WO2025115809A1 - 人工毛髪用繊維束及び頭髪装飾製品 - Google Patents

人工毛髪用繊維束及び頭髪装飾製品 Download PDF

Info

Publication number
WO2025115809A1
WO2025115809A1 PCT/JP2024/041655 JP2024041655W WO2025115809A1 WO 2025115809 A1 WO2025115809 A1 WO 2025115809A1 JP 2024041655 W JP2024041655 W JP 2024041655W WO 2025115809 A1 WO2025115809 A1 WO 2025115809A1
Authority
WO
WIPO (PCT)
Prior art keywords
artificial hair
fiber bundle
fiber
hair
fibers
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
PCT/JP2024/041655
Other languages
English (en)
French (fr)
Inventor
津田 栞里 坂本
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Denka Co Ltd
Original Assignee
Denka Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Denka Co Ltd filed Critical Denka Co Ltd
Publication of WO2025115809A1 publication Critical patent/WO2025115809A1/ja
Anticipated expiration legal-status Critical
Pending legal-status Critical Current

Abstract

本発明は、適度な滑りにくさ及び櫛通り性を両立する人工毛髪用繊維束を提供することを課題とする。　本発明の一態様は、合成繊維に異なる表面処理組成物が付着している少なくとも２種類以上の人工毛髪用繊維を含む、人工毛髪用繊維束である。上記人工毛髪用繊維束の動摩擦係数は、０．２３～０．２６である。

Description

人工毛髪用繊維束及び頭髪装飾製品
　本発明は、人工毛髪用繊維束及び頭髪装飾製品に関する。
　かつら、ヘアウィッグ、付け毛、ヘアーバンド、ドールヘアーなどの頭髪装飾製品において、人毛に代わる人工毛髪の重要性が高まってきている。人工毛髪用繊維を構成する素材としては、アクリル系樹脂、塩化ビニル系樹脂、又はポリエステル系樹脂があり、これらの樹脂からなる人工毛髪用繊維が市販されている。
　特許文献１には、塩化ビニル系樹脂であっても、繊維の艶や滑りが良く、繊維がきしまず、ボリュームに優れた繊維を提供することを目的として、所定の繊維処理剤を用いて基材繊維に処理を施す技術が開示されている。
特開２００２－２８５４７０号公報
　人工毛髪用繊維束には、使用者の違和感を防止する観点から、適度な滑りにくさを有すること及び櫛通り性を両立することが求められる。ここで、繊維束の滑りにくさとは、繊維束を編み込むとき等における繊維の滑りにくさの度合いをいう。また、繊維束の櫛通り性とは、繊維束に手櫛をしたときに感じる指の通りやすさの度合いをいう。
　本発明は、このような事情に鑑みてなされたものであり、適度な滑りにくさ及び櫛通り性を両立する人工毛髪用繊維束、及び当該人工毛髪用繊維束を備える頭髪装飾製品を提供することを目的とする。
　本発明者らが鋭意検討を行ったところ、２種類以上の人工毛髪用繊維を含む人工毛髪用繊維束において、動摩擦係数が特定の範囲にあることで、上記の課題を解決できることを見出し、本発明を完成させた。
　本発明によれば、以下が提供される。
［１］人工毛髪用繊維束であって、
　合成繊維に異なる表面処理組成物が付着している少なくとも２種類以上の人工毛髪用繊維を含み、
　上記人工毛髪用繊維束の動摩擦係数が０．２３～０．２６である、人工毛髪用繊維束。
［２］人工毛髪用繊維束であって、
　動摩擦係数の異なる少なくとも２種類以上の人工毛髪用繊維を含み、
　上記動摩擦係数が０．２５未満の人工毛髪用繊維と、０．２５以上の人工毛髪用繊維とを、それぞれ１種類以上含む、人工毛髪用繊維束。
［３］上記表面処理組成物が、それぞれ、脂肪酸骨格含有化合物、ポリアルキレングリコール、シリコーンオイル、ポリオキシアルキレンアルキルエーテル、鉱物油、カチオン系界面活性剤、アルキルアルキレート及びポリオキシエチレンアルキルエーテルからなる群より選ばれる１以上を含む、［１］に記載の人工毛髪用繊維束。
