WO2022050074A1 - Moule de moulage - Google Patents

Moule de moulage Download PDF

Info

Publication number
WO2022050074A1
WO2022050074A1 PCT/JP2021/030453 JP2021030453W WO2022050074A1 WO 2022050074 A1 WO2022050074 A1 WO 2022050074A1 JP 2021030453 W JP2021030453 W JP 2021030453W WO 2022050074 A1 WO2022050074 A1 WO 2022050074A1
Authority
WO
WIPO (PCT)
Prior art keywords
molding
region
metal pipe
thermal conductivity
molding die
Prior art date
Application number
PCT/JP2021/030453
Other languages
English (en)
Japanese (ja)
Inventor
啓 山内
Original Assignee
住友重機械工業株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 住友重機械工業株式会社 filed Critical 住友重機械工業株式会社
Publication of WO2022050074A1 publication Critical patent/WO2022050074A1/fr

Abstract

Le présent moule de moulage est destiné à mouler un matériau métallique chauffé, le moule de moulage comprenant : une première région qui a une surface de moulage qui vient en contact avec le matériau métallique lors de l'exécution du moulage, la surface de moulage étant destinée à refroidir le matériau métallique ; et une seconde région qui est formée sur une section de la surface de moulage, et qui est constituée d'un matériau à faible conductivité thermique ayant une conductivité thermique inférieure par rapport à la première région.
PCT/JP2021/030453 2020-09-04 2021-08-19 Moule de moulage WO2022050074A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2020-149127 2020-09-04
JP2020149127A JP2022043699A (ja) 2020-09-04 2020-09-04 成形型

Publications (1)

Publication Number Publication Date
WO2022050074A1 true WO2022050074A1 (fr) 2022-03-10

Family

ID=80490768

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2021/030453 WO2022050074A1 (fr) 2020-09-04 2021-08-19 Moule de moulage

Country Status (2)

Country Link
JP (1) JP2022043699A (fr)
WO (1) WO2022050074A1 (fr)

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5916389A (en) * 1996-06-07 1999-06-29 Ssab Hardtech Ab Method of producing a sheet steel product such as a reinforcement element in a larger structure
JP2009220141A (ja) * 2008-03-14 2009-10-01 Marujun Co Ltd パイプ製品の製造方法及び同製造装置
JP2012000654A (ja) * 2010-06-18 2012-01-05 Linz Research Engineering Co Ltd フランジ付金属製パイプ製造装置及びその製造方法並びにブロー成形金型
JP2014533608A (ja) * 2011-11-23 2014-12-15 ティッセンクルップ スチール ヨーロッパ アクチェンゲゼルシャフトＴｈｙｓｓｅｎＫｒｕｐｐ Ｓｔｅｅｌ Ｅｕｒｏｐｅ ＡＧ 薄鋼板製ワーク、特に亜鉛めっきされた薄鋼板製ワーク、を熱間成形およびプレス硬化する方法および成形工具

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5916389A (en) * 1996-06-07 1999-06-29 Ssab Hardtech Ab Method of producing a sheet steel product such as a reinforcement element in a larger structure
JP2009220141A (ja) * 2008-03-14 2009-10-01 Marujun Co Ltd パイプ製品の製造方法及び同製造装置
JP2012000654A (ja) * 2010-06-18 2012-01-05 Linz Research Engineering Co Ltd フランジ付金属製パイプ製造装置及びその製造方法並びにブロー成形金型
JP2014533608A (ja) * 2011-11-23 2014-12-15 ティッセンクルップ スチール ヨーロッパ アクチェンゲゼルシャフトＴｈｙｓｓｅｎＫｒｕｐｐ Ｓｔｅｅｌ Ｅｕｒｏｐｅ ＡＧ 薄鋼板製ワーク、特に亜鉛めっきされた薄鋼板製ワーク、を熱間成形およびプレス硬化する方法および成形工具

Also Published As

Publication number Publication date
JP2022043699A (ja) 2022-03-16

Similar Documents

Publication Publication Date Title
US6914225B2 (en) Apparatus and methods for single sheet forming using induction heating
CA2933110C (fr) Dispositif de moulage
JP6381967B2 (ja) 成形装置及び成形方法
JP6401953B2 (ja) 成形装置及び成形方法
KR20090037995A (ko) 예열에 의해 셀프 피어싱 리벳을 사용하여 금속요소를 접합하는 방법 및 장치
JP6240564B2 (ja) 成形装置及び成形装置の部品の交換方法
TWI597110B (zh) Mechanical joining devices and mechanical joining methods
US7823430B2 (en) Open press thermal gap for QPF forming tools
JP2016129891A (ja) フランジ付アルミニウム製パイプを製造する為のブロー成型金型及びその金型を備えたフランジ付アルミニウム製パイプ装置、並びにフランジ付アルミニウム製パイプの製造方法
CN113573824A (zh) 成型装置及成型方法
JP6417138B2 (ja) 成形装置
CA3052835A1 (fr) Dispositif de moulage et procede de moulage
WO2022050074A1 (fr) Moule de moulage
JP2019069473A (ja) 成形装置
EP4116005A1 (fr) Dispositif de moulage et procédé de moulage
WO2022034843A1 (fr) Dispositif de moulage et tuyau métallique
CN116801997A (zh) 成型装置及金属管
US20240157427A1 (en) Molding device
JP2024064701A (ja) 成形装置、及び金属部材
WO2024089990A1 (fr) Dispositif de mise en forme
US20240149323A1 (en) Molding device
CA3235296A1 (fr) Dispositif de moulage et procede de moulage
WO2024089989A1 (fr) Dispositif de moulage et élément métallique
WO2022186055A1 (fr) Système de moulage
WO2021182349A1 (fr) Système de moulage et procédé de moulage

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 21864132

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 21864132

Country of ref document: EP

Kind code of ref document: A1