Classifications

• • C—CHEMISTRY; METALLURGY
  • C01—INORGANIC CHEMISTRY
  • C01B—NON-METALLIC ELEMENTS; COMPOUNDS THEREOF; METALLOIDS OR COMPOUNDS THEREOF NOT COVERED BY SUBCLASS C01C
  • C01B21/00—Nitrogen; Compounds thereof
  • C01B21/06—Binary compounds of nitrogen with metals, with silicon, or with boron, or with carbon, i.e. nitrides; Compounds of nitrogen with more than one metal, silicon or boron
  • C01B21/064—Binary compounds of nitrogen with metals, with silicon, or with boron, or with carbon, i.e. nitrides; Compounds of nitrogen with more than one metal, silicon or boron with boron
• • C—CHEMISTRY; METALLURGY
  • C01—INORGANIC CHEMISTRY
  • C01B—NON-METALLIC ELEMENTS; COMPOUNDS THEREOF; METALLOIDS OR COMPOUNDS THEREOF NOT COVERED BY SUBCLASS C01C
  • C01B21/00—Nitrogen; Compounds thereof
  • C01B21/06—Binary compounds of nitrogen with metals, with silicon, or with boron, or with carbon, i.e. nitrides; Compounds of nitrogen with more than one metal, silicon or boron
  • C01B21/064—Binary compounds of nitrogen with metals, with silicon, or with boron, or with carbon, i.e. nitrides; Compounds of nitrogen with more than one metal, silicon or boron with boron
  • C01B21/0648—After-treatment, e.g. grinding, purification
• • C—CHEMISTRY; METALLURGY
  • C01—INORGANIC CHEMISTRY
  • C01B—NON-METALLIC ELEMENTS; COMPOUNDS THEREOF; METALLOIDS OR COMPOUNDS THEREOF NOT COVERED BY SUBCLASS C01C
  • C01B21/00—Nitrogen; Compounds thereof
  • C01B21/06—Binary compounds of nitrogen with metals, with silicon, or with boron, or with carbon, i.e. nitrides; Compounds of nitrogen with more than one metal, silicon or boron
  • C01B21/064—Binary compounds of nitrogen with metals, with silicon, or with boron, or with carbon, i.e. nitrides; Compounds of nitrogen with more than one metal, silicon or boron with boron
  • C01B21/0645—Preparation by carboreductive nitridation
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
  • C08K3/00—Use of inorganic substances as compounding ingredients
  • C08K3/38—Boron-containing compounds
• • C—CHEMISTRY; METALLURGY
  • C01—INORGANIC CHEMISTRY
  • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
  • C01P2004/00—Particle morphology
  • C01P2004/50—Agglomerated particles
• • C—CHEMISTRY; METALLURGY
  • C01—INORGANIC CHEMISTRY
  • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
  • C01P2004/00—Particle morphology
  • C01P2004/60—Particles characterised by their size
  • C01P2004/61—Micrometer sized, i.e. from 1-100 micrometer
• • C—CHEMISTRY; METALLURGY
  • C01—INORGANIC CHEMISTRY
  • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
  • C01P2006/00—Physical properties of inorganic compounds
  • C01P2006/12—Surface area
• • C—CHEMISTRY; METALLURGY
  • C01—INORGANIC CHEMISTRY
  • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
  • C01P2006/00—Physical properties of inorganic compounds
  • C01P2006/80—Compositional purity
  • C01P2006/82—Compositional purity water content
• • C—CHEMISTRY; METALLURGY
  • C01—INORGANIC CHEMISTRY
  • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
  • C01P2006/00—Physical properties of inorganic compounds
  • C01P2006/90—Other properties not specified above
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
  • C08K3/00—Use of inorganic substances as compounding ingredients
  • C08K3/38—Boron-containing compounds
  • C08K2003/382—Boron-containing compounds and nitrogen
  • C08K2003/385—Binary compounds of nitrogen with boron
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
  • C08K2201/00—Specific properties of additives
  • C08K2201/002—Physical properties
  • C08K2201/005—Additives being defined by their particle size in general
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
  • C08K2201/00—Specific properties of additives
  • C08K2201/002—Physical properties
  • C08K2201/006—Additives being defined by their surface area

