WO2022065209A1 - 弾性繊維用処理剤及び弾性繊維 - Google Patents

弾性繊維用処理剤及び弾性繊維 Download PDF

Info

Publication number
WO2022065209A1
WO2022065209A1 PCT/JP2021/034218 JP2021034218W WO2022065209A1 WO 2022065209 A1 WO2022065209 A1 WO 2022065209A1 JP 2021034218 W JP2021034218 W JP 2021034218W WO 2022065209 A1 WO2022065209 A1 WO 2022065209A1
Authority
WO
WIPO (PCT)
Prior art keywords
mass
elastic fiber
treatment agent
agent
naturally derived
Prior art date
Application number
PCT/JP2021/034218
Other languages
English (en)
French (fr)
Inventor
武志 西川
啓一郎 大島
Original Assignee
竹本油脂株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 竹本油脂株式会社 filed Critical 竹本油脂株式会社
Priority to CN202180063656.6A priority Critical patent/CN116157569B/zh
Priority to KR1020237012146A priority patent/KR102606860B1/ko
Priority to US18/026,733 priority patent/US11926956B2/en
Publication of WO2022065209A1 publication Critical patent/WO2022065209A1/ja

Abstract

本発明が解決しようとする課題は、弾性繊維の巻き取り時に飛散しにくい弾性繊維用処理剤及びかかる弾性繊維用処理剤が付着している弾性繊維を提供する。本発明の弾性繊維用処理剤は、鉱物油、シリコーン油、及びエステル油から選ばれる少なくとも１つの平滑剤（Ａ）、並びに、テルペン樹脂、及びテルペン樹脂誘導体から選ばれる少なくとも１つの天然由来成分（Ｂ）を含有することを特徴とする。あるいは、弾性繊維用処理剤は、前記少なくとも１つの平滑剤（Ａ）と、ロジン及びロジン誘導体から選ばれる少なくとも１つの天然由来成分（Ｂ）とを含有し、平滑剤（Ａ）が鉱物油を含み、平滑剤（Ａ）中の鉱物油の含有割合が５９．５～９５質量％であることを特徴とする。

Description

弾性繊維用処理剤及び弾性繊維
　本発明は、所定の天然由来成分を含有する弾性繊維用処理剤及びかかる弾性繊維用処理剤が付着している弾性繊維に関する。
　例えばポリウレタン系弾性繊維等の弾性繊維は、他の合成繊維に比べて、繊維間の粘着性が強い。そのため、例えば弾性繊維を紡糸し、パッケージに巻き取った後、該パッケージから引き出して加工工程に供する際、パッケージから安定して解舒することが困難という問題があった。そのために、従来より弾性繊維の平滑性を向上させるため、炭化水素油等の平滑剤を含有する弾性繊維用処理剤が使用されることがある。
　従来、特許文献１に開示される弾性繊維用処理剤が知られている。特許文献１は、シリコーン油等のベース成分と、２族元素金属の二価カチオンの酸性リン酸エステル塩とを所定の比率で含有するポリウレタン弾性繊維用処理剤について開示する。
