WO2023095657A1 - Feuille adhésive optique recouverte - Google Patents

Feuille adhésive optique recouverte Download PDF

Info

Publication number
WO2023095657A1
WO2023095657A1 PCT/JP2022/042207 JP2022042207W WO2023095657A1 WO 2023095657 A1 WO2023095657 A1 WO 2023095657A1 JP 2022042207 W JP2022042207 W JP 2022042207W WO 2023095657 A1 WO2023095657 A1 WO 2023095657A1
Authority
WO
WIPO (PCT)
Prior art keywords
adhesive sheet
release liner
optical
film
sensitive adhesive
Prior art date
Application number
PCT/JP2022/042207
Other languages
English (en)
Japanese (ja)
Inventor
和広 山村
新 藤原
Original Assignee
日東電工株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 日東電工株式会社 filed Critical 日東電工株式会社
Publication of WO2023095657A1 publication Critical patent/WO2023095657A1/fr

Abstract

Une feuille adhésive optique (X), en tant que feuille adhésive optique recouverte selon la présente invention, comprend une feuille adhésive optique (10), une doublure de séparation transparente (20) et un film de protection de surface (30), dans cet ordre dans le sens de l'épaisseur (H). La feuille adhésive optique (10) présente une première surface (11) et une seconde surface (12) sur le côté opposé à la première surface (11). La doublure de séparation transparente (20) est disposée sur la première surface (11). Le film de protection de surface (30) présente une surface adhésive (30a) et est fixé à la doublure de séparation transparente (20) par l'intermédiaire de la surface adhésive (30a). Une première force de pelage entre le film de protection de surface (30) et la doublure de séparation transparente (20) dans les conditions d'un angle de pelage de 180° et d'une vitesse de traction de 300 mm/minute est inférieure à une seconde force de pelage entre la doublure de séparation transparente (20) et la feuille adhésive optique (10) dans lesdites conditions.
PCT/JP2022/042207 2021-11-26 2022-11-14 Feuille adhésive optique recouverte WO2023095657A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2021192098 2021-11-26
JP2021-192098 2021-11-26

Publications (1)

Publication Number Publication Date
WO2023095657A1 true WO2023095657A1 (fr) 2023-06-01

Family

ID=86539575

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2022/042207 WO2023095657A1 (fr) 2021-11-26 2022-11-14 Feuille adhésive optique recouverte

Country Status (2)

Country Link
TW (1) TW202330834A (fr)
WO (1) WO2023095657A1 (fr)

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH05157914A (ja) * 1991-12-02 1993-06-25 Nitto Denko Corp 光学検査用保護フィルム
JP2018013727A (ja) * 2016-07-22 2018-01-25 日東電工株式会社 光学フィルムセット及びその製造方法
JP2018109093A (ja) * 2016-12-28 2018-07-12 日東電工株式会社 表面保護フィルム
JP2019044119A (ja) * 2017-09-06 2019-03-22 日東電工株式会社 有機ｅｌ表示装置用粘着剤組成物、有機ｅｌ表示装置用粘着剤層、有機ｅｌ表示装置用粘着剤層付き偏光フィルム、及び有機ｅｌ表示装置
WO2019146553A1 (fr) * 2018-01-24 2019-08-01 日東電工株式会社 Film de protection de surface et élément optique avec film de protection de surface
WO2020218806A1 (fr) * 2019-04-22 2020-10-29 삼성에스디아이 주식회사 Film de protection adhésif à base de silicone et élément optique le comprenant

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH05157914A (ja) * 1991-12-02 1993-06-25 Nitto Denko Corp 光学検査用保護フィルム
JP2018013727A (ja) * 2016-07-22 2018-01-25 日東電工株式会社 光学フィルムセット及びその製造方法
JP2018109093A (ja) * 2016-12-28 2018-07-12 日東電工株式会社 表面保護フィルム
JP2019044119A (ja) * 2017-09-06 2019-03-22 日東電工株式会社 有機ｅｌ表示装置用粘着剤組成物、有機ｅｌ表示装置用粘着剤層、有機ｅｌ表示装置用粘着剤層付き偏光フィルム、及び有機ｅｌ表示装置
WO2019146553A1 (fr) * 2018-01-24 2019-08-01 日東電工株式会社 Film de protection de surface et élément optique avec film de protection de surface
WO2020218806A1 (fr) * 2019-04-22 2020-10-29 삼성에스디아이 주식회사 Film de protection adhésif à base de silicone et élément optique le comprenant

Also Published As

Publication number Publication date
TW202330834A (zh) 2023-08-01

Similar Documents

Publication Publication Date Title
JP7265350B2 (ja) 補強フィルムおよび補強フィルム付きデバイスの製造方法
JP6757479B2 (ja) 粘着シート、粘着層付き光学フィルム、積層体、および画像表示装置
JP2023075141A (ja) 粘着剤層付き偏光フィルム、及び画像表示装置
WO2020158484A1 (fr) Feuille adhésive, film optique comprenant une couche adhésive, corps multicouche et dispositif d'affichage d'image
JP2020083996A (ja) 粘着シートおよびその製造方法、ならびに画像表示装置の製造方法
JP2020128470A (ja) 粘着シート、光学積層体、および画像表示装置
WO2023095657A1 (fr) Feuille adhésive optique recouverte
WO2021070635A1 (fr) Composition adhésive photodurcissable, feuille adhésive double face et son procédé de production, et dispositif optique et son procédé de production
JP2005023114A (ja) 感圧型両面接着テープ又はシート
JP7111558B2 (ja) 積層体
JP2022116860A (ja) フォルダブルデバイス用光学粘着シート
WO2022071212A1 (fr) Feuille adhésive sensible à la pression optique avec séparateur
WO2022071211A1 (fr) Séparateur
WO2022071213A1 (fr) Feuille adhésive optique fixée à un séparateur
US20220106501A1 (en) Pressure sensitive adhesive sheet, pressure sensitive adhesive-equipped optical film and image display device
JP2022058223A (ja) セパレータ付き光学粘着シート
WO2023276654A1 (fr) Film optique avec film de recouvrement
JP7362872B2 (ja) 光半導体素子封止用シートおよび表示体
JP2022058222A (ja) セパレータ
JP2022058224A (ja) セパレータ付き光学粘着シート
WO2024024829A1 (fr) Procédé de pelage de feuille adhésive
JP2024048326A (ja) はく離ライナー付き粘着シート、および、はく離ライナー付き粘着シートの製造方法
KR20230061258A (ko) 박리 라이너 부착 광학 점착 시트
KR20240062967A (ko) 박리 라이너
JP2023095055A (ja) カバーフィルム付き光学フィルム

Legal Events

Date Code Title Description
ENP Entry into the national phase

Ref document number: 2022570101

Country of ref document: JP

Kind code of ref document: A

121 Ep: the epo has been informed by wipo that ep was designated in this application