WO2024039059A1 - 가전기기용 텍스쳐드 우레탄 분체도장 외장재 및 이를 포함하는 세탁기 - Google Patents

가전기기용 텍스쳐드 우레탄 분체도장 외장재 및 이를 포함하는 세탁기 Download PDF

Info

Publication number
WO2024039059A1
WO2024039059A1 PCT/KR2023/009213 KR2023009213W WO2024039059A1 WO 2024039059 A1 WO2024039059 A1 WO 2024039059A1 KR 2023009213 W KR2023009213 W KR 2023009213W WO 2024039059 A1 WO2024039059 A1 WO 2024039059A1
Authority
WO
WIPO (PCT)
Prior art keywords
exterior material
home appliances
polyester resin
hardener
powder coating
Prior art date
Application number
PCT/KR2023/009213
Other languages
English (en)
French (fr)
Inventor
조철희
임명혁
Original Assignee
삼성전자주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 삼성전자주식회사 filed Critical 삼성전자주식회사
Publication of WO2024039059A1 publication Critical patent/WO2024039059A1/ko

Abstract

일 실시예에 따른 가전기기용 외장재는, 모재; 상기 모재 상부에 형성되는 전처리층; 및 상기 전처리층 상부에 마련되는 분체 도장층을 포함할 수 있다. 상기 분체 도장층은, 제1 폴리에스터 레진(Polyester Resin), 제2 폴리에스터 레진, 제1 경화제(Hardener), 제2 경화제, 안료(Pigments) 및 첨가제(Additives)를 포함할 수 있다.

Description

가전기기용 텍스쳐드 우레탄 분체도장 외장재 및 이를 포함하는 세탁기
개시된 발명은 가전기기용 텍스쳐드 우레탄 분체도장 외장재 및 이를 포함하는 세탁기에 관한 것이다.
가전기기의 표면 마무리 방법은 STS H/L, Color STS, PCM, 소부도장 및 분체도장 등 다양한 공법이 적용되고 있다. 이 중 형상이 복잡하고 전단면 내식성이 요구되는 제품 표면의 경우에는 소부도장 또는 분체도장을 적용하여 외관 보포 및 칼라를 구현하고 있다.
소부 도장은 고채도 및 고휘도 칼라 구현이 가능하지만, 텍스쳐 구현이 어렵고, 비교적 고가이므로 가격경쟁력이 떨어진다. 반면, 분체 도장은 저렴하지만, 내화학성이 열위하고 고채도 및 고휘도 컬러 구현에 제한적이라는 문제가 있다.
일반적인 분체 도료는 Epoxy-Polyester Hybrid 타입을 사용하여 다양한 칼라를 구현하지만, 내광성이 떨어져 실외 부품 사용이 제한된다. 다른 종류의 분체 도료인 Primid 타입은 내광성이 우수하지만 내화학성이 떨어져 포장 사양 및 사용 조건에 민감하다는 문제가 있다. 따라서, 포장 시 얼룩 및 눌림 등 외관 보호를 위해 Tape류, Protective Film 등이 사용된다.
상기와 같은 문제점을 해결하기 위한 개시된 발명의 목적은, 내화학성이 우수하고 심미감이 뛰어난 가전기기용 텍스쳐드 우레탄 분체도장 외장재 및 이를 포함하는 세탁기를 제공하는데 있다.
일 실시예에 따른 가전기기용 외장재는, 모재; 상기 모재 상부에 형성되는 전처리층; 및 상기 전처리층 상부에 마련되는 분체 도장층을 포함할 수 있다. 상기 분체 도장층은, 제1 폴리에스터 레진(Polyester Resin), 제2 폴리에스터 레진, 제1 경화제(Hardener), 제2 경화제, 안료(Pigments) 및 첨가제(Additives)를 포함할 수 있다.
