WO2021201089A1 - 中空マイクロバルーン - Google Patents
中空マイクロバルーン Download PDFInfo
- Publication number
- WO2021201089A1 WO2021201089A1 PCT/JP2021/013798 JP2021013798W WO2021201089A1 WO 2021201089 A1 WO2021201089 A1 WO 2021201089A1 JP 2021013798 W JP2021013798 W JP 2021013798W WO 2021201089 A1 WO2021201089 A1 WO 2021201089A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- component
- molecule
- resin
- acid
- compound
- Prior art date
Abstract
本発明の中空マイクロバルーンは、分子内に少なくとも2つの重合性官能基を有するポリロタキサンモノマーと、前記分子内に少なくとも2つの重合性官能基を有するポリロタキサンモノマー以外の重合性モノマーとを含む重合性組成物を重合させた樹脂からなる中空マイクロバルーンである。 本発明の中空マイクロバルーンを用いることにより、優れた研磨特性と耐久性を有するCMP用研磨パッドを提供することができる。
Description
本発明は、中空マイクロバルーンに関する。
マイクロバルーンは、従来から、スキンケア成分、香料成分、染料成分、鎮痛成分、消臭成分、抗酸化成分、殺菌成分、蓄熱成分などを内包したマイクロバルーン、または、マイクロバルーン内部が中空である中空マイクロバルーンとして、農薬、医薬、香料、液晶、接着剤、電子材料部品、建築材料などの多くの分野において使用されている。
特に近年、ウエハ研磨に用いられるポリウレタン(ウレア)製CMP(Chemical Mechanical Polishing)用研磨パッドに、細孔を設ける目的で、中空マイクロバルーンが検討されている。
従来、CMP用研磨パッドに用いられる中空マイクロバルーンとして、ポリウレタン(ウレア)への分散性向上のため、中空マイクロバルーンの表面に無機粒子をまぶした塩化ビニリデン樹脂等のマイクロバルーンが知られていたが、該無機粒子がウエハへのディフェクトの要因となる可能性があった。
そのため、本発明者等は、高弾性、且つ、ポリウレタン(ウレア)樹脂との相容性が良好なポリウレタン(ウレア)樹脂膜で形成された中空マイクロバルーンを、CMP用研磨パッド中に用いることにより、優れた研磨特性を有するCMP用研磨パッドを提案している(特許文献1参照)。
しかし、近年の半導体配線の微細化により、さらに高性能なCMP用研磨パッドが求められており、中空マイクロバルーンの耐久性や樹脂物性にもさらなる改良が求められている。
一方、CMP用研磨パッド用途以外の用途においても、マイクロバルーンとしての樹脂物性、たとえば耐久性の向上が求められており、特許文献2には、蓄熱材量を内包したポリウレタン(ウレア)マイクロバルーンにおいて、ポリウレタン(ウレア)にポリロタキサンを含有させることによって耐久性を向上させ、蓄熱材料の漏洩を防ぐ技術が開示されている。
しかしながら、本発明者らが検討した結果、特許文献2に記載の方法では、蓄熱材量を内包したマイクロバルーンの場合、効果があるが、中空マイクロバルーンに適用した場合、満足する耐久性を得ることができないことが判明した。
したがって、本発明の目的は、研磨特性のみならず、優れた耐久性を付与できる中空マイクロバルーンの提供にある。
本発明者等は、上記課題を解決するために鋭意検討した結果、分子内に少なくとも2つの重合性官能基を有するポリロタキサンモノマーと、前記分子内に少なくとも2つの重合性官能基を有するポリロタキサンモノマー以外の重合性モノマーとを含む重合性組成物を重合させた樹脂からなる中空マイクロバルーンを用いることにより、上記課題を解決することを見出し、本発明を完成するに至った。
すなわち、本発明は、分子内に少なくとも2つの重合性官能基を有するポリロタキサンモノマーと、前記分子内に少なくとも2つの重合性官能基を有するポリロタキサンモノマー以外の重合性モノマーとを含む重合性組成物を重合させた樹脂からなる中空マイクロバルーンである。
また、本発明は、該中空マイクロバルーンを含んでなるCMP用研磨パッドも提供するものである。
これらの本発明は、以下に示す通りである。
これらの本発明は、以下に示す通りである。
[1](A)分子内に少なくとも2つの重合性官能基を有するポリロタキサンモノマーと、(B)前記(A)分子内に少なくとも2つの重合性官能基を有するポリロタキサンモノマー以外の重合性モノマーとを含む重合性組成物を重合させた樹脂からなる中空マイクロバルーン。
[2]前記重合性組成物の(A)分子内に少なくとも2つの重合性官能基を有するポリロタキサンモノマーの含有量が、(A)分子内に少なくとも2つの重合性官能基を有するポリロタキサンモノマーの含有量と(B)前記(A)分子内に少なくとも2つの重合性官能基を有するポリロタキサンモノマー以外の重合性モノマーの合計100質量部に対し、1~50質量部である上記[1]に記載の中空マイクロバルーン。
[3]前記樹脂が、ウレタン(ウレア)樹脂、メラミン樹脂、尿素樹脂、及びアミド樹脂からなる群から選択される少なくとも1種以上である上記[1]または[2]に記載の中空マイクロバルーン。
[4]前記(A)分子内に少なくとも2つの重合性官能基を有するポリロタキサンモノマーの重合性官能基が、水酸基またはアミノ基である上記[1]~[3]のいずれか1項に記載の中空マイクロバルーン。
[5]前記(A)分子内に少なくとも2つの重合性官能基を有するポリロタキサンモノマーの環状分子の少なくとも一部に、側鎖が導入されている上記[1]~[4]のいずれか1項に記載の中空マイクロバルーン。
[6]前記(A)分子内に少なくとも2つの重合性官能基を有するポリロタキサンモノマーの側鎖の数平均分子量が5,000以下である上記[5]に記載の中空マイクロバルーン。
[7]前記(A)分子内に少なくとも2つの重合性官能基を有するポリロタキサンモノマーの重合性官能基が、前記(A)分子内に少なくとも2つの重合性官能基を有するポリロタキサンモノマーの側鎖に導入されてなる上記[5]または[6]に記載の中空マイクロバルーン。
[8]上記[1]~[7]のいずれか1項に記載の中空マイクロバルーンを含んでなるCMP用研磨パッド。
[2]前記重合性組成物の(A)分子内に少なくとも2つの重合性官能基を有するポリロタキサンモノマーの含有量が、(A)分子内に少なくとも2つの重合性官能基を有するポリロタキサンモノマーの含有量と(B)前記(A)分子内に少なくとも2つの重合性官能基を有するポリロタキサンモノマー以外の重合性モノマーの合計100質量部に対し、1~50質量部である上記[1]に記載の中空マイクロバルーン。
[3]前記樹脂が、ウレタン(ウレア)樹脂、メラミン樹脂、尿素樹脂、及びアミド樹脂からなる群から選択される少なくとも1種以上である上記[1]または[2]に記載の中空マイクロバルーン。
[4]前記(A)分子内に少なくとも2つの重合性官能基を有するポリロタキサンモノマーの重合性官能基が、水酸基またはアミノ基である上記[1]~[3]のいずれか1項に記載の中空マイクロバルーン。
[5]前記(A)分子内に少なくとも2つの重合性官能基を有するポリロタキサンモノマーの環状分子の少なくとも一部に、側鎖が導入されている上記[1]~[4]のいずれか1項に記載の中空マイクロバルーン。
[6]前記(A)分子内に少なくとも2つの重合性官能基を有するポリロタキサンモノマーの側鎖の数平均分子量が5,000以下である上記[5]に記載の中空マイクロバルーン。
[7]前記(A)分子内に少なくとも2つの重合性官能基を有するポリロタキサンモノマーの重合性官能基が、前記(A)分子内に少なくとも2つの重合性官能基を有するポリロタキサンモノマーの側鎖に導入されてなる上記[5]または[6]に記載の中空マイクロバルーン。
[8]上記[1]~[7]のいずれか1項に記載の中空マイクロバルーンを含んでなるCMP用研磨パッド。
本発明の中空マイクロバルーンは、分子内に少なくとも2つの重合性官能基を有するポリロタキサンを含有する重合性組成物を重合させた樹脂からなることが特徴である。そうすることで、中空マイクロバルーンに優れた耐久性を付与することが可能となる。
また、このような中空マイクロバルーンを含んだCMP用研磨パッドにより、優れた研磨特性を発現することが可能である。たとえば高い研磨レートやウエハへの生じるディフェクトを低減することが可能となる。
その作用は明らかではないが、以下のように推察している。
一般的に、ポリロタキサンは、ポリロタキサンの環状分子が軸分子上を動くことで、応力集中部位を緩和できる応力分散性能や、変形に対する優れた弾性回復性能が付与されることが知られている。
本発明においては、単にポリロタキサンを、中空マイクロバルーンを構成する樹脂に配合するのではなく、ポリロタキサンを、中空マイクロバルーンを構成する樹脂の一構成成分とすることにより、樹脂全体に前記した応力分散性能や弾性回復性能が付与され、優れた耐久性を有する中空マイクロバルーンとすることができる。また、このような中空マイクロバルーンをCMP用研磨パッドに応用することで、前記した応力分散性能や弾性回復性能により、CMP用研磨パッドの研磨面に細孔を形成する役割のみならず、CMP用研磨パッドが耐久性を有し、優れた研磨特性のみならず、優れた耐摩耗性を発現させることが可能となる。さらには、この特性により、研磨の際に排出される中空マイクロバルーンの研磨かすによって生じるウエハへのディフェクトも低減させることが可能となる。
さらに、本発明の中空マイクロバルーンは、CMP用研磨パッド用途以外にも、感熱記録材料、農薬、医薬、香料、液晶、接着剤、電子材料部品、建築材料などの多くの分野において利用が可能である。
本発明の中空マイクロバルーンは、(A)分子内に少なくとも2つの重合性官能基を有するポリロタキサンモノマー(以下、「(A)ポリロタキサンモノマー」、または「(A)成分」ともいう。)と、(B)前記(A)分子内に少なくとも2つの重合性官能基を有するポリロタキサンモノマー以外の重合性モノマー(以下、「(B)重合性モノマー」、または「(B)成分」ともいう。)とを含む重合性組成物を重合させた樹脂からなる中空マイクロバルーンである。なお前記樹脂は、中空マイクロバルーンの外殻部を形成するものである。まず、(A)ポリロタキサンモノマーについて説明する。
<(A)ポリロタキサンモノマー>
ポリロタキサンは公知の化合物であり、鎖状の軸分子と環状分子とから形成されている複合分子構造を有している。即ち、鎖状の軸分子を環状分子が包接しており、環状分子が有する環の内部を軸分子が貫通している構造となっている。そのため、環状分子は、軸分子上を自由にスライドし得るので、通常、軸分子の両端には、嵩高い末端基が形成されており、環状分子の軸分子からの脱落が防止されている。
ポリロタキサンは公知の化合物であり、鎖状の軸分子と環状分子とから形成されている複合分子構造を有している。即ち、鎖状の軸分子を環状分子が包接しており、環状分子が有する環の内部を軸分子が貫通している構造となっている。そのため、環状分子は、軸分子上を自由にスライドし得るので、通常、軸分子の両端には、嵩高い末端基が形成されており、環状分子の軸分子からの脱落が防止されている。
なお、一般的に、上記構造において、環状分子が複数存在する場合を「ポリロタキサン」というが、本発明においては、環状分子が一つの場合も含めて「ポリロタキサン」という。
前記ポリロタキサンは、前記したとおり環状分子が軸分子上をスライド可能である。そのため、スライディング弾性と呼ばれる性能を発現し、優れた特性を発現できるものと考えられる。本発明においては、中空マイクロバルーンを構成する樹脂の一構成成分としてポリロタキサンを用いることにより、優れた耐久性等の特性を中空マイクロバルーンに付与することが可能となる。
本発明で使用する(A)ポリロタキサンモノマーは、公知の方法、たとえば、国際公開第WO2015/068798号に記載の方法で合成することができる。上記(A)成分の構成について詳細に説明する。
本発明で使用する(A)ポリロタキサンモノマーの軸分子としては、環状分子が有する環を貫通し得れば特に限定なく、一般的に、直鎖状あるいは分岐鎖状のポリマーが用いられる。
このような軸分子に用いられるポリマーとしては、ポリビニルアルコール、ポリビニルピロリドン、セルロース系樹脂(カルボキシメチルセルロース、ヒドロキシエチルセルロース、ヒドロキシプロピルセルロースなど)、ポリアクリルアミド、ポリエチレンオキサイド、ポリエチレングリコール、ポリプロピレングリコール、ポリビニルアセタール、ポリビニルメチルエーテル、ポリアミン、ポリエチレンイミン、カゼイン、ゼラチン、でんぷん、オレフィン系樹脂(ポリエチレン、ポリプロピレンなど)、ポリエステル、ポリ塩化ビニル、スチレン系樹脂(ポリスチレン、アクリロニトリル-スチレン共重合樹脂など)、アクリル系樹脂(ポリ(メタ)アクリレート酸、ポリメチルメタクリレート、ポリメチルアクリレート、アクリロニトリル-メチルアクリレート共重合樹脂など)、ポリカーボネート、ポリウレタン、塩化ビニル-酢酸ビニル共重合樹脂、ポリビニルブチラール、ポリイソブチレン、ポリテトラヒドロフラン、ポリアニリン、アクリロニトリル-ブタジエン-スチレン共重合体(ABS樹脂)、ポリアミド(ナイロンなど)、ポリイミド、ポリジエン(ポリイソプレン、ポリブタジエンなど)、ポリシロキサン(ポリジメチルシロキサンなど)、ポリスルホン、ポリイミン、ポリ無水酢酸、ポリ尿素、ポリスルフィド、ポリフォスファゼン、ポリケトンポリフェニレン、ポリハロオレフィン等を挙げることができる。これらのポリマーは、適宜共重合されていてもよく、また変性されたものであってもよい。
本発明において、軸分子に用いられるポリマーとして好適なものは、ポリエチレングリコール、ポリイソプレン、ポリイソブチレン、ポリブタジエン、ポリプロピレングリコール、ポリテトラヒドロフラン、ポリジメチルシロキサン、ポリエチレン、ポリプロピレン、ポリビニルアルコールまたはポリビニルメチルエーテルであり、ポリエチレングリコールが最も好適である。
上記した軸分子に用いられるポリマーの分子量は、特に制限されないが、大きすぎると、その他の重合性単量体等と混合した際に、粘度が増大し、扱いが困難となるばかりか、相溶性が悪くなる傾向にある。このような観点から、軸分子の重量平均分子量Mwは、400~100000が好適であり、1000~50000がより好適であり、特に2000~30000の範囲にあることがさらに好適である。なお、この重量平均分子量Mwは、後述する実施例で記載したゲルパーミエーションクロマトグラフィー(GPC)測定方法で測定した値である。
上記した軸分子に用いられるポリマーは、環状分子の環内を貫通した環が離脱しないように、両末端に嵩高い基を有することが好ましい。前記軸分子に用いられるポリマーの両末端に形成される嵩高い基としては、軸分子からの環状分子の脱離を防ぐ基であれば、特に制限されないが、嵩高さの観点から、アダマンチル基、トリチル基、フルオレセイニル基、ジニトロフェニル基、およびピレニル基体を挙げることができ、特に導入のし易さなどの点で、アダマンチル基が好適である。
一方、本発明で使用する(A)ポリロタキサンモノマーの環状分子としては、前記した軸分子を包接し得る大きさの環を有するものであればよく、このような環としては、シクロデキストリン環、クラウンエーテル環、ベンゾクラウン環、ジベンゾクラウン環、およびジシクロヘキサノクラウン環を挙げることができ、特にシクロデキストリン環が好ましい。
前記シクロデキストリン環には、α体(環内径0.45~0.6nm)、β体(環内径0.6~0.8nm)、γ体(環内径0.8~0.95nm)がある。また、これらの混合物を使用することもできる。本発明では、特にα-シクロデキストリン環、およびβ-シクロデキストリン環が好ましく、α-シクロデキストリン環が最も好ましい。
上記した環状分子は、1つの軸分子に一つ以上の環状分子が包接することとなる。そして、1つの軸分子に包接し得る環状分子の最大包接数を1.0としたとき、環状分子の包接数は最大でも0.8以下であることが好ましい。環状分子の包接数が多すぎると、一つの軸分子に対して環状分子が密に存在するようになる。その結果、可動性(スライド幅)が低下する傾向にある。加えて、前記(A)ポリロタキサンモノマー自体の分子量が増大する。そのため、重合性組成物に使用した場合、該重合性組成物のハンドリング性が低下する傾向にある。そのため、より好ましくは、1つの軸分子が少なくとも2つ以上の環状分子で包接されており、環状分子の包接数は最大でも0.5以下の範囲にあることが好ましい。
なお、一つの軸分子に対する環状分子の最大包接数は、軸分子の長さおよび環状分子の環の厚みから算出することができる。たとえば、軸分子の鎖状部分がポリエチレングリコールで形成され、環状分子がα-シクロデキストリン環である場合を例にとると、次のようにして最大包接数が算出される。即ち、ポリエチレングリコールの繰り返し単位[-CH2-CH2O-]の2つ分がα-シクロデキストリン環1つの厚みに近似する。したがって、このポリエチレングリコールの分子量から繰り返し単位数を算出し、この繰り返し単位数の1/2が環状分子の最大包接数として求められる。この最大包接数を1.0とし、環状分子の包接数が前述した範囲に調製されることとなる。
上記の環状分子は、単独で使用することができ、また複数種を併用することもできる。
本発明で使用する(A)ポリロタキサンモノマーの重合性官能基は、環状分子が有しているのが好ましい。そうすることでポリロタキサンの特徴である環状分子のスライディング効果を十分に発現することが可能となり、優れた力学特性を発現できる。
前記重合性官能基としては、他の重合性モノマーと重合できる基であれば特に限定されない。中でも、本発明において、好ましい重合性官能基は、水酸基、アミノ基からなる群より選ばれる少なくとも1種の基である。これらの重合性官能基を有することで、後述するウレタン(ウレア)樹脂、メラミン樹脂、尿素樹脂、またはアミド樹脂中に(A)ポリロタキサンモノマーを導入することが可能となる。
環状分子中の重合性官能基は、たとえば、環状分子がシクロデキストリン環であれば、環の水酸基を重合性官能基として使用することが可能である。また、シクロデキストリン環の水酸基を公知の手法でアミノ基とすることも可能である。たとえば、水酸基をスルホン酸エステル化したシクロデキストリン誘導体を、アジ化ナトリウムと反応させ、最後にアジド基をトリフェニルホスフィンで還元することにより、アミノ基を導入することができる(ナノマテリアル・シクロデキストリン(シクロデキストリン学会編、米田出版)参照)。
前記(A)ポリロタキサンモノマーにおいて、樹脂中にポリロタキサン部分が導入されて優れた効果を発揮するためには、重合性官能基の数は、2つ以上導入されていれば、特に制限されるものではない。
本発明で使用する(A)ポリロタキサンモノマーにおいて、より優れた特性を発現させるために、(B)重合性モノマーとの相溶性を調節することを勘案すると、前記した環状分子に側鎖が導入されていることが好ましい。
さらに、(A)ポリロタキサンモノマーが側鎖を有する場合、該側鎖に重合性官能基を有するのが好ましい。そうすることで、該側鎖を介して(B)重合性モノマーと結合するため、より優れた特性を発現することが可能となる。
上記側鎖としては、特に制限されるものではないが、炭素数が3~20の範囲にある有機鎖の繰り返しにより形成されていることが好適である。また、側鎖の種類や数平均分子量が異なるものが環状分子に導入されていてもよい。このような側鎖の数平均分子量は好ましくは5000以下であり、より好ましくは45~5,000、さらに好ましくは55~3,000、さらに好ましくは100~1,500の範囲である。この側鎖の数平均分子量は、側鎖の導入時に使用する物質の量により調製ができ、計算により求めることができる。また、得られた(A)ポリロタキサンモノマーから求める場合には、1H-NMRの測定から求めることができる。
側鎖の数平均分子量を上記した下限値以上とすることにより、特性の向上への寄与が大きくなる。一方、側鎖が数平均分子量を上記した上限値以下とすることにより、ハンドリング性がよく、中空マイクロバルーンの収率が向上する。
前記側鎖は、通常、環状分子が有する反応性官能基を利用し、この反応性官能基を修飾することによって導入される。中でも、本発明においては、環状分子が水酸基を有していて、該水酸基を修飾して側鎖が導入された(A)ポリロタキサンモノマーが好ましい。たとえば、α-シクロデキストリン環は、反応性官能基として18個の水酸基を有している。この水酸基を修飾して側鎖が導入すればよい。すなわち、1つのα-シクロデキストリン環に対しては最大で18個の側鎖を導入できることとなる。
前記側鎖の機能を十分に発揮させるためには、環状分子が有する全反応性官能基数の4~70%(以下、この値を修飾度ともいう)が、側鎖で修飾されていることが好ましい。なお、この修飾度は、平均値である。
また、下記に詳述するが、環状分子の反応性官能基(たとえば水酸基)は、側鎖が有する反応性官能基(たとえば、水酸基)よりも反応性が低い。そのため、修飾度が100%でなくても、上記範囲であれば、より優れた効果を発揮する。
なお、本発明においては、水酸基が重合性官能基に該当する場合には、以下のように見なす。たとえば、環状分子がシクロデキストリン環であって、該シクロデキストリン環が有する水酸基において、側鎖が導入されていない水酸基も、重合性官能基と見なすものとする。ちなみに、上記α-シクロデキストリン環の18個のOH基の内の9個に側鎖が結合している場合、その修飾度は50%となる。
本発明において、上記側鎖は、分子量が前述した範囲内であれば、直鎖状であってもよいし、分枝状であってもよい。側鎖の導入については、公知の方法、たとえば、国際公開第WO2015/159875号に開示されている手法や化合物を適宜使用すればよい。具体的には、開環重合;ラジカル重合;カチオン重合;アニオン重合;原子移動ラジカル重合、RAFT重合、NMP重合などのリビングラジカル重合などが利用できる。上記手法により、適宜選択された化合物を前記環状分子が有する反応性官能基に反応させることによって適宜の大きさの側鎖を導入することができる。
たとえば、開環重合により、環状エーテル、環状シロキサン、環状ラクトン、環状ラクタム、環状アセタール、環状アミン、環状カーボネート、環状イミノエーテル、環状チオカーボネート等の環状化合物に由来する側鎖を導入することができる。
