WO2022239945A1 - 구리 복합 구조체의 제조방법 및 이에 의해 제조된 구리 복합 구조체를 포함하는 에너지 저장 장치 및 라만 분광 기판 구조물 - Google Patents

구리 복합 구조체의 제조방법 및 이에 의해 제조된 구리 복합 구조체를 포함하는 에너지 저장 장치 및 라만 분광 기판 구조물 Download PDF

Info

Publication number
WO2022239945A1
WO2022239945A1 PCT/KR2022/003241 KR2022003241W WO2022239945A1 WO 2022239945 A1 WO2022239945 A1 WO 2022239945A1 KR 2022003241 W KR2022003241 W KR 2022003241W WO 2022239945 A1 WO2022239945 A1 WO 2022239945A1
Authority
WO
WIPO (PCT)
Prior art keywords
copper
composite structure
copper composite
manufacturing
annealing
Prior art date
Application number
PCT/KR2022/003241
Other languages
English (en)
French (fr)
Inventor
김창구
김준현
유상현
Original Assignee
아주대학교산학협력단
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 아주대학교산학협력단 filed Critical 아주대학교산학협력단
Priority to US18/288,502 priority Critical patent/US20240141530A1/en
Publication of WO2022239945A1 publication Critical patent/WO2022239945A1/ko

Abstract

구리 복합 구조체의 제조방법이 개시된다. 구리 복합 구조체의 제조방법은 구리 기둥 구조물을 제조하는 제1 단계; 및 상기 구리 기둥 구조물을 질소 분위기에서 어닐링하는 제2 단계를 포함한다.

Description

구리 복합 구조체의 제조방법 및 이에 의해 제조된 구리 복합 구조체를 포함하는 에너지 저장 장치 및 라만 분광 기판 구조물
본 발명은 다중 스케일의 구조가 복합화된 구리 복합 구조체의 제조방법 및 이에 의해 제조된 구리 복합 구조체를 포함하는 에너지 저장장치와 라만 분광 기판에 관한 것이다.
다양한 전자소자에서는 성능을 향상시키기 위해 소자의 고밀도화, 미세화 등을 시도하고 있으며 미세 구조물의 형상을 제어하여 각 소자의 성능을 향상시키는 연구가 다양하게 수행되고 있다.
마이크로 또는 나노 크기의 구리 기둥(pillar, column, rod) 배열의 구조체는 여러 전자소자에서 사용되고 있다. 특히, 이러한 다중 스케일 구조체는 금속 음극활물질과 차세대 음극 집전체 3차원 구조로 이차전지 또는 슈퍼 캐퍼시터에서 응용성을 보였으며, 라만 분광기판 제작 시 플라즈모닉 나노필러 어레이로 제조되어 분광능력의 성능을 향상시킬 수 있다.
마이크로 또는 나노 크기의 구리 기둥 배열의 구조체의 제조방법은 매우 다양하다. 대한민국 특허 등록번호 10-1409387, 10-1509529 등에는 플라즈마 식각을 이용하여 경사 또는 3차원 구리 나노구조물을 제작하는 방법이 기재되어 있다.
다중스케일(multi-scale) 구조체는 마이크로미터 크기의 구조체와 나노미터 크기의 구조체가 동시에 혼합되어 있는 형태로서, 마이크로 구조체는 기계적인 특성을 제어할 수 있고, 나노구조체는 각각의 독특한 특성을 제어하는 것이 가능하다. 이러한 복합적인 특성으로 다중스케일 구조체는 전자공학, 광학, 화학, 미세유체학, 생체모방기술 등 다양한 분야에서 응용될 수 있다.
그러나 종래의 기술은 비표면적과 기계적 특성이 뛰어난 다중스케일 구리 기둥에 대한 대면적 제작방법이 없으며 마이크로 또는 나노 단일 크기로만 제작되기 때문에 성능 증가에 한계가 있다. 따라서 이차전지, 슈퍼 캐퍼시터, 분광기판, 친수성 표면 등 다양한 분야에서 성능을 향상시키기 위해 다중스케일 구현이 가능한 구리기둥의 형상제어 방법이 요구된다.