일 실시예에 따른 세탁기는, 캐비닛; 상기 캐비닛의 내부에 회전 가능하게 마련되고, 세탁물을 수용하도록 구성되는 회전조;를 포함할 수 있다. 상기 캐비닛은, 외장재;를 포함할 수 있다. 상기 외장재는, 모재; 상기 모재 상부에 형성되는 전처리층; 및 상기 전처리층 상부에 마련되는 분체 도장층을 포함할 수 있다. 상기 분체 도장층은, 제1 폴리에스터 레진(Polyester Resin), 제2 폴리에스터 레진, 제1 경화제(Hardener), 제2 경화제, 안료(Pigments) 및 첨가제(Additives)를 포함할 수 있다.
개시된 발명의 일 예에 의하면, 미려하고 다양한 외관 및 칼라를 구현함으로써 심미감이 향상되고, 내화학성이 우수한, 가전기기용 텍스쳐드 우레탄 분체도장 외장재 및 이를 포함하는 세탁기를 제공할 수 있다.
다만, 개시된 발명의 실시예들에 따른 가전기기용 텍스쳐드 우레탄 분체도장 외장재 및 이를 포함하는 세탁기가 달성할 수 있는 효과는 이상에서 언급한 것들로 제한되지 않으며, 언급하지 않은 또 다른 효과들은 아래의 기재로부터 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자에게 명확하게 이해될 수 있을 것이다.
도 1은, 일 실시예에 따른 가전기기용 외장재에 대한 모식도이다.
도 2는, 일 실시예에 따른 세탁기에 대한 모식도이다.
도 3은, 일반 도료를 적용한 외장재에 대한 내화학성 시험 결과를 나타낸 이미지이다.
도 4는, 텍스쳐드 우레탄을 적용한 외장재에 대한 내화학성 시험 결과를 나타낸 이미지이다.
도 5는, 일반 도료를 적용한 외장재에 대한 포장 시험 결과를 나타낸 이미지이다.
도 6은, 텍스쳐드 우레탄을 적용한 외장재에 대한 포장 시험 결과를 나타낸 이미지이다.
이하에서는 개시된 발명의 실시 예를 첨부 도면을 참고하여 상세히 설명한다. 이하의 실시 예는 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자에게 본 발명의 사상을 충분히 전달하기 위해 제시하는 것이다. 개시된 발명은 여기서 제시한 실시 예만으로 한정되지 않고 다른 형태로 구체화될 수도 있다. 도면은 개시된 발명을 명확히 하기 위해 설명과 관계 없는 부분의 도시를 생략하고, 이해를 돕기 위해 구성요소의 크기를 다소 과장하여 표현할 수 있다.
명세서 전체에서, 어떤 부분이 어떤 구성요소를 "포함"한다고 할 때, 이는 특별히 반대되는 기재가 없는 한 다른 구성요소를 제외하는 것이 아니라 다른 구성요소를 더 포함할 수 있는 것을 의미한다.
단수의 표현은 문맥상 명백하게 예외가 있지 않는 한, 복수의 표현을 포함한다.
일 실시예에 따른 가전기기용 외장재는, 모재; 상기 모재 상부에 형성되는 전처리층; 및 상기 전처리층 상부에 마련되는 분체 도장층을 포함할 수 있다.
도 1은, 일 실시예에 따른 가전기기용 외장재에 대한 모식도이다.
도 1을 참고하면, 일 실시에에 따른 가전기기용 외장재는, 모재, 전처리층 및 분체 도장층을 포함할 수 있다.
상기 모재는 목적 및 기능에 따라 스테인리스 스틸, 열연 강판, 냉연 강판, 아연도금강판, 알루미늄 합금 등 다른 소재로 대체될 수 있다.
상기 전처리층은, 필요에 따라 인산 또는 지르코늄계 화성피막을 포함할 수 있다. 상기 전처리층을 인산 또는 지르코늄계 화성피막으로 형성할 경우에는, 0.1 내지 3.0 g/m2으로 스프레이 될 수 있다. 상기 전처리층은 상기 모재와 상기 분체 도장층의 부착성을 향상시킬 수 있다. 또한, 상기 전처리층을 형성시킴으로써 외장재의 내식성도 향상될 수 있다.
