WO2022145032A1 - プロトン伝導型二次電池用電解液およびこれを備えるプロトン伝導型二次電池 - Google Patents

プロトン伝導型二次電池用電解液およびこれを備えるプロトン伝導型二次電池 Download PDF

Info

Publication number
WO2022145032A1
WO2022145032A1 PCT/JP2020/049283 JP2020049283W WO2022145032A1 WO 2022145032 A1 WO2022145032 A1 WO 2022145032A1 JP 2020049283 W JP2020049283 W JP 2020049283W WO 2022145032 A1 WO2022145032 A1 WO 2022145032A1
Authority
WO
WIPO (PCT)
Prior art keywords
conduction type
type secondary
proton conduction
secondary battery
electrolytic solution
Prior art date
Application number
PCT/JP2020/049283
Other languages
English (en)
French (fr)
Inventor
クーシャン ヤン
耕輔 中山
千明 松田
Original Assignee
カワサキモータース株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by カワサキモータース株式会社 filed Critical カワサキモータース株式会社
Priority to PCT/JP2020/049283 priority Critical patent/WO2022145032A1/ja
Publication of WO2022145032A1 publication Critical patent/WO2022145032A1/ja

Abstract

プロトン伝導型二次電池の電解液として、イオン液体と、前記イオン液体にｐＨ緩衝剤として添加された塩とを備え、前記塩の水溶液中における酸解離定数が３．０よりも低い化合物を用いる。前記イオン液体は、例えば非プロトン性液体と、前記非プロトン性液体に添加された酸とを含み、前記塩は、例えば有機塩である。

