WO2024080268A1 - シートパッド - Google Patents

シートパッド Download PDF

Info

Publication number
WO2024080268A1
WO2024080268A1 PCT/JP2023/036683 JP2023036683W WO2024080268A1 WO 2024080268 A1 WO2024080268 A1 WO 2024080268A1 JP 2023036683 W JP2023036683 W JP 2023036683W WO 2024080268 A1 WO2024080268 A1 WO 2024080268A1
Authority
WO
WIPO (PCT)
Prior art keywords
polyurethane foam
less
seat pad
polyether polyol
content
Prior art date
Application number
PCT/JP2023/036683
Other languages
English (en)
French (fr)
Inventor
景太 今井
哲史 近藤
匠 三國
Original Assignee
株式会社イノアックコーポレーション
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 株式会社イノアックコーポレーション filed Critical 株式会社イノアックコーポレーション
Publication of WO2024080268A1 publication Critical patent/WO2024080268A1/ja

Abstract

シートパッドは、ポリウレタンフォームを備え、前記ポリウレタンフォームは、たわみ係数が２．８以下であり、変位率（＝ｔ1×１００／ｔ0）が３０％以上である。但し、ｔ0は、前記ポリウレタンフォームから切り出された平板状試料の厚み、ｔ1は、前記平板状試料を用いて、ＪＡＳＯ　Ｂ４０８に準拠して減衰特性を測定したときの鉄研盤の変位量（沈み込み量）の最大値。シートパッドは、ｔ0＝５０ｍｍであるときの前記変位率が４５％以上であるものが好ましい。

Description

シートパッド
　本発明は、シートパッドに関し、さらに詳しくは、たわみ係数が小さく、かつ、変位率が大きいポリウレタンフォームを備えたシートパッドに関する。
　自動車用シートは、シートクッション（座面部）とシートバック（背面部）とが分離しているタイプと、両者が一体化しているタイプとがある。
　また、自動車用シートは、一般に、
（ａ）乗員が着座したときに、乗員の荷重を受け止めるためのシートパッドと、
（ｂ）シートパッドを支持するためのフレームと、
（ｃ）シートパッドの外表面を覆うトリムカバーと
を備えている。
　シートパッドには、一般に、ポリウレタンフォームが用いられる。
　シートパッドを備えた自動車用シートに乗員が着座すると、シートパッドに加わる荷重の大きさに比例して、シートパッドが荷重方向に圧縮される。シートパッドに加わる荷重の大きさは、自動車用シートの形状、シートバックの傾き、自動車用シートに接触する人体の部位、乗員の姿勢、自動車が走行する路面の凹凸状態などに応じて異なる。そのため、シートパッドのたわみ係数やたわみ量（又は変位率）が不適切であると、座り心地の悪いシートとなる場合がある。
　そこでこの問題を解決するために、従来から種々の提案がなされている。
　例えば、特許文献１には、
（ａ）グリセリンにプロピレンオキシドを付加させた水酸基価１６８ｍｇＫＯＨ／ｇの化合物（開始剤１）に、エチレンオキシド８質量％含むエチレンオキシド／プロピレンオキシド混合物を反応させることにより得られるポリオールＡ：６０質量部と、
（ｂ）開始剤１にプロピレンオキシドを反応させることにより得られるポリオールＧ５中に、ポリマー粒子が分散しているポリオールＫ：４０質量部と、
（ｃ）ＴＤＩ－８０（ＮＯＣ含有量：４４．８質量％）：イソシアネートインデックスで１０５に相当する量と
を含む原料を反応させることにより得られる自動車シート用軟質ポリウレタンフォームが開示されている。
　同文献には、
（Ａ）このような方法により、Ｘ値（＝荷重８８３Ｎ時の静バネ定数／荷重９８Ｎ時の静バネ定数）が２．９４である軟質ポリウレタンフォームが得られる点、及び、
（Ｂ）このような軟質ポリウレタンフォームを自動車用シートに適用すると、座り込んだ後の底付き感が解消される点
が記載されている。
　特許文献２には、
　着座部を構成するクッション本体と、
　クッション本体の底面に一体的に設けられる低通気性フォームと
からなるシートパッドが開示されている。
　同文献には、クッション本体の底面に低通気性フォームを一体的に設けると、乗り心地を悪化させる振動を吸収できる点が記載されている。
　特許文献３には、
（ａ）数平均分子量７０００、平均官能基数３、水酸基価２６ｍｇＫＯＨ／ｇであるポリエーテルポリオール：９０重量部と、