상기 분체 도장층은, 제1 폴리에스터 레진(Polyester Resin), 제2 폴리에스터 레진, 제1 경화제(Hardener), 제2 경화제, 안료(Pigments) 및 첨가제(Additives)를 포함할 수 있다.
폴리에스터 레진은 폴리올(Polyol)을 포함하고, 경화제는 폴리이소시아네이트(Polyisocyanate)를 포함할 수 있다.
아래 반응식 1을 참고하면, 상기 폴리올과 상기 폴리이소시아네이트가 반응하여 폴리우레탄(Polyurethane)이 형성될 수 있다.
Figure PCTKR2023009213-appb-img-000001
반응식1: The Reaction Mechanism of Polyurethane
상기 분체 도장층은, 중량%로, 제1 폴리에스터 레진: 5 내지 25%, 제2 폴리에스터 레진: 20 내지 50 중량%, 제1 경화제: 5 내지 10%, 제2 경화제: 5 내지 10%, 안료: 10 내지 25%, 나머지 첨가제를 포함할 수 있다.
상기 폴리에스터 레진과 경화제를 반응시켜 형성되는 우레탄 수지의 함량이 너무 낮은 경우에는, 외장제의 내구성이 떨어질 수 있다. 그러나 우레탄 수지의 함량이 너무 높은 경우에는, 표면 디자인감이 떨어질 수 있다. 따라서, 상기 폴리에스터 레진과 경화제의 함량을 제어하여 우레탄 수지의 함량을 최적화할 필요가 있다.
상기 안료는 펄(Pearl) 및 메탈릭(Meralic) 중 적어도 하나를 포함할 수 있다.
펄 안료는 외장재 표면을 더욱 미려하게 구현할 수 있고, 메탈릭 안료는 외장재 표면에 금속감을 부여할 수 있다.
안료의 함량이 너무 낮은 경우에는, 디자인 칼라감이 구현되기 어렵과 도장 작업성이 취약할 수 있다. 그러나, 안료의 함량이 너무 높은 경우에는, 안료가 소재 표면에 묻어 품질이 저하될 수 있다.
상기 첨가제는 텍스쳐 첨가제를 포함할 수 있다.
텍스쳐 첨가제의 함량이 너무 낮은 경우에는, 표면이 밋밋하여 디자인감이 떨어질 수 있다. 그러나, 텍스쳐 첨가제의 함량이 너무 높은 경우에는, 표면이 지나치게 거칠어져 안료가 표면에 묻어 품질이 저하될 수 있다.
상기 텍스쳐 첨가제는 평균 직경이 1 내지 30 ㎛일 수 있다.
텍스쳐 첨가제의 평균 직경은 외장재의 표면조도에 영향을 줄 수 있다. 텍스쳐 첨가제의 평균 직경이 클 경우에는, 표면조도가 높아져 심미감이 떨어지고 청소성이 열위해지는 문제가 발생할 수 있다.
한편, 개시된 발명에서 평균은 임의의 5개 지점에서 측정한 값의 평균을 의미한다.
상기 제1 폴리에스터 레진 및 상기 제2 폴리에스터 레진은, 하이드록시 그룹을 가진 두 개 이상의 비결정성 폴리에스터 레진을 포함할 수 있다. 예를 들어, 상기 제1 폴리에스터 레진 및 상기 제2 폴리에스터 레진은, HO-R`-OH와 같은 구조식을 가질 수 있다.
상기 제1 폴리에스터 레진은, Tg가 50 내지 56℃이고, OHv가 250 내지 350 mg KOH/g일 수 있다. 상기 제2 폴리에스터 레진은, Tg가 58 내지 64℃이고, OHv가 30 내지 40 mg KOH/g일 수 있다. 여기서, Tg(Glass Transition Temperature)는 유리전이온도이고, OHv는 하이드록시기 함량을 의미한다.