본 발명의 일 목적은 질소분위기 어닐링과 같은 간단한 공정을 통해 다중 스케일 구리 복합 구조체를 제조할 수 있는 방법을 제공하는 것이다.
본 발명의 다른 목적은 상기 방법으로 제조된 구리 복합 구조체를 적용하는 에너지 저장 장치를 제공하는 것이다.
본 발명의 또 다른 목적은 상기 방법으로 제조된 구리 복합 구조체를 적용하는 라만 분광 기판을 제공하는 것이다.
본 발명의 실시예에 따른 구리 복합 구조체의 제조방법은 구리 기둥 구조물을 제조하는 제1 단계; 및 상기 구리 기둥 구조물을 질소 분위기에서 어닐링하는 제2 단계를 포함한다.
일 실시예에 있어서, 상기 구리 기둥 구조물은 구리 또는 이의 합금으로 형성될 수 있다.
일 실시예에 있어서, 상기 제1 단계의 구리 기둥 구조물은 홀이 형성된 템플레이트에 전해 또는 무전해 도금을 통해 상기 홀을 채우도록 구리를 도금함으로써 형성될 수 있다.
일 실시예에 있어서, 상기 제2 단계의 어닐링은 360 내지 420℃의 온도 조건 하에서 수행될 수 있다. 이 경우, 상기 제2 단계의 어닐링은 1 내지 5 Torr의 압력 조건 하에서 30 내지 90분동안 수행될 수 있다.
일 실시예에 있어서, 상기 구리 복합 구조체는 마이크로 스케일의 크기를 갖는 구리 기둥 구조물 및 이의 표면에 형성된 나노 스케일의 크기를 갖는 미세 돌기들을 포함하는 하이브리드 구조를 가질 수 있다.
본 발명의 실시예에 따른 에너지 저장장치는 구리 복합 구조체를 음극 활물질로 포함하고, 상기 구리 복합 구조체는 마이크로 스케일의 크기를 갖는 구리 기둥 구조물 및 이의 표면에 형성된 나노 스케일의 크기를 갖는 미세 돌기들을 포함하는 하이브리드 구조를 가질 수 있다. 이 경우, 상기 에너지 저장 장치는 이차전지 또는 슈퍼 커패시터일 수 있다.
본 발명의 실시예에 따른 라만 분광 기판 구조물은 분광 기판; 및 상기 라만 분광 기판 표면에 배치된 플라즈모닉 나노필러 어레이를 포함하고, 상기 플라즈모닉 나노필러 어레이는 마이크로 스케일의 크기를 갖는 구리 기둥 구조물 및 이의 표면에 형성된 나노 스케일의 크기를 갖는 미세 돌기들을 포함하는 구리 복합 구조체를 포함할 수 있다.
본 발명의 구리 복합체 제조방법에 따르면, 매우 간단한 공정을 통해 다중 스케일의 구조체를 동시에 구비하는 구리 복합 구조체를 제조할 수 있다. 또한, 이러한 방법으로 제조된 구리 복합 구조체는 마이크로 스케일의 크기를 갖는 구리 기둥 구조물 표면에 나노 스케일의 크기를 갖는 미세 돌기들이 형성된 다중 스케일(multi-scale) 하이브리드 구조를 가지므로, 우수한 기계적 특성 및 높은 비표면적과 함께 상기 나노 스케일에 의한 돌기들로부터 발생되는 독특한 물리 화학적 특성을 가질 수 있고, 그 결과 이를 전자공학, 광학, 화학, 미세유체학, 생체모방기술 등의 다양한 분야에 적용할 수 있다.
[규칙 제91조에 의한 정정 24.05.2022]　
도 1은 본 발명의 실시예에 따른 구리 복합 구조체의 제조방법을 설명하기 위한 순서도이다.
도 2a 및 도 2b는 구리 기둥 구조물을 제조하기 위한 템플레이트 및 이를 이용한 구리 기둥 구조물의 제조공정을 설명하기 위한 단면도들이고, 도 2c는 구리 기둥 구조물에 대한 질소분위기 어닐링 공정에 의한 구리 기둥 구조물의 표면 몰폴로지 변화를 설명하기 위한 도면이다.
도 3은 어닐링 전의 구리 기둥 구조물, 그리고 비교예 1, 실시예 1 및 2에 따라 어닐링된 후의 구리 복합 구조체에 대한 SEM 이미지들이다.