（ｂ）数平均分子量５０００、平均官能基数３、水酸基価２５ｍｇＫＯＨ／ｇ、固形分３０％であるポリマーポリオール：１０重量部と、
（ｃ）粘度７２８０ｍＰａ・ｓ（２５℃）、表面張力２０．０８ｍＮ／ｍ（２５℃）である直鎖状シリコーン系整泡剤：０．５重量部と、
（ｄ）ＴＤＩ（８０重量％）とＭＤＩ（２０重量％）の混合物（ＮＣＯ＝４４．８％）：イソシアネートインデックスで１００に相当する量と
を含む原料を反応させることにより得られるポリウレタンフォームが開示されている。
　同文献には、このような方法により、従来よりも厚みを薄くしても底突きを生じ難く、かつ通気性が大きいポリウレタンフォームを得ることができる点が記載されている。
　特許文献４には、シートパッドではないが、非線形粘弾性挙動を有する圧縮性材料の非線形粘弾性挙動をシミュレーションする変形解析手法が開示されている。
　同文献には、一般化Ｍａｘｗｅｌｌモデルによる線形粘弾性部分と、静水応力に依存した降伏条件式を有する圧縮性弾塑性部分とを並列に備えたモデルを使用すると、ウレタンフォームがゆっくりと押されたときの減衰挙動を高精度で解析できる点が記載されている。
　特許文献５には、
（ａ）三次元構造のネット材を金型内に配置し、金型内においてポリウレタンを発泡させることにより、ポリウレタンフォーム製のクッション材に三次元構造のネット材が組み込まれたシートバック部を成形し、
（ｂ）シートバック部の両側部に突出しているネット材に張力を付与した状態で、ネット材をフレームに固定する
ことにより得られる自動車用シートが開示されている。
　同文献には、
（Ａ）このような方法により、ポリウレタンフォームからなるクッション材に三次元構造のネット材が一体的に組み込まれたシートバック部が得られる点、及び、
（Ｂ）ネット材にポリウレタンが含浸している部分は面剛性が高いので、乗員の後方から衝撃が加えられたときに、衝撃を減衰させることができる点
が記載されている。
　シートパッドの硬さや弾力性は、着座したときの座り心地に影響を与える。クッション感をより大きくするためには、高荷重域においてより大きくたわむこと、すなわち、たわみ係数が小さいことが好ましい。また、着座したときの底付き感を低減するためには、変位率が大きいことが好ましい。しかしながら、小さなたわみ係数と大きな変位率とを両立させたシートパッドが提案された例は、従来にはない。
特開２００３－１１９２４０号公報 特開２００５－１７７１７１号公報 特開２０１９－１９４３２１号公報 特開２０２０－０９４９８０号公報 特開２００２－１０２００８号公報
　本発明が解決しようとする課題は、ポリウレタンフォームからなり、たわみ係数が小さく、かつ、変位率が大きいシートパッドを提供することにある。
　上記課題を解決するために本発明に係るシートパッドは、
　ポリウレタンフォームを備え、
　前記ポリウレタンフォームは、
　たわみ係数が２．８以下であり、
　次の式（１）で表される変位率が３０％以上である。
　変位率＝ｔ1×１００／ｔ0　　　　　…（１）
　但し、
　ｔ0は、前記ポリウレタンフォームから切り出された平板状試料の厚み、
　ｔ1は、前記平板状試料を用いて、ＪＡＳＯ　Ｂ４０８に準拠して減衰特性を測定したときの鉄研盤の変位量（沈み込み量）の最大値。
　前記ポリウレタンフォームは、ポリオール成分と、ポリイソシアネート成分とを含む原料混合物を反応させることにより得られ、
　前記ポリオール成分は、
（ａ）ＥＯ含有率が５０ｍｏｌ％以上であり、
（ｂ）官能基数が２．０以上３．０以下であり、
（ｃ）重量平均分子量が３５００超である
１種又は２種以上のポリエーテルポリオールＡを含み
　前記ポリイソシアネート成分は、カルボジイミド変性ＭＤＩを含む
ものが好ましい。
　ポリウレタンフォームを製造する場合において、所定の条件を満たすポリエーテルポリオールＡと、カルボジイミド変性ＭＤＩとを含む原料混合物を用いると、たわみ係数が２．８以下であり、かつ、変位率が３０％以上であるポリウレタンフォームが得られる。
　たわみ係数が２．８以下となるのは、ＥＯ含有率の高いポリエーテルポリオールＡを用いているために、高分子鎖中に含まれる側鎖の数が相対的に少なくなり、高分子鎖間の絡み合いが少なくなるため、及び、これによって分子鎖が伸縮しやすくなり、ポリウレタンフォームに弾性が付与されるためと考えられる。
　変位率が３０％以上となるのは、重量平均分子量が大きいポリエーテルポリオールＡを用いているためと考えられる。
減衰試験機の模式図である。 実施例１～４及び比較例１～２で得られたポリウレタンフォームのＦＳカーブである。 実施例１～４及び比較例１～２で得られたポリウレタンフォーム（厚み１００ｍｍ）の減衰試験の結果である。 実施例１～４及び比較例１～２で得られたポリウレタンフォーム（厚み５０ｍｍ）の減衰試験の結果である。
　以下、本発明の一実施の形態について詳細に説明する。
［１．　シートパッド］