Tg가 너무 높으면 분체 도장층 형성 시 표면에 크랙이 발생하여 분체 도장층이 외부 충격에 매우 취약해질 수 있다. 그러나, Tg가 너무 낮은 경우에는 열에 의한 내구성이 떨어질 수 있다.
OHv가 낮을 경우에는 하이드록시(OH Group)와 이소시아네이트기(NCO Group)가 충분히 반응하지 못하여 생성되는 우레탄의 밀도가 낮을 수 있다. 그러나, OHv가 높을 경우에는, 생성되는 우레탄이 지나치게 유동적일 수 있다.
상기 제1 경화제는, Tg가 41 내지 53℃이고, 녹는점이 62 내지 82℃일 수 있다. 상기 제2 경화제는, Tg가 65 내지 82℃이고, 녹는점이 110 내지 130℃일 수 있다.
일 실시예에 따른 가전기기용 외장재는, 텍스쳐 첨가제의 평균 직경을 조절하여, 표면조도 Ra가 0.5 내지 3.5일 수 있다. 또한, 일 실시예에 따른 가전기기용 외장재는, 60도 Gloss(광택도)가 5 내지 45 GU일 수 있다. 이를 통해 뛰어난 심미감을 갖춘 외장재를 구현할 수 있다.
다음으로, 개시된 발명의 다른 일 측면에 따른 세탁기에 대해 자세히 설명한다.
일 실시예에 따른 냉장고는, 캐비닛; 상기 캐비닛의 내부에 회전 가능하게 마련되고, 세탁물을 수용하도록 구성되는 회전조;를 포함하고, 상기 캐비닛은, 외장재;를 포함하고, 상기 외장재는, 모재; 상기 모재 상부에 형성되는 전처리층; 및 상기 전처리층 상부에 마련되는 분체 도장층을 포함하고, 상기 분체 도장층은, 제1 폴리에스터 레진(Polyester Resin), 제2 폴리에스터 레진, 제1 경화제(Hardener), 제2 경화제, 안료(Pigments) 및 첨가제(Additives)를 포함할 수 있다.
상기 분체 도장층은, 중량%로, 제1 폴리에스터 레진: 5 내지 25%, 제2 폴리에스터 레진: 20 내지 50 중량%, 제1 경화제: 5 내지 10%, 제2 경화제: 5 내지 10%, 안료: 10 내지 25%, 나머지 첨가제를 포함할 수 있다.
상기 제1 폴리에스터 레진 및 상기 제2 폴리에스터 레진은, 하이드록시 그룹을 가진 두 개 이상의 비결정성 폴리에스터 레진을 포함할 수 있고, 상기 첨가제는, 텍스쳐 첨가제를 포함할 수 있다. 상기 텍스처 첨가제는, 평균 직경이 1 내지 30 ㎛일 수 있다.
상기 외장재는, 표면조도 Ra가 0.5 내지 3.5이고, 60도 Gloss(광택도)가 5 내지 45 GU일 수 있다.
상기 외장재에 대한 설명은 상술한 바와 같고, 이하 일 실시예에 따른 세탁기에 대해 자세히 설명한다.
도 2는, 일 실시예에 따른 세탁기에 대한 모식도이다.
도 2를 참고하면, 세탁기(1)는 캐비닛(20)과 상기 캐비닛의 내부에 회전 가능하게 마련되고, 세탁물을 수용하도록 구성되는 회전조(미도시)를 포함할 수 있다.
회전조의 내부에는 세탁물을 들어 올리는 리프터(미도시)가 마련되고, 회전조가 회전하면 리프터가 세탁물을 들어 올렸다가 낙하시킴으로써 세탁물을 세탁할 수 있다. 회전조의 둘레에는 터브(미도시)의 세탁수가 유출입되도록 통공(미도시)이 형성될 수 있다.
