WO2022205154A1 - Matériau actif d'électrode négative, appareil électrochimique et appareil électronique - Google Patents
Matériau actif d'électrode négative, appareil électrochimique et appareil électronique Download PDFInfo
- Publication number
- WO2022205154A1 WO2022205154A1 PCT/CN2021/084631 CN2021084631W WO2022205154A1 WO 2022205154 A1 WO2022205154 A1 WO 2022205154A1 CN 2021084631 W CN2021084631 W CN 2021084631W WO 2022205154 A1 WO2022205154 A1 WO 2022205154A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- negative electrode
- active material
- mxene
- electrode active
- silicon
- Prior art date
Abstract
Sont divulgués dans la présente demande un matériau actif d'électrode négative, un appareil électrochimique et un appareil électronique. Le matériau actif d'électrode négative de la présente demande comprend du graphite et un revêtement, le revêtement comprenant un premier revêtement et un second revêtement, le premier revêtement recouvrant au moins une partie de la surface du graphite, et le second revêtement recouvrant au moins une partie de la surface du premier revêtement, le premier revêtement comprenant un matériau de silicium et du carbone poreux, et le second revêtement comprenant un matériau MXène. Lorsqu'il est utilisé comme matériau d'électrode négative d'une batterie au lithium-ion, le présent matériau actif d'électrode négative peut augmenter l'efficacité faradique du premier cycle et réduire la perte de capacité pendant le cyclage provoquée par la polarisation.
Priority Applications (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
CN202180004954.8A CN115836408A (zh) | 2021-03-31 | 2021-03-31 | 负极活性材料、电化学装置和电子装置 |
PCT/CN2021/084631 WO2022205154A1 (fr) | 2021-03-31 | 2021-03-31 | Matériau actif d'électrode négative, appareil électrochimique et appareil électronique |
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
PCT/CN2021/084631 WO2022205154A1 (fr) | 2021-03-31 | 2021-03-31 | Matériau actif d'électrode négative, appareil électrochimique et appareil électronique |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2022205154A1 true WO2022205154A1 (fr) | 2022-10-06 |
Family
ID=83457694
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/CN2021/084631 WO2022205154A1 (fr) | 2021-03-31 | 2021-03-31 | Matériau actif d'électrode négative, appareil électrochimique et appareil électronique |
Country Status (2)
Country | Link |
---|---|
CN (1) | CN115836408A (fr) |
WO (1) | WO2022205154A1 (fr) |
Cited By (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2024082290A1 (fr) * | 2022-10-21 | 2024-04-25 | 宁德时代新能源科技股份有限公司 | Carbure de titane et son utilisation, procédé de préparation, batterie secondaire et dispositif électrique |
EP4365979A1 (fr) * | 2022-11-07 | 2024-05-08 | Hon Hai Precision Industry Co., Ltd. | Matériau composite silicium-carbone, son procédé de préparation et procédé de préparation de suspension épaisse d'électrode négative composite silicium-carbone |
Citations (6)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN1790779A (zh) * | 2004-12-18 | 2006-06-21 | 三星Sdi株式会社 | 阳极活性物质及其制备方法以及包含它的阳极和锂电池 |
CN105981206A (zh) * | 2014-02-06 | 2016-09-28 | 瓦克化学股份公司 | 用于锂离子电池的Si/G/C复合物 |
CN108682812A (zh) * | 2018-05-10 | 2018-10-19 | 山东大学 | 一种MXene包覆硅的复合电极材料及其制备方法 |
CN110752364A (zh) * | 2019-10-23 | 2020-02-04 | 广东海洋大学 | 复合材料及其制备方法、应用、电极、锂离子电池 |
WO2020144289A1 (fr) * | 2019-01-09 | 2020-07-16 | The Provost, Fellows, Scholars And Other Members Of Board Of Trinity College Dublin | Électrodes haute capacité activées par des matériaux 2d dans une encre aqueuse visqueuse |
CN112038641A (zh) * | 2020-09-09 | 2020-12-04 | 宁波富理电池材料科技有限公司 | 一种MXene硅碳复合材料、其制备方法、负极和锂离子电池 |
-
2021
- 2021-03-31 CN CN202180004954.8A patent/CN115836408A/zh active Pending
- 2021-03-31 WO PCT/CN2021/084631 patent/WO2022205154A1/fr active Application Filing
Patent Citations (6)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN1790779A (zh) * | 2004-12-18 | 2006-06-21 | 三星Sdi株式会社 | 阳极活性物质及其制备方法以及包含它的阳极和锂电池 |