該環状化合物の中でも、反応性が高く、さらには大きさ(分子量)の調製が容易であるという観点から、環状エーテル、環状ラクトン、環状ラクタムを用いることが好ましい。環状ラクトンや環状エーテル等の環状化合物を開環重合して導入した側鎖は、該側鎖の末端に水酸基が導入されることとなり、環状ラクタムを開環重合して導入した側鎖は、該側鎖の末端にアミノ基が導入されることとなる。好適な環状エーテル、環状ラクトンは国際公開第WO2015/159875号に開示されている。
中でも、本発明において、好適な環状ラクタムとしては、
4-ベンゾイルオキシ-2-アゼチジノン等の4員環ラクタム、
γ-ブチロラクタム、2-アザビシクロ(2,2,1)ヘプタ-5-エン-3-オン、5-メチル-2-ピロリドン等の5員環ラクタム、
2-ピペリドン-3-カルボン酸エチル等の6員環ラクタム、
ε-カプロラクタム、DL-α-アミノ-ε-カプロラクタム等の7員環ラクタム、
ω-ヘプタラクタムが挙げられる。なかでも、ε-カプロラクタム、γ-ブチロラクタム、DL-α-アミノ-ε-カプロラクタムが好ましく、より好ましくはε-カプロラクタムがより好ましい。
4-ベンゾイルオキシ-2-アゼチジノン等の4員環ラクタム、
γ-ブチロラクタム、2-アザビシクロ(2,2,1)ヘプタ-5-エン-3-オン、5-メチル-2-ピロリドン等の5員環ラクタム、
2-ピペリドン-3-カルボン酸エチル等の6員環ラクタム、
ε-カプロラクタム、DL-α-アミノ-ε-カプロラクタム等の7員環ラクタム、
ω-ヘプタラクタムが挙げられる。なかでも、ε-カプロラクタム、γ-ブチロラクタム、DL-α-アミノ-ε-カプロラクタムが好ましく、より好ましくはε-カプロラクタムがより好ましい。
本発明において、好適な環状ラクトンとしては、ε-カプロラクトン、α-アセチル-γ-ブチロラクトン、α-メチル-γ-ブチロラクトン、γ-バレロラクトン、γ-ブチロラクトン等が挙げられ、もっとも好ましいものはε-カプロラクトンである。
また、開環重合により環状化合物を反応させて側鎖を導入する場合、環状分子の反応性官能基(たとえば水酸基)は反応性に乏しく、特に立体障害などにより大きな分子を直接反応させることが困難な場合がある。このような場合には、たとえば、前記したカプロラクトンなどを反応させるために、一旦、プロピレンオキシドなどの低分子化合物を環状分子の反応性官能基と反応させてヒドロキシプロピル化を行ない、反応性に富んだ官能基を導入する。その後、前記した環状化合物を用いた開環重合により、側鎖を導入するという手段を採用することができる。この場合、ヒドロキシプロピル化した部分も側鎖と見なすことができる。
この他、開環重合により、前述した環状アセタール、環状アミン、環状カーボネート、環状イミノエーテル等の環状化合物に由来する側鎖を導入することにより、水酸基、アミノ基等重合性官能基を有する側鎖を導入することができる。これら環状化合物の具体例は、国際公開第2015/068798号に記載されているものである。
また、ラジカル重合を利用して環状分子に側鎖を導入する方法は、以下の通りである。前記環状分子は、ラジカル開始点となる活性部位を有していない場合がある。この場合、ラジカル重合性化合物を反応させるに先立って、環状分子が有している官能基(たとえば、水酸基)にラジカル開始点を形成するための化合物を反応させて、ラジカル開始点となる活性部位を形成しておく必要がある。
上記のようなラジカル開始点を形成するための化合物としては、有機ハロゲン化合物が代表的である。たとえば、2-ブロモイソブチリルブロミド、2-ブロモブチル酸、2-ブロモプロピオン酸、2-クロロプロピオン酸、2-ブロモイソ酪酸、エピクロロヒドリン、エピブロモヒドリン、2-クロロエチルイソシアネートなどを挙げることができる。すなわち、これら有機ハロゲン化合物は、環状分子が有している官能基との反応により、該環状分子に結合して、該環状分子にハロゲン原子を含む基(有機ハロゲン化合物残基)が導入される。この有機ハロゲン化合物残基には、ラジカル重合に際して、ハロゲン原子の移動等によりラジカルが生成し、これがラジカル重合開始点となって、ラジカル重合が進行することとなる。
また、上記した有機ハロゲン化合物残基は、たとえば環状分子が有している水酸基に、アミン、イソシアネート、イミダゾールなどの官能基を有する化合物を反応させ、水酸基以外の他の官能基を導入し、このような他の官能基に前記した有機ハロゲン化合物を反応させて導入することもできる。
また、ラジカル重合により側鎖を導入するために用いるラジカル重合性化合物としては、エチレン性不飽和結合を有する基、たとえば、(メタ)アクリレート基、ビニル基、スチリル基等の官能基を少なくとも1種有する化合物(以下、エチレン性不飽和モノマーともいう)が好適に使用される。また、エチレン性不飽和モノマーとしては、末端エチレン性不飽和結合を有するオリゴマーもしくはポリマー(以下、マクロモノマーと呼ぶ)も使用することができる。このようなエチレン性不飽和モノマーとしては、好適なエチレン性不飽和モノマーの具体例は、国際公開第WO2015/068798号に記載されているものが使用できる。
なお、本発明においては、側鎖の官能基と他の化合物とを反応させて、該他の化合物に由来する構造を導入する反応を「変性」という場合もある。変性に用いる化合物は、特に、側鎖の官能基と反応可能な化合物であれば使用できる。該化合物を選定することで、側鎖に様々な重合性官能基を導入することや、重合性を有さない基に変性することも可能である。
上記した説明から理解されるように、環状分子に導入される側鎖は、重合性官能基以外にも、様々な官能基を有していることもある。
さらに、側鎖導入のために用いる化合物が有している官能基の種類によっては、この側鎖の一部が、他の軸分子が有している環状分子の環の官能基に結合し、架橋構造を形成する場合もある。
上記したとおり、(A)ポリロタキサンモノマーの重合性官能基は、前記環状分子が有するもの、または前記環状分子に導入された前記側鎖が有するものであることが好ましい。この中でも、反応性を考慮すると、側鎖の末端が重合性官能基となることが好ましく、側鎖の末端に導入された重合性官能基が、(A)ポリロタキサンモノマー1分子当たり2つ以上存在することがより好ましい。なお、重合性官能基の数の上限は、特に制限されるものではないが、中でも、重合性官能基の数の上限は、側鎖の末端に導入された該重合性官能基のモル数を(A)ポリロタキサンモノマーの重量平均分子量(Mw)で割った値(以下、重合性官能基含有量ともいう)が、10mmol/g以下であることが好ましい。重合性官能基含有量は、上記したとおり、側鎖の末端に導入された重合性官能基のモル数を前記(A)ポリロタキサンモノマーの重量平均分子量(Mw)で割った値であり、言い換えると、前記(A)ポリロタキサンモノマー1g当たりの、側鎖の末端に導入された重合性官能基のモル数を指す。
該重合性官能基含有量は、0.2~8mmol/gが好ましく、0.5~5mmol/gが特に好ましい。なお、重量平均分子量は、後記する実施例で記載したゲルパーミエーションクロマトグラフィー(GPC)で測定した値である。
また、側鎖に導入されていない重合性官能基および前記側鎖に導入された重合性官能基の全重合性官能基の含有量は、以下の範囲であることが好ましい。具体的には、全重合性官能基の含有量が0.2~20mmol/gとなることが好ましい。より好ましくは、全重合性官能基の含有量は0.4~16mmol/gであり、特に好ましくは1~10mmol/gである。全重合性官能基の含有量は、側鎖に導入されていない重合性官能基のモル数と側鎖に導入された重合性官能基のモル数の合計を(A)ポリロタキサンモノマーの重量平均分子量(Mw)で割った値である。
なお、以上の説明した重合性官能基および全重合性官能基のモル数は、平均値である。
本発明において、最も好適に使用される(A)ポリロタキサンモノマーは、両端にアダマンチル基で結合しているポリエチレングリコールを軸分子とし、α-シクロデキストリン環を有する環状分子とし、重合性官能基として環状分子上に水酸基、またはアミノ基が導入されているのが好ましく、ε-カプロラクトンの開環重合により該環状分子に末端が水酸基の側鎖が導入されているもの、またはε-カプロラクタムの開環重合により該環状分子に末端がアミノ基の側鎖が導入されているものがより好ましい。この場合、側鎖は、α-シクロデキストリン環の水酸基をヒドロキシプロピル化した後、ε-カプロラクトンやε-カプロラクタムの開環重合により導入してもよいし、α-シクロデキストリン環の水酸基をアミノ基に変性してから、ε-カプロラクタムの開環重合により導入してもよい。
そして、導入された側鎖は、全ての末端を水酸基またはアミノ基とすることもできるし、水酸基またはアミノ基のモル数を所望のものとするため、非反応性の基に変性することもできる。
本発明において(A)ポリロタキサンモノマーは、上記したように使用する環状分子や側鎖により、(A)ポリロタキサンモノマーの水相や油相への親和性が変化する。
本発明において、(A)ポリロタキサンモノマーが親水性とは、少なくとも部分的に水中で溶解性があり、油相よりも水相で高い親和性を有している場合であり、(A)ポリロタキサンモノマーが親油性とは、少なくとも部分的に有機溶媒への溶解性があり、水相よりも油相で高い親和性を有している場合である。たとえば、(A)成分の室温で、水への溶解性が、少なくとも20g/l以上の溶解性を有する場合、(A)成分は親水性であり、水に相溶しない有機溶媒溶液への溶解性が20g/l以上の溶解性を有する場合、親油性である。
<(B)分子内に少なくとも2つの重合性官能基を有するポリロタキサンモノマー以外の重合性モノマー>
(B)分子内に少なくとも2つの重合性官能基を有するポリロタキサンモノマー以外の重合性モノマーとしては、(A)成分の重合性官能基と重合し得るものであれば、特に制限されないが、中でも(B1)少なくとも2個のイソシアネート基を有する多官能イソシアネート化合物(以下、(B1)多官能イソシアネート化合物、または(B1)成分ともいう。)、(B2)少なくとも2個の水酸基を有するポリオール化合物(以下、(B2)ポリオール化合物、または(B2)成分ともいう。)、(B3)少なくとも2個のアミノ基を有する多官能アミン化合物(以下、(B3)多官能アミン化合物、または(B3)成分ともいう。)、(B4)少なくとも水酸基とアミノ基を両方有する化合物(以下、(B4)成分ともいう。)、(B5)メラミンホルムアルデヒドプレポリマー化合物(以下、(B5)成分ともいう。)、(B6)尿素ホルムアルデヒドプレポリマー化合物(以下、(B6)成分ともいう。)、および(B7)少なくとも2個のカルボキシル基を有する多官能カルボン酸化合物(以下、(B7)多官能カルボン酸化合物、または(B7)成分ともいう。)からなる群から選択される少なくとも1種以上が好適である。
(B)分子内に少なくとも2つの重合性官能基を有するポリロタキサンモノマー以外の重合性モノマーとしては、(A)成分の重合性官能基と重合し得るものであれば、特に制限されないが、中でも(B1)少なくとも2個のイソシアネート基を有する多官能イソシアネート化合物(以下、(B1)多官能イソシアネート化合物、または(B1)成分ともいう。)、(B2)少なくとも2個の水酸基を有するポリオール化合物(以下、(B2)ポリオール化合物、または(B2)成分ともいう。)、(B3)少なくとも2個のアミノ基を有する多官能アミン化合物(以下、(B3)多官能アミン化合物、または(B3)成分ともいう。)、(B4)少なくとも水酸基とアミノ基を両方有する化合物(以下、(B4)成分ともいう。)、(B5)メラミンホルムアルデヒドプレポリマー化合物(以下、(B5)成分ともいう。)、(B6)尿素ホルムアルデヒドプレポリマー化合物(以下、(B6)成分ともいう。)、および(B7)少なくとも2個のカルボキシル基を有する多官能カルボン酸化合物(以下、(B7)多官能カルボン酸化合物、または(B7)成分ともいう。)からなる群から選択される少なくとも1種以上が好適である。
本発明の中空マイクロバルーンは上記した(A)ポリロタキサンモノマーと(B)重合性モノマーとを含む重合性組成物を重合させた樹脂からなる中空マイクロバルーンであり、(A)成分と(B)成分を選択することにより、中空マイクロバルーンの樹脂の種類を選択できる。その中でも、本発明の中空マイクロバルーンの樹脂として、好ましくはウレタン(ウレア)樹脂、メラミン樹脂、尿素樹脂、またはアミド樹脂、および、これらの2つ以上の共重合樹脂からなる群より選択される少なくとも1種の樹脂であることが好ましい。
本発明において、該ウレタン(ウレア)樹脂とは、イソシアネート基と水酸基および/またはアミノ基との反応により得られ、主鎖にウレタン結合を有する樹脂、主鎖にウレア結合を有する樹脂、または主鎖にウレタン結合とウレア結合の両方を有する樹脂であり、該メラミン樹脂とは、主鎖がメラミンを含む多官能アミンとホルムアルデヒドとの重縮合によって得られる樹脂であり、該尿素樹脂とは、主鎖が尿素(さらに多官能アミンも含む)とホルムアルデヒドとの重縮合によって得られる樹脂であり、該アミド樹脂とは、主鎖にアミド結合を有する樹脂である。
その中でも本発明で最も好ましいのはウレタン(ウレア)樹脂である。
その中でも本発明で最も好ましいのはウレタン(ウレア)樹脂である。
(A)ポリロタキサンモノマーおよび(B)重合性モノマーの組み合わせは、たとえば、中空マイクロバルーンがウレタン(ウレア)樹脂からなる場合、(A)ポリロタキサンモノマーの重合性官能基は、水酸基および/またはアミノ基であり、(B)重合性モノマーは、(B1)多官能イソシアネート化合物を必須として含み、それ以外に、(B2)少なくとも2個の水酸基を有するポリオール化合物、(B3)少なくとも2個のアミノ基を有する多官能アミン有化合物、または(B4)少なくとも水酸基とアミノ基を両方有する化合物を含んでもよい。
中空マイクロバルーンがメラミン樹脂からなる場合、(A)ポリロタキサンモノマーの重合性官能基は、アミノ基、(B)重合性モノマーは、(B5)メラミンホルムアルデヒドプレポリマー化合物が選択される。
中空マイクロバルーンが尿素樹脂からなる場合、(A)ポリロタキサンモノマーの重合性官能基は、アミノ基、(B)重合性モノマーは、(B6)尿素ホルムアルデヒドプレポリマー化合物が選択される。
中空マイクロバルーンがアミド樹脂からなる場合、(A)ポリロタキサンモノマーの重合性官能基は、アミノ基、(B)重合性モノマーは、(B7)少なくとも2個のカルボキシル基を有する多官能カルボン酸を必須として含み、それ以外に(B3)少なくとも2個のアミノ基を有する多官能アミン化合物を含んでもよい。
以下に、(B)分子内に少なくとも2つの重合性官能基を有するポリロタキサンモノマー以外の重合性モノマーの具体例を述べる。
<(B1)少なくとも2個のイソシアネート基を有する多官能イソシアネート化合物>
本発明に用いられる(B1)多官能イソシアネート化合物は、少なくとも2個のイソシアネート基を有する多官能イソシアネート化合物であれば、何ら制限なく使用できる。中でも、イソシアネート基を分子内に、2~6個有する化合物が好ましく、2~3個有する化合物がより好ましい。
本発明に用いられる(B1)多官能イソシアネート化合物は、少なくとも2個のイソシアネート基を有する多官能イソシアネート化合物であれば、何ら制限なく使用できる。中でも、イソシアネート基を分子内に、2~6個有する化合物が好ましく、2~3個有する化合物がより好ましい。
また、前記(B1)成分は、後述する2官能イソシアネート化合物と2官能のポリオール化合物又は2官能アミン化合物との反応により調製される(B12)未反応イソシアネート基を含有するウレタンプレポリマー(以下、(B12)ウレタンプレポリマー、または(B12)成分ともいう)であってもよい。前記(B12)ウレタンプレポリマーとしては、未反応のイソシアネート基を含むものであれば、何ら制限なく使用できる。
前記(B1)成分としては、大きく分類すれば、脂肪族イソシアネート、脂環族イソシアネート、芳香族イソシアネート、その他のイソシアネート、(B12)ウレタンプレポリマーに分類することができる。また、前記(B1)成分は、1種類の化合物を使用することもできるし、複数種類の化合物を使用することもできる。複数種類の化合物を使用する場合には、基準となる質量は、複数種類の化合物の合計量である。これらイソシアネート化合物を具体的に例示すると以下の化合物が挙げられる。
(脂肪族イソシアネート)
エチレンジイソシアネート、トリメチレンジイソシアネート、テトラメチレンジイソシアネート、ヘキサメチレンジイソシアネート、オクタメチレンジイソシアネート、ノナメチレンジイソシアネート、2,2’-ジメチルペンタンジイソシアネート、2,2,4-トリメチルヘキサメチレンジイソシアネート、デカメチレンジイソシアネート、ブテンジイソシアネート、1,3-ブタジエン-1,4-ジイソシアネート、2,4,4-トリメチルヘキサメチレンジイソシアネート、1,6,11-トリメチルウンデカメチレンジイソシアネート、1,3,6-トリメチルヘキサメチレンジイソシアネート、1,8-ジイソシアネート4-イソシアネートメチルオクタン、2,5,7-トリメチル-1,8-ジイソシアネート5-イソシアネートメチルオクタン、ビス(イソシアネートエチル)カーボネート、ビス(イソシアネートエチル)エーテル、1,4-ブチレングリコールジプロピルエーテル-ω,ω’-ジイソシアネート、リジンジイソシアネートメチルエステル、2,4,4,-トリメチルヘキサメチレンジイソシアネート等の2官能イソシアネートモノマー(ウレタンプレポリマーを構成する2官能ポリイソシアネート化合物に該当する)。
エチレンジイソシアネート、トリメチレンジイソシアネート、テトラメチレンジイソシアネート、ヘキサメチレンジイソシアネート、オクタメチレンジイソシアネート、ノナメチレンジイソシアネート、2,2’-ジメチルペンタンジイソシアネート、2,2,4-トリメチルヘキサメチレンジイソシアネート、デカメチレンジイソシアネート、ブテンジイソシアネート、1,3-ブタジエン-1,4-ジイソシアネート、2,4,4-トリメチルヘキサメチレンジイソシアネート、1,6,11-トリメチルウンデカメチレンジイソシアネート、1,3,6-トリメチルヘキサメチレンジイソシアネート、1,8-ジイソシアネート4-イソシアネートメチルオクタン、2,5,7-トリメチル-1,8-ジイソシアネート5-イソシアネートメチルオクタン、ビス(イソシアネートエチル)カーボネート、ビス(イソシアネートエチル)エーテル、1,4-ブチレングリコールジプロピルエーテル-ω,ω’-ジイソシアネート、リジンジイソシアネートメチルエステル、2,4,4,-トリメチルヘキサメチレンジイソシアネート等の2官能イソシアネートモノマー(ウレタンプレポリマーを構成する2官能ポリイソシアネート化合物に該当する)。
(脂環族イソシアネート)
イソホロンジイソシアネート、(ビシクロ[2.2.1]ヘプタン-2,5-ジイル)ビスメチレンジイソシアネート、(ビシクロ[2.2.1]ヘプタン-2,6-ジイル)ビスメチレンジイソシアネート、2β,5α-ビス(イソシアネート)ノルボルナン、2β,5β-ビス(イソシアネート)ノルボルナン、2β,6α-ビス(イソシアネート)ノルボルナン、2β,6β-ビス(イソシアネート)ノルボルナン、2,6-ジ(イソシアネートメチル)フラン、1,3-ビス(イソシアネートメチル)シクロヘキサン、ジシクロヘキシルメタン-4,4’-ジイソシアネート、4,4-イソプロピリデンビス(シクロヘキシルイソシアネート)、シクロヘキサンジイソシアネート、メチルシクロヘキサンジイソシアネート、ジシクロヘキシルジメチルメタンジイソシアネート、2,2’-ジメチルジシクロヘキシルメタンジイソシアネート、ビス(4-イソシアネートn-ブチリデン)ペンタエリスリトール、ダイマー酸ジイソシアネート、2,5-ビス(イソシアネートメチル)-ビシクロ〔2,2,1〕-ヘプタン、2,6-ビス(イソシアネートメチル)-ビシクロ〔2,2,1〕-ヘプタン、3,8-ビス(イソシアネートメチル)トリシクロデカン、3,9-ビス(イソシアネートメチル)トリシクロデカン、4,8-ビス(イソシアネートメチル)トリシクロデカン、4,9-ビス(イソシアネートメチル)トリシクロデカン、1,5-ジイソシアネートデカリン、2,7-ジイソシアネートデカリン、1,4-ジイソシアネートデカリン、2,6-ジイソシアネートデカリン、ビシクロ[4.3.0]ノナン-3,7-ジイソシアネート、ビシクロ[4.3.0]ノナン-4,8-ジイソシアネート、ビシクロ[2.2.1]ヘプタン-2,5-ジイソシアネートとビシクロ[2.2.1]ヘプタン-2,6-ジイソシアネート、ビシクロ[2,2,2]オクタン-2,5-ジイソシアネート、ビシクロ[2,2,2]オクタン-2,6-ジイソシアネート、トリシクロ[5.2.1.02.6]デカン-3,8-ジイソシアネート、トリシクロ[5.2.1.02.6]デカン-4,9-ジイソシアネート等の2官能イソシアネートモノマー(ウレタンプレポリマーを構成する2官能ポリイソシアネート化合物に該当する)、2-イソシアネートメチル-3-(3-イソシアネートプロピル)-5-イソシアネートメチル-ビシクロ〔2,2,1〕-ヘプタン、2-イソシアネートメチル-3-(3-イソシアネートプロピル)-6-イソシアネートメチル-ビシクロ〔2,2,1〕-ヘプタン、2-イソシアネートメチル-2-(3-イソシアネートプロピル)-5-イソシアネートメチル-ビシクロ〔2,2,1〕-ヘプタン、2-イソシアネートメチル-2-(3-イソシアネートプロピル)-6-イソシアネートメチル-ビシクロ〔2,2,1〕-ヘプタン、2-イソシアネートメチル-3-(3-イソシアネートプロピル)-5-(2-イソシアネートエチル)-ビシクロ〔2,2,1〕-ヘプタン、2-イソシアネートメチル-3-(3-イソシアネートプロピル)-6-(2-イソシアネートエチル)-ビシクロ〔2,1,1〕-ヘプタン、2-イソシアネートメチル-2-(3-イソシアネートプロピル)-5-(2-イソシアネートエチル)-ビシクロ〔2,2,1〕-ヘプタン、2-イソシアネートメチル-2-(3-イソシアネートプロピル)-6-(2-イソシアネートエチル)-ビシクロ〔2,2,1〕-ヘプタン、1,3,5-トリス(イソシアネートメチル)シクロヘキサン等の多官能イソシアネートモノマー、