Definitions

• the present disclosure relates to boron nitride powder, a resin composition, and a method for producing boron nitride powder.
• boron nitride powder which has characteristics such as high thermal conductivity, high insulation, and low dielectric constant, is attracting attention.
• boron nitride particles (particularly hexagonal boron nitride particles) have a large anisotropy in thermal conductivity, so by agglomerating the primary particles of boron nitride to form boron nitride agglomerated particles, thermal conductivity is achieved through the orientation of the primary particles. Suppressing the anisotropy of the ratio has been studied (for example, Patent Document 1).
• thermally conductive insulating materials incorporated into electronic components for example, thermally conductive insulating materials containing boron nitride powder as a filler
• the insulation properties of the material gradually decrease, and dielectric breakdown may occur. Therefore, there is a need for a heat conductive insulating material that can maintain excellent insulation properties over a long period of time, that is, a heat conductive insulating material that has excellent long-term insulation properties.
• One aspect of the present disclosure is to provide boron nitride powder that improves the long-term insulation properties of thermally conductive insulating materials. Another aspect of the present disclosure is to provide a method for producing the boron nitride powder. Another aspect of the present disclosure is to provide a resin composition using the boron nitride powder described above.
• the inventors have found that the content of boron oxide (B 2 O 3 ) in boron nitride powder affects the insulation properties of heat-conductive insulating materials, and that the content of boron oxide (B 2 O 3 ) in boron nitride powder affects the insulation properties of heat-conductive insulating materials, and that the content of boron oxide (B 2 O 3 ) in boron nitride powder It was revealed that the boron oxide content of The present inventors completed the present invention based on these findings.
• the present disclosure provides at least the following [1] to [11].
• [1] Contains agglomerated particles composed of agglomerated primary particles of boron nitride, has a graphitization index of 2.0 or less, has a boron oxide content of 0.1% by mass or less, and meets the following (i).
• 10 g of the boron nitride powder was heated from 0°C to 50°C at a temperature increase rate of 3.0°C/min under a humidity of 80% RH, held for 30 minutes, and cooled at a cooling rate of 1.5°C/min. After cooling from 50°C to 0°C, hold for 30 minutes.
• heating is performed from a temperature of 1000°C or lower to a holding temperature of 1900°C or higher at a heating rate of 0.5 to 5.0°C/min, and at the holding temperature for 2 hours or more.
• a boron nitride powder that improves the long-term insulation properties of a heat-conductive insulating material, a method for producing the same, and a resin composition using the boron nitride powder.
• the materials exemplified in this specification can be used alone or in combination of two or more, unless otherwise specified. If there are multiple substances corresponding to each component in the composition, the content of each component in the composition means the total amount of the multiple substances present in the composition, unless otherwise specified. .
• a numerical range indicated using " ⁇ " indicates a range that includes the numerical values written before and after " ⁇ " as the minimum and maximum values, respectively.
• the upper limit or lower limit of the numerical range may be replaced with the value shown in the Examples.
• the upper limit values and lower limit values described individually can be combined arbitrarily.
• the boron nitride powder includes agglomerated particles composed of agglomerated primary particles of boron nitride.
• the boron nitride powder may contain primary particles (non-agglomerated particles) in addition to agglomerated particles.
• the primary particles of boron nitride may be, for example, scaly hexagonal boron nitride particles.
• the graphitization index of the boron nitride powder is 2.0 or less.
• the graphitization index (G.I.) is an index indicating the degree of crystallinity of graphite (for example, J. Thomas, et. al, J. Am. Chem. Soc. 84 , 4619 (1962), etc.).
• the graphitization index can also be used as an index of the crystallinity of boron nitride. The smaller the graphitization index, the higher the crystallinity of boron nitride.
• boron nitride powder containing boron nitride with a small graphitization index has less impurities and has excellent insulation properties, and has high crystallinity, so it tends to have excellent thermal conductivity. be.
• the graphitization index may be 1.9 or less, 1.8 or less, or 1.7 or less. Boron nitride powder having such a graphitization index tends to have better insulation properties.
• the graphitization index may be 1.2 or more, 1.3 or more, 1.4 or more, or 1.5 or more, 1.2 to 2.0, 1.3 to 1.9, 1.4 to It may be 1.8 or 1.5 to 1.7.
• the graphitization index in this specification is calculated based on the spectrum measured by powder X-ray diffraction of primary particles of boron nitride (for example, primary particles constituting the aggregated particles) contained in the boron nitride powder.
• the integrated intensity of each diffraction peak that is, each diffraction peak
• the enclosed area values are calculated and set as S100, S101, and S102, respectively.
• the value of [(S100+S101)/S102] is calculated to determine the graphitization index. More specifically, it is determined by the method described in the Examples of this specification.
• the boron oxide (B 2 O 3 ) content in the boron nitride powder is 0.1% by mass or less, 0.08% by mass or less, 0.06% by mass or less, 0.04% by mass or less, 0. It may be 0.02% by mass or less or 0.01% by mass or less.
• the lower the boron oxide content the higher the insulation properties.
• the lower limit of the boron oxide content may be 0% by mass, 0.001% by mass, 0.002% by mass, 0.005% by mass, or 0.01% by mass.
• the boron oxide (B 2 O 3 ) content in the boron nitride powder after a heat cycle test of a total of 1000 cycles in which the operation (i) below is one cycle is 0.2% by mass or less, and 0.1 It may be less than or equal to 0.05 mass%, 0.015 mass% or less, or 0.013 mass% or less.
• 10 g of the boron nitride powder was heated from 0°C to 50°C at a temperature increase rate of 3.0°C/min under a humidity of 80% RH, held for 30 minutes, and cooled at a cooling rate of 1.5°C/min. After cooling from 50°C to 0°C, hold for 30 minutes.
• the above heat cycle test is a test assuming that boron nitride powder is used as a filler in a heat conductive insulating material for a long period of time in an environment in which electronic components are used.
• the boron oxide content increased after the above heat cycle test, resulting in a decrease in insulation properties
• the boron oxide content increased even after the above heat cycle test.
• the content is suppressed to 0.2% by mass or less. Therefore, the boron nitride powder can improve the long-term insulation properties of the heat-conductive insulating material.
• boron nitride powder having such properties (properties in which the boron oxide content is unlikely to increase in the heat cycle test) will be referred to as boron nitride powder having excellent weather resistance.
• the lower limit of the boron oxide content after the heat cycle test may be 0% by mass, 0.001% by mass, 0.002% by mass, 0.005% by mass, 0.01% by mass, 0.02% by mass. It may be 0.03% by mass or 0.03% by mass.
• the boron oxide content is the content based on the total mass of the boron nitride powder, and can be measured by the following procedure.
• (1) After drying the boron nitride powder at 120° C. for 2 hours, 5 g of the dried boron nitride powder is accurately weighed into a flat weighing tube and mixed with 15 ml of methanol (special grade reagent) to obtain a mixed solution.
