WO2022172585A1 - Matériau actif d'électrode négative, procédé de fabrication de matériau actif d'électrode négative, et batterie secondaire à électrolyte non aqueux - Google Patents
Matériau actif d'électrode négative, procédé de fabrication de matériau actif d'électrode négative, et batterie secondaire à électrolyte non aqueux Download PDFInfo
- Publication number
- WO2022172585A1 WO2022172585A1 PCT/JP2021/046423 JP2021046423W WO2022172585A1 WO 2022172585 A1 WO2022172585 A1 WO 2022172585A1 JP 2021046423 W JP2021046423 W JP 2021046423W WO 2022172585 A1 WO2022172585 A1 WO 2022172585A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- negative electrode
- active material
- electrode active
- group
- silicon
- Prior art date
Abstract
La présente invention vise à fournir: un matériau actif d'électrode négative ayant d'excellentes caractéristiques de charge et de décharge (capacité de charge et de décharge, rendement coulombique initial et caractéristiques de cycle); et une batterie secondaire à électrolyte non aqueux l'utilisant. À cet effet, l'invention concerne un matériau actif d'électrode négative comprenant: du carbure d'oxycarbure de silicium; et des particules composites dans lesquelles des nanoparticules de silicium sont dispersées dans une matrice comprenant une phase carbonée, les particules composites satisfaisant l'expression 1 dans une valeur de déplacement chimique obtenue à partir d'un spectre29Si-NMR Expression 1: 0,7 ≤ A/B ≤ 3,0 A: L'intensité de surface d'un pic dans la plage de -70 ppm à -90 ppm appartenant à Si (à valence zéro) B: L'intensité de surface d'un pic dans la plage de -90 ppm à -130 ppm dérivée d'une liaison SiO4.
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2022514554A JP7088438B1 (ja) | 2021-02-09 | 2021-12-16 | 負極活物質、負極活物質の製造方法及び非水電解質二次電池 |
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2021018891 | 2021-02-09 | ||
JP2021-018891 | 2021-02-09 |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2022172585A1 true WO2022172585A1 (fr) | 2022-08-18 |
Family
ID=82838665
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/JP2021/046423 WO2022172585A1 (fr) | 2021-02-09 | 2021-12-16 | Matériau actif d'électrode négative, procédé de fabrication de matériau actif d'électrode négative, et batterie secondaire à électrolyte non aqueux |
Country Status (1)
Country | Link |
---|---|
WO (1) | WO2022172585A1 (fr) |
Cited By (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2024048288A1 (fr) * | 2022-09-01 | 2024-03-07 | Dic株式会社 | Précurseur de matériau actif d'électrode négative, matériau actif d'électrode négative, batterie secondaire et procédé de production de matériau actif d'électrode négative |
Citations (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2019107336A1 (fr) * | 2017-12-01 | 2019-06-06 | Dic株式会社 | Substance active pour électrode négative et son procédé de production |
WO2020129467A1 (fr) * | 2018-12-19 | 2020-06-25 | Dic株式会社 | Nanoparticules de silicium, matériau actif d'électrode négative de pile rechargeable non aqueuse, comprenant lesdites nanoparticules de silicium, et pile rechargeable |
WO2020262647A1 (fr) * | 2019-06-26 | 2020-12-30 | 株式会社村田製作所 | Matériau actif d'électrode négative, électrode négative et batterie secondaire |
WO2021225092A1 (fr) * | 2020-05-07 | 2021-11-11 | Dic株式会社 | Matériau composite d'oxycarbure de silicium poreux, et procédé de fabrication de celui-ci |
-
2021
- 2021-12-16 WO PCT/JP2021/046423 patent/WO2022172585A1/fr active Application Filing