イソホロンジイソシアネート、(ビシクロ[2.2.1]ヘプタン-2,5-ジイル)ビスメチレンジイソシアネート、(ビシクロ[2.2.1]ヘプタン-2,6-ジイル)ビスメチレンジイソシアネート、2β,5α-ビス(イソシアネート)ノルボルナン、2β,5β-ビス(イソシアネート)ノルボルナン、2β,6α-ビス(イソシアネート)ノルボルナン、2β,6β-ビス(イソシアネート)ノルボルナン、2,6-ジ(イソシアネートメチル)フラン、1,3-ビス(イソシアネートメチル)シクロヘキサン、ジシクロヘキシルメタン-4,4’-ジイソシアネート、4,4-イソプロピリデンビス(シクロヘキシルイソシアネート)、シクロヘキサンジイソシアネート、メチルシクロヘキサンジイソシアネート、ジシクロヘキシルジメチルメタンジイソシアネート、2,2’-ジメチルジシクロヘキシルメタンジイソシアネート、ビス(4-イソシアネートn-ブチリデン)ペンタエリスリトール、ダイマー酸ジイソシアネート、2,5-ビス(イソシアネートメチル)-ビシクロ〔2,2,1〕-ヘプタン、2,6-ビス(イソシアネートメチル)-ビシクロ〔2,2,1〕-ヘプタン、3,8-ビス(イソシアネートメチル)トリシクロデカン、3,9-ビス(イソシアネートメチル)トリシクロデカン、4,8-ビス(イソシアネートメチル)トリシクロデカン、4,9-ビス(イソシアネートメチル)トリシクロデカン、1,5-ジイソシアネートデカリン、2,7-ジイソシアネートデカリン、1,4-ジイソシアネートデカリン、2,6-ジイソシアネートデカリン、ビシクロ[4.3.0]ノナン-3,7-ジイソシアネート、ビシクロ[4.3.0]ノナン-4,8-ジイソシアネート、ビシクロ[2.2.1]ヘプタン-2,5-ジイソシアネートとビシクロ[2.2.1]ヘプタン-2,6-ジイソシアネート、ビシクロ[2,2,2]オクタン-2,5-ジイソシアネート、ビシクロ[2,2,2]オクタン-2,6-ジイソシアネート、トリシクロ[5.2.1.02.6]デカン-3,8-ジイソシアネート、トリシクロ[5.2.1.02.6]デカン-4,9-ジイソシアネート等の2官能イソシアネートモノマー(ウレタンプレポリマーを構成する2官能ポリイソシアネート化合物に該当する)、2-イソシアネートメチル-3-(3-イソシアネートプロピル)-5-イソシアネートメチル-ビシクロ〔2,2,1〕-ヘプタン、2-イソシアネートメチル-3-(3-イソシアネートプロピル)-6-イソシアネートメチル-ビシクロ〔2,2,1〕-ヘプタン、2-イソシアネートメチル-2-(3-イソシアネートプロピル)-5-イソシアネートメチル-ビシクロ〔2,2,1〕-ヘプタン、2-イソシアネートメチル-2-(3-イソシアネートプロピル)-6-イソシアネートメチル-ビシクロ〔2,2,1〕-ヘプタン、2-イソシアネートメチル-3-(3-イソシアネートプロピル)-5-(2-イソシアネートエチル)-ビシクロ〔2,2,1〕-ヘプタン、2-イソシアネートメチル-3-(3-イソシアネートプロピル)-6-(2-イソシアネートエチル)-ビシクロ〔2,1,1〕-ヘプタン、2-イソシアネートメチル-2-(3-イソシアネートプロピル)-5-(2-イソシアネートエチル)-ビシクロ〔2,2,1〕-ヘプタン、2-イソシアネートメチル-2-(3-イソシアネートプロピル)-6-(2-イソシアネートエチル)-ビシクロ〔2,2,1〕-ヘプタン、1,3,5-トリス(イソシアネートメチル)シクロヘキサン等の多官能イソシアネートモノマー、
(芳香族イソシアネート)
キシリレンジイソシアネート(o-、m-,p-)、テトラクロロ-m-キシリレンジイソシアネート、メチレンジフェニル-4,4’-ジイソシアネート、4-クロル-m-キシリレンジイソシアネート、4,5-ジクロル-m-キシリレンジイソシアネート、2,3,5,6-テトラブロム-p-キシリレンジイソシアネート、4-メチル-m-キシリレンジイソシアネート、4-エチル-m-キシリレンジイソシアネート、ビス(イソシアネートエチル)ベンゼン、ビス(イソシアネートプロピル)ベンゼン、1,3-ビス(α,α-ジメチルイソシアネートメチル)ベンゼン、1,4-ビス(α,α-ジメチルイソシアネートメチル)ベンゼン、α,α,α’,α’-テトラメチルキシリレンジイソシアネート、ビス(イソシアネートブチル)ベンゼン、ビス(イソシアネートメチル)ナフタリン、ビス(イソシアネートメチル)ジフェニルエーテル、ビス(イソシアネートエチル)フタレート、2,6-ジ(イソシアネートメチル)フラン、フェニレンジイソシアネート(o-,m-,p-)、エチルフェニレンジイソシアネート、イソプロピルフェニレンジイソシアネート、ジメチルフェニレンジイソシアネート、ジエチルフェニレンジイソシアネート、ジイソプロピルフェニレンジイソシアネート、トリメチルベンゼントリイソシアネート、ベンゼントリイソシアネート、1,3,5-トリイソシアネートメチルベンゼン、1,5-ナフタレンジイソシアネート、メチルナフタレンジイソシアネート、ビフェニルジイソシアネート、2,4-トリレンジイソシアネート、2,6-トリレンジイソシアネート、4,4’-ジフェニルメタンジイソシアネート、2,2’-ジフェニルメタンジイソシアネート、2,4’-ジフェニルメタンジイソシアネート、3,3’-ジメチルジフェニルメタン-4,4’-ジイソシアネート、ビベンジル-4,4’-ジイソシアネート、ビス(イソシアネートフェニル)エチレン、3,3’-ジメトキシビフェニル-4,4’-ジイソシアネート、フェニルイソシアネートメチルイソシアネート、フェニルイソシアネートエチルイソシアネート、テトラヒドロナフチレンジイソシアネート、ヘキサヒドロベンゼンジイソシアネート、ヘキサヒドロジフェニルメタン-4,4’-ジイソシアネート、ジフェニルエーテルジイソシアネート、エチレングリコ-ルジフェニルエーテルジイソシアネート、1,3-プロピレングリコールジフェニルエーテルジイソシアネート、ベンゾフェノンジイソシアネート、ジエチレングリコ-ルジフェニルエーテルジイソシアネート、ジベンゾフランジイソシアネート、カルバゾールジイソシアネート、エチルカルバゾールジイソシアネート、ジクロロカルバゾールジイソシアネート、2,4-トリレンジイソシアネート、2,6-トリレンジイソシアネート等の2官能イソシアネートモノマー(ウレタンプレポリマーを構成する2官能ポリイソシアネート化合物に該当する)。
キシリレンジイソシアネート(o-、m-,p-)、テトラクロロ-m-キシリレンジイソシアネート、メチレンジフェニル-4,4’-ジイソシアネート、4-クロル-m-キシリレンジイソシアネート、4,5-ジクロル-m-キシリレンジイソシアネート、2,3,5,6-テトラブロム-p-キシリレンジイソシアネート、4-メチル-m-キシリレンジイソシアネート、4-エチル-m-キシリレンジイソシアネート、ビス(イソシアネートエチル)ベンゼン、ビス(イソシアネートプロピル)ベンゼン、1,3-ビス(α,α-ジメチルイソシアネートメチル)ベンゼン、1,4-ビス(α,α-ジメチルイソシアネートメチル)ベンゼン、α,α,α’,α’-テトラメチルキシリレンジイソシアネート、ビス(イソシアネートブチル)ベンゼン、ビス(イソシアネートメチル)ナフタリン、ビス(イソシアネートメチル)ジフェニルエーテル、ビス(イソシアネートエチル)フタレート、2,6-ジ(イソシアネートメチル)フラン、フェニレンジイソシアネート(o-,m-,p-)、エチルフェニレンジイソシアネート、イソプロピルフェニレンジイソシアネート、ジメチルフェニレンジイソシアネート、ジエチルフェニレンジイソシアネート、ジイソプロピルフェニレンジイソシアネート、トリメチルベンゼントリイソシアネート、ベンゼントリイソシアネート、1,3,5-トリイソシアネートメチルベンゼン、1,5-ナフタレンジイソシアネート、メチルナフタレンジイソシアネート、ビフェニルジイソシアネート、2,4-トリレンジイソシアネート、2,6-トリレンジイソシアネート、4,4’-ジフェニルメタンジイソシアネート、2,2’-ジフェニルメタンジイソシアネート、2,4’-ジフェニルメタンジイソシアネート、3,3’-ジメチルジフェニルメタン-4,4’-ジイソシアネート、ビベンジル-4,4’-ジイソシアネート、ビス(イソシアネートフェニル)エチレン、3,3’-ジメトキシビフェニル-4,4’-ジイソシアネート、フェニルイソシアネートメチルイソシアネート、フェニルイソシアネートエチルイソシアネート、テトラヒドロナフチレンジイソシアネート、ヘキサヒドロベンゼンジイソシアネート、ヘキサヒドロジフェニルメタン-4,4’-ジイソシアネート、ジフェニルエーテルジイソシアネート、エチレングリコ-ルジフェニルエーテルジイソシアネート、1,3-プロピレングリコールジフェニルエーテルジイソシアネート、ベンゾフェノンジイソシアネート、ジエチレングリコ-ルジフェニルエーテルジイソシアネート、ジベンゾフランジイソシアネート、カルバゾールジイソシアネート、エチルカルバゾールジイソシアネート、ジクロロカルバゾールジイソシアネート、2,4-トリレンジイソシアネート、2,6-トリレンジイソシアネート等の2官能イソシアネートモノマー(ウレタンプレポリマーを構成する2官能ポリイソシアネート化合物に該当する)。
メシチリレントリイソシアネート、トリフェニルメタントリイソシアネート、ポリメリックMDI、ナフタリントリイソシアネート、ジフェニルメタン-2,4,4’-トリイソシアネート、3-メチルジフェニルメタン-4,4’,6-トリイソシアネート、4-メチル-ジフェニルメタン-2,3,4’,5,6-ペンタイソシアネート等の多官能イソシアネートモノマー。
(その他のイソシアネート)
その他のイソシアネートとして、ヘキサメチレンジイソシアネートやトリレンジイソシアネートなどのジイソシアネート類を主原料としたビュレット構造、ウレトジオン構造、イソシアヌレート構造(たとえば、特開2004-534870号公報には、脂肪族ポリイソシアネートのビュレット構造、ウレトジオン構造、イソシアヌレート構造の変性の方法が開示されている)を有する多官能イソシアネートやトリメチロールプロパンなどの3官能以上のポリオールとのアダクト体として多官能としたもの等が挙げられる(成書(岩田敬治編 ポリウレタン樹脂ハンドブック 日刊工業新聞社(1987))等に開示されている)。
その他のイソシアネートとして、ヘキサメチレンジイソシアネートやトリレンジイソシアネートなどのジイソシアネート類を主原料としたビュレット構造、ウレトジオン構造、イソシアヌレート構造(たとえば、特開2004-534870号公報には、脂肪族ポリイソシアネートのビュレット構造、ウレトジオン構造、イソシアヌレート構造の変性の方法が開示されている)を有する多官能イソシアネートやトリメチロールプロパンなどの3官能以上のポリオールとのアダクト体として多官能としたもの等が挙げられる(成書(岩田敬治編 ポリウレタン樹脂ハンドブック 日刊工業新聞社(1987))等に開示されている)。
((B12)ウレタンプレポリマー)
本発明において、前記(B12)ウレタンプレポリマーは、前記した(B1)成分から選択された2官能イソシアネート化合物((B1)成分として例示した中で明記した化合物)と、以下に示す(B21)2官能ポリオール化合物、または、(B31)2官能アミン化合物とを反応させたものが好適である。
本発明において、前記(B12)ウレタンプレポリマーは、前記した(B1)成分から選択された2官能イソシアネート化合物((B1)成分として例示した中で明記した化合物)と、以下に示す(B21)2官能ポリオール化合物、または、(B31)2官能アミン化合物とを反応させたものが好適である。
前記(B21)2官能ポリオール化合物を例示すると以下のものが挙げられる。
((B21)2官能ポリオール)
(脂肪族アルコール)
エチレングリコール、ジエチレングリコール、プロピレングリコール、ジプロピレングリコール、ブチレングリコール、1,5-ジヒドロキシペンタン、1,6-ジヒドロキシヘキサン、1,7-ジヒドロキシヘプタン、1,8-ジヒドロキシオクタン、1,9-ジヒドロキシノナン、1,10-ジヒドロキシデカン、1,11-ジヒドロキシウンデカン、1,12-ジヒドロキシドデカン、ネオペンチルグリコール、モノオレイン酸グリセリル、モノエライジン、ポリエチレングリコール、3-メチル-1,5-ジヒドロキシペンタン、ジヒドロキシネオペンチル、2-エチル-1,2-ジヒドロキシヘキサン、2-メチル-1,3-ジヒドロキシプロパン、ポリエステルポリオール(ポリオールと多塩基酸との縮合反応により得られる両末端にのみ水酸基を有する化合物)、ポリエーテルポリオール(アルキレンオキシドの開環重合、または、分子中に活性水素含有基を2個以上有する化合物とアルキレンオキサイドとの反応により得られる化合物およびその変性体であり、分子の両末端にのみ水酸基を有するもの)、ポリカプロラクトンポリオール(ε-カプロラクトンの開環重合により得られる化合物であり、分子の両末端にのみ水酸基を有するもの)、ポリカーボネートポリオール(低分子ポリオールの1種類以上をホスゲン化して得られる化合物あるいはエチレンカーボネート、ジエチルカーボネート、ジフェニルカーボネート等を用いてエステル交換して得られる化合物であり、分子の両末端にのみ水酸基を有するもの)、ポリアクリルポリオール((メタ)アクリレート酸エステルやビニルモノマーを重合させて得られるポリオール化合物であり、分子の両末端にのみ水酸基を有するもの)等の2官能ポリオール化合物。
(脂肪族アルコール)
エチレングリコール、ジエチレングリコール、プロピレングリコール、ジプロピレングリコール、ブチレングリコール、1,5-ジヒドロキシペンタン、1,6-ジヒドロキシヘキサン、1,7-ジヒドロキシヘプタン、1,8-ジヒドロキシオクタン、1,9-ジヒドロキシノナン、1,10-ジヒドロキシデカン、1,11-ジヒドロキシウンデカン、1,12-ジヒドロキシドデカン、ネオペンチルグリコール、モノオレイン酸グリセリル、モノエライジン、ポリエチレングリコール、3-メチル-1,5-ジヒドロキシペンタン、ジヒドロキシネオペンチル、2-エチル-1,2-ジヒドロキシヘキサン、2-メチル-1,3-ジヒドロキシプロパン、ポリエステルポリオール(ポリオールと多塩基酸との縮合反応により得られる両末端にのみ水酸基を有する化合物)、ポリエーテルポリオール(アルキレンオキシドの開環重合、または、分子中に活性水素含有基を2個以上有する化合物とアルキレンオキサイドとの反応により得られる化合物およびその変性体であり、分子の両末端にのみ水酸基を有するもの)、ポリカプロラクトンポリオール(ε-カプロラクトンの開環重合により得られる化合物であり、分子の両末端にのみ水酸基を有するもの)、ポリカーボネートポリオール(低分子ポリオールの1種類以上をホスゲン化して得られる化合物あるいはエチレンカーボネート、ジエチルカーボネート、ジフェニルカーボネート等を用いてエステル交換して得られる化合物であり、分子の両末端にのみ水酸基を有するもの)、ポリアクリルポリオール((メタ)アクリレート酸エステルやビニルモノマーを重合させて得られるポリオール化合物であり、分子の両末端にのみ水酸基を有するもの)等の2官能ポリオール化合物。
(脂環族アルコール)
水添ビスフェノールA、シクロブタンジオール、シクロペンタンジオール、シクロヘキサンジオール、シクロヘプタンジオール、シクロオクタンジオール、シクロヘキサンジメタノール、ヒドロキシプロピルシクロヘキサノール、トリシクロ〔5,2,1,02,6〕デカン-ジメタノール、ビシクロ〔4,3,0〕-ノナンジオール、ジシクロヘキサンジオール、トリシクロ〔5,3,1,13,9〕ドデカンジオール、ビシクロ〔4,3,0〕ノナンジメタノール、トリシクロ〔5,3,1,13,9〕ドデカン-ジエタノール、ヒドロキシプロピルトリシクロ〔5,3,1,13,9〕ドデカノール、スピロ〔3,4〕オクタンジオール、ブチルシクロヘキサンジオール、1,1’-ビシクロヘキシリデンジオール、1,4-シクロヘキサンジメタノール、1,3-シクロヘキサンジメタノール、1,2-シクロヘキサンジメタノール、およびo-ジヒドロキシキシリレン等の2官能ポリオール化合物。
水添ビスフェノールA、シクロブタンジオール、シクロペンタンジオール、シクロヘキサンジオール、シクロヘプタンジオール、シクロオクタンジオール、シクロヘキサンジメタノール、ヒドロキシプロピルシクロヘキサノール、トリシクロ〔5,2,1,02,6〕デカン-ジメタノール、ビシクロ〔4,3,0〕-ノナンジオール、ジシクロヘキサンジオール、トリシクロ〔5,3,1,13,9〕ドデカンジオール、ビシクロ〔4,3,0〕ノナンジメタノール、トリシクロ〔5,3,1,13,9〕ドデカン-ジエタノール、ヒドロキシプロピルトリシクロ〔5,3,1,13,9〕ドデカノール、スピロ〔3,4〕オクタンジオール、ブチルシクロヘキサンジオール、1,1’-ビシクロヘキシリデンジオール、1,4-シクロヘキサンジメタノール、1,3-シクロヘキサンジメタノール、1,2-シクロヘキサンジメタノール、およびo-ジヒドロキシキシリレン等の2官能ポリオール化合物。
(芳香族アルコール)
ジヒドロキシナフタレン、ジヒドロキシベンゼン、ビスフェノールA、ビスフェノールF、キシリレングリコール、テトラブロムビスフェノールA、ビス(4-ヒドロキシフェニル)メタン、1,1-ビス(4-ヒドロキシフェニル)エタン、1,2-ビス(4-ヒドロキシフェニル)エタン、ビス(4-ヒドロキシフェニル)フェニルメタン、ビス(4-ヒドロキシフェニル)ジフェニルメタン、ビス(4-ヒドロキシフェニル)-1-ナフチルメタン、1,1-ビス(4-ヒドロキシフェニル)-1-フェニルエタン、2-(4-ヒドロキシフェニル)-2-(3-ヒドロキシフェニル)プロパン、2,2-ビス(4-ヒドロキシフェニル)ブタン、1,1-ビス(4-ヒドロキシフェニル)ブタン、2,2-ビス(4-ヒドロキシフェニル)-3-メチルブタン、2,2-ビス(4-ヒドロキシフェニル)ペンタン、3,3-ビス(4-ヒドロキシフェニル)ペンタン、2,2-ビス(4-ヒドロキシフェニル)ヘキサン、2,2-ビス(4-ヒドロキシフェニル)オクタン、2,2-ビス(4-ヒドロキシフェニル)-4-メチルペンタン、2,2-ビス(4-ヒドロキシフェニル)ヘプタン、4,4-ビス(4-ヒドロキシフェニル)ヘプタン、2,2-ビス(4-ヒドロキシフェニル)トリデカン、2,2-ビス(4-ヒドロキシフェニル)オクタン、2,2-ビス(3-メチル-4-ヒドロキシフェニル)プロパン、2,2-ビス(3-エチル-4-ヒドロキシフェニル)プロパン、2,2-ビス(3-n-プロピル-4-ヒドロキシフェニル)プロパン、2,2-ビス(3-イソプロピル-4-ヒドロキシフェニル)プロパン、2,2-ビス(3-sec-ブチル-4-ヒドロキシフェニル)プロパン、2,2-ビス(3-tert-ブチル-4-ヒドロキシフェニル)プロパン、2,2-ビス(3-シクロヘキシル-4-ヒドロキシフェニル)プロパン、2,2-ビス(3-アリル-4’-ヒドロキシフェニル)プロパン、2,2-ビス(3-メトキシ-4-ヒドロキシフェニル)プロパン、2,2-ビス(3,5-ジメチル-4-ヒドロキシフェニル)プロパン、2,2-ビス(2,3,5,6-テトラメチル-4-ヒドロキシフェニル)プロパン、ビス(4-ヒドロキシフェニル)シアノメタン、1-シアノ-3,3-ビス(4-ヒドロキシフェニル)ブタン、2,2-ビス(4-ヒドロキシフェニル)ヘキサフルオロプロパン、1,1-ビス(4-ヒドロキシフェニル)シクロペンタン、1,1-ビス(4-ヒドロキシフェニル)シクロヘキサン、1,1-ビス(4-ヒドロキシフェニル)シクロヘプタン、1,1-ビス(3-メチル-4-ヒドロキシフェニル)シクロヘキサン、1,1-ビス(3,5-ジメチル-4-ヒドロキシフェニル)シクロヘキサン、1,1-ビス(3,5-ジクロロ-4-ヒドロキシフェニル)シクロヘキサン、1,1-ビス(3-メチル-4-ヒドロキシフェニル)-4-メチルシクロヘキサン、1,1-ビス(4-ヒドロキシフェニル)-3,3,5-トリメチルシクロヘキサン、2,2-ビス(4-ヒドロキシフェニル)ノルボルナン、2,2-ビス(4-ヒドロキシフェニル)アダマンタン、4,4’-ジヒドロキシジフェニルエーテル、4,4’-ジヒドロキシ-3,3’-ジメチルジフェニルエーテル、エチレングリコールビス(4-ヒドロキシフェニル)エーテル、4,4’-ジヒドロキシジフェニルスルフィド、3,3’-ジメチル-4,4’-ジヒドロキシジフェニルスルフィド、3,3’-ジシクロヘキシル-4,4’-ジヒドロキシジフェニルスルフィド、3,3’-ジフェニル-4,4’-ジヒドロキシジフェニルスルフィド、4,4’-ジヒドロキシジフェニルスルホキシド、3,3’-ジメチル-4,4’-ジヒドロキシジフェニルスルホキシド、4,4’-ジヒドロキシジフェニルスルホン、4,4’-ジヒドロキシ-3,3’-ジメチルジフェニルスルホン、ビス(4-ヒドロキシフェニル)ケトン、ビス(4-ヒドロキシ-3-メチルフェニル)ケトン、7,7’-ジヒドロキシ-3,3’,4,4’-テトラヒドロ-4,4,4’,4’-テトラメチル-2,2’-スピロビ(2H-1-ベンゾピラン)、トランス-2,3-ビス(4-ヒドロキシフェニル)-2-ブテン、9,9-ビス(4-ヒドロキシフェニル)フルオレン、3,3-ビス(4-ヒドロキシフェニル)-2-ブタノン、1,6-ビス(4-ヒドロキシフェニル)-1,6-ヘキサンジオン、4,4’-ジヒドロキシビフェニル、m-ジヒドロキシキシリレン、p-ジヒドロキシキシリレン、1,4-ビス(2-ヒドロキシエチル)ベンゼン、1,4-ビス(3-ヒドロキシプロピル)ベンゼン、1,4-ビス(4-ヒドロキシブチル)ベンゼン、1,4-ビス(5-ヒドロキシペンチル)ベンゼン、1,4-ビス(6-ヒドロキシヘキシル)ベンゼン、2,2-ビス〔4-(2”-ヒドロキシエチルオキシ)フェニル〕プロパン、およびハイドロキノン、レゾールシン等の2官能ポリオール化合物。