国際公開第２０１１／１０５３８６号
　しかし、弾性繊維用処理剤が付与された弾性繊維をワインダーで巻き取る際に処理剤が飛散するのを抑制すること、すなわち弾性繊維用処理剤の飛散抑制効果のさらなる向上が求められていた。
　本発明者らは、前記の課題を解決するべく研究した結果、弾性繊維用処理剤において、所定の平滑剤（Ａ）と所定の天然由来成分（Ｂ）とを配合した構成が好適であることを見出した。
　上記課題を解決するために、本発明の一態様の弾性繊維用処理剤は、鉱物油、シリコーン油、及びエステル油から選ばれる少なくとも１つの平滑剤（Ａ）、並びに、テルペン樹脂及びテルペン樹脂誘導体から選ばれる少なくとも１つの天然由来成分（Ｂ）を含有することを特徴とする。
　上記弾性繊維用処理剤において、前記平滑剤（Ａ）が鉱物油を含み、前記平滑剤（Ａ）中の鉱物油の含有割合が５５～９５質量％であることが好ましい。
　上記課題を解決するために、本発明の別の態様の弾性繊維用処理剤は、鉱物油、シリコーン油、及びエステル油から選ばれる少なくとも１つの平滑剤（Ａ）、並びに、ロジン及びロジン誘導体から選ばれる少なくとも１つの天然由来成分（Ｂ）を含有し、前記平滑剤（Ａ）が鉱物油を含み、前記平滑剤（Ａ）中の鉱物油の含有割合が５９．５～９５質量％であることを特徴とする。
　上記弾性繊維用処理剤は、前記平滑剤（Ａ）及び前記天然由来成分（Ｂ）の含有割合の合計を１００質量部とすると、前記天然由来成分（Ｂ）を０．１～３０質量部の割合で含有することが好ましい。
　上記弾性繊維用処理剤は、炭素数１２～２４の脂肪族アルコールと、炭素数１２～２４の脂肪族アルコール１モルに対して炭素数２～４のアルキレンオキサイドを１～１００モルの割合で付加させた高級アルコールのアルキレンオキサイド付加物とから選ばれる少なくとも１つのヒドロキシ化合物（Ｃ）を更に含有することが好ましい。
　上記弾性繊維用処理剤は、前記平滑剤（Ａ）、前記天然由来成分（Ｂ）、及びヒドロキシ化合物（Ｃ）の含有割合の合計を１００質量部とすると、前記天然由来成分（Ｂ）を０．１～３０質量部の割合で含有することが好ましい。
　上記課題を解決するために、本発明の別の態様の弾性繊維では、前記弾性繊維用処理剤が付着していることを特徴とする。
　本発明によれば、弾性繊維用処理剤の飛散抑制効果を向上できる。
　（第１実施形態）
　以下、本発明の弾性繊維用処理剤（以下、処理剤ともいう）を具体化した第１実施形態を説明する。本実施形態の処理剤は、所定の平滑剤（Ａ）及び天然由来成分（Ｂ）を含有し、さらにヒドロキシ化合物を含んでもよい。
　平滑剤（Ａ）は、ベース成分として処理剤に配合され、弾性繊維に平滑性を付与する働きをする。平滑剤（Ａ）としては、鉱物油、シリコーン油、及びエステル油が挙げられる。
　鉱物油としては、例えば、芳香族系炭化水素、パラフィン系炭化水素、ナフテン系炭化水素等が挙げられる。より具体的には、例えば、スピンドル油、流動パラフィン等が挙げられる。これらの鉱物油は、粘度等によって規定される市販品を適宜採用してもよい。
　シリコーン油の具体例としては、例えばジメチルシリコーン、フェニル変性シリコーン、アミノ変性シリコーン、アミド変性シリコーン、ポリエーテル変性シリコーン、アミノポリエーテル変性シリコーン、アルキル変性シリコーン、アルキルアラルキル変性シリコーン、アルキルポリエーテル変性シリコーン、エステル変性シリコーン、エポキシ変性シリコーン、カルビノール変性シリコーン、メルカプト変性シリコーン、ポリオキシアルキレン変性シリコーン等が挙げられる。これらのシリコーン油は、動粘度等によって規定される市販品を適宜採用してもよい。動粘度は、適宜設定されるが、２５℃における動粘度が２～１００ｃｓｔ（ｍｍ２／ｓ）であることが好ましい。２５℃における動粘度は、ＪＩＳ　Ｚ　８８０３に準拠して測定される。