• methanol special grade reagent
• the rate of increase in boron oxide content due to the heat cycle test ((increase in boron oxide content before and after the heat cycle test)/(boron oxide content before the heat cycle test) x 100) is small.
• the rate of increase in boron oxide content may be 1000% or less, 900% or less, 800% or less, 500% or less, 300% or less, or 200% or less.
• the lower limit of the rate of increase in boron oxide content is not particularly limited, but may be 0%, 20% or 50%.
• the purity of the boron nitride powder may be 98.5% by mass or more, 99% by mass or more, 99.5% by mass or more, or 99.9% by mass or more.
• the upper limit of the purity of the boron nitride powder may be 100% by mass, 99.9% by mass, or 99.5% by mass.
• the purity of boron nitride powder in this specification means a value determined by titration described below.
• a sample of boron nitride powder is subjected to alkaline decomposition using sodium hydroxide, and ammonia is distilled from the decomposed liquid using a steam distillation method, and collected in a boric acid aqueous solution. This collected liquid is titrated with a normal sulfuric acid solution.
• the content of nitrogen atoms (N) in the sample is calculated from the titration results. From the obtained content of nitrogen atoms, the content of boron nitride in the sample can be determined based on the following formula, and the purity of the boron nitride powder can be calculated.
• the moisture content of the boron nitride powder may be 300 mass ppm or less, 250 mass ppm or less, 200 mass ppm or less, or 100 mass ppm or less. Boron nitride powders with lower moisture content tend to exhibit better weather resistance. Therefore, boron nitride powder having the above water content tends to be able to further improve the long-term insulation properties of the heat conductive insulating material.
• the lower limit of the water content may be 0 mass ppm, 10 mass ppm, or 20 mass ppm.
• the above moisture content is the moisture content based on the total mass of boron nitride powder, and is measured based on the Karl Fischer method in accordance with JIS K 0068: 2001 "Method for measuring moisture in chemical products”. means value. Specifically, first, a predetermined amount of a measurement sample (boron nitride powder) is taken on an air-fired alumina board. This is placed in a furnace whose temperature is constant at 25° C., and the moisture generated when heated to the measurement temperature (300° C.) using nitrogen gas as a carrier gas is measured by coulometric titration. The moisture content can be determined by converting the obtained measurement value per unit mass (1 g).
• the measuring device for example, "Trace moisture measuring device CA-06" (product name) manufactured by Mitsubishi Chemical Corporation can be used.
• the titration solution for example, "Aquamicron AX” (trade name) manufactured by Mitsubishi Chemical Corporation can be used as the catholyte, and "Aquamicron CXU” (trade name) manufactured by Mitsubishi Chemical Corporation can be used as the anolyte.
• the average particle size of the boron nitride powder may be 10 to 90 ⁇ m. Boron nitride powder having such an average particle size tends to have better weather resistance. Moreover, since the average particle diameter of the boron nitride powder is 90 ⁇ m or less, it becomes possible to make the layer formed by the resin composition (for example, a heat conductive insulating material) thinner. Moreover, the thermal conductivity of the resin composition can be further improved because the average particle diameter of the boron nitride powder is 10 ⁇ m or more.
• the average particle diameter of the boron nitride powder may be 80 ⁇ m or less or 70 ⁇ m or less, 20 ⁇ m or more or 30 ⁇ m or more, or 20 to 80 ⁇ m or 30 to 70 ⁇ m.
• the average particle diameter in this specification means the 50% cumulative diameter (median diameter) in the volume-based cumulative particle size distribution. More specifically, it means the particle diameter (D50) when the cumulative value in the volume-based cumulative particle size distribution obtained by the laser diffraction scattering method for powder becomes 50%.
• the laser analysis scattering method is measured in accordance with the method described in ISO 13320:2009.
• a laser diffraction scattering particle size distribution measuring device or the like can be used.
• the laser diffraction scattering particle size distribution measuring device for example, "LS-13 320" (product name) manufactured by Beckman Coulter, Inc. can be used. The measurement is performed in the presence of aggregated particles without any treatment using a homogenizer.
• the specific surface area of the boron nitride powder may be 5.0 m 2 /g or less, 4.5 m 2 /g or less, 4.0 m 2 /g or less, 3.5 m 2 /g or less, or 3.0 m 2 /g It may be the following.
• the specific surface area of the boron nitride powder is 5.0 m 2 /g or less, the primary particles of boron nitride are appropriately large and the porosity in the aggregated particles can be increased, so that when kneading with the resin, The resin can easily penetrate into the aggregated particles, and the insulation properties of the resin composition (for example, heat-conductive insulating material) can be further improved.
• the specific surface area of the boron nitride powder may be 1.6 m 2 /g or more, 1.8 m 2 /g or more, or 2.0 m 2 /g or more.
• the specific surface area of the boron nitride powder may be 1.6 to 5.0 m 2 /g, 1.8 to 4.5 m 2 /g, or 2.0 to 4.0 m 2 /g. Note that the specific surface area of the boron nitride powder can be adjusted, for example, by controlling the grain growth of primary particles when producing the boron nitride powder.
• the specific surface area in this specification refers to a value measured using a specific surface area measuring device in accordance with the description of JIS Z 8830:2013 "Method for measuring the specific surface area of powder (solid) by gas adsorption". This is a value calculated by applying the BET one point method using
• the orientation index of the boron nitride powder may be 15 or less, 12 or less, or 10 or less. If the orientation index of the boron nitride powder is within the above range, at least a portion of the aggregated particles will collapse during kneading with the resin, and even if the orientation increases, the heat dissipation properties of the resin composition will be affected. It is possible to suppress the occurrence of large anisotropy.
• the orientation index may be 3 or more, 4 or more, or 6 or more, and may be 3 to 15, 4 to 12, or 6 to 10.
• the orientation index of the boron nitride powder can be adjusted, for example, by controlling the growth of primary particles when producing the boron nitride powder.
• the orientation index of boron nitride powder in this specification means a value measured according to the following method.
• the X-ray diffraction device for example, “ULTIMA-IV” (product name) manufactured by Rigaku Co., Ltd. is used.
• the crushing strength of the agglomerated particles contained in the boron nitride powder may be 4 MPa or more.
• the crushing strength of the agglomerated particles contained in the boron nitride powder may be 5 MPa or more, 8 MPa or more, or 10 MPa or more from the viewpoint of not easily collapsing during kneading with a resin.
• the voids inside the aggregated particles become larger due to particle growth, and the crushing strength of the aggregated particles also decreases.
• the crushing strength of the aggregated particles may be 20 MPa or less, 15 MPa or less, or 12 MPa or less.
• the crushing strength of the aggregated particles is 20 MPa or less, at least a portion of the aggregated particles are appropriately collapsed during kneading with the resin, and the generation of voids is easily suppressed.