Description

プロトン伝導型二次電池用電解液およびこれを備えるプロトン伝導型二次電池
　本発明は、プロトン伝導型二次電池用電解液およびこれを備えるプロトン伝導型二次電池に関する。
　リチウムといった電気化学当量の小さいアルカリ金属は、電池の構成材料として特に有用である。リチウムを使用することにより、従前から使用されていたニッケルやカドミウムよりも重量当たりのエネルギーを大きくすることができる。しかし、充電式リチウム金属電池の開発においては、有効な充放電サイクルが重要な開発課題とされている。充電と放電を繰り返すと、リチウム金属電極の表面にリチウムの「デンドライト」が徐々に生成され、これらは最終的に正極に接触する程度まで成長し、電池の内部短絡を引き起こし、比較的少ないサイクル後に電池が使用できなくなる可能性がある。他方で、理論上の比容量が非常に高い（4000 mAh / g）ため、リチウムイオン電池の負極材料として一般的に使用されているシリコンは、リチウムと共にサイクルさせると４００％もの著しい体積格子膨張を引き起こす。この体積膨張により、サイクル寿命がさらに短縮され、多くのシステムで材料を効果的に使用できなくなる。
　そこで、二次電池の代替技術として、極めて低分子量である水素原子を循環させることが有望である。水酸化ニッケルなど金属水素化物合金の一部の材料は、水素を吸蔵および放出できることが知られている。適切な負極材料と組み合わせることにより、これらの水素貯蔵材料を燃料電池や金属水素化物電池に使用することができる（例えば、特許文献１参照。）。
米国特許第５５３６５９１号明細書
　もっとも、従前、上記の金属水酸化物電池の正極活物質として一般的に使用されているのは、ニッケルを主成分とする遷移金属の混合物の水酸化物であるが、このような正極活物質を用いた場合、得られる電池の充放電容量は十分とはいえない。
　本発明の目的は、上記の課題を解決するために、プロトン伝導型二次電池の充放電容量特性を改善することができる電解液を提供することにある。
　前記した目的を達成するために、本発明に係るプロトン伝導型二次電池用電解液は、プロトン伝導型二次電池に用いられる電解液であって、イオン液体と、前記イオン液体にｐＨ緩衝剤として添加された塩とを備え、前記塩の水溶液中における酸解離定数が３．０よりも低い。
　この構成によれば、当該電解液を用いたプロトン伝導型二次電池の放電容量および充放電サイクル特性が飛躍的に向上する。
　本発明の一実施形態に係る電解液において、前記塩は有機塩であってもよい。具体的には、前記塩は、例えば、Ｋ２Ｃ２Ｏ４であってもよい。
　本発明の一実施形態に係る電解液において、前記イオン液体が、非プロトン性液体と、前記非プロトン性液体に添加された酸とを含むものであってよい。具体的には、前記イオン液体は、例えば、１－エチル－３－メチルイミダゾリウムアセテートを含んでいてよい。
　本発明に係るプロトン伝導型二次電池は、水素の吸蔵および放出が可能な正極活物質を含む正極と、水素の吸蔵および放出が可能な負極活物質を含む負極と、前記電解液と、を備える伝導型二次電池。
　この構成によれば、プロトン伝導型二次電池の放電容量および充放電サイクル特性が飛躍的に向上する。
　本発明の一実施形態に係るプロトン伝導型二次電池において、前記正極活物質が、ニッケル水酸化物またはニッケルと他の遷移金属を含むニッケル含有複合水酸化物であってよい。具体的には、前記正極活物質は、例えば、
Ｎｉ（１－ｘ－ｙ）ＣｏｘＺｎｙ（ＯＨ）２
（ただし、０≦ｘ≦０．１，０≦ｙ≦０．１）
で表される化合物であってよい。
　本発明の一実施形態に係るプロトン伝導型二次電池において、前記負極活物質は、例えば、超格子水素吸蔵合金であってよい。
　請求の範囲および／または明細書および／または図面に開示された少なくとも２つの構成のどのような組合せも、本発明に含まれる。特に、請求の範囲の各請求項の２つ以上のどのような組合せも、本発明に含まれる。
　この発明は、添付の図面を参考にした以下の好適な実施形態の説明から、より明瞭に理解されるであろう。しかしながら、実施形態および図面は単なる図示および説明のためのものであり、この発明の範囲を定めるために利用されるべきものではない。この発明の範囲は添付の請求の範囲によって定まる。添付図面において、複数の図面における同一の符号は、同一または相当する部分を示す。