　本発明に係るシートパッドは、ポリオール成分と、ポリイソシアネート成分とを含む原料混合物を反応させることにより得られたポリウレタンフォームからなる。原料混合物は、通常、架橋剤と、発泡剤と、触媒とをさらに含む。
［１．１．　ポリウレタンフォーム］
　シートパッドを構成するポリウレタンフォームは、所定の条件を満たす原料混合物を発泡及び反応させることにより得られる。ポリウレタンフォームの製造方法の詳細については、後述する。
［１．２．　特性］
［１．２．１．　たわみ係数］
　「たわみ係数」とは、ＪＩＳ　Ｋ　６４００－２：２０１２に準拠して測定される値をいう。具体的には、「たわみ係数」とは、７５％の予備圧縮の後、一定の速度で７５％まで圧縮した時の、６５％圧縮での力（Ｆ65%）を２５％圧縮での力（Ｆ25%）で除した値（＝Ｆ65%／Ｆ25%）をいう。
　本発明に係るポリウレタンフォームは、後述するように、原料の１つとして、ＥＯ含有率の高いポリエーテルポリオールＡを用いている。ＥＯ含有率の高いポリエーテルポリオールＡを用いると、ポリウレタンフォームのたわみ係数が相対的に小さくなる。これは、高分子鎖中に含まれる側鎖の数が相対的に少なくなり、高分子鎖間の絡み合いが少なくなるため、及び、これによって分子鎖が伸縮しやすくなり、ポリウレタンフォームに弾性が付与されるためと考えられる。一般に、たわみ係数が小さくなるほど高荷重域においてより大きくたわむので、クッション感が大きくなる。
　クッション感を大きくするためには、ポリウレタンフォームのたわみ係数は、２．８以下である必要がある。製造条件を最適化すると、たわみ係数は、２．７以下、２．６以下、あるいは、２．５以下となる。
　一方、たわみ係数が小さくなりすぎると、たわみ量が大きくなりすぎ、底付き感が大きくなる場合がある。従って、たわみ係数は、２．０以上が好ましい。たわみ係数は、さらに好ましくは、２．１以上、あるいは、２．２以上である。
［１．２．２．　変位率］
　「変位率」とは、次の式（１）で表される値をいう。
　変位率＝ｔ1×１００／ｔ0　　　　　…（１）
　但し、
　ｔ0は、前記ポリウレタンフォームから切り出された平板状試料の厚み、
　ｔ1は、前記平板状試料を用いて、ＪＡＳＯ　Ｂ４０８に準拠して減衰特性を測定したときの鉄研盤の変位量（沈み込み量）の最大値。
　変位率は、厳密には、平板状試料の厚みｔ0に依存する。本発明に係るポリウレタンフォームは、厚みｔ0が異なる複数の平板状試料を用いて複数の変位率を測定したときに、少なくとも１つの変位率が以下の条件を満たしていれば良い。
　一般に、変位率が大きくなるほど、着座したときのクッション性が大きくなる。このような効果を得るためには、変位率は３０％以上である必要がある。変位率は、好ましくは、３５％以上、４０％以上、４５％以上、５０％以上、あるいは、５５％以上である。
　本発明に係るポリウレタンフォームにおいて、製造条件を最適化すると、ｔ0＝５０ｍｍであるときの変位率は、４５％以上となる。製造条件をさらに最適化すると、ｔ0＝５０ｍｍであるときの変位率は、５５％、６０％以上、あるいは、６５％以上となる。
　同様に、本発明に係るポリウレタンフォームにおいて、製造条件を最適化すると、ｔ0＝１００ｍｍであるときの変位率は、５０％以上となる。製造条件をさらに最適化すると、ｔ0＝１００ｍｍであるときの変位率は、５５％以上となる。
［２．　ポリウレタンフォームの製造方法］
　シートパッドを構成するポリウレタンフォームは、
（ａ）ポリオール成分と、ポリイソシアネート成分とを含む原料混合物を調製し、
（ｂ）原料混合物を反応させる
ことにより得られる。
　原料混合物は、通常、架橋剤と、発泡剤と、触媒とをさらに含む。
［２．１．　主原料］
［２．１．１．　ポリオール成分］
　ポリオール成分は、ポリウレタンフォームの主原料の１つである。
　本発明において、ポリオール成分は、
（ａ）ＥＯ含有率が５０ｍｏｌ％以上であり、
（ｂ）官能基数が２．０以上３．０以下であり、
（ｃ）重量平均分子量が３５００超である
ポリエーテルポリオールＡを含む。
　ポリオール成分は、このような条件を満たす１種類のポリエーテルポリオールＡを含むものでも良く、あるいは、このような条件を満たす２種以上のポリエーテルポリオールＡを含むものでも良い。
　ポリオール成分は、
（ａ）ＥＯ含有率が３０ｍｏｌ％以下であり、
（ｂ）官能基数が２．０以上である
ポリエーテルポリオールＢをさらに含むものでも良い。
　ポリオール成分は、このような条件を満たす１種類のポリエーテルポリオールＢを含むものでも良く、あるいは、このような条件を満たす２種以上のポリエーテルポリオールＢを含むものでも良い。
［Ａ．　ポリエーテルポリオールＡ］
［Ａ．１．　ＥＯ含有率］
　ポリエーテルポリオールＡの「ＥＯ含有率（ｍｏｌ％）」とは、ポリエーテルポリオールＡに含まれるアルキレンオキサイド単位の総モル数に対する、エチレンオキサイド（ＥＯ）単位のモル数の割合をいう。
　ポリエーテルポリオールＡは、ＥＯ単位以外のアルキレンオキサイド単位を含むものでも良い。この場合、ＥＯ単位以外のアルキレンオキサイド単位の種類は特に限定されないが、プロピレンオキサイド（ＰＯ）単位が好ましい。