회전조의 후방에는 구동력을 발생시키는 모터(미도시)가 마련될 수 있다. 회전조와 모터의 사이에는 구동력을 전달하는 구동축(미도시)이 마련될 수 있다. 구동축의 일 단은 회전조의 후면판에 연결되고, 구동축의 타단은 터브를 관통하여 모터에 연결될 수 있다.
터브의 상부에는 터브로 세탁수를 공급하는 급수관이 마련될 수 있다. 급수관의 일 측은 외부 급수원에 연결되고, 급수관의 타측은 세탁수 공급 장치에 연결될 수 있다. 세탁수 공급 장치는 연결관을 통해 터브에 연결될 수 있다.
터브의 하부에는 터브의 세탁수를 배수하거나 순환시키는 펌프가 마련될 수 있다.
캐비닛은 양 측에 마련되는 사이드 프레임(21), 백 프레임(미도시), 탑 프레임(22), 바텀 프레임(미도시), 전방에 마련되는 프런트 프레임(미도시) 및 프런트 프레임의 전방에 마련되는 프런트 커버(23)를 포함할 수 있다.
상기 캐비닛은, 가전기기용 텍스쳐드 우레탄 분체도장 외장재를 포함할 수 있다.
프런트 프레임은 사이드 프레임(21)과 백 프레임의 형태를 고정시키고 강성을 보강하기 위해 형성될 수 있다.
프런트 프레임에는 터브와 회전조의 개구에 연결되어 회전조의 내부로 세탁물을 투입하거나 꺼낼 수 있는 내부 투입구가 형성될 수 있다. 프런트 프레임의 내부 투입구와 터브의 개구는 연결부재에 의해 연결될 수 있다.
프런트 프레임은 사이드 프레임(21)에 나사, 볼트, 핀, 리벳 등의 나사부재에 의해 결합될 수 있다.
프런트 커버(23)는 세탁기(1)의 전방 외관을 형성할 수 있다. 상기 프런트 커버(23)는 상측의 탑 프레임(22)으로부터 하측의 바텀 프레임에 까지 연장되도록 형성되어 프런트 프레임의 전체 영역을 커버할 수 있다. 따라서, 세탁기(1)의 전면에는 상부와 하부를 구획하는 라인이 형성되지 않고 따라서 외관이 단순해지고 미감이 향상될 수 있다.
프런트 커버(23)에는 프런트 프레임의 내부 투입구에 대응되는 외부 투입구가 형성될 수 있다.
프런트 커버(23)와 프런트 프레임의 사이에는 외부 투입구와 내부 투입구를 연결하는 가이드 도어(미도시)가 마련될 수 있다. 가이드 도어는 대략 링 형상을 가질 수 있다. 가이드 도어에는 외부 투입구와 내부 투입구를 개폐하는 도어(10)가 장착될 수 있다. 도어(10)는 가이드 도어에 회전 가능하게 장착될 수 있다.
외부 투입구의 직경은 내부 투입구의 직경 보다 크게 마련될 수 있다. 따라서, 외부에서 볼 때 개방감이 커 보일 수 있으며, 세탁물의 입출이 용이한 효과를 가질 수 있다.
프런트 커버(23)와 프런트 프레임의 사이에는 세제함 등이 배치될 수 있다.
프런트 커버(23)에는 디스플레이 패널(미도시)과, 조작 패널(미도시)과, 펌프 필터 커버(미도시)가 설치될 수 있다. 이를 위해 프런트 커버(23)에는 디스플레이 패널 설치구(미도시)와, 조작 패널 설치구(미도시)와, 펌프 필터 커버 설치구(미도시)가 형성될 수 있다.
프런트 커버(23)는 프런트 프레임, 사이드 프레임(21), 탑 프레임(22) 및 바텀 프레임에 착탈 가능하게 결합될 수 있다.
상기 가전기기용 텍스쳐드 우레탄 분체도장 외장재는, 에어컨, 냉장고 등 충분한 강도 및 내화학성이 필요한 모든 가전기기에 적용할 수 있다.