［４］上記人工毛髪用繊維における上記表面処理組成物の付着量が、上記合成繊維を基準として０．０５質量％～１．０質量％である、［１］又は［３］に記載の人工毛髪用繊維束。
［５］上記２種類以上の人工毛髪用繊維が、均一に分散されている、［１］～［４］のいずれかに記載の人工毛髪用繊維束。
［６］上記人工毛髪用繊維束の上記動摩擦係数を５回測定するとき、標準偏差が０．０４以下である、［１］～［５］のいずれかに記載の人工毛髪用繊維束。
［７］上記合成繊維が、塩化ビニルの単独重合体、塩化ビニル－アクリロニトリル共重合体、ポリエチレンテレフタレート、ポリアミド系樹脂、ポリプロピレン及びアクリロニトリル－スチレン共重合体からなる群より選ばれる１以上を含む、［１］、［３］及び［４］のいずれかに記載の人工毛髪用繊維束。
［８］［１］～［７］のいずれかに記載の人工毛髪用繊維束を備える、頭髪装飾製品。
［９］［８］に記載の頭髪装飾製品であって、ブレードを含む、頭髪装飾製品。
　本発明によれば、適度な滑りにくさ及び櫛通り性を両立する人工毛髪用繊維束、及び当該人工毛髪用繊維束を備える頭髪装飾製品を提供することができる。
　以下、本発明について、詳細に説明する。本発明は、これらの記載に限定されるものではない。以下に示す実施形態の各特徴事項は、互いに組み合わせ可能である。また、各特徴事項について独立して発明が成立する。
＜用語の説明＞
　本明細書において、例えば、「Ｘ～Ｙ」なる記載は、Ｘ以上でありＹ以下であることを意味する。
１　人工毛髪用繊維
　本実施形態に係る人工毛髪用繊維は、合成繊維に表面処理組成物が付着している人工毛髪用繊維であることが好ましい。
１．１　合成繊維
　本実施形態に係る合成繊維として、例えば、塩化ビニル系樹脂、ポリエステル系樹脂、ポリアミド系樹脂、ポリオレフィン系樹脂等の樹脂を使用することができる。これらの樹脂は、単独で使用しても２種類以上を組み合わせて使用してもよい。また、必要に応じて、これらの樹脂に、添加剤を加えた樹脂組成物を紡糸して合成繊維としてもよい。
１．１．１　塩化ビニル系樹脂
　本実施形態に係る塩化ビニル系樹脂として、例えば、塩化ビニルの単独重合体、塩素化塩化ビニルの単独共重合体及び塩化ビニル系共重合体が挙げられる。これらの塩化ビニル系樹脂は、単独で使用しても２種類以上を組み合わせて使用してもよい。
　塩化ビニル系共重合体として、例えば、塩化ビニル－酢酸ビニル共重合体及び塩化ビニル－プロピオン酸ビニル共重合体等の塩化ビニルとビニルエステル類との共重合体、塩化ビニル－アクリル酸ブチル共重合体及び塩化ビニル－アクリル酸２エチルヘキシル共重合体等の塩化ビニルとアクリル酸エステル類との共重合体、塩化ビニル－エチレン共重合体、塩化ビニル－プロピレン共重合体等の塩化ビニルとオレフィン類との共重合体、並びに塩化ビニル－アクリロニトリル共重合体が挙げられる。
　本実施形態に係る塩化ビニル系樹脂として、塩化ビニルの単独重合体及び塩化ビニル－アクリロニトリル共重合体が好ましい。このような樹脂であると、合成繊維の加工性が向上し、さらに、人工毛髪用繊維束がより適度な滑りにくさを有し、触感が向上する。
１．１．２　ポリエステル系樹脂
　本実施形態に係るポリエステル系樹脂として、例えば、ポリエチレンテレフタレート、ポリトリメチレンテレフタレート、ポリブチレンテレフタレート、ポリエチレンナフタレート等の芳香族ポリエステル系樹脂、ポリ乳酸、ポリヒドロキシ酪酸、ポリカプロラクトン、ポリブチレンサクシネート、ポリブチレンアジペート、ポリエチレンサクシネート、ポリグリコール酸、ポリ－３－ヒドロキシプロピオネート、ポリ－３－ヒドロキシブチレート等の脂肪族ポリエステル樹脂が挙げられる。これらのポリエステル系樹脂は、単独で使用しても２種類以上を組み合わせて使用してもよい。
　本実施形態に係るポリエステル系樹脂として、ポリエチレンテレフタレートが好ましい。このような樹脂であると、人工毛髪用繊維の強度及び耐熱性が向上する。
１．１．３　ポリアミド系樹脂
　本実施形態に係るポリアミド系樹脂として、例えば、ナイロン６、ナイロン６６、ナイロン１１、ナイロン１２、ナイロン６・１０、ナイロン６・１２及びこれらの共重合体が挙げられる。これらのポリアミド系樹脂は、単独で使用しても２種類以上を組み合わせて使用してもよい。
１．１．４　ポリオレフィン系樹脂
　本実施形態に係るポリオレフィン系樹脂として、例えば、ポリエチレン、ポリプロピレン、エチレン－酢酸ビニル共重合体、エチレン－エチルアクリレート共重合体及びエチレン－プロピレン共重合体が挙げられる。これらのポリオレフィン系樹脂は、単独で使用しても２種類以上を組み合わせて使用してもよい。