• the resulting resin composition has higher insulation properties.
• the crushing strength of the aggregated particles may be, for example, 4 to 20 MPa, 5 to 20 MPa, 8 to 15 MPa, or 10 to 12 MPa.
• the crushing strength in this specification is a value measured in accordance with the description of JIS R 1639-5:2007 "Fine ceramics - Method for measuring grain characteristics - Part 5: Single grain crushing strength” means.
• the measurement was performed on 20 or more aggregated particles, and the value at a cumulative destruction rate of 63.2% was calculated.
• a micro compression tester can be used for the measurement.
• As the micro compression tester for example, "MCT-210" (product name) manufactured by Shimadzu Corporation can be used.
• a method for producing boron nitride powder includes firing and cooling a raw material mixture containing boron carbonitride powder and a boron source to generate primary particles of boron nitride, and the primary particles are aggregated to form a structure.
• the nitrogen gas concentration is 99.90% by volume or more and the leakage amount is 270 ⁇ 10 ⁇ 4 Pa ⁇ The raw material mixture is fired and cooled in a closed space with a velocity of m 3 /sec or less.
• the decarburization crystallization step is usually carried out in an open space where gases can flow out and in.
• the calcination and cooling in the decarburization crystallization process are performed in the closed space as described above, so that the boron oxide content in the finally obtained boron nitride powder can be reduced as much as possible.
• boron nitride powder with excellent weather resistance can be obtained.
• boron nitride powder with excellent weather resistance is not clear, but the reason is that according to the above method, it is easier to obtain boron nitride powder with high crystallinity of primary particles and high purity of hexagonal boron nitride. It can be considered as That is, it is presumed that the crystallinity of the primary particles contained in the boron nitride powder increases and the purity of hexagonal boron nitride increases, making it difficult for the boron oxide content to increase in the usage environment.
• closed space means a space that is isolated from the external environment to the extent that the amount of gas leaks is below the above upper limit, and the closed space is completely isolated from the external environment (gas It may not be blocked (to such an extent that outflow and inflow of water is impossible).
• the closed space is usually a space formed by partitioning a part of the inside of the firing furnace.
• the closed space may be, for example, a space defined by the inner wall, door, lid, etc. of the firing furnace, or may be an internal space of a container or the like independent from the firing furnace.
• a mechanism for trapping volatile components may be provided in the closed space.
• the method for producing boron nitride powder according to one embodiment may further include a step (preparation step) of preparing boron carbonitride powder used in the decarburization crystallization step. Further, the method for producing boron nitride powder according to one embodiment may further include a step of pulverizing aggregated particles in the powder obtained in the decarburization crystallization step (pulverization step). Furthermore, the method for producing boron nitride powder according to one embodiment may further include a step (cleaning step) of washing the powder obtained in the decarburization crystallization step or a pulverized product thereof.
• the preparation process includes, for example, a pressure nitriding process in which boron carbide powder (B 4 C powder) is fired in a pressurized nitrogen atmosphere.
• boron carbide in the boron carbide powder is nitrided to obtain a fired product containing boron carbonitride.
• a fired product containing hexagonal boron carbonitride with high purity can be obtained.
• Boron carbide powder is an aggregate of boron carbide particles.
• the purity of the boron carbide powder (the content of boron carbide) may be 96.0% by mass or more, or 98.0% by mass or more.
• a commercially available boron carbide powder may be used, or a separately prepared boron carbide powder may be used.
• Boron carbide powder is produced by, for example, mixing boric acid and acetylene black and then heating the mixture at 1800 to 2400°C for 1 to 10 hours in an inert gas atmosphere to obtain a boron carbide lump, and the resulting carbonization process. It can be obtained by a method including the steps of preparing a boron carbide powder by pulverizing a boron lump, sieving it, washing it, removing impurities, drying it, etc. as appropriate.
• Firing in the pressure nitriding process and cooling after firing are usually performed in a closed space where the leakage rate is 270 ⁇ 10 ⁇ 4 Pa ⁇ m 3 /sec or less.
• the details of the closed space are omitted because they are the same as the closed space in which firing in the decarburization crystallization step and cooling after firing are performed.
• the firing temperature in the pressure nitriding step is preferably higher than the firing temperature in the decarburization crystallization step.
• the firing temperature in the pressure nitriding step may be, for example, 1900 to 2200°C, 2000 to 2200°C, or 2100 to 2200°C. By setting the firing temperature within the above range, the crystallinity of boron carbonitride can be improved and the proportion of hexagonal boron carbonitride can be increased.
• the firing time in the pressure nitriding step is not particularly limited as long as the nitriding progresses sufficiently, and may be, for example, 6 to 30 hours, 8 to 25 hours, or 10 to 20 hours.
• the atmospheric pressure in the pressure nitriding step may be, for example, 0.6 to 1.0 MPa, 0.7 to 1.0 MPa, or 0.8 to 1.0 MPa.
• the atmospheric pressure in the pressure nitriding step may be, for example, 0.6 to 1.0 MPa, 0.7 to 1.0 MPa, or 0.8 to 1.0 MPa.
• the nitrogen gas concentration of the nitrogen pressurized atmosphere in the pressurized nitriding step may be, for example, 95.00 volume % or more, 98.00 volume % or more, or 99.90 volume % or more.
• boron carbide can be nitrided under milder conditions. Note that the above nitrogen gas concentration is a concentration based on volume in a standard state.
• the fired product obtained in the pressure nitriding process may be used as it is in the decarburization crystallization process, and may be appropriately subjected to pulverization treatment, classification treatment, cleaning treatment, heat treatment (for example, oxidation treatment in an atmosphere containing oxygen), etc. After that, it may be used in the decarburization crystallization step. That is, the preparation step may further include a step of performing a pulverization treatment, a classification treatment, a cleaning treatment, a heat treatment (for example, an oxidation treatment in an atmosphere containing oxygen), and the like.
• the pulverization process can be performed using a general pulverizer or crusher such as a ball mill, vibration mill, or jet mill. Note that "pulverization" in this specification also includes "crushing".
• Boron carbonitride powder is an aggregate of boron carbonitride particles.
• the purity of the boron carbonitride powder (the content of boron carbonitride) may be 98.0% by mass or more.
• As the boron carbonitride powder a commercially available boron carbonitride powder may be used, or one prepared in the above preparation step may be used.
• boron carbonitride powder with a high proportion of hexagonal boron carbonitride is used as the boron carbonitride powder, the proportion of hexagonal boron nitride in the obtained boron nitride powder can be increased.
• boron carbonitride powder obtained through the pressure nitriding step is used, the proportion of hexagonal boron nitride in the obtained boron nitride powder can be increased.