도 4는 비교예 1, 실시예 1 및 2에 따라 어닐링된 후의 구리 복합 구조체에 대한 SEM 이미지들이다.
도 5는 실시예 1에 따라 제조된 구리 복합 구조체의 상부면 및 측면 SEM 이미지들이다.
도 6은 실시예 1에 따라 구리 복합 구조체를 제조하는 전체 과정을 설명하는 SEM 이미지들이다.
이하, 첨부한 도면을 참조하여 본 발명의 실시예에 대해 상세히 설명한다. 본 발명은 다양한 변경을 가할 수 있고 여러 가지 형태를 가질 수 있는 바, 특정 실시예들을 도면에 예시하고 본문에 상세하게 설명하고자 한다. 그러나 이는 본 발명을 특정한 개시 형태에 대해 한정하려는 것이 아니며, 본 발명의 사상 및 기술 범위에 포함되는 모든 변경, 균등물 내지 대체물을 포함하는 것으로 이해되어야 한다.
제1, 제2 등의 용어는 다양한 구성요소들을 설명하는데 사용될 수 있지만, 상기 구성요소들은 상기 용어들에 의해 한정되어서는 안 된다. 상기 용어들은 하나의 구성요소를 다른 구성요소로부터 구별하는 목적으로만 사용된다. 예를 들어, 본 발명의 권리 범위를 벗어나지 않으면서 제1 구성요소는 제2 구성요소로 명명될 수 있고, 유사하게 제2 구성요소도 제1 구성요소로 명명될 수 있다.
본 출원에서 사용한 용어는 단지 특정한 실시예를 설명하기 위해 사용된 것으로서 본 발명을 한정하려는 의도가 아니다. 단수의 표현은 문맥상 명백하게 다르게 뜻하지 않는 한, 복수의 표현을 포함한다. 본 출원에서, "포함하다" 또는 "가지다" 등의 용어는 명세서 상에 기재된 특징, 단계, 동작, 구성요소, 부분품 또는 이들을 조합한 것이 존재함을 지정하려는 것이지, 하나 또는 그 이상의 다른 특징들이나 단계, 동작, 구성요소, 부분품 또는 이들을 조합한 것들의 존재 또는 부가 가능성을 미리 배제하지 않는 것으로 이해되어야 한다.
다르게 정의되지 않는 한, 기술적이거나 과학적인 용어를 포함해서 여기서 사용되는 모든 용어들은 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자에 의해 일반적으로 이해되는 것과 동일한 의미를 가지고 있다. 일반적으로 사용되는 사전에 정의되어 있는 것과 같은 용어들은 관련 기술의 문맥 상 가지는 의미와 일치하는 의미를 가지는 것으로 해석되어야 하며, 본 출원에서 명백하게 정의하지 않는 한, 이상적이거나 과도하게 형식적인 의미로 해석되지 않는다.
[규칙 제91조에 의한 정정 24.05.2022]　
도 1은 본 발명의 실시예에 따른 구리 복합 구조체의 제조방법을 설명하기 위한 순서도이고, 도 2a 및 도 2b는 구리 기둥 구조물을 제조하기 위한 템플레이트 및 이를 이용한 구리 기둥 구조물의 제조공정을 설명하기 위한 단면도들이고, 도 2c는 구리 기둥 구조물에 대한 질소분위기 어닐링 공정에 의한 구리 기둥 구조물의 표면 몰폴로지 변화를 설명하기 위한 도면이다.
도 1 및 도 2a 내지 도 2c를 참조하면, 본 발명의 실시예에 따른 구리 복합 구조체의 제조방법은 구리 기둥 구조물을 제조하는 제1 단계(S110); 및 상기 구리 기둥 구조물을 질소 분위기에서 어닐링하는 제2 단계(S120)을 포함할 수 있다.
상기 제1 단계(S110)에 있어서, 상기 구리 기둥 구조물은 구리 또는 이의 합금으로 형성될 수 있고, 단면이 원형, 다각형 또는 부정형의 형상을 갖고 일 방향으로 연장된 기둥 구조를 갖는다면 그 형상이 특별히 제한되지 않는다. 한편, 상기 구리 기둥 구조물의 상기 단면의 크기는 위치에 따라 일정할 수도 있고 변화될 수도 있다. 일 실시예로, 상기 구리 기둥 구조물은 단면의 크기가 수 내지 수십 마이크로미터의 크기를 갖고, 길이가 수십 내지 수백 마이크로미터의 크기를 가질 수 있다.