ジヒドロキシナフタレン、ジヒドロキシベンゼン、ビスフェノールA、ビスフェノールF、キシリレングリコール、テトラブロムビスフェノールA、ビス(4-ヒドロキシフェニル)メタン、1,1-ビス(4-ヒドロキシフェニル)エタン、1,2-ビス(4-ヒドロキシフェニル)エタン、ビス(4-ヒドロキシフェニル)フェニルメタン、ビス(4-ヒドロキシフェニル)ジフェニルメタン、ビス(4-ヒドロキシフェニル)-1-ナフチルメタン、1,1-ビス(4-ヒドロキシフェニル)-1-フェニルエタン、2-(4-ヒドロキシフェニル)-2-(3-ヒドロキシフェニル)プロパン、2,2-ビス(4-ヒドロキシフェニル)ブタン、1,1-ビス(4-ヒドロキシフェニル)ブタン、2,2-ビス(4-ヒドロキシフェニル)-3-メチルブタン、2,2-ビス(4-ヒドロキシフェニル)ペンタン、3,3-ビス(4-ヒドロキシフェニル)ペンタン、2,2-ビス(4-ヒドロキシフェニル)ヘキサン、2,2-ビス(4-ヒドロキシフェニル)オクタン、2,2-ビス(4-ヒドロキシフェニル)-4-メチルペンタン、2,2-ビス(4-ヒドロキシフェニル)ヘプタン、4,4-ビス(4-ヒドロキシフェニル)ヘプタン、2,2-ビス(4-ヒドロキシフェニル)トリデカン、2,2-ビス(4-ヒドロキシフェニル)オクタン、2,2-ビス(3-メチル-4-ヒドロキシフェニル)プロパン、2,2-ビス(3-エチル-4-ヒドロキシフェニル)プロパン、2,2-ビス(3-n-プロピル-4-ヒドロキシフェニル)プロパン、2,2-ビス(3-イソプロピル-4-ヒドロキシフェニル)プロパン、2,2-ビス(3-sec-ブチル-4-ヒドロキシフェニル)プロパン、2,2-ビス(3-tert-ブチル-4-ヒドロキシフェニル)プロパン、2,2-ビス(3-シクロヘキシル-4-ヒドロキシフェニル)プロパン、2,2-ビス(3-アリル-4’-ヒドロキシフェニル)プロパン、2,2-ビス(3-メトキシ-4-ヒドロキシフェニル)プロパン、2,2-ビス(3,5-ジメチル-4-ヒドロキシフェニル)プロパン、2,2-ビス(2,3,5,6-テトラメチル-4-ヒドロキシフェニル)プロパン、ビス(4-ヒドロキシフェニル)シアノメタン、1-シアノ-3,3-ビス(4-ヒドロキシフェニル)ブタン、2,2-ビス(4-ヒドロキシフェニル)ヘキサフルオロプロパン、1,1-ビス(4-ヒドロキシフェニル)シクロペンタン、1,1-ビス(4-ヒドロキシフェニル)シクロヘキサン、1,1-ビス(4-ヒドロキシフェニル)シクロヘプタン、1,1-ビス(3-メチル-4-ヒドロキシフェニル)シクロヘキサン、1,1-ビス(3,5-ジメチル-4-ヒドロキシフェニル)シクロヘキサン、1,1-ビス(3,5-ジクロロ-4-ヒドロキシフェニル)シクロヘキサン、1,1-ビス(3-メチル-4-ヒドロキシフェニル)-4-メチルシクロヘキサン、1,1-ビス(4-ヒドロキシフェニル)-3,3,5-トリメチルシクロヘキサン、2,2-ビス(4-ヒドロキシフェニル)ノルボルナン、2,2-ビス(4-ヒドロキシフェニル)アダマンタン、4,4’-ジヒドロキシジフェニルエーテル、4,4’-ジヒドロキシ-3,3’-ジメチルジフェニルエーテル、エチレングリコールビス(4-ヒドロキシフェニル)エーテル、4,4’-ジヒドロキシジフェニルスルフィド、3,3’-ジメチル-4,4’-ジヒドロキシジフェニルスルフィド、3,3’-ジシクロヘキシル-4,4’-ジヒドロキシジフェニルスルフィド、3,3’-ジフェニル-4,4’-ジヒドロキシジフェニルスルフィド、4,4’-ジヒドロキシジフェニルスルホキシド、3,3’-ジメチル-4,4’-ジヒドロキシジフェニルスルホキシド、4,4’-ジヒドロキシジフェニルスルホン、4,4’-ジヒドロキシ-3,3’-ジメチルジフェニルスルホン、ビス(4-ヒドロキシフェニル)ケトン、ビス(4-ヒドロキシ-3-メチルフェニル)ケトン、7,7’-ジヒドロキシ-3,3’,4,4’-テトラヒドロ-4,4,4’,4’-テトラメチル-2,2’-スピロビ(2H-1-ベンゾピラン)、トランス-2,3-ビス(4-ヒドロキシフェニル)-2-ブテン、9,9-ビス(4-ヒドロキシフェニル)フルオレン、3,3-ビス(4-ヒドロキシフェニル)-2-ブタノン、1,6-ビス(4-ヒドロキシフェニル)-1,6-ヘキサンジオン、4,4’-ジヒドロキシビフェニル、m-ジヒドロキシキシリレン、p-ジヒドロキシキシリレン、1,4-ビス(2-ヒドロキシエチル)ベンゼン、1,4-ビス(3-ヒドロキシプロピル)ベンゼン、1,4-ビス(4-ヒドロキシブチル)ベンゼン、1,4-ビス(5-ヒドロキシペンチル)ベンゼン、1,4-ビス(6-ヒドロキシヘキシル)ベンゼン、2,2-ビス〔4-(2”-ヒドロキシエチルオキシ)フェニル〕プロパン、およびハイドロキノン、レゾールシン等の2官能ポリオール化合物。
(ポリエステルジオール)
ポリオールと多塩基酸との縮合反応により得られる2官能ポリオール化合物が挙げられる。中でも、数平均分子量が400~2000であることが好ましく、500~1500より好ましく、600~1200が最も好ましい。
ポリオールと多塩基酸との縮合反応により得られる2官能ポリオール化合物が挙げられる。中でも、数平均分子量が400~2000であることが好ましく、500~1500より好ましく、600~1200が最も好ましい。
(ポリエーテルジオール)
アルキレンオキシドの開環重合、または、分子中に活性水素含有基を2個以上有する化合物とアルキレンオキサイドとの反応により得られる2官能ポリオール化合物およびその変性体が挙げられる。中でも、数平均分子量が400~2000であることが好ましく、500~1500より好ましく、600~1200が最も好ましい。
アルキレンオキシドの開環重合、または、分子中に活性水素含有基を2個以上有する化合物とアルキレンオキサイドとの反応により得られる2官能ポリオール化合物およびその変性体が挙げられる。中でも、数平均分子量が400~2000であることが好ましく、500~1500より好ましく、600~1200が最も好ましい。
(ポリカプロラクトンポリオール)
ε-カプロラクトンの開環重合により得られる2官能ポリオール化合物が挙げられる。中でも、数平均分子量が400~2000であることが好ましく、500~1500より好ましく、600~1200が最も好ましい。
ε-カプロラクトンの開環重合により得られる2官能ポリオール化合物が挙げられる。中でも、数平均分子量が400~2000であることが好ましく、500~1500より好ましく、600~1200が最も好ましい。
(ポリカーボネートポリオール)
低分子ポリオールの1種類以上をホスゲン化して得られる2官能ポリオール化合物あるいはエチレンカーボネート、ジエチルカーボネート、ジフェニルカーボネート等を用いてエステル交換して得られる2官能ポリオール化合物が挙げられる。中でも、数平均分子量が400~2000であることが好ましく、500~1500より好ましく、600~1200が最も好ましい
(ポリアクリルポリオール)
(メタ)アクリレート酸エステルやビニルモノマーを重合させて得られる2官能ポリオール化合物が挙げられる。
低分子ポリオールの1種類以上をホスゲン化して得られる2官能ポリオール化合物あるいはエチレンカーボネート、ジエチルカーボネート、ジフェニルカーボネート等を用いてエステル交換して得られる2官能ポリオール化合物が挙げられる。中でも、数平均分子量が400~2000であることが好ましく、500~1500より好ましく、600~1200が最も好ましい
(ポリアクリルポリオール)
(メタ)アクリレート酸エステルやビニルモノマーを重合させて得られる2官能ポリオール化合物が挙げられる。
((B31)2官能アミン化合物)
前記(B31)2官能アミン化合物を例示すると以下のものが挙げられる。
前記(B31)2官能アミン化合物を例示すると以下のものが挙げられる。
(脂肪族アミン)
エチレンジアミン、ヘキサメチレンジアミン、ノナメチレンジアミン、ウンデカンメチレンジアミン、ドデカメチレンジアミン、メタキシレンジアミン、1,3-プロパンジアミン、プトレシン等の2官能アミン化合物。
エチレンジアミン、ヘキサメチレンジアミン、ノナメチレンジアミン、ウンデカンメチレンジアミン、ドデカメチレンジアミン、メタキシレンジアミン、1,3-プロパンジアミン、プトレシン等の2官能アミン化合物。
(脂環族アミン)
イソホロンジアミン、シクロヘキシルジアミン等のポリアミン等の2官能アミン化合物。
イソホロンジアミン、シクロヘキシルジアミン等のポリアミン等の2官能アミン化合物。
(芳香族アミン)
4,4’-メチレンビス(o-クロロアニリン)(MOCA)、2,6-ジクロロ-p-フェニレンジアミン、4,4’-メチレンビス(2,3-ジクロロアニリン)、4,4’-メチレンビス(2-エチル-6-メチルアニリン)、3,5-ビス(メチルチオ)-2,4-トルエンジアミン、3,5-ビス(メチルチオ)-2,6-トルエンジアミン、3,5-ジエチルトルエン-2,4-ジアミン、3,5-ジエチルトルエン-2,6-ジアミン、トリメチレングリコール-ジ-p-アミノベンゾエート、ポリテトラメチレングリコール-ジ-p-アミノベンゾエート、4,4’-ジアミノ-3,3’,5,5’-テトラエチルジフェニルメタン、4,4’-ジアミノ-3,3’-ジイソプロピル-5,5’-ジメチルジフェニルメタン、4,4’-ジアミノ-3,3’,5,5’-テトライソプロピルジフェニルメタン、1,2-ビス(2-アミノフェニルチオ)エタン、4,4’-ジアミノ-3,3’-ジエチル-5,5’-ジメチルジフェニルメタン、N,N’-ジ-sec-ブチル-4,4’-ジアミノジフェニルメタン、3,3’-ジエチル-4,4’-ジアミノジフェニルメタン、m-キシリレンジアミン、N,N’-ジ-sec-ブチル-p-フェニレンジアミン、m-フェニレンジアミン、p-キシリレンジアミン、p-フェニレンジアミン、3,3’-メチレンビス(メチル-6-アミノベンゾエート)、2,4-ジアミノ-4-クロロ安息香酸-2-メチルプロピル、2,4-ジアミノ-4-クロロ安息香酸-イソプロピル、2,4-ジアミノ-4-クロロフェニル酢酸-イソプロピル、テレフタル酸-ジ-(2-アミノフェニル)チオエチル、ジフェニルメタンジアミン、トリレンジアミン、ピペラジン等の2官能アミン化合物。
4,4’-メチレンビス(o-クロロアニリン)(MOCA)、2,6-ジクロロ-p-フェニレンジアミン、4,4’-メチレンビス(2,3-ジクロロアニリン)、4,4’-メチレンビス(2-エチル-6-メチルアニリン)、3,5-ビス(メチルチオ)-2,4-トルエンジアミン、3,5-ビス(メチルチオ)-2,6-トルエンジアミン、3,5-ジエチルトルエン-2,4-ジアミン、3,5-ジエチルトルエン-2,6-ジアミン、トリメチレングリコール-ジ-p-アミノベンゾエート、ポリテトラメチレングリコール-ジ-p-アミノベンゾエート、4,4’-ジアミノ-3,3’,5,5’-テトラエチルジフェニルメタン、4,4’-ジアミノ-3,3’-ジイソプロピル-5,5’-ジメチルジフェニルメタン、4,4’-ジアミノ-3,3’,5,5’-テトライソプロピルジフェニルメタン、1,2-ビス(2-アミノフェニルチオ)エタン、4,4’-ジアミノ-3,3’-ジエチル-5,5’-ジメチルジフェニルメタン、N,N’-ジ-sec-ブチル-4,4’-ジアミノジフェニルメタン、3,3’-ジエチル-4,4’-ジアミノジフェニルメタン、m-キシリレンジアミン、N,N’-ジ-sec-ブチル-p-フェニレンジアミン、m-フェニレンジアミン、p-キシリレンジアミン、p-フェニレンジアミン、3,3’-メチレンビス(メチル-6-アミノベンゾエート)、2,4-ジアミノ-4-クロロ安息香酸-2-メチルプロピル、2,4-ジアミノ-4-クロロ安息香酸-イソプロピル、2,4-ジアミノ-4-クロロフェニル酢酸-イソプロピル、テレフタル酸-ジ-(2-アミノフェニル)チオエチル、ジフェニルメタンジアミン、トリレンジアミン、ピペラジン等の2官能アミン化合物。
((B12)ウレタンプレポリマーの製造方法)
(B12)ウレタンプレポリマーは、前記した2官能イソシアネート化合物と、(B21)2官能ポリオール化合物および/または(B31)2官能アミン化合物を反応させることによって製造される。ただし、本発明において(B12)ウレタンプレポリマーは、未反応のイソシアネート基を含有していなければならない。イソシアネート基を含有する(B12)ウレタンプレポリマーの製造方法は、公知の方法が特に制限されず、たとえば、2官能イソシアネート化合物におけるイソシアネート基のモル数(n5)と(B21)2官能ポリオール化合物および/または(B31)2官能アミン化合物の活性水素を持つ基のモル数(n6)とが、1<(n5)/(n6)≦2.3となる範囲で製造する方法が挙げられる。なお、2種類以上の2官能イソシアネート化合物を用いる場合、該イソシアネート基のモル数(n5)は、それら2官能イソシアネート化合物の合計のイソシアネート基のモル数とする。また、2種類以上の(B21)2官能ポリオール化合物および/または(B31)2官能アミン化合物を用いた場合、該活性水素を持つ基のモル数(n6)は、それら(B21)2官能ポリオール化合物および/または(B31)2官能アミン化合物の合計の活性水素のモル数とする。なお、本発明においては、活性水素が第一級アミノ基である場合であっても、第一級アミノ基を1モルと計算する。その理由は、第一級アミノ基において、2つ目のアミノ基(-NH)が反応するには、かなりのエネルギーを要する(第一級アミノ基であっても、2つ目の-NHは反応し難い)ため、本発明においては、第一級アミノ基を有する2官能活性水素含有化合物を使用したとしても、第一級アミノ基を1モルと計算する。
(B12)ウレタンプレポリマーは、前記した2官能イソシアネート化合物と、(B21)2官能ポリオール化合物および/または(B31)2官能アミン化合物を反応させることによって製造される。ただし、本発明において(B12)ウレタンプレポリマーは、未反応のイソシアネート基を含有していなければならない。イソシアネート基を含有する(B12)ウレタンプレポリマーの製造方法は、公知の方法が特に制限されず、たとえば、2官能イソシアネート化合物におけるイソシアネート基のモル数(n5)と(B21)2官能ポリオール化合物および/または(B31)2官能アミン化合物の活性水素を持つ基のモル数(n6)とが、1<(n5)/(n6)≦2.3となる範囲で製造する方法が挙げられる。なお、2種類以上の2官能イソシアネート化合物を用いる場合、該イソシアネート基のモル数(n5)は、それら2官能イソシアネート化合物の合計のイソシアネート基のモル数とする。また、2種類以上の(B21)2官能ポリオール化合物および/または(B31)2官能アミン化合物を用いた場合、該活性水素を持つ基のモル数(n6)は、それら(B21)2官能ポリオール化合物および/または(B31)2官能アミン化合物の合計の活性水素のモル数とする。なお、本発明においては、活性水素が第一級アミノ基である場合であっても、第一級アミノ基を1モルと計算する。その理由は、第一級アミノ基において、2つ目のアミノ基(-NH)が反応するには、かなりのエネルギーを要する(第一級アミノ基であっても、2つ目の-NHは反応し難い)ため、本発明においては、第一級アミノ基を有する2官能活性水素含有化合物を使用したとしても、第一級アミノ基を1モルと計算する。
また、特に制限されるものではないが、前記(B12)ウレタンプレポリマーは、イソシアネート当量((B12)ウレタンプレポリマーの分子量を1分子中のイソシアネート基の数で割った値)が、好ましくは300~5000、より好ましくは350~3,000、特に好ましくは400~2,000となるものである。また、本発明における(B12)ウレタンプレポリマーは、2官能イソシアネート化合物と(B21)2官能ポリオール化合物および/または(B31)2官能アミン化合物とから製造される直鎖状のものが好ましく、この場合、両末端がイソシアネート基となり、1分子中のイソシアネート基の数は2となる。
なお、前記(B12)ウレタンプレポリマーのイソシアネート当量は、(B12)ウレタンプレポリマーが有するイソシアネート基をJIS K 7301に準拠した、以下の逆滴定法によって定量できる。まず、得られた(B12)ウレタンプレポリマーを乾燥溶媒に溶解させる。次に、(B12)ウレタンプレポリマーが有するイソシアネート基の量よりも、明らかに過剰量であって、かつ濃度が既知のジ-n-ブチルアミンを、該乾燥溶媒に加え、(B12)ウレタンプレポリマーの全イソシアネート基とジ-n-ブチルアミンとを反応させる。次いで、消費されなかった(反応に関与しなかった)ジ-n-ブチルアミンを酸で滴定して、消費されたジ-n-ブチルアミンの量を求める。この消費されたジ-n-ブチルアミンと、(B12)ウレタンプレポリマーが有するイソシアネート基とは、同量であることからイソシアネート当量を求めることができる。また、たとえば、イソシアネート基を含有する直鎖状の(B12)ウレタンプレポリマーであれば、(B12)ウレタンプレポリマーの数平均分子量は、イソシアネート当量の2倍となる。この(B12)ウレタンプレポリマーの分子量は、ゲルパーミネーションクロマトグラフィー(GPC)で測定した値と一致し易い。なお、該(B12)ウレタンプレポリマーと2官能イソシアネート化合物とを併用して使用する場合には、両者の混合物を上記方法に沿って測定すればよい。
さらに、前記(B12)ウレタンプレポリマーのイソシアネート含有量((I);質量モル濃度(mol/kg))と、(B12)ウレタンプレポリマー中に存在するウレタン結合含有量((U);質量モル濃度(mol/kg))が、1≦(U)/(I)≦10になることが好ましい。この範囲は、(B12)ウレタンプレポリマーと2官能イソシアネート化合物を併用して使用する場合も同じである。
なお、イソシアネート含有量((I);質量モル濃度(mol/kg))は、イソシアネート当量の逆数に1,000をかけた値である。また、(B12)ウレタンプレポリマー中に存在するウレタン結合含有量((U)質量モル濃度(mol/kg))は、下記の手法で理論値が求められる。すなわち、(B12)ウレタンプレポリマーを構成する2官能イソシアネート化合物中に存在する、反応前のイソシアネート基の含有量を全イソシアネート含有量((aI);質量モル濃度(mol/kg))とすると、ウレタン結合含有量((U);質量モル濃度(mol/kg))は、(B1)成分の全イソシアネート基の含有量((aI);質量モル濃度(mol/kg))からイソシアネート含有量((I);質量モル濃度(mol/kg))を引いた値((U)=(aI)-(I))が(B12)ウレタンプレポリマー中に存在するウレタン結合含有量(U)となる。
また、(B12)ウレタンプレポリマーの製造において、必要に応じて加熱やウレタン化触媒を添加することも可能である。ウレタン化触媒は、任意の適切なものを使用でき、具体例は、後述しているウレタン化触媒を用いればよい。
本発明で用いられる(B1)成分で最も好ましい例を挙げると、形成されるマイクロバルーンの強度や、反応性の制御の観点から、イソホロンジイソシアネート、1,3-ビス(イソシアネートメチル)シクロヘキサン、(ビシクロ[2.2.1]ヘプタン-2,5(2,6)-ジイル)ビスメチレンジイソシアネートの脂環族イソシアネート、2,4-トリレンジイソシアネート、2,6-トリレンジイソシアネート、4,4'-ジフェニルメタンジイソシアネート、キシリレンジイソシアネート(o-、m-,p-)の芳香族イソシアネート、ヘキサメチレンジイソシアネートやトリレンジイソシアネートなどのジイソシアネート類を主原料としたビュレット構造、ウレトジオン構造、イソシアヌレート構造の多官能イソシアネート、3官能以上のポリオールとのアダクト体として多官能イソシアネート、または、(B12)ウレタンプレポリマーが挙げられる。
その中でも特に好ましいのは、ヘキサメチレンジイソシアネートやトリレンジイソシアネートなどのジイソシアネート類を主原料としたビュレット構造、ウレトジオン構造、イソシアヌレート構造の多官能イソシアネート、3官能以上のポリオールとのアダクト体として多官能イソシアネート、または、(B12)ウレタンプレポリマーが挙げられる。
<(B2)少なくとも2個の水酸基を有するポリオール化合物>
本発明に使用される(B2)ポリオール化合物は、水酸基を1分子中に2個以上有している化合物であれば制限なく使用できる。これらは前記(B12)ウレタンプレポリマー作製に用いられる(B21)2官能ポリオール化合物も含まれる。(B2)成分はウレタン(ウレア)樹脂からなる中空マイクロバルーンにおいて好適に使用される。本発明の中空マイクロバルーンにおいて特に好適に使用される(B2)成分は、水溶性ポリオール化合物である。
本発明に使用される(B2)ポリオール化合物は、水酸基を1分子中に2個以上有している化合物であれば制限なく使用できる。これらは前記(B12)ウレタンプレポリマー作製に用いられる(B21)2官能ポリオール化合物も含まれる。(B2)成分はウレタン(ウレア)樹脂からなる中空マイクロバルーンにおいて好適に使用される。本発明の中空マイクロバルーンにおいて特に好適に使用される(B2)成分は、水溶性ポリオール化合物である。
本発明において水溶性ポリオール化合物は、少なくとも部分的に水中で溶解性があり、疎水性相よりも親水性相で高い親和性を有している化合物であり、一般には、室温で、水のような親水性溶剤中での溶解性が、少なくとも1g/lの溶解性を有するものを選択することができ、好ましくは、親水性溶剤中で20g/l以上の溶解性を有する水溶性化合物が挙げられる。
これら水溶性ポリオール化合物は、分子内に水酸基を2個以上有する多官能アルコールであり、具体的には、エチレングリコール、ジエチレングリコール、トリエチレングリコール、ポリエチレングリコール、プロピレングリコール、ジプロピレングリコール、トリプロピレングリコール、ポリプロピレングリコール、ネオペンチルグリコール、トリメチレングリコール、1,2-ブタンジオール、1,3-ブタンジオール、2,3-ブタンジオール、1,4-ブタンジオール、1,5-ペンタンジオール、ヘキシレングリコール、1,6-ヘキサンジオール、2-ブテン-1,4-ジオール等の2官能ポリオール、グリセリン、トリメチロールエタン、トリメチロールプロパン等の3官能ポリオール、ペンタエリトリトール、エリスリトール、ジグリセロール、ジグリセリン、ジトリメチロールプロパン等の4官能ポリオール、アラビトール等の5官能ポリオールズルシトール、ソルビトール、マンニトール、ジペンタエリスリトール、またはトリグリセロール等の6官能ポリオールボレミトール等の7官能ポリオールイソマルト、マルチトール、イソマルチトール、またはラクチトール等の9官能ポリオールセルロース系化合物(たとえば、メチルセルロース、エチルセルロース、ヒドロキシエチルセルロース、エチルヒドロキシエチルセルロース、カルボキシメチルセルロース、ヒドロキシプロピルセルロースおよびそれらのケン化物など)、デンプン、デキストリン、環状デキストリン、キチン、キトサン、ポリビニルアルコール、ポリグリセリン等の水溶性高分子が挙げられる。
<(B3)少なくとも2個のアミノ基を有する多官能アミン化合物>
本発明に使用される(B3)多官能アミン化合物は、アミノ基を1分子中に2個以上有しているモノマーであれば制限なく使用できる。これらは前記(B12)ウレタンプレポリマー作製に用いられる(B31)2官能アミン化合物も含まれる。(B3)成分はウレタン(ウレア)樹脂、またはアミド樹脂からなる中空マイクロバルーンにおいて好適に使用される。本発明の中空マイクロバルーンにおいて特に好適に使用される(B3)成分は、水溶性ポリアミン化合物である。
