WO2023079908A1 - エッチング液、エッチング方法、半導体デバイスの製造方法及びゲートオールアラウンド型トランジスタの製造方法 - Google Patents

エッチング液、エッチング方法、半導体デバイスの製造方法及びゲートオールアラウンド型トランジスタの製造方法 Download PDF

Info

Publication number
WO2023079908A1
WO2023079908A1 PCT/JP2022/037834 JP2022037834W WO2023079908A1 WO 2023079908 A1 WO2023079908 A1 WO 2023079908A1 JP 2022037834 W JP2022037834 W JP 2022037834W WO 2023079908 A1 WO2023079908 A1 WO 2023079908A1
Authority
WO
WIPO (PCT)
Prior art keywords
silicon
component
etching
etching solution
silicon germanium
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2022/037834
Other languages
English (en)
French (fr)
Inventor
憲 原田
鉄夫 笠井
竜暢 鈴木
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Mitsubishi Chemical Corp
Original Assignee
Mitsubishi Chemical Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Mitsubishi Chemical Corp filed Critical Mitsubishi Chemical Corp
Priority to JP2023557911A priority Critical patent/JPWO2023079908A1/ja
Publication of WO2023079908A1 publication Critical patent/WO2023079908A1/ja
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

ホスホニウム塩（Ａ）を含む、シリコンマニウムに対してシリコンを選択的に溶解するエッチング液。ホスホニウム塩（Ａ）としては、特にテトラブチルホスホニウムヒドロキシドが好ましい。このエッチング液を用いて、シリコンとシリコンゲルマニウムとを含む構造体をエッチングする、エッチング方法。

Description

エッチング液、エッチング方法、半導体デバイスの製造方法及びゲートオールアラウンド型トランジスタの製造方法
　本発明は、エッチング液、エッチング方法、半導体デバイスの製造方法及びゲートオールアラウンド型トランジスタの製造方法に関する。
　ムーアの法則に則り、集積回路の微細化が進んでいる。
　近年では、従来の平面型トランジスタのサイズを小さくするだけではなく、Ｆｉｎ型トランジスタ（Ｆｉｎ型ＦＥＴ）やゲートオールアラウンド型トランジスタ（ＧＡＡ型ＦＥＴ）のように、構造を変化させて性能を向上させると共に、更なる微細化や集積化を進めるための検討がされている。
　Ｆｉｎ型ＦＥＴでは、シリコン基板に対して垂直方向にＦｉｎを形成することにより、単位面積あたりのトランジスタ数を増やすだけでなく、低い電圧時のＯＮ／ＯＦＦ制御に優れた性能を示す。