　エステル油としては、特に制限はないが、脂肪酸とアルコールとから製造されるエステル油が挙げられる。エステル油としては、例えば後述する奇数又は偶数の炭化水素基を有する脂肪酸とアルコールとから製造されるエステル油が例示される。
　エステル油の原料である脂肪酸は、その炭素数、分岐の有無、価数等について特に制限はなく、また、例えば高級脂肪酸であってもよく、シクロ環を有する脂肪酸であってもよく、芳香族環を有する脂肪酸であってもよい。エステル油の原料であるアルコールは、その炭素数、分岐の有無、価数等について特に制限はなく、また、例えば高級アルコールであっても、シクロ環を有するアルコールであっても、芳香族環を有するアルコールであってもよい。
　エステル油の具体例としては、例えば（１）オクチルパルミタート、オレイルラウラート、オレイルオレアート、イソトリデシルステアラート、イソテトラコシルオレアート等の、脂肪族モノアルコールと脂肪族モノカルボン酸とのエステル化合物、（２）１，６－ヘキサンジオールジデカナート、グリセリントリオレアート、トリメチロールプロパントリラウラート、ペンタエリスリトールテトラオクタナート等の、脂肪族多価アルコールと脂肪族モノカルボン酸とのエステル化合物、（３）ジオレイルアゼラート、チオジプロピオン酸ジオレイル、チオジプロピオン酸ジイソセチル、チオジプロピオン酸ジイソステアリル等の、脂肪族モノアルコールと脂肪族多価カルボン酸とのエステル化合物、（４）ベンジルオレアート、ベンジルラウラート等の、芳香族モノアルコールと脂肪族モノカルボン酸とのエステル化合物、（５）ビスフェノールＡジラウラート等の、芳香族多価アルコールと脂肪族モノカルボン酸との完全エステル化合物、（６）ビス２－エチルヘキシルフタラート、ジイソステアリルイソフタラート、トリオクチルトリメリタート等の、脂肪族モノアルコールと芳香族多価カルボン酸との完全エステル化合物、（７）ヤシ油、ナタネ油、ヒマワリ油、大豆油、ヒマシ油、ゴマ油、魚油及び牛脂等の天然油脂等が挙げられる。
　これらの平滑剤（Ａ）は、１種の平滑剤を単独で使用してもよく、２種以上の平滑剤を組み合わせて使用してもよい。
　本実施形態において、本発明の効果を阻害しない範囲内において、上記以外の平滑剤を併用してもよい。上記以外の平滑剤としては、公知のものを適宜採用してもよい。上記以外の平滑剤としては、例えばポリオレフィン等が挙げられる。
　ポリオレフィンは、平滑成分として用いられるポリ－α－オレフィンが適用される。ポリオレフィンの具体例としては、例えば１－ブテン、１－ヘキセン、１－デセン等を重合して得られるポリ－α－オレフィン等が挙げられる。ポリ－α－オレフィンは、市販品を適宜採用してもよい。
　本実施形態において、平滑剤（Ａ）は鉱物油を含むことが好ましい。平滑剤（Ａ）中における鉱物油の含有割合は、５５～９５質量％であることが好ましい。鉱物油の含有量をかかる範囲に規定することにより、形状特性をより向上させる。平滑剤（Ａ）中の鉱物油の含有割合は例えば、３３．３質量％以上、４６．２質量％以上、５７．９質量％以上、５９．５質量％以上、６２．０質量％以上、６４．７質量％以上、６７．３質量％以上、６７．６質量％以上、６７．７質量％以上、６８．４質量％以上、又は６９．４質量％以上である。また、平滑剤（Ａ）中の鉱物油の含有割合は例えば、８８，９質量％、６９．４質量％以下、６８．４質量％以下、６７．７質量％以下、６７．６質量％以下、６７．３質量％以下、６４．７質量％以下、６２．０質量％以下、５９．５質量％以下、５７．９質量％以下、又は４６．２質量％以下である。
