Classifications

• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J29/00—Catalysts comprising molecular sieves
  • B01J29/04—Catalysts comprising molecular sieves having base-exchange properties, e.g. crystalline zeolites
  • B01J29/06—Crystalline aluminosilicate zeolites; Isomorphous compounds thereof
  • B01J29/08—Crystalline aluminosilicate zeolites; Isomorphous compounds thereof of the faujasite type, e.g. type X or Y
  • B01J29/085—Crystalline aluminosilicate zeolites; Isomorphous compounds thereof of the faujasite type, e.g. type X or Y containing rare earth elements, titanium, zirconium, hafnium, zinc, cadmium, mercury, gallium, indium, thallium, tin or lead
  • B01J29/088—Y-type faujasite
• • C—CHEMISTRY; METALLURGY
  • C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
  • C10G—CRACKING HYDROCARBON OILS; PRODUCTION OF LIQUID HYDROCARBON MIXTURES, e.g. BY DESTRUCTIVE HYDROGENATION, OLIGOMERISATION, POLYMERISATION; RECOVERY OF HYDROCARBON OILS FROM OIL-SHALE, OIL-SAND, OR GASES; REFINING MIXTURES MAINLY CONSISTING OF HYDROCARBONS; REFORMING OF NAPHTHA; MINERAL WAXES
  • C10G45/00—Refining of hydrocarbon oils using hydrogen or hydrogen-generating compounds
  • C10G45/58—Refining of hydrocarbon oils using hydrogen or hydrogen-generating compounds to change the structural skeleton of some of the hydrocarbon content without cracking the other hydrocarbons present, e.g. lowering pour point; Selective hydrocracking of normal paraffins
  • C10G45/60—Refining of hydrocarbon oils using hydrogen or hydrogen-generating compounds to change the structural skeleton of some of the hydrocarbon content without cracking the other hydrocarbons present, e.g. lowering pour point; Selective hydrocracking of normal paraffins characterised by the catalyst used
  • C10G45/64—Refining of hydrocarbon oils using hydrogen or hydrogen-generating compounds to change the structural skeleton of some of the hydrocarbon content without cracking the other hydrocarbons present, e.g. lowering pour point; Selective hydrocracking of normal paraffins characterised by the catalyst used containing crystalline alumino-silicates, e.g. molecular sieves
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J21/00—Catalysts comprising the elements, oxides, or hydroxides of magnesium, boron, aluminium, carbon, silicon, titanium, zirconium, or hafnium
  • B01J21/02—Boron or aluminium; Oxides or hydroxides thereof
  • B01J21/04—Alumina
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J21/00—Catalysts comprising the elements, oxides, or hydroxides of magnesium, boron, aluminium, carbon, silicon, titanium, zirconium, or hafnium
  • B01J21/06—Silicon, titanium, zirconium or hafnium; Oxides or hydroxides thereof
  • B01J21/063—Titanium; Oxides or hydroxides thereof
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J21/00—Catalysts comprising the elements, oxides, or hydroxides of magnesium, boron, aluminium, carbon, silicon, titanium, zirconium, or hafnium
  • B01J21/06—Silicon, titanium, zirconium or hafnium; Oxides or hydroxides thereof
  • B01J21/066—Zirconium or hafnium; Oxides or hydroxides thereof
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J23/00—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00
  • B01J23/70—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of the iron group metals or copper
  • B01J23/76—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of the iron group metals or copper combined with metals, oxides or hydroxides provided for in groups B01J23/02 - B01J23/36
  • B01J23/84—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of the iron group metals or copper combined with metals, oxides or hydroxides provided for in groups B01J23/02 - B01J23/36 with arsenic, antimony, bismuth, vanadium, niobium, tantalum, polonium, chromium, molybdenum, tungsten, manganese, technetium or rhenium
  • B01J23/85—Chromium, molybdenum or tungsten
  • B01J23/88—Molybdenum
  • B01J23/883—Molybdenum and nickel
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J29/00—Catalysts comprising molecular sieves
  • B01J29/04—Catalysts comprising molecular sieves having base-exchange properties, e.g. crystalline zeolites
  • B01J29/06—Crystalline aluminosilicate zeolites; Isomorphous compounds thereof
  • B01J29/08—Crystalline aluminosilicate zeolites; Isomorphous compounds thereof of the faujasite type, e.g. type X or Y
  • B01J29/16—Crystalline aluminosilicate zeolites; Isomorphous compounds thereof of the faujasite type, e.g. type X or Y containing arsenic, antimony, bismuth, vanadium, niobium, tantalum, polonium, chromium, molybdenum, tungsten, manganese, technetium or rhenium
  • B01J29/166—Y-type faujasite
• • C—CHEMISTRY; METALLURGY
  • C07—ORGANIC CHEMISTRY
  • C07C—ACYCLIC OR CARBOCYCLIC COMPOUNDS
  • C07C15/00—Cyclic hydrocarbons containing only six-membered aromatic rings as cyclic parts
  • C07C15/02—Monocyclic hydrocarbons
  • C07C15/04—Benzene
• • C—CHEMISTRY; METALLURGY
  • C07—ORGANIC CHEMISTRY
  • C07C—ACYCLIC OR CARBOCYCLIC COMPOUNDS
  • C07C15/00—Cyclic hydrocarbons containing only six-membered aromatic rings as cyclic parts