　更なる性能向上を発揮させるためには、Ｆｉｎのアスペクト比を大きくする等の工夫が必要となる。しかし、アスペクト比が大き過ぎると、Ｆｉｎ形成のための洗浄工程や乾燥工程においてＦｉｎが倒壊する等の課題がある。
　ＧＡＡ型ＦＥＴでは、チャネルとなるナノシートやナノワイヤーをゲート電極で覆い、チャネルとゲート電極の接触面積を増やすことにより、単位面積あたりのトランジスタの性能を向上させる。
　ＧＡＡ型ＦＥＴを形成させるためには、シリコンとシリコンゲルマニウムが交互に積層された構造体から、シリコン又はシリコンゲルマニウムを選択的にエッチングするためのエッチング液が必要となる。そのようなエッチング液として、特許文献１には、４級水酸化アンモニウム化合物、具体的にはエチルトリメチルアンモニウムヒドロキシドを含むエッチング液が開示されている。
特開２０１９－０５０３６４号公報
　特許文献１で開示されているエチルトリメチルアンモニウムヒドロキシドを含むエッチング液は、シリコンゲルマニウムに対するシリコンの選択的溶解性が十分ではない。
　本発明の目的は、シリコンゲルマニウムの溶解を抑制し、シリコンの溶解を促進し、シリコンゲルマニウムに対するシリコンの選択的溶解性に優れるエッチング液を提供することにある。
　本発明の目的はまた、このエッチング液を用いたエッチング方法、半導体デバイスの製造方法及びゲートオールアラウンド型トランジスタの製造方法を提供することにある。
　本発明者は、後述する本発明のエッチング液が、シリコンゲルマニウムの溶解を抑制し、シリコンの溶解を促進し、シリコンゲルマニウムに対するシリコンの選択的溶解性に優れることを見出した。
　即ち、本発明の要旨は、以下の通りである。
［１］　ホスホニウム塩（Ａ）を含む、シリコンゲルマニウムに対してシリコンを選択的に溶解するエッチング液。
［２］　ホスホニウム塩（Ａ）が、第四級ホスホニウム塩を含む、［１］に記載のエッチング液。
［３］　第四級ホスホニウム塩の４つのアルキル基が、同一のアルキル基である、［２］に記載のエッチング液。
［４］　ホスホニウム塩（Ａ）が、テトラブチルホスホニウムヒドロキシドを含む、［３］に記載のエッチング液。
［５］　ホスホニウム塩（Ａ）の濃度が、０．１ｍｏｌ／Ｌ以上である、［１］～［４］のいずれかに記載のエッチング液。
［６］　ホスホニウム塩（Ａ）の濃度が、０．３ｍｏｌ／Ｌ以上である、［５］に記載のエッチング液。
［７］　更に、キレート剤（Ｂ）を含む、［１］～［６］のいずれかに記載のエッチング液。
［８］　更に、水混和性溶媒（Ｃ）を含む、［１］～［７］のいずれかに記載のエッチング液。
［９］　更に、水（Ｄ）を含む、［１］～［８］のいずれかに記載のエッチング液。
［１０］　［１］～［９］のいずれかに記載のエッチング液を用いて、シリコンとシリコンゲルマニウムとを含む構造体をエッチングする、エッチング方法。
［１１］　［１］～［９］のいずれかに記載のエッチング液を用いて、シリコンとシリコンゲルマニウムとを含む構造体をエッチングする工程を含む、半導体デバイスの製造方法。
［１２］　［１］～［９］のいずれかに記載のエッチング液を用いて、シリコンとシリコンゲルマニウムとを含む構造体をエッチングする工程を含む、ゲートオールアラウンド型トランジスタの製造方法。
　本発明のエッチング液は、シリコンゲルマニウムの溶解を抑制し、シリコンの溶解を促進し、シリコンゲルマニウムに対するシリコンの選択的溶解性に優れる。
　本発明のエッチング液を用いる本発明のエッチング方法、本発明の半導体デバイスの製造方法及び本発明のゲートオールアラウンド型トランジスタの製造方法は、エッチング工程において、シリコンゲルマニウムの溶解を抑制し、シリコンの溶解を促進し、シリコンゲルマニウムに対するシリコンの優れた選択的溶解性により、高精度のエッチングを行って所望の製品を歩留りよく製造することができる。