　ポリエーテルポリオールＡのＥＯ含有率は、主として、たわみ係数に影響を与える。一般に、ポリエーテルポリオールＡのＥＯ含有率が高くなるほど、たわみ係数が小さくなる。これは、ＥＯ含有率が高くなるほど、高分子鎖中に含まれる側鎖（－ＣＨ3）の数が相対的に少なくなり、高分子鎖間の絡み合いが少なくなるため、及び、これによって分子鎖が伸縮しやすくなり、ポリウレタンフォームに弾性が付与されるためと考えられる。
　このような効果を得るためには、ポリエーテルポリオールＡのＥＯ含有率は、５０．０ｍｏｌ％以上が好ましい。ＥＯ含有率は、さらに好ましくは、６０．０ｍｏｌ％以上、７０．０ｍｏｌ％以上、８０．０ｍｏｌ％以上、あるいは、９０．０ｍｏｌ％以上である。ポリエーテルポリオールＡのＥＯ含有率は、１００．０ｍｏｌ％でも良い。
［Ａ．２．　官能基数］
　ポリエーテルポリオールＡの官能基数は、たわみ係数に影響を与える。一般に、ポリエーテルポリオールＡの官能基数が大きくなるほど、ポリウレタンフォームの剛性が高くなり、圧縮残留歪みが小さくなる。このような効果を得るためには、ポリエーテルポリオールＡの官能基数は、２．０以上が好ましい。官能基数は、さらに好ましくは、２．１以上、あるいは、２．２以上である。
　一方、ポリエーテルポリオールＡの官能基数が過剰になると、ポリウレタンフォームの硬さが過度に高くなり、たわみ係数が増大する場合がある。従って、ポリエーテルポリオールＡの官能基数は、３．０以下が好ましい。官能基数は、さらに好ましくは、２．９以下、あるいは、２．８以下である。
［Ａ．３．　重量平均分子量］
　ポリエーテルポリオールＡの重量平均分子量が大きくなるほど、ポリウレタンフォームの硬度が低下し、たわみやすくなる。このような効果を得るためには、ポリエーテルポリオールＡの重量平均分子量は、３５００超が好ましい。重量平均分子量は、さらに好ましくは、４０００以上、あるいは、５０００以上である。
　一方、ポリエーテルポリオールＡの重量平均分子量が大きくなりすぎると、原料混合物の粘度が過度に高くなり、製造性が低下する場合がある。また、原料混合物の反応性が低下し、ポリウレタンフォームの引き裂き強度が低下する場合がある。従って、重量平均分子量は、１２０００以下が好ましい。重量平均分子量は、さらに好ましくは、１００００以下、あるいは、８０００以下である。
［Ａ．４．　水酸基価］
　ポリエーテルポリオールＡの水酸基価が大きくなりすぎると、シートパッドとしたときの座り心地が悪くなる場合がある。従って、水酸基価は、７０ｍｇＫＯＨ／ｇ以下が好ましい。水酸基価は、さらに好ましくは、６０ｍｇＫＯＨ／ｇ以下、あるいは、５５ｍｇＫＯＨ／ｇ以下である。
　一方、ポリエーテルポリオールＡの水酸基価が小さくなりすぎると、ポリウレタンフォームが硬くなりすぎ、シートパッドとして用いたときに、良好な座り心地を保つことができなくなる場合がある。従って、水酸基価は、１０ｍｇＫＯＨ／ｇ以上が好ましい。水酸基価は、さらに好ましくは、１５ｍｇＫＯＨ／ｇ以上、あるいは、２０ｍｇＫＯＨ／ｇ以上である。
［Ｂ．　ポリエーテルポリオールＢ］
［Ｂ．１．　ＥＯ含有率］
　ポリエーテルポリオールＢの「ＥＯ含有率（ｍｏｌ％）」とは、ポリエーテルポリオールＢに含まれるアルキレンオキサイド単位の総モル数に対する、エチレンオキサイド（ＥＯ）単位のモル数の割合をいう。
　ポリエーテルポリオールＢは、ＥＯ単位以外のアルキレンオキサイド単位を含むものでも良い。この場合、ＥＯ単位以外のアルキレンオキサイド単位の種類は特に限定されないが、プロピレンオキサイド（ＰＯ）単位が好ましい。
　ポリエーテルポリオールＢのＥＯ含有率が高くなりすぎると、原料混合物の反応性が低下する場合がある。また、フォーム状態やフォームの通気性が悪化する場合がある。従って、ＥＯ含有率は、３０ｍｏｌ％以下が好ましい。ＥＯ含有率は、さらに好ましくは、２０ｍｏｌ％以下、１０ｍｏｌ％以下、あるいは、５ｍｏｌ％以下である。ＥＯ含有率は、ゼロでも良い。
［Ｂ．２．　官能基数］
　ポリエーテルポリオールＢの官能基数は、２．０以上であれば良い。
　但し、ポリエーテルポリオールＢの官能基数が大きくなりすぎると、ポリウレタンフォームの伸びが低下する場合がある。従って、官能基数は、４．０以下が好ましい。官能基数は、さらに好ましくは、３．８以下、あるいは、３．６以下である。
［Ｂ．３．　重量平均分子量］
　ポリエーテルポリオールＢの重量平均分子量は、特に限定されるものではなく、目的に応じて最適な値を選択することができる。一般に、ポリエーテルポリオールＢの重量平均分子量が小さくなりすぎると、ポリウレタンフォームの伸び率や柔軟性を損ねるおそれがある。従って、重量平均分子量は、１０００以上が好ましい。重量平均分子量は、さらに好ましくは、２０００以上、あるいは、３０００以上である。
　一方、ポリエーテルポリオールＢの重量平均分子量が大きくなりすぎると、原料混合物の粘度が過度に上昇し、製造性が低下する場合がある。従って、重量平均分子量は、１２０００以下が好ましい。重量平均分子量は、さらに好ましくは、１００００以下、あるいは、８０００以下である。