• boron source examples include boric acid, boron oxide, and the like. These can be used alone or in combination of two or more. When boric acid is used as a boron source, the effect of promoting the growth of primary particles can be easily obtained.
• the amount of boron source used may be, for example, 25 to 50% by weight based on the total weight of the raw material mixture.
• materials other than boron carbonitride powder and boron source may be used.
• carbonates can be used in addition to the boron source.
• the raw material mixture may further contain carbonate.
• carbonates include sodium carbonate, calcium carbonate, strontium carbonate, and the like. These can be used alone or in combination of two or more. When sodium carbonate is used as the carbonate, the effect of promoting the growth of primary particles can be easily obtained.
• the amount of carbonate used may be, for example, 1 to 10% by weight based on the total weight of the raw material mixture.
• the amount of leakage in the closed space where firing and cooling are performed in the decarburization crystallization step is 250 ⁇ 10 ⁇ 4 Pa ⁇ m 3 /sec or less or 200 ⁇ 10 from the viewpoint of making it easier to obtain boron nitride powder with better weather resistance. It may be less than -4 Pa ⁇ m 3 /sec.
• the lower limit of the leakage amount in a closed space may be 0 Pa ⁇ m 3 /sec, 0.1 ⁇ 10 ⁇ 4 Pa ⁇ m 3 /sec or 0.5 ⁇ 10 ⁇ 4 Pa ⁇ m 3 /sec. It's okay.
• the nitrogen gas concentration in the closed space may be 99.95% by volume or more from the viewpoint of easily obtaining boron nitride powder with better weather resistance.
• the upper limit of the nitrogen gas concentration is not particularly limited, but may be 100% by volume or 99.99% by volume.
• the atmospheric pressure during firing in the decarburization crystallization step may be 1 kPa or more, 2 kPa or more, or 3 kPa or more. By setting the atmospheric pressure to 3 kPa or more, the crystallinity of boron nitride can be further improved, and boron nitride powder with better weather resistance can be easily obtained.
• the atmospheric pressure during firing in the decarburization crystallization step may be 100 kPa or less, 90 kPa or less, or 80 kPa or less. By setting the above-mentioned atmospheric pressure to 80 kPa or less, it is possible to further suppress the collapse of aggregated particles during the decarburization crystallization step. From the above viewpoint, the atmospheric pressure during firing in the decarburization crystallization step may be 1 to 100 kPa, 2 to 90 kPa, or 3 to 80 kPa. Note that the above atmospheric pressure indicates gauge pressure.
• the firing temperature in the decarburization crystallization step may be 1900°C or higher, or 2000°C or higher. By setting the firing temperature to 1900° C. or higher, not only can the growth of primary particles proceed sufficiently, but also boron nitride powder with excellent weather resistance can be easily obtained.
• the firing temperature in the decarburization crystallization step may be 2400°C or lower, 2200°C or lower, or 2100°C or lower. By setting the firing temperature to 2400° C. or lower, yellowing of the boron nitride powder can be suppressed. From the above viewpoint, the firing temperature in the decarburization crystallization step may be, for example, 1900 to 2400°C, 1900 to 2200°C, or 2000 to 2100°C.
• the above-mentioned firing temperature means the temperature maintained during heating (firing).
• the heating start temperature is not particularly limited, but may be room temperature (for example, 25° C.).
• the heating rate up to 1000°C is, for example, 0.5 to 10.0°C/min, 2.0 to 10.0°C/min, or 0.5 to 5°C.
• the heating rate above 1000°C may be, for example, 0.1-5.0°C/min, 0.5-5.0°C/min or 2.0-4.0°C/min. It may be 0°C/min.
• the firing time in the decarburization crystallization step may be 2 hours or more, 3 hours or more, or 4 hours or more. By setting the firing time to 2 hours or more, not only can the growth of primary particles proceed more fully, but also boron nitride powder with excellent weather resistance can be easily obtained.
• the firing time in the decarburization crystallization step may be 40 hours or less, 30 hours or less, or 20 hours or less. By setting the firing time to 40 hours or less, it is possible to suppress an increase in manufacturing costs. From the above viewpoint, the firing time in the decarburization crystallization step may be, for example, 4 to 40 hours, 6 to 30 hours, or 8 to 20 hours.
• the above-mentioned baking time means the holding time at the holding temperature.
• the raw material mixture is heated from a temperature of 1000°C or lower to a holding temperature of 1900°C or higher at a heating rate of 0.5 to 5.0°C/min and held at the holding temperature for 2 hours or more.
• the temperature increase rate may be set to 1.0 to 5.0°C/min, or may be set to 2.0 to 4.0°C/min. good.
• the boron nitride powder After firing, the boron nitride powder may be sufficiently cooled in the closed space.
• the temperature of the boron nitride powder when the closed space is opened to the outside environment (for example, the atmosphere) may be 40° C. or lower.
• the pulverization step aggregated particles in the powder (boron nitride powder) obtained in the decarburization crystallization step are pulverized.
• the aggregated particles that are crushed in the crushing process are mainly aggregated particles (so-called tertiary particles) that are formed by further agglomeration of aggregated particles (so-called secondary particles) that are formed by aggregating the primary particles of boron nitride. ).
• the pulverization step by pulverizing the tertiary particles in the boron nitride powder, the proportion of the secondary particles can be increased.
• the method of pulverization in the pulverization process can also affect the weather resistance of boron nitride powder.
• the crushing process may be performed by an impact type crushing method using a general crusher or crusher such as a pin mill, jet mill, vibration mill, planetary mill, attritor mill, bead mill, etc.;
• the grinding may be carried out by a grinding and shearing method using a stone mill, a feather mill, or the like.
• the latter grinding method tends to yield boron nitride powder with higher weather resistance.
• the grinding and shearing type grinding method may be a method using a stone mill type grinder and a feather mill that are capable of continuous grinding (grinding). When agglomerated particles are crushed by frictional shearing, grinding and shearing may be performed after crushing by impact or compression.
• the cleaning step the powder (boron nitride powder) obtained in the decarburization crystallization step or its pulverized product is cleaned.
• the cleaning step may be, for example, a step in which the boron nitride powder or its pulverized product is brought into contact with an acid and subjected to a wet treatment, and then the cleaning treatment is performed until the electrical conductivity of the cleaning liquid becomes 0.7 mS/m or less.
• the boron oxide content in the boron nitride powder can be reduced.
• the "pulverized product” is a powder obtained through the above-mentioned pulverization process, and may be one that has been subjected to classification treatment or the like after the pulverization process.
• Wet treatment can be performed, for example, by immersing boron nitride powder or a pulverized product thereof in an acid and stirring.
• the acid used in the wet treatment may be, for example, dilute nitric acid, concentrated nitric acid, or the like.
• As the acid used in the wet treatment for example, hydrochloric acid, hydrofluoric acid, sulfuric acid, etc. can be used, but when these acids are used, ionic impurities derived from the acid may be generated. On the other hand, when nitric acid is used, it is easy to suppress the generation of ionic impurities.
• the contact time with the acid in the wet treatment may be, for example, 10 minutes to 5 hours.
