＰＯ　Ｈ、ＩＧＭ　Ｒｅｓｉｎｓ　Ｂ．Ｖ．株式会社製）０．７質量部と、を配合して実施例２の高屈折率硬化性組成物を作製した。
　次いで、実施例２の高屈折率硬化性組成物を用いたこと以外は、実施例１と同様にして実施例２の高屈折率硬化物を作製し、評価を行った。結果を表１に示す。
（実施例３）
　合成物２を１０質量部と、１－ナフタレンメチルアクリレート（商品名：ライトアクリレートＮＭＴ－Ａ、共栄社化学株式会社製）２０質量部と、酸化チタン分散液（商品名：ＮＳ４０８、テイカ株式会社製、溶媒：ＭＥＫ、固形分：３５質量％、動的光散乱法による粒子径：１０ｎｍ～３０ｎｍ）２００質量部（酸化チタン７０質量部、及び溶媒１３０質量部）と、重合開始剤としての２－ヒドロキシ－２－メチルプロピオフェノン（商品名：Ｏｍｎｉｒａｄ１１７３、ＩＧＭ　Ｒｅｓｉｎｓ　Ｂ．Ｖ．株式会社製））１．４質量部、及び２，４，６－トリメチルベンゾイル－ジフェニルフォスフィンオキシド（商品名：Ｏｍｎｉｒａｄ　ＴＰＯ　Ｈ、ＩＧＭ　Ｒｅｓｉｎｓ　Ｂ．Ｖ．株式会社製）０．７質量部と、を配合して実施例３の高屈折率硬化性組成物を作製した。
　次いで、実施例３の高屈折率硬化性組成物を用いたこと以外は、実施例１と同様にして実施例３の高屈折率硬化物を作製し、評価を行った。結果を表１に示す。
（実施例４）
　合成物１を３質量部と、１－ナフタレンメチルアクリレート（商品名：ライトアクリレートＮＭＴ－Ａ、共栄社化学株式会社製）１７質量部と、酸化チタン分散液（商品名：ＮＳ４０８、テイカ株式会社製、溶媒：ＭＥＫ、固形分：３５質量％、動的光散乱法による粒子径：１０ｎｍ～３０ｎｍ）２２９質量部（酸化チタン８０質量部、及び溶媒１４９質量部）と、重合開始剤としての２－ヒドロキシ－２－メチルプロピオフェノン（商品名：Ｏｍｎｉｒａｄ１１７３、ＩＧＭ　Ｒｅｓｉｎｓ　Ｂ．Ｖ．株式会社製））０．９質量部、及び２，４，６－トリメチルベンゾイル－ジフェニルフォスフィンオキシド（商品名：Ｏｍｎｉｒａｄ　ＴＰＯ　Ｈ、ＩＧＭ　Ｒｅｓｉｎｓ　Ｂ．Ｖ．株式会社製）０．３質量部と、を配合して実施例４の高屈折率硬化性組成物を作製した。
　次いで、実施例４の高屈折率硬化性組成物を用いたこと以外は、実施例１と同様にして実施例４の高屈折率硬化物を作製し、評価を行った。結果を表１に示す。
（比較例１）
　１－ナフタレンメチルアクリレート（商品名：ライトアクリレートＮＭＴ－Ａ、共栄社化学株式会社製）３０質量部と、酸化チタン分散液（商品名：ＮＳ４０８、テイカ株式会社製、溶媒：ＭＥＫ、固形分：３５質量％、動的光散乱法による粒子径：１０ｎｍ～３０ｎｍ）２００質量部（酸化チタン７０質量部、及び溶媒１３０質量部）と、重合開始剤としての２－ヒドロキシ－２－メチルプロピオフェノン（商品名：Ｏｍｎｉｒａｄ１１７３、ＩＧＭ　Ｒｅｓｉｎｓ　Ｂ．Ｖ．株式会社製）１．４質量部、及び２，４，６－トリメチルベンゾイル－ジフェニルフォスフィンオキシド（商品名：Ｏｍｎｉｒａｄ　ＴＰＯ　Ｈ、ＩＧＭ　Ｒｅｓｉｎｓ　Ｂ．Ｖ．株式会社製）０．７質量部と、を配合して比較例１の高屈折率硬化性組成物を作製した。