［２．１．２．　ポリイソシアネート成分］
　ポリイソシアネート成分は、ポリウレタンフォームの主原料の他の１つである。
　本発明において、ポリイソシアネート成分は、少なくともカルボジイミド変性ＭＤＩを含む。ポリイソシアネート成分は、カルボジイミド変性ＭＤＩのみを含むものでも良く、あるいは、カルボジイミド変性ＭＤＩ以外のポリイソシアネート（以下、これを「ポリイソシアネートＢ」ともいう）をさらに含むものでも良い。
［Ａ．　カルボジイミド変性ＭＤＩ］
　カルボジイミド（－Ｎ＝Ｃ＝Ｎ－）変性ＭＤＩは、触媒存在下において、ジフェニルメタンジイソシアネート（ＭＤＩ）の－ＮＣＯ基間のＣＯ2発生を伴う縮合により生成されたものからなる。
　ポリイソシアネート成分として、カルボジイミド変性ＭＤＩを用いると、ポリウレタンフォームの弾性が高くなり、高荷重域でのたわみ量が大きくなる。
［Ｂ．　ポリイソシアネートＢ］
　本発明において、ポリイソシアネートＢの種類は、特に限定されるものではなく、目的に応じて最適なものを選択することができる。
　ポリイソシアネートＢとしては、具体的には、２官能の芳香族系イソシアネート、２官能の脂環式イソシアネート、２官能の脂肪族イソシアネート、官能基数が２を超えるイソシアネートなどがある。原料混合物は、これらのいずれか１種のポリイソシアネートＢを含むものでも良く、あるいは、２種以上を含むものでも良い。
　２官能の芳香族系イソシアネートとしては、例えば、
２，４－トリレンジイソシアネート、２，６－トリレンジイソシアネート、
ｍ－フェニレンジイソシネート、ｐ－フェニレンジイソシアネート、
４，４'－ジフェニルメタンジイソシアネート（４，４'－ＭＤＩ）、
２，４'－ジフェニルメタンジイソシアネート（２，４'－ＭＤＩ）、
２，２'－ジフェニルメタンジイソシアネート（２，２'－ＭＤＩ）、
キシリレンジイソシアネート、
３，３'－ジメチル－４，４'－ビフェニレンジイソネート、
３，３'－ジメトキシ－４，４'－ビフェニレンジイソシアネートなどがあり、これらの混合物であっても良い。
　２官能の脂環式イソシアネートとしては、例えば、
シクロヘキサン－１，４－ジイソシアネート、イソホロンジイソシアネート、
ジシクロヘキシルメタン－４，４'－ジイソシアネート、
メチルシクロヘキサンジイソシアネートなどがある。
　２官能の脂肪族系イソシアネートとしては、例えば、
ブタン－１，４－ジイソシアネート、ヘキサメチレンジイソシアネート、
イソプロピレンジイソシアネート、メチレンジイソシアネート、リジンイソシアネート
などがある。２官能以上のイソシアネートとしては、ポリメリックＭＤＩ、３官能以上のイソシアネートなどがある。
　官能基数が２を超えるイソシアネートとしては、例えば、
１－メチルベンゾール－２，４，６－トリイソシアネート、
１，３，５－トリメチルベンゾール－２，４，６－トリイソシアネート、
ビフェニル－２，４，４'－トリイソシアネート、
ジフェニルメタン－２，４，４'－トリイソシアネート、
メチルジフェニルメタン－４，６，４'－トリイソシアネート、
４，４'－ジメチルジフェニルメタン－２，２'，５，５'テトライソシアネート、
トリフェニルメタン－４，４'，４"－トリイソシアネート、
などがある。
［Ｃ．　ＮＣＯ基含有率（ＮＣＯ％）］
　「ＮＣＯ基含有率（ＮＣＯ％）」とは、ポリイソシアネート成分の総質量に対する、ＮＣＯ基の質量の割合をいう。
　ポリイソシアネート成分のＮＣＯ％は、３５％未満が好ましく、３０％未満がより好ましく、２９．５％以下がさらに好ましい。
［２．１．３．　架橋剤］
　原料混合物は、架橋剤を含むものでも良い。架橋剤は、少なくとも官能基数が３以上であり、かつ、活性水素原子を持つ官能基（例えば、水酸基、アミノ基など）を含む化合物が好ましい。架橋剤は、官能基数が３以上の化合物のみからなるものでも良く、あるいは、官能基数が３以上である化合物に加えて、官能基数が２である化合物をさらに含むものでも良い。
　架橋剤の官能基数は、圧縮残留歪みに影響を与える。圧縮残留歪の小さいポリウレタンフォームを得るためには、架橋剤の官能基数は、３以上が好ましい。
　一方、架橋剤の官能基数が大きくなりすぎると、ポリウレタンフォームの硬さが過度に高くなる場合がある。従って、架橋剤の官能基数は、６以下が好ましい。
　架橋剤の分子量は、特に限定されるものではなく、目的に応じて最適な値を選択することができる。架橋剤の分子量は、好ましくは、１０００以下、７００以下、あるいは、５００以下である。
　また、架橋剤の分子量は、６０以上、９０以上、あるいは、１２０以上が好ましい。
　架橋剤としては、例えば、グリセリン、ジエタノールアミン（ＤＥＡ）、多官能ポリオールなどがある。
　原料混合物には、これらのいずれか１種の架橋剤が含まれていても良く、あるいは、２種以上が含まれていても良い。
［２．１．４．　発泡剤］