　本実施形態に係るポリオレフィン系樹脂として、ポリプロピレンが好ましい。このような樹脂であると、人工毛髪用繊維の比重が小さくなり、使用時の重量が軽くなるため、使用感に優れる。
１．１．５　その他の樹脂
　本実施形態に係るその他の樹脂として、例えば、エチレンとビニルアルコールとの共重合体、アクリロニトリル－スチレン共重合体、アクリロニトリル－スチレン－ブタジエン三元共重合体、エチレン－エチル（メタ）アクリレート共重合体等が挙げられる。
　上述の樹脂の中でも、本実施形態に係る樹脂は、塩化ビニルの単独重合体、塩化ビニル－アクリロニトリル共重合体、ポリエチレンテレフタレート、ポリアミド系樹脂、ポリプロピレン及びアクリロニトリル－スチレン共重合体からなる群より選ばれる１以上を含むことが好ましい。このような樹脂であると、合成繊維の加工性が向上し、さらに、人工毛髪用繊維束がより適度な滑りにくさを有し、触感が向上する。
１．２　表面処理組成物
　本実施形態に係る表面処理組成物として、例えば、脂肪酸骨格含有化合物、ポリアルキレングリコール、界面活性剤及びその他の成分が含まれることが好ましい。
　本実施形態に係る人工毛髪用繊維における表面処理組成物の付着量は、合成繊維を基準として０．０５～１．０質量％であることが好ましく、０．１～０．５質量％であることがさらに好ましい。人工毛髪用繊維における表面処理組成物の付着量は、合成繊維を基準として、例えば、０．０５、０．０６、０．０７、０．０８、０．０９、０．１、０．２、０．３、０．４、０．５、０．６、０．７、０．８、０．９又は１．０質量％であってもよく、ここで例示した数値のいずれか２つの間の範囲内であってもよい。人工毛髪用繊維における表面処理組成物の付着量の下限値がこのような値であると、人工毛髪用繊維束が櫛通り性に優れる。人工毛髪用繊維における表面処理組成物の付着量の上限値がこのような値であると、人工毛髪用繊維束がより適度な滑りにくさを有する。
１．２．１　脂肪酸骨格含有化合物
　本実施形態に係る脂肪酸骨格含有化合物として、例えば、脂肪酸、グリセリド及び有機酸グリセリドが挙げられる。本実施形態に係る脂肪酸骨格含有化合物として、グリセリド及び有機酸グリセリドの少なくとも一方を含むことが好ましい。このような脂肪酸骨格含有化合物を用いると、人工毛髪用繊維束がより適度な滑りにくさを有し、櫛通り性が向上する。
１．２．１．１　脂肪酸
　本実施形態に係る脂肪酸は、例えば、ステアリン酸、パルミチン酸、ミリスチン酸、ラウリン酸及びカプリン酸等の飽和脂肪酸、並びにオレイン酸等の不飽和脂肪酸が挙げられる。
１．２．１．２　グリセリド
　本実施形態に係るグリセリドとは、脂肪酸とグリセリンの１以上の水酸基とがエステル結合している化合物をいう。グリセリドは、脂肪酸の結合数に応じて、モノグリセリド、ジグリセリド、トリグリセリドともいう。本実施形態に係るグリセリドとして、例えば、モノステアリン酸グリセリド、モノパルミチン酸グリセリド、モノミリスチン酸グリセリド、モノラウリン酸グリセリド、モノカプリン酸グリセリド、並びにこれらのジグリセリド及びトリグリセリドが挙げられる。
１．２．１．３　有機酸グリセリド
　本実施形態に係る有機酸グリセリドとは、グリセリンの水酸基に、脂肪酸及び有機酸がそれぞれエステル結合している化合物をいう。本実施形態に係る有機酸として、例えば、酢酸、乳酸、クエン酸、コハク酸及びジアセチル酒石酸が挙げられる。本実施形態に係る有機酸グリセリドとして、例えば、クエン酸モノグリセライド、コハク酸モノグリセライド及び乳酸モノグリセライドが挙げられる。
１．２．２　ポリアルキレングリコール
　本実施形態に係るポリアルキレングリコールとして、例えば、ポリエチレングリコール、ポリプロピレングリコール及びポリエチレングリコール－ポリプロピレングリコール共重合体が挙げられる。
　本実施形態に係るポリアルキレングリコールの平均重合度は、２～５０であることが好ましく、３～４０であることがより好ましく、４～３０であることがさらに好ましく、４～２０であることが特に好ましい。ポリアルキレングリコールの平均重合度は、例えば、２、３、４、５、６、７、８、９、１０、１１、１２、１３、１４、１５、１６、１７、１８、１９、２０、２１、２２、２３、２４、２５、２６、２７、２８、２９、３０、３５、４０、４５又は５０であってもよく、ここで例示した数値のいずれか２つの間の範囲内であってもよい。ポリアルキレングリコールの平均重合度がこのような範囲であると、人工毛髪用繊維束がより適度な滑りにくさを有する。