Patent Citations (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2019107336A1 (fr) * | 2017-12-01 | 2019-06-06 | Dic株式会社 | Substance active pour électrode négative et son procédé de production |
WO2020129467A1 (fr) * | 2018-12-19 | 2020-06-25 | Dic株式会社 | Nanoparticules de silicium, matériau actif d'électrode négative de pile rechargeable non aqueuse, comprenant lesdites nanoparticules de silicium, et pile rechargeable |
WO2020262647A1 (fr) * | 2019-06-26 | 2020-12-30 | 株式会社村田製作所 | Matériau actif d'électrode négative, électrode négative et batterie secondaire |
WO2021225092A1 (fr) * | 2020-05-07 | 2021-11-11 | Dic株式会社 | Matériau composite d'oxycarbure de silicium poreux, et procédé de fabrication de celui-ci |
Cited By (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2024048288A1 (fr) * | 2022-09-01 | 2024-03-07 | Dic株式会社 | Précurseur de matériau actif d'électrode négative, matériau actif d'électrode négative, batterie secondaire et procédé de production de matériau actif d'électrode négative |
JP7473098B1 (ja) | 2022-09-01 | 2024-04-23 | Dic株式会社 | 負極活物質前駆体、負極活物質、二次電池および負極活物質の製造方法 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
JP6939979B2 (ja) | シリコンナノ粒子及びそれを用いた非水二次電池負極用活物質並びに二次電池 | |
JP7288198B2 (ja) | 負極活物質及びその製造方法 | |
WO2021157459A1 (fr) | Matériau actif d'électrode négative de batterie secondaire, électrode négative et batterie secondaire | |
KR20230030569A (ko) | 전지용 활물질, 전지용 복합 활물질, 및 이차 전지 | |
WO2022172585A1 (fr) | Matériau actif d'électrode négative, procédé de fabrication de matériau actif d'électrode négative, et batterie secondaire à électrolyte non aqueux | |
WO2023017587A1 (fr) | Matériau pour batteries secondaires, matériau actif d'électrode négative et batterie secondaire | |
US20220384807A1 (en) | Low oxygen-type silicon nanoparticle-containing slurry, negative electrode active material, negative electrode and lithium-ion secondary battery | |
JP7088438B1 (ja) | 負極活物質、負極活物質の製造方法及び非水電解質二次電池 | |
JP7453631B2 (ja) | ケイ素系材料、ケイ素系材料を含む複合材料、二次電池用負極物質および二次電池 | |
JP7074273B1 (ja) | 負極活物質及び非水電解質二次電池 | |
JP7491482B2 (ja) | 二次電池用活物質、二次電池用活物質の製造方法および二次電池 | |
JP7323089B1 (ja) | 負極活物質、二次電池および負極活物質の製造方法 | |
JP7485230B2 (ja) | ナノシリコン、ナノシリコンスラリー、ナノシリコンの製造方法、二次電池用活物質および二次電池 | |
JP7491478B2 (ja) | 二次電池用活物質および二次電池 | |
WO2022124172A1 (fr) | Matériau actif d'électrode négative et batterie secondaire à électrolyte non aqueux | |
JP7435916B1 (ja) | 負極活物質の製造方法、負極活物質および二次電池 | |
WO2023157643A1 (fr) | Matière active pour batterie secondaire, procédé de fabrication de matière active pour batterie secondaire, et batterie secondaire | |
WO2023157642A1 (fr) | Matière active pour batterie secondaire, et batterie secondaire | |
WO2023074099A1 (fr) | Matériau actif composite pour batterie secondaire et batterie secondaire | |
WO2024048288A1 (fr) | Précurseur de matériau actif d'électrode négative, matériau actif d'électrode négative, batterie secondaire et procédé de production de matériau actif d'électrode négative |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
ENP | Entry into the national phase |
Ref document number: 2022514554 Country of ref document: JP Kind code of ref document: A |
|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 21925828 Country of ref document: EP Kind code of ref document: A1 |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
122 | Ep: pct application non-entry in european phase |
Ref document number: 21925828 Country of ref document: EP Kind code of ref document: A1 |