　次いで、比較例１の高屈折率硬化性組成物を用いたこと以外は、実施例１と同様にして比較例１の高屈折率硬化物を作製し、評価を行った。結果を表２に示す。
（比較例２）
　ジメチロールトリシクロデカンジアクリレート（商品名：ライトアクリレートＤＣＰ－Ａ、共栄社化学株式会社製）３０質量部と、酸化チタン分散液（商品名：ＮＳ４０８、テイカ株式会社製、溶媒：ＭＥＫ、固形分：３５質量％、動的光散乱法による粒子径：１０ｎｍ～３０ｎｍ）２００質量部（酸化チタン７０質量部、及び溶媒１３０質量部）と、重合開始剤としての２－ヒドロキシ－２－メチルプロピオフェノン（商品名：Ｏｍｎｉｒａｄ１１７３、ＩＧＭ　Ｒｅｓｉｎｓ　Ｂ．Ｖ．株式会社製）１．４質量部、及び２，４，６－トリメチルベンゾイル－ジフェニルフォスフィンオキシド（商品名：Ｏｍｎｉｒａｄ　ＴＰＯ　Ｈ、ＩＧＭ　Ｒｅｓｉｎｓ　Ｂ．Ｖ．株式会社製）０．７質量部と、を配合して比較例２の高屈折率硬化性組成物を作製した。
　次いで、比較例２の高屈折率硬化性組成物を用いたこと以外は、実施例１と同様にして比較例２の高屈折率硬化物を作製し、評価を行った。結果を表２に示す。
（比較例３）
　ジメチロールトリシクロデカンジアクリレート（商品名：ライトアクリレートＤＣＰ－Ａ、共栄社化学株式会社製）２０質量部と、酸化チタン分散液（商品名：ＮＳ４０８、テイカ株式会社製、溶媒：ＭＥＫ、固形分：３５質量％、動的光散乱法による粒子径：１０ｎｍ～３０ｎｍ）２２９質量部（酸化チタン８０質量部、及び溶媒１４９質量部）と、重合開始剤としての２－ヒドロキシ－２－メチルプロピオフェノン（商品名：Ｏｍｎｉｒａｄ１１７３、ＩＧＭ　Ｒｅｓｉｎｓ　Ｂ．Ｖ．株式会社製）０．９質量部、及び２，４，６－トリメチルベンゾイル－ジフェニルフォスフィンオキシド（商品名：Ｏｍｎｉｒａｄ　ＴＰＯ　Ｈ、ＩＧＭ　Ｒｅｓｉｎｓ　Ｂ．Ｖ．株式会社製）０．３質量部と、を配合して比較例３の高屈折率硬化性組成物を作製した。
　次いで、比較例３の高屈折率硬化性組成物を用いたこと以外は、実施例１と同様にして比較例３の高屈折率硬化物を作製し、評価を行った。結果を表２に示す。
（比較例４）
　ジメチロールトリシクロデカンジアクリレート（商品名：ライトアクリレートＤＣＰ－Ａ、共栄社化学株式会社製）１０質量部と、酸化チタン分散液（商品名：ＮＳ４０８、テイカ株式会社製、溶媒：ＭＥＫ、固形分：３５質量％、動的光散乱法による粒子径：１０ｎｍ～３０ｎｍ）２５７質量部（酸化チタン９０質量部、及び溶媒１６７質量部）と、重合開始剤としての２－ヒドロキシ－２－メチルプロピオフェノン（商品名：Ｏｍｎｉｒａｄ１１７３、ＩＧＭ　Ｒｅｓｉｎｓ　Ｂ．Ｖ．株式会社製）０．３質量部、及び２，４，６－トリメチルベンゾイル－ジフェニルフォスフィンオキシド（商品名：Ｏｍｎｉｒａｄ　ＴＰＯ　Ｈ、ＩＧＭ　Ｒｅｓｉｎｓ　Ｂ．Ｖ．株式会社製）０．１質量部と、を配合して比較例４の高屈折率硬化性組成物を作製した。
　次いで、比較例４の高屈折率硬化性組成物を用いたこと以外は、実施例１と同様にして比較例４の高屈折率硬化物を作製したが、膜のヒビ割れや酸化チタン固体の析出が見られ成膜することができなかった。結果を表２に示す。