　以下に本発明について詳述する。本発明は、以下の実施の形態に限定されるものではなく、その要旨の範囲内で種々に変更して実施することができる。
　本明細書において「～」という表現を用いる場合、その前後の数値又は物性値を含む表現として用いるものとする。
　本発明のエッチング液は、ホスホニウム塩（Ａ）（以下、「成分（Ａ）」と称す場合がある。）を含むことで、シリコンゲルマニウムに対してシリコンを選択的に溶解することができる。
　本発明のエッチング液は、更にキレート剤（Ｂ）（以下、「成分（Ｂ）」と称す場合がある。）、水混和性溶媒（Ｃ）（以下、「成分（Ｃ）」と称す場合がある。）、水（Ｄ）（以下、「成分（Ｄ）」と称す場合がある。）を含んでいてもよい。
＜成分（Ａ）＞
　成分（Ａ）は、ホスホニウム塩（Ａ）である。エッチング液にホスホニウム塩（Ａ）を含むことで、シリコンやシリコンゲルマニウムを溶解する効果を発現する。
　成分（Ａ）のホスホニウム塩（Ａ）としては、例えば、第四級ホスホニウム塩等が挙げられる。これらのうち、シリコン選択的溶解性に優れることから、第四級ホスホニウム塩が好ましい。
　第四級ホスホニウム塩は、ホスホニウムイオンの４つの水素原子がアルキル基に置換されたカチオンとアニオンとを含む化合物である。
　第四級ホスホニウム塩のアニオンの種類としては、水酸化物塩、ハロゲン化物塩、四フッ化ホウ素塩、六フッ化リン塩、スルホン酸塩、酢酸塩等が挙げられる。これらのうち、シリコン選択的溶解性に優れることから、水酸化物塩、四フッ化ホウ素塩、六フッ化リン塩、スルホン酸塩、酢酸塩が好ましく、水酸化物塩がより好ましい。
　第四級ホスホニウム塩のアルキル基の炭素数は、シリコンゲルマニウムに対するシリコンの選択的溶解性に優れることから、４～４８が好ましく、８～２４がより好ましい。
　第四級ホスホニウム塩の４つのアルキル基は、同一であってもよく、異なるものであってもよいが、同一であることが、シリコンゲルマニウムに対するシリコンの選択的溶解性の観点から好ましい。
　第四級ホスホニウム塩としては、具体的には、テトラエチルホスホニウムヒドロキシド、テトラプロピルホスホニウムヒドロキシド、テトラブチルホスホニウムヒドロキシド、テトラヘキシルホスホニウムヒドロキシド等が挙げられる。
　これらの第四級ホスホニウム塩のうち、シリコンゲルマニウムに対するシリコンの選択的溶解性の観点から、テトラエチルホスホニウムヒドロキシド、テトラプロピルホスホニウムヒドロキシド、テトラブチルホスホニウムヒドロキシド、テトラヘキシルホスホニウムヒドロキシドが好ましく、テトラブチルホスホニウムヒドロキシドがより好ましい。
　ホスホニウム塩（Ａ）は、１種を単独で用いてもよく、２種以上を併用してもよい。
　本発明のエッチング液中の成分（Ａ）の濃度は、シリコンの選択的溶解性に優れることから、０．１ｍｏｌ／Ｌ以上が好ましく、０．３ｍｏｌ／Ｌ以上がより好ましい。
　本発明のエッチング液中の成分（Ａ）の濃度は、シリコンの選択的溶解性に優れることから、３ｍｏｌ／Ｌ以下が好ましく、２ｍｏｌ／Ｌ以下がより好ましい。
　また、成分（Ａ）の含有率は、シリコンの選択的溶解性に優れることから、エッチング液１００質量％中、５質量％以上が好ましく、１０質量％以上がより好ましい。
　成分（Ａ）の含有率は、シリコンの選択的溶解性に優れることから、エッチング液１００質量％中、７８質量％以下が好ましく、５２質量％以下がより好ましい。
＜成分（Ｂ）＞
　本発明のエッチング液は、成分（Ａ）以外に、成分（Ｂ）としてキレート剤を含むことが好ましい。エッチング液にキレート剤を含むことで、シリコンゲルマニウムを保護する効果を発現する。