本発明に使用される(B3)多官能アミン化合物は、アミノ基を1分子中に2個以上有しているモノマーであれば制限なく使用できる。これらは前記(B12)ウレタンプレポリマー作製に用いられる(B31)2官能アミン化合物も含まれる。(B3)成分はウレタン(ウレア)樹脂、またはアミド樹脂からなる中空マイクロバルーンにおいて好適に使用される。本発明の中空マイクロバルーンにおいて特に好適に使用される(B3)成分は、水溶性ポリアミン化合物である。
水溶性ポリアミン化合物の好ましい溶解性については、前記水溶性ポリオール化合物と同様である。これら水溶性ポリアミン化合物は、分子内にアミノ基を2個以上有する多官能アミンであり、具体的には、エチレンジアミン、プロピレンジアミン、1,4.-ジアミノブタン、ヘキサメチレンジアミン、1.8-ジアミノオクタン、1.10-ジアミノデカン、ジプロピレントリアミン、ビスへキサメチレントリアミン、トリス(2-アミノエチル)アミン、ピペラジン、2-メチルピペラジン、イソホロンジアミン、ジエチレントリアミン、トリエチレンテトラミン、テトラエチレンペンタミン、ヒドラジン、ポリエチレンイミン類、ポリオキシアルキレンアミン類、ポリエチレンイミン等が挙げられる。
<(B4)少なくとも水酸基とアミノ基を両方有する化合物>
本発明で用いられる少なくとも水酸基とアミン基を両方有する化合物としては、分子内に少なくとも水酸基とアミノ基がそれぞれ1個以上有するものであれば制限なく使用できる。(B4)成分はウレタン(ウレア)樹脂からなる中空マイクロバルーンにおいて好適に使用される。特に好適に使用される(B4)成分は、水溶性の分子内に水酸基とアミノ基を両方有する化合物である。
<(B4)少なくとも水酸基とアミノ基を両方有する化合物>
本発明で用いられる少なくとも水酸基とアミン基を両方有する化合物としては、分子内に少なくとも水酸基とアミノ基がそれぞれ1個以上有するものであれば制限なく使用できる。(B4)成分はウレタン(ウレア)樹脂からなる中空マイクロバルーンにおいて好適に使用される。特に好適に使用される(B4)成分は、水溶性の分子内に水酸基とアミノ基を両方有する化合物である。
水溶性の分子内に水酸基とアミノ基を両方有する化合物の好ましい溶解性については、前記水溶性ポリオール化合物と同様である。これら水溶性の分子内に水酸基とアミノ基を両方有する化合物は、具体的には、ヒドロキシルアミン、モノエタノールアミン、3-アミノ-1-プロパノール、2-アミノ-2-ヒドロキシメチルプロパン-1,3-ジオール、2-ヒドロキシエチルエチレンジアミン、2-ヒドロキシエチルプロピレンジアミン、N,N-ジ-2-ヒドロキシエチルエチレンジアミン、N,N-ジ-2-ヒドロキシプロピルエチレンジアミン、N,N-ジ-2-ヒドロキシプロピルプロピレンジアミン、N-メチルエタノールアミン、ジエタノールアミン、N,N-ジ-2-ヒドロキシエチルエチレンジアミン、N,N-ジ-2-ヒドロキシプロピルエチレンジアミン、N,N-ジ-2-ヒドロキシプロピルプロピレンジアミンなどを挙げることができる。
本発明において、(B2)~(B4)成分のなかで、形成されるマイクロバルーンの強度や重合時の反応速度から、(B3)成分が好適である。
<(B5)メラミンホルムアルデヒドプレポリマー化合物>
(B5)メラミンホルムアルデヒドプレポリマー化合物は、メラミンとホルムアルデヒドのメラミン-ホルムアルデヒド初期縮合物であり、常法に従って製造することができる。メラミンとホルムアルデヒドのメラミン-ホルムアルデヒド初期縮合物としては、例えばメチロールメラミンなどが挙げられる。また、メラミンホルムアルデヒドプレポリマー化合物としては、市販されているものも適宜使用できる。たとえば、ベッカミンAPM、ベッカミンM-3、ベッカミンM-3(60)、ベッカミンMA-S 、ベッカミンJ-101、ベッカミンJ-1 01LF(DIC株式会社製)、ニカレジンS-176、ニカレジンS-260(日本カーバイト株式会社製)、ミルベンレジンSM-800(昭和高分子株式会社製)等が挙げられる。
(B5)メラミンホルムアルデヒドプレポリマー化合物は、メラミンとホルムアルデヒドのメラミン-ホルムアルデヒド初期縮合物であり、常法に従って製造することができる。メラミンとホルムアルデヒドのメラミン-ホルムアルデヒド初期縮合物としては、例えばメチロールメラミンなどが挙げられる。また、メラミンホルムアルデヒドプレポリマー化合物としては、市販されているものも適宜使用できる。たとえば、ベッカミンAPM、ベッカミンM-3、ベッカミンM-3(60)、ベッカミンMA-S 、ベッカミンJ-101、ベッカミンJ-1 01LF(DIC株式会社製)、ニカレジンS-176、ニカレジンS-260(日本カーバイト株式会社製)、ミルベンレジンSM-800(昭和高分子株式会社製)等が挙げられる。
(B5)成分は、メラミン樹脂からなる中空マイクロバルーンにおいて好適に使用される。
<(B6)尿素ホルムアルデヒドプレポリマー化合物>
(B6)尿素ホルムアルデヒドプレポリマー化合物は尿素とホルムアルデヒドの尿素-ホルムアルデヒド初期縮合物であり、常法に従って製造することができる。尿素とホルムアルデヒドの尿素-ホルムアルデヒド初期縮合物としては、例えばメチロール尿素などが挙げられる。また、尿素ホルムアルデヒドプレポリマー化合物としては、市販されているものも適宜使用できる。たとえば、8HSP(昭和高分子株式会社製)等が挙げられる。
(B6)尿素ホルムアルデヒドプレポリマー化合物は尿素とホルムアルデヒドの尿素-ホルムアルデヒド初期縮合物であり、常法に従って製造することができる。尿素とホルムアルデヒドの尿素-ホルムアルデヒド初期縮合物としては、例えばメチロール尿素などが挙げられる。また、尿素ホルムアルデヒドプレポリマー化合物としては、市販されているものも適宜使用できる。たとえば、8HSP(昭和高分子株式会社製)等が挙げられる。
(B6)成分は、尿素樹脂からなる中空マイクロバルーンにおいて好適に使用される。
<(B7)少なくとも2個のカルボキシル基を有する多官能カルボン酸化合物>
(B7)多官能カルボン酸化合物としては、ジカルボン酸化合物が好適であり、該ジカルボン酸化合物としては、コハク酸、アジピン酸、セバシン酸、ドデセニルコハク酸、アゼライン酸、セバシン酸、ドデカンジカルボン酸、オクタデカンジカルボン酸、ドデセニルコハク酸、ペンタデセニルコハク酸、オクタデセニルコハク酸 、マレイン酸、フマール酸などのアルケニレンジカルボン酸、デシルコハク酸、ドデシルコハク酸、オクタデシルコハク酸、フタル酸、イソフタル酸、テレフタル酸、ナフタレンジカルボン酸などが挙げられる。
(B7)多官能カルボン酸化合物としては、ジカルボン酸化合物が好適であり、該ジカルボン酸化合物としては、コハク酸、アジピン酸、セバシン酸、ドデセニルコハク酸、アゼライン酸、セバシン酸、ドデカンジカルボン酸、オクタデカンジカルボン酸、ドデセニルコハク酸、ペンタデセニルコハク酸、オクタデセニルコハク酸 、マレイン酸、フマール酸などのアルケニレンジカルボン酸、デシルコハク酸、ドデシルコハク酸、オクタデシルコハク酸、フタル酸、イソフタル酸、テレフタル酸、ナフタレンジカルボン酸などが挙げられる。
また、ジカルボン酸ジハロゲン化物も含まれる。それらの具体例は、脂肪族ジカルボン酸ジハロゲン化物、脂環族ジカルボン酸ジハロゲン化物、および芳香族ジカルボン酸ジハロゲン化物が挙げられる。
脂肪族ジカルボン酸ジハロゲン化物としては、たとえば、シュウ酸ジクロライド、マロン酸ジクロライド、コハク酸ジクロライド、フマル酸ジクロライド、グルタル酸ジクロライド、アジピン酸ジクロライド、ムコン酸ジクロライド、セバシン酸ジクロライド、ノナン酸ジクロライド、ウンデカン酸ジクロライド、シュウ酸ジブロマイド、マロン酸ジブロマイド、コハク酸ジブロマイド、フマル酸ジブロマイド等が挙げられる。
脂環族ジカルボン酸ジハロゲン化物としては、たとえば1,2-シクロプロパンジカルボン酸ジクロライド、1,3-シクロブタンジカルボン酸ジクロライド、1,3-シクロペンタンジカルボン酸ジクロライド、1,3-シクロヘキサンジカルボン酸ジクロライド、1,4-シクロヘキサンジカルボン酸ジクロライド、1,3-シクロペンタンジカルボン酸ジクロライド、1,2-シクロプロパンジカルボン酸ジブロマイド、1,3-シクロブタンジカルボン酸ジブロマイド等が挙げられる。
芳香族ジカルボン酸ジハロゲン化物としては、たとえば、フタル酸ジクロライド、イソフタル酸ジクロライド、テレフタル酸ジクロライド、1,4-ナフタレンジカルボン酸ジクロライド、1,5-(9-オキソフルオレン)ジカルボン酸ジクロライド、1,4-アントラセンジカルボン酸ジクロライド、1,4-アントラキノンジカルボン酸ジクロライド、2,5-ビフェニルジカルボン酸ジクロライド、1,5-ビフェニレンジカルボン酸ジクロライド、4,4’-ビフェニルジカルボニルクロライド、4,4’-メチレン二安息香酸ジクロライド、4,4’-イソプロピリデン二安息香酸ジクロライド、4,4’-ビベンジルジカルボン酸ジクロライド、4,4’-スチルベンジカルボン酸ジクロライド、4,4’-トランジカルボン酸ジクロライド、4,4’-カルボニル二安息香酸ジクロライド、4,4’-オキシ二安息香酸ジクロライド、4,4’-スルホニル二安息香酸ジクロライド、4,4’-ジチオ二安息香酸ジクロライド、p-フェニレン二酢酸ジクロライド、3,3’-p-フェニレンジプロピオン酸ジクロライド 、フタル酸ジブロマイド、イソフタル酸ジブロマイド、テレフタル酸ジブロマイド等が挙げられる。
本発明において(B7)成分で好ましい例を挙げると、重合速度の観点から、ジカルボン酸ジハロゲン化物が挙げられる。
本発明の中空マイクロバルーンを形成する樹脂は、上記したとおり(A)成分及び(B)成分を含む重合性組成物を重合させて得られる。該重合組成物は、(A)成分及び(B)成分以外の成分を含んでもよいが、(A)成分及び(B)成分のみからなるものであることが好ましい。
<中空マイクロバルーンの製造方法>
本発明の中空マイクロバルーンの製造方法は、公知の方法が制限なく使用することができ、たとえば、界面重合、コアセルベーション法、In-situ重合等の水相と油相によるエマルションを利用した既知の手法を用いてマイクロバルーンを作製した後、内部の液体を取り除くことで中空マイクロバルーンを製造する方法を採用すればよい。
本発明の中空マイクロバルーンの製造方法は、公知の方法が制限なく使用することができ、たとえば、界面重合、コアセルベーション法、In-situ重合等の水相と油相によるエマルションを利用した既知の手法を用いてマイクロバルーンを作製した後、内部の液体を取り除くことで中空マイクロバルーンを製造する方法を採用すればよい。
本発明の中空マイクロバルーンは、ウレタン(ウレア)樹脂、メラミン樹脂、尿素樹脂及びアミド樹脂からなる群から選ばれた少なくとも1種の樹脂からなることが好ましい。これらの樹脂からなる中空マイクロバルーンとすることにより、優れた特性のみならず、CMP用研磨パッドにした際に優れた研磨特性を発現できる。
本発明の中空マイクロバルーンは、具体的には、たとえば、以下の方法で製造できるが、以下の方法に限定されない。なお、(A)ポリロタキサンモノマーは、選択する環状分子や側鎖の種類、導入量により、親水性か親油性が変化するため、使用する(A)ポリロタキサンモノマーの親油性を確認した後、水相、または油相に溶解させて使用すればよい。
<中空マイクロバルーンがウレタン(ウレア)樹脂、またはアミド樹脂からなる場合>
中空マイクロバルーンがウレタン(ウレア)樹脂、またはアミド樹脂からなる場合、界面重合により作製できる。界面重合の場合、水中油(O/W)エマルション(以下、O/Wエマルションともいう。)または、油中水(W/O)エマルション(以下、W/Oエマルションともいう。)を作製した後に、界面で重合することでマイクロバルーンを作製することができる。本発明においては、O/Wエマルション、または、W/Oエマルションのどちらも選択可能であるが、O/Wエマルションによる界面重合が効率よく中空マイクロバルーンを作製可能であるから好ましい。下記に、O/Wエマルションでの界面重合法を例示する。なお、「アミド樹脂からなる場合」以外は、ウレタン(ウレア)樹脂の例示である。
中空マイクロバルーンがウレタン(ウレア)樹脂、またはアミド樹脂からなる場合、界面重合により作製できる。界面重合の場合、水中油(O/W)エマルション(以下、O/Wエマルションともいう。)または、油中水(W/O)エマルション(以下、W/Oエマルションともいう。)を作製した後に、界面で重合することでマイクロバルーンを作製することができる。本発明においては、O/Wエマルション、または、W/Oエマルションのどちらも選択可能であるが、O/Wエマルションによる界面重合が効率よく中空マイクロバルーンを作製可能であるから好ましい。下記に、O/Wエマルションでの界面重合法を例示する。なお、「アミド樹脂からなる場合」以外は、ウレタン(ウレア)樹脂の例示である。
O/Wエマルションでの重合方法を細分化すると、第1工程:(a)少なくとも(B1)成分(アミド樹脂からなる場合は(B7)成分)と有機溶媒とを含む油相(以下、(a)成分ともいう)を調製する工程、第2工程:(b)乳化剤を含む水相(以下、(b)成分ともいう)を調製する工程、第3工程:前記(a)成分と前記(b)成分とを混合・撹拌して、前記水相が連続相、前記油相が分散相としてなるO/Wエマルションを調製する工程、第4工程:前記O/Wエマルション中に、(B2)~(B4)成分(アミド樹脂からなる場合は(B3)~(B4)成分(「アミド樹脂からなる場合」の(B4)成分は、少なくともアミノ基を2つ以上有する(B4)成分に限る。以下、同様である。))から選ばれる親水性の化合物を加えて、前記O/Wエマルションの界面上で重合を進行させ、樹脂膜を形成させてマイクロバルーンとし、マイクロバルーンが分散したマイクロバルーン分散液を得る工程、第5工程:前記マイクロバルーン分散液からマイクロバルーンを分離する工程、第6工程:前記マイクロバルーンの内部から、有機溶媒溶液を取り除く工程に分別される。ここで、本発明の(A)ポリロタキサンモノマーが親油性の場合、(A)ポリロタキサンモノマーは、第1工程の(a)成分に均一に溶解させればよく、(A)ポリロタキサンモノマーが親水性の場合、(A)ポリロタキサンモノマーは、第4工程で(B2)~(B4)成分(アミド樹脂からなる場合は(B3)~(B4)成分)から選ばれる親水性の化合物と一緒にO/Wエマルションに加えればよい。こうすることで、(A)ポリロタキサンモノマーは前記(B1)成分(アミド樹脂からなる場合は(B7)成分)と反応することが可能となる。
第1工程:
第1工程は、O/Wエマルションにおいて分散相となる(a)少なくとも(B1)成分(アミド樹脂からなる場合は(B7)成分)と有機溶媒とを含む油相を調製する工程である。
第1工程は、O/Wエマルションにおいて分散相となる(a)少なくとも(B1)成分(アミド樹脂からなる場合は(B7)成分)と有機溶媒とを含む油相を調製する工程である。
この工程は、後述する有機溶媒中に、(B1)成分(アミド樹脂からなる場合は(B7)成分)を溶解させて油相とする工程であり、公知の方法で溶解させて均一な溶液とすれはよい。また、(A)ポリロタキサンモノマーが親油性の場合、(A)成分を上記油相の溶液に溶解させて均一な溶液とした(a)成分を調製すればよい。
中空マイクロバルーンがウレタン(ウレア)樹脂からなる場合、好ましい(B1)成分の使用量は、有機溶媒100質量部に対して0.1~50質量部、好ましくは0.5~20質量部、さらに好ましくは1~10質量部である。さらに、(B1)成分が含有しているイソシアネート基のモル数(n1)に対し、(A)成分と(B2)~(B4)成分の合計の活性水素基含有化合物のモル数が(n2)の場合、0.5≦(n1)/(n2)≦2の範囲であることが好ましい。
中空マイクロバルーンがアミド樹脂からなる場合、好ましい(B7)成分の使用量は、有機溶媒100質量部に対して0.1~50質量部、好ましくは0.5~20質量部、さらに好ましくは1~10質量部である。さらに、(B7)成分が含有しているカルボン酸基のモル数(n3)に対し、(A)成分と(B3)~(B4)成分の合計の活性水素基含有化合物のモル数が(n4)の場合、0.5≦(n3)/(n4)≦2の範囲であることが好ましい。
また、(a)成分には、界面重合の反応を促進させる目的のため、後述する触媒を添加してもよい。
第2工程:
第2工程は、O/Wエマルションにおいて連続相となる、(b)乳化剤と水とを含む水相を調製する工程である。
第2工程は、O/Wエマルションにおいて連続相となる、(b)乳化剤と水とを含む水相を調製する工程である。
この工程は、水中に、後述する乳化剤を溶解させて水相とする工程であり、公知の方法で溶解させて均一な溶液とすれはよい。
本発明において乳化剤の使用量は、水100質量部に対して0.01~20質量部、好ましくは0.1~10質量部である。この範囲であれば、O/Wエマルション中の分散相の液滴の凝集が回避され、平均粒径が揃ったマイクロバルーンが得られ易い。
また、(b)成分には、界面重合の反応を促進させる目的のため、後述する触媒を添加してもよい。
第3工程:
第3工程は、第1工程で得られた(a)成分と第2工程で得られた(b)成分とを混合・撹拌して、(a)成分が分散相、(b)成分が連続相としてなるO/Wエマルションを調製する工程である。
第3工程は、第1工程で得られた(a)成分と第2工程で得られた(b)成分とを混合・撹拌して、(a)成分が分散相、(b)成分が連続相としてなるO/Wエマルションを調製する工程である。
本発明において、(a)成分と(b)成分とを混合、攪拌してO/Wエマルションとする方法は、製造したいマイクロバルーンの粒径を勘案して、適宜公知の方法により混合・撹拌させることにより調製することができる。
その中でも、(a)成分と(b)成分とを混合させた後、撹拌として高速せん断式、摩擦式、高圧ジェット式、超音波式等の公知の分散機を用いて分散する方法によって、O/Wエマルション化する方法が好適に採用され、これらのなかでも高速せん断式が好ましい。高速せん断式分散機を使用した場合、回転数は、好ましくは500~20,000rpm、さらに好ましくは1,000~10,000rpmである。分散時間は、好ましくは0.1~60分であり、好ましくは、0.5~30分である。分散温度は、好ましくは10~40℃である。
また、本発明において(a)成分と(b)成分の重量比は、(b)成分を100質量部とした際に、(a)成分が1~100質量部であることが好ましく、さらに好ましくは、2~90質量部であり、もっとも好ましくは、5~50質量部であることが好ましい。この範囲であれば、良好なエマルションが得られる。
第4工程:
第4工程は、前記O/Wエマルション中に(B2)~(B4)成分(アミド樹脂からなる場合は(B3)~(B4)成分)から選択される少なくとも1種類の化合物を加えて、O/Wエマルションの界面上で重合させて樹脂膜を形成させ、マイクロバルーンとすることにより、該マイクロバルーンが分散したマイクロバルーン分散液を得る工程である。また、(A)ポリロタキサンモノマーが親水性の場合は、第4工程において、(B2)~(B4)成分(アミド樹脂からなる場合は(B3)~(B4)成分)から選択される少なくとも1種類の化合物と同様にO/Wエマルション中に加えればよい。
第4工程は、前記O/Wエマルション中に(B2)~(B4)成分(アミド樹脂からなる場合は(B3)~(B4)成分)から選択される少なくとも1種類の化合物を加えて、O/Wエマルションの界面上で重合させて樹脂膜を形成させ、マイクロバルーンとすることにより、該マイクロバルーンが分散したマイクロバルーン分散液を得る工程である。また、(A)ポリロタキサンモノマーが親水性の場合は、第4工程において、(B2)~(B4)成分(アミド樹脂からなる場合は(B3)~(B4)成分)から選択される少なくとも1種類の化合物と同様にO/Wエマルション中に加えればよい。
また、(B2)~(B4)成分(アミド樹脂からなる場合は(B3)~(B4)成分)、および(A)成分をO/Wエマルション中に加える場合は、そのまま加えてもよく、予め水に溶解させて使用してもよい。
予め水に溶解させる場合、(B2)~(B4)成分(アミド樹脂からなる場合は(B3)~(B4)成分)、および(A)成分の合計量を100質量部とした際、水が50~10,000質量部の範囲で用いるのが好適である。
反応温度は、O/Wエマルションが壊れない温度であれば特に制限なく、好ましくは、5~70℃の範囲で反応を実施するのが好ましい。反応時間もW/Oエマルションが形成できれば特に制限なく、通常は0.5~24時間の範囲から選択される。
第5工程
第5工程は、前記のマイクロバルーン分散液からマイクロバルーンを分離する工程である。マイクロバルーン分散液からマイクロバルーンを分離する分離方法は、特に制限なく一般的な分離手法から選択すればよく、具体的には、濾別や遠心分離等が用いられる。
第5工程は、前記のマイクロバルーン分散液からマイクロバルーンを分離する工程である。マイクロバルーン分散液からマイクロバルーンを分離する分離方法は、特に制限なく一般的な分離手法から選択すればよく、具体的には、濾別や遠心分離等が用いられる。
第6工程
第6工程は、第5工程で得られた前記のマイクロバルーンから、内部の油相を取り除き、中空マイクロバルーンにする工程である。マイクロバルーンから油相を取り除く方法は、特に制限なく一般的な分離手法から選択すればよく、具体的には、循風乾燥機、スプレードライヤー、流動層式乾燥機、真空乾燥機等が用いられる。乾燥する場合の温度としては、好ましくは40~250℃、さらに好ましくは50~200℃である。
第6工程は、第5工程で得られた前記のマイクロバルーンから、内部の油相を取り除き、中空マイクロバルーンにする工程である。マイクロバルーンから油相を取り除く方法は、特に制限なく一般的な分離手法から選択すればよく、具体的には、循風乾燥機、スプレードライヤー、流動層式乾燥機、真空乾燥機等が用いられる。乾燥する場合の温度としては、好ましくは40~250℃、さらに好ましくは50~200℃である。
<中空マイクロバルーンがメラミン樹脂、または尿素樹脂からなる場合>
中空マイクロバルーンがメラミン樹脂または尿素樹脂からなる場合も、O/Wエマルションを形成後、界面重合やIn-situ重合により作製できる。下記に具体例を示すが、本発明の製造方法はこれに限定されない。
中空マイクロバルーンがメラミン樹脂または尿素樹脂からなる場合も、O/Wエマルションを形成後、界面重合やIn-situ重合により作製できる。下記に具体例を示すが、本発明の製造方法はこれに限定されない。