CN105981206A (zh) * | 2014-02-06 | 2016-09-28 | 瓦克化学股份公司 | 用于锂离子电池的Si/G/C复合物 |
CN108682812A (zh) * | 2018-05-10 | 2018-10-19 | 山东大学 | 一种MXene包覆硅的复合电极材料及其制备方法 |
WO2020144289A1 (fr) * | 2019-01-09 | 2020-07-16 | The Provost, Fellows, Scholars And Other Members Of Board Of Trinity College Dublin | Électrodes haute capacité activées par des matériaux 2d dans une encre aqueuse visqueuse |
CN110752364A (zh) * | 2019-10-23 | 2020-02-04 | 广东海洋大学 | 复合材料及其制备方法、应用、电极、锂离子电池 |
CN112038641A (zh) * | 2020-09-09 | 2020-12-04 | 宁波富理电池材料科技有限公司 | 一种MXene硅碳复合材料、其制备方法、负极和锂离子电池 |
Cited By (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2024082290A1 (fr) * | 2022-10-21 | 2024-04-25 | 宁德时代新能源科技股份有限公司 | Carbure de titane et son utilisation, procédé de préparation, batterie secondaire et dispositif électrique |
EP4365979A1 (fr) * | 2022-11-07 | 2024-05-08 | Hon Hai Precision Industry Co., Ltd. | Matériau composite silicium-carbone, son procédé de préparation et procédé de préparation de suspension épaisse d'électrode négative composite silicium-carbone |
Also Published As
Publication number | Publication date |
---|---|
CN115836408A (zh) | 2023-03-21 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
WO2022267534A1 (fr) | Plaque d'électrode négative en métal lithium, appareil électrochimique et dispositif électronique | |
CN114975980A (zh) | 负极材料及使用其的电化学装置和电子装置 | |
CN113451546B (zh) | 钠金属电池、电化学装置 | |
CN114530604A (zh) | 负极材料及包含其的电化学装置和电子装置 | |
WO2022205658A1 (fr) | Matériau d'électrode négative et appareil électrochimique le contenant, et dispositif électronique | |
CN113161532B (zh) | 负极活性材料及包含该负极活性材料的负极、二次电池和电子设备 | |
WO2022142241A1 (fr) | Matériau actif d'électrode négative, dispositif électrochimique et dispositif électronique | |
WO2021249400A1 (fr) | Matériau actif d'électrode positive et dispositif électrochimique comprenant ce dernier | |
WO2021217617A1 (fr) | Matériau actif d'électrode négative, son procédé de fabrication, batterie secondaire et dispositif comprenant une batterie secondaire | |
WO2021120434A1 (fr) | Solution électrolytique et dispositif électrochimique | |
WO2022206151A1 (fr) | Plaque d'électrode négative et dispositif électrochimique la comprenant, et dispositif électronique | |
WO2022206175A1 (fr) | Électrode négative, dispositif électrochimique la comprenant et dispositif électronique | |
WO2022193286A1 (fr) | Matériau d'électrode négative et son procédé de préparation, dispositif électrochimique et dispositif électronique | |
WO2022205154A1 (fr) | Matériau actif d'électrode négative, appareil électrochimique et appareil électronique | |
CN117317137A (zh) | 电化学装置和电子装置 | |
WO2024007142A1 (fr) | Plaque d'électrode négative, batterie secondaire, module de batterie, bloc-batterie et dispositif électrique | |
WO2021189455A1 (fr) | Dispositif électrochimique et dispositif électronique le comprenant | |
WO2023273652A1 (fr) | Diaphragme, batterie au lithium-ion, module de batterie, bloc-batterie et dispositif d'alimentation | |
WO2024001483A1 (fr) | Feuille d'électrode négative, appareil électrochimique et dispositif électronique | |
WO2023070992A1 (fr) | Dispositif électrochimique et dispositif électronique comprenant celui-ci | |
CN111146433A (zh) | 负极及包含其的电化学装置和电子装置 | |
WO2022204974A1 (fr) | Dispositif électrochimique et dispositif électronique | |
WO2021189338A1 (fr) | Matériau d'électrode négative, plaque d'électrode négative, dispositif électrochimique et dispositif électronique | |
US20230216026A1 (en) | Positive electrode material, and electrochemical apparatus and electronic apparatus containing same | |
WO2021088167A1 (fr) | Électrode positive ainsi que dispositif électronique et dispositif électrochimique comprenant une électrode positive |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 21933819 Country of ref document: EP Kind code of ref document: A1 |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
122 | Ep: pct application non-entry in european phase |
Ref document number: 21933819 Country of ref document: EP Kind code of ref document: A1 |