　「発泡剤」とは、液状の原料混合物が樹脂化していく過程で原料混合物中に気泡を生成させるための添加剤をいう。
　本発明において、発泡剤は、
（ａ）圧力低下又は加熱によりガスを発生させる物理発泡剤、又は、
（ｂ）熱分解又は化学反応によりガスを発生させる化学発泡剤
のいずれであっても良い。
　物理発泡剤としては、例えば、
（ａ）シクロペンタン、イソペンタン、ノルマルペンタンなどの炭化水素、
（ｂ）塩化メチレン、トリクロロフルオロメタン、ジクロロジフルオロメタン、ノナフルオロブチルメチルエーテル、ペンタフルオロエチルメチルエーテル、ペンタフルオロイソプロピルメチルエーテルなどのハロゲン系化合物、
などがある。
　化学発泡剤としては、例えば、
（ａ）イソシアネート基と反応してＣＯ2を発生させる水、
（ｂ）熱分解によって、窒素、一酸化炭素、二酸化炭素、又は、アンモニアガスを発生させるアゾジカルボンアミド
などがある。
　原料混合物には、これらのいずれか１種の発泡剤が含まれていても良く、あるいは、２種以上が含まれていても良い。
　これらの中でも、発泡剤は、水が好ましい。発泡剤として水を用いると、水とイソシアネート基とが反応することにより発生したＣＯ2ガスが発泡を促す。また、水とイソシアネート基との反応熱が樹脂の硬化を促進する。
［２．１．５．　触媒］
　「触媒」とは、樹脂化反応を促進する作用が大きい触媒、及び／又は、泡化反応を促進する作用が大きい触媒をいう。
　なお、発泡剤として、化学発泡剤（水）を用いない場合には、樹脂化反応を促進する作用が大きい触媒を用いるのが好ましい。
　触媒としては、例えば、アミン系触媒、金属触媒などがある。アミン系触媒は、樹脂化反応と泡化反応の双方を促進する作用が大きい触媒である。金属触媒は、樹脂化反応を促進する作用が大きい触媒である。原料混合物には、これらのいずれか１種の触媒が含まれていても良く、あるいは、２種以上が含まれていても良い。
　アミン系触媒としては、例えば、
Ｎ，Ｎ－ジメチルシクロヘキシルアミン、Ｎ，Ｎ－ジメチルベンジルアミン、
Ｎ，Ｎ－ジメチルアミノエタノール、
Ｎ，Ｎ’，Ｎ’－トリメチルアミノエチルピペラジン、トリエチレンジアミン
等が挙げられる。
　金属触媒としては、例えば、
（ａ）スタナスオクトエート、ジブチルチンジラウレートなどの錫触媒、
（ｂ）フェニル水銀プロピオン酸塩などの水銀触媒、
（ｃ）オクテン酸鉛などの鉛触媒
等が挙げられる。
［２．２．　副原料］
　原料混合物は、上述した主原料に加えて、以下の１種又は２種以上の副原料をさらに含むものでも良い。副原料としては、具体的には、以下のようなものがある。
［２．２．１．　整泡剤］
　「整泡剤」とは、気泡の大きさや分布を均一化する作用がある添加剤をいう。
　原料混合物に整泡剤を添加すると、気泡の大きさや分布が均一なポリウレタンフォームを得ることができる。整泡剤としては、例えば、シリコーン系整泡剤、含フッ素化合物系整泡剤、公知の界面活性剤などがある。
［２．２．２．　難燃剤］
　「難燃剤」とは、ポリウレタンフォームを難燃化させる作用がある添加剤をいう。
　難燃剤としては、例えば、ハロゲン系難燃剤、リン系難燃剤、金属水酸化物系難燃剤、アンチモン系難燃剤などがある。
［２．３．　配合量、含有量］
［２．３．１．　主原料の配合量、含有量］
［Ａ．　ポリエーテルポリオールＡの配合量］
　「ポリエーテルポリオールＡの配合量（質量部）」とは、ポリオール成分の総質量を１００としたときの、ポリオール成分中のポリエーテルポリオールＡの総質量をいう。
　一般に、ポリエーテルポリオールＡの配合量が多くなるほど、ポリウレタンフォームのたわみ係数が小さくなる。このような効果を得るためには、ポリエーテルポリオールＡの配合量は、５０質量部以上が好ましい。配合量は、さらに好ましくは、６０質量部以上、あるいは、７０質量部以上である。
　ポリエーテルポリオールＡの配合量は、１００質量部でも良い。しかしながら、ポリエーテルポリオールＡの配合量が過剰になると、フォームの成形性が低下する場合がある。従って、ポリエーテルポリオールＡの配合量は、９０質量部以下が好ましい。
［Ｂ．　カルボジイミド変性ＭＤＩの含有量］
　「カルボジイミド変性ＭＤＩの含有量（質量％）」とは、ポリイソシアネート成分の総質量に対する、カルボジイミド変性ＭＤＩの質量の割合をいう。
　一般に、カルボジイミド変性ＭＤＩの含有量が多くなるほど、ポリウレタンフォームのたわみ係数が小さくなり、かつ、変位率が大きくなる。このような効果を得るためには、カルボジイミド変性ＭＤＩの含有量は、５０質量％以上が好ましい。含有量は、さらに好ましくは、６０質量％以上、あるいは、７０質量％以上である。
　カルボジイミド変性ＭＤＩの含有量は、１００質量％でも良い。カルボジイミド変性ＭＤＩの含有量は、好ましくは、９０質量％以下、あるいは、８０質量％以下である。
　カルボジイミド変性ＭＤＩのＮＣＯ含有率は、４０％以下、３５％以下、あるいは、３２％以下が好ましく、特に３０％以下が好ましい。また、ＮＣＯ含有率は、１５％以上、２０％以上、２５％以上、あるいは、２７％以上が好ましい。