１．２．３　界面活性剤
　本実施形態に係る界面活性剤として、例えば、ノニオン系界面活性剤、カチオン系界面活性剤及びアニオン系界面活性剤が挙げられる。本実施形態に係る界面活性剤として、ノニオン系界面活性剤及びカチオン系界面活性剤の少なくとも一方を含むことが好ましい。このような界面活性剤を用いると、人工毛髪用繊維束がより適度な滑りにくさを有し、櫛通り性、触感及び耐べたつき性が向上する。
１．２．３．１　ノニオン系界面活性剤
　本実施形態に係るノニオン系界面活性剤として、例えば、ポリオキシエチレン脂肪酸エステル、ポリオキシアルキレンアルキルエーテル、ポリオキシエチレンアルキルエーテル、ポリオキシエチレン硬化ヒマシ油エーテル、ポリオキシエチレンアルキルフェニルエーテル、ソルビタン脂肪酸エステル、ポリオキシエチレンソルビタン脂肪酸エステル、ショ糖脂肪酸エステル、グリセリン脂肪酸エステル、ポリオキシエチレンポリオキシプロピレンブロックポリマー、ポリオキシエチレンアルキルアミンエーテル及び脂肪酸アルカノールアミドが挙げられる。
　本実施形態に係るポリオキシエチレン脂肪酸エステルは、ポリアルキレングリコール骨格及び脂肪酸骨格を有する化合物であれば特に限定されない。本実施形態に係るポリオキシエチレン脂肪酸エステルとして、例えば、モノステアリン酸ポリエチレングリコール、ジステアリン酸ポリエチレングリコール、モノパルミチン酸ポリエチレングリコール、ジパルミチン酸ポリエチレングリコール、モノミリスチン酸ポリエチレングリコール、モノラウリン酸ポリエチレングリコール及びモノカプリン酸ポリエチレングリコールが挙げられる。
　本実施形態に係るポリオキシエチレン脂肪酸エステル中のポリアルキレングリコール骨格の平均重合度は、５～８０であることが好ましく、１０～７０であることがより好ましく、１５～６０であることがさらに好ましく、２０～５０であることが特に好ましい。ポリアルキレングリコール骨格の平均重合度は、たとえば、５、１０、１５、２０、２５、３０、３５、４０、４５、５０、５５、６０、６５、７０、７５又は８０であってもよく、ここで例示した数値のいずれか２つの間の範囲内であってもよい。ポリアルキレングリコール骨格の平均重合度がこのような範囲であると、人工毛髪用繊維束がより適度な滑りにくさを有する。
１．２．３．２　カチオン系界面活性剤
　本実施形態に係るカチオン系界面活性剤として、例えば、オキシアルキレン基を有する第四級アンモニウム塩、アルキルトリメチルアンモニウム塩、ジアルキルジメチルアンモニウム塩及びアルキルジメチルエチルアンモニウム塩等のアルキル基を有する第四級アンモニウム塩、ステアロオキシメチルピリジニウム塩、脂肪酸トリエタノールアミン及び脂肪酸トリエタノールアミンギ酸塩等のエステル結合を有するアンモニウム塩、並びにポリオキシエチレンアルキルアミン、Ｎ－アルキルプロピレンアミン及びＮ－アルキルポリエチレンポリアミン等のアルキル鎖を有するアミン誘導体が挙げられる。
１．２．４　その他の成分
　本実施形態に係る表面処理組成物は、必要に応じて本願発明の効果を阻害しない範囲で、その他の成分を含み得る。その他の成分として、例えば、アルキルアルキレート、シリコーンオイル（例えば、アミノ変性シリコーン）、鉱物油等が挙げられる。
１．２．４．１　アルキルアルキレート
　本実施形態に係るアルキルアルキレートとして、例えば、ミリスチン酸ミリスチル、ミリスチン酸イソプロピル、オレイン酸オクチル、ステアリン酸ステアリル、パルミチン酸イソプロピル及びパルミチン酸オクチルが挙げられる。
１．２．５　表面処理組成物の組み合わせ
　本実施形態に係る人工毛髪用繊維束は、後述するとおり、合成繊維に異なる表面処理組成物が付着している少なくとも２種類以上の人工毛髪用繊維を含むことが好ましいが、その表面処理組成物の組み合わせとして、例えば、脂肪酸骨格含有化合物、ポリアルキレングリコール及び界面活性剤を含む表面処理組成物と、界面活性剤及びシリコーンオイルを含む表面処理組成物、並びに界面活性剤（好ましくは２種類以上）を含む表面処理組成物のうちいずれかの表面処理組成物と、の組み合わせ、又は界面活性剤（好ましくは２種類以上）を含む表面処理組成物と、界面活性剤、アルキルアルキレート及び鉱物油を含む表面処理組成物と、の組み合わせが挙げられる。
１．３　人工毛髪用繊維の製造方法
　本実施形態に係る人工毛髪用繊維の製造方法は、合成繊維に表面処理組成物を付着させることができれば特に限定されない。本実施形態に係る人工毛髪用繊維の製造方法は、合成繊維を構成する樹脂又は樹脂と添加剤とを含む樹脂組成物を紡糸して合成繊維を得る紡糸工程と、得られた合成繊維に表面処理組成物を付着させる付着工程と、を含むことが好ましい。