이하에서, 본 발명에 대한 이해를 돕기 위하여 실시예 및 비교예를 기재한다. 다만, 하기 기재는 본 발명의 내용 및 효과에 관한 일 예에 해당할 뿐, 본 발명의 권리범위 및 효과가 반드시 이에 한정되는 것은 아니다.
{실시예}
아래 표 1에는 가전기기용 텍스쳐드 우레탄 분체도장 외장재 분체 도장층의 기초 성분 물성에 대해 나타냈다.
Tg 는, ASTM E1356에 의거하여, DSC(Differential Scanning Calorimetry) 분석을 통해 측정했다.
OHv는, ASTM D6342에 의거하여, NIR(Near InfraRed　Analysis) 장비를 통해 측정했다.
구분 분체 도장층의 기초 성분 물성
(중량%)
Tg
(℃)		 OHv
(mg KOH/g)		 녹는점
(℃)
제1 폴리에스터 레진 53 300 -
제2 폴리에스터 레진 61 30 -
제3 폴리에스터 레진 63 35 -
제4 폴리에스터 레진 63 50 -
제1 경화제 47 - 72
제2 경화제 74 - 120
아래 표 2에 나타낸 가전기기용 텍스쳐드 우레탄 분체도장 외장재 분체 도장층의 성분으로 외장재 시편을 제조했다.
구분 분체 도장층의 성분
(중량%)
폴리에스터 레진 경화제 안료 첨가제
제1폴리에스터 레진 제2폴리에스터 레진 제3폴리에스터 레진 제4폴리에스터 레진 제5폴리에스터 레진 제1경화제 제2경화제
실시예 15 45 - - 7 8 23 2
비교예1 60 - - 7 8 23 2
비교예2 - 60 - - 15 - 23 2
비교예3 - - 60 - 15 23 2
비교예4 - - - 60 - 15 23 2
비교예5 15 - 45 - 15 - 23 2
비교예6 15 - - 45 15 - 23 2
아래 표 3에는 상기 비교예 및 실시예에 대한 광택도, 연필경도, 내화학성 및 포장 시험을 실시한 결과를 나타냈다.광택도는, ASTM D523. D2457에 의거하여, 상온에서, 60°의 측정 각도로, 모델명이 BYK #4563인 광택계를 이용하여 측정했다.
연필경도는, ISO 15184에 의거하여, Motorized Pencil Hardness Tester및 미쓰비시 Pencil이용하여 측정했다. 이때, 경도가 다른 연필을 500g의 하중을 가해 5개의 선을 그었을 때, 3개 이상의 선에서 결점이 발생하는 경우 불합격으로 판단하고, 최대로 견디는 연필강도를 나타냈다.
내화학성은, 내알칼리성 시험, 내락스성 시험 및 내세제성 시험을 실시했다.
내알칼리성 시험은, KS M ISO 2812-1에 의거하여, NaOH 용액에 시편을 침적하고, 24시간 경과 후 외관 변이를 관찰했다.
내락스성 시험은, 락스에 시편을 침적하고, 24시간 경과 후 외관 변이를 관찰했다.
내세제성 시험은, ASTM D2248-01에 의거하여, 시편에 세제 용액에 시편을 침적하고, 96시간 경과 후 외관 변이를 관찰했다.
상기 3개의 시험을 모두 합격한 경우 ○로 나타냈고, 상기 3개의 시험 중 2개의 시험을 합격한 경우 △로 나타냈고, 상기 3개의 시험 중 1개 이하의 시험을 합격한 경우 X로 나타냈다.
한편, 침적 전 후 시편의 색차계(△E) 값이 0.5 이하이면, 합격한 것으로 판단했다.
포장 시험은, 65℃ 습도 90% 조건에서, 시편 위에 EPS(가로 2cmm X 세로 3cm)를 놓고 6kg의 하중을 24시간 가하였을 때, 얼룩이 나타나는지 여부로 판단했다.
포장 시험을 합격한 경우 ○로 나타냈고, 불합격한 경우X로 나타냈다.