本発明の一実施例に係る電解液の特性を試験するための試験用セルを模式的に示す断面図である。 本発明の一実施例に係る電解液と比較例に係る電解液についての充放電サイクル試験結果を示すグラフである。
　以下、本発明に係る実施形態を図面に従って説明するが、本発明はこの実施形態に限定されるものではない。
　本実施形態に係るプロトン伝導型二次電池に用いられる電解液（以下、単に「電解液」と呼ぶ。）は、イオン液体と、前記イオン液体にｐＨ緩衝剤として添加された特定の塩とを備える。この電解液の水溶液中における酸解離定数は、３．０よりも低い。後に詳述するように、このような電解液をプロトン伝導型二次電池に用いることにより、プロトン伝導型二次電池の放電容量を大幅に増大させることができるとともに、充放電を繰り返したのちも安定的に放電容量を維持できることが見出された。
　電解液に含まれる前記イオン液体は、例えば、非プロトン性液体と、前記非プロトン性液体に添加されたプロトン源としての１種類または２種類以上の酸とを含むものであってよい。非プロトン性液体は、電解液中の組成物として適した化合物であって、電池内の他の化合物と有害な反応を起こし得ない化合物であれば、いかなる化合物であってもよい。非プロトン性液体を構成する化合物の例としては、アンモニウムまたはホスホニウム化合物が含まれ、任意選択で、アンモニウムまたはホスホニウムが、窒素またはリンに結合した１つまたは複数の直鎖、分岐または環状置換または非置換アルキル基を含む。
　非プロトン性化合物は、例えば、１または２以上の直鎖状、正の荷電を有する窒素またはリン原子に結合した直鎖状、分岐状または環状の、置換もしくは非置換のアルキルを含むアンモニウムまたはホスホニウム化合物であってよい。窒素またはリンは、中心環から延びる１つ以上のペンダント基を有し得る５または６員環構造の構成元素であってよい。具体的な例として、アンモニウムイオンはイミダゾリウムイオンであってよく、ホスホニウムイオンはピロリジニウムイオンであってよい。
　アンモニウムまたはホスホニウムは、１～６個の炭素原子を有する１個または２個の直鎖状または環状、置換または非置換のアルキルを含む。任意選択で、アルキルは、２～６個の炭素を含む。アルキルの置換元素は、例えば、窒素、酸素、または硫黄であってよい。
　電解液として使用するための非プロトン性化合物の具体例には、１-ブチル-３-メチルイミダゾリウム（ＢＭＩＭ）、１－エチル－３－メチルイミダゾリウム（ＥＭＩＭ），１，３－ジメチルイミダゾリウム，１，２，３－トリメチルイミダゾリウム，トリス（ヒドロキシエチル）メチルアンモニウム、１，２，４－トリメチルピラゾリウム、またはこれらの組合せが含まれるが、これらに限定されない。
　非プロトン性化合物は、必要に応じて非プロトン性化合物と組み合わせて一つ以上の陰イオンを含む。陰イオンの例には、メチド、硝酸塩、カルボキシレート、イミド、ハロゲン化物、ホウ酸塩、リン酸塩、ホスフィン酸塩、ホスホネート、スルホン酸塩、硫酸塩、炭酸塩およびアルミン酸塩が含まれるが、これらに限定されない。さらに具体的な例として、陰イオンは、酢酸塩などのカルボン酸塩、水素、アルキル、またはフルオロリン酸塩などのリン酸塩、ホスフィン酸アルキルなどのホスフィネートを含む。このような非プロトン性化合物の例には、１－ブチル－３－メチルイミダゾリウム（ＢＭＩＭ）、１－エチル－３－メチルイミダゾリウム（ＥＭＩＭ）、１，３－ジメチルイムジアゾリウム、１，２，３－トリメチルイミダゾリウム、トリス（ヒドロキシエチル）メチルアンモニウム、１，２，４－トリメチルピラゾリウム、またはこれらの組み合わせの酢酸塩、スルホン酸塩、またはホウ酸塩が含まれるが、これらに限定されない。このような化合物の具体的な例として、トリフルオロメタンスルホン酸ジエチルメチルアンモニウム（ＤＥＭＡ／ＴｆＯ）、１－エチル－３－メチルイミダゾリウムアセテート（ＥＭＩＭ／ＡＣ）、または１－ブチル-3-メチルイミダゾリウムビス（トリフルオロメチルスルホニル）イミド（ＢＭＩＭ／ＴＦＳＩ）が挙げられる。
　電解液のイオン液体にｐＨ緩衝剤として添加される塩は、有機塩または無機塩であってよい。有機塩の例には、カリウムまたはナトリウムクエン酸、カリウムまたはナトリウムシュウ酸塩が含まれ、無機塩の例には、カリウムまたはナトリウムのリン酸塩、炭酸塩、または硫酸塩が含まれるが、これらに限定されない。また、これら塩添加剤の水溶液中での酸解離定数（ｐＫａ）は、１～１４の範囲であってよい。塩の前記ｐＫａの値は、７より低くてもよく、さらに３より低くてもよく、さらに１．５より低いものであってよい。