  • C07C15/02—Monocyclic hydrocarbons
  • C07C15/06—Toluene
• • C—CHEMISTRY; METALLURGY
  • C07—ORGANIC CHEMISTRY
  • C07C—ACYCLIC OR CARBOCYCLIC COMPOUNDS
  • C07C15/00—Cyclic hydrocarbons containing only six-membered aromatic rings as cyclic parts
  • C07C15/02—Monocyclic hydrocarbons
  • C07C15/067—C8H10 hydrocarbons
  • C07C15/08—Xylenes
• • C—CHEMISTRY; METALLURGY
  • C07—ORGANIC CHEMISTRY
  • C07C—ACYCLIC OR CARBOCYCLIC COMPOUNDS
  • C07C4/00—Preparation of hydrocarbons from hydrocarbons containing a larger number of carbon atoms
  • C07C4/08—Preparation of hydrocarbons from hydrocarbons containing a larger number of carbon atoms by splitting-off an aliphatic or cycloaliphatic part from the molecule
  • C07C4/12—Preparation of hydrocarbons from hydrocarbons containing a larger number of carbon atoms by splitting-off an aliphatic or cycloaliphatic part from the molecule from hydrocarbons containing a six-membered aromatic ring, e.g. propyltoluene to vinyltoluene
  • C07C4/14—Preparation of hydrocarbons from hydrocarbons containing a larger number of carbon atoms by splitting-off an aliphatic or cycloaliphatic part from the molecule from hydrocarbons containing a six-membered aromatic ring, e.g. propyltoluene to vinyltoluene splitting taking place at an aromatic-aliphatic bond
  • C07C4/18—Catalytic processes
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J2229/00—Aspects of molecular sieve catalysts not covered by B01J29/00
  • B01J2229/10—After treatment, characterised by the effect to be obtained
  • B01J2229/16—After treatment, characterised by the effect to be obtained to increase the Si/Al ratio; Dealumination
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J2229/00—Aspects of molecular sieve catalysts not covered by B01J29/00
  • B01J2229/10—After treatment, characterised by the effect to be obtained
  • B01J2229/26—After treatment, characterised by the effect to be obtained to stabilize the total catalyst structure
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J29/00—Catalysts comprising molecular sieves
  • B01J29/04—Catalysts comprising molecular sieves having base-exchange properties, e.g. crystalline zeolites
  • B01J29/06—Crystalline aluminosilicate zeolites; Isomorphous compounds thereof
  • B01J29/08—Crystalline aluminosilicate zeolites; Isomorphous compounds thereof of the faujasite type, e.g. type X or Y
  • B01J29/10—Crystalline aluminosilicate zeolites; Isomorphous compounds thereof of the faujasite type, e.g. type X or Y containing iron group metals, noble metals or copper
  • B01J29/14—Iron group metals or copper
  • B01J29/146—Y-type faujasite
• • C—CHEMISTRY; METALLURGY
  • C07—ORGANIC CHEMISTRY
  • C07C—ACYCLIC OR CARBOCYCLIC COMPOUNDS
  • C07C2529/00—Catalysts comprising molecular sieves
  • C07C2529/04—Catalysts comprising molecular sieves having base-exchange properties, e.g. crystalline zeolites, pillared clays
  • C07C2529/06—Crystalline aluminosilicate zeolites; Isomorphous compounds thereof
  • C07C2529/08—Crystalline aluminosilicate zeolites; Isomorphous compounds thereof of the faujasite type, e.g. type X or Y
• • C—CHEMISTRY; METALLURGY
  • C07—ORGANIC CHEMISTRY
  • C07C—ACYCLIC OR CARBOCYCLIC COMPOUNDS
  • C07C2529/00—Catalysts comprising molecular sieves
  • C07C2529/04—Catalysts comprising molecular sieves having base-exchange properties, e.g. crystalline zeolites, pillared clays
  • C07C2529/06—Crystalline aluminosilicate zeolites; Isomorphous compounds thereof
  • C07C2529/08—Crystalline aluminosilicate zeolites; Isomorphous compounds thereof of the faujasite type, e.g. type X or Y
  • C07C2529/10—Crystalline aluminosilicate zeolites; Isomorphous compounds thereof of the faujasite type, e.g. type X or Y containing iron group metals, noble metals or copper
  • C07C2529/14—Iron group metals or copper
• • C—CHEMISTRY; METALLURGY
  • C07—ORGANIC CHEMISTRY
  • C07C—ACYCLIC OR CARBOCYCLIC COMPOUNDS
  • C07C2529/00—Catalysts comprising molecular sieves
  • C07C2529/04—Catalysts comprising molecular sieves having base-exchange properties, e.g. crystalline zeolites, pillared clays
  • C07C2529/06—Crystalline aluminosilicate zeolites; Isomorphous compounds thereof
  • C07C2529/08—Crystalline aluminosilicate zeolites; Isomorphous compounds thereof of the faujasite type, e.g. type X or Y
  • C07C2529/16—Crystalline aluminosilicate zeolites; Isomorphous compounds thereof of the faujasite type, e.g. type X or Y containing arsenic, antimony, bismuth, vanadium, niobium, tantalum, polonium, chromium, molybdenum, tungsten, manganese, technetium or rhenium
• • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
  • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
  • Y02P—CLIMATE CHANGE MITIGATION TECHNOLOGIES IN THE PRODUCTION OR PROCESSING OF GOODS
  • Y02P20/00—Technologies relating to chemical industry
  • Y02P20/50—Improvements relating to the production of bulk chemicals
  • Y02P20/52—Improvements relating to the production of bulk chemicals using catalysts, e.g. selective catalysts