• the cleaning treatment is performed by bringing the boron nitride powder into contact with the cleaning liquid.
• the cleaning liquid is usually a liquid containing water, and water, ion exchange water, etc. are used. A mixed solution of an organic solvent and water can also be used as the cleaning liquid.
• the cleaning liquid contains components other than water, the content of water in the cleaning liquid may be 60% by mass or more based on the total mass of the cleaning liquid.
• the cleaning treatment may be performed, for example, by a method of mixing boron nitride powder after wet treatment or a pulverized product thereof and a cleaning liquid and stirring the mixture.
• the amount of the cleaning liquid used may be, for example, 100 to 500 parts by mass per 100 parts by mass of boron nitride powder (or pulverized product thereof).
• the temperature of the cleaning liquid may be, for example, 50 to 90°C.
• the cleaning liquid may be stirred using, for example, a stirrer, a magnetic stirrer, a disperser, or the like.
• the stirring time may be, for example, 30 to 180 minutes.
• the stirring speed may be, for example, 10-100 rpm.
• the cleaning process may be repeated multiple times.
• a series of operations may be repeated in which boron nitride powder and cleaning liquid are mixed and stirred, the boron nitride powder is separated from the cleaning liquid, and the separated boron nitride powder is mixed with new cleaning liquid again.
• cleaning may be performed until the electrical conductivity of the cleaning solution is 0.7 mS/m or less, and the electrical conductivity of the cleaning solution is 0.5 mS/m or less, 0.3 mS/m or less, or 0.2 mS/m or less. You may wash until it becomes below m.
• the washing step may be carried out before the pulverizing step, a higher cleaning effect is likely to be obtained if the washing step is carried out after the pulverizing step. That is, when the cleaning step is performed on the pulverized powder (boron nitride powder) obtained in the decarburization crystallization step, a higher cleaning effect is likely to be obtained.
• the boron nitride powder after the decarburization crystallization step may be subjected to treatments other than the above-mentioned pulverization and washing. For example, a classification process may be performed to obtain boron nitride powder having a desired average particle size. Classification processing is usually performed after pulverization processing. Further, for example, when the boron nitride powder contains magnetic particles, a process for removing the magnetic particles may be performed.
• Magnetized particle removal treatment is usually carried out on a slurry containing boron nitride powder or a pulverized product thereof and water (for example, a slurry containing boron nitride powder or a pulverized product thereof after the above-mentioned cleaning treatment).
• a slurry containing boron nitride powder or a pulverized product thereof after the above-mentioned cleaning treatment for example, an electromagnetic metal removal device (for example, electromagnetic iron removal device), a magnetic type metal removal device (for example, magnetic type iron removal device), etc.
• the lower limit of the magnetic flux density of the magnetic field applied to the slurry may be, for example, 0.5T or more, 0.6T or more, 1.0T or more, or 1.3T or more.
• the upper limit of the magnetic flux density of the magnetic field applied to the slurry may be, for example, 1.8T or less, 1.7T or less, or 1.6T or less.
• the magnetic flux density of the magnetic field applied to the slurry can be adjusted within the above-mentioned range, and may be, for example, 0.5 to 1.8T.
• boron nitride powder with excellent weather resistance can be obtained. More specifically, for example, it contains agglomerated particles formed by agglomeration of primary particles of boron nitride, has a graphitization index of 2.0 or less, and has a boron oxide content of 0.1% by mass or less, Boron nitride powder having a boron oxide content of 0.2% by mass or less after the heat cycle test described above can be obtained.
• a resin composition according to one embodiment contains the boron nitride powder according to the above embodiment.
• the resin composition is used, for example, as a heat conductive insulating material.
• heat conductive insulating materials include insulating layers of printed wiring boards used in electronic components such as word devices, transistors, thyristors, and CPUs, thermal interface materials, and the like.
• the resin contained in the resin composition known resins used for heat conductive insulating materials can be used.
• the resin include liquid crystal polymer, fluororesin, silicone resin, silicone rubber, acrylic resin, polyolefin (polyethylene, etc.), epoxy resin, phenol resin, melamine resin, urea resin, unsaturated polyester, polyimide, polyamideimide, polyether.
• Imide polybutylene terephthalate, polyethylene terephthalate, polyphenylene ether, polyphenylene sulfide, fully aromatic polyester, polysulfone, polyether sulfone, polycarbonate, maleimide modified resin, ABS (acrylonitrile-butadiene-styrene) resin, AAS (acrylonitrile-acrylic rubber/styrene) ) resin and AES (acrylonitrile-ethylene-propylene-diene rubber-styrene) resin.
• ABS acrylonitrile-butadiene-styrene
• AAS acrylonitrile-acrylic rubber/styrene
• AES acrylonitrile-ethylene-propylene-diene rubber-styrene
• the content of the resin may be, for example, 15% by volume or more, 20% by volume or more, or 30% by volume or more, based on the total volume of the resin composition.
• the content of the resin may be, for example, 60% by volume or less, 50% by volume or less, or 40% by volume or less, based on the total volume of the resin composition.
• the content of the boron nitride powder may be, for example, 30% by volume or more, 40% by volume or more, 50% by volume or more, or 60% by volume or more, based on the total volume of the resin composition.
• the content of boron nitride powder may be, for example, 85% by volume or less, 80% by volume or less, or 70% by volume or less, based on the total volume of the resin composition.
• the resin composition may further contain a curing agent for curing the resin.
• the curing agent can be appropriately selected depending on the type of resin.
• examples of the curing agent include phenol novolac compounds, acid anhydrides, amino compounds, and imidazole compounds.
• the content of the curing agent may be, for example, 0.5 parts by mass or more or 1.0 parts by mass or more with respect to 100 parts by mass of the resin.
• the content of the curing agent may be, for example, 15.0 parts by mass or less or 10.0 parts by mass or less based on 100 parts by mass of the resin.
• boron carbide powder 100 parts by mass of orthoboric acid manufactured by Nippon Denko Corporation and 35 parts by mass of acetylene black (trade name: HS100L) manufactured by Denka Corporation were mixed using a Henschel mixer. The obtained mixture was filled into a graphite crucible and heated in an arc furnace at 2200° C. in an argon atmosphere for 6 hours to obtain bulk boron carbide (B 4 C). The obtained lumps were coarsely crushed using a jaw crusher to obtain coarse powder. The obtained coarse powder was further pulverized using a ball mill having silicon carbide balls (diameter: 10 mm) to obtain a pulverized powder.
• boron carbide powder (B 4 C powder) with an average particle size of 20 ⁇ m.
• the specific surface area of the boron carbide powder was 0.4 m 2 /g, and the purity was 98% by mass.
• the average particle diameter of the boron carbide powder was measured in accordance with the description of ISO 13320:2009 using a laser diffraction scattering particle size distribution analyzer (device name: LS-13 320) manufactured by Beckman Coulter. Note that the boron carbide powder was not subjected to homogenizer treatment.