　キレート剤としては、例えば、アミン化合物、アミノ酸、有機酸等が挙げられる。キレート剤は、１種を単独で用いてもよく、２種以上を併用してもよい。
　これらのキレート剤の中でも、シリコンゲルマニウムに対するシリコンの選択的溶解性に優れることから、アミン化合物、アミノ酸、有機酸が好ましく、アミン化合物がより好ましい。
　アミン化合物としては、例えば、エチレンジアミン、１，３－ジアミノプロパン、１，４－ジアミノブタン、エチレンジアミン四酢酸、ジエチレントリアミン五酢酸、トリエチレンテトラアミン六酢酸、ジエチレントリアミンペンタキス（メチルホスホン酸）、エチレンジアミン－Ｎ，Ｎ’－ビス［２－（２－ヒドロキシフェニル)酢酸］、Ｎ，Ｎ’－ビス（３－アミノプロパン）エチレンジアミン、Ｎ－メチル－１，３－ジアミノプロパン、２－アミノエタノール、Ｎ－メチルジエタノールアミン、２－アミノ－２－メチル－１－プロパノール等が挙げられる。アミン化合物は、１種を単独で用いてもよく、２種以上を併用してもよい。
　これらのアミン化合物の中でも、シリコンゲルマニウムに対するシリコンの選択的溶解性に優れることから、エチレンジアミン、１，３－ジアミノプロパン、１，４－ジアミノブタン、エチレンジアミン四酢酸、ジエチレントリアミン五酢酸、トリエチレンテトラアミン六酢酸、ジエチレントリアミンペンタキス（メチルホスホン酸）、エチレンジアミン－Ｎ，Ｎ’－ビス［２－（２－ヒドロキシフェニル)酢酸］、Ｎ，Ｎ’－ビス（３－アミノプロパン）エチレンジアミン、Ｎ－メチル－１，３－ジアミノプロパン、２－アミノエタノール、Ｎ－メチルジエタノールアミン、２－アミノ－２－メチル－１－プロパノールが好ましく、エチレンジアミン、１，３－ジアミノプロパン、１，４－ジアミノブタン、エチレンジアミン四酢酸、ジエチレントリアミン五酢酸、トリエチレンテトラアミン六酢酸、ジエチレントリアミンペンタキス（メチルホスホン酸）、エチレンジアミン－Ｎ，Ｎ’－ビス［２－（２－ヒドロキシフェニル)酢酸］がより好ましい。
　アミノ酸としては、例えば、グリシン、アルギニン、ヒスチジン、（２－ジヒドロキシエチル）グリシン等が挙げられる。アミノ酸は、１種を単独で用いてもよく、２種以上を併用してもよい。
　これらのアミノ酸の中でも、シリコンゲルマニウムに対するシリコンの選択的溶解性に優れることから、グリシン、アルギニン、ヒスチジン、（２－ジヒドロキシエチル）グリシンが好ましく、（２－ジヒドロキシエチル）グリシンがより好ましい。
　有機酸としては、例えば、シュウ酸、クエン酸、酒石酸、リンゴ酸、２－ホスホノブタン－１，２，４－トリカルボン酸等が挙げられる。有機酸は、１種を単独で用いてもよく、２種以上を併用してもよい。
　これらの有機酸の中でも、シリコンゲルマニウムに対するシリコンの選択的溶解性に優れることから、シュウ酸、クエン酸、酒石酸、リンゴ酸、２－ホスホノブタン－１，２，４－トリカルボン酸が好ましく、クエン酸、２－ホスホノブタン－１，２，４－トリカルボン酸がより好ましい。
　成分（Ｂ）の含有率は、シリコンゲルマニウムに対するシリコンの選択的溶解性に優れることから、エッチング液１００質量％中、０．００１質量％以上が好ましく、０．０１質量％以上がより好ましい。
　成分（Ｂ）の含有率は、シリコンゲルマニウムに対するシリコンの選択的溶解性に優れることから、エッチング液１００質量％中、２５質量％以下が好ましく、１０質量％以下がより好ましい。
＜成分（Ｃ）＞
　本発明のエッチング液は、成分（Ａ）、成分（Ｂ）以外に、成分（Ｃ）として水混和性溶媒を含むことが好ましい。エッチング液に水混和性溶媒を含むことで、シリコンゲルマニウムを保護する効果を発現する。