　天然由来成分（Ｂ）は、ロジン、ロジン誘導体、テルペン樹脂、及びテルペン樹脂誘導体から選ばれる少なくとも１つである。これらの天然由来成分（Ｂ）は、１種の天然由来成分を単独で使用してもよく、２種以上の天然由来成分を組み合わせて使用してもよい。ロジンは、松から得られる天然樹脂であり、アビエチン酸又はその異性体の混合物を主成分とする。ロジンの代わりに、あるいはロジンに加えて、ロジン誘導体が使用されてもよい。ロジン誘導体としては、アビエチン酸又はその異性体の水素化、脱水素化、アミド化、エステル化合物、ＥＯ又はＰＯ付加物、グリシジルエステル化合物、アクリル化ロジン、ロジン含有ジオール、部分金属塩等が挙げられる。これらのロジン又はロジン誘導体は、軟化点、粘度、平均分子量等によって規定される市販品を適宜採用してもよい。
　テルペン樹脂は、松の木、オレンジの表皮から採取されるテルペン系化合物を原料として、カチオン重合することにより得られる。テルペン樹脂は、テルペンモノマーの単独重合体であるポリテルペン樹脂であってもよい。テルペン樹脂の代わりに、あるいはテルペン樹脂に加えて、テルペン樹脂誘導体が使用されてもよい。テルペン樹脂誘導体としては、例えばテルペンモノマーと芳香族モノマーを共重合させた芳香族変性テルペン樹脂、テルペンモノマーとフェノール類を反応させたテルペンフェノール樹脂、水素添加して得られる水添テルペン樹脂等が挙げられる。これらのテルペン樹脂又はテルペン樹脂誘導体は、軟化点等によって規定される市販品を適宜採用してもよい。
　これらの中で、ロジン又はロジン誘導体が適用されることが好ましい。ロジン又はロジン誘導体が適用されることにより、処理剤の飛散抑制効果をより向上させることができる。
　天然由来成分（Ｂ）の具体例としては、例えば重合ロジン樹脂（荒川化学工業社製「ペンセルＤ－１６０」、軟化点（環球法）：１６０℃）、重合ロジン樹脂（荒川化学工業社製「ペンセルＤ－１３５」、軟化点（環球法）：１３５℃）、ロジンエステル樹脂（荒川化学工業社製「スーパーエステルＡ－７５」、軟化点（環球法）：７５℃）、ロジンエステル樹脂（荒川化学工業社製「スーパーエステルＡ－１００」、軟化点（環球法）：１００℃）、ロジンエステル樹脂（荒川化学工業社製「スーパーエステルＡ－１２５」、軟化点（環球法）：１２５℃）、液状ロジン誘導体（荒川化学工業社製「パインクリスタルМＥ－ＧＨ」、粘度（４０℃）：８３０ｍＰａ・ｓ）、テルペンフェノール樹脂（ヤスハラケミカル社製「ＹＳポリスターＴ－１３０」、軟化点：１３０℃）、テルペンフェノール樹脂（ヤスハラケミカル社製「ＹＳポリスターＴ－１００」、軟化点：１００℃）等が挙げられる。
　処理剤は、平滑剤（Ａ）及び天然由来成分（Ｂ）の含有割合の合計を１００質量部とすると、天然由来成分（Ｂ）を０．１～３０質量部の割合で含有することが好ましい。かかる範囲に規定されることにより、本発明の効果をより向上させることができる。
　処理剤は、平滑剤（Ａ）及び天然由来成分（Ｂ）の含有割合の合計を１００質量部とすると、平滑剤（Ａ）を８０～９９．９質量部、及び天然由来成分（Ｂ）を０．１～２０質量部の割合で含有することが好ましい。かかる範囲に規定されることにより、本発明の効果をより向上させることができる。
　本実施形態の処理剤は、高級アルコールとして炭素数１２～２４の脂肪族アルコールと、炭素数１２～２４の脂肪族アルコール１モルに対して炭素数２～４のアルキレンオキサイドを１～１００モルの割合で付加させた高級アルコールのアルキレンオキサイド付加物とから選ばれる少なくとも１つのヒドロキシ化合物（Ｃ）をさらに含んでもよい。かかるヒドロキシ化合物（Ｃ）を配合することにより、後述する綾落ち防止性をより向上できる。