中空マイクロバルーンがメラミン樹脂、または尿素樹脂からなる場合のO/Wエマルションでの重合方法を細分化すると、第1工程:(c)有機溶媒を含む油相(以下、(c)成分ともいう)を調製する工程、第2工程:(d)乳化剤を含む水相(以下、(d)成分ともいう)を調製する工程、第3工程:前記(c)成分と前記(d)成分とを混合・撹拌して、前記水相が連続相、前記油相が分散相としてなるO/Wエマルションを調製する工程、第4工程:前記O/Wエマルション中に、(B5)成分、または(B6)成分を添加し、前記O/Wエマルションの界面上で重合を進行させて、樹脂相を形成させ、マイクロバルーンが分散したマイクロバルーン分散液を得る工程、第5工程:前記マイクロバルーン分散液からマイクロバルーンを分離する工程、第6工程:前記マイクロバルーンの内部から、有機溶媒溶液を取り除く工程に分別される。ここで、本発明の(A)ポリロタキサンモノマーが親油性の場合、第1工程の油相に均一に溶解させればよく、(A)ポリロタキサンモノマーが親水性の場合、第4工程で(B5)成分、または(B6)成分と同様に添加すれば良い。こうすることで、(A)ポリロタキサンモノマーは、前記(B5)成分、または(B6)成分と共に、マイクロバルーンを構成する樹脂中に取り込まれる。
第1工程:
第1工程は、O/Wエマルションにおいて分散相となる、(c)有機溶媒を含む油相を調製する工程である。
第1工程は、O/Wエマルションにおいて分散相となる、(c)有機溶媒を含む油相を調製する工程である。
この工程では、(A)ポリロタキサンモノマーが親油性の場合、前記有機溶媒中に(A)成分を溶解させて均一な油相を調製すればよい。
一方、(A)ポリロタキサンモノマーが親水性の場合、前記有機溶媒中に(A)成分を溶解させることはないので、単に有機溶媒を油相とすればよい。
第2工程:
第2工程は、O/Wエマルションにおいて連続相となる、(d)乳化剤と水とを含む水相であり、且つpHを調製する工程である。
第2工程は、O/Wエマルションにおいて連続相となる、(d)乳化剤と水とを含む水相であり、且つpHを調製する工程である。
この工程は、水中に、後述する乳化剤を溶解させ、pHを調製する工程が含まれる。pHの調製等は公知の方法を用いて調合すればよい。
本発明において乳化剤の使用量は、水100質量部に対して0.01~20質量部、好ましくは0.1~10質量部である。この範囲であれば、O/Wエマルション中の分散相の液滴の凝集が回避され、平均粒径が揃ったマイクロバルーンが得られ易い。
また、好ましいpHとしては、pHを7未満、さらに好ましくは、pHは3.5~6.5、最も好ましいのはpHが4.0~5.5に調製されることが好ましい。このpH域とすることにより、後述する(B5)成分、または(B6)成分の重合を進行させることが可能となる。
第3工程:
第3工程は、第1工程で得られた(c)成分と第2工程で得られた(d)成分とを混合・撹拌して、(c)成分が分散相、(d)成分が連続相としてなるO/Wエマルションを調製する工程である。
第3工程は、第1工程で得られた(c)成分と第2工程で得られた(d)成分とを混合・撹拌して、(c)成分が分散相、(d)成分が連続相としてなるO/Wエマルションを調製する工程である。
本発明において、(c)成分と(d)成分とを混合、攪拌してO/Wエマルションとする方法は、製造したいマイクロバルーンの粒径を勘案して、適宜公知の方法により混合・撹拌させることにより調製することができる。さらに、O/Wエマルションを調製する工程において、温度やpHを調製することもできる。
その中でも、(c)成分と(d)成分とを混合させた後、撹拌として高速せん断式、摩擦式、高圧ジェット式、超音波式等の公知の分散機を用いて分散する方法によって、O/Wエマルション化する方法が好適に採用され、これらのなかでも高速せん断式が好ましい。高速せん断式分散機を使用した場合、回転数は、好ましくは500~20,000rpm、さらに好ましくは1,000~10,000rpmである。分散時間は、好ましくは0.1~60分であり、好ましくは、0.5~30分である。分散温度は、好ましくは20~90℃が好ましい。
また、本発明において(c)成分と(d)成分の重量比は、(d)成分を100質量部とした際に、(c)成分が1~100質量部であることが好ましく、さらに好ましくは、2~90質量部であり、もっとも好ましくは、5~50質量部であることが好ましい。この範囲であれば、良好なエマルションが得られる。
第4工程:
第4工程は、前記O/Wエマルション中に(B5)成分、または(B6)成分を加えて、O/Wエマルションの界面上で重合を進行させて、樹脂膜を形成させ、マイクロバルーンとすることにより、形成したマイクロバルーンが分散したマイクロバルーン分散液を得る工程である。
第4工程は、前記O/Wエマルション中に(B5)成分、または(B6)成分を加えて、O/Wエマルションの界面上で重合を進行させて、樹脂膜を形成させ、マイクロバルーンとすることにより、形成したマイクロバルーンが分散したマイクロバルーン分散液を得る工程である。
用いる(B5)成分、または(B6)成分の使用量は、特に制限されないが、良好にマイクロバルーンを形成させるためには、第1工程で用いた有機溶媒100質量部あたり、0.5~50質量部であることが好ましく、1~20質量部であることがより好ましい。
(A)ポリロタキサンモノマーが親水性の場合は、第4工程において、(B5)成分、または(B6)成分と同様にO/Wエマルション中に加えればよい。
また、(B5)成分、または(B6)成分、および(A)成分をO/Wエマルション中に加える場合は、そのまま加えてもよく、水に溶解させて使用してもよい。
水に溶解させる場合、(B5)成分、または(B6)成分、および(A)成分の合計量を100質量部とした際、水が50~10,000質量部の範囲で用いるのが好適である。
連続相である水相のpHは第2工程で調製してもよく、第4工程の、(B5)成分、または(B6)成分を加えた後に、調製してもよい。連続相である水相のpHは、少なくとも7未満であることが好ましい。好ましい反応温度は、40~90℃の範囲で反応を実施するのが好ましい。反応時間は1~48時間の範囲で実施されるのが好ましい。
第5工程、第6工程
第5工程、第6工程は前記中空マイクロバルーンがウレタン(ウレア)樹脂(またはポリアミド樹脂)からなる場合と同様の工程である。
第5工程、第6工程は前記中空マイクロバルーンがウレタン(ウレア)樹脂(またはポリアミド樹脂)からなる場合と同様の工程である。
<好適な配合割合>
本発明の中空マイクロバルーンを構成する樹脂の製造に用いる重合性組成物中の(A)ポリロタキサンモノマーの含有量は、(A)ポリロタキサンモノマーと(B)重合性モノマーの合計100質量部に対し、1~50質量部であることが好ましい。この割合で(A)ポリロタキサンモノマーを含有することで、優れた耐久性や、特性を発現することが可能となる。また、該中空マイクロバルーンをCMP用研磨パッドに利用した場合、優れた耐久性のみならず、優れた研磨特性を発現することが可能となる。
本発明の中空マイクロバルーンを構成する樹脂の製造に用いる重合性組成物中の(A)ポリロタキサンモノマーの含有量は、(A)ポリロタキサンモノマーと(B)重合性モノマーの合計100質量部に対し、1~50質量部であることが好ましい。この割合で(A)ポリロタキサンモノマーを含有することで、優れた耐久性や、特性を発現することが可能となる。また、該中空マイクロバルーンをCMP用研磨パッドに利用した場合、優れた耐久性のみならず、優れた研磨特性を発現することが可能となる。
中でも、さらに好ましくは、(A)ポリロタキサンモノマーと(B)重合性モノマーの合計100質量部に対し、(A)成分が2~40質量部、さらに好ましくは、(A)成分が3~30質量部であることが好ましい。
(A)成分の含有量は、重合した樹脂を固体NMR等の分析からも求めることはできるが、一般的には、使用量から求められる。O/Wエマルションの場合、油相に含有した(A)成分、および、(B)成分は使用量の全量がマイクロバルーンを構成する樹脂中に含有すると考えられる。一方、水相に添加した(A)成分、および、(B)成分も、前記した好ましい範囲内での使用量あれば、使用量の全量がマイクロバルーンを構成する樹脂中に含有すると考えられる。また、好ましい範囲外、つまり、第4工程での(B)成分や(A)成分を好ましい範囲外で添加した際は、反応終了後の水相を分析することで重合に関与しなかった残存している(B)成分や(A)成分を同定することが出来る。これらを考慮することで、マイクロバルーン形成に関与したモノマー量を規定することが可能となる。
すなわち、換言すると、本発明における中空マイクロバルーンを構成する樹脂における、(A)成分の含有量は、(A)成分と(B)成分の合計100質量に対して、好ましくは1~50質量部であり、より好ましくは2~40質量部であり、さらに好ましくは3~30質量部である。
すなわち、換言すると、本発明における中空マイクロバルーンを構成する樹脂における、(A)成分の含有量は、(A)成分と(B)成分の合計100質量に対して、好ましくは1~50質量部であり、より好ましくは2~40質量部であり、さらに好ましくは3~30質量部である。
上記に記載した範囲とすることにより、エマルション中で効率よくマイクロバルーンを作製可能である。
以下に本発明で用いられる各成分について説明する。
<乳化剤>
本発明において、(b)成分または(d)成分に用いられる乳化剤には、分散剤、界面活性剤、またはこれらの組み合わせが含まれる。
本発明において、(b)成分または(d)成分に用いられる乳化剤には、分散剤、界面活性剤、またはこれらの組み合わせが含まれる。
分散剤としては、たとえば、ポリビニルアルコールおよびその変性物(たとえば、アニオン変性ポリビニルアルコール)、セルロース系化合物(たとえば、メチルセルロース、エチルセルロース、ヒドロキシエチルセルロース、エチルヒドロキシエチルセルロース、カルボキシメチルセルロース、ヒドロキシプロピルセルロースおよびそれらのケン化物など)、ポリアクリル酸アミドおよびその誘導体、エチレン-酢酸ビニル共重合体、スチレン-無水マレイン酸共重合体、エチレン-無水マレイン酸共重合体、イソブチレン-無水マレイン酸共重合体、ポリビニルピロリドン、エチレン-アクリル酸共重合体、酢酸ビニル-アクリル酸共重合体、ポリアクリル酸ナトリウム、ポリアクリル酸カリウム、ポリアクリル酸アンモニウム、ポリアクリル酸の部分中和物、アクリル酸ナトリウムーアクリル酸エステル共重合体、カルボキシメチルセルロース、カゼイン、ゼラチン、デキストリン、キチン、キトサン、澱粉誘導体、アラビアゴムおよびアルギン酸ナトリウムなどが挙げられる。
これらの分散剤は、本発明で用いる重合性組成物と反応しない、または極めて反応し難いことが好ましく、たとえばゼラチンなどの分子鎖中に反応性のアミノ基を有するものは、予め反応性を失わせる処理をしておくことが好ましい。
これらの分散剤は、本発明で用いる重合性組成物と反応しない、または極めて反応し難いことが好ましく、たとえばゼラチンなどの分子鎖中に反応性のアミノ基を有するものは、予め反応性を失わせる処理をしておくことが好ましい。
界面活性剤としては、アニオン界面活性剤、カチオン界面活性剤、両性界面活性剤、非イオン界面活性剤などが挙げられる。界面活性剤は2種以上の界面活性剤を併用したものであってもよい。
アニオン界面活性剤としては、カルボン酸またはその塩、硫酸エステル塩、カルボキシメチル化物の塩、スルホン酸塩およびリン酸エステル塩が挙げられる。
カルボン酸またはその塩としては、炭素数8~22の飽和または不飽和脂肪酸またはその塩が挙げられ、具体的にはカプリン酸、ラウリン酸、ミリスチン酸、パルミチン酸、ステアリン酸、アラキジン酸、ベヘン酸、オレイン酸、リノール酸、リシノール酸およびヤシ油、パーム核油、米ぬか油、牛脂などをケン化して得られる高級脂肪酸の混合物があげられる。塩としてはそれらのナトリウム、カリウム、アンモニウム、アルカノールアミンなどの塩があげられる。
硫酸エステル塩としては、高級アルコール硫酸エステル塩(炭素数8~18の脂肪族アルコールの硫酸エステル塩)、高級アルキルエーテル硫酸エステル塩(炭素数8~18の脂肪族アルコールのエチレンオキサイド付加物の硫酸エステル塩)、硫酸化油(不飽和油脂または不飽和のロウをそのまま硫酸化して中和したもの)、硫酸化脂肪酸エステル(不飽和脂肪酸の低級アルコールエステルを硫酸化して中和したもの)および、硫酸化オレフィン(炭素数12~18のオレフィンを硫酸化して中和したもの)が挙げられる。塩としては、ナトリウム塩,カリウム塩,アンモニウム塩,アルカノールアミン塩が挙げられる。
高級アルコール硫酸エステル塩の具体例としては、オクチルアルコール硫酸エステル塩、デシルアルコール硫酸エステル塩、ラウリルアルコール硫酸エステル塩、ステアリルアルコール硫酸エステル塩、オキソ法で合成されたアルコール(オキソコール900、トリデカノール:協和発酵製)の硫酸エステル塩が挙げられる。
高級アルキルエーテル硫酸エステル塩の具体例としては、ラウリルアルコールエチレンオキサイド2モル付加物硫酸エステル塩、オクチルアルコールエチレンオキサイド3モル付加物硫酸エステル塩が挙げられる。
硫酸化油の具体例としては、ヒマシ油、落花生油、オリーブ油、ナタネ油、牛脂、羊脂などの硫酸化物のナトリウム、カリウム、アンモニウム、アルカノールアミン塩が挙げられる。
硫酸化脂肪酸エステルの具体例としては、オレイン酸ブチル,リシノレイン酸ブチルなどの硫酸化物のナトリウム、カリウム、アンモニウム、アルカノールアミン塩が挙げられる。
カルボキシメチル化物の塩としては、炭素数8~16の脂肪族アルコールのカルボキシメチル化物の塩および炭素数8~16の脂肪族アルコールのエチレンオキサイド付加物のカルボキシメチル化物の塩が挙げられる。
脂肪族アルコールのカルボキシメチル化物の塩の具体例としては、オクチルアルコールカルボキシメチル化ナトリウム塩、デシルアルコールカルボキシメチル化ナトリウム塩、ラウリルアルコールカルボキシメチル化ナトリウム塩、トリデカノールカルボキシメチル化ナトリウム塩などが挙げられる。
脂肪族アルコールのエチレンオキサイド付加物のカルボキシメチル化物の塩の具体例としては、オクチルアルコールエチレンオキサイド3モル付加物カルボキシメチル化ナトリウム塩、ラウリルアルコールエチレンオキサイド4モル付加物カルボキシメチル化ナトリウム塩、トリデカノールエチレンオキサイド5モル付加物カルボキシメチル化ナトリウム塩などが挙げられる。
スルホン酸塩としては、アルキルベンゼンスルホン酸塩、アルキルナフタレンスルホン酸塩、スルホコハク酸ジエステル型、α-オレフィンスルホン酸塩、イゲポンT型、その他芳香環含有化合物のスルホン酸塩が挙げられる。
アルキルベンゼンスルホン酸塩の具体例としては、ドデシルベンゼンスルホン酸ナトリウム塩などが挙げられる。
アルキルナフタレンスルホン酸塩の具体例としては、ドデシルナフタレンスルホン酸ナトリウム塩などが挙げられる。
スルホコハク酸ジエステル型の具体例としては、スルホコハク酸ジ-2-エチルヘキシルエステルナトリウム塩などが挙げられる。
芳香環含有化合物のスルホン酸塩としては、アルキル化ジフェニルエーテルのモノまたはジスルホン酸塩、スチレン化フェノールスルホン酸塩などが挙げられる。
リン酸エステル塩としては、高級アルコールリン酸エステル塩、および高級アルコールエチレンオキサイド付加物リン酸エステル塩が挙げられる。
高級アルコールリン酸エステル塩の具体例としては、ラウリルアルコールリン酸モノエステルジナトリウム塩、ラウリルアルコールリン酸ジエステルナトリウム塩などが挙げられる。
高級アルコールエチレンオキサイド付加物リン酸エステル塩の具体例としては、オレイルアルコールエチレンオキサイド5モル付加物リン酸モノエステルジナトリウム塩が挙げられる。
カチオン界面活性剤としては、第4級アンモニウム塩型、アミン塩型などが挙げられる。
第4級アンモニウム塩型としては、3級アミン類と4級化剤(メチルクロライド、メチルブロマイド、エチルクロライド、ベンジルクロライド、ジメチル硫酸などのアルキル化剤、エチレンオキサイドなど)との反応で得られ、たとえば、ラウリルトリメチルアンモニウムクロライド、ジデシルジメチルアンモニウムクロライド、ジオクチルジメチルアンモニウムブロマイド、ステアリルトリメチルアンモニウムブロマイド、ラウリルジメチルベンジルアンモニウムクロライド(塩化ベンザルコニウム)、セチルピリジニウムクロライド、ポリオキシエチレントリメチルアンモニウムクロライド、ステアラミドエチルジエチルメチルアンモニウムメトサルフェートなどが挙げられる。
アミン塩型としては、1~3級アミン類を無機酸(塩酸、硝酸、硫酸、ヨウ化水素酸など)または有機酸(酢酸、ギ酸、蓚酸、乳酸、グルコン酸、アジピン酸、アルキル燐酸など)で中和することにより得られる。たとえば、第1級アミン塩型のものとしては、脂肪族高級アミン(ラウリルアミン、ステアリルアミン、セチルアミン、硬化牛脂アミン、ロジンアミンなどの高級アミン)の無機酸塩または有機酸塩、低級アミン類の高級脂肪酸(ステアリン酸、オレイン酸など)塩などが挙げられる。
第2級アミン塩型のものとしては、たとえば、脂肪族アミンのエチレンオキサイド付加物などの無機酸塩または有機酸塩が挙げられる。
また、第3級アミン塩型のものとしては、たとえば、脂肪族アミン(トリエチルアミン、エチルジメチルアミン、N,N,N’,N’-テトラメチルエチレンジアミンなど)、脂肪族アミンのエチレンオキサイド付加物、脂環式アミン(N-メチルピロリジン、N-メチルピペリジン、N-メチルヘキサメチレンイミン、N-メチルモルホリン、1,8-ジアザビシクロ(5,4,0)-7-ウンデセンなど)、含窒素ヘテロ環芳香族アミン(4-ジメチルアミノピリジン、N-メチルイミダゾール、4,4’-ジピリジルなど)の無機酸塩または有機酸塩、トリエタノールアミンモノステアレート、ステアラミドエチルジエチルメチルエタノールアミンなどの3級アミン類の無機酸塩または有機酸塩などが挙げられる。
両性界面活性剤としては、カルボン酸塩型両性界面活性剤、硫酸エステル塩型両性界面活性剤、スルホン酸塩型両性界面活性剤、リン酸エステル塩型両性界面活性剤などが挙げられ、カルボン酸塩型両性界面活性剤は、さらにアミノ酸型両性界面活性剤とベタイン型両性界面活性剤が挙げられる。
カルボン酸塩型両性界面活性剤は、アミノ酸型両性界面活性剤、ベタイン型両性界面活
性剤、イミダゾリン型両性界面活性剤などが挙げられ、これらのうち、アミノ酸型両性界面活性剤は、分子内にアミノ基とカルボキシル基を持っている両性界面活性剤で、具体的には、たとえば、アルキルアミノプロピオン酸型両性界面活性剤(ステアリルアミノプロピオン酸ナトリウム、ラウリルアミノプロピオン酸ナトリウムなど)、アルキルアミノ酢酸型両性界面活性剤(ラウリルアミノ酢酸ナトリウムなど)などが挙げられる。
性剤、イミダゾリン型両性界面活性剤などが挙げられ、これらのうち、アミノ酸型両性界面活性剤は、分子内にアミノ基とカルボキシル基を持っている両性界面活性剤で、具体的には、たとえば、アルキルアミノプロピオン酸型両性界面活性剤(ステアリルアミノプロピオン酸ナトリウム、ラウリルアミノプロピオン酸ナトリウムなど)、アルキルアミノ酢酸型両性界面活性剤(ラウリルアミノ酢酸ナトリウムなど)などが挙げられる。
ベタイン型両性界面活性剤は、分子内に第4級アンモニウム塩型のカチオン部分とカルボン酸型のアニオン部分を持っている両性界面活性剤で、たとえば、アルキルジメチルベタイン(ステアリルジメチルアミノ酢酸ベタイン、ラウリルジメチルアミノ酢酸ベタインなど)、アミドベタイン(ヤシ油脂肪酸アミドプロピルベタインなど)、アルキルジヒドロキシアルキルベタイン(ラウリルジヒドロキシエチルベタインなど)などが挙げられる。
さらに、イミダゾリン型両性界面活性剤としては、たとえば、2-ウンデシル-N-カルボキシメチル-N-ヒドロキシエチルイミダゾリニウムベタインなどが挙げられる。
さらに、イミダゾリン型両性界面活性剤としては、たとえば、2-ウンデシル-N-カルボキシメチル-N-ヒドロキシエチルイミダゾリニウムベタインなどが挙げられる。
その他の両性界面活性剤としては、たとえば、ナトリウムラウロイルグリシン、ナトリウムラウリルジアミノエチルグリシン、ラウリルジアミノエチルグリシン塩酸塩、ジオクチルジアミノエチルグリシン塩酸塩などのグリシン型両性界面活性剤、ペンタデシルスルフォタウリンなどのスルフォベタイン型両性界面活性剤などが挙げられる。
非イオン界面活性剤としては、アルキレンオキシド付加型非イオン界面活性剤および多価アルコール型非イオン界面活性剤などが挙げられる。
アルキレンオキシド付加型非イオン界面活性剤は、高級アルコール、高級脂肪酸またはアルキルアミン等に直接アルキレンオキシドを付加させるか、グリコール類にアルキレンオキシドを付加させて得られるポリアルキレングリコール類に高級脂肪酸などを反応させるか、あるいは多価アルコールに高級脂肪酸を反応して得られたエステル化物にアルキレンオキシドを付加させるか、高級脂肪酸アミドにアルキレンオキシドを付加させることにより得られる。
アルキレンオキシドとしては、たとえばエチレンオキサイド、プロピレンオキサイドおよびブチレンオキサイドが挙げられる。
アルキレンオキシド付加型非イオン界面活性剤の具体例としては、オキシアルキレンアルキルエーテル(たとえば、オクチルアルコールエチレンオキサイド付加物、ラウリルアルコールエチレンオキサイド付加物、ステアリルアルコールエチレンオキサイド付加物、オレイルアルコールエチレンオキサイド付加物、ラウリルアルコ-ルエチレンオキサイドプロピレンオキサイドブロック付加物など)、ポリオキシアルキレン高級脂肪酸エステル(たとえば、ステアリル酸エチレンオキサイド付加物、ラウリル酸エチレンオキサイド付加物など)、ポリオキシアルキレン多価アルコール高級脂肪酸エステル(たとえば、ポリエチレングリコールのラウリン酸ジエステル、ポリエチレングリコールのオレイン酸ジエステル、ポリエチレングリコールのステアリン酸ジエステルなど)、ポリオキシアルキレンアルキルフェニルエーテル(たとえば、ノニルフェノールエチレンオキサイド付加物、ノニルフェノールエチレンオキサイドプロピレンオキサイドブロック付加物、オクチルフェノールエチレンオキサイド付加物、ビスフェノールAエチレンオキサイド付加物、ジノニルフェノールエチレンオキサイド付加物、スチレン化フェノールエチレンオキサイド付加物など)、ポリオキシアルキレンアルキルアミノエーテル(たとえば、ラウリルアミンエチレンオキサイド付加物,ステアリルアミンエチレンオキサイド付加物など)、ポリオキシアルキレンアルキルアルカノールアミド(たとえば、ヒドロキシエチルラウリン酸アミドのエチレンオキサイド付加物、ヒドロキシプロピルオレイン酸アミドのエチレンオキサイド付加物、ジヒドロキシエチルラウリン酸アミドのエチレンオキサイド付加物など)が挙げられる。