　水混和性溶媒としては、水に対する溶解性に優れるものであればよく、溶解パラメータ（ＳＰ値）が７．０（ｃａｌ／ｃｍ３）１／２以上の溶媒が好ましい。
　水混和性溶媒としては、例えば、イソプロパノール、エチレングリコール、プロピレングリコール、メタノール、エタノール、プロパノール、ブタノール、グリセロール、２－（２－アミノエトキシエタノール）等の極性プロトン性溶媒；アセトン、ジメチルスルホキシド、Ｎ，Ｎ－ジメチルホルムアミド、Ｎ－メチルピロリドン、アセトニトリル等の極性非プロトン性溶媒；ヘキサン、ベンゼン、トルエン、ジエチルエーテル等の非極性溶媒等が挙げられる。水混和性溶媒は、１種を単独で用いてもよく、２種以上を併用してもよい。
　これらの水混和性溶媒の中でも、シリコンゲルマニウムに対するシリコンの選択的溶解性に優れることから、グリセロール、２－（２－アミノエトキシエタノール）、エチレングリコール、プロピレングリコールが好ましい。
　成分（Ｃ）の含有率は、シリコンゲルマニウムに対するシリコンの選択的溶解性に優れることから、エッチング液１００質量％中、０．０１質量％以上が好ましく、０．１質量％以上がより好ましい。
　成分（Ｃ）の含有率は、シリコンゲルマニウムに対するシリコンの選択的溶解性に優れることから、エッチング液１００質量％中、８０質量％以下が好ましく、６０質量％以下がより好ましい。
＜成分（Ｄ）＞
　本発明のエッチング液は、成分（Ａ）、成分（Ｂ）、成分（Ｃ）以外に、成分（Ｄ）として水を含むことが好ましい。成分（Ｄ）の含有率は、成分（Ａ）、成分（Ｂ）、成分（Ｃ）及び後述する他の成分の残部とすればよい。
＜他の成分＞
　本発明のエッチング液は、成分（Ａ）、成分（Ｂ）、成分（Ｃ）、成分（Ｄ）以外に、他の成分を含んでもよい。
　他の成分としては、例えば、アニオン型界面活性剤、ノニオン型界面活性剤、カチオン型界面活性剤等の界面活性剤；ポリビニルアルコール、ポリエチレングリコール、ポリプロピレングリコール、ポリエチレンイミン、ポリプロピレンイミン、ポリアクリル酸等の水溶性高分子；過酸化水素、過塩素酸、過ヨウ素酸等の酸化剤；アスコルビン酸、没食子酸、ピロガロール、ピロカテコール、レゾルシノール、ヒドロキノン等の還元剤等が挙げられる。他の成分は、１種を単独で用いてもよく、２種以上を併用してもよい。
＜各成分の質量比＞
　本発明のエッチング液が成分（Ａ）と成分（Ｂ）を含む場合、成分（Ａ）に対する成分（Ｂ）の質量比（成分（Ｂ）の質量／成分（Ａ）の質量、以下、「（Ｂ）／（Ａ）」と記載する。）は、シリコンゲルマニウムに対するシリコンの選択的溶解性に優れることから、０．０００１～２が好ましく、０．００１～１がより好ましい。
　本発明のエッチング液が成分（Ａ）と成分（Ｃ）を含む場合、成分（Ａ）に対する成分（Ｃ）の質量比（成分（Ｃ）の質量／成分（Ａ）の質量、以下、「（Ｃ）／（Ａ）」と記載する。）は、シリコンゲルマニウムに対するシリコンの選択的溶解性に優れることから、０．００１～６が好ましく、０．０１～２がより好ましい。
＜エッチング液の製造方法＞
　本発明のエッチング液の製造方法は、特に限定されず、成分（Ａ）と、必要に応じて成分（Ｂ）、成分（Ｃ）、成分（Ｄ）、及び他の成分を混合することで製造することができる。
　混合の順番は、特に限定されず、一度にすべての成分を混合してもよく、一部の成分を予め混合した後に残りの成分を混合してもよい。
＜エッチング液の物性＞
　本発明のエッチング液のシリコンのエッチレートＥＲＳｉは、シリコンゲルマニウムに対するシリコンの選択的溶解性に優れることから、１ｎｍ／分以上が好ましく、３ｎｍ／分以上がより好ましい。