　炭素数１２～２４の脂肪族アルコールは、不飽和結合の有無について特に制限はなく、直鎖状又は分岐鎖状の炭化水素基を有するアルコールであってもよいし、シクロ環を有するアルコールであってもよい。分岐鎖状の炭化水素基を有するアルコールの場合、その分岐位置は特に制限されるものではなく、例えば、α位が分岐した炭素鎖であってもよいし、β位が分岐した炭素鎖であってもよい。また、第１級アルコールであっても、第２級アルコールであってもよい。
　脂肪族アルコールの具体例としては、例えばラウリルアルコール、トリデシルアルコール、ミリスチルアルコール、ペンタデシルアルコール、セタノール、ステアリルアルコール、エイコサノール、ベヘニルアルコール、テトラコサノール、オレイルアルコール、１２－エイコシルアルコール、ヘキサデセニルアルコール、エイコセニルアルコール、オクタデセニルアルコール、ドコシルアルコール、イソドデシルアルコール、イソトリデシルアルコール、イソミリスチルアルコール、イソヘキサデシルアルコール、イソステアリルアルコール、イソテトラコサノール等の１価の脂肪族アルコール等が挙げられる。
　アルキレンオキサイドを付加した化合物が用いられる場合、アルキレンオキサイドの具体例としては、例えばエチレンオキサイド、プロピレンオキサイド、ブチレンオキサイド等の炭素数２～４のアルキレンオキサイドが挙げられる。高級アルコール１モルに対するアルキレンオキサイドの付加モル数は、好ましくは１～１００モル、より好ましくは１～５０モル、さらに好ましくは１～３０モルである。なお、アルキレンオキサイドの付加モル数は、仕込み原料中における脂肪族アルコール１モルに対するアルキレンオキサイドのモル数を示す。
　これらのヒドロキシ化合物は、一種類のヒドロキシ化合物を単独で使用してもよいし、又は二種以上のヒドロキシ化合物を適宜組み合わせて使用してもよい。
　処理剤は、平滑剤（Ａ）、天然由来成分（Ｂ）、及びヒドロキシ化合物（Ｃ）の含有割合の合計を１００質量部とすると、天然由来成分（Ｂ）を０．１～３０質量部の割合で含有することが好ましい。かかる範囲に規定されることにより、本発明の効果をより向上させることができる。
　処理剤は、平滑剤（Ａ）、天然由来成分（Ｂ）、及びヒドロキシ化合物（Ｃ）の含有割合の合計を１００質量部とすると、平滑剤（Ａ）を６０～９９．８質量部、天然由来成分（Ｂ）を０．１～２０質量部、及びヒドロキシ化合物（Ｃ）を０．１～２０質量部の割合で含有することが好ましい。かかる範囲に規定されることにより、本発明の効果をより向上させることができる。
　（第２実施形態）
　次に、本発明に係る弾性繊維を具体化した第２実施形態について説明する。本実施形態の弾性繊維には、第１実施形態の処理剤が付着している。弾性繊維に対する第１実施形態の処理剤（溶媒を含まない）の付着量は、特に制限はないが、本発明の効果をより向上させる観点から０．１～１０質量％の割合で付着していることが好ましい。
　弾性繊維としては、特に制限はないが、例えばポリエステル系弾性繊維、ポリアミド系弾性繊維、ポリオレフィン系弾性繊維、ポリウレタン系弾性繊維等が挙げられる。これらの中でもポリウレタン系弾性繊維が好ましい。かかる場合に本発明の効果の発現をより高くすることができる。
　本実施形態の弾性繊維の製造方法は、第１実施形態の処理剤を弾性繊維に給油することを含む。処理剤の給油方法としては、希釈することなくニート給油法により、弾性繊維の紡糸工程において弾性繊維に付着させる方法が好ましい。付着方法としては、例えばローラー給油法、ガイド給油法、スプレー給油法等の公知の方法が適用できる。給油ローラーは通常、口金から巻き取りトラバースまでの間に位置することが一般的であり、本実施形態の製造方法にも適用できる。これらの中でも延伸ローラーと延伸ローラーの間に位置する給油ローラーにて第１実施形態の処理剤を弾性繊維、例えばポリウレタン系弾性繊維に付着させることが効果の発現が顕著であるため好ましい。