１．３．１　紡糸工程
１．３．１．１　紡糸ステップ
　本実施形態に係る紡糸工程は、少なくとも紡糸ステップを含む。本実施形態に係る紡糸ステップは、公知の紡糸方法を用いることができる。例えば、樹脂又は樹脂組成物を、加熱されたシリンダーからノズルを経由して押し出し、溶融紡糸することができる。押出し機としては、従来公知の押出し機を使用でき、例えば、単軸押出し機、異方向２軸押出し機、コニカル２軸押出し機等を挙げることができる。
　溶融紡糸の条件は、樹脂及び樹脂組成物の種類に応じて適宜設定することができる。一例として、シリンダー温度は１５０～１９０℃とでき、ノズル温度は１８０±１５℃とすることができる。この際に用いるノズルの断面形状は、作製する人工毛髪用繊維の断面形状に応じて適宜設定することができる。
　ノズルから溶融紡糸された未延伸の糸は、加熱円筒（例えば、加熱円筒温度２５０℃）に導入されて瞬間的に熱処理され、ノズル直下（例えば、約４．５ｍ）の位置に設置した引取機にて巻き取ることができる。巻き取りの際に、未延伸の糸が所望の太さとなるように、引き取り速度を調節することができる。
１．３．１．２　延伸ステップ
　本実施形態に係る紡糸工程は、さらに、延伸ステップを含んでもよい。延伸ステップでは、上述の紡糸ステップで得られた未延伸の合成繊維を、延伸機で延伸して、延伸後合成繊維を得ることができる。一例として、延伸工程では、未延伸の合成繊維を、例えば、空気雰囲気下９０～１１０℃で２～５倍に延伸することができる。
　なお、本発明において、「合成繊維」とは、紡糸後の合成繊維であり、表面処理組成物付着前の合成繊維を包含する。
１．３．２　付着工程
　本実施形態に係る付着工程は、任意の付着方法を用いることができる。例えば、ロール転写法によって合成繊維に表面処理組成物を付着させてもよく、表面処理組成物中に合成繊維を浸漬させて付着させてもよい。本実施形態に係る合成繊維の表面処理組成物の付着量は、仕込み量を調節することや、表面処理組成物の溶媒以外の各成分の濃度を調節することによって調整することができる。
１．３．３　熱処理工程
　本実施形態に係る人工毛髪用繊維の製造方法は、さらに、熱処理工程を含んでもよい。熱処理工程では、表面処理組成物付着前の合成繊維又は付着工程後の人工毛髪用繊維を、熱処理機を用いて熱処理することができる。したがって、本実施形態に係る熱処理工程は、付着工程の前に行ってもよく、付着工程の後に行ってもよい。一例として、熱処理ステップでは、表面処理組成物付着前の合成繊維又は付着後人工毛髪用繊維を空気雰囲気下９０～１１０℃で、０．５～０．９９倍になるように熱処理を施し、繊維全長を熱収縮させて、所望の繊度の熱処理後合成繊維又は熱処理後人工毛髪用繊維を得ることができる。
１．３．４　ギア加工工程
　本実施形態に係る人工毛髪用繊維の製造方法は、さらに、ギア加工工程を含んでもよい。ギア加工工程では、２つの噛み合う高温のギアの間に繊維束を通すことによって捲縮を施すことができる。ギア加工工程で使用するギアの材質、ギアの波の形、ギアの端数などは特に限定されない。ギア加工工程では、繊維材質、繊度を考慮し、ギア波形の溝の深さ、ギアの表面温度、加工速度、ギア間の圧力条件等を適切に調整することによって、得られる人工毛髪用繊維の形状を制御することができる。これらの加工条件に特に制限はないが、一例として、ギア波形の溝の深さ（ギアピッチ）は０．２～６ｍｍ、好ましくは０．５～５ｍｍ、ギアの表面温度は３０～１００℃、好ましくは４０～８０℃、加工速度は０．５～１０ｍ／分、好ましくは１．０～８．０ｍ／分とできる。
　なお、本発明において、「人工毛髪用繊維」とは、表面処理組成物が付着した後の合成繊維をいい、付着後人工毛髪用繊維、熱処理後人工毛髪用繊維、ギア加工後人工毛髪用繊維を包含する。
２　人工毛髪用繊維束
　本実施形態に係る人工毛髪用繊維束は、少なくとも２種類以上の人工毛髪用繊維を含む。したがって、本実施形態に係る人工毛髪用繊維束は、人工毛髪用繊維を混合する混合工程により得ることができる。本実施形態に係る混合工程は、任意の混合方法を用いることができる。例えば、２種類以上の人工毛髪用繊維をハックリングで混在させることができる。本実施形態に混合工程は、ギア加工工程後に行うことが好ましい。
