WO2022043370A1 - Feuille d'emballage thermoscellable - Google Patents

Feuille d'emballage thermoscellable Download PDF

Info

Publication number
WO2022043370A1
WO2022043370A1 PCT/EP2021/073479 EP2021073479W WO2022043370A1 WO 2022043370 A1 WO2022043370 A1 WO 2022043370A1 EP 2021073479 W EP2021073479 W EP 2021073479W WO 2022043370 A1 WO2022043370 A1 WO 2022043370A1
Authority
WO
WIPO (PCT)
Prior art keywords
layer
sheet
ethylene
grammage
packaging sheet
Prior art date
Application number
PCT/EP2021/073479
Other languages
English (en)
Inventor
Peter Johansen
Steen MIDTIBY
Original Assignee
Danapak Flexibles A/S
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from EP20193463.5A external-priority patent/EP3960446A1/fr
Application filed by Danapak Flexibles A/S filed Critical Danapak Flexibles A/S
Priority to EP21766636.1A priority Critical patent/EP4204230A1/fr
Publication of WO2022043370A1 publication Critical patent/WO2022043370A1/fr

Abstract

Feuille d'emballage thermoscellable comprenant une feuille de base de papier, une couche d'éthylène thermoscellable, une couche de polyamide et une couche de liaison de revêtement par coextrusion de polymère, la couche de liaison, la couche de polyamide et la couche d'éthylène ayant été revêtues par coextrusion sur une seconde surface de la feuille de base, la feuille de base constituant au moins 73 % en poids d'un grammage total de la feuille d'emballage, et le revêtement par coextrusion ne constituant pas plus de 27 % en poids d'un grammage total de la feuille d'emballage, la feuille de base présentant un grammage de 60 à 150 g/m2, et le revêtement par coextrusion présentant un grammage de 5 à 32 g/m2, la couche de liaison présentant un grammage de 1 à 30 g/m2, la couche de polyamide présentant un grammage de 1 à 30 g/m2, la couche d'éthylène présentant un grammage de 1 à 30 g/m2, et la couche d'éthylène étant essentiellement constituée d'un copolymère d'éthylène pouvant être revêtu par coextrusion et d'au moins un comonomère acide, ledit comonomère constituant de 5 à 20 % en poids de la couche d'éthylène.
PCT/EP2021/073479 2020-08-28 2021-08-25 Feuille d'emballage thermoscellable WO2022043370A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
EP21766636.1A EP4204230A1 (fr) 2020-08-28 2021-08-25 Feuille d'emballage thermoscellable

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
EP20193463.5A EP3960446A1 (fr) 2020-08-28 2020-08-28 Feuille d'emballage thermoscellable
EP20193463.5 2020-08-28
DKPA202070850 2020-12-17
DKPA202070850 2020-12-17

Publications (1)

Publication Number Publication Date
WO2022043370A1 true WO2022043370A1 (fr) 2022-03-03

Family

ID=77693505

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/EP2021/073479 WO2022043370A1 (fr) 2020-08-28 2021-08-25 Feuille d'emballage thermoscellable

Country Status (2)

Country Link
EP (1) EP4204230A1 (fr)
WO (1) WO2022043370A1 (fr)

Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
FR2462998A1 (fr) * 1979-08-10 1981-02-20 Scheuch Folien Papier Kg Feuille multicouche pour la fermeture de recipients
US20040245138A1 (en) * 2001-10-15 2004-12-09 Tapani Penttinen Package lid, method for manufacturing the same and package sealed with the lid
WO2006058952A1 (fr) 2004-11-30 2006-06-08 Walki Wisa Oy Matiere multicouche et emballage de produit thermosoude constitue de celle-ci
WO2011160627A1 (fr) 2010-06-22 2011-12-29 Danapak Flexibles A/S Feuille, procédé de fabrication et d'utilisation d'une feuille comme couvercle pour emballages
WO2013075713A1 (fr) 2011-11-22 2013-05-30 Danapak Flexibles A/S Feuille, procédé de fabrication et d'utilisation d'une feuille comme couvercle pour emballages
JP2017056722A (ja) * 2015-09-17 2017-03-23 大日本印刷株式会社 積層体及びそれよりなる蓋材
WO2018215606A1 (fr) 2017-05-24 2018-11-29 Danapak Flexibles A/S Procédé de fabrication de stratifiés de feuille destinés à être pré-poinçonnés sur un couvercle de feuille destiné à être fixé à un récipient

Patent Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
FR2462998A1 (fr) * 1979-08-10 1981-02-20 Scheuch Folien Papier Kg Feuille multicouche pour la fermeture de recipients
US20040245138A1 (en) * 2001-10-15 2004-12-09 Tapani Penttinen Package lid, method for manufacturing the same and package sealed with the lid
WO2006058952A1 (fr) 2004-11-30 2006-06-08 Walki Wisa Oy Matiere multicouche et emballage de produit thermosoude constitue de celle-ci
WO2011160627A1 (fr) 2010-06-22 2011-12-29 Danapak Flexibles A/S Feuille, procédé de fabrication et d'utilisation d'une feuille comme couvercle pour emballages
WO2013075713A1 (fr) 2011-11-22 2013-05-30 Danapak Flexibles A/S Feuille, procédé de fabrication et d'utilisation d'une feuille comme couvercle pour emballages
JP2017056722A (ja) * 2015-09-17 2017-03-23 大日本印刷株式会社 積層体及びそれよりなる蓋材
WO2018215606A1 (fr) 2017-05-24 2018-11-29 Danapak Flexibles A/S Procédé de fabrication de stratifiés de feuille destinés à être pré-poinçonnés sur un couvercle de feuille destiné à être fixé à un récipient

Also Published As

Publication number Publication date
EP4204230A1 (fr) 2023-07-05

Similar Documents

Publication Publication Date Title
US8852725B2 (en) Vessel closing laminate
EP1843951B1 (fr) Element de scellement a tirette avec repartition de chaleur amelioree destine a un recipient
US10071841B2 (en) Scored package
US20160185485A1 (en) Tabbed Sealing Member With Improved Heat Distribution For A Continer
US20010048178A1 (en) Lids for closing off containers
MXPA00009933A (es) Capa sellante para tapa de contenedor.
JP5822956B2 (ja) 低吸着性ラミネート用多層フィルム、これを用いた複合フィルム及び包装材
US20240116272A1 (en) Fracture film for peelable membrane containers
JP5991504B2 (ja) 易貫通性蓋材
JP2006282257A (ja) 紙カップ
US6224973B1 (en) Multi-layer sheet suitable as sealable sheet
US20200079000A1 (en) A method for making sheet laminates for being pre-punched to a sheet lid to be attached to a container
EP3960446A1 (fr) Feuille d'emballage thermoscellable
WO2022043370A1 (fr) Feuille d'emballage thermoscellable
JP2003237816A (ja) 蓋 材
JP5948912B2 (ja) 易引裂き性エンボスフィルム及びこれを用いた包装材料
US20230311458A1 (en) A heat-sealable packaging film
JP4152037B2 (ja) 積層体及び密封容器
JP2003226349A (ja) 蓋材及びその製造方法
AU2012238195B2 (en) Vessel closing laminate
JP2003267422A (ja) 蓋材及びその製造方法
JPS5924700Y2 (ja) カツプ状易開封性容器
JP2006282254A (ja) 紙カップ

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 21766636

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

ENP Entry into the national phase

Ref document number: 2021766636

Country of ref document: EP

Effective date: 20230328