Definitions

• the present disclosure relates to a process for the hydrodealkylation of aromatic rich hydrocarbon streams to produce benzene, toluene and mixed xylenes (BTX), with high selectivity towards high value xylenes.
• the process uses catalysts containing a framework-substituted zirconium and/or titanium and/or hafnium-modified ultra-stable Y (USY) type zeolite.
• Catalytic reforming is a widely used process for refining hydrocarbon mixtures, resulting in reformate, an aromatic -rich gasoline blending fraction useful for aromatics production.
• the reformate from a catalytic reforming unit is sent to an aromatic complex in order to recover high value products, e.g., xylenes and benzene, and to convert lower value products, e.g., toluene, into higher value products.
• toluene is typically recovered as a separate fraction and undergoes disproportionation to produce benzene and xylenes or is hydrodealkylated to produce benzene.
• the aromatic complex produces a reject stream or bottoms that is very heavy (boiling in the range 100-450 °C), containing C9+ alkylated aromatics with alkyl groups containing 3 or more carbon number.
• the heavy bottoms fraction is not suitable as a gasoline blending component since it deteriorates the gasoline quality and in the long run negatively impacts engine performance. Moreover, blending is becoming more difficult due to more stringent regulations on the aromatics content in gasoline.
• Para-xylene is experiencing a market grown rate of demand. Consequently, the conversion of heavy aromatics to p-xylene provides a valuable product stream. It is therefore desirable to utilize the heavy reformate fraction to obtain BTX rich in xylenes via dealkylation of alkylated aromatics.
• USY ultra-stable Y
• the present disclosure relates to a system for hydrodealkylating the bottoms stream from an aromatic recovery complex to produce benzene, toluene and xylenes (BTX), with selectivity towards high value xylenes.
• the process utilizes a catalyst containing post-modified, framework substituted ultra-stable Y (USY) zeolite in which titanium (Ti) and/or, zirconium (Zr) and/or hafnium (Hf) are inserted into the zeolite catalyst after dealumination.
• USY zeolite catalysts according to the present disclosure results in a higher ratio of xylene to toluene and benzene compared to known processes.
• the process of the present disclosure provides a technical advantage in that it preferentially forms high value xylenes and reduces formation of lower value benzene and toluene.
• the present disclosure provides a process for hydrodealkylating a hydrocarbon feed comprising aromatic hydrocarbons with nine or more carbon atoms (C9+ aromatics), by reacting the hydrocarbon feed with a hydrogen feed in the presence of a dealkylation catalyst, wherein the dealkylation catalyst is framework-substituted ultra-stable Y (USY)-type zeolite.
• a dealkylation catalyst is framework-substituted ultra-stable Y (USY)-type zeolite.
• the present disclosure provides a process for producing mixed xylenes from a hydrocarbon feed comprising aromatic hydrocarbons with C9+ aromatics, by reacting the hydrocarbon feed with a hydrogen feed in the presence of a dealkylation catalyst which hydrodealkylates aromatic compounds in the hydrocarbon feed; wherein the dealkylation catalyst is framework-substituted ultra-stable Y (USY)- type zeolite.
• a dealkylation catalyst which hydrodealkylates aromatic compounds in the hydrocarbon feed
• the dealkylation catalyst is framework-substituted ultra-stable Y (USY)- type zeolite.
• the framework-substituted USY zeolite is one in which a portion of aluminum atoms constituting a zeolite framework thereof is substituted with zirconium atoms and/or titanium and/or hafnium atoms.
• the framework-substituted USY zeolite may be carried on a support which contains an inorganic oxide, e.g., alumina, silica-alumina and the like, as described herein.
• the hydrocarbon feed comprises an aromatic nch heavy reformate feed (e.g., a bottoms stream) comprising an aromatic rich hydrocarbon oil having a boiling point range of about 50°C to about 500°C.
• the process of the invention results in formation a BTX fraction with strong selectivity towards xylenes.
• the ratio of mixed xylenes to benzene and toluene is at least about 2 to 1, preferably at least about 3 to 1. In other embodiments, the ratio of benzene to toluene to xylene is about 1: 4-10: 15-25.
• FIG. 1 provides a diagram of an embodiment of the process.
• Descnbed herein is a process and system for the production of mixed xylenes by hydrodealkylating a heavy hydrocarbon feed containing C9+ aromatic compounds (e.g., a heavy bottoms reformate feed).
• a heavy bottoms reformate feed and a hydrogen feed are introduced to a dealkylation reactor containing a dealkylation catalyst.
• the dealkylation catalyst is a catalyst containing a framework-substituted ultrastable Y (US Y) -type zeolite in which a portion of aluminum atoms constituting a zeolite framework thereof is substituted with zirconium atoms and/or titanium and/or hafnium atoms.
• the dealkylation effluent from the dealkylation reactor may optionally be introduced to a splitter unit to separate the components of the dealkylation effluent.
• the use of a catalyst containing a framework-substituted ultrastable Y (USY)-type zeolite increases the overall production of xylenes as compared to other catalysts.
• the process results in dealkylation of C9+ aromatics to result in benzene, toluene and mixed xylene (BTX) with a preference towards high value xylenes.
• C refers to the number of carbon atoms in a hydrocarbon.
• C6 refers to a hydrocarbon with 6 carbon atoms
• C7 refers to a hydrocarbon with seven carbon atoms, and the like.
• C8 aromatics refers to aromatic hydrocarbons with eight carbon atoms.
• Examples of C8 aromatic hydrocarbons include mixed xylenes and ethyl benzene.
• mixed xylenes refers to one or more of para-xylene (p- xylene), meta- xylene (m- xylene), and ortho-xylene (o-xylene).
• C9 aromatics refers to aromatic hydrocarbons with nine carbon atoms.