　本実施形態に係る人工毛髪用繊維束は、動摩擦係数の異なる少なくとも２種類以上の人工毛髪用繊維を含むことが好ましい。本実施形態に係る人工毛髪用繊維束は、動摩擦係数の異なる３種類以上の人工毛髪用繊維を含んでもよい。本実施形態に係る人工毛髪用繊維束は、例えば、動摩擦係数の異なる２種類、３種類、４種類、又５種類（あるいは２～５種類）の人工毛髪用繊維を含んでもよい。人工毛髪用繊維の動摩擦係数は、表面処理組成物に含まれる成分及びその量によって調整することができる。したがって、本実施形態に係る人工毛髪用繊維束は、合成繊維に異なる表面処理組成物が付着している少なくとも２種類以上の人工毛髪用繊維を含むことが好ましい。本実施形態に係る人工毛髪用繊維束は、合成繊維に異なる表面処理組成物が付着している３種類以上の人工毛髪用繊維を含んでもよい。本実施形態に係る人工毛髪用繊維束は、例えば、合成繊維に異なる表面処理組成物が付着している２種類、３種類、４種類、又５種類（あるいは２～５種類）の人工毛髪用繊維を含んでもよい。なお、以下、本実施形態に係る人工毛髪用繊維束の好ましい性質について述べるが、各測定は、ギア加工後人工毛髪用繊維を混合した人工毛髪用繊維束を使用することが好ましい。
２．１　動摩擦係数
　本実施形態に係る人工毛髪用繊維束の動摩擦係数は、０．２３～０．２６であることが好ましい。人工毛髪用繊維束の動摩擦係数は、例えば、０．２３、０．２４、０．２５又は０．２６であってもよく、ここで例示した数値のいずれか２つの間の範囲内であってもよい。人工毛髪用繊維束の動摩擦係数は、例えば、長さ３００ｍｍ、質量１０ｇの人工毛髪用繊維束の一端から１００ｍｍの位置から他端方向に、移動速度１０ｍｍ／秒、移動距離４５ｍｍ、荷重２００ｇでウレタン製端子を移動させたときの、摺動後の摩擦係数の平均値とすることができる。人工毛髪用繊維束の動摩擦係数は、表面処理組成物に含まれる成分及びその量によって調整することができ、また、動摩擦係数の異なる人工毛髪用繊維を適当な割合で混ぜ合せることにより調節することができる。人工毛髪用繊維束の動摩擦係数がこのような範囲であると、人工毛髪用繊維束の適度な滑りにくさと櫛通り性とを両立することができる。
　本実施形態に係る人工毛髪用繊維束に含まれる人工毛髪用繊維は、動摩擦係数の異なる少なくとも２種類以上の人工毛髪用繊維を含むことが好ましく、動摩擦係数が０．２５未満の人工毛髪用繊維と、０．２５以上の人工毛髪用繊維とを、それぞれ１種類以上含むこと好ましい。本実施形態に係る人工毛髪用繊維束は、例えば、動摩擦係数が０．１５以上０．２５未満の人工毛髪用繊維と、０．２５以上０．３５以下の人工毛髪用繊維とを、それぞれ１種類以上含むことが好ましい。本実施形態における人工毛髪用繊維束における、動摩擦係数が０．２５未満の人工毛髪用繊維と、０．２５以上の人工毛髪用繊維との含有比は、例えば、１０：９０～９０：１０であり、好ましくは３０：７０～７０：３０である。人工毛髪用繊維の動摩擦係数は、例えば、同種類の人工毛髪用繊維を長さ３００ｍｍ、質量１０ｇの人工毛髪用繊維束に束ねて、上述と同様の方法で測定することができる。人工毛髪用繊維束がこのような構成であると、人工毛髪用繊維束の適度な滑りにくさと櫛通り性とを両立することができる。
２．２　静摩擦係数
　本実施形態に係る人工毛髪用繊維束の静摩擦係数は、０．２０～０．３５であることが好ましい。人工毛髪用繊維束の静摩擦係数は、例えば、０．２０、０．２１、０．２２、０．２３、０．２４、０．２５、０．２６、０．２７、０．２８、０．２９、０．３０、０．３１、０．３２、０．３３、０．３４又は０．３５であってもよく、ここで例示した数値のいずれか２つの間の範囲内であってもよい。人工毛髪用繊維束の静摩擦係数は、例えば、上述と同様の方法で測定したときの、摺動開始時の摩擦係数とすることができる。人工毛髪用繊維束の静摩擦係数がこのような範囲であると、人工毛髪用繊維束の適度な滑りにくさと櫛通り性とを両立することができる。
２．３　均一性
　本実施形態に係る人工毛髪用繊維束は、上述のとおり、少なくとも２種類以上の人工毛髪用繊維を含むが、２種類以上の人工毛髪用繊維が、均一に分散されていることが好ましい。なお、「均一に分散されている」とは、人工毛髪用繊維束中で各種類の人工毛髪用繊維がよく混じり合った状態をいい、具体的には、人工毛髪用繊維束の動摩擦係数を異なる箇所で複数回測定したときの標準偏差の値が低い状態をいう。本実施形態に係る人工毛髪用繊維束の動摩擦係数を５回測定するとき、標準偏差は、０．０４以下であることが好ましい。人工毛髪用繊維束の動摩擦係数を５回測定するとき、標準偏差は、例えば、０．０４、０．０３、０．０２、０．０１又は０であってもよく、ここで例示した数値のいずれか２つの間の範囲内であってもよい。
２．４　滑りにくさ
　本実施形態に係る人工毛髪用繊維束は、適度な滑りにくさを有することが好ましい。人工毛髪用繊維束の滑りにくさは、例えば、長さ６００ｍｍ、質量１２０ｇの人工毛髪用繊維束を、毛髪用繊維処理技術者（実務経験５年以上）が三つ編み状に編込みを行った時に感じる繊維の滑りにくさの度合いによって評価することができる。