　本実施形態に係るプロトン伝導型二次電池は、水素の吸蔵および放出が可能な正極活物質を含む正極と、水素の吸蔵および放出が可能な負極活物質を含む負極と、上記で例示した化合物からなる電解液とを備える。
　本明細書における「プロトン伝導型二次電池」は、従来の金属水素化物を用いた電池とは、水系電解液を用いない等多くの点で異なる。この新型のプロトン伝導型二次電池は、従来の電池と同様、負極と正極の間で水素を循環させることによって動作する。これにより、負極においては、充電中に１つまたは複数の元素の水素化物が形成される。この水素化物は可逆的な生成物であり、放電中に、負極の活物質の一部としてプロトンと電子の両方を生成する。
　なお、本明細書において「負極」とは、充電時において、電気化学的に電子を受け取る物質を含む側の極を指し、「正極」とは、充電時において、電気化学的に電子を放出する物質を含む側の極を指す。
　プロトン伝導型二次電池の負極で生じる反応は、以下の半反応式で表される。
Figure JPOXMLDOC01-appb-C000001
 　この式における負極活物質であるＭについては後述する。
　上記反応に対応する正極で生じる反応は、以下の半反応式で表される。
Figure JPOXMLDOC01-appb-C000002
 　この式におけるＭＣは正極活物質ＭＣ（ＯＨ）２中の金属元素である。
　前記正極活物質は、例えば、遷移金属の水酸化物である。具体的には、前記正極活物質は、例えば、ニッケル水酸化物またはニッケルと他の遷移金属を含むニッケル含有複合水酸化物であってよい。より具体的には、正極活物質は、例えば、Ｎｉ（１－ｘ－ｙ）ＣｏｘＺｎｙ（ＯＨ）２（ただし、０≦ｘ≦０．１，０≦ｙ≦０．１）で表される化合物であってよい。
　前記負極活物質は、例えば、充電時に電解液中で電気化学的に発生させた水素を吸蔵でき、かつ放電時にその吸蔵水素を容易に放出できる水素吸蔵合金である。このような水素吸蔵合金は、ＡＢｘ型として表される構造を有するものであってよい。ここで、Ａは水素化物形成元素であり、Ｂは非水素化物形成元素であり、ｘは１～５の実数である。水素化物形成元素（Ａ）は、例えばランタン、セリウム、プラセオジム、ネオジム、プロメチウム、サマリウム、イットリウム、チタン、ジルコニウムまたはこれらの組み合わせ、またはミッシュメタルなどの他の金属を含むが、これらに限定されない。非水素化物形成元素は、例えば、アルミニウム、ニッケル、コバルト、銅、マンガン、又はそれらの組み合わせである金属を含むが、これらに限定されない。水素吸蔵合金のさらに具体的な例として、ＬａＮｉ５やＭｍＮｉ５（Ｍｍはミッシュメタル）等のＡＢ５型系、希土類－マグネシウム－ニッケル系等のＡＢ３型系、超格子構造をなす希土類－マグネシウム－ニッケル系等のＡ２Ｂ７型系、（Ｚｒ，Ｔｉ）Ｎｉ２等のＡＢ2型系のものが挙げられるが、これらに限定されない。負極活物質の他の例として、第１４族元素、または複数の第１４族元素からなる化合物または合金、具体的には、例えば、炭素、ケイ素、炭化ケイ素（ＣｘＳｉ１－ｘ）、シリコンゲルマニウム合金（ＳｉｘＧｅ１－ｘ）が挙げられる。
　負極活物質および正極活物質の一方または両方は、粉末または粒状の形態であってよい。粒子同士は、バインダによって保持されて、負極または正極の形成において集電体上に層状に形成され得る。バインダとしては、負極、正極、またはその両方の形成に使用するのに適し、かつプロトン伝導に適したものであれば、当技術分野において知られている任意のバインダを使用することができる。
　負極の形成に用いられるバインダの例には、ポリマーバインダ材料が含まれるが、これに限定されない。バインダの素材の具体例としては、エラストマー材料が挙げられ、より具体的には、例えば、スチレン－ブタジエン（ＳＢ）、スチレン－ブタジエン-スチレンブロック共重合体（ＳＢＳ）、スチレン－イソプレン－スチレンブロック共重合体（SIS）およびスチレン－エチレン－ブタジエン－スチレンブロック共重合体（ＳＥＢＳ）等が挙げられる。バインダのより具体的な例としては、ポリテトラフルオロエチレン（ＰＴＦＥ）、ポリビニルアルコール（ＰＶＡ）、テフロン（登録商標）化アセチレンブラック（ＴＡＢ－２）、スチレン－ブタジエンバインダ材料、またはカルボキシメチルセルロース（ＣＭＣ）が含まれるが、これらに限定されない。