［Ｃ．　架橋剤の配合量］
　「架橋剤の配合量（質量部）」とは、ポリオール成分の総質量を１００としたときの、架橋剤の質量をいう。
　一般に、架橋剤の配合量が多くなるほど、ポリウレタンフォームの圧縮残留歪が小さくなる。このような効果を得るためには、架橋剤の配合量は、０質量部超が好ましい。配合量は、さらに好ましくは、１質量部以上、あるいは、２質量部以上である。
　一方、架橋剤の配合量が過剰になると、ポリウレタンフォームの硬さが過度に高くなる場合がある。従って、架橋剤の配合量は、１０質量部以下が好ましい。配合量は、さらに好ましくは、８質量部以下、あるいは、６質量部以下である。
［Ｄ．　ポリエーテルポリオールＢの配合量］
　「ポリエーテルポリオールＢの配合量（質量部）」とは、ポリオール成分の総質量を１００としたときの、ポリオール成分中のポリエーテルポリオールＢの質量をいう。
　一般に、ポリエーテルポリオールＢの配合量が過剰になると、相対的にポリエーテルポリオールＡの配合量が少なくなる。その結果、ポリウレタンフォームのたわみ係数が大きくなり、あるいは、変位率が低下する場合がある。従って、ポリエーテルポリオールＢの配合量は、５０質量部未満が好ましい。配合量は、さらに好ましくは、４０質量部以下、あるいは、３０質量部以下である。
［Ｅ．　イソシアネートインデックス］
　「イソシアネートインデックス」とは、原料混合物中の活性水素基の当量に対する、原料混合物中のポリイソシアネートのイソシアネート基の当量の比に１００を掛けた値をいう。
　本発明において、イソシアネートインデックスは、特に限定されるものではなく、目的に応じて最適な値を選択することができる。一般に、イソシアネートインデックスが大きくなるほど、圧縮残留歪が小さくなる。このような効果を得るためには、イソシアネートインデックスは、９０以上が好ましい。イソシアネートインデックスは、さらに好ましくは、９５以上である。
　一方、イソシアネートインデックスが大きくなりすぎると、ポリウレタンフォームの硬度が過度に高くなる場合がある。従って、イソシアネートインデックスは、１１５以下が好ましい。
［２．３．２．　副原料の配合量］
　本発明において、副原料の配合量は特に限定されるものではなく、目的に応じて最適な含有量を選択することができる。
［２．４．　原料混合物の反応］
　本発明に係るポリウレタンフォームの製造方法における発泡は、スラブ発泡及びモールド発泡のいずれを採用することもできる。
　スラブ発泡は、ポリウレタンフォーム製造用組成物（ポリウレタンフォームの原料）を混合してベルトコンベア上に吐出し、大気圧下、常温で発泡させる方法である。
　一方、モールド発泡は、モールド（金型）のキャビティにポリウレタンフォーム製造用原料（ポリウレタンフォームの原料）を混合して注入し、キャビティ形状に発泡させる方法である。モールド発泡は、シートパッドの形状に近い形状を有するポリウレタンフォームが得られる点で好ましい。
　なお、モールド成形する場合には、ポリイソシアネートは、粘度が低いものが好ましく、例えば、プレポリマータイプのポリイソシアネートは好ましくない。
［３．　作用］
　ポリウレタンフォームを製造する場合において、所定の条件を満たすポリエーテルポリオールＡと、カルボジイミド変性ＭＤＩとを含む原料混合物を用いると、たわみ係数が２．８以下であり、かつ、変位率が３０％以上であるポリウレタンフォームが得られる。
　このようなポリウレタンフォームをシートパッドとして用いた場合には、薄肉（例えば、５０ｍｍ以下）でも、優れたたわみ係数を有し、優れた減衰特性におけるたわみ量（変位率）を有する。
　たわみ係数が２．８以下となるのは、ＥＯ含有率の高いポリエーテルポリオールＡを用いているために、高分子鎖中に含まれる側鎖の数が相対的に少なくなり、高分子鎖間の絡み合いが少なくなるため、及び、これによって分子鎖が伸縮しやすくなり、ポリウレタンフォームに弾性が付与されるためと考えられる。
　変位率が３０％以上となるのは、重量平均分子量が大きいポリエーテルポリオールＡを用いているためと考えられる。
（実施例１～４、比較例１～２）
［１．　試料の作製］
　ポリエーテルポリオール、架橋剤、発泡剤、触媒、及び、整泡剤を所定の比率で配合し、混合液（以下、「成分Ａ」ともいう）を得た。
　また、ポリメリックＭＤＩ、カルボジイミド変性ＭＤＩを含有するＭＤＩ（ＮＣＯ含有率：２９％、カルボジイミド変性ＭＤＩの含有量：７５質量％）、及び、ＭＤＩプレポリマー（ＮＣＯ含有率：２８．５％）を所定の比率で配合し、混合液（以下、「成分Ｂ」ともいう）を得た。
　さらに、イソシアネートインデックスが所定の値となるように、成分Ａと成分Ｂとを混合し、原料混合物を得た。表１に、成分Ａ及び成分Ｂの組成を示す。
　なお、実施例１は、ポリエーテルポリオールＡとして、ポリエーテルポリオール２（分子量：４０００、官能基数：２、ＥＯ含有率：８０ｍｏｌ％）のみを用いた例である。
　実施例２、３は、ポリエーテルポリオールＡとして、