• Examples of C9 aromatic hydrocarbons include methylethylbenzene, trimethylbenzene, and propylbenzene.
• C10+ aromatics refers to aromatic hydrocarbons with ten carbon atoms and aromatics with more than ten carbon atoms, such as an aromatic hydrocarbon with eleven carbon atoms.
• C10+ aromatics can include double ring aromatic compounds. Examples of double ring aromatic compounds of C10+ aromatics include naphthalene, methylnaphthalene, naphthalene derivatives, and combinations of the same. Examples of methylnaphthalene include 1 -methylnaphthalene, 2-methylnaphthalene, and combinations of the same.
• C9+ aromatics refers to the group of C9 aromatics and C10+ aromatics.
• BTX means a composition comprising benzene (C6), toluene (C7) and mixed xylenes (C8).
• xylenes as denoted herein means any one of ortho xylene (o-xylene), meta-xylene (m- xylene), para- xylene (p-xylene) or any combination thereof.
• mixed xylenes refers to any one or more of o- xylene, m-xylene and p-xylene.
• dealkylation reaction refers to a reaction that results in the removal of one or more alkyl groups from one or more of the reactants.
• light hydrocarbons refers to one or more of alkanes, including methane, ethane, propane, butanes, pentanes, alkenes, and trace amounts of naphthenes, such as cyclopentane, cyclohexane.
• light gases refers to one or more of light hydrocarbons, hydrogen, and air.
• single ring aromatic compounds refers to aromatic compounds containing at least six carbon atoms arranged in a central aromatic ring and includes rings with hydrogen and hydrocarbons as substituents.
• Heavy reformate feed 100 is introduced to dealkylation reactor 10 along with hydrogen feed 105.
• Heavy reformate feed 100 can include toluene, mixed xylenes, C9 aromatics, and C10+ aromatics as described below.
• Hydrogen feed 105 can be any stream containing hydrogen gas. Hydrogen feed 105 can be a stream of pure hydrogen from a fresh hydrogen source. In at least one embodiment, hydrogen feed 105 can be from a hydrogen source in a refinery and can contain light hydrocarbons.
• Dealkylation reactor 10 can be any type of reactor capable of containing and supporting a dealkylation reaction.
• Dealkylation reactor 10 can be a fixed bed reactor or a fluidized bed reactor.
• the dealkylation temperature in dealkylation reactor 10 can be between 400 degrees Celsius (°C) and 500 °C.
• the dealkylation pressure in dealkylation reactor 10 can be between 20 bar (2,000 kilopascal (kPa)) and 50 bar (5,000 kPa).
• the liquid hourly space velocity (LHSV) can be between about 0.5 per hour (hr 1 ) and about 5 hr 1 .
• the hydrogen to hydrocarbon ratio can be about 100 to about 500 SLt/Lt.
• Dealkylation reactor 10 includes dealkylation catalyst containing a framework- substituted USY zeolite is one in which a portion of aluminum atoms constituting a zeolite framework thereof is substituted with zirconium atoms and/or titanium atoms and/or hafnium atoms, as further described below.
• the dealkylation catalyst can be selected to selectively convert one or more of the C9+ aromatics in dealkylation reactions.
• Dealkylation reactions can convert C9+ aromatics to toluene, benzene, mixed xylenes, and light gases.
• Reactions in dealkylation reactor 10 can remove methyl, ethyl, propyl, butyl and pentyl groups, and their isomers, attached to C9+ aromatics.
• a dealkylation catalyst can be selected to convert more than 97.5 wt % of the methylethylbenzene to toluene.
• the overall conversion of C9+ aromatics can be greater than 98 wt % due to conversion of C9 aromatics and the removal of methyl, ethyl, propyl, butyl and pentyl groups attached to C10+ aromatics.
• splitter unit 20 can be any type of separation unit capable of separating a stream into its component parts.
• splitter unit 20 can be one splitter column designed to separate the feed stream into multiple split streams.
• splitter unit 20 can be multiple splitter columns in series designed to separate one component from the feed stream.
• splitter unit 20 can be one or more distillation units.
• splitter unit 20 comprises a distillation column operating at a pressure of between 4 bar gauge (barg) and 6 barg and a temperature between 20 °C and 100 °C to separate light gases from the first column feed to produce light gas stream 120 and a liquid reaction effluent 122 comprising C6+ hydrocarbons.
• splitter unit 20 separates the components to produce light gas stream 120, and a liquid reaction effluent 122 containing BTX (C6-8 aromatic hydrocarbons) and C9+ aromatics stream.
• effluent 122 can be introduced to an aromatic recovery complex (ARC) 30 wherein such effluent is further processed in order to recover BTX stream 124.
• ARC aromatic recovery complex
• splitter unit 20 can be designed to operate at a temperature and pressure to produce the desired streams.
• the distillation column can include multiple sections in one vessel, where each section has the operating conditions corresponding to each of the separate columns described in this paragraph.
• the apparatus for the hydrodealkylation process in the present disclosure is not particularly limited to the aforementioned embodiments, and that any other apparatus may be used, as long as the foregoing reactions are carried out. Various types of apparatuses may be used. In accordance with some embodiments, the process of the present disclosure may be conducted on ebullated-bed or slurry-bed or moving-bed reactors or CSTR or batch type reactors, and the like.
• the hydrocarbon feed 100 used in the process of the present disclosure may be any hydrocarbon feed that is rich in aromatic hydrocarbons.
• the hydrocarbon feed is a heavy reformate feed produced from aromatic recovery processes (also designed herein “aromatics bottoms fraction”).
• aromatics bottoms fraction also designed herein “aromatics bottoms fraction”.
• the heavy reformate feed is preferably enriched in aromatic hydrocarbons and can include toluene, mixed xylenes, C9 aromatics, and C10+ aromatics.