　本実施形態に適用される弾性繊維自体の製造方法は、特に限定されず、公知の方法で製造が可能である。例えば湿式紡糸法、溶融紡糸法、乾式紡糸法等が挙げられる。これらの中でも、弾性繊維の品質及び製造効率が優れる観点から乾式紡糸法が好ましく適用される。
　本実施形態の処理剤及び弾性繊維の作用及び効果について説明する。
　（１）本実施形態の処理剤は、鉱物油、シリコーン油、及びエステル油から選ばれる少なくとも１つの平滑剤（Ａ）、並びにロジン、ロジン誘導体、テルペン樹脂、及びテルペン樹脂誘導体から選ばれる少なくとも１つの天然由来成分（Ｂ）を含有する。したがって、処理剤が付与された弾性繊維を特にワインダーで巻き取る際の処理剤の飛散抑制効果を向上できる。また、処理剤が付与された弾性繊維の形状特性、特にチーズ形状に巻き取った際の形状特性を向上させることができる。また、処理剤が付与された弾性繊維の綾落ち防止性を向上させることもできる。
　なお、上記実施形態は以下のように変更してもよい。上記実施形態及び以下の変更例は、技術的に矛盾しない範囲で互いに組み合わせて実施できる。
　・上記実施形態の処理剤には、本発明の効果を阻害しない範囲内において、処理剤の品質保持のための安定化剤、制電剤、つなぎ剤、酸化防止剤、紫外線吸収剤等の通常、処理剤に用いられる成分をさらに配合してもよい。
　以下、本発明の構成及び効果をより具体的に説明するために実施例等を挙げるが、本発明がこれらの実施例に限定されるというものではない。尚、以下の実施例及び比較例の説明において、部は質量部を、また％は質量％を意味する。
　試験区分１（弾性繊維用処理剤の調製）
　各実施例、各比較例に用いた処理剤は、表１に示される各成分を使用し、下記調製方法により調製した。
　鉱物油（４０℃におけるレッドウッド粘度計での粘度が６０秒）（Ａ－１）５５部（％）及びジメチルシリコーン（１０ｃｓｔ（ｍｍ２／ｓ）、２５℃）（Ａ－３）３０部（％）と、天然由来成分として重合ロジン樹脂（Ｂ－１）７部（％）、ヒドロキシ化合物としてイソステアリルアルコール（Ｃ－１）を８部（％）とをよく混合して均一にすることで実施例１の処理剤を調製した。
　実施例２～１５，１７，１９～２２、参考例１６，１８、比較例１，２は、実施例１と同様にして平滑剤、天然由来成分、及びヒドロキシ化合物を表１に示した割合で混合することで処理剤を調製した。
　各例の処理剤中における平滑剤（Ａ）、天然由来成分（Ｂ）、及びヒドロキシ化合物（Ｃ）の各成分の種類、各成分の含有割合の合計を１００％とした場合における各成分の比率を、表１の「平滑剤（Ａ）」欄、「天然由来成分（Ｂ）」欄、「ヒドロキシ化合物（Ｃ）」欄にそれぞれ示す。
Figure JPOXMLDOC01-appb-T000001
　表１に記載するＡ－１～Ａ－４、Ｂ－１～Ｂ－８、Ｃ－１、Ｃ－２の詳細は以下のとおりである。
　（平滑剤（Ａ））
　Ａ－１：鉱物油（４０℃におけるレッドウッド粘度計での粘度が６０秒）
　Ａ－２：鉱物油（４０℃におけるレッドウッド粘度計での粘度が１００秒）
　Ａ－３：ジメチルシリコーン（１０ｃｓｔ（ｍｍ２／ｓ）、２５℃）
　Ａ－４：イソトリデシルステアラート
　（天然由来成分（Ｂ））
　Ｂ－１：重合ロジン樹脂（荒川化学工業社製「ペンセルＤ－１６０」、軟化点：１６０℃）
　Ｂ－２：重合ロジン樹脂（荒川化学工業社製「ペンセルＤ－１３５」、軟化点：１３５℃）
　Ｂ－３：ロジンエステル樹脂（荒川化学工業社製「スーパーエステルＡ－７５」、軟化点：７５℃）