한편, EPS가 놓여진 곳과 놓여지지 않은 곳의 색차계(△E) 값이 1 이하이면, 합격한 것으로 판단했다.
광택도
(GU)		 연필경도 내화학성 포장 시험
실시예 30 4H ○ ○
비교예1 30 2H △ ○
비교예2 30 2H △ ○
비교예3 30 H X X
비교예4 30 H X ○
비교예5 25 H X X
비교예6 30 H X ○
표 3을 참고하면, 실시예에 따른 가전기기용 외장재는, 광택도 5 내지 45 GU, 연필경도 4H이상, 내화학성 합격 및 포장 시험 합격을 모두 만족했다. 즉, 개시된 발명의 일 예에 따른 가전기기용 외장재는, 내화학성이 우수하고 외관이 미려하다고 판단할 수 있었다.그러나, 비교예 1 및 2는, 연필경도 4H 이상을 만족하지 못했고, 내화학성 시험 중 일부를 합격하지 못했다. 따라서, 비교예 1 및 2는 내화학성이 비교적 열위하고 내구성도 떨어진다고 판단할 수 있었다.
비교예 3 내지 6은 연필경도 4H 이상을 만족하지 못했고, 내화학성 시험 중 일부를 합격하지 못했다. 따라서, 비교예 3 내지 6은 내화학성이 매우 열위하고 내구성도 떨어진다고 판단할 수 있었다.
비교예 3 및 5는, 포장 시험을 합격하지 못했다. 따라서, 비교예 3 및 5는 별도의 보호 필름이 사용되어야 하는 문제가 있었다.
도 3은, 일반 도료를 적용한 외장재에 대한 내화학성 시험 결과를 나타낸 이미지이고, 도 4는, 텍스쳐드 우레탄을 적용한 외장재에 대한 내화학성 시험 결과를 나타낸 이미지이다. 도 3 및 도 4를 참고하면, 개시된 발명에 따른 가전기기용 외장재는 내화학성이 우수하다는 것을 알 수 있다.
도 5는, 일반 도료를 적용한 외장재에 대한 포장 시험 결과를 나타낸 이미지이고, 도 6은, 텍스쳐드 우레탄을 적용한 외장재에 대한 포장 시험 결과를 나타낸 이미지이다.
도 5 및 도 6을 참고하면, 개시된 발명에 따른 가전기기용 외장재는 별도의 보호 필름이 필요 없다는 것을 알 수 있다.
<표면조도 측정>
텍스쳐 첨가제 평균 직경에 따른 가전기기용 외장재의 표면조도 변화를 확인하기 위해 표면조도 측정 시험을 수행했다.
텍스쳐 첨가제 평균 직경은, TEM(transmission electron microscopy, 투과전자현미경)으로 임의의 5개소의 직경을 측정하여 평균값으로 나타냈다.
표면조도는, ISO 1302 기준으로, 상온에서, 모델명이 SJ-320인 MITUTOYO 표면조도 측정기를 이용하여 측정했다.
텍스쳐 첨가제 평균 직경이 6㎛인 경우, 가전기기용 외장재의 표면조도 Ra는 2.2로 측정되었다. 텍스쳐 첨가제 평균 직경이 31㎛인 경우, 가전기기용 외장재의 표면조도 Ra는 5로 측정되었다. 즉, 텍스쳐 첨가제 평균 직경이 30㎛를 초과하는 경우에는, 표면조도가 커지므로 외장재 표면이 거칠어지는 것을 확인할 수 있었다.
상기 비교예 및 실시예에 의해 개시된 발명의 일 실시예에 따른 가전기기용 텍스쳐드 우레탄 분체도장 외장재는 내화학성이 우수하고 외관이 미려하다는 것을 확인할 수 있었다.