• heavy reformate feed 100 can contain between 0 wt % and 10 wt % C6 aromatics (benzene). In at least one embodiment, heavy reformate feed 100 can contain between 0 wt % and 10 wt % C7 aromatics (toluene). In at least one embodiment, heavy reformate feed 100 can contain between 0 wt % and 10 wt % mixed xylenes. In at least one embodiment, heavy reformate feed 100 can contain between 0 wt % and 10 wt % C6-C8 aromatics.
• heavy reformate feed 100 can contain between 0 wt % and 10 wt % mixed xylenes and between 60 wt % and 100 wt % C9+ aromatics. In at least one embodiment, heavy reformate feed 100 can contain between 0 wt % and 40 wt % C6-C8 aromatics and between 60 wt % and 100 wt % C9+ aromatics. In at least one embodiment, heavy reformate feed 100 can contain between 0 wt % and 10 wt % mixed xylenes, between 0 wt % and 10 wt % toluene, and between 80 wt % and 100 wt % C9+ aromatics.
• heavy reformate feed 100 contains between 60 wt % and 100 wt % C9+ aromatics. In at least one embodiment, heavy reformate feed 100 contains between 60 wt % and 100 wt % C10+ aromatics. In at least one embodiment, heavy reformate feed 100 contains between 90 wt % and 100 wt % C10+ aromatics. In at least one embodiment, heavy reformate feed 100 contains between 60 wt % and 100 wt % C11+ aromatics. In at least one embodiment, heavy reformate feed 100 contains between 90 wt % and 100 wt % C11+ aromatics.
• heavy reformate feed 100 can include trace amounts of C8+ naphthenes and C10+ naphthylenes, including the alkyl derivatives of the same. In further embodiments, heavy reformate feed includes trace amounts of non- aromatic hydrocarbons. In at least one embodiment, heavy reformate feed 100 contains between 0 wt% and 1 wt% C4-C12 n-paraffins. In at least one embodiment, heavy reformate feed 100 contains between 0 wt% and 1 wt% C4-C12 i-paraffins. In at least one embodiment, heavy reformate feed 100 contains between 0 wt% and 1 wt% C8+ naphthenes and C10+ naphthylenes.
• the heavy reformate feed comprises an aromatic rich hydrocarbon oil having a boiling point range of about 50°C to about 500°C. In other embodiments, the hydrocarbon feed comprises an aromatic rich hydrocarbon oil having a boiling point range of about 100°C to about 500°C. In other embodiments, the heavy reformate feed comprises an aromatic rich hydrocarbon oil having a boiling point range of about 150°C to about 500°C. In other embodiments, the heavy reformate feed comprises an aromatic rich hydrocarbon oil having a boiling point range of about 150°C to about 400°C.
• Reformate feeds usually contain very low amount of sulfur, as they are typically subjected to desulfurization prior to reforming such that the resulting gasoline product contains an acceptable level of sulfur for compliance with current sulfur specification.
• the dealkylated hydrocarbon product preferably contains less than about 500 ppm sulfur, preferably less than about 10 ppm, most preferably less than about 0.5 ppm.
• the dealkylated hydrocarbon product containing less than about 100 ppm nitrogen, preferably less than about 10 ppm, most preferably less than about 0.5 ppm.
• the hydrocarbon feed is dealkylated at least about 50%.
• the hydrocarbon feed is dealkylated at least about 60%.
• the hydrocarbon feed is dealkylated at least about 70%.
• the process of the present disclosure produces a dealkylated product comprising benzene, toluene, mixed xylenes (BTX), C9 aromatics and C10+ aromatics.
• the dealkylated product contains trace amounts of C8+ naphthenes, C10+ naphthylenes, C4-C12 n-paraffins and/or C4-C12 i-paraffins.
• the process of the present disclosure is characterized by production of a BTX fraction with strong selectivity towards xylene relative to benzene and toluene.
• the process produces a higher amount of mixed xylenes compared with benzene and toluene.
• the ratio of mixed xylenes to benzene and toluene is at least about 2 to 1.
• the ratio of mixed xylenes to benzene and toluene is preferably at least about 3 to 1.
• the ratio of benzene to toluene to xylene is about 1: 4-10: 15-25 (expressed as benzene : toluene : xylene, and normalized to benzene). In other embodiments, the ratio of benzene to toluene to xylene is about 1: 4-7: 18-25.
• Dealkylation reactor 10 can include a dealkylation catalyst.
• the dealkylation catalyst contains a framework substituted zeolite in which a part of aluminum atoms constituting a zeolite framework is substituted with zirconium atoms and/or titanium atoms and/or hafnium atoms.
• the catalyst with the framework- substituted zeolite catalyst used in the process of the present disclosure is an ultra-stable Y-type zeolite in which silicon atoms and aluminum atoms form a zeolite framework and in which a part of the aluminum atoms is substituted with zirconium atoms and/or titanium atoms and/or hafnium atoms.
• the framework-substituted zeolite in the catalyst in which a part of aluminum atoms forming a zeolite framework is substituted only with zirconium atoms is referred to as a "zirconium- substituted zeolite” or "Zr-USY”
• the framework- substituted zeolite in the catalyst in which a part of aluminum atoms forming a zeolite framework of the framework-substituted zeolite is substituted only with titanium atoms is referred to as a "titanium-substituted zeolite” or "Ti-USY”
• the framework-substituted zeolite in the catalyst in which a part of aluminum atoms forming a zeolite framework is substituted only with zirconium atoms and titanium atoms is referred to as a "zirconium.titanium-substituted zeolite” or "ZrTi-USY”)
• Zirconium atoms and/or titanium and/or hafnium atoms which are substituted for the aluminum atoms forming a framework of the ultra-stable Y-type zeolite serve as constituents of the framework of the ultra-stable Y-type zeolite. Substitution can be verified by, e.g., ultraviolet, visible, and near-infrared spectrophotometry (UV-Vis-NIR), Fourier transform infrared spectroscopy (FT-IR.
• UV-Vis-NIR ultraviolet, visible, and near-infrared spectrophotometry
• FT-IR Fourier transform infrared spectroscopy