（ａ）ポリエーテルポリオール２（分子量：４０００、官能基数：２、ＥＯ含有率：８０ｍｏｌ％）と、
（ｂ）ポリエーテルポリオール３（分子量：５０００、官能基数：３、ＥＯ含有率：８０ｍｏｌ％）と
の混合物を用いた例である。
　実施例４は、ポリエーテルポリオールＡとして、ポリエーテルポリオール３のみを用いた例である。
Figure JPOXMLDOC01-appb-T000001
　得られた原料混合物を、４００ｍｍ×４００ｍｍ×１００ｍｍの金型に注入し、型温約６０℃で発泡及び硬化させた。なお、キュア時間は５分とした。
［２．　試験方法］
［２．１．　コア密度］
　得られた発泡体からスキン層を取り除き、コア密度測定用の試料とした。得られた試料を用いて、ＪＩＳ　Ｋ　７２２２に準拠してコア密度を測定した。
［２．２．　２５％硬さ］
　ＪＩＳ　Ｋ　６４００－２　Ｄ法に準拠して、２５％硬さを測定した。
［２．３．　ヒステリシスロス］
　ＪＩＳ　Ｋ　６４００－２　Ｅ法に準拠して、ヒステリシスロスを測定した。
［２．４．　たわみ係数］
　ＪＩＳ　Ｋ　６４００－２　Ｅ法に準拠して、たわみ係数を測定した。たわみ係数は、６５％圧縮荷重を２５％圧縮荷重で割ることにより求めた。
［２．５．　応力緩和］
　ＪＩＳ　Ｋ　６４００－４に準拠して、応力緩和を求めた。荷重は１９６Ｎとし、加圧時間は５分とした。
［２．６．　減衰特性］
　図１に、減衰試験機の模式図を示す。試料の上方２０ｍｍの位置に、質量５０ｋｇの鉄研盤を配置した。その位置から鉄研盤を試料に向かって自由落下させた。落下後の鉄研盤の変位や、振動が停止するまでの時間から、試料の振動特性を評価した。
［３．　結果］
　表２に、結果を示す。なお、表２には、テストピースサイズ、及び、各物性値の評価試験方法も併せて示した。図２に、実施例１～４及び比較例１～２で得られたポリウレタンフォームのＦＳカーブを示す。図３に、実施例１～４及び比較例１～２で得られたポリウレタンフォーム（厚み１００ｍｍ）の減衰試験の結果を示す。図４に、実施例１～４及び比較例１～２で得られたポリウレタンフォーム（厚み５０ｍｍ）の減衰試験の結果を示す。表２及び図２～図４より、以下のことが分かる。
（１）比較例１は、ｔ0＝５０ｍｍにおける変位率及びｔ0＝１００ｍｍにおける変位率が、いずれも３０％未満となった。これは、重量平均分子量が３５００を超えるポリエーテルポリオールＡを含まないためと考えられる。
（２）比較例２は、変位率は大きいが、たわみ係数が２．８を超えた。これは、ポリエーテルポリオールＡの含有量が過度に少ないためと考えられる。
（３）実施例１～４は、いずれも、たわみ係数が２．８以下であった。また、試料の厚みｔ0によらず、いずれも、変位率が５０％以上であった。
Figure JPOXMLDOC01-appb-T000002
　以上、本発明の実施の形態について詳細に説明したが、本発明は上記実施の形態に何ら限定されるものではなく、本発明の要旨を逸脱しない範囲内で種々の改変が可能である。
　本発明に係るシートパッドは、自動車、航空機、鉄道車両の座席のシートパッド、ソファーやマットレス及びそれらのクッション材として使用することができる。

Claims (5)

  1. 　ポリウレタンフォームを備えるシートパッドであって、
    　前記ポリウレタンフォームは、
    　たわみ係数が２．８以下であり、
    　次の式（１）で表される変位率が３０％以上である
    シートパッド。
    　変位率＝ｔ1×１００／ｔ0　　　　　…（１）
    　但し、
    　ｔ0は、前記ポリウレタンフォームから切り出された平板状試料の厚み、
    　ｔ1は、前記平板状試料を用いて、ＪＡＳＯ　Ｂ４０８に準拠して減衰特性を測定したときの鉄研盤の変位量（沈み込み量）の最大値。
  2. 　ｔ0＝５０ｍｍであるときの前記変位率が４５％以上である請求項１に記載のシートパッド。
  3. 　ｔ0＝１００ｍｍであるときの前記変位率が５０％以上である請求項１に記載のシートパッド。
  4. 　前記ポリウレタンフォームは、ポリオール成分と、ポリイソシアネート成分とを含む原料混合物を反応させることにより得られ、
    　前記ポリオール成分は、
    （ａ）ＥＯ含有率が５０ｍｏｌ％以上であり、
    （ｂ）官能基数が２．０以上３．０以下であり、
    （ｃ）重量平均分子量が３５００超である
    １種又は２種以上のポリエーテルポリオールＡを含み
    　前記ポリイソシアネート成分は、カルボジイミド変性ＭＤＩを含む
    請求項１に記載のシートパッド。
  5. 　前記ポリオール成分は、
    （ａ）ＥＯ含有率が３０ｍｏｌ％以下であり、
    （ｂ）平均官能基数が２．０以上である
    １種又は２種以上のポリエーテルポリオールＢをさらに含む
    請求項４に記載のシートパッド。
PCT/JP2023/036683 2022-10-13 2023-10-10 シートパッド WO2024080268A1 (ja)