• water was used as the solvent for dispersing the boron carbide powder, and hexametaphosphoric acid was used as the dispersant. At this time, a value of 1.33 was used as the refractive index of water, and a value of 2.6 was used as the refractive index of boron carbide powder.
• the purity of boron carbide powder was calculated from the sum of carbon content and boron content.
• the amount of carbon was calculated from combustion infrared absorption method, and the amount of boron was calculated from ICP emission spectrometry.
• the crucible was taken out of the dryer and baked in a closed space in a resistance heating furnace (leakage rate: 150 ⁇ 10 -4 Pa ⁇ m 3 /sec) for 5 hours, and then heated to room temperature (25°C) in the closed space. Cooled.
• the nitrogen gas concentration in the firing atmosphere was 99.95% by volume
• the firing temperature was 2000° C.
• the atmospheric pressure was 0.01 MPa.
• heating to the firing temperature started from room temperature, and after raising the temperature to 1000°C at a temperature increase rate of 4°C/min, the temperature was raised from 1000°C to 2000°C at a temperature increase rate of 2°C/min.
• the powder obtained in the decarburization crystallization step was pulverized using a non-impact pulverization method. Specifically, the fired powder is crushed using a jaw crusher manufactured by Makino, and then the crushed powder is crushed using a friction shear type crusher (Multi Mill manufactured by Grow Engineering) to eliminate agglomerations in the powder. The particles were ground. Thereafter, the obtained pulverized product was classified by passing through a sieve with an opening of 75 ⁇ m to obtain the boron nitride powder of Example 1 containing aggregated particles formed by agglomeration of primary particles of hexagonal boron nitride.
• Example 2 The nitriding process of Example 2 was carried out in the same manner as in Example 1, except that the amount of sodium carbonate used in the decarburization crystallization step was adjusted to 0.5% by mass based on the total mass of the raw material mixture. Boron powder was obtained.
• Example 3 The procedure was carried out in the same manner as in Example 1, except that the pulverized material obtained in the pulverization step was classified by passing it through a sieve with an opening of 75 ⁇ m, and then the following washing step was performed on the obtained powder. Boron nitride powder of Example 3 was obtained.
• a solution was prepared by adding 40 g of the classified powder to 400 g of dilute nitric acid (nitric acid concentration: 1% by mass), and the solution was stirred at room temperature for 60 minutes. After stirring, the solution was allowed to stand for one hour, and the supernatant liquid was discarded by decantation, followed by adding ion-exchanged water and stirring for 30 minutes. Thereafter, solid-liquid separation was performed by suction filtration, and the filtrate was washed by replacing water until it became neutral. Finally, cleaning was performed until the electrical conductivity of the cleaning solution (water) became 0.2 mS/m. When the electrical conductivity of the cleaning liquid was confirmed to be 0.2 mS/m, the solid content (cake portion) obtained by filtration was subjected to the following magnetizable particle removal treatment.
• the above solid content and ion-exchanged water at 25°C were mixed to prepare 10 L of water slurry with a solid content concentration of 30% by mass.
• 10 L of the above water slurry was put into a 20 L resin container.
• the water slurry in the resin container was stirred at a rotation speed of 100 rpm using a stirrer manufactured by Yamato Scientific Co., Ltd. (product name: Labo Stirra LR500B (all PTFE coated with a length of 100 mm and equipped with a stirring rod with blades)). I let it happen.
• a resin hose with an inner diameter of 12 mm was used as a flow path connecting the resin container and the electromagnetic de-iron machine, and the length of the flow path was 5 m.
• the obtained slurry was subjected to solid-liquid separation by suction filtration to obtain a solid content from which magnetic particles were removed.
• the solid content from which the magnetized particles had been removed was placed on a boron nitride plate, and then heated at 400° C. for 30 minutes in a nitrogen atmosphere using a high-temperature dryer to obtain a dry powder.
• the dry powder was used as the boron nitride powder of Example 3.
• Example 4 The amount of leakage in the closed space in the resistance heating furnace used in the decarburization crystallization process was changed to 5.5 ⁇ 10 -4 Pa ⁇ m 3 /sec, and the nitrogen gas concentration in the firing atmosphere (nitrogen gas concentration in the closed space ) was increased to 99.99% by volume, boron nitride powder of Example 4 was obtained in the same manner as in Example 3.
• Example 5 In [Preparation of boron carbide powder], the grinding conditions and classification conditions were changed so that the average particle size of the obtained boron carbide powder was 50 ⁇ m, and the boron carbide powder with an average particle size of 50 ⁇ m was used in the [pressure nitriding process] A boron nitride powder of Example 5 was obtained in the same manner as in Example 4, except that the opening of the sieve used in the pulverization step was changed to 150 ⁇ m.
• Example 6> In [Preparation of boron carbide powder], the grinding conditions and classification conditions were changed so that the average particle size of the obtained boron carbide powder was 15 ⁇ m, and the boron carbide powder with an average particle size of 15 ⁇ m was used in the [pressure nitriding process] A boron nitride powder of Example 6 was obtained in the same manner as in Example 4, except that the sieve opening used in the pulverization step was changed to 45 ⁇ m.
• Example 7 In [Preparation of boron carbide powder], the grinding conditions and classification conditions were changed so that the average particle size of the obtained boron carbide powder was 8 ⁇ m, and the boron carbide powder with an average particle size of 8 ⁇ m was used in the [pressure nitriding process] A boron nitride powder of Example 7 was obtained in the same manner as in Example 4, except that the sieve opening used in the pulverization step was changed to 53 ⁇ m.
• Comparative example 1 In the decarburization crystallization process, an open-type firing furnace was used instead of a resistance heating furnace with a closed space, and firing was performed under normal pressure. A boron nitride powder of Comparative Example 1 was obtained in the same manner as in Example 1, except that the pulverization treatment was carried out using a mold pulverization method. Note that nitrogen gas having a nitrogen gas concentration of 99.9% by volume was continuously supplied to the space where the powder was fired in the open furnace, so that the firing atmosphere was made into a nitrogen gas atmosphere.
• Comparative example 2 In the crushing process, the fired powder was crushed using a jaw crusher manufactured by Makino, and then the crushed powder was crushed using a friction shear type crusher (Multi Mill manufactured by Grow Engineering). A boron nitride powder of Comparative Example 2 was obtained in the same manner as Comparative Example 1 except for the above.
• Comparative example 3 In the decarburization crystallization step, the boron nitride of Comparative Example 3 was prepared in the same manner as Comparative Example 1, except that the firing temperature (holding temperature) was changed to 1850°C and the firing time (holding time) was changed to 15 hours. A powder was obtained.
• the boron oxide (B 2 O 3 ) content in the boron nitride powder was measured according to the following procedure. (1) After drying the boron nitride powder at 120° C. for 2 hours, 5 g of the dried boron nitride powder was accurately weighed into a flat weighing tube and mixed with 15 ml of methanol (special grade reagent) to obtain a mixed solution. (2) The mixture obtained in (1) above was allowed to stand on a hot plate at 80°C for 1 hour and then dried in a dryer at 120°C for 1.5 hours to evaporate methanol and remove boron oxide. A boron nitride powder from which was removed was obtained.