• the zirconium atoms and/or titanium and/or hafnium atoms may further be attached (carried) to the outside of, or combined with the framework of the USY-type catalyst, as described in U.S. Patent No. 10,293,332, which is hereby incorporated by reference in its entirety as if fully set forth herein.
• the framework-substituted zeolite of the catalyst contains about 0.1% to about 5%, preferably about 0.2% to about 4%, more preferably about 0.3% to about 3% zirconium atoms and/or titanium and/or hafnium atoms by mass in terms of oxide (i.e., "ZrO ", "TiCh” and "HI'O ”) based on the framework-substituted zeolite.
• a content range (based on oxides) of zirconium atoms and/or titanium and/or hafnium atoms includes all of the contents of zirconium atoms and/or titanium and/or hafnium atoms substituted for aluminum atoms forming a zeolite framework and zirconium atoms and/or titanium and/or hafnium atoms which are not substituted for the above aluminum atoms.
• the framework- substituted zeolite in the catalyst contains the zirconium atoms and the titanium atoms and/or the hafnium atoms described above, a mass ratio (in terms of oxides) of the zirconium atoms to the titanium atoms and/or the hafnium atoms is not specifically be restricted, and any ratio of zirconium or titanium or hafnium that is effective to carry out the process of the present invention may be used.
• the zirconium atom and/or titanium and/or hafnium atom content of the framework-substituted zeolite in the catalyst can be measured with, for example, an X-ray fluorescence analyzer, a high frequency plasma emission spectrometer, an atomic absorption spectrometer or the like.
• particles of the zirconium and/or titanium and/or hafnium- modified USY catalyst have a diameter of 50 nm or less.
• the framework-substituted zeolite in the catalyst in the present invention can be produced in accordance with the methods described by U.S. 10,293,332.
• the framework-substituted zeolite in the catalyst may be produced by firing a USY-type zeolite at 500° C to 700° C, the USY-type zeolite having a crystal lattice constant of 2.430 to 2.450 nm, a specific surface area of 600 to 900 m 2 /g, and a molar ratio of SiCh to AI2O3 of 20 to 100, forming a suspension containing the fired USY-type zeolite, the suspension having a liquid/solid mass ratio of 5 to 15, adding an inorganic acid or an organic acid so that a pH of the above suspension is 1.0 to 2.0, subsequently adding a solution containing a zirconium compound and/or a hafnium compound and mixing them and neutralizing the solution with, for example, an aqueous ammonia in such a manner that
• Ultra-stable Y-type zeolite is used as one of the raw materials for preparing the framework-substituted zeolite in the catalyst.
• Ultra-stable Y-type zeolite means zeolite having a crystal lattice constant (UD) falling in a range of 2.430 nm or more and 2.450 nm or less, a specific surface area of 600 to 900 m 2 /g and a molar ratio (silica-alumina ratio) falling in a range of 20 to 100 in terms of SiCh to AI2O3.
• the ultra-stable Y-type zeolite may be prepared by any method known in the art.
• extraskeletal aluminum (aluminum atoms which do not form the zeolite framework) may be removed from the ultra- stable Y-type zeolite raw material in order to obtain the ultrastable Y-type zeolite.
• Extraskeletal aluminum can be removed by, for example, a method of dispersing the ultra-stable Y-type zeolite in warm water of 40 to 95° C to prepare a suspension, adding sulfuric acid to the above suspension and stirring it for 10 minutes to 3 hours while maintaining the temperature at 40 to 95° C to thereby dissolve the extraskeletal aluminum.
• the suspension After dissolving the extraskeletal aluminum, the suspension is filtrated, and a residue on the filter is washed with purified water of 40 to 95° C and dried at 100 to 180° C for 3 to 30 hours, whereby an ultra-stable Y-type zeolite from which the extraskeletal aluminum is removed can be obtained.
• the ultra-stable Y-type zeolite raw material may be calcined at 500° C to 700° C, preferably 550° C to 650° C.
• the calcining time shall not specifically be restricted as long as the targeted framework-substituted zeolite is obtained, and it is calcined in a range of, for example, 30 minutes to 10 hours.
• a calcining atmosphere of the ultra-stable Y-type zeolite it is carried out preferably in the air.
• the calcined ultra-stable Y-type zeolite is suspended in water having a temperature of about 20° C to about 30° C to form a suspension.
• the liquid/solid mass ratio is preferably in the range of 5 to 15, and more preferably, a mass ratio of 8 to 12 is recommended.
• an inorganic acid or an organic acid is added thereto so that a pH of the suspension described above is controlled to 1.0 to 2.0, and subsequently a solution containing a zirconium compound and/or a hafnium compound is added and mixed. Then, the mixed solution is neutralized (pH 7.0 to 7.5) and dried desirably at 80 to 180° C, whereby the framework-substituted zeolite described above can be obtained.
• Sulfuric acid, nitric acid, hydrochloric acid and the like can be given as the above inorganic acid used, and among them, sulfuric acid, hydrochloric acid and the like are particularly preferred.
• carboxylic acids can suitably be used as the organic acid described above.
• a use amount of the inorganic acid or the organic acid shall not be restricted as long as a pH of the suspension can be controlled to a range of 1.0 to 2.0, and it is, for example, a 0.5- to 4.0-fold molar amount and preferably 0.7- to 3.5-fold molar amount based on an amount of AI2O3 in the ultra-stable Y-type zeolite, but it shall not be restricted to the above range.
• zirconium compound described above examples include zirconium sulfate, zirconium nitrate, zirconium chloride and the like. Among these compounds, zirconium sulfate, zirconium nitrate, and the like are particularly preferred.
• the amount of the zirconium compound added is preferably about 0.1% to about 5% by mass and more preferably about 0.2% to about 4% by mass on a zirconium oxide basis with respect to the ultra-stable Y-type zeolite described above.
