WO2024105999A1 - Tôle d'acier laminée à chaud et son procédé de production - Google Patents

Tôle d'acier laminée à chaud et son procédé de production Download PDF

Info

Publication number
WO2024105999A1
WO2024105999A1 PCT/JP2023/033820 JP2023033820W WO2024105999A1 WO 2024105999 A1 WO2024105999 A1 WO 2024105999A1 JP 2023033820 W JP2023033820 W JP 2023033820W WO 2024105999 A1 WO2024105999 A1 WO 2024105999A1
Authority
WO
WIPO (PCT)
Prior art keywords
hot
less
steel sheet
rolled steel
rolling
Prior art date
Application number
PCT/JP2023/033820
Other languages
English (en)
Japanese (ja)
Inventor
典晃 ▲高▼坂
広志 松田
Original Assignee
Ｊｆｅスチール株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ｊｆｅスチール株式会社 filed Critical Ｊｆｅスチール株式会社
Priority to JP2024504863A priority Critical patent/JP7569029B2/ja
Publication of WO2024105999A1 publication Critical patent/WO2024105999A1/fr

Abstract

La présente invention concerne une tôle d'acier laminée à chaud ayant une limite d'élasticité supérieure ou égale à 650 MPa, et ayant une excellente aptitude au façonnage par flexion, une excellente aptitude au formage de bride par étirage et une excellente aptitude au formage de bride par rétraction. La présente invention concerne également un procédé de production de celle-ci. L'invention concerne une tôle d'acier laminée à chaud ayant une composition de composants choisie arbitrairement parmi C, Si, Mn, P, S, Al, N, B, Ti et Nb, ayant une structure métallique qui, en termes de rapport de surface, est de 0 à 75 % de ferrite, le total de la baïnite, martensite, martensite revenue et l'austénite résiduelle n'étant pas supérieur à 3 %, et les grains cristallins comprenant une limite d'angle faible n'étant pas inférieurs à 25 %, ladite tôle d'acier laminée à chaud comprenant un carbure incluant du Ti ou du Nb ayant une taille de particule moyenne inférieure ou égale à 8 nm, la limite d'élasticité n'étant pas inférieure à 650 MPa. L'invention concerne également un procédé de production d'une tôle d'acier laminée à chaud, ledit procédé comprenant : une étape de laminage grossier dans laquelle une matière première d'acier ayant la composition de composants ci-dessus est chauffée ou non chauffée ; une étape de laminage de finition dans laquelle une température de départ est supérieure à 1 000 °C, la réduction au laminage dans chacun d'un premier passage et d'un deuxième passage n'est pas inférieure à 35 %, et la réduction au laminage totale d'un troisième passage à l'achèvement du laminage n'est pas supérieure à 85 % ; une étape de refroidissement ; et une étape d'enroulement.
PCT/JP2023/033820 2022-11-16 2023-09-19 Tôle d'acier laminée à chaud et son procédé de production WO2024105999A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2024504863A JP7569029B2 (ja) 2022-11-16 2023-09-19 熱延鋼板およびその製造方法

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2022-183476 2022-11-16
JP2022183476 2022-11-16

Publications (1)

Publication Number Publication Date
WO2024105999A1 true WO2024105999A1 (fr) 2024-05-23

Family

ID=91084303

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2023/033820 WO2024105999A1 (fr) 2022-11-16 2023-09-19 Tôle d'acier laminée à chaud et son procédé de production

Country Status (2)

Country Link
JP (1) JP7569029B2 (fr)
WO (1) WO2024105999A1 (fr)

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2012147898A1 (fr) * 2011-04-25 2012-11-01 Ｊｆｅスチール株式会社 Tôle d'acier à résistance élevée présentant une excellente aptitude à la déformation et stabilité des propriétés du matériau et son procédé de fabrication
WO2014119259A1 (fr) * 2013-01-31 2014-08-07 Ｊｆｅスチール株式会社 Tôle d'acier laminée à chaud à haute résistance et procédé de fabrication associé
WO2015093596A1 (fr) * 2013-12-19 2015-06-25 日新製鋼株式会社 Tôle d'acier revêtue par immersion à chaud par un système à base de zn-al-mg ayant une excellente aptitude au façonnage et son procédé de fabrication
WO2016136810A1 (fr) * 2015-02-24 2016-09-01 新日鐵住金株式会社 Tôle d'acier laminée à froid et son procédé de fabrication
WO2018143318A1 (fr) * 2017-02-06 2018-08-09 Ｊｆｅスチール株式会社 Tôle d'acier plaquée de zinc fondu et procédé pour sa production
JP2021055135A (ja) * 2019-09-27 2021-04-08 日本製鉄株式会社 溶融Ｚｎ−Ａｌ−Ｍｇ系めっき鋼板およびその製造方法