상기 구리 기둥 구조물의 제조방법은 특별히 제한되지 않는다. 일 실시예로, 상기 구리 기둥 구조물은 수열합성의 방법으로 형성되거나, 템플레이트를 이용한 전해 또는 무전해 도금 공정을 통해 제조될 수 있다. 이와 다른 실시예로, 상기 구리 기둥 구조물은 구리 박막을 형성한 후 이에 대한 식각 공정을 통해 형성될 수도 있다.
일 실시예에 있어서, 상기 구리 기둥 구조물은 도 2a 및 도 2b에 도시된 바와 같이, 템플레이트를 이용한 도금 공정을 통해 형성될 수 있다. 예를 들면, 지지 기판(10) 상에 에치스톱층(20) 및 식각대상층(30)을 순차적으로 적층되도록 형성한 후 상기 식각대상층(30)을 마스크(40)를 이용하여 이방성 식각함으로써, 상기 구리 기둥 구조물에 대응되는 홀이 형성된 상기 템플레이트를 제조할 수 있고, 상기 홀을 전해 도금 또는 무전해 도금을 통해 구리로 채운 후 상기 마스크(40) 및 식각대상층(30)을 제거함으로써, 상기 구리 기둥 구조물을 제조할 수 있다.
일 실시예로, 상기 지지 기판(10)은 실리콘 웨이퍼로 형성될 수 있고, 상기 식각대상층(30)은 폴리실리콘으로 형성될 수 있으며, 상기 에치스톱층(20)은 SiO2 등과 같은 실리콘 산화물, Si3N4 등과 같은 실리콘 질화물, SiC 등과 같은 실리콘 탄화물, 비정질 탄소 등과 같이 식각대상층(30)의 재료 대비 식각 선택비가 높은 물질로 형성될 수 있다.
일 실시예로, 상기 식각대상층(30)의 홀은 순환식각공정(cyclic etch process) 또는 가스변전공정(gas chopping process) 등의 식각 공정으로 형성될 수 있다. 예를 들면, 상기 식각대상층(30)의 홀은 SF6 등의 플라즈마를 이용한 식각 단계 및 C4F8 등의 플라즈마를 이용한 증착 단계가 교대로 반복적으로 수행되는 보쉬 공정(Bosch process)을 통해 형성될 수 있다.
일 실시예에 있어서, 상기 홀을 채우는 도금 공정은 무전해 도금을 통해 수행될 수 있다. 예를 들면, 상기 템플레이트의 표면을 제1 용액을 이용한 전처리한 후 제2 용액을 이용하여 도금함으로써 상기 홀을 구리로 채울 수 있다. 상기 제 1 용액은 약 4~6 ml/L 농도의 HF(불화수소), 약 2~4 ml/L 농도의 HCl(염산) 및 약 0.05~0.15 g/L 농도의 PdCl2(염화팔라듐)를 포함할 수 있고, 상기 HF(불화수소)의 비율은 약 45~55 vol%일 수 있고, 상기 HCl(염산)의 비율은 약 30~40 vol%일 수 있으며, 나머지 잔부가 상기 PdCl2(염화팔라듐)일 수 있다. 한편, 상기 제2 용액은 약 4~6 ml/L 농도의 triton-X100 [2,2'-Dipyridyl(2,2'-디피리딜](계면활성제), 약 4~6 g/L 농도의 CuSO4·5H2O(황산동), 약 14~16 g/L 농도의 EDTA(ethylenediaminetetraacetic acid), 약 4~6 ml/L 농도의 HCHO(formaldehyde), 약 0.02~0.06 g/L 농도의 2,2’Bipyridyl(2,2’비피리딜)를 포함하는 염기성 수용액일 수 있다. 상기 제2 용액을 이용한 무전해 도금 공정은 약 85~90℃에서 약 4~10 분 동안 수행될 수 있다.