• an aqueous solution of a zirconium compound prepared by dissolving the zirconium compound in water is suitably used as the zirconium compound.
• hafnium compound described above examples include hafnium chloride, hafnium nitrate, hafnium fluoride, hafnium bromide, hafnium oxalate and the like.
• hafnium chloride, hafnium nitrate, and the like are particularly preferred.
• the amount of the hafnium compound added is preferably about 0.1 % to about 5% by mass and more preferably about 0.2% to about 4% by mass on a hafnium oxide basis with respect to the ultra-stable Y-type zeolite.
• an aqueous solution of a hafnium compound prepared by dissolving the hafnium compound in water is suitably used as the hafnium compound.
• a titanium compound may be added to the mixed solution described above.
• the titanium compound include titanium sulfate, titanium acetate, titanium chloride, titanium nitrate, and titanium lactate. Among these compounds, titanium sulfate, titanium acetate, and the like are particularly preferred.
• the amount of the titanium compound added is preferably about 0.1% to about 5% by mass and more preferably about 0.2% to about 4% by mass on an oxide basis with respect to the ultrastable Y-type zeolite.
• an aqueous solution of a titanium compound prepared by dissolving the titanium compound in water is suitably used as the titanium compound.
• a pH of the above suspension has to be controlled in advance to 1.0 to 2.0 for the purpose of preventing precipitation from being generated in mixing an aqueous solution of the zirconium compound, the hafnium compound or the titanium compound with a suspension of the ultra-stable Y-type zeolite described above.
• the above aqueous solution is gradually added to the suspension.
• the solution is preferably mixed by stirring at, for example, room temperature (about 25° C to about 35° C) for 3 to 5 hours.
• the mixed solution described above is neutralized by adding an alkali such as aqueous ammonia and the like so that a pH thereof is controlled to 7.0 to 7.5, whereby the framework-substituted zeolite in the catalyst can be obtained.
• the framework-substituted zeolite in the catalyst (Zr-USY) in which zirconium atoms is substituted for a part of aluminum atoms forming the framework of the ultra-stable Y-type zeolite is formed; when only the hafnium compound (or an aqueous solution thereof) is used, the framework-substituted zeolite in the catalyst (Hf-USY) in which hafnium atoms is substituted for a part of aluminum atoms forming the framework of the ultra-stable Y- type zeolite is formed; when only the titanium compound (or an aqueous solution thereof) is used, the framework-substituted zeolite in the catalyst (Ti-USY) in which titanium atoms is substituted for a
• the resulting framework-substituted zeolite in the catalyst is preferably filtered, if desired, washed with water, and dried at about 80° C to about 180° C.
• the framework-substituted USY zeolite may be carried on a support which contains an inorganic oxide excluding the above framework-substituted zeolite in the catalyst in addition to the framework-substituted zeolite in the catalyst described above.
• the inorganic oxide typically contains a substance serving as a granulating agent or a binder.
• a known substance that is contained in a support including the ultrastable Y-type zeolite and that is used as a granulating agent or the like can be used.
• inorganic oxides include, but are not limited to alumina, silica, titania, silica- alumina, alumina-titania, alumina-zirconia, alumina-boria, phosphorus-alumina, silica- alumina-boria, phosphorus-alumina-boria, phosphorus-alumina-silica, silica-alumina- titania, and silica-alumina-zirconia.
• an inorganic oxide mainly composed of alumina, silica-alumina is preferred.
• the content of the framework- substituted zeolite in the catalyst and the inorganic oxide content of the support can be appropriately determined according to the object.
• the support includes a framework-substituted zeolite in the catalyst of about 2% to about 80% by mass, preferably about 10% to about 80% by mass, and more preferably about 20% to about 70% by mass, and an inorganic oxide content of about 98% to about 20% by mass, preferably about 90% to about 20% by mass and more preferably about 80% to about 30% by mass.
• the catalyst used in the process of the present disclosure may further include active metal components selected from the group consisting of IUPAC Group 6 to 11 metals of the Periodic Table.
• active metals include iron, cobalt, nickel, rhodium, palladium, silver, iridium, platinum or gold in group 8 of the long periodic table and/or metal components chromium, molybdenum or tungsten in group 6.
• Preferred examples of the metal component include combinations of molybdenum or tungsten in group 6 and cobalt or nickel in group 8; and metal components of the platinum group (platinum, rhodium, palladium and the like).
• the metal component may be contained in the catalyst in an amount of about 0.0001 to about 40% by mass in terms of oxide.
• an amount thereof is particularly preferably about 3 to about 30% by mass in terms of oxide based on a mass of the catalyst.
• platinum group platinum, rhodium, palladium and the like
• an amount thereof is particularly preferably about 0.01 to about 2% by mass in terms of metal.
• Example 1 provides an analysis of a dealkylation reactor 10 with reference to FIG. 1.
• Heavy reformate feed 100 has the composition of Table 1.
• the feedstock composition and properties are summarized in Table 1.
• Detail composition obtained from PIONA analysis is shown in Table 2.
• the catalyst was a framework-substituted ultra-stable Y (USY)-type zeolite in which a portion of aluminum atoms constituting a zeolite framework thereof is substituted with zirconium atoms and titanium atoms, which further includes Nickel (Ni) and
• Mo Molybdenum
• Table 8 provides the benzene/toluene/xylene ratio obtained according to the process of US 2019/0194095, Example 1.
• the process of US 2019/0194095 uses a ZSM- 5 zeolite catalyst at 400°C.
• US 2019/0194095 is hereby expressly incorporated by reference in its entirety.