　本発明のエッチング液のシリコンゲルマニウムのエッチレートＥＲＳｉＧｅは、シリコンゲルマニウムに対するシリコンの選択的溶解性に優れることから、３ｎｍ／分以下が好ましく、２ｎｍ／分以下がより好ましく、１．５ｎｍ／分以下が更に好ましい。
　本発明のエッチング液のシリコンゲルマニウムとシリコンの溶解選択比（ＥＲＳｉ／ＥＲＳｉＧｅ）は、シリコンゲルマニウムに対するシリコンの選択的溶解性に優れることから、４以上が好ましく、１０以上がより好ましい。
　エッチレートＥＲＳｉ、エッチレートＥＲＳｉＧｅ、溶解選択比は、後掲の実施例の項に記載の方法で測定、算出される。
＜エッチング液のエッチング対象＞
　本発明のエッチング液は、シリコンゲルマニウムの溶解を抑制し、シリコンの溶解を促進し、シリコンゲルマニウムに対するシリコンの選択的溶解性に優れる。このため、本発明のエッチング液は、エッチング対象として、シリコンとシリコンゲルマニウムとを含む構造体、例えば、半導体デバイスに好適であり、ＧＡＡ型ＦＥＴの形成に必要なシリコンとシリコンゲルマニウムが交互に積層された構造体に特に好適である。
　エッチング対象となるシリコンゲルマニウム中のシリコンの含有率は、本発明のエッチング液によるエッチングに好適であることから、シリコンゲルマニウム１００質量％中、１０質量％以上が好ましく、２０質量％以上がより好ましい。
　エッチング対象となるシリコンゲルマニウム中のシリコンの含有率は、本発明のエッチング液によるエッチングに好適であることから、シリコンゲルマニウム１００質量％中、９５質量％以下が好ましく、８５質量％以下がより好ましい。
　エッチング対象となるシリコンゲルマニウム中のゲルマニウムの含有率は、本発明のエッチング液によるエッチングに好適であることから、シリコンゲルマニウム１００質量％中、５質量％以上が好ましく、１５質量％以上がより好ましい。
　エッチング対象となるシリコンゲルマニウム中のゲルマニウムの含有率は、本発明のエッチング液によるエッチングに好適であることから、シリコンゲルマニウム１００質量％中、９０質量％以下が好ましく、８０質量％以下がより好ましい。
　シリコンゲルマニウムの合金膜は、公知の方法で成膜して製造すればよい。トランジスタ形成後の電子やホールの移動性に優れることから、シリコンゲルマニウムの合金膜は、結晶成長法で成膜して製造することが好ましい。
　シリコンとシリコンゲルマニウムとを含む構造体やシリコンとシリコンゲルマニウムが交互に積層された構造体は、シリコン酸化物が露出していてもよい。
＜エッチング方法＞
　本発明のエッチング方法は、本発明のエッチング液を用いて、シリコンとシリコンゲルマニウムとを含む構造体をエッチングする方法である。
　エッチング様式は、公知の様式を用いることができる。例えば、バッチ式、枚葉式等が挙げられる。
　エッチング時の温度は、エッチレートを向上させることができることから、１５℃以上が好ましく、２０℃以上がより好ましい。
　エッチング時の温度は、基板へのダメージ低減とエッチングの安定性の観点から、１００℃以下が好ましく、８０℃以下がより好ましい。
　ここで、エッチング時の温度とは、エッチング時のエッチング液の温度に該当する。
＜用途＞
　本発明のエッチング液や本発明のエッチング方法は、シリコンとシリコンゲルマニウムとを含む構造体をエッチングする工程を含む半導体デバイスの製造に好適に用いることができる。特に、シリコンゲルマニウムの溶解を抑制し、シリコンの溶解を促進し、シリコンゲルマニウムに対するシリコンの選択的溶解性に優れることから、シリコンとシリコンゲルマニウムとを含む構造体をエッチングする工程を含むＧＡＡ型ＦＥＴの製造に特に好適に用いることができる。
　以下、実施例を用いて本発明を更に具体的に説明する。本発明は、その要旨を逸脱しない限り、以下の実施例の記載に限定されるものではない。