상기 제2 단계(S120)에 있어서, 상기 구리 기둥 구조물은 약 360 내지 420℃의 온도, 약 1 내지 5 Torr의 압력 및 질소 분위기의 조건 하에서 약 30 내지 90분 동안 어닐링될 수 있다. 이러한 어닐링 공정을 통해, 도 2c에 도시된 바와 같이, 상기 구리 기중 구조물의 표면에는 나노 스케일, 예를 들면 약 수 내지 수십 nm의 크기를 갖는 돌기들이 형성될 수 있고, 그 결과 상기 구리 기둥 구조물의 비표면적을 현저하게 증가시킬 수 있다.
상기 구리 기둥 구조물의 표면 형상, 예를 들면, 상기 나노 스케일 돌기들의 밀도, 크기, 형상 등은 상기 어닐링의 온도, 압력 등에 많은 영향을 받는다. 예를 들면, 상기 어닐링 온도가 300℃ 미만인 경우에는 상기 미세 돌기가 형성되지 않을 수 있고, 상기 어닐링 온도가 500℃를 초과하는 경우에는 상기 돌기들의 크기가 지나치게 커지고 그 결과 비표면적이 크게증가되지 않는 문제점이 발생될 수 있다. 한편, 상기 어닐링 공정의 압력이 1 Torr 미만인 경우에는 상기 돌기들의 크기가 지나치게 커지고 그 결과 표면적이 크게 증가되지 않는 문제점이 발생될 수 있고, 상기 어닐링 공정의 압력이 5 Torr를 초과하는 경우에는 상기 미세 돌기가 형성되지 않거나 낮은 밀도로 형성되는 문제점이 발생될 수 있다.
본 발명의 구리 복합체 제조방법에 따르면, 매우 간단한 공정을 통해 다중 스케일의 구조체를 동시에 구비하는 구리 복합 구조체를 제조할 수 있다. 또한, 이러한 방법으로 제조된 구리 복합 구조체는 마이크로 스케일의 크기를 갖는 구리 기둥 구조물 표면에 나노 스케일의 크기를 갖는 미세 돌기들이 형성된 다중 스케일(multi-scale) 하이브리드 구조를 가지므로, 우수한 기계적 특성 및 높은 비표면적과 함께 상기 나노 스케일에 의한 돌기들로부터 발생되는 독특한 물리 화학적 특성을 가질 수 있고, 그 결과 이를 전자공학, 광학, 화학, 미세유체학, 생체모방기술 등의 다양한 분야에 적용할 수 있다.
일 실시예로, 상기 구리 복합 구조체는 이차전지 또는 슈퍼커패시터의 음극활물질로 적용될 수 있다. 이 경우, 상기 구리 복합 구조체는 구리 금속 기반의 음극 활물질로서 높은 에너지 밀도를 가지고, 높은 비표면적으로 인해 음극소재의 성능을 현저하게 향상시킬 수 있다.
다른 실시예로, 상기 구리 복합 구조체는 라만 분광 기판에 플라즈모닉 나노필러 어레이로 적용되어 라만 분광 기판의 분광 능력을 현저하게 향상시킬 수 있다.
또 다른 실시예로, 상기 구리 복합 구조체는 친수성 표면 특성을 가지므로, 친수성 표면 코팅제로 적용될 수 있다.
이하 본 발명의 실시예들에 대해 상술한다. 다만, 하기 실시예는 본 발명의 일부 실시 형태에 불과한 것으로서, 본 발명의 범위가 하기 실시예에 한정되는 것은 아니다.
[비교예 1, 실시예 1 및 2]
실리콘웨이퍼 상에 실리콘 산화막 및 폴리실리콘층을 순차적으로 형성한 후 마스크를 이용한 보쉬 공정(Bosch process) 공정을 통해 상기 폴리실리콘층에 홀을 형성하고, 무전해 도금 공정을 이용하여 상기 폴리실리콘층의 홀을 채우도록 구리를 도금하였다.
이어서, 폴리싱 공정을 통해 과도금된 구리를 제거한 후 상기 마스크 및 폴리실리콘층을 제거하여 구리 기둥 구조물을 제조하였다.
이어서, 하기 표 1에 기재된 바와 같이, 어닐링 온도를 변경하면서 비교예 1(350℃), 실시예 1(375℃) 및 실시예 2(400℃)의 구리 복합 구조체를 제조하였다.