２．５　櫛通り性
　本実施形態に係る人工毛髪用繊維束は、櫛通り性に優れることが好ましい。人工毛髪用繊維束の櫛通り性は、例えば、長さ６００ｍｍ、質量１２０ｇの人工毛髪用繊維束を、毛髪用繊維処理技術者（実務経験５年以上）が手櫛を通したときに感じる指の通りやすさの度合によって評価することができる。
３　頭髪装飾製品
　本実施形態に係る頭髪装飾製品は、上述した人工毛髪用繊維束を備える。
　本実施形態に係る人工毛髪用繊維束は頭髪装飾製品に用いることができる。頭髪装飾製品としては、かつら、ヘアピース、ブレード、エクステンションヘアー、ドールヘアー、ヘアウィッグ、付け毛、ヘアーバンド等が挙げられる。本実施形態に係る人工毛髪用繊維束から得られる頭髪装飾製品は、適度な滑りにくさ及び優れた櫛通り性を有する。
　本実施形態に係る頭髪装飾製品は、様々なスタイルに適用可能であるが、三つ編みやツイスト等の編み込みを含むブレード（ｂｒａｉｄ）に特に好適である。
　以下、実施例に基づいて本発明をさらに詳細に説明する。なお、以下に説明する実施例は、本発明の代表的な実施例の一例を示したものであり、これにより本発明の範囲が狭く解釈されることはない。
＜合成繊維の準備＞
　合成繊維として、以下を準備した。
・合成繊維Ａ－１：７０質量％のポリ塩化ビニル（大洋塩ビ株式会社製「ＴＨ－７００」）及び３０質量％のアクリロニトリル－スチレン共重合体（デンカ株式会社製「ＧＲ－ＡＴ－６Ｓ」）を原料として、溶融紡糸法によりノズルから紡糸して得られた繊維
・合成繊維Ａ－２： ポリ塩化ビニル（大洋塩ビ株式会社製「ＴＨ－７００」）を原料として、溶融紡糸法によりノズルから紡糸して得られた繊維
・合成繊維Ａ－３：アクリロニトリル－スチレン共重合体（デンカ株式会社製「ＧＲ－ＡＴ－６Ｓ」）を原料として、溶融紡糸法によりノズルから紡糸して得られた繊維
・合成繊維Ａ－４：ポリエチレンテレフタレート（三井化学株式会社製「Ｊ１２５Ｓ」）を原料として、溶融紡糸法によりノズルから紡糸して得られた繊維
・合成繊維Ａ－５：ポリプロピレン（住友化学株式会社製「住友ノーブレン（登録商標）Ｓ１３１」）を原料として、溶融紡糸法によりノズルから紡糸して得られた繊維
＜表面処理組成物の準備＞
　表１に示す組成で、各成分を混合し、各表面処理組成物を得た。表面処理組成物を得るために用いた各成分は、以下のとおりである。なお、表面処理組成物Ｂ－６は、表面処理組成物Ｂ－１及び表面処理組成物Ｂ－３を、質量比１：１で混合して作製した。
（脂肪酸骨格含有化合物）
グリセリド：
・モノステアリン酸グリセリド：日本エマルジョン株式会社製「ＥＭＡＬＥＸ（登録商標）ＧＭＳ－Ｂ」
（ポリアルキレングリコール）
ポリアルキレングリコール：
・ポリエチレングリコール：青木油脂株式会社製「ＰＥＧ－２００」、平均重合度４
（界面活性剤）
ノニオン系界面活性剤：
・モノステアリン酸ポリエチレングリコール：日本エマルジョン株式会社製「ＥＭＡＬＥＸ（登録商標）８４０」
・ポリオキシアルキレンアルキルエーテル：日油株式会社製「ユニルーブ（登録商標）５０ＭＢ－２６」
・ポリオキシエチレンアルキルエーテル１：日光ケミカルズ株式会社製「ポリ（オキシエチレン）オレイルエーテル」
・ポリオキシエチレンアルキルエーテル２：青木油脂工業株式会社製「ブラウノン（登録商標）ＣＨ－３３０Ｌ」
カチオン系界面活性剤：
・四級アンモニウム塩型カチオン系界面活性剤：吉村油化学社製「Ｆ－２０」
・アルキルトリメチルアンモニウムクロライド：東邦化学工業株式会社製「カチナール（登録商標）ＤＣ－８０」
（その他の成分）
アルキルアルキレート：
・アルキルアルキレート：ＢＯＣ　Ｓｃｉｅｎｃｅ社製「パルミチン酸オクチル」
シリコーンオイル：
・アミノ変性シリコーン：吉村油化学株式会社製「ＴＣＳ３８２」
鉱物油：
・鉱物油：ＤＫＳＨジャパン株式会社製「ミネラルオイル」
＜人工毛髪用繊維の作製＞
　各合成繊維を１００℃で延伸した後、ロール転写法によって各合成繊維に各表面処理組成物を付着させた。ロール転写の条件は、ロールの半径が１２５ｍｍ、ロールの下端から２０ｍｍの高さまでロールが表面処理組成に浸かっており、ロール回転速度が０．２～８ｍ／分であった。その後、１１０℃で熱処理工程を行い、単繊度が２０～１００デシテックスの各熱処理後人工毛髪用繊維を得た。
　ギアマシン（ＳＵＮＧ　ＪＩＮ　ＩＮＤＵＳＴＲＩＡＬ　ＣＯ．，ＬＴＤ．製「ＮＥＷ　ＹＡＫＩ　ＢＲＡＩＤ　ＣＲＩＭＰＩＮＧ　Ｍ／Ｃ－２．５ｍｍ」）を用いて、ギアピッチ２．５ｍｍ、予熱９０℃、ギアロール温度９０℃、ギアロール回転速度１ｍ／分の条件で、各熱処理後人工毛髪用繊維にギア加工を施し、ギア加工後人工毛髪用繊維を得た。