Claims (15)

  1. 모재;
    상기 모재 상부에 형성되는 전처리층; 및
    상기 전처리층 상부에 마련되는 분체 도장층을 포함하고,
    상기 분체 도장층은,
    제1 폴리에스터 레진(Polyester Resin), 제2 폴리에스터 레진, 제1 경화제(Hardener), 제2 경화제, 안료(Pigments) 및 첨가제(Additives)를 포함하는, 가전기기용 외장재.
  2. 제1항에 있어서,
    상기 분체 도장층은,
    중량%로, 제1 폴리에스터 레진: 5 내지 25%, 제2 폴리에스터 레진: 20 내지 50 중량%, 제1 경화제: 5 내지 10%, 제2 경화제: 5 내지 10%, 안료: 10 내지 25%, 나머지 첨가제를 포함하는, 가전기기용 외장재.
  3. 제1항에 있어서,
    상기 제1 폴리에스터 레진 및 상기 제2 폴리에스터 레진은,
    하이드록시 그룹을 가진 두 개 이상의 비결정성 폴리에스터 레진을 포함하는, 가전기기용 외장재.
  4. 상기 제1 폴리에스터 레진은,
    Tg가 50 내지 56℃이고, OHv가 250 내지 350 mg KOH/g인, 가전기기용 외장재.
    (여기서, Tg는 유리전이온도이고, OHv는 하이드록시기 함량을 의미한다)
  5. 제1항에 있어서,
    상기 제2 폴리에스터 레진은,
    Tg가 58 내지 64℃이고, OHv가 30 내지 40 mg KOH/g인, 가전기기용 외장재.
  6. 제1항에 있어서,
    상기 경화제는,
    이소시아네이트(Isocyanate)계 경화제를 포함하는, 가전기기용 외장재.
  7. 제1항에 있어서,
    상기 제1 경화제는,
    Tg가 41 내지 53℃이고, 녹는점이 62 내지 82℃인, 가전기기용 외장재.
  8. 제1항에 있어서,
    상기 제2 경화제는,
    Tg가 65 내지 82℃이고, 녹는점이 110 내지 130℃인, 가전기기용 외장재.
  9. 제1항에 있어서,
    상기 안료는,
    펄(Pearl) 및 메탈릭(Meralic) 중 적어도 하나를 포함하는, 가전기기용 외장재.
  10. 제1항에 있어서,
    상기 첨가제는,
    텍스쳐 첨가제를 포함하는, 가전기기용 외장재.
  11. 제10항에 있어서,
    상기 텍스처 첨가제는,
    평균 직경이 1 내지 30 ㎛인, 가전기기용 외장재.
  12. 제1항에 있어서,
    표면조도(Ra)가 0.5 내지 3.5인, 가전기기용 외장재.
  13. 제1항에 있어서,
    60도 Gloss(광택도)가 5 내지 45 GU인, 가전기기용 외장재.
  14. 캐비닛;
    상기 캐비닛의 내부에 회전 가능하게 마련되고, 세탁물을 수용하도록 구성되는 회전조;를 포함하고,
    상기 캐비닛은,
    외장재;를 포함하고,
    상기 외장재는,
    모재;
    상기 모재 상부에 형성되는 전처리층; 및
    상기 전처리층 상부에 마련되는 분체 도장층을 포함하고,
    상기 분체 도장층은,
    제1 폴리에스터 레진(Polyester Resin), 제2 폴리에스터 레진, 제1 경화제(Hardener), 제2 경화제, 안료(Pigments) 및 첨가제(Additives)를 포함하는, 세탁기.
  15. 제14항에 있어서,
    상기 분체 도장층은,
    중량%로, 제1 폴리에스터 레진: 5 내지 25%, 제2 폴리에스터 레진: 20 내지 50 중량%, 제1 경화제: 5 내지 10%, 제2 경화제: 5 내지 10%, 안료: 10 내지 25%, 나머지 첨가제를 포함하는, 세탁기.
PCT/KR2023/009213 2022-08-18 2023-06-30 가전기기용 텍스쳐드 우레탄 분체도장 외장재 및 이를 포함하는 세탁기 WO2024039059A1 (ko)