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2012147898A1 (fr) * 2011-04-25 2012-11-01 Ｊｆｅスチール株式会社 Tôle d'acier à résistance élevée présentant une excellente aptitude à la déformation et stabilité des propriétés du matériau et son procédé de fabrication
WO2014119259A1 (fr) * 2013-01-31 2014-08-07 Ｊｆｅスチール株式会社 Tôle d'acier laminée à chaud à haute résistance et procédé de fabrication associé
WO2015093596A1 (fr) * 2013-12-19 2015-06-25 日新製鋼株式会社 Tôle d'acier revêtue par immersion à chaud par un système à base de zn-al-mg ayant une excellente aptitude au façonnage et son procédé de fabrication
WO2016136810A1 (fr) * 2015-02-24 2016-09-01 新日鐵住金株式会社 Tôle d'acier laminée à froid et son procédé de fabrication
WO2018143318A1 (fr) * 2017-02-06 2018-08-09 Ｊｆｅスチール株式会社 Tôle d'acier plaquée de zinc fondu et procédé pour sa production
JP2021055135A (ja) * 2019-09-27 2021-04-08 日本製鉄株式会社 溶融Ｚｎ−Ａｌ−Ｍｇ系めっき鋼板およびその製造方法

Also Published As

Publication number Publication date
JPWO2024105999A1 (fr) 2024-05-23
JP7569029B2 (ja) 2024-10-17

Similar Documents

Publication Publication Date Title
JP6052472B2 (ja) 高強度溶融亜鉛めっき鋼板およびその製造方法
JP4635525B2 (ja) 深絞り性に優れた高強度鋼板およびその製造方法
JP5565534B2 (ja) 高強度熱延鋼板及びその製造方法
WO2011162412A1 (fr) Tôle d'acier laminée à chaud hautement résistante présentant une excellente capacité à former des bords par étirage et son procédé de production
WO2020136988A1 (fr) Tôle en acier galvanisé à chaud hautement résistante, et procédé de fabrication de celle-ci
WO2016113788A1 (fr) Tôle d'acier haute résistance galvanisée à chaud au trempé et son procédé de production
KR20210091790A (ko) 강판
WO2013046476A1 (fr) Tôle d'acier à haute résistance et son procédé de fabrication
WO2014188966A1 (fr) Tôle d'acier laminée à chaud et son procédé de fabrication
JP4501699B2 (ja) 深絞り性と伸びフランジ性に優れた高強度鋼板およびその製造方法
CN113366134B (zh) 高强度钢板及其制造方法
TW202016327A (zh) 熱軋鋼板及其製造方法
WO2016120914A1 (fr) Tôle d'acier plaquée à résistance élevée et procédé pour sa fabrication
JP4407449B2 (ja) 高強度鋼板およびその製造方法
WO2017168961A1 (fr) Tôle d'acier mince, tôle d'acier plaquée, procédé de fabrication de tôle d'acier laminée à chaud, procédé de fabrication de tôle d'acier laminée à froid très dure, procédé de fabrication de tôle d'acier mince, et procédé de fabrication de tôle d'acier plaquée
JP2004250749A (ja) バーリング性高強度薄鋼板およびその製造方法
JP5594438B2 (ja) 高張力熱延めっき鋼板およびその製造方法
JP7569029B2 (ja) 熱延鋼板およびその製造方法
JP5076480B2 (ja) 強度−延性バランスと深絞り性に優れた高強度鋼板およびその製造方法
WO2021172299A1 (fr) Tôle d'acier, élément et procédés respectivement pour la production de ladite tôle d'acier et dudit élément
WO2021172298A1 (fr) Tôle d'acier, élément et procédés respectivement pour la production de ladite tôle d'acier et dudit élément
WO2021172297A1 (fr) Tôle d'acier, élément et procédés respectivement pour la production de ladite tôle d'acier et dudit élément
WO2021140901A1 (fr) Tôle d'acier, et procédé de fabrication de celle-ci
JP5861434B2 (ja) 打ち抜き性に優れた高強度熱延鋼板およびその製造方法
JP2012158797A (ja) 高強度鋼板およびその製造方法

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 23891157

Country of ref document: EP

Kind code of ref document: A1