Annealing
Temperature(℃)		 Pressure
(Torr)		 N2 flow rate
(sccm)		 Annealing time
(min)
350, 375, 400 1 500 60
[비교예 2 내지 4, 실시예 3 내지 5]
실시예 1 내지 3과 동일하게 구리 기둥 구조물을 제조한 후 하기 표 2에 기재된 바와 같이, 어닐링 공정의 압력을 변경하면서 비교예 2(0.2 Torr), 비교예 3(0.5 Torr), 실시예 3(1.0 Torr), 실시예 4(5.0 Torr), 실시예 5(50.0 Torr) 및 비교예 4(250.0 Torr)의 구리 복합 구조체를 제조하였다.
Annealing
Temperature(℃)		 Pressure
(Torr)		 N2 flow rate
(sccm)		 Annealing time
(min)
375 0.2, 0.5, 1, 5, 50, 250 500 60
[실험예]
도 3은 어닐링 전의 구리 기둥 구조물, 그리고 비교예 1, 실시예 1 및 2에 따라 어닐링된 후의 구리 복합 구조체에 대한 SEM 이미지들이다.
도 3을 참조하면, 질소 분위기 어닐링 이전의 구리 기둥 구조물은 구리 입자가 모여 형성된 구리 박막의 형태를 나타내었다.
비교예 1에 따라 350℃에서 어닐링한 구리 기둥 구조물은 표면에 미세 돌기들이 미세하게 나타났으나, 큰 변화가 없는 것으로 나타났다.
실시예 1에 따라 온도 375℃에서 어닐링한 구리 기둥 구조물의 표면에는 미세한 크기의 돌기가 조밀하게 형성되었으며 미세 돌기가 구리 기둥 구조물 전체 표면을 덮는 형상을 나타내었고, 그 결과 어닐링 이후 구리 기둥 구조물의 표면은 어닐링 이전보다 거친 표면이 형성되었다.
실시예 2에 따라 온도 400℃에서 어닐링한 구리 기둥 구조물의 표면에는 미세 돌기들이 형성되었으나, 미세 돌기들의 크기는 실시예 1의 구리 복합 구조체보다 작은 것으로 나타났다. 이는 어닐링 온도의 상승으로 미세 돌기들 중 일부가 녹아서 뭉개졌기 때문이다.
이상의 사항을 고려하면, 상기 구리 기둥 구조물에 대한 어닐링 온도는 약 360℃ 이상 420℃ 이하인 것이 바람직할 것으로 판단된다.
도 4는 비교예 1, 실시예 1 및 2에 따라 어닐링된 후의 구리 복합 구조체에 대한 SEM 이미지들이고, 도 5는 실시예 1에 따라 제조된 구리 복합 구조체의 상부면 및 측면 SEM 이미지들이다.
도 4 및 도 5를 참조하면, 어닐링 공정의 압력이 상대적으로 낮은 비교예 2(0.2 Torr), 비교예 3(0.5 Torr)의 경우 구리 기둥 구조물 표면이 어닐링 전보다 거칠게 변하였으나, 미세 돌기는 형성되지 않는 것으로 나타났다. 또한, 어닐링 공정의 압력이 상대적으로 높은 비교예 4(250 Torr)의 경우에는 구리 기둥 구조물 표면에 돌기의 형상은 보이지 않았으며 단순히 구리 기둥 구조물이 온도에 의해 분리되는 것으로 나타났다.
이에 반해, 실시예 3(1 Torr), 실시예 4(5 Torr)의 구리 복합 구조체에서는 구리 기둥 구조물 표면에 미세 돌기가 뚜렷하게 나타났으며, 특히 실시예 3에서 돌기가 가장 선명하게 나타났다. 실시예 4의 구리 복합 구조체에서는 구리 기둥 구조물 표면의 미세 돌기 밀도가 실시예 3보다 조금 낮아진 것으로 나타났고, 실시예 5(50 Torr)에서는 미세 돌기가 형성되기는 하였으나, 그 밀도가 실시예 3 및 4보다 낮은 것으로 나타났다.
이상의 사항을 고려하면, 상기 어닐링 공정은 약 0.9 내지 50 Torr의 압력, 바람직하게는 약 0.9 내지 5 Torr의 압력에서 수행되는 것이 바람직할 것으로 판단된다.