＜人工毛髪用繊維束の作製＞
　表２又は表３に示す割合で、各ギア加工後人工毛髪用繊維をよく混合して人工毛髪用繊維束を得た。また、比較例１～５及び８については、１種類の各ギア加工後人工毛髪用繊維のみからなる人工毛髪用繊維束を得た。このようにして作製した各人工毛髪用繊維束について、後述の試験・評価を行った結果を、表２及び表３に示す。
（動摩擦係数）
　上述の各人工毛髪用繊維束のうち、長さ３００ｍｍ、質量１０ｇの評価用人工毛髪用繊維束について、一端から１００ｍｍの位置から他端方向に、移動速度１０ｍｍ／秒、移動距離４５ｍｍ、荷重２００ｇでウレタン製端子（ＴＲＩＮＩＴＹ－ＬＡＢ社製、触覚接触子、指モデル）を移動させたときの、摺動後の摩擦係数を、静・動摩擦測定機（ＴＲＩＮＩＴＹ－ＬＡＢ社製「ＴＬ２０１Ｔｔ」）を用いて測定した。各評価用人工毛髪用繊維束の異なる箇所について５回測定した平均値を、各人工毛髪用繊維束の動摩擦係数とした。
（静摩擦係数）
　上述の測定を行ったときの、摺動開始時の摩擦係数の平均値を、各人工毛髪用繊維束の静摩擦係数とした。
（均一性）
　上述の測定を行ったときの、動摩擦係数の標準偏差の値を、各人工毛髪用繊維束の均一性とした。
（滑りにくさ）
　上述の各人工毛髪用繊維束のうち、長さ６００ｍｍ、質量１２０ｇの評価用人工毛髪用繊維束について、毛髪用繊維処理技術者（実務経験５年以上）１０人が三つ編み状に編込みを行った時に感じる繊維の滑りにくさの度合いを、"滑りにくい"又は"滑りやすい"の２ランク評価を行い、下記の基準で評価した。
　　５：１０人が滑りにくいと評価
　　４：７～９人が滑りにくいと評価
　　３：５～６人が滑りにくいと評価
　　２：２～４人が滑りにくいと評価
　　１：１人以下が滑りにくいと評価
（櫛通り性）
　上述の各人工毛髪用繊維束のうち、長さ６００ｍｍ、質量１２０ｇの評価用人工毛髪用繊維束について、毛髪用繊維処理技術者（実務経験５年以上）１０人が手櫛を通したときに感じる指の通りやすさの度合いを、"櫛通りが良い"又は"櫛通りが悪い"の２ランク評価を行い、下記の基準で評価した。
　　５：１０人が櫛通りが良いと評価
　　４：７～９人が櫛通りが良いと評価
　　３：５～６人が櫛通りが良いと評価
　　２：２～４人が櫛通りが良いと評価
　　１：１人以下が櫛通りが良いと評価
（総合評価）
　上述の滑りにくさ及び櫛通り性の評価結果にもとづき、下記の基準で総合評価した。

Claims (9)

  1. 　人工毛髪用繊維束であって、
    　合成繊維に異なる表面処理組成物が付着している少なくとも２種類以上の人工毛髪用繊維を含み、
    　前記人工毛髪用繊維束の動摩擦係数が０．２３～０．２６である、人工毛髪用繊維束。
  2. 　人工毛髪用繊維束であって、
    　動摩擦係数の異なる少なくとも２種類以上の人工毛髪用繊維を含み、
    　前記動摩擦係数が０．２５未満の人工毛髪用繊維と、０．２５以上の人工毛髪用繊維とを、それぞれ１種類以上含む、人工毛髪用繊維束。
  3. 　前記表面処理組成物が、それぞれ、脂肪酸骨格含有化合物、ポリアルキレングリコール、シリコーンオイル、ポリオキシアルキレンアルキルエーテル、鉱物油、カチオン系界面活性剤、アルキルアルキレート及びポリオキシエチレンアルキルエーテルからなる群より選ばれる１以上を含む、請求項１に記載の人工毛髪用繊維束。
  4. 　前記人工毛髪用繊維における前記表面処理組成物の付着量が、前記合成繊維を基準として０．０５質量％～１．０質量％である、請求項１又は請求項３に記載の人工毛髪用繊維束。
  5. 　前記２種類以上の人工毛髪用繊維が、均一に分散されている、請求項１又は請求項２に記載の人工毛髪用繊維束。
  6. 　前記人工毛髪用繊維束の前記動摩擦係数を５回測定するとき、標準偏差が０．０４以下である、請求項５に記載の人工毛髪用繊維束。
  7. 　前記合成繊維が、塩化ビニルの単独重合体、塩化ビニル－アクリロニトリル共重合体、ポリエチレンテレフタレート、ポリアミド系樹脂、ポリプロピレン及びアクリロニトリル－スチレン共重合体からなる群より選ばれる１以上を含む、請求項１又は請求項３に記載の人工毛髪用繊維束。
  8. 　請求項１又は請求項２に記載の人工毛髪用繊維束を備える、頭髪装飾製品。
  9. 　請求項８に記載の頭髪装飾製品であって、ブレードを含む、頭髪装飾製品。
PCT/JP2024/041655 2023-11-30 2024-11-25 人工毛髪用繊維束及び頭髪装飾製品 Pending WO2025115809A1 (ja)