＜原料＞
　以下の実施例及び比較例において、エッチング液の製造原料としては、以下のものを用いた。
　成分（Ａ－１）：テトラブチルホスホニウムヒドロキシド
　成分（Ａ’－１）：エチルトリメチルアンモニウムヒドロキシド
　成分（Ａ’－２）：テトラメチルアンモニウムヒドロキシド
　成分（Ａ’－３）：テトラエチルアンモニウムヒドロキシド
　成分（Ａ’－４）：水酸化カリウム
　成分（Ｂ－１）：エチレンジアミン
　成分（Ｂ－２）：グリシン
　成分（Ｂ－３）：クエン酸
　成分（Ｃ－１）：エチレングリコール
　成分（Ｃ－２）：グリセロール
　成分（Ｃ－３）：イソプロピルアルコール
　成分（Ｄ－１）：水
＜シリコンのエッチレート＞
　膜厚１０ｎｍのシリコンゲルマニウムと膜厚１０ｎｍ（浸漬前のシリコン層の幅＝１０ｎｍ）のシリコンが積層された構造体を含む基板を０．５質量％のフッ化水素酸水溶液に６０秒浸漬させた後、超純水でリンスし、その後、実施例及び比較例で得られたエッチング液に５０℃で２分間浸漬させた。浸漬後の基板断面を電子顕微鏡で観察してシリコン層の幅（ｎｍ）を測定し、下記式（１）を用いてシリコンのエッチレートＥＲＳｉ［ｎｍ／分］を算出した。
　ＥＲＳｉ［ｎｍ／分］＝（浸漬前のシリコン層の幅－浸漬後のシリコン層の幅）÷２分　（１）
＜シリコンゲルマニウムのエッチレート＞
　膜厚１０ｎｍ（浸漬前のシリコンゲルマニウム層の幅＝１０ｎｍ）のシリコンゲルマニウムと膜厚１０ｎｍのシリコンが積層された構造体を含む基板を０．５質量％のフッ化水素酸水溶液に６０秒浸漬させた後、超純水でリンスし、その後、実施例及び比較例で得られたエッチング液に５０℃で２分間浸漬させた。浸漬後の基板断面を電子顕微鏡で観察して、シリコンゲルマニウム層の幅（ｎｍ）を測定し、下記式（２）を用いてシリコンゲルマニウム層のエッチレートＥＲＳｉＧｅ［ｎｍ／分］を算出した。
　ＥＲＳｉＧｅ［ｎｍ／分］＝（浸漬前のシリコンゲルマニウム層の幅－
　浸漬後のシリコンゲルマニウム層の幅）÷２分　　　　　　（２）
＜シリコンとシリコンゲルマニウムの溶解選択比＞
　下記式（３）を用いて、シリコンゲルマニウムとシリコンの溶解選択比を算出した。
　溶解選択比＝ＥＲＳｉ［ｎｍ／分］÷ＥＲＳｉＧｅ［ｎｍ／分］　（３）
［実施例１］
　エッチング液１００質量％中、成分（Ａ－１）が０．５ｍｏｌ／Ｌ（１３．８質量％）、成分（Ｄ－１）が残部となるよう、各成分を混合し、エッチング液を得た。
　得られたエッチング液の評価結果を、表１に示す。
［実施例２］
　成分（Ａ－１）の含有率を１．０ｍｏｌ／Ｌ（２７．６質量％）とした以外は、実施例１と同様に操作を行い、エッチング液を得た。
　得られたエッチング液の評価結果を、表１に示す。
［実施例３］
　成分（Ａ－１）の含有率を１．３ｍｏｌ／Ｌ（３５．９質量％）とした以外は、実施例１と同様に操作を行い、エッチング液を得た。
　得られたエッチング液の評価結果を、表１に示す。
［実施例４～９］
　実施例２において、エッチング液１００質量％中、成分（Ｂ－１）、成分（Ｂ－２）、成分（Ｂ－３）、成分（Ｃ－１）、成分（Ｃ－２）又は成分（Ｃ－３）の含有率が表１に示す量で、成分（Ｄ－１）が残部となるように、更にこれらの成分を添加したこと以外は、各成分を混合し、それぞれエッチング液を得た。
　得られたエッチング液の評価結果を、表１に示す。
［比較例１］
　成分（Ａ－１）の代りに成分（Ａ’－１）を１．４ｍｏｌ／Ｌ用いた以外は、実施例１と同様に操作を行い、エッチング液を得た。
　得られたエッチング液の評価結果を、表１に示す。
［比較例２～４］
　成分（Ａ－１）の代りに、表１に示す通り、成分（Ａ’－２）、成分（Ａ’－３）又は成分（Ａ’－４）を用いた以外は、実施例２と同様に操作を行い、エッチング液を得た。