　Ｂ－４：ロジンエステル樹脂（荒川化学工業社製「スーパーエステルＡ－１００」、軟化点：１００℃）
　Ｂ－５：ロジンエステル樹脂（荒川化学工業社製「スーパーエステルＡ－１２５」、軟化点：１２５℃）
　Ｂ－６：液状ロジン誘導体（荒川化学工業社製「パインクリスタルМＥ－ＧＨ」、粘度（４０℃）：８３０ｍＰａ・ｓ）
　Ｂ－７：テルペンフェノール樹脂（ヤスハラケミカル社製「ＹＳポリスターＴ－１３０」、軟化点：１３０℃）
　Ｂ－８：テルペンフェノール樹脂（ヤスハラケミカル社製「ＹＳポリスターＴ－１００」、軟化点：１００℃）
　（ヒドロキシ化合物（Ｃ））
　Ｃ－１：イソステアリルアルコール
　Ｃ－２：イソトリデシルアルコールのエチレンオキサイド３モル付加物
　試験区分２（弾性繊維の製造）
　分子量１０００のポリテトラメチレングリコールとジフェニルメタンジイソシアネートとから得たプレポリマーをジメチルホルムアミド溶液中にてエチレンジアミンにより鎖伸長反応させ、濃度３０％の紡糸ドープを得た。この紡糸ドープを紡糸口金から加熱ガス流中において乾式紡糸した。乾式紡糸したポリウレタン系弾性繊維に、試験区分１で調製した処理剤をローラーオイリング法でニート給油した。引き続いて、処理剤を付与したポリウレタン系弾性繊維をパッケージに巻き取り、２０デニール（モノフィラメント）の処理済みポリウレタン系弾性繊維を得た。処理剤の付着量の調節は、給油ローラーの回転数を調整することで何れも５％となるように行った。
　こうして得られた弾性繊維、ローラー給油した乾式紡糸ポリウレタン系弾性繊維のパッケージを用いて、飛散抑制効果、弾性繊維の形状特性、綾落ち防止性を以下に説明するようにして評価した。
　試験区分３（弾性繊維の評価）
　・飛散抑制効果
　得られた紡糸直後の乾式紡糸ポリウレタン系弾性繊維パッケージ（５００ｇ巻き）を送り出し速度１００ｍ／分、巻き取り速度２５０ｍ／分で３０分巻き取った場合のワインダー付近で認められる処理剤の飛散量を目視で観察した。飛散量の観察は、ワインダーの下に厚紙を敷き、厚紙に付着した処理剤を観察することにより行った。以下の基準で評価した結果を表１の「飛散」欄に示す。
　◎（良好）：飛散が認められない場合
　〇（可）：僅かに飛散が認められた場合
　×（不良）：かなりの飛散が認められた場合
　・形状特性の評価
　２０デニール（モノフィラメント）のポリウレタン系弾性繊維に試験区分１で調製した処理剤をローラー給油法で５．０％付着させた。そして、巻き取り速度５５０ｍ／分で、長さ５７ｍｍの円筒状紙管に、巻き幅４２ｍｍを与えるトラバースガイドを介して、サーフェイスドライブの巻取機を用いて５００ｇ巻き取り、ポリウレタン系弾性繊維のパッケージを得た。
　得られたポリウレタン系弾性繊維パッケージ（５００ｇ巻き）について、捲き幅の最大値（Ｗｍａｘ）と最小幅（Ｗｍｉｎ）を計測し、双方の差（Ｗｍａｘ－Ｗｍｉｎ）からバルジを求め、下記の基準で評価した。その結果を表１の「形状」欄に示す。
　◎（良好）：バルジが３ｍｍ未満の場合
　○（可）：バルジが３ｍｍ以上且つ６ｍｍ未満の場合
　×（不可）：バルジが６ｍｍ以上の場合
　・綾落ち防止性の評価
　得られた紡糸直後の乾式紡糸ポリウレタン系弾性繊維パッケージ（５００ｇ巻き）を送り出し速度２０ｍ／分、巻き取り速度４０ｍ／分で１０００ｍ巻き取った場合のパッケージの綾落ちによる断糸の回数を次の基準で評価した。その結果を表１の「綾落ち防止性」欄に示す。
　◎（良好）：綾落ちによる断糸が０回である場合
　○（可）：綾落ちによる断糸が１回以上且つ３回未満である場合
　×（不良）：綾落ちによる断糸が３回以上である場合