　正極および負極の一方または両方は、さらに、活物質に含まれる１種類または複数種類の添加剤を含んでいてもよい。添加剤は、例えば導電性材料である。この導電性材料は、好適には導電性炭素である。導電性炭素の例としては、グラファイト、あるいは黒鉛化コークスなどの黒鉛状炭素が挙げられる。導電性炭素のさらに他の例には、アモルファスまたは非晶質である非黒鉛化炭素、例えば石油コークスやカーボンブラックが含まれる。導電性材料は、正極または負極に、例えば、０．１重量％から２０重量％の範囲で含まれる。
　負極および正極は、当該技術分野において公知の任意の方法によって形成することができる。例えば、負極の活物質または正極の活物質を、適切な溶媒中でバインダ、および任意選択で導電性の材料と混合してスラリーを形成し、スラリーを集電体上にコーティングし、乾燥させて溶媒の一部または全部を蒸発させることによって、集電体の表面に活物質の層を形成することができる。
　集電体は、メッシュ状、箔状、または他の適当な形態であってよい。例えば、集電体は、アルミニウム合金などのアルミニウム系金属、ニッケルまたはニッケル合金、ステンレス鋼などの鋼、銅または銅合金等の材料で形成することができる。集電体は、例えばシート状であってよく、さらには、箔、固体基板、多孔質基板、グリッド、発泡体、または当技術分野において公知の形態であり得る。集電体は、任意の適切な電子伝導性かつ選択的に不透過性または実質的に不透過性の材料であってよく、その例として銅、ステンレス鋼、チタン、または炭素紙／フィルム、非穿孔金属箔、アルミ箔、ニッケルおよびアルミニウムを含むクラッド材、銅およびアルミニウムを含むクラッド材、ニッケルめっき鋼、ニッケルめっき銅、ニッケルめっきアルミニウム、金、銀、またはこれらの任意の適切な組み合わせであってよい。
　プロトン伝導型二次電池は、負極と正極との間に介在するセパレータを備えていてよい。セパレータとしては、負極と正極との間のイオン移動を許容可能にまたは許容できないほど制限しないように、水素イオンに対して透過性のものを用いることができる。セパレータとしては、例えば、ナイロン、ポリエステル、ポリ塩化ビニル、ガラス繊維、綿などの材料を用いることができるが、これらに限定されない。より具体的な例として、セパレータは、ポリエチレンまたはポリプロピレンであってよい。
　負極、正極、セパレータ、及び電解液として使用されるイオン性液体は、外装体に収容される。外装体は、例えば、金属またはポリマー製の缶、またはアルミニウム被覆ポリプロピレンフィルムなどのヒートシール可能なアルミホイルなどのラミネートフィルムであってよい。このように、本明細書において提供される電気化学電池は、任意の公知の形態、例えばボタン電池，パウチ電池，円筒型電池、角型電池等であってよい。
　集電体および／または基板は、集電体から電池の外部への電子の移動を可能にし、集電体を回路などの装置に接続するための１つ以上のタブを備えていていよい。タブは、任意の適切な導電性材料（例えば、ニッケル、アルミニウム、または他の金属）で形成することができ、集電体に、例えば溶接することによって接続される。
　以下の実施例により、本発明をさらに具体的に説明するが、本発明はこれらに限定されるものではない。
（試験電池の作製）
　正極活物質として、共沈法により作製したＮｉ０．８７Ｃｏ０．０８Ｚｎ０．０５（ＯＨ）２を２重量％のオキシ水酸化コバルト（ＣｏＯＯＨ）でコーティングした粒子の粉末を用いた。この粉末を１：３の重量比で乾燥状態のＴＡＢ－２バインダと混合したうえで、集電体であるニッケルメッシュ基板にプレス成形することにより正極を作製した。
　負極活物質として、市販の超格子水素吸蔵合金（Ａ２Ｂ７型）を標準的な方法で作製したものを使用した。
　電解液は、３．３３ｍの酢酸を含有するＥＭＩＭ／ＡＣ（純度＞９５重量％）をベースの溶媒とし、これに塩として有機塩であるシュウ酸カリウム（Ｋ２Ｃ２Ｏ４）０．１ｍを添加したものを実施例の電解液とした。これとは別に、３．３３ｍの酢酸を含有するＥＭＩＭ／ＡＣに添加材を加えなかった電解液、他の塩（無機塩）またはＨ２Ｏを添加した電解液を作製して比較例とした。実施例および各比較例における電解液の添加剤、添加剤の水溶液中の酸解離定数ｐＫａ，および濃度を表１に示す。
 