　得られたエッチング液の評価結果を、表１に示す。
Figure JPOXMLDOC01-appb-T000001
　表１からも分かるように、実施例１～９で得られた、成分（Ａ）としてテトラブチルホスホニウムヒドロキシドを含むエッチング液は、シリコンゲルマニウムの溶解を抑制し、シリコンの溶解を促進し、シリコンゲルマニウムに対するシリコンの選択的溶解性に優れた。
　一方、テトラブチルホスホニウムヒドロキシドの代りに特許文献１のようにエチルトリメチルアンモニウムヒドロキシドを用いた比較例１で得られたエッチング液は、シリコンゲルマニウムの溶解も促進し、シリコンゲルマニウムに対するシリコンの選択的溶解性に劣った。
　また、比較例２～４のように、テトラメチルアンモニウムヒドロキシド、テトラエチルアンモニウムヒドロキシド、水酸化カリウムを用いた場合も、シリコンゲルマニウムに対するシリコンの選択的溶解性は劣るものであった。
　本発明を特定の態様を用いて詳細に説明したが、本発明の意図と範囲を離れることなく様々な変更が可能であることは当業者に明らかである。
　本出願は、２０２１年１１月２日付で出願された日本特許出願２０２１－１７９５７９に基づいており、その全体が引用により援用される。
　本発明のエッチング液及びこのエッチング液を用いた本発明のエッチング方法は、シリコンゲルマニウムの溶解を抑制し、シリコンの溶解を促進し、シリコンゲルマニウムに対するシリコンの選択的溶解性に優れる。このため、本発明のエッチング液及びこのエッチング液を用いた本発明のエッチング方法は、半導体デバイスの製造に好適に用いることができ、特にＧＡＡ型ＦＥＴの製造に好適に用いることができる。

Claims (12)

  1. 　ホスホニウム塩（Ａ）を含む、シリコンゲルマニウムに対してシリコンを選択的に溶解するエッチング液。
  2. 　ホスホニウム塩（Ａ）が、第四級ホスホニウム塩を含む、請求項１に記載のエッチング液。
  3. 　第四級ホスホニウム塩の４つのアルキル基が、同一のアルキル基である、請求項２に記載のエッチング液。
  4. 　ホスホニウム塩（Ａ）が、テトラブチルホスホニウムヒドロキシドを含む、請求項３に記載のエッチング液。
  5. 　ホスホニウム塩（Ａ）の濃度が、０．１ｍｏｌ／Ｌ以上である、請求項１～４のいずれか１項に記載のエッチング液。
  6. 　ホスホニウム塩（Ａ）の濃度が、０．３ｍｏｌ／Ｌ以上である、請求項５に記載のエッチング液。
  7. 　更に、キレート剤（Ｂ）を含む、請求項１～６のいずれか１項に記載のエッチング液。
  8. 　更に、水混和性溶媒（Ｃ）を含む、請求項１～７のいずれか１項に記載のエッチング液。
  9. 　更に、水（Ｄ）を含む、請求項１～８のいずれか１項に記載のエッチング液。
  10. 　請求項１～９のいずれか１項に記載のエッチング液を用いて、シリコンとシリコンゲルマニウムとを含む構造体をエッチングする、エッチング方法。
  11. 　請求項１～９のいずれか１項に記載のエッチング液を用いて、シリコンとシリコンゲルマニウムとを含む構造体をエッチングする工程を含む、半導体デバイスの製造方法。
  12. 　請求項１～９のいずれか１項に記載のエッチング液を用いて、シリコンとシリコンゲルマニウムとを含む構造体をエッチングする工程を含む、ゲートオールアラウンド型トランジスタの製造方法。
PCT/JP2022/037834 2021-11-02 2022-10-11 エッチング液、エッチング方法、半導体デバイスの製造方法及びゲートオールアラウンド型トランジスタの製造方法 Ceased WO2023079908A1 (ja)