Landscapes

• Chemical & Material Sciences (AREA)
• Organic Chemistry (AREA)
• Engineering & Computer Science (AREA)
• Chemical Kinetics & Catalysis (AREA)
• Materials Engineering (AREA)
• Crystallography & Structural Chemistry (AREA)
• Oil, Petroleum & Natural Gas (AREA)
• General Chemical & Material Sciences (AREA)
• Organic Low-Molecular-Weight Compounds And Preparation Thereof (AREA)
• Catalysts (AREA)
• Low-Molecular Organic Synthesis Reactions Using Catalysts (AREA)

Priority Applications (4)

Applications Claiming Priority (2)

Publications (1)

Family

ID=79601540

Family Applications (1)

Country Status (6)

Families Citing this family (2)

Citations (5)

Family Cites Families (30)

• 2020
  • 2020-12-09 US US17/116,856 patent/US11484869B2/en active Active
• 2021
  • 2021-12-08 KR KR1020237020338A patent/KR20230117363A/ko active Pending
  • 2021-12-08 EP EP21843817.4A patent/EP4259754B1/en active Active
  • 2021-12-08 CN CN202180083101.8A patent/CN116568656B/zh active Active
  • 2021-12-08 JP JP2023535556A patent/JP7823050B2/ja active Active
  • 2021-12-08 WO PCT/US2021/062424 patent/WO2022125674A1/en not_active Ceased

Patent Citations (5)

Non-Patent Citations (1)

Also Published As

Similar Documents

Legal Events