Figure JPOXMLDOC01-appb-T000003
  
　上記の実施例および各比較例に係る電解液について、電気化学的特性の比較試験を行うために、テフロンのスウェージロック製ティー内に試験用の電気化学セルを作製した。この充放電試験に使用した試験用セルＴの構造を図１に示す。この試験用セルＴは、中央グランド１を備え、中央グランド１は、その両端がカラー３によって固定されたフェルール２で覆われている。試験サンプル４は、中央グランド１内に挿入された、Ｎｉメッキ鋼（ＮＳ）から形成された２つの集電ロッド５の間に挟まれている。試験セルＴの上部チャネルは、圧力ベント装置であるパラフィルム６によって覆われている。試験サンプル４は、上記の負極および正極を、標準的なセパレータを介して積層させて形成した。この試験セルＴ内に、上記の各電解液を充填した。
（試験結果）
　このようにして作製した試験用セルについて、充電条件として充電レート７００ｍＡ／ｇ（正極活物質重量基準）、充電時間２０時間、および放電条件として放電レート７０ｍＡ／ｇ（正極活物質重量基準），放電終止電圧０Ｖの充放電条件にて充放電サイクル試験を行った。その結果を図２に示す。
　図２から明らかなように、塩としてシュウ酸カリウム（Ｋ２Ｃ２Ｏ４）０．１ｍを添加した実施例が、ｋＰａ値として唯一０．３よりも低い１．２５を示すと共に、１サイクル目の放電容量及び１３サイクル目の放電容量のいずれにおいても他の電解液を用いた比較例に比較して大幅に改善された放電容量を示した。具体的には、１３サイクル目の放電容量で比較すると、実施例電解液を用いたセルは、無添加の電解液を用いた比較例１に対して約９５％，無機塩を添加した比較例電解液の中で最も優れた特性を示した比較例２に対して約６２％，水を添加した比較例６に対して５７％、その他の比較例電解液に対しては約７～９倍も改善された特性を示した。
　このように、実施例に係る電解液をプロトン伝導型二次電池の電解液として用いることにより、プロトン伝導型二次電池の放電容量および充放電サイクル特性を著しく向上させることができる。
　以上のとおり、図面を参照しながら本発明の好適な実施形態を説明したが、本発明の趣旨を逸脱しない範囲内で、種々の追加、変更または削除が可能である。したがって、そのようなものも本発明の範囲内に含まれる。

Claims (9)

  1. 　プロトン伝導型二次電池に用いられる電解液であって、
    　イオン液体と、
    　前記イオン液体にｐＨ緩衝剤として添加された塩と、
    を備え、
    　前記塩の水溶液中における酸解離定数が３．０よりも低い、
    プロトン伝導型二次電池用電解液。
  2. 　請求項１に記載の電解液において、前記塩が有機塩である、プロトン伝導型二次電池用電解液。
  3. 　請求項２に記載の電解液において、前記塩が、Ｋ２Ｃ２Ｏ４である、プロトン伝導型二次電池用電解液。
  4. 　請求項１から３のいずれか一項に記載の電解液において、
    　前記イオン液体が、非プロトン性液体と、前記非プロトン性液体に添加された酸とを含む、
    プロトン伝導型二次電池用電解液。
  5. 　請求項１から４のいずれか一項に記載の電解液において、
    　前記イオン液体が、１－エチル－３－メチルイミダゾリウムアセテートを含む、
    プロトン伝導型二次電池用電解液。
  6. 　水素の吸蔵および放出が可能な正極活物質を含む正極と、
    　水素の吸蔵および放出が可能な負極活物質を含む負極と、
    　請求項１から５のいずれか一項に記載の電解液と、
    を備えるプロトン伝導型二次電池。
  7. 　請求項６に記載のプロトン伝導型二次電池において、
    　前記正極活物質が、ニッケル水酸化物またはニッケルと他の遷移金属を含むニッケル含有複合水酸化物である、
    プロトン伝導型二次電池。
  8. 　請求項７に記載のプロトン伝導型二次電池において、
    　前記正極活物質が、
    　Ｎｉ（１－ｘ－ｙ）ＣｏｘＺｎｙ（ＯＨ）２
    （ただし、０≦ｘ≦０．１，０≦ｙ≦０．１）
    で表される化合物である、
    プロトン伝導型二次電池。
  9. 　請求項７または８に記載のプロトン伝導型二次電池において、
    　前記負極活物質が、超格子水素吸蔵合金である、
    プロトン伝導型二次電池。
PCT/JP2020/049283 2020-12-29 2020-12-29 プロトン伝導型二次電池用電解液およびこれを備えるプロトン伝導型二次電池 WO2022145032A1 (ja)