（比較例５）
　フルオレン誘導体ジアクリレート（商品名：Ｆ５７１０、大阪ガスケミカル株式会社製）３０質量部と、酸化チタン分散液（商品名：ＮＳ４０８、テイカ株式会社製、溶媒：ＭＥＫ、固形分：３５質量％、動的光散乱法による粒子径：１０ｎｍ～３０ｎｍ）２００質量部（酸化チタン７０質量部、及び溶媒１３０質量部）と、重合開始剤としての２－ヒドロキシ－２－メチルプロピオフェノン（商品名：Ｏｍｎｉｒａｄ１１７３、ＩＧＭ　Ｒｅｓｉｎｓ　Ｂ．Ｖ．株式会社製）１．４質量部、及び２，４，６－トリメチルベンゾイル－ジフェニルフォスフィンオキシド（商品名：Ｏｍｎｉｒａｄ　ＴＰＯ　Ｈ、ＩＧＭ　Ｒｅｓｉｎｓ　Ｂ．Ｖ．株式会社製）０．７質量部と、を配合して比較例５の高屈折率硬化性組成物を作製した。
　次いで、比較例５の高屈折率硬化性組成物を用いたこと以外は、実施例１と同様にして比較例５の高屈折率硬化物を作製し、評価を行った。結果を表２に示す。なお、屈折率を測定した結果、測定箇所によって屈折率に大きなばらつきがあり、測定値を特定することができなかった。
（比較例６）
　合成物１を１５質量部と、１－ナフタレンメチルアクリレート（商品名：ライトアクリレートＮＭＴ－Ａ、共栄社化学株式会社製）８５質量部と、重合開始剤としての２－ヒドロキシ－２－メチルプロピオフェノン（商品名：Ｏｍｎｉｒａｄ１１７３、ＩＧＭ　Ｒｅｓｉｎｓ　Ｂ．Ｖ．株式会社製）１質量部、及び２，４，６－トリメチルベンゾイル－ジフェニルフォスフィンオキシド（商品名：Ｏｍｎｉｒａｄ　ＴＰＯ　Ｈ、ＩＧＭ　Ｒｅｓｉｎｓ　Ｂ．Ｖ．株式会社製）１質量部と、を配合して比較例６の高屈折率硬化性組成物を作製した。
　次いで、比較例６の高屈折率硬化性組成物を用いたこと以外は、実施例１と同様にして比較例６の高屈折率硬化物を作製し、評価を行った。結果を表２に示す。
（比較例７）
　合成物２を１５質量部と、１－ナフタレンメチルアクリレート（商品名：ライトアクリレートＮＭＴ－Ａ、共栄社化学株式会社製）８５質量部と、重合開始剤としての２－ヒドロキシ－２－メチルプロピオフェノン（商品名：Ｏｍｎｉｒａｄ１１７３、ＩＧＭ　Ｒｅｓｉｎｓ　Ｂ．Ｖ．株式会社製）１質量部、及び２，４，６－トリメチルベンゾイル－ジフェニルフォスフィンオキシド（商品名：Ｏｍｎｉｒａｄ　ＴＰＯ　Ｈ、ＩＧＭ　Ｒｅｓｉｎｓ　Ｂ．Ｖ．株式会社製）１質量部と、を配合して比較例７の高屈折率硬化性組成物を作製した。
　次いで、比較例７の高屈折率硬化性組成物を用いたこと以外は、実施例１と同様にして比較例７の高屈折率硬化物を作製し、評価を行った。結果を表２に示す。
　実施例１～４の高屈折率硬化性組成物では、得られた高屈折率硬化物の屈折率１．８２以上、Ｔｇ７５℃以上と非常に優れ、ヘーズが１．０以下で透明性に優れ、高屈折率、高ガラス転移温度、及び優れた透明性を兼ね備える高屈折率硬化物を製造可能であることがわかった。
