WO2024024534A1 - Dispersant polymère contenant un groupe carboxy, pâte électroconductrice, composant électronique et condensateur en céramique stratifiée - Google Patents

Dispersant polymère contenant un groupe carboxy, pâte électroconductrice, composant électronique et condensateur en céramique stratifiée Download PDF

Info

Publication number
WO2024024534A1
WO2024024534A1 PCT/JP2023/025984 JP2023025984W WO2024024534A1 WO 2024024534 A1 WO2024024534 A1 WO 2024024534A1 JP 2023025984 W JP2023025984 W JP 2023025984W WO 2024024534 A1 WO2024024534 A1 WO 2024024534A1
Authority
WO
WIPO (PCT)
Prior art keywords
conductive paste
mass
dispersant
less
containing polymer
Prior art date
Application number
PCT/JP2023/025984
Other languages
English (en)
Japanese (ja)
Inventor
健二 福田
正剛 川口
聖也 山本
Original Assignee
住友金属鉱山株式会社
国立大学法人山形大学
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 住友金属鉱山株式会社, 国立大学法人山形大学 filed Critical 住友金属鉱山株式会社
Publication of WO2024024534A1 publication Critical patent/WO2024024534A1/fr

Abstract

La présente invention concerne : une pâte électroconductrice à faible viscosité qui peut empêcher la séparation entre une poudre électroconductrice et une poudre céramique, présente une bonne stabilité de viscosité dans le temps et un bonne régularité d'une surface de membrane sèche après application ; un dispersant polymère contenant un groupe carboxy ; un composant électronique ; et un condensateur en céramique stratifiée.　Ce dispersant polymère contenant un groupe carboxy comprend un copolymère d'un acide acrylique et/ou d'un acide méthacrylique, et d'un ester d'acide acrylique représenté par la formule générale (1) et/ou d'un ester d'acide méthacrylique représenté par la formule générale (2). Dans le dispersant, le poids moléculaire moyen en masse est supérieur ou égal à 2 000 et inférieur à 30 000, pour le rapport molaire, le rapport du total de l'acide acrylique et de l'acide méthacrylique sur le total de l'ester d'acide acrylique et de l'ester d'acide méthacrylique est X:1–X, X est supérieur ou égal à 0,1 et inférieur à 0,4, et dans la formule générale (1) et la formule générale (2), R1 est une chaîne droite ou un groupe alkyle ramifié.
PCT/JP2023/025984 2022-07-29 2023-07-14 Dispersant polymère contenant un groupe carboxy, pâte électroconductrice, composant électronique et condensateur en céramique stratifiée WO2024024534A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2022-121641 2022-07-29
JP2022121641 2022-07-29

Publications (1)

Publication Number Publication Date
WO2024024534A1 true WO2024024534A1 (fr) 2024-02-01

Family

ID=89706307

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2023/025984 WO2024024534A1 (fr) 2022-07-29 2023-07-14 Dispersant polymère contenant un groupe carboxy, pâte électroconductrice, composant électronique et condensateur en céramique stratifiée

Country Status (1)

Country Link
WO (1) WO2024024534A1 (fr)

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS6477110A (en) * 1987-09-18 1989-03-23 Toa Gosei Chem Ind Aluminum electrolytic capacitor
JP2003055571A (ja) * 2001-08-13 2003-02-26 Mikuni Color Ltd 水性顔料分散液及び水性インク組成物
JP2007238859A (ja) * 2006-03-10 2007-09-20 Daido Toryo Kk 導電性クリヤー用水性組成物

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS6477110A (en) * 1987-09-18 1989-03-23 Toa Gosei Chem Ind Aluminum electrolytic capacitor
JP2003055571A (ja) * 2001-08-13 2003-02-26 Mikuni Color Ltd 水性顔料分散液及び水性インク組成物
JP2007238859A (ja) * 2006-03-10 2007-09-20 Daido Toryo Kk 導電性クリヤー用水性組成物

Similar Documents

Publication Publication Date Title
WO2021106470A1 (fr) Pâte électroconductrice pour héliogravure, composant électronique et condensateur céramique stratifié
CN112334995B (zh) 导电性浆料、电子部件以及叠层陶瓷电容器
CN113227246B (zh) 导电性浆料、电子部件以及叠层陶瓷电容器
JP7279643B2 (ja) 導電性ペースト、電子部品、及び積層セラミックコンデンサ
TWI801445B (zh) 導電性漿料、電子零件以及層積陶瓷電容器
JP7405098B2 (ja) 導電性ペースト、電子部品、及び積層セラミックコンデンサ
JP2024032861A (ja) 導電性ペースト、電子部品、及び積層セラミックコンデンサ
CN111066098B (zh) 导电性浆料、电子部件以及叠层陶瓷电容器
WO2024024534A1 (fr) Dispersant polymère contenant un groupe carboxy, pâte électroconductrice, composant électronique et condensateur en céramique stratifiée
WO2021020557A1 (fr) Pâte conductrice pour héliogravure, composant électronique et condensateur céramique stratifié
CN111095439A (zh) 导电性浆料、电子部件以及叠层陶瓷电容器
CN111373490A (zh) 导电性浆料、电子部件以及叠层陶瓷电容器
JP2022070803A (ja) グラビア印刷用導電性ペースト、電子部品、及び積層セラミックコンデンサ
WO2023033163A1 (fr) Pâte conductrice pour héliogravure, composant électronique et condensateur céramique multicouche
WO2022255467A1 (fr) Pâte conductrice pour héliogravure, composant électronique et condensateur céramique stratifié
WO2023190613A1 (fr) Pâte conductrice, composant électronique et condensateur céramique multicouche
TW202411411A (zh) 含有羧基之高分子分散劑，導電性糊，電子零件及積層陶瓷電容器
WO2019043674A2 (fr) Pâte conductrice, composant électronique et condensateur céramique multicouche
WO2023190614A1 (fr) Pâte électriquement conductrice, composant électronique et condensateur céramique stratifié
TW202229471A (zh) 凹版印刷用導電性漿料、電子零件及積層陶瓷電容器
WO2019043673A2 (fr) Pâte conductrice, composant électronique et condensateur à base de céramique multicouche

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application