WO2024062850A1 - Film optique ainsi que procédé de fabrication de celui-ci, plaque de polarisation, et dispositif d'affichage d'images - Google Patents

Film optique ainsi que procédé de fabrication de celui-ci, plaque de polarisation, et dispositif d'affichage d'images Download PDF

Info

Publication number
WO2024062850A1
WO2024062850A1 PCT/JP2023/031117 JP2023031117W WO2024062850A1 WO 2024062850 A1 WO2024062850 A1 WO 2024062850A1 JP 2023031117 W JP2023031117 W JP 2023031117W WO 2024062850 A1 WO2024062850 A1 WO 2024062850A1
Authority
WO
WIPO (PCT)
Prior art keywords
group
optical film
optically anisotropic
anisotropic layer
liquid crystal
Prior art date
Application number
PCT/JP2023/031117
Other languages
English (en)
Japanese (ja)
Inventor
悠太 福島
智則 三村
慎平 吉田
勇太 高橋
Original Assignee
富士フイルム株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 富士フイルム株式会社 filed Critical 富士フイルム株式会社
Publication of WO2024062850A1 publication Critical patent/WO2024062850A1/fr

Abstract

L'invention a pour objet de fournir un film optique ainsi qu'un procédé de fabrication de celui-ci, une plaque de polarisation et un dispositif d'affichage d'images, lequel film optique présente une orientation satisfaisante d'un composé cristallin liquide dans une couche d'anisotropie optique, et une inhibition d'apparition de défaut de point brillant. Le film optique de l'invention possède un corps de support et une couche d'anisotropie optique adjacents. La couche d'anisotropie optique est formée à l'aide d'une composition pour formation de couche d'anisotropie optique comprenant un composé cristallin liquide polymérisable. Le corps de support comprend un agent tensio-actif possédant un groupe hydrophile et un groupe hydrophobe, le groupe hydrophobe consistant en au moins une sorte de groupe choisie parmi un groupe alkyle de 5 à 29 atomes de carbone, un groupe à teneur en silicium et un groupe fluoré.
PCT/JP2023/031117 2022-09-22 2023-08-29 Film optique ainsi que procédé de fabrication de celui-ci, plaque de polarisation, et dispositif d'affichage d'images WO2024062850A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2022-151111 2022-09-22
JP2022151111 2022-09-22

Publications (1)

Publication Number Publication Date
WO2024062850A1 true WO2024062850A1 (fr) 2024-03-28

Family

ID=90454114

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2023/031117 WO2024062850A1 (fr) 2022-09-22 2023-08-29 Film optique ainsi que procédé de fabrication de celui-ci, plaque de polarisation, et dispositif d'affichage d'images

Country Status (1)

Country Link
WO (1) WO2024062850A1 (fr)

Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2015148745A (ja) * 2014-02-07 2015-08-20 大日本印刷株式会社 光学フィルム用転写積層体
WO2016043087A1 (fr) * 2014-09-19 2016-03-24 Dic株式会社 Composition polymérisable et film l'utilisant
WO2016171041A1 (fr) * 2015-04-24 2016-10-27 日本ゼオン株式会社 Procédé de fabrication de film multicouche et film multicouche
WO2017057005A1 (fr) * 2015-09-30 2017-04-06 日本ゼオン株式会社 Film optique et son procédé de fabrication
WO2018003653A1 (fr) * 2016-06-27 2018-01-04 Dic株式会社 Composition de cristaux liquides polymérisable, ainsi qu'objet optiquement anisotrope et élément d'affichage à cristaux liquides obtenus tous deux à l'aide de celle-ci
WO2020071169A1 (fr) * 2018-10-01 2020-04-09 富士フイルム株式会社 Dispositif d'affichage
JP2021015188A (ja) * 2019-07-11 2021-02-12 住友化学株式会社 長尺フィルム

Patent Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2015148745A (ja) * 2014-02-07 2015-08-20 大日本印刷株式会社 光学フィルム用転写積層体
WO2016043087A1 (fr) * 2014-09-19 2016-03-24 Dic株式会社 Composition polymérisable et film l'utilisant
WO2016171041A1 (fr) * 2015-04-24 2016-10-27 日本ゼオン株式会社 Procédé de fabrication de film multicouche et film multicouche
WO2017057005A1 (fr) * 2015-09-30 2017-04-06 日本ゼオン株式会社 Film optique et son procédé de fabrication
WO2018003653A1 (fr) * 2016-06-27 2018-01-04 Dic株式会社 Composition de cristaux liquides polymérisable, ainsi qu'objet optiquement anisotrope et élément d'affichage à cristaux liquides obtenus tous deux à l'aide de celle-ci
WO2020071169A1 (fr) * 2018-10-01 2020-04-09 富士フイルム株式会社 Dispositif d'affichage
JP2021015188A (ja) * 2019-07-11 2021-02-12 住友化学株式会社 長尺フィルム

Similar Documents

Publication Publication Date Title
KR102443875B1 (ko) 위상차 필름, 위상차 필름의 제조 방법, 적층체, 조성물, 편광판 및 액정 표시 장치
JP4802409B2 (ja) 光学補償フィルム、それを用いた偏光板及び液晶表示装置
JP4328243B2 (ja) 液晶表示装置
US11243436B2 (en) Liquid crystal display device
TWI391757B (zh) 光學功能薄膜，相位差薄膜，光學功能層形成用組成物，及光學功能薄膜之製造方法
JP2005505019A (ja) 透過型液晶表示装置
WO2005116741A1 (fr) Affichage à cristaux liquides
JP6677722B2 (ja) 水平配向型液晶表示装置
WO2006067916A1 (fr) Plaque de polarisation elliptique et affichage d’image l’employant
US10739641B2 (en) Liquid crystal display device
JP2010072516A (ja) 光学フィルム、偏光板、及び液晶表示装置
JP3935489B2 (ja) 液晶表示装置
JP2024022690A (ja) 光学積層体、画像表示装置及びガラス複合体
WO2018174194A1 (fr) Film optique, corps stratifié de film optique, plaque polarisante et dispositif d'affichage d'image
WO2018030449A1 (fr) Film optique, plaque polarisante et dispositif d'affichage d'image
JP2002207125A (ja) 光学補償シート及び液晶表示装置
WO2005116700A1 (fr) Plaque polarisante elliptique et affichage d’image
JP2009036860A (ja) 液晶表示装置
WO2022030308A1 (fr) Couche optiquement anisotrope
JP7434336B2 (ja) 光学異方性層の製造方法、積層体の製造方法、偏光子付き光学異方性層の製造方法、偏光子付き積層体の製造方法、組成物、光学異方性層
WO2024062850A1 (fr) Film optique ainsi que procédé de fabrication de celui-ci, plaque de polarisation, et dispositif d'affichage d'images
JP5036209B2 (ja) 液晶表示装置
WO2023171518A1 (fr) Film optique, couche optiquement anisotrope, composition de formation de film d'alignement, procédé de production de film optique, plaque de polarisation et dispositif d'affichage d'image
JP2006323348A (ja) 光学フィルムの製造方法、光学フィルム、および光学フィルムを用いた画像表示装置
JP7434573B2 (ja) 光学異方性層

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application