多価アルコール型非イオン界面活性剤としては、多価アルコール脂肪酸エステル、多価アルコール脂肪酸エステルアルキレンオキサイド付加物、多価アルコールアルキルエーテル、多価アルコールアルキルエーテルアルキレンオキサイド付加物が挙げられる。
多価アルコール脂肪酸エステルの具体例としては、ペンタエリスリトールモノラウレート、ペンタエリスリトールモノオレート、ソルビタンモノラウレート、ソルビタンモノステアレート、ソルビタンモノラウレート、ソルビタンジラウレート、ソルビタンジオレート、ショ糖モノステアレートなどが挙げられる。
多価アルコール脂肪酸エステルアルキレンオキサイド付加物の具体例としては、エチレングリコールモノオレートエチレンオキサイド付加物、エチレングリコールモノステアレートエチレンオキサイド付加物、トリメチロールプロパンモノステアレートエチレンオキサイドプロピレンオキサイドランダム付加物、ソルビタンモノラウレートエチレンオキサイド付加物、ソルビタンモノステアレートエチレンオキサイド付加物、ソルビタンジステアレートエチレンオキサイド付加物、ソルビタンジラウレートエチレンオキサイドプロピレンオキサイドランダム付加物などが挙げられる。
多価アルコールアルキルエーテルの具体例としては、ペンタエリスリトールモノブチルエーテル、ペンタエリスリトールモノラウリルエーテル、ソルビタンモノメチルエーテル、ソルビタンモノステアリルエーテル、メチルグリコシド、ラウリルグリコシドなどが挙げられる。
多価アルコールアルキルエーテルアルキレンオキサイド付加物の具体例としては、ソルビタンモノステアリルエーテルエチレンオキサイド付加物、メチルグリコシドエチレンオキサイドプロピレンオキサイドランダム付加物、ラウリルグリコシドエチレンオキサイド付加物、ステアリルグリコシドエチレンオキサイドプロピレンオキサイドランダム付加物などが挙げられる。
これらの中でも、本発明で用いられる乳化剤は、分散剤や非イオン界面活性剤から選ばれることが好ましく、さらに好ましい乳化剤の具体例を挙げると、本発明の中空マイクロバルーンがウレタン(ウレア)樹脂からなる場合、ポリビニルアルコール、またはアニオン変性ポリビニルアルコールが好ましく、該中空マイクロバルーンがアミド樹脂からなる場合、アクリル酸ナトリウム-アクリル酸エステル共重合体が好ましい。これらを選択することで、安定なエマルションとすることができる。
また、該中空マイクロバルーンがメラミン樹脂、尿素樹脂からなる場合、乳化剤としては、スチレン-無水マレイン酸共重合体、エチレン-無水マレイン酸共重合、イソブチレン-無水マレイン酸共重合体であることが好ましい。これらを水酸化ナトリム等のアルカリ性化合物で中和することで、高密度のアニオン性ポリマーとなり、(B5)成分や(B6)成分の重合反応が進行させることができる。
<有機溶媒>
本発明において、(a)成分または(c)成分に用いられる有機溶媒は、(B1)成分、(B7)成分、または親油性の(A)成分が溶解するものであれば特に制限されず、たとえば、炭化水素系、ハロゲン化系、ケトン系溶剤等が挙げられる。
本発明において、(a)成分または(c)成分に用いられる有機溶媒は、(B1)成分、(B7)成分、または親油性の(A)成分が溶解するものであれば特に制限されず、たとえば、炭化水素系、ハロゲン化系、ケトン系溶剤等が挙げられる。
中でも、マイクロバルーンの内部から該有機溶媒を除去し、中空マイクロバルーンとするためには、沸点が200℃以下のものが好ましく、より好ましくは沸点が150℃以下のものである。これらを例示すると、以下のものが挙げられる。
(炭化水素系)
n-ヘキサン、n-ヘプタン、n-オクタン等の炭素数が6~11の脂肪族炭化水素、ベンゼン、トルエン、キシレン等の芳香族炭化水素、シクロヘキサン、シクロペンタン、メチルシクロヘキサン等の脂環式炭化水素が挙げられる。
n-ヘキサン、n-ヘプタン、n-オクタン等の炭素数が6~11の脂肪族炭化水素、ベンゼン、トルエン、キシレン等の芳香族炭化水素、シクロヘキサン、シクロペンタン、メチルシクロヘキサン等の脂環式炭化水素が挙げられる。
(ハロゲン化系)
クロロホルム、ジクロロメタン、テトラクロロエタン、モノまたはジクロルベンゼン等が挙げられる。
クロロホルム、ジクロロメタン、テトラクロロエタン、モノまたはジクロルベンゼン等が挙げられる。
(ケトン系)
メチルイソブチルケトン等が挙げられる。
メチルイソブチルケトン等が挙げられる。
これらの有機溶媒は単独で用いてもよく、また、二種以上の混合溶媒としてもよい。
本発明で用いられる有機溶媒は、中でも、n-ヘキサン、n-ヘプタン、n-オクタン、ベンゼン、トルエン、キシレン等がさらに好ましい。
<添加剤>
本発明において、エマルションをより安定化させる目的で、本発明の効果を損なわない範囲で、水相に添加剤を加えてもよい。このような添加剤としては、炭酸ナトリウム、炭酸カルシウム、炭酸カリウム、リン酸ナトリウム、リン酸カリウム、リン酸カルシウム、塩化ナトリウム、塩化カリウム等の水溶性の塩が挙げられる。これらの添加剤は、単独で、あるいは、2種以上を組み合わせて用いることもできる。
本発明において、エマルションをより安定化させる目的で、本発明の効果を損なわない範囲で、水相に添加剤を加えてもよい。このような添加剤としては、炭酸ナトリウム、炭酸カルシウム、炭酸カリウム、リン酸ナトリウム、リン酸カリウム、リン酸カルシウム、塩化ナトリウム、塩化カリウム等の水溶性の塩が挙げられる。これらの添加剤は、単独で、あるいは、2種以上を組み合わせて用いることもできる。
<触媒>
(ウレタン化触媒)
本発明において、(B12)成分であるウレタンプレポリマーを合成する場合や、中空マイクロバルーンがウレタン(ウレア)樹脂からなる場合に用いられるウレタン化触媒は、任意の適切なものが何ら制限なく使用できる。具体的に例示すると、トリエチレンジアミン、ヘキサメチレンテトラミン、N,N-ジメチルオクチルアミン、N,N,N′,N′-テトラメチル-1,6-ジアミノヘキサン、4,4′-トリメチレンビス(1-メチルピペリジン)、1,8-ジアザビシクロ-(5,4,0)-7-ウンデセン、ジメチルスズジクロライド、ジメチルスズビス(イソオクチルチオグリコレート)、ジブチルスズジクロライド、ジブチルチンジラウレート、ジブチルスズマレエート、ジブチルスズマレエートポリマー、ジブチルスズジリシノレート、ジブチルスズビス(ドデシルメルカプチド)、ジブチルスズビス(イソオクチルチオグリコレート)、ジオクチルスズジクロライド、ジオクチルスズマレエート、ジオクチルスズマレエートポリマー、ジオクチルスズビス(ブチルマレエート)、ジオクチルスズジラウレート、ジオクチルスズジリシノレート、ジオクチルスズジオレエート、ジオクチルスズジ(6-ヒドロキシ)カプロエート、ジオクチルスズビス(イソオクチルチオグリコレート)、ジドデシルスズジリシノレート、各種金属塩、たとえば、オレイン酸銅、アセチルアセトン酸銅、アセチルアセトン酸鉄、ナフテン酸鉄、乳酸鉄、クエン酸鉄、グルコン酸鉄、オクタン酸カリウム、チタン酸2-エチルヘキシル等が挙げられる。
(ウレタン化触媒)
本発明において、(B12)成分であるウレタンプレポリマーを合成する場合や、中空マイクロバルーンがウレタン(ウレア)樹脂からなる場合に用いられるウレタン化触媒は、任意の適切なものが何ら制限なく使用できる。具体的に例示すると、トリエチレンジアミン、ヘキサメチレンテトラミン、N,N-ジメチルオクチルアミン、N,N,N′,N′-テトラメチル-1,6-ジアミノヘキサン、4,4′-トリメチレンビス(1-メチルピペリジン)、1,8-ジアザビシクロ-(5,4,0)-7-ウンデセン、ジメチルスズジクロライド、ジメチルスズビス(イソオクチルチオグリコレート)、ジブチルスズジクロライド、ジブチルチンジラウレート、ジブチルスズマレエート、ジブチルスズマレエートポリマー、ジブチルスズジリシノレート、ジブチルスズビス(ドデシルメルカプチド)、ジブチルスズビス(イソオクチルチオグリコレート)、ジオクチルスズジクロライド、ジオクチルスズマレエート、ジオクチルスズマレエートポリマー、ジオクチルスズビス(ブチルマレエート)、ジオクチルスズジラウレート、ジオクチルスズジリシノレート、ジオクチルスズジオレエート、ジオクチルスズジ(6-ヒドロキシ)カプロエート、ジオクチルスズビス(イソオクチルチオグリコレート)、ジドデシルスズジリシノレート、各種金属塩、たとえば、オレイン酸銅、アセチルアセトン酸銅、アセチルアセトン酸鉄、ナフテン酸鉄、乳酸鉄、クエン酸鉄、グルコン酸鉄、オクタン酸カリウム、チタン酸2-エチルヘキシル等が挙げられる。
(アミド化触媒)
中空マイクロバルーンがアミド樹脂からなる場合に用いられるアミド化触媒は、任意の適切なものが何ら制限なく使用できる。具体的に例示すると、ホウ素やリン酸二水素ナトリウム等が挙げられる。
中空マイクロバルーンがアミド樹脂からなる場合に用いられるアミド化触媒は、任意の適切なものが何ら制限なく使用できる。具体的に例示すると、ホウ素やリン酸二水素ナトリウム等が挙げられる。
<中空マイクロバルーンの粒子径>
本発明の中空マイクロバルーンの平均粒子径は、特に制限されるものではないが、1μm~500μmであることが好ましく、5μm~200μmであることがより好ましく、10~100μmであることが最も好ましい。この範囲にあることで、CMP研磨パッドに配合した場合、優れた研磨特性を発現することができる。
中空マイクロバルーンの平均粒子径の測定は、公知の方法を採用すればよく、具体的には、画像解析法を用いることができる。画像解析法を用いることで容易に粒子サイズを測定できる。なお、平均粒径は一次粒子の平均粒径である。画像解析法による平均粒子径の測定は、例えば走査型電子顕微鏡(SEM)などを用いて行うことができる。
本発明の中空マイクロバルーンの平均粒子径は、特に制限されるものではないが、1μm~500μmであることが好ましく、5μm~200μmであることがより好ましく、10~100μmであることが最も好ましい。この範囲にあることで、CMP研磨パッドに配合した場合、優れた研磨特性を発現することができる。
中空マイクロバルーンの平均粒子径の測定は、公知の方法を採用すればよく、具体的には、画像解析法を用いることができる。画像解析法を用いることで容易に粒子サイズを測定できる。なお、平均粒径は一次粒子の平均粒径である。画像解析法による平均粒子径の測定は、例えば走査型電子顕微鏡(SEM)などを用いて行うことができる。
<中空マイクロバルーンの嵩密度>
本発明の中空マイクロバルーンの嵩密度は、特に制限されるものではないが、0.01~0.5g/cm3であることが好ましく、0.02~0.3g/cm3であることがより好ましい。この範囲にあることでCMP研磨パッドの研磨面に最適な細孔を形成することが可能となる。
本発明の中空マイクロバルーンの嵩密度は、特に制限されるものではないが、0.01~0.5g/cm3であることが好ましく、0.02~0.3g/cm3であることがより好ましい。この範囲にあることでCMP研磨パッドの研磨面に最適な細孔を形成することが可能となる。
<中空マイクロバルーンの灰分>
本発明の中空マイクロバルーンの灰分は、特に制限されるものではないが、後述する実施例に記載した方法において、該中空マイクロバルーンを100質量部あたり、0.5質量部以下であることが好ましく、0.3質量部以下であることがさらに好ましく、0.1質量部以下であることがより好ましく、測定されないことが最も好ましい。この範囲にあることで、CMP研磨パッドに用いた際に、ウエハのディフェクトを低減することが可能となる。
本発明の中空マイクロバルーンの灰分は、特に制限されるものではないが、後述する実施例に記載した方法において、該中空マイクロバルーンを100質量部あたり、0.5質量部以下であることが好ましく、0.3質量部以下であることがさらに好ましく、0.1質量部以下であることがより好ましく、測定されないことが最も好ましい。この範囲にあることで、CMP研磨パッドに用いた際に、ウエハのディフェクトを低減することが可能となる。
<CMP用研磨パッドへの応用>
本発明のCMP用研磨パットは、上記した中空マイクロバルーンを含んでなるものである。該中空マイクロバルーンを含むことにより、優れた耐久性、および、優れた研磨特性を発現したCMP用研磨パッドすることができる。
本発明のCMP用研磨パットは、上記した中空マイクロバルーンを含んでなるものである。該中空マイクロバルーンを含むことにより、優れた耐久性、および、優れた研磨特性を発現したCMP用研磨パッドすることができる。
このようなCMP用研磨パッドを作製する方法としては、公知の方法が制限なく採用することができ、本発明の中空マイクロバルーンを含有した樹脂、たとえばウレタン樹脂を、切断、表面研磨をすることで、該ウレタン樹脂の研磨表面に細孔を有するCMP用研磨パッドとすることができる。
ウレタン樹脂からなるCMP用研磨パッドの場合、用いるウレタン樹脂は、特に制限なく公知の方法により作製すればよく、たとえば、イソシアネート基を有する化合物、イソシアネート基と重合可能な活性水素を持つ活性水素基を有する化合物、および本発明の中空マイクロバルーンを均一混合・分散させた後に、硬化させる方法が挙げられる。
硬化方法も特に制限なく公知の方法を採用すればよく、具体的には、ワンポット法、プレポリマー法等の乾式法、および、溶剤を用いた湿式法等を用いることができる。その中でも、乾式法が好適に採用される。
前記したウレタン樹脂からなるCMP用研磨パッドの場合、本発明の中空マイクロバルーンのウレタン樹脂への配合量は、イソシアネート基を有する化合物、および、イソシアネート基と重合可能な活性水素を持つ活性水素基を有する化合物の合計100質量部あたり、本発明の中空マイクロバルーンを0.1~20質量部とすることが好ましく、0.2~10質量部とすることがより好ましく、0.5~8質量部とすることがさらに好ましい。この範囲にすることにより、優れた研磨特性を発現することが可能である。
また、本発明においては、前記イソシアネート基と重合可能な活性水素を持つ活性水素基を有する化合物として、本発明の(A)ポリロタキサンモノマーを含んでいることが、さらに研磨特性を向上させる点で好適である。
本発明において、CMP用研磨パッドの様態は、特に制限されるものではなく、たとえば、その表面に溝構造を形成してもよい。該CMP用研磨パッドの溝構造としては、スラリーを保持・更新する形状とすることが好ましく、具体的には、X(ストライプ)溝、XY格子溝、同心円状溝、貫通孔、貫通していない穴、多角柱、円柱、螺旋状溝、偏心円状溝、放射状溝、およびこれらの溝を組み合わせたものが挙げられる。
また、上記CMP用研磨パッドの溝構造の作製方法は、特に限定されるものではない。たとえば、所定の溝構造を有した金型に前記した化合物等を流しこみ、硬化させることにより作製する方法、あるいは、得られた樹脂を用いて溝構造を作成する方法、たとえば、所定サイズのバイトのような治具を用い機械切削する方法、所定の表面形状を有したプレス板で樹脂をプレスして作製する方法、フォトリソグラフィを用いて作製する方法、印刷手法を用いて作製する方法、炭酸ガスレーザー等レーザー光による作製方法などが挙げられる。
次に、実施例および比較例を用いて本発明を詳細に説明するが、本発明は本実施例に限定されるものではない。以下の実施例および比較例において、上記の各成分および評価方法等は、以下のとおりである。
(分子量測定;ゲルパーミエーションクロマトグラフィー(GPC測定))
GPC測定は、装置として液体クロマトグラフ装置(日本ウォーターズ社製)を用いた。カラムは分析するサンプルの分子量に応じて、昭和電工株式会社製Shodex GPC KF-802(排除限界分子量:5,000)、KF802.5(排除限界分子量:20,000)、KF-803(排除限界分子量:70,000)、KF-804(排除限界分子量:400,000)、KF-805(排除限界分子量:2,000,000)を適宜使用した。また、展開液としてジメチルホルムアミドを用い、流速1ml/min、温度40℃の条件にて測定した。標準試料にポリスチレンを用い、比較換算により重量平均分子量を求めた。なお、検出器には示差屈折率計を用いた。
(灰分)
中空マイクロバルーンを600℃の温度で燃焼した燃焼残さの質量と、燃焼前の中空マイクロバルーンの質量との割合である。
(分子量測定;ゲルパーミエーションクロマトグラフィー(GPC測定))
GPC測定は、装置として液体クロマトグラフ装置(日本ウォーターズ社製)を用いた。カラムは分析するサンプルの分子量に応じて、昭和電工株式会社製Shodex GPC KF-802(排除限界分子量:5,000)、KF802.5(排除限界分子量:20,000)、KF-803(排除限界分子量:70,000)、KF-804(排除限界分子量:400,000)、KF-805(排除限界分子量:2,000,000)を適宜使用した。また、展開液としてジメチルホルムアミドを用い、流速1ml/min、温度40℃の条件にて測定した。標準試料にポリスチレンを用い、比較換算により重量平均分子量を求めた。なお、検出器には示差屈折率計を用いた。
(灰分)
中空マイクロバルーンを600℃の温度で燃焼した燃焼残さの質量と、燃焼前の中空マイクロバルーンの質量との割合である。
<各成分>
(A)ポリロタキサンモノマー
RX-1:側鎖に水酸基を有し、側鎖の数平均分子量が約350、重量平均分子量が165,000のポリロタキサンモノマー
RX-2:側鎖にアミノ基を有する、側鎖の数平均分子量が約400、重量平均分子量78,000のポリロタキサンモノマー
(A)ポリロタキサンモノマー
RX-1:側鎖に水酸基を有し、側鎖の数平均分子量が約350、重量平均分子量が165,000のポリロタキサンモノマー
RX-2:側鎖にアミノ基を有する、側鎖の数平均分子量が約400、重量平均分子量78,000のポリロタキサンモノマー
((A)ポリロタキサンモノマーの製造方法)
(1-1)PEG-COOHの調製;
軸分子用ポリマーとして、分子量10,000の直鎖状ポリエチレングリコール(PEG)を用意い、PEG:10g、TEMPO(2,2,6,6-テトラメチル-1-ピペリジニルオキシラジカル):100mg、臭化ナトリウム:1gを水100mLに溶解させた。この溶液に、次亜塩素酸ナトリウム水溶液(有効塩素濃度5%):5mLを添加し、室温で10分間撹拌した。その後、エタノール:5mL添加して反応を終了させた。そして、塩化メチレン:50mLを用いて抽出を行った後、塩化メチレンを留去し、エタノール:250mLに溶解させてから、-4℃の温度で12時間かけて再沈させ、PEG-COOHを回収し、乾燥した。
(1-1)PEG-COOHの調製;
軸分子用ポリマーとして、分子量10,000の直鎖状ポリエチレングリコール(PEG)を用意い、PEG:10g、TEMPO(2,2,6,6-テトラメチル-1-ピペリジニルオキシラジカル):100mg、臭化ナトリウム:1gを水100mLに溶解させた。この溶液に、次亜塩素酸ナトリウム水溶液(有効塩素濃度5%):5mLを添加し、室温で10分間撹拌した。その後、エタノール:5mL添加して反応を終了させた。そして、塩化メチレン:50mLを用いて抽出を行った後、塩化メチレンを留去し、エタノール:250mLに溶解させてから、-4℃の温度で12時間かけて再沈させ、PEG-COOHを回収し、乾燥した。
(1-2)ポリロタキサンの調製;
上記で調製されたPEG-COOH:3gおよびα-シクロデキストリン(α-CD):12gを、それぞれ、70℃の水50mLに溶解させ、得られた各溶液を混合し、よく振り混ぜた。次いで、この混合溶液を、4℃の温度で12時間再沈させ、析出した包接錯体を凍結乾燥して回収した。その後、室温でジメチルホルムアミド(DMF):50mlに、アダマンタンアミン0.13gを溶解した後、上記の包接錯体を添加して速やかによく振り混ぜた。続いてベンゾトリアゾール-1-イル-オキシ-トリス(ジメチルアミノ)ホスホニウムヘキサフルオロホスフェート試薬:0.38gをDMF:5mLに溶解した溶液をさらに添加して、よく振り混ぜた。さらにジイソプロピルエチルアミン:0.14mlをDMF:5mLに溶解させた溶液を添加してよく振り混ぜてスラリー状の試薬を得た。
上記で調製されたPEG-COOH:3gおよびα-シクロデキストリン(α-CD):12gを、それぞれ、70℃の水50mLに溶解させ、得られた各溶液を混合し、よく振り混ぜた。次いで、この混合溶液を、4℃の温度で12時間再沈させ、析出した包接錯体を凍結乾燥して回収した。その後、室温でジメチルホルムアミド(DMF):50mlに、アダマンタンアミン0.13gを溶解した後、上記の包接錯体を添加して速やかによく振り混ぜた。続いてベンゾトリアゾール-1-イル-オキシ-トリス(ジメチルアミノ)ホスホニウムヘキサフルオロホスフェート試薬:0.38gをDMF:5mLに溶解した溶液をさらに添加して、よく振り混ぜた。さらにジイソプロピルエチルアミン:0.14mlをDMF:5mLに溶解させた溶液を添加してよく振り混ぜてスラリー状の試薬を得た。
上記で得られたスラリー状の試薬を4℃で12時間静置した。その後、DMF/メタノール混合溶媒(体積比1/1):50mlを添加、混合、遠心分離を行なって上澄みを捨てた。さらに、上記DMF/メタノール混合溶液による洗浄を行った後、メタノールを用いて洗浄、遠心分離を行い、沈殿物を得た。得られた沈殿物を真空乾燥で乾燥させた後、ジメチルスルオキシド(DMSO):50mLに溶解させ、得られた透明な溶液を700mLの水中に滴下してポリロタキサンを析出させた。析出したポリロタキサンを遠心分離で回収し、真空乾燥させた。さらにDMSOに溶解、水中で析出、回収、乾燥を行い、精製ポリロタキサンを得た。このときのα-CDの包接数は0.25であった。
ここで、包接数は、DMSO-d6にポリロタキサンを溶解し、1H-NMR測定装置(日本電子製JNM-LA500)により測定し、以下の方法により算出した。
ここで、X,YおよびX/(Y-X)は、以下の意味を示す。
ここで、X,YおよびX/(Y-X)は、以下の意味を示す。
X:4~6ppmのシクロデキストリンの水酸基由来プロトンの積分値
Y:3~4ppmのシクロデキストリンおよびPEGのメチレン鎖由来プロトンの積分値
X/(Y-X):PEGに対するシクロデキストリンのプロトン比
まず、理論的に最大包接数1の時のX/(Y-X)を予め算出し、この値と実際の化合物の分析値から算出されたX/(Y-X)を比較することにより包接数を算出した。
Y:3~4ppmのシクロデキストリンおよびPEGのメチレン鎖由来プロトンの積分値