　表１の各比較例に対する各実施例の評価結果からも明らかなように、本発明の処理剤によると、処理剤が付与された弾性繊維からの処理剤の飛散を抑制できる。また、形状特性及び綾落ち防止性を向上することができる。
　本発明は以下の態様も包含する。
　（付記１）
　鉱物油、シリコーン油、及びエステル油から選ばれる少なくとも１つの平滑剤（Ａ）、並びにロジン、ロジン誘導体、テルペン樹脂、及びテルペン樹脂誘導体から選ばれる少なくとも１つの天然由来成分（Ｂ）を含有することを特徴とする弾性繊維用処理剤。
　（付記２）
　前記天然由来成分（Ｂ）が、ロジン及びロジン誘導体から選ばれる少なくとも１つである付記１に記載の弾性繊維用処理剤。
　（付記３）
　前記平滑剤（Ａ）が鉱物油を含み、前記平滑剤（Ａ）中の鉱物油の含有割合が５５～９５質量％である付記１又は２に記載の弾性繊維用処理剤。
　（付記４）
　前記平滑剤（Ａ）及び前記天然由来成分（Ｂ）の含有割合の合計を１００質量部とすると、前記天然由来成分（Ｂ）を０．１～３０質量部の割合で含有する付記１～３のいずれか一つに記載の弾性繊維用処理剤。
　（付記５）
　更に、炭素数１２～２４の脂肪族アルコールと、炭素数１２～２４の脂肪族アルコール１モルに対して炭素数２～４のアルキレンオキサイドを１～１００モルの割合で付加させた高級アルコールのアルキレンオキサイド付加物とから選ばれる少なくとも１つのヒドロキシ化合物（Ｃ）を含有する付記１～３のいずれか一つに記載の弾性繊維用処理剤。
　（付記６）
　前記平滑剤（Ａ）、前記天然由来成分（Ｂ）、及びヒドロキシ化合物（Ｃ）の含有割合の合計を１００質量部とすると、前記天然由来成分（Ｂ）を０．１～３０質量部の割合で含有する付記５に記載の弾性繊維用処理剤。
　（付記７）
　付記１～６のいずれか一つに記載の弾性繊維用処理剤が付着していることを特徴とする弾性繊維。

Claims (7)

  1. 　鉱物油、シリコーン油、及びエステル油から選ばれる少なくとも１つの平滑剤（Ａ）、並びに、テルペン樹脂及びテルペン樹脂誘導体から選ばれる少なくとも１つの天然由来成分（Ｂ）を含有することを特徴とする弾性繊維用処理剤。
  2. 　前記平滑剤（Ａ）が鉱物油を含み、前記平滑剤（Ａ）中の鉱物油の含有割合が５５～９５質量％である請求項１に記載の弾性繊維用処理剤。
  3. 　鉱物油、シリコーン油、及びエステル油から選ばれる少なくとも１つの平滑剤（Ａ）、並びに、ロジン及びロジン誘導体から選ばれる少なくとも１つの天然由来成分（Ｂ）を含有し、前記平滑剤（Ａ）が鉱物油を含み、前記平滑剤（Ａ）中の鉱物油の含有割合が５９．５～９５質量％であることを特徴とする弾性繊維用処理剤。
  4. 　前記平滑剤（Ａ）及び前記天然由来成分（Ｂ）の含有割合の合計を１００質量部とすると、前記天然由来成分（Ｂ）を０．１～３０質量部の割合で含有する請求項１～３のいずれか一項に記載の弾性繊維用処理剤。
  5. 　更に、炭素数１２～２４の脂肪族アルコール、及び炭素数１２～２４の脂肪族アルコール１モルに対し、炭素数２～４のアルキレンオキサイドを１～１００モルの割合で付加させた高級アルコールのアルキレンオキサイド付加物から選ばれる少なくとも１つのヒドロキシ化合物（Ｃ）を含有する請求項１～３のいずれか一項に記載の弾性繊維用処理剤。
  6. 　前記平滑剤（Ａ）、前記天然由来成分（Ｂ）、及びヒドロキシ化合物（Ｃ）の含有割合の合計を１００質量部とすると、前記天然由来成分（Ｂ）を０．１～３０質量部の割合で含有する請求項５に記載の弾性繊維用処理剤。
  7. 　請求項１～６のいずれか一項に記載の弾性繊維用処理剤が付着していることを特徴とする弾性繊維。
PCT/JP2021/034218 2020-09-23 2021-09-17 弾性繊維用処理剤及び弾性繊維 WO2022065209A1 (ja)