도 6은 실시예 1에 따라 구리 복합 구조체를 제조하는 전체 과정을 설명하는 SEM 이미지들이다.
도 6을 참조하면, 어닐링 전 구리 기둥 구조물은 522 nm의 지름, 1271 nm의 길이를 가졌으나, 어닐링 후의 구리 복합 구조체는 693 nm의 지름, 1283 nm의 길이를 갖는 것으로 나타났다. 즉, 어닐링 전후 구리 기둥의 길이는 거의 차이가 없으나 돌기의 형성으로 지름은 약 170 nm 증가하는 것으로 나타났다. 어닐링 전 구리 기둥 구조물은 표면이 비교적 매끈하였으나 어닐링 후 표면은 수십 나노 크기의 미세 돌기들이 형성된 것으로 나타났다.
상기에서는 본 발명의 바람직한 실시예를 참조하여 설명하였지만, 해당 기술 분야의 숙련된 당업자는 하기의 특허 청구 범위에 기재된 본 발명의 사상 및 영역으로부터 벗어나지 않는 범위 내에서 본 발명을 다양하게 수정 및 변경시킬 수 있음을 이해할 수 있을 것이다.

Claims (9)

  1. 구리 기둥 구조물을 제조하는 제1 단계; 및
    상기 구리 기둥 구조물을 질소 분위기에서 어닐링하는 제2 단계를 포함하는, 구리 복합 구조체의 제조방법.
  2. 제1항에 있어서,
    상기 구리 기둥 구조물은 구리 또는 이의 합금으로 형성된 것을 특징으로 하는, 구리 복합 구조체의 제조방법.
  3. 제1항에 있어서,
    상기 제1 단계의 구리 기둥 구조물은 홀이 형성된 템플레이트에 전해 또는 무전해 도금을 통해 상기 홀을 채우도록 구리를 도금함으로써 형성되는 것을 특징으로 하는, 구리 복합 구조체의 제조방법.
  4. 제1항에 있어서,
    상기 제2 단계의 어닐링은 360 내지 420℃의 온도 조건 하에서 수행되는 것을 특징으로 하는, 구리 복합 구조체의 제조방법.
  5. 제4항에 있어서,
    상기 제2 단계의 어닐링은 1 내지 5 Torr의 압력 조건 하에서 30 내지 90분동안 수행되는 것을 특징으로 하는, 구리 복합 구조체의 제조방법.
  6. 제1항에 있어서,
    상기 구리 복합 구조체는 마이크로 스케일의 크기를 갖는 구리 기둥 구조물 및 이의 표면에 형성된 나노 스케일의 크기를 갖는 미세 돌기들을 포함하는 하이브리드 구조를 갖는 것을 특징으로 하는, 구리 복합 구조체의 제조방법.
  7. 구리 복합 구조체를 음극 활물질로 포함하는 에너지 저장장치에 있어서,
    상기 구리 복합 구조체는 마이크로 스케일의 크기를 갖는 구리 기둥 구조물 및 이의 표면에 형성된 나노 스케일의 크기를 갖는 미세 돌기들을 포함하는 하이브리드 구조를 갖는 것을 특징으로 하는, 에너지 저장장치.
  8. 제7항에 있어서,
    상기 에너지 저장 장치는 이차전지 또는 슈퍼 커패시터를 포함하는 것을 특징으로 하는, 에너지 저장장치.
  9. 분광 기판; 및
    상기 라만 분광 기판 표면에 배치된 플라즈모닉 나노필러 어레이를 포함하고,
    상기 플라즈모닉 나노필러 어레이는 마이크로 스케일의 크기를 갖는 구리 기둥 구조물 및 이의 표면에 형성된 나노 스케일의 크기를 갖는 미세 돌기들을 포함하는 구리 복합 구조체를 포함하는 것을 특징으로 하는, 라만 분광 기판 구조물.
PCT/KR2022/003241 2021-05-12 2022-03-08 구리 복합 구조체의 제조방법 및 이에 의해 제조된 구리 복합 구조체를 포함하는 에너지 저장 장치 및 라만 분광 기판 구조물 WO2022239945A1 (ko)