• boron nitride powder was sealed in a zippered polyethylene bag Unipack C-4.
• the bag filled with boron nitride powder was placed in a constant temperature and humidity device (manufactured by Etak, trade name: FX420N) preset at a temperature of 0°C and a humidity of 80% RH, and the following operation (I) was performed for one cycle.
• a heat cycle test was conducted for a total of 1000 cycles. (I) Heating from 0°C to 50°C at a heating rate of 3.0°C/min, then holding for 30 minutes, cooling from 50°C to 0°C at a cooling rate of 1.5°C/min, then holding for 30 minutes. do.
• the boron oxide (B 2 O 3 ) content in the boron nitride powder after the heat cycle test was measured in the same manner as above.
• the graphitization index (GI) of the boron nitride powder was calculated from the measurement results by powder X-ray diffraction method.
• the integrated intensity of each diffraction peak that is, each diffraction peak
• the area values (units are arbitrary) surrounded by the line were calculated and set as S100, S101, and S102, respectively.
• the graphitization index was determined based on the following equation (1).
• G. I. (S100+S101)/S102...(1)
• the orientation index of boron nitride powder was determined from the measurement results by powder X-ray diffraction method. First, boron nitride powder was filled into the recess of a glass cell with a depth of 0.2 mm attached to an X-ray diffraction device (manufactured by Rigaku Co., Ltd., product name: ULTIMA-IV). A measurement sample was prepared by solidifying at a set pressure M using a sample manufactured by Amenatech Co., Ltd. (trade name: PX700). If the surface of the filling material solidified by the molding machine was not smooth, it was smoothed manually before measurement.
• the peak intensity ratio between the (002) plane and the (100) plane of boron nitride is calculated, and based on this value, the orientation index [I (002 )/I(100)] was determined.
• the purity of boron nitride powder was determined by the following method. First, boron nitride powder was subjected to alkaline decomposition with sodium hydroxide, and ammonia was distilled from the decomposed liquid by steam distillation and collected in an aqueous boric acid solution. This collected liquid was subjected to titration with a normal sulfuric acid solution. The content of nitrogen atoms (N) in the boron nitride powder was calculated from the titration results. From the obtained content of nitrogen atoms, the content of boron nitride in the boron nitride powder was determined based on formula (2), and the purity of the boron nitride powder was calculated.
• the moisture content of the boron nitride powder was measured based on the Karl Fischer method in accordance with JIS K 0068:2001 "Method for measuring moisture in chemical products". Specifically, first, a predetermined amount of a measurement sample (boron nitride powder) was taken on an air-fired alumina board, and the sample was placed in a furnace whose temperature was constant at 25°C. Next, using nitrogen gas as a carrier gas, the moisture generated when heated to the measurement temperature (400° C.) was measured by coulometric titration. The moisture content was determined by converting the obtained results per unit mass (1 g).
• the average particle diameter of the boron nitride powder was measured in accordance with the description of ISO 13320:2009 using a laser diffraction scattering particle size distribution analyzer (device name: LS-13 320) manufactured by Beckman Coulter. Note that the boron nitride powder was not subjected to homogenizer treatment.
• water was used as the solvent for dispersing the boron nitride powder, and hexametaphosphoric acid was used as the dispersant. At this time, a value of 1.33 was used as the refractive index of water, and a value of 1.80 was used as the refractive index of boron nitride powder.
• the specific surface area of the boron nitride powder was calculated by applying the BET single point method using nitrogen gas in accordance with the description in JIS Z 8830:2013 "Specific surface area measurement method of powder (solid) by gas adsorption".
• a specific surface area measuring device (device name: Cantersorb) manufactured by Yuasa Ionics Co., Ltd. was used. Note that the measurement was performed after the boron nitride powder was dried and degassed at 300° C. for 15 minutes.
• crushed strength The crushing strength of the aggregated particles was measured in accordance with the description in JIS R 1639-5:2007 "Fine ceramics - Method for measuring grain characteristics - Part 5: Single grain crushing strength”.
• a micro compression tester manufactured by Shimadzu Corporation, product name "MCT-210" was used. Note that the measurement was performed on 20 or more aggregated particles, and the value at a cumulative destruction rate of 63.2% was calculated.
• a resin composition was prepared using each of the boron nitride powders obtained in Examples 1 to 7 and Comparative Examples 1 to 3, and an evaluation sheet was produced using the resin composition. Specifically, first, boron nitride powder was added to a mixture of 100 parts by mass of naphthalene type epoxy resin (manufactured by DIC Corporation, HP4032) and 10 parts by mass of an imidazole compound (manufactured by Shikoku Kasei Co., Ltd., 2E4MZ-CN) as a curing agent. A resin composition was obtained by mixing so that the amount of the resin composition was 60% by volume.
• naphthalene type epoxy resin manufactured by DIC Corporation, HP4032
• an imidazole compound manufactured by Shikoku Kasei Co., Ltd., 2E4MZ-CN
• Awatori Rentaro manufactured by Shinky Co., Ltd. was used for kneading with the resin.
• the kneading conditions were 1600 rpm for 3 minutes.
• the obtained resin composition was applied onto a PET film to a thickness of 0.3 mm. Thereafter, a 0.3 mm resin sheet (evaluation sheet) was produced by heating and pressurizing under relatively mild conditions at a temperature of 160° C. and 50 kgf/cm 2 for 50 minutes.
• the evaluation sheet was subjected to a weathering test in which it was treated at 60° C. and 90RH% for 500 hours, and then the dielectric breakdown voltage of the evaluation sheet after the weathering test was measured.
• the dielectric breakdown voltage was measured using a voltage tester (manufactured by Kikusui Electronics Co., Ltd., device name: TOS-8650) in accordance with the description of JIS C 6481-1996 "Test method for copper-clad laminates for printed wiring boards". I used it.
• the obtained dielectric breakdown voltage was evaluated relative to the result of Comparative Example 1 as 1.0.
• Density B was determined using the Archimedes method.
• the specific heat capacity C was determined using DSC (manufactured by Rigaku Co., Ltd., product name: ThermoPlusEvoDSC8230).
• the obtained thermal conductivity was evaluated relative to the result of Comparative Example 1 as 1.0. Note that all the obtained thermal conductivities were 10 W/mK or more.

Landscapes

• Chemical & Material Sciences (AREA)
• Organic Chemistry (AREA)
• Inorganic Chemistry (AREA)
• Health & Medical Sciences (AREA)
• Chemical Kinetics & Catalysis (AREA)
• Medicinal Chemistry (AREA)
• Polymers & Plastics (AREA)
• Ceramic Products (AREA)
• Compositions Of Macromolecular Compounds (AREA)

Priority Applications (4)

Applications Claiming Priority (2)

Publications (1)

Family

ID=88201752

Family Applications (1)

Country Status (5)

Cited By (2)

Citations (5)

Family Cites Families (1)

• 2023
  • 2023-03-28 CN CN202380020357.3A patent/CN118660861A/zh active Pending
  • 2023-03-28 WO PCT/JP2023/012545 patent/WO2023190528A1/ja not_active Ceased
  • 2023-03-28 US US18/850,543 patent/US20250215192A1/en active Pending
  • 2023-03-28 JP JP2024512573A patent/JP7769784B2/ja active Active
  • 2023-03-28 KR KR1020247032264A patent/KR20240153387A/ko active Pending