X/(Y-X):PEGに対するシクロデキストリンのプロトン比
まず、理論的に最大包接数1の時のX/(Y-X)を予め算出し、この値と実際の化合物の分析値から算出されたX/(Y-X)を比較することにより包接数を算出した。
(1-3)ポリロタキサンへの側鎖の導入;
上記で精製されたポリロタキサン:500mgを1mol/LのNaOH水溶液:50mLに溶解し、プロピレンオキシド:3.83g(66mmol)を添加し、アルゴン雰囲気下、室温で12時間撹拌した。次いで、1mol/LのHCl水溶液を用い、上記のポリロタキサン溶液を、pHが7~8となるように中和し、透析チューブにて透析した後、凍結乾燥し、ヒドロキシプロピル化ポリロタキサンを得た。得られたヒドロキシプロピル化ポリロタキサンは、1H-NMRおよびGPCで同定し、所望の構造を有するヒドロキシプロピル化ポリロタキサンであることを確認した。
上記で精製されたポリロタキサン:500mgを1mol/LのNaOH水溶液:50mLに溶解し、プロピレンオキシド:3.83g(66mmol)を添加し、アルゴン雰囲気下、室温で12時間撹拌した。次いで、1mol/LのHCl水溶液を用い、上記のポリロタキサン溶液を、pHが7~8となるように中和し、透析チューブにて透析した後、凍結乾燥し、ヒドロキシプロピル化ポリロタキサンを得た。得られたヒドロキシプロピル化ポリロタキサンは、1H-NMRおよびGPCで同定し、所望の構造を有するヒドロキシプロピル化ポリロタキサンであることを確認した。
なお、ヒドロキシプロピル基による環状分子の水酸基への修飾度は0.5であり、GPC測定により重量平均分子量Mw:50,000であった。
得られたヒドロキシプロピル化ポリロタキサン:5gを、ε-カプロラクトン:15gに80℃で溶解させた混合液を調製した。この混合液を、乾燥窒素をブローさせながら110℃で1時間攪拌した後、2-エチルヘキサン酸錫(II)の50wt%キシレン溶液:0.16gを加え、130℃で6時間攪拌した。その後、キシレンを添加し、不揮発濃度が約35質量%の側鎖を導入したε-カプロラクトン修飾ポリロタキサンキシレン溶液を得た。
(1-4)末端水酸基導入側鎖修飾ポリロタキサン(RX-1)の調製;
上記で調製されたε-カプロラクトン修飾ポリロタキサンキシレン溶液をヘキサン中に滴下し、回収し、乾燥させることによりε-カプロラクトン修飾ポリロタキサン(RX-1)を取得した。
この(A)ポリロタキサンモノマー;RX-1の物性は以下の通りであった。
上記で調製されたε-カプロラクトン修飾ポリロタキサンキシレン溶液をヘキサン中に滴下し、回収し、乾燥させることによりε-カプロラクトン修飾ポリロタキサン(RX-1)を取得した。
この(A)ポリロタキサンモノマー;RX-1の物性は以下の通りであった。
ポリロタキサン重量平均分子量Mw(GPC):165,000
側鎖の修飾度:0.5(%で表示すると50%となる)
側鎖の分子量:数平均分子量約350
側鎖の末端に重合性基として水酸基を有する(A)ポリロタキサンモノマーである。
側鎖の修飾度:0.5(%で表示すると50%となる)
側鎖の分子量:数平均分子量約350
側鎖の末端に重合性基として水酸基を有する(A)ポリロタキサンモノマーである。
(1-5)アミノ基導入ポリロタキサンの調製;
前記(1-2)で得られたポリロタキサン:5gを、ピリジン:100mL中に分散させ、氷浴中で冷却を行った。その後、パラトルエンスルホニルクロリド:14.3gを加え、5℃で6時間反応を行った。その後、脱イオン水:1000mL中に反応液を流し込むことによって固形分を析出させ、ガラスフィルターを用いて固形分の回収を行った。
前記(1-2)で得られたポリロタキサン:5gを、ピリジン:100mL中に分散させ、氷浴中で冷却を行った。その後、パラトルエンスルホニルクロリド:14.3gを加え、5℃で6時間反応を行った。その後、脱イオン水:1000mL中に反応液を流し込むことによって固形分を析出させ、ガラスフィルターを用いて固形分の回収を行った。
得られた固形分を多量の脱イオン水、およびジエチルエーテルによって洗浄後、真空乾燥させることによってトシル化ポリロタキサンを得た。トシル化ポリロタキサンは1H-NMRおよびGPCで同定し、確認した。なお、トシル基による環状分子の水酸基への修飾度は0.06であった。
合成したトシル化ポリロタキサン:5gをジメチルホルムアミド:150mLに溶解させた。この溶液を予め70℃に加熱しておいたエチレンジアミン:200mLとジメチルホルムアミド:100mLの混合溶液に滴下添加を行い、滴下終了後70℃で5時間反応を行った。その後、反応液をジエチルエーテル:3Lに流し込むことによって固形分を析出させ、遠心分離によって析出固形分の回収を行った。その後、固形分をDMFに溶解させて、ジエチルエーテルに再沈殿精製を行った後、得られた固形分を乾燥させることによりアミノ基導入ポリロタキサンを得た。
(1-6)末端アミノ基側鎖導入修飾ポリロタキサン(RX-2)の調製;
ε-カプロラクタム:3.6gを窒素フロー下、150℃で加熱溶解させ、前記したアミノ基導入ポリロタキサン:5.0gと、オクチル酸スズ:0.3gをトルエン:2.0gに溶解させた溶液とを添加した。その後、190℃まで昇温させた後、190℃で1時間反応を行った。得られた反応物をメタノール:200mL中に滴下し、回収し、乾燥させることにより末端アミノ基側鎖導入修飾ポリロタキサン(RX-2)を取得した。
ε-カプロラクタム:3.6gを窒素フロー下、150℃で加熱溶解させ、前記したアミノ基導入ポリロタキサン:5.0gと、オクチル酸スズ:0.3gをトルエン:2.0gに溶解させた溶液とを添加した。その後、190℃まで昇温させた後、190℃で1時間反応を行った。得られた反応物をメタノール:200mL中に滴下し、回収し、乾燥させることにより末端アミノ基側鎖導入修飾ポリロタキサン(RX-2)を取得した。
この(A)ポリロタキサンモノマー;RX-2の物性は以下の通りであった。
ポリロタキサン重量平均分子量Mw(GPC):78,000。
ポリロタキサン重量平均分子量Mw(GPC):78,000。
側鎖の修飾度:0.06(%で表示すると50%となる)
側鎖の分子量:数平均分子量約400
側鎖の末端に重合性基としてアミノ基を有する(A)ポリロタキサンモノマーである。
側鎖の分子量:数平均分子量約400
側鎖の末端に重合性基としてアミノ基を有する(A)ポリロタキサンモノマーである。
(B)前記(A)分子内に少なくとも2つの重合性官能基を有するポリロタキサンモノマー以外の重合性モノマー
(B1)成分;少なくとも2個のイソシアネート基を有する多官能イソシアネート化合物
(B12)成分;ウレタンプレポリマー
Pre-1:イソ(チオ)シアネート当量が905の末端イソシアネートウレタンプレポリマー
(Pre-1の製造方法)
窒素導入管、温度計、攪拌機を備えたフラスコに窒素雰囲気下中、2,4-トリレンジイソシアネート:50g、ポリオキシテトラメチレングリコール(数平均分子量;1,000):90gとジエチレングリコール:12gを、80℃で6時間反応させ、イソシアネート当量が905の末端イソシアネートウレタンプレポリマー(Pre-1)を得た。
(B3)成分;多官能アミン化合物
EDA;エチレンジアミン
(B5)成分;メラミンホルムアルデヒドプレポリマー化合物
ニカレジンS-260(日本カーバイト工業株式会社製)
(有機溶媒)
Tol;トルエン
(乳化剤)
PVA:完全けん化型で平均重合度約500のポリビニルアルコール
ET/AMA:ポリエチレン-無水マレイン酸(平均分子量が100,000~500,000)
(B1)成分;少なくとも2個のイソシアネート基を有する多官能イソシアネート化合物
(B12)成分;ウレタンプレポリマー
Pre-1:イソ(チオ)シアネート当量が905の末端イソシアネートウレタンプレポリマー
(Pre-1の製造方法)
窒素導入管、温度計、攪拌機を備えたフラスコに窒素雰囲気下中、2,4-トリレンジイソシアネート:50g、ポリオキシテトラメチレングリコール(数平均分子量;1,000):90gとジエチレングリコール:12gを、80℃で6時間反応させ、イソシアネート当量が905の末端イソシアネートウレタンプレポリマー(Pre-1)を得た。
(B3)成分;多官能アミン化合物
EDA;エチレンジアミン
(B5)成分;メラミンホルムアルデヒドプレポリマー化合物
ニカレジンS-260(日本カーバイト工業株式会社製)
(有機溶媒)
Tol;トルエン
(乳化剤)
PVA:完全けん化型で平均重合度約500のポリビニルアルコール
ET/AMA:ポリエチレン-無水マレイン酸(平均分子量が100,000~500,000)
<実施例1>
トルエン:15質量部に、(A)成分のRX-1:0.11質量部と(B1)成分のPre-1:1質量部を溶解して(a)成分を調製した。次に、水:150質量部にPVA:10質量部を溶解して(b)成分を調製した。次に、調製した(a)成分と(b)成分を混合し、高速せん断式分散機を用いて2,000rpm×10分、25℃の条件で攪拌し、O/Wエマルションを調製した。調製したO/Wエマルションに、25℃で、水:30質量部にエチレンジアミン:0.04質量部を溶解した水溶液を滴下した。滴下後、25℃で60分ゆっくりと攪拌した後、60℃で4時間攪拌し、ウレタン(ウレア)樹脂からなるマイクロバルーン分散液を得た。得られたマイクロバルーン分散液を濾過によりマイクロバルーンを取り出し、温度60℃で真空乾燥24時間し、その後、分級機により篩い分け、中空ウレタンマイクロバルーン1を得た。なお、マイクロバルーン分散液を濾過した際、濾液にはエチレンジアミンは検出されなかった。
トルエン:15質量部に、(A)成分のRX-1:0.11質量部と(B1)成分のPre-1:1質量部を溶解して(a)成分を調製した。次に、水:150質量部にPVA:10質量部を溶解して(b)成分を調製した。次に、調製した(a)成分と(b)成分を混合し、高速せん断式分散機を用いて2,000rpm×10分、25℃の条件で攪拌し、O/Wエマルションを調製した。調製したO/Wエマルションに、25℃で、水:30質量部にエチレンジアミン:0.04質量部を溶解した水溶液を滴下した。滴下後、25℃で60分ゆっくりと攪拌した後、60℃で4時間攪拌し、ウレタン(ウレア)樹脂からなるマイクロバルーン分散液を得た。得られたマイクロバルーン分散液を濾過によりマイクロバルーンを取り出し、温度60℃で真空乾燥24時間し、その後、分級機により篩い分け、中空ウレタンマイクロバルーン1を得た。なお、マイクロバルーン分散液を濾過した際、濾液にはエチレンジアミンは検出されなかった。
取得した中空マイクロバルーン1中の(A)成分と(B)成分の合計100質量部に対する(A)成分は9.6質量部であった。
また、中空マイクロバルーン1の平均粒子径は約25μmであり、嵩密度は0.1g/cm3であり、灰分は測定されなかった。
また、中空マイクロバルーン1の平均粒子径は約25μmであり、嵩密度は0.1g/cm3であり、灰分は測定されなかった。
<実施例2>
実施例1において、(A)成分のRX-1を1.05質量部、エチレンジアミンを0.01質量部に変更した以外は、同様の手法で中空マイクロバルーン2を作製した。
実施例1において、(A)成分のRX-1を1.05質量部、エチレンジアミンを0.01質量部に変更した以外は、同様の手法で中空マイクロバルーン2を作製した。
取得した中空マイクロバルーン2中の(A)成分と(B)成分の合計100質量部に対する(A)成分の割合は、51質量部であった。
また、中空マイクロバルーン2の平均粒子径は約30μmであり、嵩密度は0.3g/cm3であり、灰分は測定されなかった。
また、中空マイクロバルーン2の平均粒子径は約30μmであり、嵩密度は0.3g/cm3であり、灰分は測定されなかった。
<実施例3>
実施例1において、(A)成分のRX-1を0.01質量部、エチレンジアミンを0.05質量部に変更した以外は、同様の手法で中空マイクロバルーン3を作成した。
実施例1において、(A)成分のRX-1を0.01質量部、エチレンジアミンを0.05質量部に変更した以外は、同様の手法で中空マイクロバルーン3を作成した。
取得した中空マイクロバルーン3中の(A)成分と(B)成分の合計100質量部に対する(A)成分の割合は0.9質量部であった。
また、中空マイクロバルーン3の平均粒子径は約25μmであり、嵩密度は0.1g/cm3であり、灰分は測定されなかった。
また、中空マイクロバルーン3の平均粒子径は約25μmであり、嵩密度は0.1g/cm3であり、灰分は測定されなかった。
<比較例1>
実施例1において、(A)成分を用いず、エチレンジアミンを0.05質量部に変更した以外は、同様の手法で中空マイクロバルーン4を作成した。
実施例1において、(A)成分を用いず、エチレンジアミンを0.05質量部に変更した以外は、同様の手法で中空マイクロバルーン4を作成した。
取得した中空マイクロバルーン4中の(A)成分と(B)成分の合計100質量部に対する(A)成分の割合は0質量部であった。
また、中空マイクロバルーン4の平均粒子径は約25μmであり、嵩密度は0.1g/cm3であり、灰分は測定されなかった。
また、中空マイクロバルーン4の平均粒子径は約25μmであり、嵩密度は0.1g/cm3であり、灰分は測定されなかった。
<実施例4>
トルエン:100質量部に、(A)成分のRX-2:0.9質量部溶解することで(c)成分を調製した。次に、水:200質量部にポリエチレン-無水マレイン酸:10質量部混合し、この混合液を10%水酸化ナトリウム水溶液でpH4に調製し、(d)成分を調製した。次に、調製した(c)成分と(d)成分を混合し、高速せん断式分散機を用いて2,000rpm×10分、25℃の条件で攪拌し、O/Wエマルションを調製した。調製したO/Wエマルションに、(B5)成分のニカレジンS-260:9質量部を加え、65℃で24時間攪拌した後、30℃に冷却後、アンモニア水でpH7.5になるまで添加し、メラミン樹脂からなるマイクロバルーン分散液を得た。得られたマイクロバルーン分散液を濾過によりマイクロバルーンを取り出し、温度60℃で真空乾燥24時間し、その後、分級機により篩い分け、中空ウレタンマイクロバルーン5を得た。なお、マイクロバルーン分散液を濾過した際、濾液にはメラミンは検出されなかった。
トルエン:100質量部に、(A)成分のRX-2:0.9質量部溶解することで(c)成分を調製した。次に、水:200質量部にポリエチレン-無水マレイン酸:10質量部混合し、この混合液を10%水酸化ナトリウム水溶液でpH4に調製し、(d)成分を調製した。次に、調製した(c)成分と(d)成分を混合し、高速せん断式分散機を用いて2,000rpm×10分、25℃の条件で攪拌し、O/Wエマルションを調製した。調製したO/Wエマルションに、(B5)成分のニカレジンS-260:9質量部を加え、65℃で24時間攪拌した後、30℃に冷却後、アンモニア水でpH7.5になるまで添加し、メラミン樹脂からなるマイクロバルーン分散液を得た。得られたマイクロバルーン分散液を濾過によりマイクロバルーンを取り出し、温度60℃で真空乾燥24時間し、その後、分級機により篩い分け、中空ウレタンマイクロバルーン5を得た。なお、マイクロバルーン分散液を濾過した際、濾液にはメラミンは検出されなかった。
取得した中空マイクロバルーン5中の(A)成分と(B)成分の合計100質量部に対する(A)成分の割合は、9.1質量部であった。
また、中空マイクロバルーン5の平均粒子径は約30μmであり、嵩密度は0.13g/cm3であり、灰分は測定されなかった。
また、中空マイクロバルーン5の平均粒子径は約30μmであり、嵩密度は0.13g/cm3であり、灰分は測定されなかった。
<比較例2>
実施例4において、(A)成分を用いずに、トルエン100質量部のみで(c)成分を調製した以外は、同様の手法で中空マイクロバルーン6を作成した。なお、マイクロバルーン分散液を濾過した際、濾液にはメラミンは検出されなかった。
実施例4において、(A)成分を用いずに、トルエン100質量部のみで(c)成分を調製した以外は、同様の手法で中空マイクロバルーン6を作成した。なお、マイクロバルーン分散液を濾過した際、濾液にはメラミンは検出されなかった。
取得した中空マイクロバルーン6中の(A)成分と(B)成分の合計100質量部に対する(A)成分の割合は、0質量部であった。
また、中空マイクロバルーン6の平均粒子径は約30μmであり、嵩密度は0.13g/cm3であり、灰分は測定されなかった。
また、中空マイクロバルーン6の平均粒子径は約30μmであり、嵩密度は0.13g/cm3であり、灰分は測定されなかった。
<実施例5>
(中空マイクロバルーンを用いたCMP用研磨パッド製造方法)
上記で製造したRX-1:24質量部と4,4’-メチレンビス(o-クロロアニリン)(MOCA):5質量部とを120℃で混合して均一溶液にした後、十分に脱気し、A液を調製した。別途、70℃に加温した上記で製造したPre-1:71質量部に、実施例1で得られた中空マイクロバルーン1:3.3質量部を加え、自転公転攪拌機で攪拌して均一な溶液とした。そこに、100℃に調製したA液を加え、自転公転攪拌機で攪拌して均一な重合性組成物とした。前記重合性組成物を金型へ注入し、100℃で15時間硬化させ、ウレタン樹脂を得た。
(中空マイクロバルーンを用いたCMP用研磨パッド製造方法)
上記で製造したRX-1:24質量部と4,4’-メチレンビス(o-クロロアニリン)(MOCA):5質量部とを120℃で混合して均一溶液にした後、十分に脱気し、A液を調製した。別途、70℃に加温した上記で製造したPre-1:71質量部に、実施例1で得られた中空マイクロバルーン1:3.3質量部を加え、自転公転攪拌機で攪拌して均一な溶液とした。そこに、100℃に調製したA液を加え、自転公転攪拌機で攪拌して均一な重合性組成物とした。前記重合性組成物を金型へ注入し、100℃で15時間硬化させ、ウレタン樹脂を得た。
得られたウレタン樹脂をスライスして、以下に示す厚さ1mmのウレタン樹脂からなるCMP用研磨パッドを得た。
上記で得られたウレタン樹脂からなるCMP研磨パッドの研磨レートは4.5μm/hr、被研磨物であるウエハの研磨後の表面粗さは0.14nm、CMP用研磨パッドの耐摩耗性評価のために実施したテーバー摩耗試験におけるテーバー摩耗量は14mgであった。各評価方法を以下に示す。
(1)研磨レート:研磨条件を下記に示す。ウエハは10枚を使用した。
下記条件にて、研磨を実施した際の研磨レートを測定した。研磨レートは10枚ウエハの平均値である。
CMP用研磨パッド:表面に同心円状の溝を形成した、大きさ500mmφ、厚さ1mmのパッド
被研磨物:2インチサファイアウエハ
スラリー:FUJIMI コンポール 80原液
圧力:4psi
回転数:45rpm
時間:1時間
下記条件にて、研磨を実施した際の研磨レートを測定した。研磨レートは10枚ウエハの平均値である。
CMP用研磨パッド:表面に同心円状の溝を形成した、大きさ500mmφ、厚さ1mmのパッド
被研磨物:2インチサファイアウエハ
スラリー:FUJIMI コンポール 80原液
圧力:4psi
回転数:45rpm
時間:1時間
(2)表面粗さ(Ra):上記(1)で記載した条件で研磨した際の10枚のウエハの表面をナノサーチ顕微鏡SFT-4500(株式会社島津製作所製)により表面粗さ(Ra)を測定した。表面粗さは10枚の平均値である。
(3)耐摩耗性:テーバー社製の5130型の装置で摩耗量を測定した。荷重は1Kg、回転速度は60rpm、回転数は1000回転、摩耗輪はH-18でテーバー摩耗試験を同一サンプルで同じ箇所で2回実施し、その平均値で評価した。
<実施例6~9、比較例3~5>
表1に示した組成を用いた以外は、実施例5と同様な方法でウレタン樹脂からなるCMP用研磨パッドを作製し、評価を行なった。結果を表1に記載する。
表1に示した組成を用いた以外は、実施例5と同様な方法でウレタン樹脂からなるCMP用研磨パッドを作製し、評価を行なった。結果を表1に記載する。
表1の結果から分かるように、本発明の製造方法で得られた(A)ポリロタキサンモノマーを含有してなる中空マイクロバルーンを用いたCMP用研磨パッドは、優れた研磨レートや被研磨物のウエハをより平滑に研磨する等の研磨特性が向上している。さらに、該CMP研磨パッドは、耐摩耗性の試験の結果が良好であり、優れた耐久性も有していた。
また、前記したとおり、CMP用研磨パッド母体の樹脂組成にも(A)ポリロタキサンモノマー成分を含有しているほうが好ましいが、実施例9と比較例5の比較から分かるように、CMP用研磨パッド母体の樹脂組成として(A)成分を用いていない場合でも、本発明の中空マイクロバルーンを用いることで、研磨特性を向上させることが可能となる。
Claims (8)
- (A)分子内に少なくとも2つの重合性官能基を有するポリロタキサンモノマーと、(B)前記(A)分子内に少なくとも2つの重合性官能基を有するポリロタキサンモノマー以外の重合性モノマーとを含む重合性組成物を重合させた樹脂からなる中空マイクロバルーン。
- 前記重合性組成物の(A)分子内に少なくとも2つの重合性官能基を有するポリロタキサンモノマーの含有量が、(A)分子内に少なくとも2つの重合性官能基を有するポリロタキサンモノマーの含有量と(B)前記(A)分子内に少なくとも2つの重合性官能基を有するポリロタキサンモノマー以外の重合性モノマーの合計100質量部に対し、1~50質量部である請求項1に記載の中空マイクロバルーン。
- 前記樹脂が、ウレタン(ウレア)樹脂、メラミン樹脂、尿素樹脂、及びアミド樹脂からなる群から選択される少なくとも1種以上である請求項1または2に記載の中空マイクロバルーン。
- 前記(A)分子内に少なくとも2つの重合性官能基を有するポリロタキサンモノマーの重合性官能基が、水酸基またはアミノ基である請求項1~3のいずれか1項に記載の中空マイクロバルーン。
- 前記(A)分子内に少なくとも2つの重合性官能基を有するポリロタキサンモノマーの環状分子の少なくとも一部に、側鎖が導入されている請求項1~4のいずれか1項に記載の中空マイクロバルーン。
- 前記(A)分子内に少なくとも2つの重合性官能基を有するポリロタキサンモノマーの側鎖の数平均分子量が5,000以下である請求項5に記載の中空マイクロバルーン。
- 前記(A)分子内に少なくとも2つの重合性官能基を有するポリロタキサンモノマーの重合性官能基が、前記(A)分子内に少なくとも2つの重合性官能基を有するポリロタキサンモノマーの側鎖に導入されてなる請求項5または6に記載の中空マイクロバルーン。
- 請求項1~7のいずれか1項に記載の中空マイクロバルーンを含んでなるCMP用研磨パッド。