　一方、多官能（メタ）アクリレート化合物（Ａ）を含有しない比較例１～５の高屈折率硬化性組成物では、得られた高屈折率硬化物の高屈折率、及び高ガラス転移温度を両立することができなかった。加えて、比較例２～４では、無機ナノ粒子の質量比が高くなるに従い、透明性が低下し、成膜できない結果となった。単官能の他の（メタ）アクリレート化合物（Ｃ）を含有する比較例５では、均一な硬化物が得られず、ヘーズが１．５であり透明性に欠ける結果となった。
　また、無機ナノ粒子を含有しない比較例６～７の高屈折率硬化性組成物では、得られた高屈折率硬化物の屈折率が１．８０を大きく下回り、優れた高屈折率を実現することができなかった。
　本出願は、２０２４年５月１７日に出願した日本国特許出願２０２４－０８１１５２号に基づいて優先権を主張し、日本国特許出願２０２４－０８１１５２号の全内容を参照することにより本国際出願に援用する。

Claims (11)

  1. 　下記一般式（１）で表される多官能（メタ）アクリレート化合物（Ａ）と、
    　ナフタレン骨格を有する単官能（メタ）アクリレート化合物（Ｂ）と、
    　無機ナノ粒子と、
    　重合開始剤と、を含有することを特徴とする高屈折率硬化性組成物。
    　前記一般式（１）中、Ｒ１は各々独立に水素又はメチル基を表し、ｌ、ｍ、ｎ、ｏ、ｐ、ｑ、ｒ、ｓ、ｔ、ｕ、ｖ及びｗは各々独立に０～１０までの整数であり、ａ及びｃは１であり、ｂ及びｄは各々独立に０又は１であり、ａ＋ｂ＋ｃ＋ｄが２、３又は４である。
  2. 　他の（メタ）アクリレート化合物（Ｃ）を更に含有する請求項１に記載の高屈折率硬化性組成物。
  3. 　前記多官能（メタ）アクリレート化合物（Ａ）と前記単官能（メタ）アクリレート化合物（Ｂ）との質量比（Ａ／Ｂ）が、１／９９～７０／３０である請求項１又は２に記載の高屈折率硬化性組成物。
  4. 　前記多官能（メタ）アクリレート化合物（Ａ）及び前記単官能（メタ）アクリレート化合物（Ｂ）の合計含有量が、１５質量％以上４５質量％以下である請求項１から３のいずれかに記載の高屈折率硬化性組成物。
  5. 　前記無機ナノ粒子の含有量が、５５質量％以上８５質量％以下である請求項１から４のいずれかに記載の高屈折率硬化性組成物。
  6. 　前記無機ナノ粒子が、酸化チタンである請求項１から５のいずれかに記載の高屈折率硬化性組成物。
  7. 　前記無機ナノ粒子の粒子径が、１ｎｍ以上１００ｎｍ以下である請求項１から６のいずれかに記載の高屈折率硬化性組成物。
  8. 　請求項１から７のいずれかに記載の高屈折率硬化性組成物を光硬化してなることを特徴とする高屈折率硬化物。
  9. 　波長６３６ｎｍにおける屈折率ｎが、１．８０以上である請求項８に記載の高屈折率硬化物。
  10. 　示差走査熱量測定により測定したガラス転移温度が、６０℃以上である請求項８又は９に記載の高屈折率硬化物。
  11. 　ヘーズが、１．０以下である請求項８から１０のいずれかに記載の高屈折率硬化物。
PCT/JP2025/017442 2024-05-17 2025-05-13 高屈折率硬化性組成物、及び高屈折率硬化物 Pending WO2025239368A1 (ja)